The durable, contemporary timber solution. Internal · Architect: Javier Martínez Oroquieta Parklex 500, Walnut Parklex 2000, Walnut Thermae Bath Spa The Minerva Bath. Bath, United

InternalThe durable, contemporary timbersolution.

Cover photo:

Guipuzcoan Football Federation

Project: Izaskun Larzábal

Photography: Susana Aréchaga and Luis M. Ambrós

Parklex 2000, Eucalyptus

The natural wood used to manufacture Parklex providesa look of quality and comfort for building interiors fromthe very first moment.

With Parklex, ceilings, walls and floors, in addition toany other surface, such as counter tops, bathroomsand even showers take on a new leading role.

If you’re looking for quality and comfort, Parklex has awide range of natural wood finishes that achieve bothpurposes. In addition, its variety of finishes allowsdecorators and architects to be creative with combinationson any type of surface, allowing them to decorate thefloors, walls or ceiling in the same wood, providing thedegree of quality and comfort that only natural, high-quality materials can convey.

Indoor woodcoverings.

Floor,walls andceiling.

The same colors andfinishes throughout theinterior.

Parklex paneling may be installed on any surface:floors, walls and ceilings, combining aesthetic elementsor keeping the same colors and finishes throughoutthe interior, converting rooms into authentic enclosures,completely lined with natural wood panels.

Floors:20003000

·

Walls and ceiling:Dry areas:

500Damp areas:

700

·

Recommended products:

Quality atyour feet.

It demonstrates itsquality where it suffersthe most wear.

The quality of Parklex comes from the materials andprocesses used to manufacture them. This quality isdemonstrated precisely where the product suffers themost wear: floors, transit spaces and areas of intensiveuse, where any material suffers a high level of wear.Parklex, however, performs at top levels in these areas,with its properties remaining unchanged. Simplemaintenance is all that is needed to prolong the life ofthese coverings, which makes them immediatelyeconomical.

Floors:20003000

·Recommended products:

Silence:another formof comfort.

Coverings for locationswith high acoustic ab-sorption requirements.

Noise and reverberation prevention is also a form ofcomfort. Parklex 500 is designed to be installed as anindoor wall and ceiling covering in locations with highacoustic absorption requirements: conference halls,presentation rooms, auditoriums, offices, etc., as wellas furniture coverings.These panels insulate rooms from outside noise or thatof nearby areas, providing an even greater feeling ofcomfort.

Walls and ceiling:500

·Recommended products:

Excellent firebehavior. Parklexmeans peace ofmind.

Natural wood with thebest results for reactionto fire.

In addition to being manufactured from natural wood,the entire Parklex line is tested according to the newEuropean standard EN 13.501 regarding reaction tofire, obtaining the best results possible for organicmaterials.With Parklex, you are sure to make the right decision.

Floors:2000

·

Walls and ceiling:Dry areas:

500Damp areas:

700

·


Bathrooms,gymnasiums, spasor pools: don’trelinquish comfort.

Cozy, moisture resistantspaces.

Moisture is a factor that generally determines the materialsused in bathrooms. Thanks to the production and treatmentprocesses Parklex uses on natural wood, it is now possibleto use Parklex coverings in any area of the bathroom,even in the shower, transforming them into areas that arejust as inviting as the rest of the interior.The Parklex line stands out for its moisture resistance,which also allows its problem-free use in gymnasiums,spas or pools, making these areas (and any other spacewhere appearance, hygiene, resistance and cleanlinessare important) exclusive places that are both pleasant andtotally unique.

Floors (bathrooms andgymnasiums):

2000

·


Walls and ceiling:Damp areas:

700

·

ParklexProjects

Bilbao, May 14, 2007

Dear Sirs:

After ten years of intensive use, withs-

tanding the regular heavy machinery

traffic and the exposition of sculptures

weighing many tons, we would like to

express our satisfaction with the wood

floors in the Guggenheim Museum ga-

lleries (Manufacturer: Composites Gu-

rea, model Parklex 2000, lightened

ash), with regards to both the ease of

cleaning

and their durability and strength.

Rogelio Diez

Maintenance and Installations Supervisor

GuggenheimBilbaoBilbao, Spain.

