Pages 177–186 http://dx.doi.org/10.1680/grim.12.00016
materials
Ground Improvement
sands
Markou and Droudakis
Shear strength of microfine cement grouted sands j1 Ioannis N.
Markou PhD
Assistant Professor, Department of Civil Engineering, Democritus
University of Thrace, Xanthi, Greece
j2 Alexandros I. Droudakis PhD Department of Civil
Engineering, Democritus University of Thrace, Xanthi, Greece
j1 j2
Unconsolidated–undrained (single and multi-stage) triaxial
compression tests were conducted to evaluate the shear
strength of microfine cement grouted sands. Microfine cements of
three different types were obtained by pulverising
ordinary cements produced in Greece. Multi-stage triaxial
compression tests can be used dependably for determina-
tion of the shear strength parameters of cement grouted sands. It
has been observed that the Mohr–Coulomb failure
criterion represents adequately the behaviour of the grouted sands.
Grouting with microfine cement suspensions
improves the strength of sands significantly, and the improvement
is primarily controlled by the water-to-cement
(W/C) ratio of the suspensions. The positive effect of microfine
cement grouting on the shear strength of sands is
mainly the addition of cohesion, which is substantial even at a
distance of 1.2 m from the injection point. Grouting
with suspension, using W/C 1 provides the sand with cohesion of
about 2.6 MPa. The shear strength parameters
vary with axial strain, and cohesion attains a maximum value well
before failure.
Notation C u uniformity coefficient
c cohesion (total stresses)
d i i% of grains finer than this grain size
d max nominal maximum grain size of cements
emax maximum void ratio
emin minimum void ratio
K f -line failure envelope resulting from
pf , qf values
p, q stress path coordinates (total
stresses)
pf , qf values of p
and q at failure (total stresses)
R2 correlation coefficient
3 confining pressure
j angle of internal friction (total stresses)
1. Introduction Microfine cement grouts have been used in the last
few decades
to extend the application range of ordinary cement grouts in
permeation grouting for ground improvement and to reduce
the
use of harmful chemical solutions. A variety of projects
through-
out the world, in which different microfine cement grouts
were
utilised, was reported by Henn and Soule (2010). The design
of
structural grouting projects is mostly based on the evaluation
of
mechanical properties of the grouted mass on the basis of
results
obtained from unconfined compression tests, although it is
generally accepted that the triaxial compression test best
simu-
lates field conditions. The available, relatively limited in
number,
laboratory investigations of the mechanical behaviour of
sands
grouted with microfine cement suspensions include results
obtained from consolidated–drained (Clarke et al., 1993;
Dano
et al., 2004; Krizek et al., 1992),
consolidated–undrained
(Krizek et al., 1986, 1992; Naeini and
Ziaie-Moayed, 2003) and
unconsolidated–undrained (Maalej et al., 2007) triaxial
compres-
sion tests. Numerical simulations of triaxial compression
test
results were also performed for the modelling of the
mechanical
behaviour of grouted sand (Hicher et al.,
2008).
The experimental investigation reported herein is part of an
extensive research effort aimed toward the development of a
relatively fine-grained material, suitable for permeation
grouting,
obtained by pulverisation of ordinary cements produced in
Greece. Suspensions of three different cement types, each at
three
different gradations, were tested. The aim of this study was
to
quantify the improvement of the shear strength parameters
of
sands by grouting with these coarse- and fine-grained cements,
to
177
document the effect of cement type and fineness, grout
water-to-
cement (W/C) ratio, sand gradation and distance from the
injec-
tion point and to evaluate the development of shear strength
parameters with axial strain. Multi-stage
unconsolidated–
undrained (M-UU) and unconsolidated–undrained (UU) triaxial
compression tests were conducted on grouted sand specimens
produced using a specially constructed grouting
apparatus.
2. Materials For the purpose of this investigation, three cement
types (Port-
land, Portland-composite and pozzolanic cement,
code-named
CEM I, CEM II/B-M and CEM IV/B, respectively, according to
European Standard EN 197-1 (BSI, 2000)) were utilised. The
amount of clinker used for production of the CEM I cement
(90%) is significantly higher in comparison with 63% and 58%
for CEM II/B-M and CEM IV/B cements, respectively, and the
pozzolan content increases from 0% (CEM I) to 23.5% (CEM
II/
B-M) and 38% (CEM IV/B). Consequently, the selected cement
types reflect the tendency of the cement industry to reduce
the
clinker percentage, by replacing a part of it with pozzolan,
in
order to produce more economical cements. Each ordinary
cement (nominal d max ¼ 100 m) was
pulverised, by performing
dry grinding in a special laboratory mill, to produce
additional
cements with nominal maximum grain sizes (d max) of 20 and
10 m. Characteristic grain sizes and Blaine specific
surface
values for all cements used in this research effort were
reported
by Pantazopoulos et al. (2012). In terms of
gradation, all cements
with nominal d max ¼ 10 m can be considered
as ‘microfine’
since they satisfy the requirements of Standard EN 12715
(d 95 , 20 m and specific surface over 800 m2/kg;
BSI (2001)),
as well as definitions adopted by the International Society
for
Rock Mechanics (ISRM), the American Concrete Institute (ACI)
Committee 552 and the Portland Cement Association (PCA)
(Henn and Soule, 2010). Furthermore, cements with nominal
d max ¼ 20 m have adequately small characteristic
grain sizes to
be considered, marginally, as ‘microfine’.
