TEST REPORT No. : XMIN180300438CCM Date : May.25, 2018 Page: 1 of 27 CUSTOMER NAME: SHANGHAI KELESI INDUSTRY DEVELOPMENT CO., LTD. ADDRESS: NO.5199, GONGHEXIN ROAD, BAOSHAN DISTRICT, SHANGHAI Sample Name : PURE ACRYLIC SOLID SURFACE Kind of Stone : SOLID SURFACE Place of Origin : SHANDONG, CHINA Manufacturer : SHANDONG KELESI NEW MATERIAL TECHNOLOGY CO., LTD. Model/type : KS003 PURE WHITE Above information and sample(s) was/were submitted and confirmed by the client. SGS, however, assumes no responsibility to verify the accuracy, adequacy and completeness of the sample information provided by client. *********** Test Required : Selected test(s) as requested by applicant SGS Ref. No. : CANMLC1804744501, XMIN1803001763SC, SDHL1803005229FB, KV-18-02411A, GZIN1803011762MR, GZAFN1803003470S001, XMAFN180300138-1, GZIN1805025488MR Date of Receipt : Mar.12, 2018 Testing Start Date : Mar.12, 2018 Testing End Date : May.25, 2018 Test result(s) : For further details, please refer to the following page(s) (Unless otherwise stated the results shown in this test report refer only to the sample(s) tested) ******** To be continued******** Signed for SGS-CSTC Standards Technical Services Co., Ltd. XM Branch Civi Huang Authorized Signatory
27
Embed
TEST REPORT - KELESI · 15 Tensile Modulus ASTM D638-14 10500MPa 16 Tensile Strength ASTM D638-14 42.5MPa 17 Antimicrobial activity test With reference to ASTM G 21-15 0 Grade 18
This document is posted to help you gain knowledge. Please leave a comment to let me know what you think about it! Share it to your friends and learn new things together.
Transcript
TEST REPORT No. : XMIN180300438CCM
Date : May.25, 2018
Page: 1 of 27
CUSTOMER NAME: SHANGHAI KELESI INDUSTRY DEVELOPMENT CO., LTD.
Manufacturer : SHANDONG KELESI NEW MATERIAL TECHNOLOGY CO., LTD.
Model/type : KS003 PURE WHITE
Above information and sample(s) was/were submitted and confirmed by the client. SGS, however, assumes no responsibility to verify the accuracy, adequacy and completeness of the sample information provided by client.
*********** Test Required : Selected test(s) as requested by applicant
Test result(s) : For further details, please refer to the following page(s) (Unless otherwise stated the results shown in this test report refer only to the sample(s) tested)
******** To be continued********
Signed for SGS-CSTC Standards Technical
Services Co., Ltd. XM Branch
Civi Huang Authorized Signatory
TEST REPORT No. : XMIN180300438CCM
Date : May.25, 2018
Page: 2 of 27
Summary of test results:
(Average of results)
No. Test item(s) Test method(s) Test result(s)
1 Absorption by weight
Refer to ASTM C97/C97M-15 0.05%
Density 1750 kg/m3
2 Abrasion resistance Refer to ASTM C241/C241M-
15ε1 32
3 Stain resistance test Refer to ANSI Z124.6-2007
Section 5.2
Total stain resistance value: 52
Maximum individual depth of staining: 0.04mm
4 Cigarette test Refer to ANSI Z124.6-2007
Section 5.4
After test, there were visible stains remains which can be
restorable by clean cheesecloth and water.
5 Heated pan test Refer to ANSI Z124.6-2007
Section 5.6
After test, the sample had no visible blister, crazing, or color
change in the surface.
6 High temperature resistance Refer to NEMA LD-3-2005 No effect
7 Chemical resistance test Refer to ANSI Z124.6-2007
9 Thermomechanical Analyzer Refer to ASTM D696-16 -30℃~ 30℃: 29.08×10-6(1/℃)
10 Surface Burning Characteristics ASTM E84-17 Class A
11 Volatile Organic Compounds SGS In-house method Not Detected
******** To be continued********
TEST REPORT No. : XMIN180300438CCM
Date : May.25, 2018
Page: 3 of 27
No. Test item(s) Test method(s) Test result(s)
12 Barcol Hardness ASTM D2583-13a 58
13 Flexural Test With reference to ASTM D790-17
Procedure A and client’s requirement
Flexural Strength
64.3MPa
Flexural Modulus
9600MPa
14 Rockwell Hardness ASTM D785-08(2015) Procedure A 107L
15 Tensile Modulus ASTM D638-14 10500MPa
16 Tensile Strength ASTM D638-14 42.5MPa
17 Antimicrobial activity test With reference to ASTM G 21-15 0 Grade
18 Assessment of Antimicrobial
activity With reference to ASTM E 2180-07
(Reapproved 2012) 97.2%
19 Izod Notched Impact Strength ASTM D256-10ε1 Method A 18J/m
Note: 1. Thermomechanical Analyzer was carried out by SGS Taiwan Ltd. Material and Engineering Laboratory-Kaohsiung.2. Surface Burning Characteristics was carried out by SGS-CSTC Standards Technical Services Co., Ltd. ShundeBranch.3. Test items 11~19 were carried out by SGS-CSTC Standards Technical Services Co., Ltd. Guangzhou Branch.
