4 Bottlewithcups,1981. La Borne stoneware, china clay slip on cups, salt glaze. Bottle: H 10 cm, cups: H 4 cm. Private collec-tion.
5 Jugwithtwocups,1982. Stoneware, china clay slip, wood-fired salt glaze. Jug: H 25 cm. The National Museum of Decorative Arts, Trondheim, Norway.
6 Vase,1981. Stoneware, china slip, calcium wadding marks, wood-fired salt glaze. H 22 cm. Sør-Trøndelag County, Norway.
kvasboe_korr_010813_END.indd 91 01.08.13 13:46
114
kvasboe_korr_010813_END.indd 114 01.08.13 13:51
115
34 Chest/houseform,1993. Iron-rich stoneware, slab built, silica rocks, wire cut, thick slip on roof, crushed seashells, natural ash glaze, reduction cooling, contact flashing, anagama-fired. H 50 x W 35 x D 20 cm. Auckland War Memorial Museum, Auckland, New Zealand. Judge’s Commendation, Fletcher Challenge Ceramics Award, New Zealand, 1993.
35 Chestform,1993.Borgestad alumina-rich stoneware, ornaments by stretching layers of clay, slab built, natural ash glaze and flashing, ana gama-fired. W 75 cm. Private collection.
kvasboe_korr_010813_END.indd 115 01.08.13 13:51
136
kvasboe_korr_010813_END.indd 136 01.08.13 13:53
137
kvasboe_korr_010813_END.indd 137 01.08.13 13:53
154
Pages 152–153:
66 Stack,turquoise,2010. White earthenware clay, extruded pipe ele-ments roughly modelled together in centre of stack around a wheel-thrown bottom centre cone, alkaline frit-based copper oxide Egyptian blue glaze; the darker parts also contain cobalt carbonate. The low viscosity of the glaze clearly reveals all the details in the body under-neath, kiln shelf, electric kiln. H 75 x Dia. 50 cm. Private collection, Oslo, Norway.
67 Tubeforms,red,2013. Stoneware clay, extruded tube elements roughly modelled together, lead bisilicate-based glaze thickly applied, running glaze with red stain, kiln shelf, electric kiln. H 90 x Dia. 80 cm. Private collection.
kvasboe_korr_010813_END.indd 154 01.08.13 13:57
155
68 Stack,green,2009. Terracotta clay, extruded pipe elements, roughly modelled together in centre of stack round a wheel-thrown bottom centre cone, white ball clay slip sprayed on, lead bisilicate-based semi-transparent glaze with copper oxide, electric kiln. H 90 x Dia. 60 cm. Private collection.
69 Stack,red,2009. Terracotta clay, extruded pipe elements roughly modelled together in centre of stack around a wheel-thrown bottom centre cone, white ball clay slip sprayed on surface, lead bisilicate-
based glaze with red stain thickly applied, running glaze with red stain, kiln shelf, electric kiln. H 75 x Dia. 50 cm. Lillehammer Art Museum, Lillehammer, Norway.
70 Stack,yellow,2010. Terracotta clay, extruded pipe elements, roughly modelled together in centre of stack around a wheel-thrown bottom centre cone, white ball clay slip sprayed on, red lead-based glaze, kiln shelf, electric kiln. H 80 x Dia. 50 cm. Private collection.
71 Stack,green,2009. Terracotta clay, extruded pipe elements, roughly modelled together in centre of stack around a wheel-thrown bottom centre cone, white ball clay slip sprayed on, lead bisilicate-based semi-transparent glaze with copper oxide, kiln shelf, electric kiln.
H 80 x Dia. 50 cm. Private collection, London, Great Britain.
kvasboe_korr_010813_END.indd 155 01.08.13 13:57
158
73 Stack,terracotta,2010. English terracotta clay (Evans), extruded pipe elements roughly modelled together in centre of stack around a wheel-thrown bottom centre cone, unglazed, sandblasted when dry, electric-fired. H 80 x Dia. 50 cm. Private collection.
74 Stack,black,2010. Black earthenware clay, extruded pipe elements roughly modelled together in centre of stack around a wheel-thrown bottom centre cone, unglazed, sandblasted when dry, electric-fired.
H 80 x Dia. 50 cm. Private collection.