i KARAKTERISTIK EKSTRAK ASBUTON DENGAN METODE ASBUTON EMULSI MENGGUNAKAN PEREMAJA OLI BEKAS DAN KARAKTERISTIK PENAMBAHAN EKSTRAK ASBUTON EMULSI PADA ASPAL PENETRASI 60/70 SEBAGAI MODIFIKASI BITUMEN (SEMARBUT ASPAL TIPE III) Characteristic of Extracted Asbuton with Emulsion Asbuton Method Using Regeneration Of Used Lubricant Oil and Characteristics of Extracted Asbuton Addition on 60/70 Penetration Asphalt As Bitumen Modification (Semarbut Asphalt Type III) SKRIPSI Disusun sebagai Syarat Memperoleh Gelar Sarjana Teknik Pada Program Studi Teknik Sipil Fakultas Teknik Universitas Sebelas Maret Surakarta Disusun oleh : DEVI PRAPITA NUARI I 0113032 PROGRAM STUDI TEKNIK SIPIL FAKULTAS TEKNIK UNIVERSITAS SEBELAS MARET SURAKARTA 2017
16
Embed
SKRIPSI - eprints.uns.ac.id · mixing campuran bahan padat terhadap kadar aspal asbuton emulsi, karakteristik ekstrak asbuton emulsi, karakteristik Semarbut Aspal Tipe III dan penambahan
This document is posted to help you gain knowledge. Please leave a comment to let me know what you think about it! Share it to your friends and learn new things together.
Transcript
i
KARAKTERISTIK EKSTRAK ASBUTON DENGAN METODE
ASBUTON EMULSI MENGGUNAKAN PEREMAJA OLI BEKAS DAN
KARAKTERISTIK PENAMBAHAN EKSTRAK ASBUTON EMULSI
PADA ASPAL PENETRASI 60/70 SEBAGAI MODIFIKASI BITUMEN
(SEMARBUT ASPAL TIPE III)
Characteristic of Extracted Asbuton with Emulsion Asbuton Method Using
Regeneration Of Used Lubricant Oil and Characteristics of Extracted Asbuton
Addition on 60/70 Penetration Asphalt As Bitumen Modification (Semarbut
Asphalt Type III)
SKRIPSI
Disusun sebagai Syarat Memperoleh Gelar Sarjana Teknik
Pada Program Studi Teknik Sipil Fakultas Teknik
Universitas Sebelas Maret
Surakarta
Disusun oleh :
DEVI PRAPITA NUARI
I 0113032
PROGRAM STUDI TEKNIK SIPIL FAKULTAS TEKNIK
UNIVERSITAS SEBELAS MARET
SURAKARTA
2017
ii
iii
iv
MOTTO
“Sebaik-baiknya orang adalah yang bermanfaat bagi orang lain”
“Harapan selalu ada ketika kita tidak menyerah”
“Berusaha, Berdoa dan Bersyukur”
-Penulis-
v
PERSEMBAHAN
Saya persembahkan karya ini untuk:
-Kedua Orang Tua Saya Tercinta-
Ibu Yani Asih dan Bapak Setya Utama Yang senantiasa memotivasi, mendoakan penuh kasih sayang serta memberi dukungan
dan kepercayaan untuk saya
-Sister and Brother Terkasih- Mbak Ayu, Mas Dimas, Dek Cilent, Mas Amad
Yang senantiasa mengganggu saya dalam proses mengerjakan skripsi tetapi itu sangat
menghibur dan membuat kejenuhan saya hilang
-My Sweetest Coffee-
Afif Adhiyan Yang senantiasa menjadi penyemangat terbaik serta mengisi hari-hari saya dan menjadi
tempat berbagi segala keluh kesah
-Suami Skripsi-
Muhammad Rifa’i Yang senantiasa menemani saya selama proses Skripsi berlangsung (dari ngelab hingga
nyari dosen untuk ACC laporan). Terima kasih telah menjadi teman hidup selama 8
bulan untuk segala canda, tawa dan tangis (apalagi ketika hampir menyerah) hehe
-3 Jomblo Menuju Akad Bahagia-
Hera, Siti, Tri Ang Yang senantiasa menciptakan segala bentuk lekuk senyuman diwajah saya, terima kasih
atas dukungan dan tak luput juga kegilaan kalian. Semoga kita akan akad pada
waktunya dan senantiasa dalam kebahagiaan (maaf nama grupnya tak jadiin satu, tapi
nyambung juga hehe)
-Sipil Oh Yeah-
Mahasiswa Teknik Sipil Angkatan 2013 Yang telah menjadi teman hidup selama 4 tahun, terima kasih untuk kekeluargaan yang
kalian berikan selama ini
vi
ABSTRAK
Devi Prapita Nuari, 2017. Karakteristik Ekstrak Asbuton dengan Metode Asbuton
Emulsi Menggunakan Peremaja Oli Bekas dan Karakteristik Penambahan Ekstraksi
Asbuton Emulsi pada Aspal Penetrasi 60/70 Sebagai Modifikasi Bitumen (Semarbut
Aspal Tipe III). Skripsi. Program Studi Teknik Sipil Fakultas Teknik Universitas Negeri
Sebelas Maret Surakarta.
