Some Essentials of Thermo Compression Bonding A Machine Vendor’s View Hugo Pristauz Dec-2016 (presented on the 3D-ASIP 2016 conference in San Francisco)
Some Essentials of
Thermo Compression
Bonding
A Machine Vendor’s View
Hugo Pristauz
Dec-2016
(presented on the 3D-ASIP 2016 conference in San Francisco)
Introduction
TCB Core Capabilities
Accuracy
Co-planarity
Bond Control
Conclusions
Dec-2016
Adoption of 2.5D/3D Integration
3 3D-ASIP 2016
Source: Yole
TCB is still seen as the key assembly technology
for 2.5/3DI C2S, C2C or C2W (might change in the future)
Dec-2016
Challenges Which are Mastered with TCB
4 3D-ASIP 2016
warping
substrate
thin warping die
Warpage
non-wets
solder bridging
Ultra Fine Pitch small
solder volume
dielectric
cracks
Thermal Stress extra
low-k
solder climbing squish
non-wet
Dec-2016
3 Kinds of TCB Processes
5 3D-ASIP 2016
TC-NCF Process (WL applied nonconductive
film or wafer level underfill)
T F
future
killer process
enables
collective
bonding !!!
simple
bond
control
TC-NCP Process (pre-applied nonconductive
paste) T F TCB pioneer!
not good for
thin (memory)
die
simple
bond
control
TC-CUF Process (capillary underfill, or
TC-MUF: molded underfill) T F still major
volume
(material
readiness)
z hybrid bond
control
Dec-2016
Video Clips from 8800 TCadvanced
6 3D-ASIP 2016
Face-up TCB Robot handling for C2W
TC-NCF @ C2W TC-CUF @ C2S
Dec-2016
3D TSV Stacks - Done in 2014
7 3D-ASIP 2016
60 ... 80 µ pitch
Dec-2016
10µ pitch TC-NCF C2W face-up stacked die
Some Results from 2016
8 3D-ASIP 2016
Dec-2016
3D Technology Landscape
9 3D-ASIP 2016
IMEC Test Dies
• 40µ pitch
• 20µ pitch
• 10µ pitch
Now at 10µ pitch!
2µ @ 3 accuracy
3D stacked IC 3D system-on-chip True 3D IC public source:
IMEC
3D-SIC roadmap: 40µ 20µ 10µ 5µ pitch 10µ
3D stacked IC 3D system-on-chip
Dec-2016
Get Back to 3D Technology Landscape
10 3D-ASIP 2016
next target
200 nm @ 3 accuracy
source: IMEC (public)
Next step to focus:
• 1µ @ 3 pitch, needs 200 nm @ 3 placement accuracy!
3D-SOC roadmap: 5µ pitch 1µ
Introduction
TCB Core Capabilities
Accuracy
Co-planarity
Bond Control
Conclusions
Dec-2016
TCB Core Capabilities – Yield
12 3D-ASIP 2016
3 Core Capabilities
Accuracy Co-planarity Bond Control
Essential - Yield
3 core capabilities are major
responsible for making yield
Current HVM requirement:
99.8% yield per die
Introduction
TCB Core Capabilities
Accuracy
Co-planarity
Bond Control
Conclusions
Dec-2016
Breaking Up the Accuracy Chain
14 3D-ASIP 2016
2µ@3
hot
matrix
high force
real die
2µ@3 2µ @ 3
Dec-2016
Breaking Up the Accuracy Chain
15 3D-ASIP 2016
2µ@3
hot process
matrix position
high force
GoG real die
2µ@3 2µ @ 3 2µ @ 4
Dec-2016
Breaking Up the Accuracy Chain
16 3D-ASIP 2016
2µ@3
hot process
matrix position
high force low force
glass-on-glass (GoG) real die
2µ@3 2µ @ 3 2µ @ 4 2µ @ 5
Dec-2016
Breaking Up the Accuracy Chain
17 3D-ASIP 2016
2µ@3
cold proc. hot process
matrix position
low force high force
glass-on-glass aplication (GoG) real die
2µ@3 2µ @ 3 2µ @ 4 2µ @ 5 2µ @ 6
Dec-2016
Breaking Up the Accuracy Chain
18 3D-ASIP 2016
2µ@3
cold process hot process
matrix position single pos.