Architect: Frank O. Gehry

Project manager: César Caicoya

Parklex 2000, Museum Ash

Bilbao, 14 de mayo de 2007

Estimados Señores:

Tras diez años de funcionamiento intensivo de los suelosde madera en las Galerías del Museo Guggenheim(Fabricante Composites Gurea, modelo Parklex 2000,fresno clarificado), soportando el paso habitual demaquinaria pesada y la exposición de esculturas de grantonelaje, comunicamos nuestra satisfacción con losmismos, tanto en su facilidad de limpieza como en sudurabilidad y resistencia.

NavarranGovernmentPress RoomPamplona, Spain.

Architects: Javier Barcos Berruezo

and Manolo Enríquez Jiménez

Parklex 500, Walnut

Parklex 2000, Walnut

Marqués de RiscalHotelThe Luxury Collection.

Alava, Spain.

Architect: Frank O. Gehry

Project manager: César Caicoya

Parklex 500, Maple

Parklex 2000, Maple

Cepa 21 WineriesValladolid, Spain.

Architects: BSA Arquitectos

Interior design: TGA+Asociados

and Javier Machimbarrena

Parklex 500, Maple

Burlada CulturalCenterNavarre, Spain.

Architect: Miguel Ayate Bariain

Parklex 500

Puerta de AmericaHotelMadrid, Spain.

Architect: Jean Nouvel

Parklex 2000

Zubieta XXI SportsComplexGuipuzcoa, Spain.

Project: Izaskun Larzábal, FernandoGárate and Agustín Oteiza

Photography: Susana Aréchaga

and Luis M. Ambrós

Parklex 2000, Natural Beech

De la Peña StationBilbao, Spain.

Architect: GPD Studio

Parklex 500

La Perla HotelPamplona, Spain.

Architect: Javier Martínez Oroquieta

Parklex 500, Walnut


Thermae Bath SpaThe Minerva Bath.

Bath, United Kingdom.

Architect: Nicholas Grimshaw & Partners

Photography: Matt Cardy

Parklex 700, Maple

GuipuzcoanFootballFederationGuipuzcoa, Spain.

Project: Izaskun Larzábal


and Luis M. Ambrós

Parklex 2000, Eucalyptus

Attic in SanSebastianGuipuzcoa, Spain.

Interior design: Verónica Conejos

Parklex 2000, Museum Ash

COEC, CatalonianOdontologist andStomatologistAssociationBarcelona, Spain.

Architect: Pere Fosch i Alvarez

Parklex 3000, Maple

Beroa BarGuipuzcoa, Spain.

Design: Formak Studio

Parklex 2000 (floor)

Parklex 3000, Zebrano (bar)

Home inPamplonaNavarre, Spain.

Interior design: Héctor Elizaga


and Luis M. Ambrós

Parklex 2000, Maple

Air France, VIPLoungeNarita International Airport.

Tokyo, Japan.

Architect: Noé Duchaufour-Lawrance

Parklex 500, Reconstituted Oak

Parklex 2000, Reconstituted Oak

Electronics ArtsLondon, United Kingdom.

Architect: Foster + Partners

Photography: Nigel Young

Parklex 2000, Natural Beech

Amrey HotelBarcelona, Spain.

Architect: Ramón Domenech

Parklex 2000, Maple

Home in SanSebastianGuipuzcoa, Spain.

Interior design: Javier Machimbarrena


and Luis M. Ambrós


Home in PuertoPollençaMajorca, Spain.

Architect: Joan Riusech


and Luis M. Ambrós

Parklex 2000, Maple

Technicalcharacteristics

Rigorous testing guarantees Parklex’s excellent performance.

Guarantees / Quality Certificates

About Parklex

Perfect adaptation to the project design is an essential requi-rement. That’s why the technology used to manufacture Parklexallows us to apply different finishes, all in natural wood, tointegrate them completely into the environment that is requiredfor each project.

Finishes

The variety of finishes and colors in natural and dyed panelssets Parklex apart as a result of its versatility, making it theideal covering from any type of project.

Range

Providing service on an international level has meant establi-shing an extensive network of Parklex distributors on all fivecontinents. This allows us to work more closely with our clientsand offer them better service in a way that is more accessibleto them. It also lets us understand their needs perfectly andfirst hand.

International

The best architects in the world use Parklex in their mostemblematic creations. Why is this so? Because they feelcomfortable and at ease, and because the results do notdisappoint them. Without a doubt, it is because at Parklex wehave been working for over 15 years on a daily basis witharchitects from all over the world, including, for example,Santiago Calatrava, Frank Gehry, Norman Foster, Jean Nouveland Nicholas Grimshaw, adapting our range to their require-ments. This has made Parklex the natural wood covering ofchoice in many of the best quality and best-known projects inthe world.This can only be achieved by a brand with an absoluteguarantee, capable of offering the perfect product, totallyadapted to their needs, with problem-free application.

