Radiation-Shielding Properties of Heavy Bentonite-Based Slurry for the Decommissioning of the Fukushima First Nuclear Power Plant
Ema Yoshikawa1; Hideo Komine1; Yuma Saito1;
Shigeru Goto1; Seiichi Narushima2; Yasunori Arai2;
Masayuki Mizuno3; Shinsuke Ujiie3; Yuki Sakoda3; Yasushi Nagae4;
Mitsugu Yoshimura5; and Akihiko Suzuki5
1Dept. of Civil and Environmental Engineering, School of Creative Science and
Engineering, Waseda Univ., Japan. 2Seibu Construction Co., Ltd.; 3Hojun Co., Ltd.; 4TELNITE Co., Ltd.;
5Soil and Rock Engineering Co., Ltd.
Abstract: The 2011 off the Pacific coast of Tohoku earthquake has impacted Japan, and it made serious damage to nuclear power plant in Fukushima. At present, Japanese government and engineers proceed decommissioning of the power plant, and ensuring safety of workers is the most important matter especially in fuel debris retrieval. On these backgrounds, the authors focus on heavy bentonite based slurry for filling material of nuclear reactor. Heavy slurry is capable of shielding gamma ray and neutron beam from its high specific gravity and water content. The purpose of this research is to investigate and define the properties of heavy bentonite based slurry by soil mechanics experiment. That is, the research described in this paper is a proposal to use it for decommissioning of the Fukushima I nuclear power plant. For quantifying the radiation shielding properties, the authors measured the transmitted radiation dose through heavy slurry. The result shows the heavy slurry has definite radiation shielding properties. In conclusion, the heavy bentonite based slurry may be useful for radiation shielding, and save workers health in particular. 1. INTRODUCTION
Whole of Japan was impacted by the 2011 off the Pacific coast of Tohoku earthquake. There has been severe situation because of the radioactive contamination around and inside of the nuclear reactors in Fukushima I nuclear power plant. Moreover, there must be some people who struggle to cope with difficult problems on the surrounding spot. Under such circumstance, radiation shielding material is necessary from the point of view of reducing the possibility of exposure to the workers in fuel debris retrieval and construction of soil covered facility of radioactive waste. Since the accident occurred, Nuclear Emergency Response Headquarters had decided the medium- and long-term roadmap for decommissioning of Units 1 to 4. FIG.1 shows one of the methods to protect workers from radiation in fuel debris retrieval proposed in the roadmap. It makes a suggestion that filling a reactor vessel with water to cooling a reactor and radiation shielding. However, the radiation shielding by water is not fully effective.
Geo-Chicago 2016 GSP 269 292
© ASCE
FI
W
Consnuclehigh relateconteneutrbeta beamthe pshiel 2. P 2.1 M
Hbentogravibaritheavparam
Soil LiquPlastPlast
G.1. Metho
Water can ssequently, thear reactor, b
specific gred to gamment, shieldinron beam harays. Note
m is indispenprevious reslding.
PRODUCT
Materials of
Heavy slurryonite. Bariteity that is the is about 4.
vy slurry for meter of ben
Tab
particle densuid limit (%) tic limit (%) ticity index
d of fuel deaccordin
shield only he authors fobecause of itravity mater
ma ray. In adng effect of nave prominethat such ra
nsable to thsearch (Kom
HEAVY SL
heavy bento
y is composee is a minerahe greatest f.21. Sodium preventing
ntonite and m
ble 1. Funda
sity (Mg/m3)
bris retrievng to mediu
neutron beocus on heavts exceptionaial shows e
ddition, if thneutron beament penetratiadiation shiee constructimine, 2015)
LURRY
onite based s
ed of water, al composedfeature of hpyrophosphprecipitation
mixing ratio
amental par
)
al that fillinm- and long
am as almovy bentoniteal shielding
excellent chahe high specm increasesion of substelding conceon of decom), the heavy
slurry
sodium pyrd mainly of beavy slurry
hate is dispern of particleof heavy ben
rameter of b
2.62 547.0 47.39 499.61
ng the nucleg-term road
ost same me based slurproperties. Iaracteristic
cific gravity . As a familtance in comerned with
mmissioningy slurry can
rophosphatebarium sulfais due to b
rsing agent aes. Table 1 antonite based
bentonite (S
ear reactor wdmap
mass as hydrry for fillingIt was confirof radioactimaterial ha
liar fact, gammparison wigamma ray
g. Accordingn be used
, barite and fate and the barite. Particand bentonitand 2 show d slurry.
Super clay)
with water
drogen atomg material ormed that thive reductionas high watemma ray anith alpha an
and neutrongly, based onfor radiation
sodium-typhigh specifile density ote is added tfundamenta
m. of he n
er d d n n n
e ic of o al
Geo-Chicago 2016 GSP 269 293
© ASCE
Table 2. Mixing ratio of heavy bentonite based slurry Case Water
(g) Sodium pyrophosphate(g)
Barite (g)
Bentonite (Super clay) (g)
Specific gravity
A 100 0.2 400 7 2.5 B 100 0.2 140 10 1.8 C 100 0.2 10 12 1.1 2.2 Method of producing heavy bentonite based slurry
The method of manufacturing the heavy bentonite slurry is presented as below. An electric stirrer is used to production of heavy slurry. FIG.2 shows a method of producing heavy bentonite based slurry and FIG.3 is a picture of heavy bentonite based slurry . 1) Required amount of water in stirring vessel is stirred 2 minutes on about 400rpm after added sodium pyrophosphate. 2) The slurry is stirred 2 minutes on 400rpm after added bentonite. 3) The slurry is stirred 2 minutes on 400rpm after added barite.