Asbuton belum dapat dimanfaatkan secara optimal di Indonesia karena pemanfaatannya
terbatas dalam bentuk butiran. Tujuan penelitian ini adalah menganalisis hubungan waktu
mixing campuran bahan padat terhadap kadar aspal asbuton emulsi, karakteristik ekstrak
asbuton emulsi, karakteristik Semarbut Aspal Tipe III dan penambahan ekstrak asbuton
emulsi optimum yang memenuhi persyaratan aspal yang dimodifikasi dengan asbuton.
Asbuton emulsi terdiri dari bahan padat (asbuton butir 5/20 dan oli bekas yang dimixing
dengan variasi waktu 3,5,7,9 dan 11 menit dengan waktu pemeraman 24 jam) dan bahan
cair (texapon, HCl dan aquades). Ekstrak asbuton emulsi diuji nilai kadar aspal hingga
diperoleh kadar aspal optimum kemudian mencampurkannya ke aspal penetrasi 60/70
dengan variasi kadar 30%,35%,40%,45% dan 50% (Semarbut Aspal Tipe III).
Kadar aspal optimum diperoleh pada waktu mixing 8 menit 54 detik. Hasil pengujian
karakteristik ekstrak asbuton emulsi adalah nilai penetrasi 5 dmm; titik lembek 92⁰C; titik
nyala 252⁰C; titik bakar 259⁰C; Daktilitas 0cm; berat jenis 1,44 gr/cc; kelekatan terhadap
agregat 100%. Dengan hasil karakteristik ekstrak asbuton tersebut belum dapat digunakan
sebagai bahan pengikat pada lapis permukaan, namun masih bisa dikembangkan menjadi
bahan tambah pada aspal penetrasi 60/70 sebagai modifikasi aspal Semarbut Aspal Tipe
III. Semarbut Aspal Tipe III kadar ekstrak asbuton emulsi 30% memenuhi persyaratan
aspal yang dimodifikasi dengan asbuton. Karakteristik aspal Semarbut Aspal Tipe III
adalah nilai penetrasi 56,9 dmm; titik lembek 57⁰C; titik nyala 290⁰C; titik bakar 310⁰C;
Daktilitas 55,5 cm; berat jenis 1,15 gr/cc; kelekatan terhadap agregat 100%.
Kata Kunci: Asbuton Emulsi, Ekstraksi, Waktu Mixing, Semarbut Aspal Tipe III.
vii
ABSTRACT
Devi Prapita Nuari, 2017. Characteristics of Asbuton Extracted with Emulsion Asbuton
Method Using Regeneration of Used Lubricant Oil and Characteristics of Emulsion
Asbuton Extracted Addition on 60/70 Penetration Asphalt As Bitumen Modification
(Semarbut Asphalt Type III). Thesis. Civil Engineering Department Faculty of
Engineering Sebelas Maret University of Surakarta.
Asbuton cannot be utilized optimally in Indonesia because its terms is limited in granules
form. The purpose of this research is to analyze the relations of time mixing of emulsion
bitumen content in solid phase to emulsion asphalt content, characteristics of emulsion
asbuton extracted, Semarbut Asphalt type III characteristic and addition of an optimum
emulsion asbuton extracted that fulfill asbuton modified asphalt requirement.