All suspensions tested during this investigation were
prepared
using potable water since it is considered appropriate for
prepar-
ing cement-based suspension grouts (Eriksson et al.,
2003;
Littlejohn, 1982). The W/C ratio of the suspensions was set
equal
to 1, 2 or 3 by weight because suspensions with a W/C. 3
would have prohibitively large bleeding, long setting times
and
low strengths, whereas suspensions with a W/C , 1 would have
prohibitively high viscosity (Bruce et al., 1997;
Littlejohn, 1982;
Lombardi, 2003). A superplasticiser (patented new generation
of
admixture based on polycarboxylate chemistry), at a dosage
of
1.4% by weight of dry cement, was used to improve the
suspension properties of the microfine cements. This fixed
super-
plasticiser dosage was determined following a laboratory
evalua-
tion of the effect of various dosages on the apparent viscosity
and
the rheological characteristics of the pulverised cement
suspen-
sions (Pantazopoulos et al., 2012). Suspension
preparation
required a total mixing time of 10 min in high-speed mixers,
of
the type used for the preparation of soil specimens for
hydro-
meter testing, with a speed of 10000 rpm at no load. The
experimental documentation of the suspension properties
and
groutability of the cements used in this investigation
indicates
that microfine cement suspensions, enhanced with
superplastici-
ser, have acceptable apparent viscosity, behave as Bingham
fluids,
that is, they present linear rheological (shear stress– shear
rate)
curves with constant slope defined as the plastic viscosity
and
intersecting the shear stress axis at a value defined as the
yield
stress, are stable for W/C ¼ 1, have reasonable setting times
for
field applications and can be injected into medium-to-fine
sands
(Pantazopoulos et al., 2012).
The soils used were clean, uniform, limestone sands with
angular
grains and were grouted at a dense (mean value of relative
density, Dr , 98 1%) and dry state. Four different sand
grada-
tions were used with grain sizes limited between ASTM sieve
sizes 5 and 10, 10 and 14, 14 and 25, and 25 and 50. The
properties of the sands, designated using the
aforementioned
sieve, are presented in Table 1. The values of the angle of
internal friction of the sands were obtained from UU triaxial
compression tests conducted on dense and dry specimens,
under
confining pressures equal to 100, 200 and 400 kPa. Dense
sands
tested under a wide range of confining pressures are expected
to
exhibit curved failure envelopes and, as a result, have
friction
angle values that decrease with increasing stress level.
However,
this behaviour was not observed in the present investigation,
possibly due to the range of confining pressures used in
the
Sand
friction,a j: o
a Sands in dense and dry condition.
Table 1. Properties of sands
178
grouted sands
triaxial compression tests. More specifically, the fitting of
the
experimental data with a linear failure envelope was
satisfactory
in all sands, resulting in the constant friction angle values
shown
in Table 1.
3. Experimental procedures The special apparatus shown in
Figure 1 was constructed and
used for injecting sand columns with cement suspensions. It
allows adequate laboratory simulation of the injection
process
and investigation of the influence of the distance from
injection
point on the properties of the grouted sand. The grouting
column
was made of a thick PVC tube with an internal diameter
of
75 mm and a height of 1440 mm, and was formed by placing at
each end a 50 mm thick gravel layer, between two screens
of
suitable aperture, and filling the remaining length (1340 mm)
with dense, dry sand. The rate of discharge of the pump was
regulated to be constant and equal to 60 l/h. Injection was
stopped when either the volume of the injected grout was
equal
to two void volumes of the sand in the column or when the
injection pressure became equal to 700 kPa. After injection,
the
grouted column remained on its base for 24 h, then its ends
were
sealed with plastic and it was stored in a vertical position.