low force high force (250N)
glass-on-glass aplication (GoG) real die
2µ@3 2µ @ 3 2µ @ 4 2µ @ 5 2µ @ 6 2µ @ 7
0 100 200 300 400 500 600 700 800 900
-2.5
-2
-1.5
-1
-0.5
0
0.5
1
1.5
2
2.5
x [
µ],
y [
µ]
@4305.77.Speck Challenge (17:04:43) [stream]: mean = 0.17/0.02, sigma = 0.16/0.12 @ x/y [µ/µ]
Cpk = 3.88/5.57, Cp = 4.24/5.62 @ x/y [2µ/2µ]
Dec-2016
A Closer Look at the Data
19 3D-ASIP 2016
2µ @ 7
required
Single position GoG application
cold (20°C), low force (30N)
2µ @ 11 sigma
achieved!
(+/- 0.55µ)
Matrix GoG application
hot (380°C), high force (250N)
0 200 400 600 800 1000 1200
-2.5
-2
-1.5
-1
-0.5
0
0.5
1
1.5
2
2.5
x [
µ],
y [
µ]
Matrix GoG, T: 100->380°C, 30N [stream]: mean = 0.17/-0, sigma = 0.4/0.4 @ x/y [µ/µ]
Cpk = 1.53/1.68, Cp = 1.67/1.68 @ x/y [2µ/2µ]
2µ @ 4 required
2µ @ 5 sigma
achieved!
(+/- 1.2µ)
Temperature
Ramp
>300°C/s
Heat Up
Accuracy – Essential !
20 3D-ASIP 2016
Essential - Accuracy
Maintain position accuracy while
ramping from cold to hot state
Dec-2016
Accuracy – Essential !
21 3D-ASIP 2016
Essential - Accuracy
Maintain position accuracy while
ramping from cold to hot state
Dec-2016
single position GoG application
hot (380°C), low force (30N)
2µ @ 5 required weird
behavior !!!
1000 1500 2000 2500 3000 3500 4000 4500-10
-8
-6
-4
-2
0
2
4
6
8
[email protected]_Test_left_heated_tool_hot (13:51:51)
time
x [µ
], y
[µ
]
Potential Issue
Or: bring accuracy
from bond head down to die
80°C
80°C
80°C->380°C
Dec-2016
The Problem with CTE
22 3D-ASIP 2016
Tool Holder: Material A
isolator
CTE = 3ppm/K
Issues: • expansion on bottom: 13.5µ/15mm
• Loss of planarity
• Thermal stress
• life time issues
(cracks after >30.000 cycles)
Solution: controlled relative movements
80°C
380°C
Benefits: • stays highly planar
• life time: >2 Mio cycles
Drawback • CTE mismatch between nozzle
& tool holder (Si: CTE = 2.6 ppm/K)
• relative movements !!!
• 15 mm Si die: 11.7µ @ 300°C
• isolator: 2.7µ @ 300°C
Tool Holder: Material B+C
isolator, CTE = 0.6 ppm/K
any, CTE = 9-12 ppm/K
380°C
70°C
80°C
Introduction
TCB Core Capabilities
Accuracy
Co-planarity
Bond Control
Conclusions
Dec-2016
Co-Planarity
24 3D-ASIP 2016
US Patent 6 651 866 B1
US Patent 2014/0030052A1
Besi: Two approaches to
achieve co-planarity
better than +/-1µ@10mm
Why? - a picture says
more than 1000 words!
Challenge: small solder volume of micro bumps is not forgiving!
Dec-2016
Co-planarity Auto Setup
25 3D-ASIP 2016
Automatic procedure for co-planarity setup
Target for tilt setup: +/- 1µ@10mm
Principle 1
implemented in
8800 TC & 8800 TC advanced
used for dynamic tilt
compensation
Co-planarity can be adjusted by
servo actuators
in spec!
Dec-2016
Co-planarity Auto Setup
26 3D-ASIP 2016
Target for tilt setup: +/- 0.5µ @ 10mm
Principle 2
More simple principle!
if dynamic tilt compensation
is not reqired!
