Valve tests according to ISO 15848-1 (June 2015), VDI 2440 (November 2000), and user defined procedures SERVICE OFFER Issue: September 2016 amtec Messtechnischer Service GmbH, Hoher Steg 13, 74348 Lauffen, Germany Tel. +49 7133 9502-0, Fax +49 7133 9502-22, E-Mail: [email protected]; Internet: www.amtec.eu 1/4 Test according to ISO 15848-1 for isolating valves (CO1) - Valve size: max. DN150/PN250 bzw. DN250/PN25 - Assembly of the valve in the test rig - (1) Preliminary test at RT: Leakage measurement at the valve stem and the body seal - (2) 50 mechanical cycles at RT, leakage measurement at the valve stem - (3) Adjust test temperature, leakage measurement at the valve stem - (4) 50 mechanical cycles at test temperature, leakage measurement at the valve stem - (5) Cooling down to RT, leakage measurement at the valve stem - Repeat steps (2) to (4) - (6) Cooling down to RT, 5 mechanical cycles at RT, leakage measurement at the valve stem and the body seal Test according to ISO 15848-1 for isolating valves (Extension CO2) - Continuation of the test after finish CO1 - (2) 795 mechanical cycles at RT, leakage measurement at the valve stem - (3) Adjust test temperature, leakage measurement at the valve stem - (4) 500 mechanical cycles at test temperature, leakage measurement at the valve stem - (6) Cooling down to RT, leakage measurement at the valve stem and the body seal
26
Embed
Valve tests according to ISO 15848-1 (June 2015), VDI 2440 ... · Valve test procedure acc. to VDI 2440 ... test medium Helium, test pressure ... Compression test ASTM F36-15 (dated
This document is posted to help you gain knowledge. Please leave a comment to let me know what you think about it! Share it to your friends and learn new things together.
Transcript
Valve tests according to ISO 15848-1 (June 2015),
VDI 2440 (November 2000), and user defined procedures
SERVICE OFFER Issue: September 2016
amtec Messtechnischer Service GmbH, Hoher Steg 13, 74348 Lauffen, Germany
Test according to ISO 15848-1 for isolating valves (CO1) - Valve size: max. DN150/PN250 bzw. DN250/PN25 - Assembly of the valve in the test rig - (1) Preliminary test at RT: Leakage measurement at the valve
stem and the body seal - (2) 50 mechanical cycles at RT, leakage measurement at the
valve stem - (3) Adjust test temperature, leakage measurement at the valve
stem - (4) 50 mechanical cycles at test temperature, leakage
measurement at the valve stem - (5) Cooling down to RT, leakage measurement at the valve
stem - Repeat steps (2) to (4) - (6) Cooling down to RT, 5 mechanical cycles at RT, leakage
measurement at the valve stem and the body seal Test according to ISO 15848-1 for isolating valves (Extension CO2) - Continuation of the test after finish CO1 - (2) 795 mechanical cycles at RT, leakage measurement at
the valve stem - (3) Adjust test temperature, leakage measurement at the valve
stem - (4) 500 mechanical cycles at test temperature, leakage
measurement at the valve stem - (6) Cooling down to RT, leakage measurement at the valve
stem and the body seal
Valve tests according to ISO 15848-1 (June 2015),
VDI 2440 (November 2000), and user defined procedures
SERVICE OFFER Issue: September 2016
amtec Messtechnischer Service GmbH, Hoher Steg 13, 74348 Lauffen, Germany
Test according to ISO 15848-1 for isolating valves (Extension CO3) - Continuation of the test after finish CO2 - (2) 500 mechanical cycles at RT, leakage measurement at the
valve stem - (3) Adjust test temperature, leakage measurement at the valve
stem - (4) 500 mechanical cycles at test temperature, leakage
measurement at the valve stem - (6) Cooling down to RT, leakage measurement at the valve
stem and the body seal Test according to ISO 15848-1 for control valves (CC1) - Valve size: max. DN150/PN250 bzw. DN250/PN25 - Assembly of the valve in the test rig - (1) Preliminary test at RT: Leakage measurement at the valve
stem and the body seal - (2) 5,000 mechanical cycles at RT, leakage measurement at
the valve stem - (3) Adjust test temperature, leakage measurement at the valve
stem - (4) 5,000 mechanical cycles at test temperature, leakage
measurement at the valve stem - (5) Cooling down to RT, leakage measurement at the valve
