Page 1: tugas korosi 1

KOROSIANDI NINA ASRIANA14142-01-007

MK. ANALISIS KOROSIDOSEN PENGAMPU: SUPRAPTO PhD

Page 2: tugas korosi 1

PENGERTIAN

KOROSI: PENURUNAN KUALITAS LOGAM KARENA REAKSI DENGAN LINGKUNGAN

Page 3: tugas korosi 1

Penggolongan Korosi:

1. Uniform/general attack (korosi umum)

2. Galvanic corrosion (korosi galvanis)

3. Crevice corrosion (korosi celah)

4. Pitting corrosion (korosi sumur)

5. Intergranular corrosion (korosi batas butir)

6. Selective leaching (korosi selectif)

7. Erosion corrosion (korosi erosi)

8. Stress corrosion (korosi tegangan)

Page 4: tugas korosi 1

1. Uniform/general attack (korosi umum)⇒ Korosi yang umum terjadi pada baja.

⇒ Akibat adanya reaksi kimia atau elektro kimia yang merata

pada permukaan logam

Page 5: tugas korosi 1

2. Galvanic corrosion (korosi galvanis)

Terjadi akibat adanya beda potensial antara dua benda yang terhubung secara elektrolit.

Logam yang ketahanan korosinya kurang: anodik

logam yang ketahanan korosinya tinggi : katodik

Page 6: tugas korosi 1

3. Crevice corrosion (korosi celah)

Korosi lokal yang sering terjadi pada celah atau daerah yang dilindungi.

Penyebabnya: adanya larutan yang terjebak pada lubang dari permukaan gasket, lap joint, atau kotoran yang terjebak dibawah baut atau pada kepala rivet.

Pencegahannya: sangat sulit. Cara lain dengan mengkondisikan dalam kelembaban yan rendah (low humadity)

Daerah yang kemungkinan terkena korosi.

Cara pencegahannya.

Page 7: tugas korosi 1

4. Pitting corrosion (korosi sumur)

Serangan korosi mengakibatkan terjadinya lubang-lubang pada logam. Diameter lubang relatif kecil.

Jenis korosi yang sangat berbahaya karena sulit untuk mendeteksi dan mengukurnya secara kuantitatif.

Pencegahannya dengan memilih material yang tahan terhadap korosi sumur.

Page 8: tugas korosi 1

5. Intergranular corrosion (korosi batas butir)

Korosi yang terjadi akibat adanya :

ketidakmurnian di batas butir.

bertambahnya salah satu dari elemen paduan di batas butir.

pengurangan salah satu elemen paduan di batas butir.

Contoh peristiwa sensitasi (sensitizing).

Page 9: tugas korosi 1

6. Selective leaching (korosi selectif)

Penghilangan satu elemen dari suatu paduan padat melalui proses korosi.

Contoh: 1. Penghilangan Zn pada paduan brass (kuningan)

2. Penghilangan Al, atau Co atau Fe atau Cr dari

paduannya.

Page 10: tugas korosi 1

7. Erosion corrosion (korosi erosi)

Proses korosi yang dipercepat dengan adanya gesekan antara fluida korosif dengan permukaan logam.

Page 11: tugas korosi 1

8. Stress corrosion (korosi tegangan)

Sering juga disebut stress corrosion cracking, yaitu retak (crack) yang disebabkan oleh tegangan tarik (tensile stress) dan korosi yang spesifik. Contoh : hydrogen embrittlement

Pencegahannya:

• proteksi katodik,

• menurunkan beban/tegangan yang bekerja,

• menghilangkan zat-zat yang korosif,

• pelapisan (coating),

• shot-peening atau shot-blasting untuk menghasilkan

tegangan sisa tekan.

