LIDER w produkcji wyrobów z metali nieżelaznych
LIDERw produkcji wyrobówz metali nieżelaznych
Walcownia Metali Nieżelaznych”Łabędy” S.A.
ul. Metalowców 644-108 Gliwice
+48 32 33 06 [email protected]
LIDERw produkcji wyrobówz metali nieżelaznych
Leading Polish manufacturer of non-ferrous goods, including flat rolled products from
copper, copper alloys, casting alloys and silver.
WMN ” Łabędy” S.A. is member of capital group KGHM Polska Miedź S.A. > 100 years on the non-ferrous metals marketArea > 75.000 m2
3 production departments: foundry, strips department, sheets departmentLocation: Gliwice (Łabędy), Polska
>190 employees
COPPERSTRIPS AND SHEETS
NICKLE SILVERSTRIPS AND SHEETS
BRONZESTRIPS AND SHEETS
BRASSSTRIPS AND SHEETS
CASTING ALLOYS
ARMAMENTSINDUSTRY
CONSTRUCTION(INCLUDING ROOFING AND ARCHITECTURALELEMENTS)
AUTOMOTIVEINDUSTRY
ENERGY ELECTRONICS ENGINEERINGINDUSTRY
ELECTRICALENGINEERING TELECOMMUNICATIONS
CHEMICALINDUSTRY
ca 4500 tons annually ca 90 MLN PLN annually
EXAMPLES OF PRODUCTS
SUPPORTED INDUSTRIES
> 25 % export
PLN
GRADES
PN- 77/H-82120Foreign standard equivalents
PN-EN 1652 PN-EN 13599 DIN 1787 ASTM B152 JIS H3100 BS 2870 GOST
Cu99,9
M1E Cu-ETP, Cu-FRTP Cu-ETPE-Cu57, E-Cu58,
SE-CuC11000 C1100 C101 M1
M1R Cu-DLP SW-Cu C12000 C1201 - M1R
M2R Cu-DHP SF-Cu C12200 C1220 C106 M2R
Cu99,7 M2G - - - - - -
Cu99,95 - -Cu-HCP, Cu-PHC
- C10300 - - -
STRAIN HARDENING
1. Mechanical properties of strips as above-seen standards specified in table
above.
2. On the Customer's request strips are also available manufactured in the H
strain hardening.
3. After having agreed the recrystalization strain hardening
condition, strips of grain size determined by the Customer's can be manufactured.
4. On the Customer's request other strain hardenes strips are also manufactured.
Strain hardeningDesignation acc. to Foregin standard equivalents
PN-79/H-92710 PN-EN 1652 DIN 40500
ASTMB 152 M
BS2870
JISH 3100
1 2 3 4 5 6 7
hot rolled pg
recrystallized (anneled)
r R200/R220 F20 H00 0 0
recrystallized up to required grain size
W...
