Cool roofs are highly reflective, highly emissive roofing materials that stay 10 to 15 degrees Centigrade cooler than a normal roof under a hot summer sun.

Cool roofs can cut building owners' energy costs. Because cool roofs gain less heat than normal roofs, they reduce the need for air conditioning making buildings more comfortable to the people inside.

Cool roofs have other benefits, too. For building owners they can cut maintenance costs and increase the life expectancy of the roof. And for society in general, cool roofs can even help to reduce the urban heat island effect that makes our cities hotter and produces unhealthy air.

THERMO-SHIELD ROOF COATDESCRIPTION Thermo-Shield® Roof Coats are highly efficient, energy-saving, flexible coatings, made from a water-based pure acrylic resin system filled with hollow sodium borosilicate glass micro spheres. Each micro sphere acts as a sealed cell and the entire mastic acts as a thermally efficient blanket covering the entire structure. These coatings are non-toxic, friendly to the environment and form a monolithic (seamless) membrane that bridges hairline cracks. They are completely washable and resist many harsh chemicals. Thermo-Shield® Roof Coats have high reflectance and high emittance as well as a very low conductivity value. Thermo-Shield® Roof Coats greatly reduce thermal shock and heat penetration by keeping roof surfaces much cooler in hot summer weather. They offer UV protection and low VOC’s. They display excellent dirt pick-up resistance and retain their flexibility long after aging. Thermo-Shield® Roof Coats reduce noise transmission and have an effective use range from –40 Deg F to 375 Deg C (700 Deg F).

TYPICAL USES Primarily used as a roof coating where joints, seams, cracks and gaps around protrusions are reinforced with a 100% polyester spun laced fabric embedded in the membrane. They may be utilized wherever a weather resistant membrane-like coating is required. The STD formula is used in most climatic conditions. The TROPICAL formula is used in climatic conditions where fungi growth is a major concern. The ULA formula is used on buildings and installations where shear extra-high fire resistance is desired i.e. oil & gas.

PRIMER No primer is usually required. Follow instructions for proper application regarding warranted systems on bitumen roofs. Our Flex Tac barrier and bonding coat is required to obtain good adhesion between a bitumen substrate and out water-based roof coatings. Flex Tac is usually used with Pol-E-Force reinforcing fabric. Rusty surfaces require rust control prior to the application of the roof coats. See application manual for details.

SURFACE PREPARATION All surfaces must be clean and free from laitance, dust, dirt, oil and grease. Minimally, surfaces should be power washed prior to coating, providing this will not damage the roof or cause leaks.

COLOR Tinting may be achieved with Thermo-Shield® Roof Coatings by the addition of universal colorants. Darker colors will give a correspondingly lower reflectivity.

SPECIFIED DRY FILM THICKNESS Flat Roof 700 microns DFT (27 mills) Sloped Roof 300 microns DFT (12 mills)

PERCENT NON-VOLATILE 51.67% by volume 51.14% by weight

THEORETICAL COVERAGE (2 or more coats) 3 m2 per gallon at 700 microns DFT (32 sf/g at 27 mills DFT) 8 m2 per gallon at 300 microns DFT (75 sf/gl at 12 mills DFT)

DRYING TIME To set: 45 minutes To re-coat: 12 hours To through: 12 hours At 24 deg C and 50% relative humidity After 45 minutes, Thermo-Shield® Roof Coats have surface set to the point where it is no longer susceptible to airborne dust and will not run in the presence of increase humidity. Do not apply Thermo-Shield® Roof Coats if precipitation is imminent or is likely to occur before Thermo-Shield® Roof Coatings are dry through, or if temperature is expected to drop below 40 deg C.

INSULATION Although these Roof Coats enjoy very low Conductance (0.05 W/mK), it is the combination of their high Reflectance (82%), high Emittance (94%) and Endothermic Effect® that makes them a very good choice for protecting your roofs from heat buildup. Unlike typical mass insulation, where heat conduction is just slowed down, this technology keeps the heat out. Sun light only produces heat when it is absorbed by the roof surface, and being able to keep heat from forming into the surface of the roof is a very effective way to insulate. The cooling process of Endothermic Effect® ensures that the surface continues to insulate, even if Reflectance is diminished with aging, dust build-up or darker colors. FLEXIBILITY Coatings remain flexible at –50 Deg F (-45.6 Deg C) – Eliminate thermal-shock damage – Maintain their strength at 400 Deg F (204.44 Deg C), Will pass 180 Deg bend at 1.11 Deg C after 60month exposure.