Page 12: tugas korosi 1

Metals and Alloys

No Environment Proper material

1 Nitric acid Stainless steels

2 Caustic Nickel and nickel alloys

3 Hydrofluoric acid Monel (Ni-Cu)

4 Hot hydrochloric acid

Hastelloys (Ni-Cr-Mo) (Chlorimets)

5 Dilute sulfuric acid Lead

Page 13: tugas korosi 1

No Environment Proper material

6 Nonstaining atmospheric

exposure

Aluminium

7 Distilled water Tin

8 Hot strong oxidizing solution

Titanium

9 Ultimate resistance Tantalum

10 Concentrated sulfuric acid

Steel

Page 14: tugas korosi 1

E.g : Stainless Steels

Stainless steels are iron base alloys that contain a minimum of approximately 11% Cr, the amount needed to prevent the formation of rust in unpolluted atmosphere.

wt.% Cr

Dis

solu

tio

n r

ate,

cm

/sec

Page 15: tugas korosi 1

Alloying elements of stainless steel : Other than Ni, Cr and C, the following alloying

elements may also present in stainless steel: Mo, N, Si, Mn, Cu, Ti, Nb, Ta and/or W.

Main alloying elements (Cr, Ni and C):

1. Chromium Minimum concentration of Cr in a stainless steel is 12-14wt.% Structure : BCC (ferrite forming element)

* Note that the affinity of Cr to form Cr-carbides is very

high. Chromium carbide formation along grain boundaries may induce intergranular corrosion.

Page 16: tugas korosi 1

Binary diagram of Fe-Cr

Sigma phase formation which is initially formed at grain boundaries has to be avoided because it will increase hardness, decrease ductility and notch toughness as well as reduce corrosion resistance.

Page 17: tugas korosi 1

2. Nickel

Structure: FCC (austenite forming element/stabilize austenitic structure)

Added to produce austenitic or duplex stainless steels. These materials possess excellent ductility, formability and toughness as well as weld-ability.

Nickel improves mechanical properties of stainless steels servicing at high temperatures.

Nickel increases aqueous corrosion resistance of materials.

Page 18: tugas korosi 1

Ternary diagram of Fe-Cr-Ni at 6500 and 10000C

AISI : American Iron and Steel Institute

Page 19: tugas korosi 1

Anodic polarization curves of Cr, Ni and Fe in 1 N H2SO4 solution

Page 20: tugas korosi 1

Influence of Cr on corrosion resistance of iron base alloy

Page 21: tugas korosi 1

Influence of Ni on corrosion resistance of iron base alloy

Page 22: tugas korosi 1

Influence of Cr on iron base alloy containing 8.3-9.8wt.%Ni

Page 23: tugas korosi 1

3. Carbon

Very strong austenite forming element (30x more effective than Ni). I.e. if austenitic stainless steel 18Cr-8Ni contains ≤0.007%C, its structure will convert to ferritic structure. However the concentration of carbon is usually limited to ≤ 0.08%C (normal stainless steels) and ≤0.03%C (low carbon stainless steels to avoid sensitization during welding).

Page 24: tugas korosi 1

Minor alloying elements :

Manganese Austenitic forming element. When necessary can be

used to substitute Ni. Concentration of Mn in stainless steel is usually 2-3%.

Molybdenum Ferritic forming element. Added to increase pitting

corrosion resistance of stainless steel (2-4%). Molybdenum addition has to be followed by

decreasing chromium concentration (i.e. in 18-8SS has to be decreased down to 16-18%) and increasing nickel concentration (i.e. has to be increased up to 10-14%).

Improves mechanical properties of stainless steel at high temperature. Increase aqueous corrosion resistance of material exposed in reducing acid.

Page 25: tugas korosi 1

Tungsten Is added to increase the strength and toughness

of martensitic stainless steel.

Nitrogen (up to 0.25%)Stabilize austenitic structure. Increases strength

and corrosion resistance. Increases weld ability of duplex SS.

Titanium, Niobium and TantalumTo stabilize stainless steel by reducing susceptibility

of the material to intergranular corrosion. Ti addition > 5x%C. Ta+Nb addition > 10x%C.

Page 26: tugas korosi 1

CopperIs added to increase corrosion resistance of

stainless steel exposed in environment containing sulfuric acid.

Silicon Reduce susceptibility of SS to pitting and crevice

corrosion as well as SCC.