half - hard z4 R240 F25 H02 1/2H 1/2H
hard z6 R290/R360 F30/F37 H04 H H
STRIPSThickness (mm) Width (mm) Strain hardening Coil inside diameter (mm)
0,10 – 0,145 – 9
pz260, 360
10 – 310* 100, 200, 300, 400, 500
0,15 – 0,605 – 9
r, pz260, 360
10 – 310* 100, 200, 300, 400, 500
0,50 – 1,00 max 310*r, p
260, 300, 400, 500
1,00 – 3,00 max 310* 400, 500
* another width is possible in agreement with the Customer pz – state after cold rolling
COLD ROLLED SHEETS AND STRIPS
Thickness (mm) Width (mm) Length (mm) Strain hardening
0,30 – 2,192,20 – 10,00
max 310*max 1000
max 2500
r, pz
5,00 – 100,00** max 1000 pg
* another width is possible in agreement with the Customer pz – state after cold rolling **widht and lenght of plates after hot rolling with a thickness of 50 – 100 mm are also manufactured after previous agreement
COPPER STRIPS, SHEETS
www.wmn.com.pl
APPLICATION For example: ELECTRONICAL, ELECTROTECHNICAL, CHEMICAL AND ENGINEERING INDUSTRY, MOTORIZATION AND ARTISTIC METALWORK
GRADES
PN-92/H-87025Foreign standard equivalents
PN-EN 1652 PN-EN 1653* DIN 17660
ASTM B36 ASTM B 171* JIS H3100 BS 2870 GOST
M60 CuZn40 CuZn40 - C2801 - Ł60
M63 CuZn37, CuZn36 CuZn37, CuZn36 C27200 C2720 CZ108 Ł63
M67 CuZn33 CuZn33 C26800 C2680 CZ107 Ł68
M70 CuZn30 CuZn30 C26000 C2600 CZ106 Ł70
M80 CuZn20 CuZn20 C24000 C2400 CZ103 Ł80
M85 CuZn15 CuZn15 C23000 C2300 CZ102 Ł85
M90 CuZn10 CuZn10 C22000 C2200 CZ101 Ł90
M95 CuZn5 CuZn5 C21000 C2100 CZ125 Ł95
MO59* CuZn39Pb2* CuZn39Pb2* - C3560* CZ120* ŁS59-1*
MC62 / CuZn38Sn1* CuZn38Sn1* CuZn38Sn1* C46400* C4640* CZ112* -
*dimensions and strain hardening on request
STRAIN HARDENING
1. Mechanical properties of strips as above-seen standards
specified in table.
2. On the Customer’s request strips are also manufactured.
3. On the Customer's request strips of the H strain hardening
condition to DIN 17670 are also manufactured.
Grade Strain hardeningDesignation acc. to Foregin standard equivalents
PN-80/H-92816
PN-EN1652 DIN 17670 ASTM B 36 BS 2870
JISH 3100
1 2 3 4 5 6 7 8
CuZn10recrystallized (annealed)
half-hardhard
rz4z6
R240R280R350
F24F29F35
H02H04
01/2H
H
01/2H
H
CuZn15
recrystallized (annealed)recrystallized up to required grain size
half-hardhard
spring-hard
rW...z4z6z8
R260
R300R350R410
F26
F31F37F46
H02H04H06
0
1/2HH
0
1/2HH
CuZn20
recrystallized (annealed)recrystallized up to required grain size
half-hardhard
spring-hard
rW...z4z6z8
R270
R320R400R480
F27
F32F39
H02H04H06
0
1/2HH
0
1/2HH
CuZn30
recrystallized (annealed)recrystallized up to required grain size
half-hardhard
spring-hard
rW...z4z6z8
R270
R350R410R480
F27
F35F42F52
H02H04H06
0
1/2HH
0
1/2HH
EH
CuZn33
recrystallized (annealed)recrystallized up to required grain size
half-hardhard
spring-hard
rW...z4z6z8
R280
R350R420R500
F28
F36F43F53
H02H04H06
0
1/2HH
EH
0
1/2HH
EH
CuZn37
recrystallized (annealed)recrystallized up to required grain size
half-hardhard
spring-harddouble spring-hard
rW...z4z6z8z9
R300
R350R410R480R550
F30
F37F44F54F61
H02H04H06
0
1/2HH
EH
0
1/2HH
STRIPSThickness
(mm)Width(mm) Strain hardening
Coil inside diameter (mm)
0,10 – 0,605 – 9
r, pz260, 360
10 – 360 100, 200, 300, 400, 500
0,50 – 0,80 max 360r, pz
260, 300, 400, 500
0,80 – 3,00 max 360* 400*, 500
* the width is 380 mm for thickness above 2,50 mmpz – state after cold rolling
COLD ROLLED SHEETS AND STRIPS
Thickness (mm) Width(mm)Length(mm) Strain hardening
0,30 – 2,192,20 – 10,00
max 360max 1000 max 2500
r, pz
5,00 – 100,00* max 1000 pg
*width and lenght of plates after hot rolling with a thickness of 35 – 100 mm are also manufactured after agreement pz – state after cold rolling
BRASS STRIPS, SHEETS
www.wmn.com.pl
APPLICATION For example: ELECTRONICS, TELE-AND RADIO-ENGINEERING, MOTORIZATION AND ELECTROTECHNICAL INDUSTRY
GRADES
PN-92/H-87050Foreign standard equivalents
PN-EN 1652 DIN 17662 ASTM B103, B97 JIS H3110 BS 2870CuSn4 B4 CuSn4 CuSn4 C51100 C5111 PB101
CuSn6 B6 CuSn6 CuSn6 C51000 C5191 PB103
CuSn8 B8 CuSn8 CuSn8 C52100 C5212 -
PN-92/H-87060CuSi3Mn1 BK31 - - C65500 - C5101
STRAIN HARDENING
1. Mechanical properties of strips
and sheets standards specified in table.
