800 160 100:200 5 minutes Beige, black, not colored Polyols Isocyanates Adjustable to be white or black Viscometer Type BM Standard Hydrometer Standard Hydrometer Parts by weight Resin 100 g JIS K-7112 JIS K-6911 Izod V Notch JIS K-6911 JIS K-7207(18.5kg/cm 2 ) Clear pale yellow A Comp. B Comp. A Comp. B Comp. A Comp. 25℃ B Comp. Shore D Ivory 1.09 1.19 A:B 1 2 . 1 80-85 MPa 73 6 1 % 1790 kJ/m 2 12 3 . 0 % ℃-1 ℃ 6X 10 -5 0 0 1 ABS-LIKE VACUUM CASTING URETHANE FOR TECHNICAL PARTS AND PROTOTYPES BASIC PHYSICAL PROPERTIES Item Data Remarks Appearance Color of Finished Article Viscosity (mPa · s,25℃) Specific Gravity(25℃) Mixing Ratio Pot Life Hardness Tensile Strength Elongation Young’s modulus in flexure Impact strength Shrinkage Factor Coefficient of Thermal Expansion Specific Gravity of Finished Article V201506 25℃ MPa JIS K-7113 JIS K-7113 Deflection Temperature Under Load Viscometer Type BM JIS K-7171 78 Bending Strength MPa JIS K-7171 studiofathom.com | oakland 510.281.9000 | seattle 206.582.1062
7
Embed
ABS-LIKE - Fathom · 2021. 7. 1. · Hardness Tensile Strength Elongation Young’s modulus in flexure Impact strength Shrinkage Factor Coefficient of Thermal Expansion Specific Gravity
This document is posted to help you gain knowledge. Please leave a comment to let me know what you think about it! Share it to your friends and learn new things together.
Transcript
800
160
100:200
5 minutes
Beige, black, not colored Polyols
Isocyanates
Adjustable to be white or black
Viscometer Type BM
Standard Hydrometer
Standard Hydrometer
Parts by weight
Resin 100 g
JIS K-7112
JIS K-6911
Izod V Notch
JIS K-6911
JIS K-7207(18.5kg/cm2)
Clear pale yellow
A Comp.
B Comp.
A Comp.
B Comp.
A Comp.
25℃
B Comp.
Shore D
Ivory
1.09
1.19
A:B
12.1
80-85
MPa 73
61 %
1790
kJ/m2 12
3.0 %
℃-1
℃
6X 10-5
001
ABS-LIKE VACUUM CASTING URETHANEFOR TECHNICAL PARTS AND PROTOTYPES
CLEAR HIGH-TEMPVACUUM CASTING URETHANEFOR TECHNICAL PARTS AND PROTOTYPES
BASIC PROPERTIES
MECHANICAL PROPERTIES AT 23°C (1)
THERMAL & SPECIFIC PROPERTIES (1)
(1) Average values obtained on standard specimens/Hardening 4 hrs at 80°C + 16 hrs at 100°C(2) PX 522 is available in orange (PX 522HT OE Part B) and in red (PX 522HT RD Part B)
Composition UPX 5210POLYOL
UPX 5210-SPOLYOL MIXED
Mix ratio by weight 100 100
Aspect liquid liquid liquid
Colour Light blue - purple Transparent
Viscosity at 23°C (mPa.s) 600 - 800 600 - 800 500 - 650 Specific gravity at 23°C Specific gravity of cured product at 23°C
1.01 -
1.01 -
- 1.10
Pot life at 20 - 25°C on 100g (min)
Flexural modulus ISO 178 : 2001 MPa 2,000-2,2000
Flexural strength ISO 178 : 2001 MPa 90-95
Tensile strength ISO 527 : 1993 MPa 65-70
Elongation at break in tension ISO 527: 1993 % 15-20
Impact strength ISO 179/1 eU : 1994 kJ/m^2 60-70
Final hardness ISO 868 : 2003 Shore D 87
Glass temperature transition (Tg) ISO 11359 : 2002 °C 80
Heat deflection temperature ( HDT 1.8 MPa) ISO 75 Ae :1993 °C 100
Maximal casting thickness mm 50
Demoulding time at 70°C (thickness 3 mm) min. 60-90
TRANSPARENT RUBBER-LIKEVACUUM CASTING URETHANEFOR TECHNICAL PARTS AND PROTOTYPES
V20150607/09/18
BASIC PROPERTIES FOR A80, A70, AND A60. PHYSICAL PROPERTIES TESTED BY JIS K-7312Mixing Ratio
Hardness Shore A 80 70 60
Tensile Strength MPa 40 21 10
Elongation % 300 300 300
Tear Strength N/mm 44 28 28
S. G. ofFinished Article
g/cm³ 1.14 1.14 1.14
A : B : C 100 : 95 : 0 100 : 95 : 20 100 : 95 : 30
BASIC PROPERTIES FOR A50, A40, AND A30. PHYSICAL PROPERTIES TESTED BY JIS K-7312Mixing Ratio
Hardness Shore A 50 40 30
Tensile Strength MPa 4.0 2.0 1.5
Elongation % 270 300 260
Tear Strength N/mm 17 13 10
S. G. ofFinished Article
g/cm³ 1.15 1.16 1.16
A : B : C 100 : 95 : 80 100 : 95 : 150 100 : 95 : 200
BASIC PROPERTIESITEM
Product No.
Appearance
Color of Finished Article
Viscosity(mPa.s,25°C)
Specific Gravity(25°C)
Comp. A Colorless transparent Polyol (Freezes at temp. below 15°C)
Isocyanate
Polyol
Pale yellow transparent
Pale yellow transparent
Transparent
Viscometer Type BM
Standard Hydrometer
Comp. B
Comp. C
Comp. A 450
200
700
Comp. B
Comp. C
Comp. A 0.99
1.19
1.18
Comp. B
Comp. C
Pot Life 25°C 5 min. 30 sec. Resin 100g
T0387
VALUE REMARKS
(1) Cured material is transparent(2) Any desired hardness in a range from Shore A 30 to 80 can be obtained through the combined use of “component C” in different ratio.