Page 27: tugas korosi 1

Five basic types of stainless steels :

Austenitic - Susceptible to SCC. Can be hardened by only by cold working. Good toughness and formability, easily to be welded and high corrosion resistance. Nonmagnetic except after excess cold working due to martensitic formation.

Martensitic - Application: when high mechanical strength and wear resistance combined with some degree of corrosion resistance are required. Typical application include steam turbine blades, valves body and seats, bolts and screws, springs, knives, surgical instruments, and chemical engineering equipment.

Ferritic - Higher resistance to SCC than austenitic SS. Tend to be notch sensitive and are susceptible to embrittlement during welding. Not recommended for service above 3000C because they will loss their room temperature ductility.

Page 28: tugas korosi 1

Duplex (austenitic + ferritic) – has enhanced resistance to SCC with corrosion resistance performance similar to AISI 316 SS. Has higher tensile strengths than the austenitic type, are slightly less easy to form and have weld ability similar to the austenitic stainless steel. Can be considered as combining many of the best features of both the austenitic and ferritic types. Suffer a loss impact strength if held for extended periods at high temperatures above 3000C.

Precipitation hardening - Have the highest strength but require proper heat-treatment to develop the correct combination of strength and corrosion resistance. To be used for specialized application where high strength together with good corrosion resistance is required.

Page 29: tugas korosi 1
Page 30: tugas korosi 1
Page 31: tugas korosi 1
Page 32: tugas korosi 1
Page 33: tugas korosi 1
Page 34: tugas korosi 1
Page 35: tugas korosi 1
Page 36: tugas korosi 1

Stress Corrosion Cracking of Stainless Steel

Stress corrosion cracking (SCC) is defined as crack nucleation and propagation in stainless steel caused by synergistic action of tensile stress, either constant or slightly changing with time, together with crack tip chemical reactions or other environment-induced crack tip effect.

SCC failure is a brittle failure at relatively low constant tensile stress of an alloy exposed in a specific corrosive environment.

However the final fracture because of overload of remaining load-bearing section is no longer SCC.

Page 37: tugas korosi 1

Three conditions must be present simultaneously to produce SCC:

- a critical environment - a susceptible alloy - some component of tensile

stress

Page 38: tugas korosi 1

Tensile stress

Corrosive environment

Susceptible material

Stress corrosion cracking

Tensile stress is below yield point

Corrosive environment is often specific to the alloy system

Pure metals are more resistance to SCC but not immune and susceptibility increases with strength

Page 39: tugas korosi 1

Typical micro cracks formed during SCC of sensitized AISI 304 SS

Surface morphology

Page 40: tugas korosi 1

Example of crack propagation during transgranular stress corrosion cracking (TGSCC)

brass

Page 41: tugas korosi 1

Example of crack propagation during intergranular stress corrosion cracking (IGSCC) ASTM A245 carbon steel

Page 42: tugas korosi 1

Fracture surface of transgranular SCC on austenitic stainless steel in hot chloride solution

Fracture surface of intergranular SCC on carbon steel in hot nitric solution

Page 43: tugas korosi 1

Fracture surface due to intergranular SCC

Fracture surface due to local stress has reached its tensile strength value on the remaining section

Page 44: tugas korosi 1

Electrochemical effect

pitting

passive

active

cracking zones

Usual region for TGSCC, mostly is initiated by pitting corrosion (transgranular cracking propagation needs higher energy)

Usual region for IGSCC, SCC usually occurs where the passive film is relatively weak

Zone 1

Zone 2

Page 45: tugas korosi 1

Note that non-susceptible alloy-environment combinations, will not crack the alloy even if held in one of the potential zones.

Temperature and solution composition (including pH, dissolved oxidizers, aggressive ions and inhibitors or passivators) can modify the anodic polarization behavior to permit SCC.

Susceptibility to SCC cannot be predicted solely from the anodic polarization curve.