Architects

The surface is always made from 100% natural wood, treatedaccording to its application: to resist special weather conditionsor to perfectly resist the intensive use it might receive ininteriors.

Natural wood

Each type of Parklex is subjected to a different productionprocess, depending on its final application: interiors, exteriors,damp areas, etc.The base is always high-density laminated wood with a paperfiber core that has been treated with thermosetting resins andcompressed at high pressure and temperature.

Production process

Parklex – The ideal solution

Characteristics

Quality and performance are only the most visible resultsof Parklex. As if this weren’t enough, the advantagesoffered by Parklex are evident from the momentit is installed, up to its long-term maintenance.

Strength.Material for intensive use indoor areas is made with the highestquality natural wood panels that have been impregnated usingthe Gureprex system, which provides a series of benefits withregards to abrasion, moisture resistance, hardness, scratchresistance and dimensional stability that are far superior toany of the varnish-treated products currently found on themarket.

Quality.Parklex means quality. All our products have earned the CEmark and carry an absolute guarantee. Exterior panels aremanufactured according to the European standard EN 438,which applies to HPL (high pressure laminates). This is whyParklex is the covering preferred by the world’s most prestigiousarchitects.

Moisture resistance.The technology used by Parklex to manufacture the exteriorcoverings completely guarantees them against extreme weatherconditions: rain, sun, humidity and heat. This same technologyallows us to provide a material for interiors with identicalresistance properties. Parklex therefore provides the idealproduct for damp areas.

Fire behavior.The entire Parklex line is classified according to the newEuropean standard EN 13.501-1:2002 regarding reaction tofire, obtaining the best results possible for organic materials.

Ease of installation.The floating flooring system is simple and low-cost. The restof the products may be easily installed, following clear, pro-fessional instructions.

Maintenance.Parklex does not require any sort of scraping or varnishingas part of its maintenance. It need only be lightly cleansedwith a mop, using liquid ph-neutral soap and water.

Service.Parklex has a technical support department to answer anyquestions regarding product assembly and to give advice onthe most appropriate type of covering to meet every need.

Acoustic absorption.Parklex 500 and Parklex 700 may be perforated, making themthe ideal materials for acoustic absorption. They have beenmanufactured specifically for interiors where the acousticfactor is important.

External

High-density stratified timberpanels for external use.

700

Natural timber ceiling and wallfinishes.

500

Natural timber finish for fullaccess raised floors.

3000

Stratified timber panels for in-ternal use, with high resistanceto humidity.

Natural timber floor for ex-treme wear environments.

2000

Internal

Floors

Walls andceilings

Damp areas

Dry areas

Floatingparquet

Raisedflooring

Façades Facade

Parklex product guide

Panel construction

HPL core

Moisture resistant overlay

Natural timber veneer

HPL core


Balancing film

Parklex is manufactured from fine timber veneers, therefore the colour and grain of different batches will exhibit natural variations. Due to the limitations ofprinted media, the finishes printed in this catalogue are merely an approximation of their real color. For this reason, before placing any order, Parklexrecommends consulting our sales personnel to request actual samples.

Woodskin®. A finish that allows you to

feel the grain and subtlety of natural

timber.

Smooth. Traditional Parklex finish.

Reveals the simple, natural beauty of the

wood it is manufactured with.

Surface characteristics

Smooth Rubber

Special finishes

Chequerplate Rubber PerforatedChequerplate (3)

(1) Panels manufactured from joined timber

veneers. There may be as many as 12 veneer

pieces in each full panel (16 in the case of

stained finishes).

Stratified timber panels for internal use,with high resistance to humidity.

Parklex 700 is a high-density stratified natural timber panel,made from kraft paper that has been treated with thermosetresins compressed under high pressures and temperatures,finished with natural timber veneers.

Assembly systems *

Exposed fastening. The Parklex panels

are fastened with stainless steel screws

or rivets to the treated wood or metal

substructure.

Hidden fastening, with special hanging

profiles. The Parklex panels are attached

to the aluminum substructure, using guide

profiles and hanging pins.

Hidden fastening, using adhesive. The

Parklex panels are fastened using adhe-

sive to the treated wood or metal subs-

tructure.