******** To be continued********
TEST REPORT No. : XMIN180300438CCM
Date : May.25, 2018
Page: 4 of 27
1. Absorption by weight and density
Test Method:
Refer to ASTM C97/C97M-15 Standard Test Methods for Absorption and Bulk Specific Gravity of Dimension
Stone
Specimens: artificial stone with one face polished, 50mm×50mm×12mm, 5pcs
Test Result:
Specimens identification No. 1 2 3 4 5
Absorption by weight (%) 0.06 0.05 0.03 0.06 0.07
Mean water absorption (%) 0.05
Density (kg/m3) 1752 1747 1752 1751 1748
Mean density (kg/m3) 1750
2. Abrasion resistance
Test Method:
Refer to ASTM C241/C241M-15ε1 Standard Test Method for Abrasion Resistance of Stone Subjected to Foot
Traffic
Specimens: artificial stone with one face polished, 50mm×50mm×12mm, 3pcs
Test Result:
Testing surface: polished
Specimens identification No. 1 2 3
Abrasive hardness 34 32 31
Mean abrasive hardness 32
******** To be continued********
TEST REPORT No. : XMIN180300438CCM
Date : May.25, 2018
Page: 5 of 27
3. Stain resistance test
Test Method:
Refer to ANSI Z124.6-2007 Plastic Sinks - 5.2 Stain resistance test
Specimens: artificial stone with one face polished, 100mm×100mm×12mm, 11pcs
Testing surface: polished
Test Result:
Reagents
Test results
(Covered) (Uncovered)
Individual stain rating
Depth removed
Individual stain rating
Depth removed
Black Crayon 2 / 2 /
Black Liquid Shoe Polish 4 / 4 /
Blue Washable Ink 5 0.02mm 5 0.02mm
Gentian Violet Solution 5 0.04mm 5 0.02mm
Beet Juice 1 / 1 /
Grape Juice 1 / 1 /
Lipstick 1 / 1 /
Hair Dye 1 / 1 /
Iodine solution 5 0.02mm 5 0.02mm
Wet Tea Bag 1 / 1 /
Total stain resistance rating 52
Maximum individual depth of staining
0.04 mm
Note: According to ANSI Z124.6-2007 - 5.2.1.1~5.2.1.5, total stain resistance rating shall be ≤ 64 and maximum
individual depth of staining shall be 0.127mm. Individual stain rating as below:
1- non-staining, removable by tap water (using 20 scrub cycles);2- removable by alcohol or naphtha (using 20 scrub cycles);3- removable by first application of standard scouring powder (using 20 scrub cycles);4- removable by two standard scouring powder scrubbings (using an additional 40 scrub cycles);5- Any specimen with stain remaining after the aforementioned cleanings. Any specimen with stain remaining after
the above cleanings shall be tested to determine the depth of staining. The affected area shall be sanded with600 grit abrasive until the stain is removed. The depth shall be measured.
******** To be continued********
TEST REPORT No. : XMIN180300438CCM
Date : May.25, 2018
Page: 6 of 27
4. Cigarette test
Test Method:
Refer to ANSI Z124.6-2007 Plastic Sinks - 5.4 Cigarette test
Specimens: artificial stone with one face polished, 100mm×100mm×12mm, 3pcs
Testing surface: polished
Test Result:
After test, all the three samples had visible stains which can be restorable by clean cheesecloth and water.
5. Heated pan test
Test Method:
Refer to ANSI Z124.6-2007 Plastic Sinks - 5.6 Heated pan test
Specimens: artificial stone with one face polished, 250mm×250mm×12mm, 2pcs
Testing surface: polished
Temperature: 185°C
Test Result:
After test, the samples had no visible blister, crazing, or color change in the surface.