stem - Repeat steps (2) to (4) - (6) Cooling down to RT, leakage measurement at the valve
stem and the body seal
Valve tests according to ISO 15848-1 (June 2015),
VDI 2440 (November 2000), and user defined procedures
SERVICE OFFER Issue: September 2016
amtec Messtechnischer Service GmbH, Hoher Steg 13, 74348 Lauffen, Germany
Test according to ISO 15848-1 for control valves (Extension CC2) - Continuation of the test after finish CC1 - (2) 20,000 mechanical cycles at RT, leakage measurement at
the valve stem - (3) Adjust test temperature, leakage measurement at the valve
stem - (4) 20,000 mechanical cycles at test temperature, leakage
measurement at the valve stem - (6) Cooling down to RT, leakage measurement at the valve
stem and the body seal Test according to ISO 15848-1 for control valves (Extension CC3) - Continuation of the test after finish CC2 - (2) 20,000 mechanical cycles at RT, leakage measurement at
the valve stem - (3) Adjust test temperature, leakage measurement at the valve
stem - (4) 20,000 mechanical cycles at test temperature, leakage
measurement at the valve stem - (6) Cooling down to RT, leakage measurement at the valve
stem and the body seal Valve test procedure acc. to VDI 2440 - Valve size: max. DN150/PN250 bzw. DN250/PN25 - Assembly of the valve in the test rig - Preliminary test at RT: short term leakage test - Heating up to max. 400 °C - Stem cycles at test temperature (1,000 pcs.) - Tightness test 24 hours, test medium Helium, test pressure
max 160 bar, - Disassembly after test - Evaluation of test results
Valve tests according to ISO 15848-1 (June 2015),
VDI 2440 (November 2000), and user defined procedures
SERVICE OFFER Issue: September 2016
amtec Messtechnischer Service GmbH, Hoher Steg 13, 74348 Lauffen, Germany
Additional options for valve tests acc. to VDI 2440 - Additional stem cycles, 1,000 pcs. - Additional temperature cycle - Additional leakage measurement 24 h test medium Helium,
test pressure max 160 bar, - Additional charge medium nitrogen - Additional charge medium methane Preparation - of the valve (vacuum chamber, connection to the actuator,
flange sealings, mounting temperature sensors) - of the test rig (gas connection, heating, isolation) Test Report - documentation of the boundary conditions - compilation of the test results - english or german Certificate / Confirmation - only in conjunction with a test report - same language as test report Special tests, Leakage tests and long term tests on request.
Gasket testing according to DIN 28090, DIN 3535, DIN 52913, EN 13555, VDI 2440, ASTM, Shell
DIN 28090-1 (withdrawn – replaced by DIN EN 13555) - compression tests, creep compression tests, creep-/relaxation tests and leakage tests on request
DIN 28090-2 (dated November 2014) - compressive creep test
compression modulus at ambient temperature (εKSW) percentage creep relaxation at ambient temperature (εKRW) compression modulus at elevated temperature (εWSW,T) percentage creep relaxation at elevated temperature (εWRW,T) short test long term test
DIN 3535-6 (dated Ja nuary 2011) - leakage test
single test triple test
DIN 52913 (dated April 2002) - compression creep test
compression creep strength (σdE/16) single test triple test
VDI 2440 (dated November 2000) - leakage test – TA-Luft
VDI 2200 (dated June 2007) - leakage test – safety against blow-out
Gasket testing according to DIN 28090, DIN 3535, DIN 52913, EN 13555, VDI 2440, ASTM, Shell
DIN EN 13555 (dated July 2014) - compression test at ambient temperature
determination of the characteristics QSMAX and EG at ambient temperature
- compression test at elevated temperature T (≤ 400 °C) determination of the characteristics QSMAX and EG at elevated temperature
- creep-/relaxation test at ambient temperature determination of the characteristic PQR
- creep-/relaxation test at elevated temperature – T (≤ 400 °C) determination of the characteristic PQR - leakage test
1 internal pressure level diagram for increasing gasket stress (QMIN/L) diagram for decreasing gasket stress (QSMIN/L)
- gasket characteristics for one gasket material:
Leakage test at 1 pressure level, Compression tests at ambient and 2 elevated temperatures, creep relaxations tests at 3 different stress levels and 3 temperatures, test report single test (13 tests) double test (26 tests)