2. On the Customer’s request strips
and plates in the other dimensional tolerances are also
manufactured.
Grade Strain hardening
Designation acc. to
PN-77/H-92815
Acc. to Polish Standard
PN-EN 1652
Foreign standard equivalents
DIN17670
ASTMB 103, B 97
BS2870
JISH3100
1 2 3 4 5 6 7 8
CuSn4
recrystallized (annealed)half – hard
hardspring - hard
R290R390R480R540
F33F38F47F54
060H02H04H06H08
01/2H
HEH
01/2H
HEH
CuSn6
recrystallized (annealed)half – hard
hardspring – hard
double spring - hard
rz4z6z8z9
R350R420R500R560R640
F35F41F48F55F63
060H02H04H06H08H10
01/2H
HEHSH
01/2H
HEH
CuSn8
recrystallized (annealed)half – hard
hardspring – hard
double spring - hard
rz4z6z8z9
R370R450R540R600R660
F37F45F54F59F66
060H02H04H06H08H10
01/2H
HEH
CuSi3Mn1
Hot rolled recystallized (annealed)
hardspring - hard
rz6z8
H70H04H08
STRIPSThickness (mm) Width (mm) Strain hardening Coil inside diameter (mm)
0,10 – 0,605 – 9
r, pz
260, 360
10 – 360 100, 200, 300, 400, 500
0,61 – 2,00 20 – 360 300, 400, 500
pz – state after cold rolling
COLD ROLLED SHEETS AND STRIPSGrade Thickness (mm) Width (mm) Length (mm) Strain hardening
CuSn4, CuSn6, CuSn8, CuSi3Mn1
0,20 – 5,00 max 360max 2000*
r, pz
CuSi3Mn1 5,00 – 30,00 max 600 pg
* for 2mm thickness – max lenght is 2500 mm pz – state after cold rolling
BRONZE STRIPS, SHEETS
www.wmn.com.pl
APPLICATION For example: ELECTRONICS, TELE-AND RADIO-ENGINEERING, MOTORIZATION AND ELECTROTECHNICAL INDUSTRY
GRADES
PN – 93/H-87027Foreign standard equivalents
PN-EN 1652 DIN 17663 DIN 17664* ASTM B122 BS 2870
CuNi18Zn27 MZN18 CuNi18Zn27 CuNi18Zn27 C77000 NS107
CuNi18Zn20 MZ20N18 CuNi18Zn20 CuNi18Zn20 C75200 NS106
CuNi12Zn24 MZN12 CuNi12Zn24 CuNi12Zn24 C76200 NS104
COPPER NICKEL
CuNi10Fe1Mn*
CuNi10Fe1Mn* C70600* CN 102*
*dimensions and strain hardening on request
STRAIN HARDENING
1. Mechanical properties of strips and sheets
standards specified in table.
2. On the Customer's request other strain hardened sheets and
strips are manufactured, for example the H strain hardened sheets acc. to
DIN 17670.