After
curing for 28 days, the grouted columns were cut and some of
the
resulting specimens, with a length of 160 mm, were utilised
for
triaxial compression testing. Prior to testing, the loading
surfaces
of each specimen were capped using a cement-based
low-strength
compound.
content in multi-stage (three-stage)
unconsolidated–undrained
(M-UU) triaxial compression according to the procedures de-
scribed by Head (1982), using conventional laboratory
equipment
without modifications. As typically shown in Figure 2(a),
after
applying the confining pressure for the first stage (100 kPa),
a
constant rate of axial strain, equal to 0.05%/min, was
applied
Grout outflow
Pressure sensors
0
1000
2000
3000
4000
0 2 4 6 8
D e v ia t o r s t re s s ,
: k P a
q f : k P a
pf: kPa
compression test and (b) failure envelopes for grouted sand
from
UU and M-UU triaxial compression tests
179
grouted sands
until failure of the specimen was imminent; that is, the
stress–
strain curve was in the curved (plastic) area and approached
the
peak deviator stress value. The decision to terminate the
loading
stage was facilitated by the use of an automatic data
acquisition
system, which provided real-time observation and full control
of
the test progress. Then, the axial load was reduced to zero,
and
the confining pressure for the second stage (200 kPa) was
applied.
The loading and unloading sequence was repeated, the
confining
pressure for the third stage (400 kPa) was applied, and axial
load
was applied until the specimen failed (point of maximum
deviator
stress). The M-UU triaxial compression tests were preferred
to
conventional single-stage UU tests for material economy,
since
the latter would require the preparation of several (at least
three)
identical grouted sand columns and the testing of specimens
with
equal distances from the injection point for the reliable study
of
this parameter.
the past to determine the shear strength parameters of
pulverised
fly ash grouted sands (Markou, 2001). A method for conducting
multi-stage drained triaxial compression tests on weakly ce-
mented sands and estimating the resulting shear strength
para-
meters was proposed recently (Sharma et al., 2011).
However,
this type of test is more satisfactory for plastic soils than
for
brittle soils (Head, 1982). Accordingly, it was necessary
to
document its trustworthiness, by comparing with the results
obtained from conventional UU tests on specimens of identical
composition. For this purpose, grouted sand columns with
proper-
ties unaffected by distance from the injection point were
selected,
and UU tests were conducted on specimens adjacent to the
M-UU specimens. UU triaxial compression tests were
conducted
under confining pressures of 100, 200 and 400 kPa and at a
constant axial strain rate equal to 0.05%/min. Failure was
defined
as the point of maximum deviator stress. Typical stress–
strain
curves of grouted sand from M-UU tests and failure envelopes
( K f -lines) obtained for the same grouted sand
from UU and
M-UU tests (total stresses) are presented in Figure 2. The
shape
of the stress–strain curves obtained from the M-UU test
(Figure
2(a)) indicates that the specimen behaviour during testing
was
normal for tests of this type (Head, 1982). As typically shown
in
Figure 2(b), the Mohr– Coulomb failure criterion represents
adequately the behaviour of the grouted sand, and the two
types
of test give equivalent shear strength parameters. More
specifi-
cally, the comparison of UU and M-UU tests results in three
cases leads to identical values for the angle of internal
friction
and comparable values for cohesion, since the observed
differ-
ences of 5.5, 8.5 and 10.3% between cohesion values were low.
Therefore, the performance of M-UU triaxial compression tests
on cement grouted sand specimens was considered as
practicable,
and the values of the shear strength parameters obtained were
considered as credible.
reported in the literature, the research effort reported herein
was
limited to one-dimensional grout flow (a simplification of
the
actual three-dimensional field conditions) and did not
address
shear strength behaviour of the sands grouted in
saturated
conditions. An idea of the effect of the saturation of sands
prior
to grouting, on the strength of them after cement grouting, can
be
given on the basis of the very limited information reported in
the
literature. From the unconfined compression test results
published
by Schwarz and Krizek (2006), it is evident that the
strength of
initially saturated, microfine cement grouted sands is, on
average,
lower by 15% than the strength of initially dry, grouted
sands.
However, the injection process is adequately simulated on a
laboratory scale, and the results of the present investigation
can
be used for the evaluation of the mechanical behaviour
of
microfine cement grouted sands. Moreover, the M-UU triaxial
compression tests can be particularly useful for the study of
the
effect of the distance from the injection point on the
shear
strength parameters of grouted sands.
4. Strength improvement The effect that grouting has on the
strength of the sands is
presented in Figure 3, in terms of the strength ratio,
S R , a s a
function of the confining pressure used in the tests. The
strength
ratio is defined as the ratio of the maximum deviator stress
(stress
at failure) of the grouted sand, ( 1 3)g, to the
maximum
deviator stress, ( 1 3)s, obtained for the clean sand at
the same
confining pressure. The values of the strength ratio are
always
higher than unity, are often higher than 2 and can be as high as
15,
indicating that the grouted sands have higher strength and, in
many
cases, considerably higher strength than the clean sands.
Signifi-
cant improvement of sand strength after grouting has also
been
reported by several researchers (e.g. Clarke et al.,
1993; Dano et
al., 2004; Krizek et al., 1992). The strength
ratio and, conse-
quently, the positive effect of grouting on the strength of
sands
increases as the confining pressure decreases. This behaviour
is
attributed to the fact that the failure envelopes of the
correspond-
ing clean and grouted sands are, as concluded in the next
section,
approximately parallel, straight lines intersecting the shear
stress
axis at a value equal to zero or equal to cohesion,
respectively.
