RESEARCH INSTITUTE OF WOOD INDUSTRY (CRIWI), CHINESE ACADEMY OF FORESTRY (CAF) 1 Rubberwood preservation by friendly preservatives Mingliang Jiang, Zhijun.

1

RESEARCH INSTITUTE OF WOOD INDUSTRY (CRIWI), CHINESE ACADEMY OF FORESTRY (CAF)

Rubberwood preservation by friendly preservatives

Mingliang Jiang, Zhijun WangResearch Institute of Wood Industry, Chinese

Academy of Forestry, Beijing 100091, China

Dec 8-10, 2008 Haikou, China

2


Contents1. Brief introduction of wood and rubberwood pre

servation

2. Treatment specification and quality control

3. Laboratory test of Antistain and Antimold Formulations on rebberwood (ITTO 1996-1998)

4. Laboratory test of Antistain and Antimold Formulations (2003-2007)

5. Technical report of vacuum pressure treatment by NaPCP free preservative during 2006-2007

3


1 Brief introduction of wood and rubberwood (RW) preservation

4


Wood preservation in China

Railway sleeper by creosote Exterior uses treated by CCA/ACQ/CuAz Indoor uses of rubberwood by boron

5


ACQ treated Chinese fir for exterior use, Anhui, 2006

6


RW Preservation in China Began on 1970’s Today mainly by vacuum/pressure

process

7


Sawing of rubberwood

8


The rubberwood treated

9


Some facts on RW preservation:

The rubberwood timber production in China is about 0.4 millionM3 /a in the recent years

100 rubberwood treating plants in China

The RW timber mainly used for furniture making

RW primary products: timber, particleboard, plywood

10


2 Treatment specification and quality control

11


Specification for the treated wood:LY/T1636-2005

Specification for the treated rubberwood: No specific standard currently Usually adopt 0.4 % BAE (Malaysia for wood) Ref: LY/T1636-2005(wood for C1: 2.8kg/m3

B2O3)

12


Penetration check

13


Solution for checking boron

14


Drying rubberwood, Red-Present of boron; Yellow- without boron

15


No spraying

Fresh treated rubberwood spraying with reagent solution

16


Retention determination

17


By chemical analysis of boron:Titration,ICP etc

Retention calculation by treating record

18


Treating record for each charge at Lezhong Wood Factory, Hainan

19


3 Laboratory test of Antistain and Antimold Formulations (1996-1998)

3.1 Experimental methods

20


Rubberwood sample size: 50×20×1 mm, maple 40×20×3 mm.

Fungicidal formulations for stain control: F1, F2: chlorothalonil/carbendizam fungicides.

21


Ranking Standard 1 - Clean: stain or mold covering less than

5% upper surface. 2 - Light stain: stain or mold covering 5 -

20% upper surface. 3 - Moderate stain: stain or mold covering

20-40 % upper surface. 4 - Heavy stain: stain or mold covering more

than 40% upper surface.

22


3.2 Results

23


Table 1. Comparison of the effectiveness of anti-sapstain treat

ments against Botryodiplodia theobromae Pat. on rubberwood Anti-sapstain Treatment Average Std

Untreated Control 4.0 0.0

0.25%NaPCP 4.0 0.0

0.5%NaPCP 3.0 0.0

1%NaPCP 3.0 0.0

1.0%F1（ F） 3.0 0.0

24


0.20%F2 2.0 0.0

0.40%F2 1.0 0.0

0.5%F1（ E） +0.10%F2 1.0 0.0

0.5%F1（ E） +0.20%F2 1.0 0.0

0.5%F1（ F） +0.05%F2 1.0 0.0

0.5%F1（ F） +0.10%F2 1.0 0.0

0.5%F1（ F） +0.20%F2 1.0 0.0

25


Conclusion for 3

The formulations containing 0.05-0.2% F2, mixed with 0.5%F1 or 0.40%F2 alone are effectiveness for controlling Botryodiplodia theobromae in lab test.

26


4 Laboratory test of Antistain and Antimold Formulations (2003-2007)

4.1 Experimental methods

27


4.1.1 Fungal species and their characteristic

Five fungal species were identified as ： Bt: Botryodiplodia theobromae Pat., Fv: Fusarium verticillioides(Sacc.)Nirenberg, Th: Trichoderma harzianum Rifai, Tv: Trichoderma viride Pers., Pp: Penicillium purpurogenum Stoll.

