Ceramic lining pipe Kingcera offer optimized wear protection for plant components and pipe systems. Why wear protection?--- reduce costs and avoid downtime. Ceramic lining pipe: The kind of pipe composite three parts, the steel pipe glue and ceramic. The steel pipe is hot pressing, which is different to section welding bend. The ceramic tiles is 95% high alumina, and the glue is high temperature adhesive up to 100OC.This kind of bend are good for the powder transport and no tile fall off oraging working under 100OC for long time. The service life span is 4 to 5 times than normal steel pipe. Ceramic Specification: Item K-95 K-99 K-ZTA K-Z Ceramic wear material 94% alumina 98% alumina 80% alumina 99% zirconia Density 3.65 g/cm3 3.85 g/cm3 4.2 g/cm3 6.1 g/cm3 Porosity < 0.1 < 0.1 < 0.1 < 0.1 Compressive Strength ≥ 1700 Mpa ≥ 1800 Mpa ≥ 2100 Mpa ≥ 2400 Mpa Rockwell Hardness ≥ 85 HRA ≥ 86 HRA ≥ 90 HRA ≥ 88 HRA Vickers Hardness ≥ 1000 HV10 ≥ 1100 HV10 ≥ 1200 HV10 ≥ 1150 HV10 Fracture Toughness (KIC) ≥ 4.5 Mpa.m1/2 ≥ 4.8 Mpa.m1/2 ≥ 5.5 Mpa.m1/2 ≥ 7.5 Mpa.m1/2 Bending Strength ≥ 290 Mpa ≥ 290 Mpa ≥ 320 Mpa ≥ 360 Mpa Wear Volume ≤ 0.05 cm3 ≤ 0.01 cm3 ≤ 0.009 cm3 ≤ 0.007 cm3 ASTM G65 Relative Factor 9-11 9-11 11-14 12-15
This document is posted to help you gain knowledge. Please leave a comment to let me know what you think about it! Share it to your friends and learn new things together.
Transcript
Ceramic lining pipe
Kingcera offer optimized wear protection for plant components and pipe systems.
Why wear protection?--- reduce costs and avoid downtime.
Ceramic lining pipe:
The kind of pipe composite three parts, the steel pipe glue and ceramic. The steel pipe is hot pressing, which is different to
section welding bend. The ceramic tiles is 95% high alumina, and the glue is high temperature adhesive up to 100OC.This kind of
bend are good for the powder transport and no tile fall off oraging working under 100OC for long time. The service life span is 4