Accordingly, the difference between the diameters (maximum
deviator stresses) of the two Mohr semicircles, which are
tangent
to the failure envelopes of grouted and clean sand at the
same
confining pressure, increases with decreasing confining
pressure.
The type of cement (Figure 3(a)) appears to have some effect
only at the lower confining pressure applied (100 kPa), with
CEM
I (pure Portland cement) suspension grouted sand yielding a
higher strength ratio value than sand grouted with suspensions
of
the other two cement types containing pozzolans. As shown in
Figure 3(b), strength improvement increased slightly with
increas-
ing cement fineness. Fine-grained suspensions (d max ¼ 10
and
20 m) yielded a range of strength ratios from 1.6 to
2.4 (average
1.9) and from 1.5 t o 2.3 (average 1.8), respectively, while
the
range for coarse-grained suspensions (d max ¼ 100
m) was from
1.4 to 2.1 (average 1.7). The strength ratio ranged from 7.1
to
15.7 (average 11.0), from 1.5 to 2.3 (average 1.8) and from 1.1
to
1.2 (average 1.1) when grouting with suspensions of W/C¼ 1, 2
180
grouted sands
and 3, respectively (Figure 3(c)). Therefore, grouting with
suspen-
sions of W/C¼ 1 resulted in significantly higher strength im-
provement than grouting with suspensions of W/C¼ 2 o r 3
.
Average values of strength ratio equal to 1.82, 1.85, 2.39 and
2.42
were obtained for sands 5–10, 10–14, 14–25 and 25–50, respec-
tively (Figure 3(d)). These values indicate that sand gradation
has
an effect on the strength improvement of the grouted sands,
which
increases with decreasing sand grain size. From all the
aforemen-
tioned observations, it is also evident that the suspension
W/C
ratio affects the strength improvement of the grouted sands
more
drastically than any of the other investigated parameters.
5. Shear strength parameters As typically shown in Figure
2(b), all triaxial compression tests
conducted during this investigation yielded linear failure
envel-
opes ( K f -lines) with exceptionally high
correlation coefficients,
R2, ranging from 0.997 to 1. These results indicate that
the
Mohr–Coulomb failure criterion represents the behaviour of
the
grouted sands adequately, as also observed by other
researchers
(Dano et al., 2004; Krizek et al., 1982,
1986, 1992; Maalej,
2007). Accordingly, the shear strength of the grouted sands
is
quantified in terms of the angle of internal friction, j, and
the
cohesion, c, after total stress analysis. The resulting
friction angle
and cohesion values, obtained from M-UU triaxial compression
tests, are shown in Tables 2 and 3,
respectively, as a function of
the distance of the grouted sand specimens from the injection
point. It can be observed that the distance from the
injection point
had no consistent effect on the shear strength parameter values
of
the grouted sands. However, the differences between the
measured
values and the average value of the shear strength
parameters,
obtained for each grouted sand column, were lower than 4%
for
the angle of internal friction and 12.5% (valid for 80% of
columns) for the cohesion. Therefore, distance from the
injection
point can be considered to have an insignificant effect on
the
1
2
3
4
S t re n g t h
r a t io , S
R
Confining pressure, : kPa (a)
S t re n g t h
r a t io , S
R
Confining pressure, : kPa (b)
S t re n g t h
r a t io , S
R
Confining pressure, : kPa (c)
S t re n g t h
r a t io , S
R
Confining pressure, : kPa (d)
d max µ
Figure 3. Effect of (a) cement type, (b) cement fineness, (c)
grout
W/C ratio and (d) sand gradation on the improvement of sand
strength due to microfine cement grouting
181
grouted sands
values of the shear strength parameters of the grouted sands,
even
at a distance of about 1.2 m from the injection point.