Automatic procedure
a) spherical air bearing in bond head can be
switched from fixed to friction-less state
b) co-planarity is established while pressing
bond head to stage in friction-less state
c) after establishing co-planarity spherical
bearing is fixed
max 0.45µ
Dec-2016
Co-planarity – Essential !
27 3D-ASIP 2016
0 1 2 3 4 5 6 7 8
10
15
20
25
30
#2.56 Tilt 119G-05 (2015-01-29)
F [N
] (fo
rce
- blu
e), T
/10
[°C
] (te
mp.
- re
d), w
[µ](p
os. -
gre
en)
(C) Time t [s] - (selection by: tasks: All Tasks, types: * gantry: L layer: 0)
100
150
200
250
300
Test: Run 40 repeatable
temperature ramps
from 80°C to 300°C
0 1 2 3 4 5 6 7 8-4
-2
0
2
4
6
Residues: kinematic: std = NaNµ (Cpk = NaN), thermal: std = 0.69µ (Cpk = 0.48)
#2.56 Tilt 119G-05 (2015-01-29)
-40
-20
0
20
40
60
Improper Co-planarity Integrity
Position traces of
4 die corners
Residual analysis out of spec
0 1 2 3 4 5 6 7 8-4
-2
0
2
4
6
Residues: kinematic: std = 0.03µ (Cpk = 12.29), thermal: std = 0.09µ (Cpk = 3.8)
#2.56 Tilt 119G-05 (2015-01-29)
-40
-20
0
20
40
60
Proper Co-planarity Integrity
Position traces of
4 die corners
Residual analysis in spec +/-1µ
Essential:
Coplanarity Integrity
„Maintain co-planarity during
temperature ramp!“
Introduction
TCB Core Capabilities
Accuracy
Co-planarity
Bond Control
Conclusions
Dec-2016
TC-CUF – Most Sophisticated Bond Control
29 3D-ASIP 2016
Essential: Sophisticated Hybrid Bond Control
TC-CUF Process (capillary underfill, or
TC-MUF:molded underfill) T F
TC-CUF
sophisticated
z
• start in force control mode, switch to position control ...
• ... controlling BLT (bond line thickness) tightly within +/-1µ tolerance
• ... despite of thermal expansion movements (10-20x larger)
• ... which cannot be sensed life (in liquification phase)
Dec-2016
Bond Control for TC-CUF Process
30 3D-ASIP 2016
z (position)
T (temperature)
F (force)
0 0.5 1 1.5 2 2.5 3 3.5 4 4.5 5 5.5-20
-10
0
10
20
30
40
50
-200
-100
0
100
200
300
400
500
Tem
pera
ture
[°C
]
Bond Control for CUF Process
Forc
e [
N],
Positio
n [
µm
]
time [s]
high temperature
ramping rate
200°C/s
dynamic
z-control
during collapse
thermal
compensation
rapid cooling
-100°C/s
• Challenge 1: How do you teach the position control?
• Challenge 2: How do you move from one tool to another?
T (temperature)
F (force)
z (position)
position control. force
control
Dec-2016
Enhanced Bond Control for TC-CUF Process
31 3D-ASIP 2016
0 0.5 1 1.5 2 2.5 3 3.5 4 4.5 5 5.5-20
-10
0
10
20
30
40
50
-200
-100
0
100
200
300
400
500
Tem
pera
ture
[°C
]
Enhanced Bond Control for CUF Process
Forc
e [
N],
Positio
n [
µm
]
time [s]
• By distributing bond control over two position axes the
complexity of the bond control is reduced
w (position)
T (temperature)
F (force)
z (position)
thermal
compensation
@ z-position-axis
w-position axis
used for
BLT control
-7µ@2s responsibility of
process engineer kinematic
compensation position control. force
control
Dec-2016
1) Start with Force Ramp
32 3D-ASIP 2016
0 0.5 1 1.5 2 2.5 3 3.5 4 4.5 5 5.5-20
-10
0
10
20
30
40
50
-200
-100
0
100
200
300
400
500
Tem
pera
ture
[°C
]
Enhanced Bond Control for CUF Process
Forc
e [
N],
Positio
n [
µm
]
time [s]
w (position)
T (temperature)
z (position)
start with
force ramping
-7µ@2s
responsibility of
process engineer
bond head position (w)
reacts with elastic movement)
F (force)
0 0.5 1 1.5 2 2.5 3 3.5 4 4.5 5 5.5-20
-10
0
10
20
30
40
50
-200
-100
0
100
200
300
400
500
Tem
pera
ture
[°C
]
Enhanced Bond Control for CUF Process
Forc
e [
N],
Positio
n [
µm
]
time [s]
Dec-2016
2) Start Temperature Ramping
33 3D-ASIP 2016
w (position)
T (temperature)
z (position)
-7µ@2s
responsibility of
process engineer
start
temperature
ramping
bond head position (z)
will start moving due to
thermal expansion
Shortly before liquification:
switch from force to position
control (to be prepared for the
soon following force collapse)
hold force
start your compensation for
the thermal expansion
0 0.5 1 1.5 2 2.5 3 3.5 4 4.5 5 5.5-20
-10
0
10
20
30
40
50
-200
-100
0
100
200
300
400
500
Tem
pera
ture
[°C
]
Enhanced Bond Control for CUF Process
Forc
e [
N],
Positio
n [
µm
]
time [s]
Dec-2016
3) Liquification Phase: Hurry up!