Hidden fastening, with caps. The Parklex

panels are attached with screws hidden

by caps with a diameter of 10,75mm and

a section of 2mm, using the same material

and finish as the panel.

For more information on installation, consult the Internal Parklex Assembly Catalogue

or our web page (www.parklex.com).

*

(2) Available only in a Smooth surface finish.

700

Finish range

Ayous NaturalAmbar (2) Antra (2)

Natural Zebrano (1)

Onix (2)Walnut (1)Maple (1)Green Beech (1)Natural Beech (1)Gold (2) Grey Beech (1)

Black

Quartz (2)

Wengue (1)Natural Oak (1) Reconstituted Oak (1) Sapelli (1)Rubi (2) Silver (2)

Cherry (1) Eucalyptus (1)Copper (2) Museum Ash (1)

Technical characteristics

Tests Stand Property or attribute Measurement unit

1. Inspection Rev: 03 (09.2009) Rev: 03 (09.2009)

Colour, pattern and surface finish EN 438-8 Part 5.2.2.3

Thickness (t) EN 438-2 Part 5 6,0 ≤ t < 8,0 mm

8,0 ≤ t < 12,0

12,0 ≤ t < 16,0

16,0 ≤ t < 20,0

20,0 ≤ t < 25,0

Length and width EN 438-2 Part 6 – mm

Edge straightness EN 438-2 Part 7 – mm/m

Edge squareness EN 438-2 Part 8 – mm/m

3. Physical properties

Dimensional stability at elevated temperatures EN 438.-2 Part 17 Cumulative dimensional change(t≥6_mm)

% max Longrain

% max Crossgrain

Resistance to impact with large diameter ball EN 438-2 Part 21 mm

Tensile strength EN ISO 527-2 Longrain

Crossgrain

Water vapour permeability EN 438-7 Part 4.4 Wet cup method µ

Dry cup method

Resistance to fixings EN 438-7 Part 4.5 Screw holding value t ≥ 6_mm N

FScrew holding value t ≥ 8_mm

Screw holding value t ≥ 10_mm

Release of formaldehyde EN 438-7 Part 4.11 Classification Rating

Flexural strength EN ISO 178 Longrain MPa

Crossgrain

Flexural Modulus EN ISO 178 Longrain MPa

Crossgrain

Resistance to inmersion in boiling water EN 438-2 Part 12 Moisture absorbed % ² 2 ² 3

Moisture absorbed % ≤ 2 ≤ 6

Appear Degree

Density EN ISO 1.183 Density g/cm3

Reaction to fire EN 13.501-1 Euroclass t ≥ 6_mm Classification C-s2,d0 B-s2,d0

Length (grain direction) x width 2440 x 1220 mm Thickness* - Smooth finish

Thickness* - Chequerplate finish

Panel dimensions

10, 12,14, 18 & 22 mm

* 3 and 6 mm can only be used for special applications. Other thicknesses may be available upon request.

3, 6, 8, 10, 12,14, 18 & 22 mm

Parklex 700 CGS(Standard)

Parklex 700 CGF(Fire Class)

Thickness ³ 6mm

Maximum height for which no visible surfacecracking or imprint greater than 10mm(t≥ 6mm)

4. CE Safety requirements

2. Dimensional tolerances

Due to the fact that wood is a natural product, each veneer may be considered as unique. Colour and structure differencesare considered as normal. Singularities such as knots and resin inclusions are not considered as defects, but as a part of thedécor. There are differences in light fastness performances depending on the wood species and the source of the wood.

1,5

1,5

+10 / - 0

MPa

± 0,40

± 0,60

± 0,50

≥ 60

≥ 1.800

0,3

0,6

± 0,80

± 0,70

≥ 1,35

≥ 80

≥ 9.000

≥ 9.000

5. CE Safety requirements - Reaction to fire

Result

> 2.000

> 3.000

> 4.000

≥ 80

E1

250

110

≥ 4

Assembly systems *

Exposed fastening. The Parklex panels

are fastened with stainless steel screws

or rivets to the treated wood or metal

substructure.

Hidden fastening, with special hanging

profiles. The Parklex panels are attached

to the aluminum substructure, using guide

profiles and hanging pins.


Parklex panels are fastened using adhe-

sive to the treated wood or metal subs-

tructure.

Hidden fastening, with caps. The Parklex

panels are attached with screws hidden

by caps with a diameter of 10,75mm and

a section of 2mm, using the same material

and finish as the panel.