The average values of the angle of internal friction obtained
for
each grouted sand column are shown in Table 2. The values
of
the internal friction angle, based on M-UU triaxial
compression
tests, ranged from 40.78 to 45.78. Although the internal
friction
angles of grouted sands (Table 2) were up to 5.58 higher
than
those of the clean sands (Table 1), the average increase was
considered as low since it was equal to 1.78 or 4%. Due to
the
fact that grouting had a positive, but not pronounced, effect
on
the angle of internal friction of the sands, it was confirmed
that
the improvement of the shear strength of the sands consists
primarily of the development of cohesion and not of an
increase
in the angle of internal friction. This general beneficial effect
of
grouting has also been documented for sodium silicate
solutions
Cement W/C ratio Sand Angle of internal friction, j: o
Differencea
Type d max: m Distance from injection point
Average
value
o %
I 20 2 14–25 – 40.4 41.0 40.7 1.9 4.5
II/B-M 20 2 10–14 43.2 45.0 46.2 44.8 +2.6 +6.2
IV/B 20 2 14–25 43.1 43.8 45.2 44.0 +1.4 +3.3
II/B-M 100 2 10–14 42.5 42.9 42.7 42.7 +0.5 +1.2
II/B-M 10 2 10–14 44.2 44.6 45.8 44.9 +2.7 +6.4
II/B-M 20 1 10–14 – 42.0 40.2 41.1 1.1 2.6
II/B-M 20 3 10–14 44.2 41.3 43.4 43.0 +0.8 +1.9
II/B-M 20 2 5–10 44.7 45.3 47.0 45.7 +5.4 +13.4
II/B-M 20 2 14–25 42.9 44.2 45.4 44.2 +1.6 +3.8
II/B-M 20 2 25–50 44.8 43.9 44.4 44.4 +1.8 +4.2
a Difference between angles of internal friction of grouted and
clean sand.
Table 2. Friction angle values of grouted sands from
multi-stage
unconsolidated–undrained triaxial compression tests
Cement W/C ratio Sand Cohesion, c : kPa Variationa: %
Examined
parameterb
value
I 20 2 14–25 – 455 543 499 +20.5 1
II/B-M 20 2 10–14 245 274 273 264 0.0 (C), 2, 3, 4
IV/B 20 2 14–25 407 454 380 414 0.0 (C), 1
II/B-M 100 2 10–14 187 235 345 256 3.0 2
II/B-M 10 2 10–14 253 309 263 275 +4.2 2
II/B-M 20 1 10–14 – 2421 2907 2664 +909.1 3
II/B-M 20 3 10–14 96 76 148 107 59.5 3
II/B-M 20 2 5–10 210 266 237 238 9.8 4
II/B-M 20 2 14–25 398 433 365 399 3.6/+51.1 1, 4
II/B-M 20 2 25–50 381 416 426 408 +54.5 4
a Relative to the average cohesion value of equivalent control
column. b (C), control column; 1, cement type; 2, cement
d max; 3, W/C ratio; 4, sand gradation.
Table 3. Cohesion values of grouted sands from
multi-stage
unconsolidated–undrained triaxial compression tests
182
grouted sands
(Krizek et al., 1982), microfine cement suspensions
(Dano et al.,
2004; Krizek et al., 1986) and microfine
cement–sodium silicate
mixtures (Krizek et al., 1992).
Also presented in Table 3 are the average cohesion
values of the
grouted sands, obtained for each grouted sand column. The
utilisation of the grouted sand columns in the subsequent
parametric analysis is clarified in the last column
of Table 3, by
referring to the relevant parameters investigated using a
particular
column, and by defining the control columns used to quantify
the
effect of parameter variations. It can be observed that the
cohesion of the grouted sand increased with increasing cement
fineness and with decreasing suspension W/C ratio and sand
grain
size. It can also be observed that grouting with CEM I
suspension
provided higher cohesion than those provided by the other
two
cement types. The superiority of CEM I suspension can be
justified by the composition of the cements, since CEM I is
a
pure Portland cement consisting of a larger proportion of
clinker
in comparison with the other two cement types and does not
contain pozzolanic materials. The observed increase of
cohesion
with decreasing sand grain size was attributed to the
increased
number of grain-to-grain contact points in a finer soil and, as
a
result, to the increased number of points available for
cementa-
tion (Dano et al., 2004; Zebovitz et al.,
1989).
A review of the variations of cohesion values of grouted
sand
columns relative to the cohesion of equivalent control
columns,
presented in Table 3, indicates that the suspension W/C
ratio was
the most important of the investigated parameters, since it
yielded
the largest variations in cohesion values. Grout W/C ratio
was
followed, in order of decreased cohesion variations, by sand
grain
size, cement type and cement fineness. The average cohesion
values of sands grouted with microfine cement suspensions
were
as high as 2664 kPa for W/C ¼ 1, ranged from 238 to 499 kPa
for W/C ¼ 2 and were equal to 107 kPa for W/C¼ 3. The
significant increase of the cohesion of grouted sands with
de-
creasing suspension W/C ratio has also been documented by
other researchers (Dano et al., 2004;
Krizek et al., 1992). The
very small effect of cement fineness on grouted sand cohesion
is
also attributed to the relatively high suspension W/C ratio
(W/C¼ 2) used in the injections. Using suspensions of the
same
cements, Pantazopoulos and Atmatzidis (2011) observed
that
grouting with microfine cements of W/C¼ 1 provides, in
general,
double the cohesion provided by ordinary cements.
