Proses Produksi PTKS

7/22/2019 Proses Produksi PTKS

1/24

Partnership for Sustainable Growth

ROMBONGAN MAHASISWA

TEKNIK KIMIA POLITEKNIK NEGERI SRIWIJAYAPALEMBANG

Di

Cilegon, 26 Agustus 2013


2/24

Partnership for Sustainable Growth

1. Sambutan ;

- Pimpinan Romongan

- Management PT Krakatau Steel (Persro) Tbk

2. Film Company Profile of PT KS

3. Presentasi Business Process PTKS

4. Kunjungan Lapangan (Plant Visit)


3/24

Partnership fo r Sustainable Grow th

)


4/24

Map Of anten Province

PT Krakatau Steel



5/24

SEJARAH PT KRAKATAU STEEL

1956 1957 Gagasan Ir.H Juanda untuk membangun Industri baja danPenelitian lokasi oleh Biro Perancang Nasional

07-06-1960 Kontrak Pembangunan dengan Uni Sovyet20-05-1962 Peletakan Batu Pertama Proyek Besi Baja TRIKORA

( TAP MPRS No.2 tahun 1962)

1965 1967 Terhenti ( terjadi gejolak politik ) meletusnya G30SPKI

28 - 12 -1967 Pembangunan Industri Baja dilanjutkan status Proyek

diganti menjadi PT KRAKATAU STEEL( Inpres No.17)

31 - 08 -1970 PT KRAKATAU STEEL didirikan melanjutkan Proyek BesiBaja TRIKORA ( Peraturan Pemerintah No.35)

1977 Diresmikan Pabrik Kawat,Pabrik Baja Tulangan danPabrik Baja Profil

1979 Diresmikan Pabrik Besi Spons ( HYL-I),Pabrik Billet Baja,Pabrik Batang Kawat,dan Fasilitas infrastruktur ( PLTU,Pengadaan Air,Pelsus Cigading dan Telekomunikasi)

1983 Diresmikan Pabrik Slab Baja dan Pabrik Baja Lembaran

Panas


6/24

1983 Diresmikan Pabrik Slab Baja dan Pabrik BajaLembaran Panas

1991 Pabrik Baja Lembaran Dingin diakuisisi ( merger)menjadi unit produksi PT KS Pabrik Kawat,PabrikBaja Tulangan dan Pabrik Baja Profil menjadi PTKrakatau Wajatama

1993 Diresmikan Pabrik Besi Spons HYL III dan Pabrik Slab

Baja -21996 Restrukturisasi Perusahaan : PLTU, Pengadaan Air

Pelabuhan dan Rumah Sakit

1999 Bergabung menjadi anggota PT BPIS ( BahanaPakarya Industri Strategis)

2002 Pembubaran PT BPIS menjadi BUMN2003 Optimalisasi Cold Rolling Mill : 950.000 ton/thn

Optimalisasi Hot Rolling Mill : 2.4juta ton/thn


7/24

Korporasi PTKS

PT KRAKATAU STEEL(Persero) Tbk

ANAK PERUSAHAAN PERUSAHAAN PATUNGAN

PT KRAKATAU INFORMATIONTECHNOLOGY

100%

PT KHI PIPE INDUSTRIES

93,20%

PT KRAKATAU ENGINEERING100%

PT KRAKATAU BANDARSAMUDRA

100%

PT KRAKATAU MEDIKA

100%

PT KRAKATAU WAJATAMA

100%

PT BUKIT BAJA BUANA

30%

PT KRAKATAU NASIONAL,

PT KRAKATAU TIRTA INDUSTRI100%

PT KRAKATAU DAYA LISTRIK100%

PT KRAKATAU INDUSTRIALESTATE CILEGON

100%

PT MARGA MANDALA SAKTI1,29%

PT SPIJ3,24%

PT INDAREF10%

PT METBELOSA

15%

PT KERISMAS W MAKMUR29,34% = PTKS : 9,8%

PT KIEC: 19,54%

PT KPDS30%

PT. Meratus Jaya Iron

SteelPT.Meratus Jaya Iron & Steel

RESOURCES 100 %


8/24Partnership fo r Sustainable Grow th

Visi Perusahaan

Perusahaan baja terpadu dengan keunggulan kompetitif

untuk tumbuh dan berkembang secara berkesinambungan

menjadi perusahaan terkemuka di dunia

Misi Perusahaan

Menyediakan produk baja bermutu dan jasa terkait bagikemakmuran bangsa


9/24

Fasilitas Pabrik PTKS

Pabrik

Kapasitas

(ton/th)2004

Teknologi & Kontraktor TahunPembuatan

Pabrik Besi Spons 1 1.000.000 Direct Reduction HyL-1 / HYLSA 1978

Pabrik Besi Spons 2 1.500.000 Direct Reduction HyL-3 / HYLSA 1993

Pabrik Slab Baja 1 1.000.000 EAF & CCM / MANGHH & CONCAST 1983

Pabrik Slab Baja 2 800.000 EAF & CCM / VAI & CONCAST 1993

Pabrik Billet Baja 675.000 EAF & CCM / MANGHH & CONCAST 1978

Pabrik Baja Lembaran

Panas

2.400.000 Conventional Hot Rolling Mill / SMS 1983

Pabrik Baja LembaranDingin

950.000 Continuous Tandem / VAI CLECIM 1986

Pabrik Batang Kawat 450.000 Wire Rod Mill / SMS & MORGAN 1978


10/24

ALIRAN PRODUK PT KRAKATAU STEEL

Hot Strip Coil

Billet SteelWire Rod

Cold Roll C/S

Hot Strip Sheet

Slab Steel

Steel MakingSpongePellet

Iron Pellet Besi

Spons

Dapur

Listrik

Billet Baja Batang Kawat /Baja Batangan

Slab BajaCoil Shet /

Plat Baja

Gulungan

Plat Baja

Lembaran


11/24

1650oC


12/24

Gas Based IRON MAKING

PROCESS

MANUFACTURING METHOD(AT PTKS)