34 3D-ASIP 2016
w (position)
T (temperature)
z (position)
-7µ@2s
responsibility of
process engineer
temperature
exceeds
liquification
threshold
Liquification:
the bump gets
liquid and the
force breaks
down
Luckily you are already in
position mode and you can
control bond head position
for whatever you want!
Hurry up and raise the bond
head position, since by collapse
of the force your compressed
elasticities relax at sudden
don‘t forget: your materials
are thermally expanding!
Compensate with porper
bond head raise movement!
solder climbing
squish
otherwise you get these
nasty results
0 0.5 1 1.5 2 2.5 3 3.5 4 4.5 5 5.5-20
-10
0
10
20
30
40
50
-200
-100
0
100
200
300
400
500
Tem
pera
ture
[°C
]
Enhanced Bond Control for CUF Process
Forc
e [
N],
Positio
n [
µm
]
time [s]
Dec-2016
4) Relax – Solder Joint Formation
35 3D-ASIP 2016
w (position)
T (temperature)
z (position)
-7µ@2s
Relax!
Adjust bond head position to
form final solder joint height
and never forget:
your materials are still
thermally expanding!
Compensate with porper
bond head raise movement!
responsibility of
process engineer
temperature
is still in a
transient
phase
0 0.5 1 1.5 2 2.5 3 3.5 4 4.5 5 5.5-20
-10
0
10
20
30
40
50
-200
-100
0
100
200
300
400
500
Tem
pera
ture
[°C
]
Enhanced Bond Control for CUF Process
Forc
e [
N],
Positio
n [
µm
]
time [s]
Dec-2016
5) Bring to the End
36 3D-ASIP 2016
w (position)
T (temperature)
z (position)
-7µ@2s
Hold your solder joint thickness!
Especially during solidification
phase, otherwise you will
impact your solder joint strength
And never forget:
your materials are still
thermally expanding, later
on shrinking!
Compensate with porper
bond head movement!
run the rest of
your thermal profile.
solder joints are still
liquid until
solidification
Dec-2016
Further Essential
37 3D-ASIP 2016
Essential:
The control of each process variable
must be highly repeatable !
Keep in mind!
• There is no sensor which helps you how to do the
• thermal compensation (this is the current standard)
• The thermal compensation movement has to be identified
automatically and to be recalled from memory during bond
control
Introduction
TCB Core Capabilities
Accuracy
Co-planarity
Bond Control
Conclusions
Dec-2016
• For 2.5D/3DI C2S, C2C and C2W TCB is fully established in HVM
packaging
• Essential for TCB yield are 3 core capabilities: accuracy, co-planarity
and bond control.
• Essential for TCB is to maintain high accuracy from a cold die position
to a hot die position during rapid temperature ramps (rapid means:
>300°C/s)
• Essential for TCB is to maintain high co-planarity during whole rapid
temperature transients (heating & cooling)
• Essential for TCB is a highly repeatable bond control, especially for
TC-CUF where BLT control of +/-1µ needs to be achieved
Conclusions
39 3D-ASIP 2016
Thank You
Questions ?