6. Shear strength development It has been documented in the
literature that the cohesion and the
angle of internal friction of grouted sands are functions of
the
axial strain and that the sum of their contribution to
shear
strength is maximum at failure (Krizek et al., 1982,
1986). For
saturated cohesive soils, the development of shear strength
with
axial strain can be quantified, and the effective shear
strength
parameters can be evaluated as functions of axial strain
(Schmert-
mann and Osterberg, 1960). The application of this principle
in
the investigation reported herein is based solely on the results
of
UU triaxial compression tests, analysed in terms of total
stresses.
Although, as pointed out earlier, M-UU tests result in
trustworthy
values of stresses and shear strength parameters for cement
grouted sands, they may lead to questionable values of axial
strain because, as is typically shown in Figure 2(a): (a) a
residual
axial strain exists at the end of the first and second loading
stages
and (b) the axial strain at failure can be determined
accurately
only for the third (last) loading stage. Consequently, the results
of
the M-UU tests were not utilised herein for quantifying the
shear
strength development of microfine cement grouted sands.
Based on the stress–strain curves obtained from UU tests
(Figure
4), it can be observed that the deformation at failure (point
of
maximum deviator stress), f , of 14–25 sand grouted
with
microfine cement suspension of W/C¼ 2, increased with
increas-
ing confining pressure. More specifically, the average strain
at
failure of the grouted sand was equal to 2.5, 3.8 and 4.8%
for
tests conducted with confining pressures equal to 100, 200
and
400 kPa, respectively. The strain at failure of the clean sand
was
significantly higher and presented similar behaviour, as it
was
equal to 5.7, 6.4 and 9.3% for confining pressures equal to
100,
200 and 400 kPa, respectively. This means that the three
speci-
mens of grouted or clean sand, tested under different
confining
pressures, were in different states of strength development
for
each specific strain value. For this reason, the shear
strength
parameters of grouted sand were determined for specific
percen-
tages of failure strain of each specimen. Selected percentages
of
failure strain are shown on the stress–strain curves
of Figure 4. It
is evident that, for each one of these percentages, all
specimens
were in the same state of strength development, regardless of
the
confining pressures and that percentage equal to 100% corre-
sponds to the failure strain of each specimen.
0
1000
2000
3000
4000
0 2 4 6 8
D e v ia t o r s t re s s ,
: k P a
grouted sand at various failure strain percentages
183
grouted sands
The methodology for the quantification of shear strength
develop-
ment was applied to the grouted sand by determining, for all
UU
tests, the deviator stresses corresponding to each percentage
of
failure strain, plotting the resulting p – q
envelopes ( K -lines), as
shown in Figure 5(a) for all percentages of failure
strain, and
evaluating the shear strength parameters, as presented in
Figure
6, as functions of the percentage of failure strain. Both
cohesion
and angle of internal friction exhibit a high rate of
increase
during the initial stages of axial loading. Cohesion (Figure
6(a))
attains a maximum value for an axial strain ranging between
20
and 30% of the failure strain. This point also corresponds to
the
transition of the stress–strain curves from the initial linear part
to
the curved (plastic) area, as shown in Figure 4. The
maximum
cohesion value, which is 35% higher than the cohesion
obtained
at failure, decreases, thereafter, at a progressively decreasing
rate
until failure (point of maximum deviator stress). The angle
of
internal friction (Figure 6(b)) attains a value approximately
equal
to 90% of the value obtained at failure, for an axial strain
corresponding to 40% of the failure strain and increases,
there-
after, at a lower rate until failure. These observations are in
good
agreement with the behaviour observed for sands grouted with
sodium silicate solutions (Krizek et al., 1982) or
microfine
cement suspensions (Krizek et al., 1986). More
specifically, it has
been reported that cohesion increases rapidly, reaches a
maximum
value at low strain levels, then decreases and maintains a
constant
value until failure; the angle of internal friction increases
gradually as axial strain increases and becomes maximum at
failure.
Application of this methodology to the data obtained from UU
tests conducted on clean sand specimens, yielded the
p – q
envelopes ( K -lines) shown in Figure 5(b). These
envelopes were
plotted using stress values for the clean sand corresponding
to the
strain percentages used for grouted sand. In this manner, the
development of the internal friction angle of the clean sand
was
quantified at the same compression levels as for grouted
sand,
0
500
1000
1500
2000
q
(a)
0
500
1000
30%
5%
Figure 5. K -lines for (a) microfine cement grouted sand
and
(b) clean 14–25 sand at various failure strain percentages
0
100
200
300
400
500
C o h e s io n ,
: k P a
a n g le ,
Clean 14 25 sand
Grouted 14 25 sand
Failure of grouted sand
Failure of clean sand
Figure 6. Development of (a) cohesion and (b) angle of
internal
friction of microfine cement grouted sand as a function of
failure
strain percentage
grouted sands
internal friction angle development of clean and grouted sand
are
compared in Figure 6(b). It can be observed that the angle
of
internal friction of the clean sand increases rapidly up to an
axial
strain approximately equal to 25% of the failure strain of
the
grouted sand, and continues to increase at a substantially
reduced
rate, until failure. A very similar behaviour has been observed
for
other clean sands (Krizek et al., 1982). It can also be
observed
that at the failure point of the grouted sand (failure strain
percentage¼ 100%), the internal friction angle of the clean
sand
reaches 95% of its maximum (failure) value, attained at
consider-
ably higher axial strains, and that the grouted sand exhibits
the
same form of internal friction angle development and system-
atically higher values than the clean sand, for axial strains up
to
the failure strain of the grouted sand. Grouting is most
effective
when the sand voids are filled with solidified grout
material,
which also adheres to the surfaces of the sand grains. Apart
from
providing cohesion to the grouted sand, the combined effect
of
cementation and void filling restricts the relative movement
between sand grains during shear, and is quantified as an
increase
in the value of the angle of internal friction.