Typical DRI quality :

Metalization 92 - 94%Fe Metal 92 - 94%

Total Carbon 1 - 3 %

Phosphor max. 0.05%Sulphur max. 0.03%



13/24

Jenis Produk Baja

Baja Carbon Rendah

Baja Carbon Medium

Baja Carbon Tinggi


14/24

14

Gas Base Integrated Steel Plant Route

Direct Reduction Plantconvert iron ore pellet into

sponge iron

Slab Steel Plantproduce slab steel fromsponge iron and scrap

Hot Strip Millroll slab steel into

hot rolled coil and plateCold Rolling Mill

manufacture cold rolled plateand sheet from hot rolled coil

Billet Steel Plantmake billet steel fromsponge iron and scrap

Wire Rod Millfabricate wire rodfrom billet steel


15/24

15

Coal BaseIntegrated Steel Plant Route

Blast Furnace Plantconvert iron ore into hot

metal/pigiron

Slab Casterproduce slab steel

Hot Strip Millroll slab steel into

hot rolled coil and plate

Cold Rolling Millmanufacture cold rolled plateand sheet from hot rolled coil

Billet Casterproduce billet steel

Wire Rod Millfabricate wire rodfrom billet steel

BF

BOF

Basic OxygenFurnace

convert hot metal into

liquid steel


16/24

Proses Produksi di PT Krakatau Steel

Pabrik Besi Spons

Pabrik Slab Baja Pabrik Baja GulunganHot Rolled

(2,000,000 t/y)Pabrik Baja GulunganCold Rolled

(850,000 t/y)

Pabrik Bilet Baja Pabrik Batang Kawat(600,000 t/y)

Pellet:

Bijih Besi

(2,200,000t/thn)


17/24

PERBEDAANBESIDAN BAJA

BESI

Paduan antara unsur besi (Fe) dengan unsur karbon(C).Apabila paduan tersebut mengandung Carbon lebih besardari pada 2%maka disebut BESI. BESImempunyai sifat-sifatdominant kekerasanyang relative tinggi, tetapi sangat getas

(brittle)dan tidak dapat ditempa.

BAJA

Paduan antara unsur besi (Fe) dengan unsur karbon(C).Apabila paduan tersebut

mengandung Carbon lebih kecildari pada 2%maka disebut BAJA. BAJArelative lebih lenturdan dapatditempadan dilas.


18/24

Keunggulan Baja

Kaya akan sifat-sifat

Tersedia di alam dalam jumlah yang melimpah

Proses pengolahan yang mudah dan murah Dapat didaur ulang



19/24

HOT ROLLING PROCESS(HSM)

Shape & surface

defect

Dimension

Weighing Sampling

% final thickness

reduction

Temperature

Pass Schedule Automatic Gauge

Control

Rolling speed

Cooling mode

Width setting

% thickness

reduction

Temperature Pass schedule

Rolling speed

Temperature

setting

Soaking time

Air pressure Appearance of slab

DOWN COILERFINISHINGROUGHINGFURNACE

MANUFACTURING METHOD(AT PTKS)HSM : 2,000,000 T/y


20/24

Cold Rolled Products

Cold Rolled Coil(CRC)

Cold Rolled

Sheet (CRS)


21/24

SIZE & APPLICATION

PRODUCT SIZE SPECIFICATION MAJOR APPLICATION

HRC/P Thickness 1.8 to 25 mm Automotive Ship Build

(Hot Rolling Width 600 to 2080 mm Constr. & Fab. Containers

Coil / Plate) Pipe & Tube

CRC/S Thickness 0.18 to 3.0 mm Appliance Tin Plate

(Cold Rolling Width 500 to 1250 mm Automotive Enamel

Coil / Shet) Drum Pipe

Galvalum

Wire Rod Diameter 5.5 to 20 mm Nail Electroda

Bendrad Bold & Nut

Wiremesh Spring Bed

Shafting Bar


22/24

Perhatian!

Tata Tertib Kunjungan Industri PT Krakatau Steel:

1. Memakai Alat Pelindung Diri (APD) : Helm.

2. Dilarang merekam atau mengambil gambar.

3. Berjalan di jalur hijau.


23/24

Untuk PKL Surat ditujukan

Kepada Yth.

Manager Human Capital Training

& Education Center

PT Krakatau Steel (Persero) Tbk

Jl. Jend. Sudirman Km.3

Cilegon 42435

Telp.: 0254 372130 Fax: 0254 372337


24/24

TERIMAKASIH

Proses Produksi PTKS