*

Acoustics

Parklex 500 acoustic is designed for

interior wall and ceiling finishes requiring

high levels of acoustic absorption.

It is machined in different forms and

dimensions allowing for the desired level

of acoustic performance.

Slots Perforated

Woodskin®. A finish that allows you to

feel the grain and subtlety of natural

timber.



500

Natural timber ceiling and wall finishes.

Parklex 500 is a timber panel manufactured from 100% naturaltimber fibres, pressed under high temperatures and impreg-nated with thermoset resins using our exclusive Gureprexsystem.




stained finishes).

Panel construction

Gureprex wear resistant overlay


Resin bonded WBP plywood core

HPL balancer

Wood

Finish range

Ayous Natural

Natural Oak (1)Walnut (1)Maple (1)Grey Beech (1) Natural Beech (1) Green Beech (1)

Cherry (1) Eucalyptus (1) Museum Ash (1)AntraAmbar Black

Onix Reconstituted Oak (1)

Sapelli (1) Wengue (1) Natural Zebrano (1)Rubi

Bamboo (1)


Tests Standard Property or attribute Measurement unit

1. Inspection requirements Rev: 03 (09.2009) Rev: 03 (09.2009)


Thickness (t) EN 438-2 Part 5 t = 6,0 mm +1,0 / -0,6

t = 8,0 +1,6 / -1 +1,0 / -0,7

t = 11,0 +1,4 / -1,1 +1,2 / -0,8

t = 14,0 +1,6 / -1,1 +1,3 / -0,9

t = 17,0 +1,3 / -1,3 +1,4 / -1,0

t = 20,0 +1,3 / -1,1 +1,6 / -1,2

t = 40,0 +2,0 / -1,6

Tolerance for thickness variations inside a panel EN 315:1993 t (nominal thickness) mm

Length and width EN 438-2 Part 6 – mm

Edge straightness EN 438-2 Part 7 – mm/m

Edge squareness EN 438-2 Part 8 – mm/m


Revolutions

Initial wear point

Wear resistance

Resistance to inmersion in boiling water EN 438-2 Part 12 Aspect Rating

Resistance to scratching EN 438-2 Part 25 Force Rating

Longitudinal direction

Transversal direction

Longitudinal direction

Transversal direction

Perpendicular tensile strength ASTM C 297 Adhesion force MPa

Density - Density g/cm3 ≥ 0,75 ≥ 0,80

Resistance to fixings EN 438-7 Part 4.5 Force N/mm ≥ 200 ≥ 130

Bonding strength EN 438-7 Part 4.7 Bond strength MPa ≥ 1,42 ≥ 2,64

Flexural tensile strength EN 438-7 Part 4.8 Bond strength MPa ≥ 1,42 ≥ 2,64

Content of pentachlorophenol EN 438-7 Part 4.10 Content pentachlorophenol ppm

Release of formaldehyde EN 717-2 Release of formaldehyde Rating

Glue-line quality EN 438-7 Part 4.13.3 Expression of results Rating 5 3

Resistance to elevated temperature EN 438-7 Part 4.13.3 Aspect Result

Water resistance EN 438-7 Part 4.13.3 Thickness increase % ≤ 7 ≤ 2,5

Reaction to fire EN 13.501-1 Euroclass t ≥ 8mm Classification D-s3,d0 –

Euroclass t ≥ 14mm Classification – B-s2,d0

Length (grain direction) x width 2440 x 1220 mm Thickness*

Result

Thickness ³ 8mm

Due to the fact that wood is a natural product, each veneer may be considered as unique. Colour and structuredifferences are considered as normal. Singularities such as knots and resin inclusions are not considered asdefects, but as a part of the décor. There are differences in light fastness performances depending on the woodspecies and the source of the wood


Resistance to surface wear EN 438-2 Part 10 Resistance to surface wear

≤0,6

+10 / - 0

1,5

1,5

≥ 50

Lightfastness (xenon arc) EN 438-2 Part27 Contrast Grey scale rating

(A) Maple; Bryna; Ayous Natural; Cherry; Natural Beech; Reconstituted Oak

Flexural strength EN 310 MPa

Flexural modulus EN 310 MPa≥ 7000

≥ 6000


* Other thicknesses may be available upon request.