28


4.1.2 Fungicides for the test

29


Table 2: Fungicidal formulations for the stain control test

Formulations Common nameFormulation

types

CTL Chlorothalonil Emulsion

CBZ Carbendazim50% wetable powe

r

Benomyl Benomyl50% wetable powe

r

BACDodecyl dimethyl benzyl amm

onium chlorideWater solution

Cu-8 Copper oxineAcetic acid

solution

DDACDidecyl dimethyl ammonium c

hlorideWater solution

PPZ Propiconazole Emulsion

TEB Tebuconazole Emulsion

30


4.1.3 Method for stain control

31


4.2 Results

32


Table 3: Result of the stain control test

FormulationsConcentrations of a. i. B t

CBZ

0.001% 36.6

0.005% 39.2

0.010% 40.1

0.02% 40.6

0.10% 41.2

0.20% 43.6

33


FormulationsConcentrationsof a. i. B t

benomyl

0.001% 32.4

0.005% 35.5

0.010% 37.0

0.02% 38.1

0.10% 40.7

0.20% 50.6

Contd

34


Contd

Formulations Concentrationsof a. i. B t

CBZ+Cu-8

0.01%+0.01% 21.4

0.01%+0.05% 22.3

0.01%+0.1% 23.8

0.1%+0.2% 42.3

0.1%+0.5% 47.2

0.2%+0.5% 59.7

35


Contd

Formulations Concentrationsof a. i. B t

Benomyl+Cu-8

0.005%+0.01% 42.7

0.01%+0.01% 43.1

0.02%+0.01% 46.1

0.02%+0.02% 48.9

0.1%+0.02% 50.4

0.2%+0.08% 52.9

36


Conclusion for 4

Some formulations containing CBZ, Benomyl, Cu-8 have excellent effectiveness for the controlling of Botryodiplodia theobromae Pat.

37


5 Technical report of vacuum pressure treatment by NaPCP free preservative during 2006-2007

38


5.1 Materials and method

5.1.1 Materials Fresh rubberwood timber.

39


Formulations

Boric acid Borax F2

Site 1 0.50 1.000.035-

0.045

Site 2 1.00 0.200.035-

0.050

5.1.2 Preservatives

40


5.1.3 Test sites and treating procedure

Vacuum pressure treatment was used in the

following procedure.

41


Site 1 ： Lezhong Wood Factory, Hainan Nongken Wood Co ， duration ： Aug 3, 2006– May 31, 2007.

42


Site 1: Schedule for the rubberwood Vacuum / Pressure treatment

Phase Vacuum / Pressure (Mpa) Duration (min)

Initial vacuum 0.02 15

Pressure 1.2 35

Final vacuum 0.015 10

43


Fungicide F2 for stain control made in Jiangsu, China

44


Tank for preparation of treating solution at Lezhong wood plant

45


Control panal

46


Site 2 ： Cangjiang Wood Plant, Xishuangbanna, Yunnan Province. duration ： July 24, 2006– Oct 31, 2006.

47


Site2: Schedule for the rubberwood

Vacuum / Pressure treatment Phase Vacuum / Pressure (Mpa) Duration (min)

Initial vacuum 0.02 15

Pressure 1.1 60

Final vacuum 0.02 10

48


Tank for preparation of treating solution in Cangjiang wood plant, Yunnan

49


RW timber before treatment

50


Air drying after treatment prior to kiln

51


5.2 Results

This field demonstration indicated that F2 could prevent the treated timber for 15-20 days from stain and mold during air drying.

52


Fungicide carbendazim (F2) can be used for stain and mold control instead of NaPCP.

Conclusion for 5

53


Related publications of this RW project:

Mingliang Jiang, Terry L. Highley, Leslie Ferge, Thomas L. Woods. Laboratory Evaluation of Chrolothalonil Formulation for Stain and Mold Control on Rubberwood and Maple, International Research Group on Wood Preservation, IRG/WP 98-30175. 29th IRG, Maastricht, Netherlands, June 14-19, 1998.

Mingliang Jiang. Polit test of antisapstain and mold formulations on rubberwood, China Wood Industry (Chinese), 2001,2

Mingliang Jiang. China Wood Industry (Chinese), 1998, 12(3). Mingliang Jiang. Current Research Situation of the New Wood P

reservative Chlorothalonil, China Wood Industry, 1997,11(4), 21-22.

Xiuying Liu, Mingliang Jiang. Currently Situation of Rubberwood Processing and Utilization Technology in China, China Wood Industry, 1997, 11(5), 6-8.

Mingliang Jiang et al. Overview on Rubberwood Preservation Technology, China Wood Industry, 1996, 10(6), 22-24.

ITTO technical report: Currently Situation of Rubberwood Processing and Utilization Technology in China, CRIWI, Beijing, 1995.

Mingliang Jiang et al. Laboratory test of blue stain control by chemicals, IRG 07-30430

54


The support and cooperation of Lezhong and Cangjiang wood plant for the field treatment are much appreciated.

55


Thanks for your attention! wish you have a nice stay during the

workshop and visiting tour around the Island.

RESEARCH INSTITUTE OF WOOD INDUSTRY (CRIWI), CHINESE ACADEMY OF FORESTRY (CAF) 1 Rubberwood preservation by friendly preservatives Mingliang Jiang, Zhijun.

Documents

treated wood

wood ref

boron slide

chinese fir

sawing of rubberwood

plywood slide

record slide

brief introduction of