Test Completion Date : Aug.06.2015 Receipt Date : Jul.24.2015 7_8F, CENTER1 Bldg, 26, Uljiro 5-gil, Jung-gu, Seoul, Korea Hanwha L&C Client : HAN MYEUNG HO Report No : TAC-003235 40, Yeongudanji-ro, Ochang-eup, Cheongwon-gun, Chungcheongbuk-do, 363-883 Rep. of KOREA TEL 82-43-211-6144 FAX 82-43-211-6148 Sample : Scagliola(HANEX) D-2 TEST RESULTS TEST ITEM UNIT SAMPLE RESULT TEST METHOD ASTM D792-13(Method A) 1.760 - - Specific Gravity((23/23) ℃) ASTM D785-08(Procedure A) 88 - - Rockwell Hardness(HRM) ASTM D638-14(*) 39.4 - MPa Tensile Strength ASTM D638-10(*) 10.8 - GPa Tensile Modulus of Elasticity ASTM D790-10(**) 65.2 - MPa Flexural Strength ASTM D790-10(**) 10.3 - GPa Flexural Modulus of Elasticity ASTM D256-10(Method A) 17 - J/m Izod Impact Strength ASTM D570-98(2010)e1 0.02 - % Water Absorption(24 h Immersion) ASTM D792-13(Method A) 1.755 - g/㎤ Density(23 ℃) JIS K 6902 : 2008 No Defects - - Heat Resistance Test JIS K 6902 : 2008 No Defects - - Hot Water Resistance Test ASTM D648-07(Method B) 111 - ℃ Deflection Temperature Under Load(1.82 MPa) JIS K 6911 : 2006 2.6×10 - 1/℃ Thermal Expansion * Specimen: Type I, Speed of Testing: 5 mm/min(Modulus: 1 mm/min) ** Speed of Testing: 5.1 mm/min, Support Span: 190 mm - Next Page - Reviewed by You Seok Technical Manager Tel: 1577-0091(ARS ①→④) Prepared by Cho Hyeong-gil E-mail: [email protected] Cho Hyeong-gil You Seok Korea Testing & Research Institute Aug.06.2015 2 1 of Total Page(s) President 전자문서본(Electronic Copy) QR Code to verify genuineness Electronic copy is for your reference only.