BS 7531 (dated 2006) - compressibility test Triple test - residual stress test Double test - gas permeability test Triple test
Gasket testing according to DIN 28090, DIN 3535, DIN 52913, EN 13555, VDI 2440, ASTM, Shell
MESC SPE 85/300 (dated September 2012) - 3.3.2 Fugitive Emissions
leakage test – RT leakage test - T (≤ 400 °C)
- 3.3.3 Fire Test API 6FB (dated 1998)
- 3.3.4 Room Temperature Operation Tightness Test (ROTT) According to EN 13555 (dated July 2014) compression test - RT compression test – T (≤ 400 °C) creep-/ relaxation test – RT creep-/ relaxation test – T (≤ 400 °C) leakage test
- 3.3.5 High Temperature Operational Tightness Test (HOTT) leakage test with thermal cycles (T≤ 400 °C)
- 3.3.6 Hot Blowout Test leakage test (T≤ 400 °C)
- 3.3.11 Cold Compression / Hot Recovery Test Compression test ASTM F36-15 (dated 2015)
- 3.3.12 Leak Test leakage test ASTM F37-06 (dated 2013 – test method B)
- 3.3.13 Gasket Adhesion
Gasket testing according to DIN 28090, DIN 3535, DIN 52913, EN 13555, VDI 2440, ASTM, Shell
certificate/ confirmation englisch test report englisch High temperature tests (up to 600 °C) on request. High pressure test up to 500 bar on request. Special tests, leakage tests and long term tests on request. Tests according to API 6FB, FAS-G-605-11, ASTM F1574-03a und ASTM F2837-11 are not part of the accreditation.
Tests on Stuffing Box Packings according to VDI 2440, API 622,
and user defined procedures
SERVICE OFFER Issue: September 2016
amtec Messtechnischer Service GmbH, Hoher Steg 13, 74348 Lauffen, Germany
Compression Test - Packing ring Ø 60 x 80 x 10 mm - Determination of the compressibility of a packing ring - Determination of the transmission factor Kinner and Kouter Friction Test - Packing geometry:
Ø 28.2 x 19 mm or Ø 41 x 25 mm or Ø 48 x 32 mm or Ø 56 x 40 mm (standard) or Ø 75 x 55 mm (max stress. 50 MPa)
- Assembly - Prestressing regarding to customers specification - Heating up to max. 400 °C - 100 stem cycles at elevated temperature - Determination of the friction factor µ*k Leakage Test - Packing geometry:
Ø 28.2 x 19 mm or Ø 41 x 25 mm or Ø 48 x 32 mm or Ø 56 x 40 mm (standard) or Ø 75 x 55 mm (max stress. 50 MPa)
- Assembly - Prestressing regarding to customers specification - Leakage test 24 hours, medium Helium, internal pressure level
of max. 160 bar
Tests on Stuffing Box Packings according to VDI 2440, API 622,
and user defined procedures
SERVICE OFFER Issue: September 2016
amtec Messtechnischer Service GmbH, Hoher Steg 13, 74348 Lauffen, Germany
Packing test according to VDI 2440 (dated November 2000) Standard leakage test - Packing geometry
Ø 28.2 x 19 mm or Ø 41 x 25 mm or Ø 48 x 32 mm or Ø 56 x 40 mm (standard) or Ø 75 x 55 mm (max stress. 50 MPa)
- Assembly - Prestressing regarding to customers specification - Functional testing (short leakage test with test medium) - Heating up to max. 400 °C - 100 stem cycles at elevated temperature - Leakage test 24 hours, medium Helium, internal pressure level
of max. 160 bar - Cooling-down to ambient temperature Option s - Additional 100 stem cycles - Additional Temperature up to max. 400 °C - Additional leakage test 24 hours, medium Helium - Additional charge medium nitrogen - Additional charge medium methane
Tests on Stuffing Box Packings according to VDI 2440, API 622,
and user defined procedures
SERVICE OFFER Issue: September 2016
amtec Messtechnischer Service GmbH, Hoher Steg 13, 74348 Lauffen, Germany
Packing Testing according to API 622 (dated October 2011) A Fugitive Emission Test - Packing geometry
Ø 28.2 x 19 mm or Ø 41 x 25 mm or Ø 48 x 32 mm or Ø 56 x 40 mm (standard) or Ø 75 x 55 mm (max stress. 50 MPa)
- Assembly - Prestressing regarding to customers specification - Duration: 6 days - Per day: 1 Temperature cycle – 125 stem cycles at RT, 125
stem cycles at T, 1 pressure cycle, leakage measurement every 50 stem cycles
- Medium: Methane B Corrosion Test - Corrosion test at RT, packing stress 30 MPa, duration 28 days - Corrosion test at 150 °C, packing stress 30 MPa, water
pressure: 45 bar, duration 35 days C Packing Materials Test Test Report Certificate Special tests, leakage tests and long term tests on request.