Parklex 500 VDS(Standard)

Parklex 500 VDF(Fire Class)

≥ 2

≤ 5

E1

No damage

≥ 4

< 4 (A)

≥ 70

Panel dimensions

8, 11, 14, 17, 20 & 26 mm

≥ 60

≥ 150

≥ 4

≥ 2



Resistance to abrasion AC4

Resistance to abrasion

Maintenance. The non-porous nature of

the surface prevents the penetration of

dirt. Parklex 2000 requires no specific

stripping or re-finishing.

Cleaning. Mop with water and (neutral)

gel soap.

Maintenance and cleaning

Matt. A finish that provides a high quality,

comfortable surface appearance that only

authentic natural timber can provide.


2000

Natural timber floor for extreme wearenvironments.

Parklex 2000 is a natural timber floating floor made from thehighest quality veneers, impregnated using our exclusiveGureprex system. This provides extraordinary qualities ofdimensional stability and resistance to both abrasion andhumidity.




stained finishes).

Assembly systems *

Floating parquet. Floating installation of

boards glued tongue-in-groove over a

layer of insulation.

Glued. Installation of tongue-in-groove

boards that are adhered to waterproof

DM, using lines of adhesive.

Parquet over underfloor heating. Installa-

tion as floating parquet over underfloor

heating.



*

Panel construction



Resin bonded WBP plywood core

HPL balancer

Wood

Finish range

Ayous Natural





Bamboo (1)


Thickness ³ 11 mm

Tests Standard Property or attribute Measurement unit Result

1. Inspection requirements Rev: 04 (09.2009)


Gap between pieces EN 13.329 – mm ≤ 0,2

Leap between pieces EN 13.329 – mm ≤ 0,15


≥ AC4

≥ 4.000

Resistance to inmersion in boiling water EN 438-2 Part 12 Aspect Rating ≥ 4

Impact resistance (small diameter ball) EN 438-2 Part 20 Force resort N ≥ 10

Resistance to scratching EN 438-2 Part 25 Force Rating ≥ 3

Rating (Group 1 & 2) ≥ 5

Rating (Group 3) ≥ 4

≥ 4

< 4 (B)

Resistance to cigarettes burn EN 438-2 Part 20 Aspect Rating ≥ 4

Longrain ≥ 70

Crossgrain ≥ 60

Longrain ≥ 7000

Crossgrain ≥ 6000

Density - Density g/cm3 ≥ 0,75

Pentachlorophenol content EN 438-7 Part 4.10 Content pentachlorophenol ppm ≤ 5

Release of formaldehyde EN 717-2 Release of formaldehyde Rating E1

Electric resistance EN 1.081 Vertical resistance M_ 825 (antiestático)

Tendency to accumulation electrostratic charges EN 1.815 Potential difference KV <2

Thermal conductivity EN 12.524 Conductivity W/(m*K) 0,17

Water tightness EN 13.553 Water penetration Classification Watertight

Slide EN 13.893 Dynamic coefficient of friction _ 0,73 (D5)

Slip/skid resistance UNE-ENV 12.633 Slip resistance value USRV(Rd) Clase 1

Reaction to fire EN 13.501-1 Euroclass t ≥ 11mm Classification Bfl-s1

Package measurements

Contents per package 2440 x 188 x 14 mm* 2440 x 290 x 14 mm*

Minimum no. Panels 8 1

m2 3,68 0,71

Kg 40 9,5

Maximum contents per pallet

No. panels 192 84

No. packages 24 –

m2 88,3 59,7

Kg 960 800 800

* Standard thickness 14mm. Other thicknesses may be available upon request.

42

–

60,7

2440 x 590 x 14 mm*

1

1,44

17


Grey scale rating



Flexural strength EN 310 MPa

Flexural modulus EN 310 MPa

Resistance to stain EN 438-2 Part26 Aspect

Lightfastness (xenon arc) EN 438-2 Part27 Contrast

Due to the fact that wood is a natural product, each veneer may be considered as unique. Colour and structuredifferences are considered as normal. Singularities such as knots and resin inclusions are not considered as defects,but as a part of the décor. There are differences in light fastness performances depending on the wood species andthe source of the wood


Parklex 2000 HDS (Standard)

Resistance to surface wear EN 438-2 Part10 Initial point (PI) Revolutions


Matt. A finish that provides a high quality,

comfortable surface appearance that only

authentic natural timber can provide.


3000

Natural timber finish for full access raisedfloors.