The aforementioned quantitative and qualitative observations
indicate that there is a sequence of axial strain ranges
where
distinct behavioural patterns are exhibited by the microfine
cement grouted sands: (a) as shown in Figure 6(a), for axial
strain
values between 20 and 30% of the failure strain, the cohesion
reaches a peak value that is 35% higher than the value at
failure,
(b) for axial strains over 20 to 30% and up to 60 to 70% of
the
failure strain, it is postulated that a breakdown of bonds
between
sand grains and grout occurs, followed by a decrease of the
cohesion values and (c) beyond an axial strain of
approximately
60 to 70% of the failure strain, both cohesion and angle
of
internal friction vary at a very low rate, and the grouted
sand
appears to behave as very dense sand with voids filled by
another
fine-grained material.
7. Conclusions Based on the results obtained and the observations
made during
this laboratory investigation and within the limitations of
the
range of parameters investigated, the following conclusions
may
be made.
(a) Multi-stage UU triaxial compression tests on specimens
obtained from a single grouted sand column can be utilised to
determine the shear strength parameters of the grouted sands
and to quantify the effect of distance from the injection
point.
(b) Grouting with microfine cements, produced by pulverising
ordinary cements, improves the shear strength of sands
significantly, even at a distance of about 1.2 m from the
injection point. Grouting is most effective when thick cement
suspensions (stable, W/C¼ 1) are injected, when pure
Portland cement suspensions (no pozzolan) are used and
when finer sands are grouted.
(c) The Mohr– Coulomb failure criterion represents the
behaviour
of microfine cement grouted sands that obtain cohesion values
ranging from 240 to 500 kPa for W/C¼ 2 and reach 2650 kPa
for W/C ¼ 1 and angle of internal friction values higher by
up
to 5.58 compared to that of the clean sands.
(d ) The activated cohesion of the grouted sands reaches
a
maximum value for an axial strain of about 25% of the
failure strain and decreases thereafter, until failure.
(e) The activated angle of internal friction of the grouted
sands
increases with increasing axial strain, as for clean sands,
but
it attains higher values than clean sand, possibly due to the
restriction of the relative movement between sand grains
during shear, caused by the cementation and void filling
effect of grouting.
Acknowledgements The research effort reported herein is part of the
research project
PENED-03ED527 that was co-financed by the EU–European
Social Fund (75%) and the Greek Ministry of
Development–
GSRT (25%). The contribution of TITAN Cement Company S.A.
was substantial for the selection, chemical analysis,
pulverisation
and grain size analysis of the cements.
REFERENCES
Bruce DA, Littlejohn S and Naudts CA (1997) Grouting
materials
for ground treatment: a practitioner’s guide. Proceedings
of
Conference on Grouting: Compaction, Remediation,
Testing
(Vipulanandan C (ed.)). ASCE, New York, pp. 306–334.
BSI (2000) EN 197-1:2000 Cement – Part 1: Composition,
specifications and conformity criteria for common cements.
BSI, London, UK.
works – grouting. BSI, London, UK.
Clarke WJ, Boyd MD and Helal M (1993) Ultrafine cement
tests
and drilling Warm Spring dam. Proceedings of Specialty
Conference on Geotechnical Practice in Dam Rehabilitation
(Anderson LR (ed.)). ASCE, New York, pp. 718–732.
Dano C, Hicher PY and Tailliez S (2004) Engineering properties
of
grouted sands. Journal of Geotechnical and
Geoenvironmental Engineering ASCE 130(3): 328–338.
Eriksson M, Friedrich M and Vorschulze C (2003) Variations
in
the rheology and penetrability of cement-based grouts – an
experimental study. Cement and Concrete Research
34(7):
1111–1119.
Head KH (1982) Manual of Soil Laboratory Testing ,
vol. 2.
Pentech Press, London, UK.
