Wood Technology and Wood Chemistry
(;E()K(;,.ALJ(:;L)ST-l)N]VEKSITA1(, ()7TIN(;r\
FTIRAnalysis Report
Client:ZHEJIANG XINHAIYE BAMBOO TECHNOLOGY CO, LTD.
Sample Receivedon: 07/26/2019
Sample Name: DassoCTECHSample State: Powder
(Obtained from test sample)
Manufacturer: Jiangxi Zhushang Bamboo Industry Co., LtdFujian Dasso Bamboo Technology Co., Ltd
Brand: DASSO
TestTechnique: Infrared Spectrum Analysis
Test Instrument: Bruker Alpha FourierTransform Infrared Spectrometer
Chemical compounds for comparison:
Compound l: Boricacid, CAS-No: 10043-35-3, EC-No: 233-139-2, Received from Applichem GmbH;
Compound 2: Diboron trioxide, CAS-No: 1303-86-2, EC-No: 215-125-8, Received from Alfa Aesar;
Compound 3: Tetraboron disodium heptaoxide, hydrate, CAS-No: 12267-73-1, EC-No: 235-541-3,
Received from MerckGroup;
Compound 4: Disodium tetraborate anhydrous, CAS-No: 1330-43-4, EC-No: 215-540-4, Received
from Merck Group;
Compound 5: Sodium perborate, CAS-No: 10332-33-9, EC-No: 231-556-4, Received from Sigma-
Aldrich;
Compound 6: Lead bis(tetrafluoroborate), CAS-No: 13814-96- 5, EC-No: 237-486-0, Received from
Sigma-Aldrich;
Compound 7: Disodium octaborate tetrahydrate, CAS-No: 12008-41-2, EC-No: 234- 541-0, As-prepared
according to the Patent: CN104477930A;
Page l of11 August 2, 2019
Page 2
Wood Technology and Wood Chemistry
Results
FTIR analysis was used to confirm whether the tested sample contains boron-based chemical
compounds or not. Figure l shows the FTIR spectra oftested samples (DassoCTECH-1 from the inner
part and DassoCTECH-2 from the surface part). Since the FTIR spectra of DassoCTECH-1 and
DassoCTECH-2 are the same, the spectrum of DassoCTECH-1 was used to compare with other chemical
compounds. Figure 2 displays the comparison of FTIR spectra of DassoCTECH-1 and boric acid (CAS#
10043-35-3). Figure 3 displays the comparison of FTIR spectra of DassoCTECH-1 and diboron trioxide
(CAS#1303-86-2). Figure 4 displays the comparison of FTIR spectra of DassoCTECH-1 and tetraboron
disodium heptaoxide, hydrate (CAS#12267-73-1). Figure 5 displaysthe comparison of FTIR spectra of
DassoCTECH-1 and disodium tetraborate anhydrous (CAS#1330-43-4). Figure 6 displays the comparison
of FTIR spectra of DassoCTECH-1 and sodium perborate (CAS#10332-33-9). Figure 7 displays the
comparison of FTIR spectra of DassoCTECH-1 and Lead bis(tetrafluoroborate) (CAS#13814-96- 5).
Figure 8 displays the comparison of FTIR spectra of DassoCTECH-1 and disodium octaborate
(CAS#12008-41-2).
On the basis of these comparisons, a conclusion is confirmed äs follows:
FTIR spectrum oftested sample DassoCTECH doesn't displaythe characteristic peaks of boric
|acid, diboron trioxide, sodium tetraborate heptahydrate, disodium tetraborate anhydrous, sodium
perborate, Lead bis(tetrafluoroborate), and disodium octaborate.
Inspector: Hua Zhang Facility: Wood Technology and Wood Chemistry,Georg-August-University of Göttingen
Büsgenweg 4, 37077 Göttingen, Germany
"^^s
Page 2 of11 August 2, 2019
Page 3
I % W p i cra c ä NJ s 1->
U3
n> -0 0) r5 a.
in EU 3 -a fü W fD t/1
t^^^-
«.
:^~
%
S' s i i
. ^.^
!W^'
^ .* t
^ 5 l l Q.
t/1
eu 3 -0 fD 0 tu tn s
j"ji }'f
< v. ji
i: ^
i<
';
is ^ ;:1
i .^.
t;;;
;/;i^i .
-
?ii'
i'i!ji
iiii
>i§i
Il.
>ii l?i
j sl
JH S i? 8 ?