ADHESION Excellent adhesion to a wide variety of substrates: wood, urethane foam, galvanized steel, aluminum, asphalt roof shingles, concrete, asbestos and others. ACCELERATED WEATHERING ASTM G53, Q-UV 3000 no evidence of chalking, de-laminating or loss of flexibility. RESISTANCE TO WATER PONDING Excellent resistance to ponding water. This is a result of a careful balancing of the following properties: Passage of bulk water at 50 hours … 40-55 mg/m2 Permeability (ASTM E 96-80) … 08.80% Perms Film Swelling (at Equilibrium) …10.17%

VARIABLE PERMEABILITY This feature, unique to Thermo-Shield®, allows the membrane to perform unlike any other coating. When conditions are dry, the polymers shrink and open pores to allow trapped water vapor to breathe out of the substrate, but when conditions are wet (raining, ponding of water, etc.), the polymers swell, close the pores, and the entire membrane becomes watertight.

SPREADING RATE PER C0AT (1 millimeter = 1000 microns) Suggested: 9 sm/gl – 371 microns WFT (15 mills) – 233 microns DFT (9 mills) Maximum: 12 sm/gl – 275 microns WFT (11 mills) – 175 microns DFT (7 mills) Minimum: 6 sm/gl – 567 microns WFT (22 mills) – 350 microns DFT (14 mills) This rate allows for 10% loss

MIXING Stir each container thoroughly using low speed mechanical agitation to avoid air entrapment.

NUMBER OF COATS Two to three coat application (minimum dry film-build of 700 microns DFT for flat and asphalt shingle granulated roofs, and 300 microns for well sloped roofs – consult Application Manual) will give the best long-term protection at minimum cost. The principle cause of coating failure is water ponding in low film thickness i.e. less than the recommended thickness. THINNING None required. Clean water in small amounts (up to 0.24 Liter –1 cup- per gallon) may be added to replace evaporation losses or to adjust for spray equipment configuration. Caution: excessive thinning will cause the coating to loose adhesion and elasticity.

EQUIPMENT Roller or airless spray application is recommended. Very small areas may be brushed. When Thermo-Shield® Roof Coatings are applied by brush, three (3) coats cross-brushed are required for adequate protection.

Air less Spray: Tip Orifice .31 inches Atomizing Pressure 2200 - 2500 psi Fan Spread 0 degrees Pump 1gallon per minute at 2500 psi Filer Remove filters and screens

*** Prime pump with water before attempting to spray Thermo-Shield® Roof Coatings. (Acceptable equipment includes Binks Super Hornet, Graco 433 or larger, and many others)

METHODS To assure adequate and uniform coverage, the “spray and back roll” or the “cross spray” techniques are recommended. Thermo-Shield® Roof Coatings should be applied in full wet coats.

CLEAN UP Clean all tools and equipment with warm soapy water. Rinse with clean water; flush mineral spirits through spray equipment to prevent rusting and to lubricate packing and gaskets.

PACKAGING One and five-gallon pails.

APPROXIMATE SHIPPING WEIGHT Net weight per gallon 4.64 kg (10 lbs)

Case of 4 1-gallon cans 20.4 kg (15 lbs) Five-gallon pail 24.13 kg (53 lbs)

STORAGE Minimum 0 Deg. C Maximum 30 Deg. C (32 Deg F – 86 Deg F) DO NOT FREEZE

SHELF LIFE Minimum 2 years (keep from freezing)

SETA FLASH POINT Non-Flammable (water based)

DOT CLASS Not regulated

PRODUCT CODES STD WHITE: 5962 – STD ACCENT BASE: 5965 – TROPICAL WHITE: 5966 – TROPICAL ACCENT BASE: 5967 – UL CLASS A: 5975

WARRANTY 5 to 10 year extendable LIMITED WARRANTY The sole remedy for goods not in conformance with any warranty is replacement of the product or return of purchase price. SPM Thermo-Shield® shall not be liable for any other damages, including but not limited to labor expenses.