Asbuton emulsions are composed of solid material (5/20 grain asbuton and used lubricant
oil mixed with time variation is 3,5,7,9 and 11 minutes with 24 hours curing time) and
liquid material (texapon, HCl and aquades). The emulsion of asbuton extracted tested the
bitumen content until the optimum bitumen content was obtained and then mixed it into
penetration asphalt 60/70 with variation of content is 30%, 35%, 40%, 45%, and 50%
(Semarbut asphalt type III).
The optimum bitumen content was obtained at mixing time 8 minutes 54 seconds. Based on
research, can be obtained characteristics of emulsion asbuton extracted were penetration
value of 5 dmm, softening point 92⁰C, flash point 252⁰C, fuel point 259⁰C, ductility 0cm,
specific gravity 1.44 gr / cc, stickiness to aggregate 100% With the characteristic results of
this asbuton extract can not be used as a binder on the surface layer, but can still be
developed into additional material on asphalt penetration 60/70 as asphalt Semarbut
Asphalt Type III content of 30% asbuton emulsion extract meets asphalt modified asphalt
requirements. Characteristics of Semarbut Asphalt Type III are penetration asphalt 56,9
dmm; softening point of 57⁰C; flash point 290⁰C; burn point 310⁰C; Ductility 55.5 cm,
specific gravity 1.15 g / cc, stickiness to aggregate 100%.
Keywords: Emulsion Asbuton, Extraction, Mixing Time, Semarbut Asphalt Type III.
viii
PRAKATA
Puji syukur penyusun panjatkan kepada Tuhan Yang Maha Kuasa yang telah
melimpahkan rahmat-Nya sehingga penyusun dapat menyelesaikan Skripsi dengan
judul “Karakteristik Ekstrak Asbuton dengan Metode Asbuton Emulsi
Menggunakan Peremaja Oli Bekas dan Karakteristik Penambahan Ekstrak Asbuton
Emulsi pada Aspal penetrasi 60/70 Sebagai Modifikasi Bitumen (Semarbut Aspal
Tipe III)”. Skripsi ini merupakan persyaratan akademik untuk menyelesaikan
Program Sarjana pada Program Studi Teknik Sipil Fakultas Teknik Universitas
Sebelas Maret Surakarta.
Penyusun telah banyak mendapatkan bantuan bimbingan maupun kerjasama dari
berbagai pihak. Oleh karena itu, penyusun mengucapkan terima kasih kepada :
1. Segenap Pimpinan Program Studi Teknik Sipil Fakultas Teknik Universitas
Sebelas Maret Surakarta
2. Ir. Djoko Sarwono, MT selaku Dosen Pembimbing I
3. Dr. F Pungky P ,ST, MT selaku Dosen Pembimbing II
4. Ir. A Mediyanto, MT selaku Pembimbing Akademik
5. Mas Sigit selaku staff pengelola/laboran Laboratorium Perkerasan Jalan Raya
Fakultas Teknik Universitas Sebelas Maret Surakarta
6. Muhammad Rifa’i selaku patner dalam penelitian Skripsi Asbuton Oli Bekas
2017
7. Teman-teman Teknik Sipil 2013 Universitas Sebelas Maret.
Penyusun menyadari keterbatasan kemampuan dan pengetahuan yang penyusun
miliki sehingga masih ada kekurangan dalam penyusunan skripsi ini, untuk itu
penyusun mengharapkan kritik dan saran yang membangun dari para pembaca.
Akhir kata semoga skripsi ini bermanfaat bagi penyusun khususnya dan pembaca
umumnya.
Surakarta, Oktober 2016
Penyusun
ix
DAFTAR ISI
HALAMAN JUDUL ............................................................................................. i
HALAMAN PERSETUJUAN ............................................................................. ii
HALAMAN PENGESAHAN .............................................................................. iii
MOTTO DAN PERSEMBAHAN ....................................................................... iv
ABSTRAK ........................................................................................................... vi
ABSTRACT ............................................................................................................ vii
PRAKATA ........................................................................................................... viii
DAFTAR ISI ......................................................................................................... ix
DAFTAR TABEL ................................................................................................. xiii
DAFTAR GAMBAR ........................................................................................... xv
DAFTAR LAMPIRAN ......................................................................................... xvi
BAB 1 PENDAHULUAN
1.1 Latar Belakang Masalah ........................................................................ 1
1.2 Rumusan Masalah ................................................................................... 3
1.3 Batasan Masalah .................................................................................... 3
1.4 Tujuan Penelitian ................................................................................... 4