3. On the Customer's request other strain
hardened sheets and strips ale also
manufactured.
Grade Stain hardening
Designation acc. to
PN-77/H-92815
Acc. to Polish Standard
PN-EN 1652
Foreign standard equivalents
DIN 17670 ASTMB 122MBS
2870
1 2 3 4 5 6 7
CuNi18Zn27
recrystallized (annealed)half – hard
hardspring – hard
double spring - hard
rz4z6z8z9
R390R470R540R600R700
F39F47F54F60F70
H01H02H04H06H08
CuNi12Zn24
recrystallized (annealed)half – hard
hardspring – hard
double spring - hard
rz4z6z8z9
R360R430R490R550R620
F36F43F51F56F65
H01H02H04H06H08
01/2H
HEH
-
CuNi18Zn20
recrystallized (annealed)half – hard
hardspring – hard
double spring - hard
rz4z6z8z9
R380R450R500R580R640
F38F45F52F58F68
H01H02H04H06H08
01/2H
HEH
-
STRIPSThickness (mm) Width (mm) Strain hardening Coil inside diameter (mm)
0,10 – 0,605 – 9
r, pz
260, 360
10 – 350 100, 200, 300, 400, 500
0,61 – 2,00 20 – 350 300, 400, 500
pz – state after cold rolling
COLD ROLLED SHEETS AND STRIPSThickness (mm) Width (mm) Length (mm) Strain hardening
0,20 – 5,00 max 350 max 2000* r, pz
* for 2mm thickness – max lenght is 2500 mm pz – state after cold rolling
www.wmn.com.pl
NICKEL SILVER COPPER NICKEL STRIPS, SHEETS
APPLICATION For example: ELECTRONICS, TELE AND RADIO-ENGINEERING, METALWORK
CAST BRASS
Designation Grade acc. toPN-91/H-87026 FormDimensions (mm)
(thickness x width x length) Surface
CuZn34Al2Mn1Fe MA58 pig-sows 80 x 90 x 400
raw
CuZn39Pb2 MO59pig-sowsflat bars
80 x 90 x 40030 x 87 x 600
CuZn38Pb2 MM47 pig-sows 80 x 90 x 400
CuZn16Si3,5 MK80flat barspig-sows
30 x 87 x 60080 x 90 x 400
* There is a possibility of casting copper alloy according to Customer’s requirements
CAST BRONZE
Designation Grade acc. toPN-91/H-87026 FormDimensions (mm)
(thickness x width x length) Surface
CuSn10 B10flat barspig-sows
16 x 408 x 20080 x 90 x 400
raw
CuSn10P B101flat barspig-sows
16 x 408 x 20080 x 90 x 400
CuSn10Zn2 B102 pig-sows 80 x 90 x 400
CuSn12 B12flat barspig-sows
16 x 408 x 20080 x 90 x 400
CuSn16 B16 flat bars 12 x 200 x 1610
CuSn10Pb10 B 1010 pig-sows 80 x 90 x 400
CuSn5ZnPb5 B 555 flat barspig-sows
30 x 87 x 60080 x 90 x 400CuSn5ZnPb RG5
CuAl10Fe3Mn2 BA 1032 pig-sows 80 x 90 x 400
CuAl10Fe4Ni4 BA 1044 pig-sows 80 x 90 x 400
CuSi3Zn3Mn1 BK 331 pig-sows 80 x 90 x 400
* There is a possibility of casting copper alloy according to Customer’s requirements
INGOTS OF COPPER AND COPPER ALLOYSDesignation Grade Standard* Form Dimensions (mm) Surface
Cu-DHPCu-ETPCuZn37
CW 024 ACW 004 ACW 508 L
EN 12449 rollfi 115 x max 2700fi 128 x max 2700fi 205 x max 2700
raw
CuZn39Pb3CuZn40Pb2
CW 614 NCW 617 N
EN 12165 rollfi 115 x max 2700fi 128 x max 2700fi 205 x max 2700
raw
* There is a possibility of casting ingots from all grades mentioned in the standards above
CASTING ALLOYS
www.wmn.com.pl
CASTINGALLOYS
Casting alloys are manufactured in accordance with:- the standard PN, EN, DIN- the additional Customer’s requirements.