Thermo-Shield® is a charter member of the U.S. Government Energy Star Roof Program. The U.S. Department of Energy (DOE) and the Environmental Protection Agency (EPA) state the following benefits are derived from the use of reflective coatings:

✔ Reduction of energy used and cooling costs (up to 40%) ✔ Downsizing of air-conditioning equipment ✔ Lowering of the surrounding air temperature in a community ✔ Decreasing of pollution in urban areas

Thermo-Shield® is a trademark of SPM Thermo-Shield since 1987 in the US and across many countries. Thermo-Shield is currently under trademark process in the UAE

THERMO-SHIELD EXTERIORDESCRIPTION Thermo-Shield® Exterior Wall Coats are highly efficient, energy-saving, flexible coatings designed to insulate and waterproof exterior walls. They are non-toxic, friendly to the environment , and form a monolithic (seamless) membrane that bridges hairline cracks. They are completely washable and resist many harsh chemicals and dirt pick-up. These water-based coatings are made from an acrylic resin system filled with vacuumed ceramic micro spheres that acts as a thermally efficient blanket. Thermo-Shield® Exterior Wall Coats put a stop to the “frequent painting cycle” – they outlast other paints several times over. They have superb waterproofing performance, fire resistance and their adhesion increases with saturation. These coatings have “Variable Permeability” – they become watertight when saturated by water, and breathe away trapped water vapor when dry. They protect against UV, greatly reduce thermal shock and sound transmission, and have low VOC levels. These coatings come in a variety of architectural colors and leave a beautiful satin finish.

TYPICAL USES For painting concrete, metal, wood, polymerized surfaces and reducing condensation. STD EXTERIOR: Used in most climatic conditions where color fading is a major concern. It has superb fire resistance, excellent chemical resistant to salt spray, strong acids, petroleum products and other harsh chemicals. TROPICAL EXTERIOR: With same properties as STD, it is used in climatic conditions where fungi growth is a major concern. ACENT BASE: No pigmentation. Used as a semi-clear coat or when tinting for darker colors.

INSULATION Although these coatings enjoy very low Conductance (0.06 W/mK), it is the combination of their high Reflectance (89%), high Emittance (94%) and Endothermic Effect® that makes them a very good choice for protecting your exterior walls from heat buildup. Unlike typical mass insulation, where heat conduction is just slowed down, this technology keeps the heat out. Sun light only produces heat when it is absorbed by the wall surface, and being able to keep heat from forming into the surface of the walls is a very effective way to insulate. The cooling process of Endothermic Effect® ensures that the surface continues to insulate, even if Reflectance is diminished with aging, dust build-up or darker colors.

PRIMER No primer is usually required. Follow instructions for proper application and film build-up

SURFACE PREPARATION All surfaces must be clean and free from laitance, dust, dirt, rust, oil and grease. Minimally, surfaces must be cleaned to remove any loose or chipping paint, or any other foreign material prior to coatings.

COLOR Tinting may be achieved with Thermo-Shield® Exterior Wall Coatings by the addition of universal colorants. Darker colors will give a correspondingly lower reflectivity.

PERCENT NON-VOLATILE: 54.41% by VOLUME / 54.85% BY weight

THEORETICAL COVERAGE (To be applied in 2 coats) 10.4 sm. Per gallon at 150 microns DFT with no loss. (130 sf/gl at 6-mills DFT)

DRYING TIME To set: 20 minutes To re-coat: 4 hours To through: 12 hours (At 24 deg C and 50% relative humidity)

THINNING None required. Clean water in small amounts (up to 0.24 Liter –1 cup- per gallon) may be added to replace evaporation losses or to adjust for spray equipment configuration. Caution: excessive thinning will cause the coating to loose adhesion and elasticity.

EQUIPMENT Roller or airless spray application is recommended. Very small areas may be brushed. When Thermo-Shield® Exterior Wall Coatings are applied by brush, three (3) coats cross-brushed are required for adequate protection.

AIRLESS SPRAY: Tip Orifice .031 inches Atomizing Pressure 2200 - 2500 psi Fan Spread 60 Degrees Pump Minimum 1 gallon per minute at 2500 psi Filter Remove filters & screens

*** Prime pump with water before attempting to spray Thermo-Shield® Wall Coatings. Acceptable equipment includes Binks Super Hornet, Graco 433 or larger, and many others.

METHODS To assure adequate and uniform coverage, the “spray and back roll” techniques are recommended – spray all coats in the same direction, do not cross spray to avoid showing undulations and other small imperfections in the walls. Thermo-Shield® Exterior Wall Coats should be applied in full wet coats.

CLEAN UP Clean the tools and equipment with warm soapy water. Rinse with clean water; flush mineral spirits through spray equipment to prevent rusting and to lubricate packing and gaskets.