Page 46: tugas korosi 1

Models of stress corrosion cracking

Slip step dissolution model Discontinuous intergranular crack growth Crack nucleation by rows of corrosion

micro-tunnels Absorption induced cleavage Surface mobility (atoms migrate out of

the crack tips) Hydrogen embrittlement→HIC

Page 47: tugas korosi 1

Control/prevention :

Reduce applied stress level Remove residual tensile stress (internal

stress) Lowering oxidizing agent and/or critical

species from the environment Add inhibitor Use more resistant alloys Cathodic protection

Page 48: tugas korosi 1

Alteration of Environment

Typical changes in medium are : Lowering temperature – but there are cases

where increasing T decreases attack. E.g hot, fresh or salt water is raised to boiling T and result in decreasing O2 solubility with T.

Decreasing velocity – exception ; metals & alloys that passivate (e.g stainless steel) generally have better resistance to flowing mediums than stagnant. Avoid very high velocity because of erosion-corrosion effects.

Page 49: tugas korosi 1

Removing oxygen or oxidizers – e.g boiler feedwater was deaerated by passing it thru a large mass of scrap steel. Modern practice – vacuum treatment, inert gas sparging, or thru the use of oxygen scavengers. However, not recommended for active-passive metals or alloys. These materials require oxidizers to form protective oxide films.

Changing concentration – higher concentration of acid has higher amount of active species (H ions). However, for materials that exhibit passivity, effect is normally negligible.

Page 50: tugas korosi 1

Environment factors affecting corrosion design :

Dust particles and man-made pollution – CO, NO, methane, etc.

Temperature – high T & high humidity accelerates corrosion.

Rainfall – excess washes corrosive materials and debris but scarce may leave water droplets.

Proximity to sea Air pollution – NaCl, SO2, sulfurous acid, etc. Humidity – cause condensation.

Page 51: tugas korosi 1

Design Do’s & Don’ts

Wall thickness – allowance to accommodate for corrosion effect.

Avoid excessive mechanical stresses and stress concentrations in components exposed to corrosive mediums. Esp when using materials susceptible to SCC.

Avoid galvanic contact / electrical contact between dissimilar metals to prevent galvanic corrosion.

Avoid sharp bends in piping systems when high velocities and/or solid in suspension are involved – erosion corrosion.

Avoid crevices – e.g weld rather than rivet tanks and other containers, proper trimming of gasket, etc.

Page 52: tugas korosi 1

Avoid sharp corners – paint tends to be thinner at sharp corners and often starts to fail.

Provide for easy drainage (esp tanks) – avoid remaining liquids collect at bottom. E.g steel is resistant against concentrated sulfuric acid. But if remaining liquid is exposed to air, acid tend to absorb moisture, resulting in dilution and rapid attack occurs.

Avoid hot spots during heat transfer operations – localized heating and high corrosion rates. Hot spots also tend to produce stresses – SCC failures.

Design to exclude air – except for active-passive metals and alloys coz they require O2 for protective films.

Most general rule : AVOID HETEROGENEITY!!!

Page 53: tugas korosi 1

Protective Coatings / Wrapping Provide barrier between metal and environment. Coatings may act as sacrificial anode or release

substance that inhibit corrosive attack on substrate.

Metal coatings : Noble – silver, copper, nickel, Cr, Sn, Pb on steel.

Should be free of pores/discontinuity coz creates small anode-large cathode leading to rapid attack at the damaged areas.

Sacrificial – Zn, Al, Cd on steel. Exposed substrate will be cathodic & will be protected.

Application – hot dipping, flame spraying, cladding, electroplating, vapor deposition, etc.

Page 54: tugas korosi 1

Surface modification – to structure or composition by use of directed energy or particle beams. E.g ion implantation and laser processing.

Inorganic coating : cement coatings, glass coatings, ceramic coatings, chemical conversion coatings.

Chemical conversion – anodizing, phosphatizing, oxide coating, chromate.

Organic coating : paints, lacquers, varnishes. Coating liquid generally consists of solvent, resin and pigment. The resin provides chemical and corrosion resistance, and pigments may also have corrosion inhibition functions.