amtec Messtechnischer Service GmbH, Hoher Steg 13, 74348 Lauffen
Armaturenprüfungen nach DIN EN ISO 15848-1 (November 2015), VDI 2440 (November 2000) und benutzerdefinierten Abläufen
LEISTUNGSANGEBOT Stand: September 2016
Prüfung nach ISO 15848 -1 für Absperrventile (CO1) - Armaturengröße: max. DN150/PN250 bzw. DN250/PN25 - Einbau der Armatur in den Prüfstand - (1) Vorversuch bei RT: Leckagemessung an der
Stopfbuchspackung und an der Gehäusedeckeldichtung - (2) 50 mechanische Zyklen bei RT, Leckagemessung an der
Stopfbuchspackung - (3) Aufheizen auf Prüftemperatur, Leckagemessung an der
Stopfbuchspackung - (4) 50 mechanische Zyklen unter Temperatur,
Leckagemessung an der Stopfbuchspackung - (5) Abkühlen auf RT, Leckagemessung an der
Stopfbuchspackung - Wiederholung der Schritte (2) bis (4) - (6) Abkühlen auf RT, 5 mechanische Zyklen,
Leckagemessung an der Stopfbuchspackung und an der Gehäusedeckeldichtung
Prüfung nach ISO 15848 -1 für Absperrventile (Erweiterung CO2) - Fortsetzung des Versuches nach Abschluss CO1 - (2) 795 mechanische Zyklen bei RT, Leckagemessung an der
Stopfbuchspackung - (3) Aufheizen auf Prüftemperatur, Leckagemessung an der
Stopfbuchspackung - (4) 500 mechanische Zyklen unter Temperatur,
Leckagemessung an der Stopfbuchspackung - (6) Abkühlen auf RT, Leckagemessung an der
Stopfbuchspackung und an der Gehäusedeckeldichtung
Armaturenprüfungen
LEISTUNGSANGEBOT September 2016
amtec Messtechnischer Service GmbH, Hoher Steg 13, 74348 Lauffen
Prüfung nach ISO 15848 -1 für Absperrventile (Erweiterung CO3) - Fortsetzung des Versuches nach Abschluss CO2 - (2) 500 mechanische Zyklen bei RT, Leckagemessung an der
Stopfbuchspackung - (3) Aufheizen auf Prüftemperatur, Leckagemessung an der
Stopfbuchspackung - (4) 500 mechanische Zyklen unter Temperatur,
Leckagemessung an der Stopfbuchspackung - (6) Abkühlen auf RT, Leckagemessung an der
Stopfbuchspackung und an der Gehäusedeckeldichtung
Prüfung nach ISO 15848 -1 für Regelventile (CC1) - Armaturengröße: max. DN150/PN250 bzw. DN250/PN25 - Einbau der Armatur in den Prüfstand - (1) Vorversuch bei RT: Leckagemessung an der
Stopfbuchspackung und an der Gehäusedeckeldichtung - (2) 5000 mechanische Zyklen bei RT, Leckagemessung an
der Stopfbuchspackung - (3) Aufheizen auf Prüftemperatur, Leckagemessung an der
Stopfbuchspackung - (4) 5000 mechanische Zyklen unter Temperatur,
Leckagemessung an der Stopfbuchspackung - (5) Abkühlen auf RT, Leckagemessung an der
Stopfbuchspackung - Wiederholung der Schritte (2) bis (4) - (6) Abkühlen auf RT, Leckagemessung an der
Stopfbuchspackung und an der Gehäusedeckeldichtung
Armaturenprüfungen
LEISTUNGSANGEBOT September 2016
amtec Messtechnischer Service GmbH, Hoher Steg 13, 74348 Lauffen