FIG.2. Method of producing heavy bentonite based slurry
Required amount of wateris in stirring vessel.
2)The slurry is stirred 2 minuteson 400 rpm after added bentonite.
3)The slurry is stirred 2 minuteson 400 rpm after added barite.
mix
1)Water is stirred 2 minutes onabout 400 rpm after addedsodium pyrophosphate
sodium pyrophosphatebarite
bentonite
electric stirrer
Geo-Chicago 2016 GSP 269 294
© ASCE
3. R
3.1 M
Mray sconfishielbeam 1) Aheav2) A survedetec3) W4) W
RADIATION
Method of exp
Measuremensource and nfirm a relatilding. FIG.4 m test.
After preparivy slurry. (InA source of g
ey meter is ctor is fixed
When measurWhen a case o
FIG
FIG.3. P
N SHILDIN
xperiment
nt method ofneutron beamion betweenand 5 show
ng the heavside dimensi
gamma ray oput on the to 150 mm bed value becof test has be
G. 4. Picture (left: gam
Picture of he
NG PROPE
f transmittedm source ar
n specific grw the setup o
vy bentoniteions of acrylor neutron b
contrast sidboth of gammcomes steadyeen complete
of setup of mma ray tes
eavy benton
RTIES TES
d radiation dre used in thravity of he
of the experim
e based slurrlic container
beam is put ode. The distma ray and ny, record theed, the test p
radiation shst, right: neu
nite based sl
ST
dose is presehe test. Maineavy slurry ment of gam
ry, acrylic cr is 300mm xon the side tance betweneutron beam
e transmittedpasses next c
hielding proutron beam
lurry
ented the ben theme of and effect
mma ray test
containers fix 300mm x 1of acrylic co
een radiationm test.
d radiation docase.
operties testm test)
elow. Gammthe test is tof radiation
t and neutron
illed up with100mm.) ontainer, ann source an
ose.
t
ma o n n
h
d d
Geo-Chicago 2016 GSP 269 295
© ASCE
3.2 T
Fheav
FIG
FIG
Test Result an
FIG.6 showsvy slurry in c
G.6. Relation
G.5. Image o(left: gam
nd discussio
s the relationcase of heavy
n between th(right graph
of setup of rmma ray tes
on
n between thy slurry thick
he gamma rh) and the s
radiation shst, right: neu
he gamma rkness is 100m
ray dose (lefspecific grav
hielding proutron beam
ray dose andmm fixed.
ft graph) or vity of heav
operties test m test)
d the specif
the neutronvy slurry
fic gravity o
n beam dose
of
e
Geo-Chicago 2016 GSP 269 296
© ASCE
Following the study, it is clarified that gamma ray shielding is due to specific gravity of the heavy slurry. Gamma ray dose decreases with increasing of specific gravity. On the other hand, neutron beam dose increases with increasing of specific gravity because neutron beam dose is caused by water content. That is penetrated material has high neutron beam shielding property when it has low specific gravity. The test result shows specific gravity of heavy slurry has opposite effect between gamma ray and neutron beam shielding. Based on the study, the authors will pursue the most suitable mixing ratio of heavy slurry with the perspective of the shielding properties of gamma ray and neutron beam. 4. CONCLUSIONS
In this paper, author describes fundamental data to confirm the radiation shielding properties of bentonite based heavy slurry. The following conclusions were drawn from this study. 1) Gamma ray shielding is due to high specific gravity of the heavy slurry. 2) Neutron beam dose is caused by water content and it means material has high neutron beam shielding property when it has low specific gravity. 3) The specific gravity of heavy slurry must be considered from a point of view of difference shielding effect between gamma ray and neutron beam. On the actual construction, a balance of each radiation shielding is a matter of great importance. 5. REFERENCES Komine, H., (2015). “Radiation shielding experiments of geo-material for recovery from
the Fukushima I nuclear power plant accident”, Geo-Environmental Engineering 2015 (to be published).
Suzuki, A., (2014). “The absorption/capture of the neutron ray to emit from Californium 252”, 50th JGS Symposium (in Japanese) (to be published).
Ujie, S., (2014). “The development of high-radiation-shielding and flexible materials”, 11th JGS Symposium on Environmental Geotechnics (in Japanese) :471-478.
Saito, Y., (2014). “Radiation shielding poroperties of heavy slurry which assumed fuel debris retrival”, 11th JGS Symposium on Environmental Geotechnics (in Japanese): 483-488.
Nuclear Emergency Response Headquarters ., (2015) "Mid-to-Long Term Roadmap (RM) on decommissioning of Fukushima Daiichi Nuclear Power Station"
Geo-Chicago 2016 GSP 269 297
© ASCE