APPROXIMATE SHIPPING WEIGHT Net weight per gallon 4.55 kg (10 lbs) Case of 4 1-gallon cans 19.96 kg (44 lbs) Five-gallon pail 23.63 kg (52 lbs)

STORAGE Minimum 0 Deg. C Maximum 30 Deg. C DO NOT FREEZE


SETA FLASH POINT DOT CLASS

Non-Flammable (water based) not regulated

PRODUCT CODES

EXTERIOR WHITE: 5961, EXTERIOR WHITE TROPICAL: 5968, EXTERIOR ACCENT BASE: 5964, EXTERIOR ACCENT BASE TROPICAL: 5969

WARRANTY: 10 year LIMITED WARRANTY


www.thermoshield.com

THERMO-SHIELD INTERIORDESCRIPTION Thermo-Shield® Interior Wall Coats are highly efficient, energy-saving, flexible coatings designed to insulate and waterproof your walls. They are non-toxic, friendly to the environment, and form a monolithic (seamless) membrane that bridges hairline cracks. They are completely washable and resist many harsh chemicals and dirt pick-up. These water-based coatings are made from an acrylic resin system filled with vacuumed ceramic micro spheres that acts as a thermally efficient blanket. Thermo-Shield® Interior Wall Coats can be applied by roller or sprayer. Thermo-Shield Interior® Wall Coats have 4 times the fire resistance and 1/26th the smoke development necessary to classify for Class I rating. They have superb adhesion; chemical resistance and reduces sound transmission and echo. They help maintain a more uniform temperature ceiling-to-floor and reduces cold weather heat loss though walls and ceilings. These coatings come in a variety of architectural colors and leave a beautiful satin finish.

TYPICAL USES For regular indoors painting where durability, reduction of the noise factor and superb smoke protection are important. Thermo-Shield® Interior Wall Coats reduce condensation and help maintain an even level of comfort in the room.

INSULATION Reflectivity 89% - Emittance 94% - Conductance 0.06 W/mK – Endothermic Effect®

PRIMER No primer is usually required. Follow instructions for proper application and film build-up

SURFACE PREPARATION All surfaces must be clean and free from laitance, dust, dirt, rust, oil and grease. Minimally, surfaces must be cleaned to remove any loose or chipping paint, or any other foreign material prior to coatings. COLOR Tinting may be achieved with Thermo-Shield® Interior Wall Coatings by the addition of universal colorants. Darker colors will give a correspondingly lower reflectivity.

PERCENT NON-VOLATILE: 46.61% by VOLUME / 49.77% By weight

THEORETICAL COVERAGE (To be applied in 2 coats) 10.4 sm. Per gallon at 150 microns DFT with no loss. (130 sf/gl at 6-mills DFT) DRYING TIME To set: 20 minutes To re-coat: 4 hours To through: 12 hours (At 24 deg C and 50% relative humidity)


EQUIPMENT Roller or airless spray application is recommended. Very small areas may be brushed. When Thermo-Shield® Interior Wall Coatings are applied by brush, three (3) coats cross-brushed are required for adequate protection.

AIRLESS SPRAY: Tip Orifice .031 inches Atomizing Pressure 2200 - 2500 psi Fan Spread 60 Degrees Pump Minimum 1 gallon per minute at 2500 psi Filter Remove filters & screens

*** Prime pump with water before attempting to spray Thermo-Shield® Wall Coatings. Acceptable equipment includes Binks Super Hornet, Graco 433 or larger, and many others.

METHODS To assure adequate and uniform coverage, the “spray and back roll” techniques are recommended – spray all coats in the same direction, do not cross spray to avoid showing undulations and other small imperfections in the walls. Thermo-Shield® Interior Wall Coats should be applied in full wet coats.

CLEAN UP Clean the tools and equipment with warm soapy water. Rinse with clean water; flush mineral spirits through spray equipment to prevent rusting and to lubricate packing and gaskets.