Prüfung nach ISO 15848 -1 für Regelventile (Erweiterung CC2) - Fortsetzung des Versuches nach Abschluss CC1 - (2) 20000 mechanische Zyklen bei RT, Leckagemessung an
der Stopfbuchspackung - (3) Aufheizen auf Prüftemperatur, Leckagemessung an der
Stopfbuchspackung - (4) 20000 mechanische Zyklen unter Temperatur,
Leckagemessung an der Stopfbuchspackung - (6) Abkühlen auf RT, Leckagemessung an der
Stopfbuchspackung und an der Gehäusedeckeldichtung
Prüfung nach ISO 15848 -1 für Regel ventile (Erweiterung CC3) - Fortsetzung des Versuches nach Abschluss CC2 - (2) 20000 mechanische Zyklen bei RT, Leckagemessung an
der Stopfbuchspackung - (3) Aufheizen auf Prüftemperatur, Leckagemessung an der
Stopfbuchspackung - (4) 20000 mechanische Zyklen unter Temperatur,
Leckagemessung an der Stopfbuchspackung - (6) Abkühlen auf RT, Leckagemessung an der
Stopfbuchspackung und an der Gehäusedeckeldichtung
Armaturenprüfung nach VDI 2440 - Armaturengröße: max. DN150/PN250 bzw. DN250/PN25 - Einbau der Armatur in den Prüfstand - Funktionstest (Kurzeitleckageversuch mit Prüfmedium) - Aufheizen auf max. 400 °C - Mechanische Zyklen unter Temperatur (1000 Zyklen) - Dichtheitstest 24 Stunden, Prüfmedium Helium, Prüfdruck
max. 160 bar - Abkühlen auf Raumtemperatur
Armaturenprüfungen
LEISTUNGSANGEBOT September 2016
amtec Messtechnischer Service GmbH, Hoher Steg 13, 74348 Lauffen
DIN 28090-1 (zurückgezogen – wurde ersetzt durch DIN EN 13555) - Stauchversuche, Druckstandversuche, Kriech-/Relaxationsversuche und Leckageversuche auf Anfrage
DIN 28090-2 (Ausgabe November 2014) - Verformungsverhalten
DIN EN 13555 (Ausgabe Juli 2014) - Stauchversuch - RT
Bestimmung der Kennwerte Qsmax und EG bei Raumtemperatur - Stauchversuch – T (≤ 400 °C) Bestimmung der Kennwerte Qsmax und EG bei erhöhter Temperatur - Kriech-/Relaxationsversuch – RT Bestimmung der Kennwerte PQR und ∆eGc - Kriech-/Relaxationsversuch – T (≤ 400 °C) Bestimmung des Kennwertes PQR und ∆eGc - Leckageversuch 1 Druckstufe Belastungskurve (QMIN/L) Entlastungskurve (QSMIN/L) - Kennwertermittlung für ein Dichtungsmaterial:
Leckageversuch bei 1 Druckstufe, Stauchversuch bei RT und 2 erhöhten Temperaturen, Relaxationsversuch bei 3 Flächenpressungen und 3 Temperaturen, Prüfbericht 13 Versuche für Einfachprüfung 26 Versuche für Doppelprüfung
MESC SPE 85/300 (Ausgabe September 2012) - 3.3.2 Fugitive Emissions
Leckageversuch – RT Leckageversuch - T (≤ 400 °C)
- 3.3.3 Fire Test API 6FB (Ausgabe 1998)
- 3.3.4 Room Temperature Operation Tightness Test (ROTT) nach DIN EN 13555 (Ausgabe Juli 2014) Stauchversuch - RT Stauchversuch – T (≤ 400 °C) Kriech-/Relaxationsversuch – RT Kriech-/Relaxationsversuch – T (≤ 400 °C) Leckageversuch