Henn RW and Soule NC (2010) Ultrafine Cement in
Pressure
Grouting . ASCE Press, Reston, VA, USA.
Hicher PY, Dano C and Chang CS (2008) Multi-scale modelling
of
the mechanical behaviour of grouted sand. Studia
Geotechnica et Mechanica XXX(1–2): 83– 94.
Krizek RJ, Benltayf MA and Atmatzidis DK (1982)
Effective
stress – strain – strength behavior of silicate-grouted sand.
Proceedings of Conference on Grouting in
Geotechnical
Engineering (Baker WH (ed.)). ASCE, New York, USA,
vol.
1, pp. 482– 497.
grouted sands
Krizek RJ, Atmatzidis DK and Wu ZH (1986) Behavior of
Grouted
Erksak Sand . Northwestern University, Department of
Civil
Engineering, Evanston, IL, USA.
Krizek RJ, Liao HJ and Borden RH (1992) Mechanical
properties
of microfine cement/sodium silicate grouted sand.
Proceedings of Conference on Grouting, Soil
Improvement
and Geosynthetics (Borden RH, Holtz RD and Juran I
(eds)).
ASCE, New York, vol. 1, pp. 688–699.
Littlejohn GS (1982) Design of cement based grouts.
Proceedings
of Conference on Grouting in Geotechnical Engineering
(Baker WH (ed.)). ASCE, New York, USA, vol. 1, pp. 35 –48.
Lombardi G (2003) Grouting of rock masses. Proceedings of
the
3rd International Conference on Grouting and Ground
Treatment, New Orleans. ASCE, Reston, USA, vol. 1,
pp. 164– 197.
Maalej Y (2007) Comportement Me canique d’un Milieu
Granulaire
Injecte par un Coulis de Ciment: Etude Expe rimentale
et
Mode lisation Microme canique. These de Doctorat,
Ecole
Nationale des Ponts et Chaussees, Paris, France.
Maalej Y, Dupla J-C, Canou J, Maalej Y and Dormieux
L (2007)
Caracteristiques de deformabilite d’un sable injecte par un
coulis de micro ciment. Proceedings of the 14th
European
Conference on Soil Mechanics and Geotechnical
Engineering, Madrid . Millpress, Rotterdam, the
Netherlands,
vol. 3, pp. 1361–1365.
Markou IN (2001) Long term behavior of a pulverized fly
ash
grouted sand. Proceedings of the 15th
International
Conference on Soil Mechanics and Geotechnical
Engineering, Istanbul . Balkema, Lisse, the
Netherlands,
vol. 2, pp. 1529–1532.
Naeini SA and Ziaie-Moayed R (2003) Undrained shear
strength
and liquefaction potential of loose silty sand treated with
microfine cement. Proceedings of the 13th European
Conference on Soil Mechanics and Geotechnical
Engineering, Prague, vol. 1, pp. 849– 854.
Pantazopoulos IA and Atmatzidis DK (2011) Mechanical
behavior of microfine cement grouted sands. Proceedings
of
the 15th European Conference on Soil Mechanics and
Geotechnical Engineering, Athens. IOS Press, Amsterdam,
the Netherlands, vol. 1, pp. 241–246.
Pantazopoulos IA, Markou IN, Christodoulou DN et al.
(2012)
Development of microfine cement grouts by pulverizing
ordinary cements. Cement and Concrete
Composites 34(5):
593–603.
study of the development of cohesion and friction with axial
strain in saturated cohesive soils. Proceedings of
Research
Conference on Shear Strength of Cohesive Soils,
Boulder .
ASCE, New York, USA, pp. 643–694.
Schwarz LG and Krizek RJ (2006) Hydrocarbon residuals
and
containment in microfine cement grouted sand. Journal
of
Materials in Civil Engineering ASCE 18(2):
214–228.
Sharma MSR, Baxter CDP, Moran K, Vaziri H and
Narayanasamy R (2011) Strength of weakly
cemented
sands from drained multistage triaxial tests. Journal
of
Geotechnical and Geoenvironmental Engineering ASCE
137(12): 1202–1210.
Zebovitz S, Krizek RJ and Atmatzidis DK (1989) Injection of
fine
sands with very fine cement grout. Journal of
Geotechnical
Engineering ASCE 115(12): 1717– 1733.
WHAT DO YOU THINK?
To discuss this paper, please email up to 500 words to the
editor at
[email protected]. Your contribution will be
forwarded to the author(s) for a reply and, if considered
appropriate by the editorial panel, will be published as a
discussion in a future issue of the journal.
Proceedings journals rely entirely on contributions sent
in
by civil engineering professionals, academics and students.
Papers should be 2000–5000 words long (briefing papers
should be 1000–2000 words long), with adequate illustra-
tions and references. You can submit your paper online via
www.icevirtuallibrary.com/content/journals, where you
186
grouted sands