******** To be continued********
TEST REPORT No. : XMIN180300438CCM
Date : May.25, 2018
Page: 7 of 27
6. High temperature resistance test
Test Method:
Refer to NEMA LD-3-2005 High-Pressure Decorative Laminates - 3.6 High temperature resistance
Specimens: artificial stone, 200mm×200mm×12mm, 2pcs, one face polished
Testing surface: polished
Hot wax method
Test Result:
Specimens identification No. 1 2
Test result(s) No effect No effect
Note: a. No effect – no change in color or surface finish.b. Slight effect – a change in color or surface finish only visible at certain angles or directions.c. Moderate effect – a change in color or surface finish visible from all angles and directions, but does not appreciablyalter the original condition of the specimen.d. Severe effect – a change in color or surface finish which obviously and markedly alters the original condition of thespecimen.
******** To be continued********
TEST REPORT No. : XMIN180300438CCM
Date : May.25, 2018
Page: 8 of 27
7. Chemical resistance test
Test Method:
Refer to ANSI Z124.6-2007 Plastic Sinks - 5.5 Chemical resistance test
Specimens: artificial stone with one face polished, 100mm×100mm×12mm, 15pcs
Note: 1. “Affected”: superficial surface changes which can be removable by sanding with 600 grit sandpaper, any resulting damage shall not impair the serviceability of the unit, and shall be easily repairable to original finish. 2. “Severe damage”: Any resulting damage impairs the serviceability of the unit, and was not easily repairable to originalfinish.
******** To be continued********
TEST REPORT No. : XMIN180300438CCM
Date : May.25, 2018
Page: 9 of 27
8. Test Item: Light Aging Test - Xenon Lamp Exposure
Sample Description: See photo
Test Method: Refer to ANSI Z124.6-2007 section 5.1 & ASTM D2565-99(2008) & ASTM D2244-16 and
Note: ∆E*ab was measured by sphere spectrophotometer under D65 standard light source and with 10° observer. The results exclude specular reflection condition, 8mm aperture.
******** To be continued********
TEST REPORT No. : XMIN180300438CCM
Date : May.25, 2018
Page: 10 of 27
Test photo:
Reference sample Tested samples
Equipment information:
Equipment Model Equipment number Calibration dates Next calibration
date
Xenon Test Chamber Q-Sun Xe-3 HBS XMML-POL-018 2018-01-24 2019-01-23
Sphere Spectrophotometer
SP64 XMML-CON-025 2018-01-03 2019-01-02
******** To be continued********
TEST REPORT No. : XMIN180300438CCM
Date : May.25, 2018
Page: 11 of 27
9. Thermomechanical Analyzer
Test Method:
Refer to ASTM D696-16 Standard Test Method for Coefficient of Linear Thermal Expansion of Plastics
Between −30°C and 30°C with a Vitreous Silica Dilatometer
Test Condition:
Test temperature range :Ramp 10℃/min from -30℃ to 30℃
Purge gas /:Nitrogen (N2), Purity 99.999%, Flow rate 50ml/min.
Probe Type :Expansion
Force /:0.05N
Measurement Direction /:X-Y
Test Result:
Test Item Test Method Test Results
Coefficient of
linear thermal expansion (1/℃)Refer to ASTM D696-16 -30℃ ~ 30℃: 29.08×10-6
******** To be continued********
TEST REPORT No. : XMIN180300438CCM
Date : May.25, 2018
Page: 12 of 27
Test Spectrum:
******** To be continued********
TEST REPORT No. : XMIN180300438CCM
Date : May.25, 2018
Page: 13 of 27
10. Surface Burning Characteristics
Test Conducted:
This test was conducted in accordance with ASTM E84-17 Standard Test Method for Surface Burning
Characteristics of Building Materials
Introduction:
The method, designated as ASTM E84-17, "Standard Method of Test for Surface Burning Characteristics of
Building Materials", is designed to determine the relative surface burning characteristics of materials under
specific test conditions. Results are expressed in terms of flame spread index (FSI) and smoke developed
index (SDI).
The purpose of this test method is to determine the relative burning behavior of the material by observing the
flame spread along the specimen. Flame spread and smoke developed index are reported. However, there
is not necessarily a relationship between these two measurements.
Test Procedure:
The tunnel is preheated to 150°F, as measured by the floor-embedded thermocouple located 23.25 feet
downstream of the burner ports, and allowed to cool to 105°F, as measured by the floor-embedded
thermocouple located 13 feet from the burners. At this time the tunnel lid is raised and the test sample is
placed along the ledges of the tunnel so as to form a continuous ceiling 24 feet long, 12 inches above the
floor. The lid is then lowered into place.