- 3.3.5 High Temperature Operational Tightness Test (HOTT) Leckageversuch mit Temperaturzyklen (T≤ 400 °C)
- 3.3.6 Hot Blowout Test Leckageversuch (T≤ 400 °C)
- 3.3.11 Cold Compression / Hot Recovery Test Stauchversuch ASTM F36-15 (Ausgabe 2015)
- 3.3.12 Leak Test Leckageversuch ASTM F37-06 (Ausgabe 2013 – Methode B)
- 3.3.13 Gasket Adhesion
Dichtungsprüfungen nach DIN 28090, DIN 3535, DIN 52913, EN 13555, VDI 2440, VDI 2200, ASTM, Shell
LEISTUNGSANGEBOT Stand: September 2016
amtec Messtechnischer Service GmbH, Hoher Steg 13, 74348 Lauffen
Zertifikat/ Bescheinigung deutsch englisch Prüfbericht deutsch englisch Temperaturversuche bis max. 600 °C auf Anfrage. Hochdruckleckagevesuche bis max. 500 bar auf Anfrage. Sonderprüfungen, Dichtheitstest, Langzeitversuche auf Anfrage. Prüfungen nach API 6FB, FAS-G-605-11, ASTM F1574-03a und ASTM F2837-11 sind nicht im Akkreditierungsumfang enthalten.
Packungsprüfungen nach VDI 2440, API 622 und benutzerdefinierten Abläufen
Ermittlung von Packungskennwerten
LEISTUNGSANGEBOT Stand: September 2016
amtec Messtechnischer Service GmbH, Hoher Steg 13, 74348 Lauffen,
Stauchversuch - Packungsring Ø 60 x 80 x 10 mm - Ermittlung der Kraft-Verformungskennlinie bei
Raumtemperatur - Ermittlung der Umlenkfaktoren Kinnen und Kaußen
Reibversuch - Packungsgeometrie:
Ø 28.2 x 19 mm oder Ø 41 x 25 mm oder Ø 48 x 32 mm oder Ø 56 x 40 mm (standard) oder Ø 75 x 55 mm
- Montage in den Prüfraum - Verspannen nach Kundenvorgabe - Aufheizen auf max. 400 °C - 100 mechanische Zyklen unter Temperatur - Bestimmung des Faktors µ*k
Leckage versuch - Packungsgeometrie:
Ø 28.2 x 19 mm oder Ø 41 x 25 mm oder Ø 48 x 32 mm oder Ø 56 x 40 mm (standard) oder Ø 75 x 55 mm
- Montage in den Prüfraum - Verspannen nach Kundenvorgabe - Leckageversuch 24 Stunden, Prüfmedium Helium, Prüfdruck
max. 160 bar
Packungsprüfungen nach VDI 2440, API 622 und benutzerdefinierten Abläufen
Ermittlung von Packungskennwerten
LEISTUNGSANGEBOT Stand: September 2016
amtec Messtechnischer Service GmbH, Hoher Steg 13, 74348 Lauffen,
Packungsprüfung nach VDI 2440 (Ausgabe November 2000) Leackageversuch - Packungsgeometrie
Ø 28.2 x 19 mm oder Ø 41 x 25 mm oder Ø 48 x 32 mm oder Ø 56 x 40 mm (standard) oder Ø 75 x 55 mm (max. Flächenpressung 50 MPa)
- Montage in den Prüfraum - Verspannen nach Kundenvorgabe - Funktionstest (Kurzeitleckageversuch mit Prüfmedium) - Aufheizen auf max. 400 °C - 100 mechanische Zyklen unter Temperatur - Leckageversuch 24 Stunden, Prüfmedium Helium, Prüfdruck
max. 160 bar - Abbkühlen auf Raumtemperatur
Zusatzoptionen - Zusätzliche 100 Spindelhübe - Zusätzlicher Temperaturzyklus bis max. 400 °C - Zusätzliche Leckagemessung 24 Stunden, Prüfmedium