Parklex 3000 is a high-density stratified timber panel, impreg-nated using our exclusive Gureprex system. It may be adheredto any type of support material (fibreboard, MDF, fibre cement,galvanised steel etc.) normally used to construct full accessfloors.


Parklex panels are attached to different

types of supports, using adhesive.

Assembly systems *



*




stained finishes).

Panel construction



HPL balancer

Wood

Finish range

Ayous Natural





Bamboo (1)


Thickness 1 mm

Tests Standard Property or attribute Measurement unit Result

1. Inspection requirements Rev: 03 (09.2009)


Thickness (t) EN 438-2 Part 5 t = 1 mm mm ± 0,15

Length and width EN 438-2 Part 6 – mm +10 / - 0

Edge straightness EN 438-2 Part 7 – mm/m 1,5

Edge squareness EN 438-2 Part 8 – mm/m 1,5

Planimetry EN 438-2 Part 9 – mm/m 120


Revolutions 0

Abrasion class AC4

Initial point ≥ 4.000

Resistance to inmersion in boiling water EN 438-2 Part 12 Delamination Pass/ No pass Pass

Longitudinal % max 0,75

Transversal % max 1,25

Impact resistance (small diameter ball) EN 438-2 Part 20 Force ressort N ≥ 10

Resistance to scratching EN 438-2 Part 25 Force Rating ≥ 3

Grupos 1 & 2 ≥ 5

Grupo 3 ≥ 4

≥ 4

< 4 (A)

Resistance to cigarette burns EN 438-2 Part 30 Aspect Rating ≥ 2

Density EN ISO 1.183 Density Classification ≥ 1,1

4. Reaction to fire

Reaction to fire EN 13.501-1 Euroclass Classification D-s2,d0 (B)

610 x 610 mm Thickness 1 mm

2440 x 1220 mm


(B) Composite panels made by a non FIRE RETARDANT HPL adhered to a non fireproof wood substrate.

Lightfastness (xenon arc) EN 438-2 Part27 Contrast Grey scale rating

Due to the fact that wood is a natural product, each veneer may be considered as unique. Colour and structuredifferences are considered as normal. Singularities such as knots and resin inclusions are not considered asdefects, but as a part of the décor. There are differences in light fastness performances depending on thewood species and the source of the wood


Resistance to surface wear EN 438-2 Part 10 Resistance to surface wear

Resistance to stain EN 438-2 Part26 Aspect

Dimensional stability at high temperatures EN 438-2 Part17

Maximum - Length (grain direction) x width

Panel dimensions *

Standard - Length (grain direction) x width

* Special dimensions available for other applications, upon request.

Parklex 3000 HGS

Panel construction

PVDF Antigraffiti overlay


HPL core


Balancing film

HPL core

Everlook

Finish range


High-density stratified timber panels forexternal use.

ExternalFacade

Other Parklex products

NOTE. For more information about this product, consult theExternal Parklex Catalogue, the External Parklex AssemblyCatalogue or our web page (www.parklex.com).

Parklex Facade is a high-density stratified timber panelmanufactured from kraft paper treated with resins thermosetunder high pressure and temperature, finished with naturaltimber veneers highly resistant to UV radiation and atmosphericagents.

Parklex Facade includes Everlook®, a special overlay thatdramatically increases the normal life of the panel, improvingUV resistance and colour stability. It also allows for the de-velopment of new panels with an extensive range of finishes.

Smooth. Traditional Parklex finish.

Reveals the simple, natural beauty of the

wood it is manufactured with.


Ambar Antra Copper Gold Onix Quartz Rubi Silver

1. Semilcos head officeVicenza, Italy.

Architect: Pollini+Smania

2. HospitalKorea.

Architect: Seo hae-cheon

3. Children MuseumIreland.

Architect: Traynor O’Toole

4. Alhambra Information pointsGranada, Spain.

Architect: Francisco Martínez Manso, Rafael

Soler Márquez

Applications

1.

2. 3.

4.

www.parklex.comCOMPOSITES GUREA, S.A.Zalain auzoa, 1331780 Vera de BidasoaNavarra (Spain)

[email protected][t ] +34 948 625 045[f ] +34 948 625 015

EN

/v04

/091

2

3000

2000

500

700

Facade

ER-0370/2003

The durable, contemporary timber solution. Internal · Architect: Javier Martínez Oroquieta Parklex 500, Walnut Parklex 2000, Walnut Thermae Bath Spa The Minerva Bath. Bath, United

Documents