8 Q. i 3 0 i 0) 3 Q. l n 3-
eo 3
Page 4
(/) �
C
Q)
C
.0
(/) .0
Comments:
\XI� 0.10��R �
0.08 �
0.06
0.04 �
0.02
0.00 1w I._,,
4000 3500
I
co N
,..__ 0) co N
I
3000
Wood Technology and Wood Chemistry
N co co 0
co 0) N 0) ,..__ I{) ...... ...-
...--,-....cococo(")N O lO CO,..__ NO(") 0 N
c--.i<rimoor---:�00 ...-- 10 ...-- CO N (") lO N 10 -.:t -.:t (") C'0 N ...-- 0 �r-r--r-r- r-r--r-
��\�\
DassoCTECH-1 DassoCTECH-2
�M��
2500 2000 1500 1000
Wavenumber cm-1
500
DassoCTECH-1 and DassoCTECH-2 were obtained from the inner and the surface part of the sample received from ZHEJIANG XINHAIYE
BAMBOO TECHNOLOGY CO., LTD. As seen, the FTIR spectra of these two samples are totally the same without any external peaks appeared.
Page 4 of 11 August 2, 2019
Page 5
Wood Technology and Wood Chemistry
0. 06
Ü) DassoCTECH
0.0
4000 3500 3000 2500 2000 1500
Wavenumber cm-1
1000 500
Comments:
The characteristic peaks of boric acid (CAS# 10043-35-3) can't be observed in the spectrum of DassoCTECH-1, which indicates that the
DassoCTECH-1 sample doesn't contain boric acid.
Page 5 of 11 August 2, 2019
Page 6
Wood Technology and Wood Chemistry
0. 06
0. 04ü)
-§ 0. 02(U^ 0. 00(ü£ 0. 16
l 0. 12<
0. 08
0. 04
0. 00
BBKER
4000
DassoCTECH
Diboron trioxide
3500 3000 2500 2000 1500
Wavenumber cm-1
1000 500
Comments:
The characteristic peaks ofdiboron trioxide (CAS#1303-86-2) can't be observed in the spectrum of DassoCTECH-1, which indicates
that the DassoCTECH-1 sample doesn't contain diboron trioxide.
Page 6 of11 August 1, 2019
Page 7
Wood Technology and Wood Chemistry
0. 06
0. 04
^S 0. 02
(Ug 0. 00co.Q
l 0. 04<
0. 02
0. 00
-00--BR%R
4000
Tetraboron disodium heptaoxide, hydrate
3500 3000 2500 2000 1500Wavenumbercm
-11000 500
Comments:
The characteristic peaks oftetraboron disodium heptaoxide, hydrate (CAS#12267-73-1) can't be observed in the spectrum of
DassoCTECH-1, which indicates that the DassoCTECH-1 sample doesn't contain tetraboron disodium heptaoxide, hydrate.
Page 7 of11 August 2, 2019
Page 8
Wood Technology and Wood Chemistry
0. 06
0. 04
0. 02
</)
c
=)
8c 0. 00s
l °. 12<
0. 08
0. 04
0. 00
[.̂ S
4000
DassoCTECH-1
Disodium Tetraborate anhydrous
3500 3000 2500 2000 1500
Wavenumber cm-1
1000 500
Comments:
The characteristic peaks ofdisodium tetraborate anhydrous (CAS#1330-43-4) can't be observed in the spectrum of DassoCTECH-1,
which indicates that the DassoCTECH-1 sample doesn't contain disodium tetraborate anhydrous.
Page 8 of 11 August 2, 2019
Page 9
Wood Technology and Wood Chemistry
0. 06
0. 04W
'^ 0. 02<ü^ 0. 00(U-2l °-35 0.2
0.1
0.0
.88R
4000 3500
Sodium perborate
3000 2500 2000 1500Wavenumber cm
-11000 500
Comments:
The characteristic peaks ofsodium perborate (CAS#10332-33-9) can't be observed in the spectrum of DassoCTECH-1, which indicates
that the DassoCTECH-1 sample doesn't contain sodium perborate.
Page 9 of 11 August 2, 2019
Page 10
Wood Technology and Wood Chemistry
0. 06
0. 04(^
^ 0. 02<ü^ 0. 00(0-sS 0.4^<
0.2
0.0
.^
Lead bis(tetrafluoroborate)
Wavenumber cm-1
1026. 60
DassoCTECH
4000 3500 3000 2500 2000 1500 1000 500
Comments:
The characteristic peaks of lead bis(tetrafluoroborate) (CAS#13814-96-5) can't be observed in the spectrum of DassoCTECH-1, which
indicates that the DassoCTECH-1 sample doesn't contain lead bis(tetrafluoroborate).
Page 10 of 11 August 2, 2019
Page 11
Wood Technology and Wood Chemistry
0. 06
0. 04
.1 0. 02D
CÜ
^ 0. 0003
g c)-12-Q<
0. 08
0. 04
0. 00
B88'
4000
l-l-l-l-l
Disodium octaborate
3500 3000 2500 2000 1500
Wavenumbercm-1
1000 500
Comments:
The characteristic peaks of disodium octaborate (CAS#12008-41-2) can't be observed in the spectrum of DassoCTECH-1, which
indicates that the DassoCTECH-1 sample doesn't contain disodium octaborate.
Page 11 of 11 August 2, 2019