SPECIFICATIONGrades
acc. to ZN-WMŁ-002/97 Strain hardening Thickness (mm) Width (mm) Length (mm)
CuAl z6 0,50 – 2,00 max 400 900 - 1100
SPECIFICATION1. Strain hardening:r – soft statepz – state after cold rolling (hard)2. On the Customer’s request products in the other dimensional tolerances are also manufactured.3. There is a possibility of producing silver plates/anodes of the defined parameters on the customer’s request.
Grades acc. toPN-80/M-69411
Strain hardening acc. to PN-80/M-69411 Thickness (mm) Width (mm) Length (mm)
LS 25pz, r 0,50 – 2,00 max 400 max 500
LS 45
www.wmn.com.pl
BIMETAL SHEETS
SILVER FILLER METAL / SILVER SHEETS
APPLICATION For example: ELECTRONICS, CHEMICAL EQUIPMENT ELEMENTS AND ELEMENTS WORKING IN SEA WATER
APPLICATION For example: ELECTRONICS, FOR SOLDERING COPPER AND ITS ALLOY AS WELL AS CAST IRON AND CARBON AND LOW-ALLOY STEEL
Mechanical polishing sheets (grinding and polisching machine P-1200)
thickness 5 – 10 mm
width 650 – 1200 mm
length to 2000 mm
Annealing sheets in chamber furnace in 700 ºCwidth 1400 mm
length max 3000 mm
loading height 600 mm
Annealing strips in protective-atmosphere furnanceoutside diameter of coil max 1500 mm
inside diameter 100 – 600 mm
width 10 – 420 mm
weight of coll max 3000 kg
temeprature to 650 ºC
Straightening stripsthickness 0,15 – 0,80 mm
width 170 – 400 mm
weight of coil max 3000 kg
diameter of uncoiler 300, 600 mm
diameter of coiler 600 mm
Straightening sheetsthickness 0,50 – 11 mm
width 25 – 1300 mm
length min 500 – 2500 mm
Plasma cutting Cu alloythickness 5 – 50 mm
width 1200 mm
length to 2000 mm
Pickling in solution H2SO4 pickle tank size 3400 x 1100 x 1350 mm
Pickling in solution HCL pickle tank size 2750 x 1100 x 1250 mm
Cutting and slitting sheets and strips
Hot rolling ingost and cold rolling strips and sheets
Thermal cutting by cutting-off machine YUN with numerical control, equip with water-table
Oxycutting sheets from carbon steel and low-alloy steel
Plasma cutting sheets from high-alloy steel and non-ferrous metals
maximum size of working field 8000 x 2000 mm
thickness of oxygen-cutting 6 – 150 mm
thickness of plasma cutting 4 – 70 mm
SERVICES
www.wmn.com.pl
BROADBAND GRINDER WEBER
PARAMETERS:• Dimensions of grinded sheets: - max 1300 x 2500 x 50 mm - min 300 x 800 x 3 mm
• Maximum weight of workpiece 1500 kg
• Waviness tolerance +/- 3 mm
• Surface roughness dependent on applied abrasive paper
CIRCULAR SAW SCHELLING
PARAMETERS:• Cutting length max 3100 mm
• Cutting width max 1500 mm
• Cutting thickness from 3 to 60 mm
• Cutting tolerance: +/- 1 mm
LIDERw produkcji wyrobówz metali nieżelaznych
Walcownia Metali Nieżelaznych”Łabędy” S.A.
ul. Metalowców 644-108 Gliwice
+48 32 33 06 [email protected]
LIDERw produkcji wyrobówz metali nieżelaznych