Upon ignition of the gas burners, the flame spread distance is observed and recorded every 15 seconds.
Flame spread distance versus time is plotted ignoring any flame front recessions. If the area under the curve
(A) is less than or equal to 97.5 min·ft, FSI = 0.515·A; if greater, FSI = 4900/(195-A). Smoke developed is
determined by comparing the area under the obscuration curve for the test sample to that of inorganic
reinforced cement board and red oak, arbitrarily established as 0 and 100, respectively.
Sample Description:
Thickness : Approximately 12mm
Exposed face : Smooth face
******** To be continued********
TEST REPORT No. : XMIN180300438CCM
Date : May.25, 2018
Page: 14 of 27
Sample Preparation:
Prior to testing, the specimen was conditioned to constant weight at a temperature of 73 ± 5°F (23 ± 3°C)
and a relative humidity of 50 ± 5%.
The test specimen consisted of a total of 4 sections of material. The sections were butted together during
testing to form the requisite specimen length. The specimen was self-supporting on the ledges of the test
chamber.
Test Results:
Test data and observations: Maximum flame spread (ft): 6.5 Time To Maximum Spread: 581 seconds. Fallout: None Test Duration: 10 minutes. FS*Time area (ft*min): 27.3 Smoke area (%A*min): 3.3 Red oak smoke area (%A*min):
90.8
Summary of results:
Flame-spread Index (FSI)
Smoke-developed Index (SDI)
15 5
Rating:
The National Fire Protection Association Life Safety Code 101, “Interior Wall and Ceiling Finish
Classification”, has a means of classifying materials with respect to Flame Spread and Smoke Developed
when tested in accordance with NFPA 255, (ASTM E84) “Method of Test of Surface Burning Characteristics
of Building Materials”.
The classifications are as follows:
Flame-Spread Index (FSI) Smoke-developed Index(SDI)
Class A 0 - 25 0 - 450
Class B 26 - 75 0 - 450
Class C 76 - 200 0 - 450
Conclusion:
Refer to the National Fire Protection Association Life Safety Code 101, “Interior Wall and Ceiling Finish
Classification”, the submitted sample meets the requirement of Class A.
******** To be continued********
TEST REPORT No. : XMIN180300438CCM
Date : May.25, 2018
Page: 15 of 27
Appendix 1-Graphs:
Graph1. Flame Spread Index
Graph2. Smoke Developed Index ******** To be continued********
TEST REPORT No. : XMIN180300438CCM
Date : May.25, 2018
Page: 16 of 27
Appendix 2-Pictures:
Sample picture
After test ******** To be continued********
TEST REPORT No. : XMIN180300438CCM
Date : May.25, 2018
Page: 17 of 27
11. Volatile Organic Compounds
Test Method:
With reference to SGS In-house method. Weight sample to headspace bottle, then heat 1hr at 100°C in
headspace instrument. Analysis was performed by HS-GC-MS.
Notes: 1. According to ASTM G 21-15 Standard Practice for Determining Resistance of Synthetic Polymeric Materials to Fungi,observed fungi growth rating on the specimens include:0 –None1 –Traces of growth (less than 10%)2 –Light growth (10 to 30%)3 –Medium growth (30 to 60%)4 –Heavy growth (60% to complete coverage)2. History name of test organismAHistorically known as A.niger.BHistorically known as P.pinophilum.CHistorically known as Gliocladium virens.
3.* The microscope(50 X) was used to confirm the observation.******** To be continued********
TEST REPORT No. : XMIN180300438CCM
Date : May.25, 2018
Page: 25 of 27
18. Assessment of Antimicrobial activity
Test method: With reference to ASTM E 2180-07 (Reapproved 2012)
Test organism: Staphylococcus aureus ATCC 6538
Name of test bacteria
(Strain number)
Concentration of bacteria (cells/mL)
/
The antilog of the geometric mean of
the number of organisms
recovered from “0h” (cfu/mL)
The antilog of the geometric mean of
the number of organisms
recovered from “24h” (cfu/mL)
Reduction (%)
Staphylococcus aureus
ATCC 6538 3.3 х 106
Sample / 2.2 х 104 97.2
Control Sample
1.2 х 106 1.7 х 107
19. Test Item: Izod Notched Impact Strength
Sample Description: See photo
Test Method: ASTM D256-10ε1 Method A
Test Condition:
Specimen width: 11.86 mm (Notch preparation: machining)