30 LAMPIRAN 1 DATA PENELITIAN L1.1. DATA HASIL UJI Ph TERHADAP MIKROKRISTALIN SELULOSA BERDASARKAN VARIASI KONSENTRASI H 2 SO 4 Tabel L1.1 Data Hasil Uji pH Terhadap Mikrokristalin Selulosa Berdasarkan Variasi Konsentrasi H 2 SO 4 Variasi Kosentrasi(H 2 SO 4 ) pH 1 N 7 1,5 N 6 2 N 7 2,5 N 6 3 N 6 L1.2. DATA HASIL SUSUT PENGERINGAN TERHADAP MIKROKRISTALIN SELULOSA BERDASARKAN VARIASI KONSENTRASI H 2 SO 4 Tabel L1.2 Data Hasil Susut Pengeringan Terhadap Mikrokristalin Selulosa Berdasarkan Variasi Konsentrasi H 2 SO 4 Variasi Kosentrasi(H 2 SO 4 ) Susut Pengeringan(%) 1 N 0.01% 1.5 N 0.08% 2 N 0.02% 2.5 N 0.05% 3 N 0.09%
This document is posted to help you gain knowledge. Please leave a comment to let me know what you think about it! Share it to your friends and learn new things together.
Transcript
30
LAMPIRAN 1
DATA PENELITIAN
L1.1. DATA HASIL UJI Ph TERHADAP MIKROKRISTALIN
SELULOSA BERDASARKAN VARIASI KONSENTRASI H2SO4
Tabel L1.1 Data Hasil Uji pH Terhadap Mikrokristalin Selulosa
Berdasarkan Variasi Konsentrasi H2SO4
Variasi Kosentrasi(H2SO4) pH
1 N 7
1,5 N 6
2 N 7
2,5 N 6
3 N 6
L1.2. DATA HASIL SUSUT PENGERINGAN TERHADAP
MIKROKRISTALIN SELULOSA BERDASARKAN VARIASI
KONSENTRASI H2SO4
Tabel L1.2 Data Hasil Susut Pengeringan Terhadap Mikrokristalin
Selulosa Berdasarkan Variasi Konsentrasi H2SO4
Variasi Kosentrasi(H2SO4) Susut Pengeringan(%)
1 N 0.01%
1.5 N 0.08%
2 N 0.02%
2.5 N 0.05%
3 N 0.09%
31
L1.3. DATA BILANGAN GELOMBANG SPECTRUM HASIL FTIR
Tabel L1.3 Data Bilangan Gelombang Spectrum Hasil Ftir
Ikatan Tipe Senyawa Daerah Frekuensi
(cm-1
)
Intensitas
C-H Alkana 2850-2970 Kuat
1340-1470 Kuat
C-H Alkena 3010-3095 Sedang
675-900 Kuat
C-H Alkuna 3300 kuat
C-H Cincin Aromatik 3010-3100 Sedang
690-900 Kuat
O-H Fenol,monomer,alkohol 3590-3650 Berubah-ubah
Alcohol ikatan
hydrogen, fenol
3200-3600 Berubah-ubah
Terkadang
Monomer asam
karboksilat
3500-3650 Sedang
Ikatan hydrogen asam
karboksilat
2500-2700 Melebar
N-H Amina, Amida 3300-3500 Sedang
C=C Alkena 1610-1680 Berubah-ubah
C=C Cincin Aromatik 1500-1600 Berubah-ubah
C=C Alkun 2100-2260 Berubah-ubah
C-N Amina, Amida 1180-1360 Kuat
C≡N Nitrit 2210-2280 Kuat
C-O Alkoho, ester, asam
karboksilat, ester
1050-1300 Kuat
C=O Aldehid, keton, asam
karboksilat, ester
1690-1760 kuat
NO2 Senyawa nitro 1500-1570 Kuat
1300-1370 kuat
Sumber : Principle of Instrumental Analysis, Skoong, Holler, Nieman,
1998
32
LAMPIRAN 2
CONTOH PERHITUNGAN
L2.1. PEMBUATAN H2SO4 1 N ; 1,5 N ; 2 N ; 2,5 N ; DAN 3 N DALAM
100 ML DARI H2SO4 96% ( ρ=1,84 g/ml)
N = (%×10×𝜌)×𝑒
𝑀𝑟
= 96%×10×1,84 ×2
98,08
= 36 N
Pembuatan H2SO4 1 N
V1 . N1 = V2 . N2
100 . 1 = V2 . 36 N
V2 = 2,77 mL
Pembuatan H2SO4 1,5 N
V1 . N1 = V2 . N2
100 . 1,5 = V2 . 36 N
V2 = 4,16 mL
Pembuatan H2SO4 2 N
V1 . N1 = V2 . N2
100 . 2 = V2 . 36 N
V2 = 5,55 mL
Pembuatan H2SO4 2,5 N
V1 . N1 = V2 . N2
100 . 2,5 = V2 . 36 N
V2 = 6,94 mL
Pembuatan H2SO4 3 N
V1 . N1 = V2 . N2
100 . 3 = V2 . 36 N
V2 = 8,33 mL
33
L2.2. PERHITUNGAN RENDEMEN MIKROKRISTAL SELULOSA
Jumlah α-Selulosa yang digunakan = 15 g
Jumlah perolehan Mikrokristalin selulosa = 12,231 g
Sehingga perhitungan rendemen Mikrokristal Selulosa yang dihasilkan
dari α-Selulosa adalah sebagai berikut.
Rendemen = berat selulosa mikrokristal
berat α−selulosa kering × 100%
= 12,231 𝑔
15 g × 100%
= 81,5 %
Sebagai contoh Untuk menghitung rendemen Mikrokristal Selulosa
disetiap variasi konsentrasi diambil sampel Mikrokristal Selulosa pada
konsentrasi H2SO4 2 N dengan data sebagai berikut.
Jumlah sampel α-Selulosa = 3 g
Perhitungan rendemen 2 N
Rendemen = be rat selulosa mikrokristal
berat α−selulosa kering × 100%
= 2,450 𝑔
3 g × 100%
= 81,7 %
34
L2.3. PERHITUNGAN SUSUT PENGERINGAN MIKROKRISTAL
SELULOSA
Sebagai contoh perhitungan nilai susut pengeringan Mikrokristal
Selulosa, di ambil sampel Mikrokristal Selulosa pada konsentrasi H2SO4
2 N dengan data sebagai berikut.
Berat cawan Kosong (A) = 44,467g
Berat cawan Kosong + Sampel sebelum di oven (B) = 45,474g
Berat cawan Kosong + Sampel sesudah di oven (C) = 45,461g
Sehingga diperoleh perhitungan susut pengeringan :