STORAGE Minimum 0 Deg. C Maximum 30 Deg. C DO NOT FREEZE


SETA FLASH POINT DOT CLASS Non-Flammable (water based) not regulated

PRODUCT CODES INTERIOR WHITE: 5977 INTERIOR/Interior ACCENT BASE: 5964

WARRANTY: 10 year LIMITED WARRANTY


www.thermoshield.com

THERMO-SHIELD STUCCO BASE & STUCCO FINISH COATThermo-Shield Stucco water based coatings can be applied in place of paint, and as an alternative to the conventional and often costly three and more part stucco systems. This unique wall coating applies quickly, is much less labor intensive and provides an effective and durable thermal barrier. The insulating hollow micro spheres incorporated in the finish and base coat formulas are reluctant to conducting heat, and refract as well as dissipate heat away from the coated surface. The formulas also incorporates 100% acrylic polymer resins that allows the transmission of water vapor to escape thus reducing moisture build-up in the wall assembly.

COMPONENTS: Pre-mixed base coat and pre-mixed finish coat.

USES: Thermo-Shield Stucco Base and Finish Coatings are designed for Interior and Exterior wall surfaces as a flexible wall coating.They can be applied over drywall, wood, steel, reinforced insulation board, brick, concrete block, concrete and over existing stucco.It is designed to go on ready-to-paint surfaces that meet local standards and building codes.

DRYING TIME: Base Coat, one hour to set and 12 hours to re-coat.Finish Coat, 40 to 70 hours to cure at 24 deg. C(75 Deg F) and 50% relative humidity.

COLORS AVAILABLE: Many colors to choose from.

CONTAINER SIZE: Available in five-gallon containers.(one gallon cans can be purchased, however, higher price rates do apply)

SHELF LIFE: Two years. Store in room temperature between 10 and 32 deg. C. DO NOT FREEZE

CLEAN UP: Clean tools and equipment with soap and warm water and rinse with clean water.

LIMITATIONS: Do not apply Thermo-Shield Stucco Base or Finish Coats when freezing temperatures are expected within 48 hours or when rain is predicted. Ambient temperature should be 10 deg. C or above for at least 24 hours. Water-based coatings depend on evaporation to cure so avoid application in damp or cold conditions; there must be good drying time of at least two hours before dew point.

APPLICATION PROCEDURES: Apply Thermo-Shield Stucco Base Coat to the entire substrate. Prepare corners and joints with recommended corner bead, mesh and Thermo-Shield Stucco Finish Coat. Allow drying and then apply a coat of Finish Coat the entire structure (see application manual for more detailed information).

APPLICATION: Thermo-Shield Stucco Finish Coat has a spray or roll-on viscosity. Commercial sprayers with texture guns can be used to apply this coating. Various textures may be achieved, from a very find sand finish to a heavy plaster coat (see manufacturer’s specification s for each individual sprayer).Recommended application of Thermo-Shield Stucco Base Coat is via roller or airless sprayer. Use a roller with a nap of 19mm or airless spray unit with the following qualifications: Tip Orifice/ .031 to .039 – Pressure / 2200 to 2500 psi

THERMO-SHIELD TANK SHIELDDESCRIPTION Thermo-Shield® Tank Shield is a highly efficient, energy-saving, flexible coating, designed to protect and lower the external surface temperature of storage vessels. It is non-toxic and friendly to the environment. It is completely washable and resist many harsh chemicals and dirt pick-up. This water-based coating is made from an acrylic resin system filled with vacuumed ceramic micro spheres that acts as a thermally efficient blanket. Thermo-Shield® Tank Shield has superb fire resistance – it is grade Class A by UL Standards. It can be obtained in a variety of architectural colors for signs and logo making. It leaves a beautiful satin finish.

TYPICAL USES For the exterior of steel petrol storage tanks and pipelines where reduction of surface temperature is desired. Exterior of steel or polymer water tanks or grain storage silos. Exterior of most chemical storage tanks – this coating is resistant to 26 different harsh chemicals including 20% hydrochloric and 25% sulphuric acids.

PRIMER Use alkyd or epoxy quality primers where required and/or rust inhibitors to make sure rust will not be present during the application of the coating.

SURFACE PREPARATION All surfaces must be clean and free from dust, dirt, oil or grease. Minimally, surfaces must be cleaned to remove any loose or chipped paint, or any other foreign material prior to coating. Rust should be controlled with the use of rust inhibitors.

COLOR Tinting may be achieved with Thermo-Shield® Tank Shield by the addition of universal colorants. Darker colors will give a correspondingly lower reflectivity.

PERCENT NON-VOLATILE 51.67% by volume 51.14% by weight

THEORETICAL COVERAGE (2 or more coats) 7 sq m per gallon at 300 microns DFT (75 sf/gl at 12 mills DFT) with no loss (To be applied in 2 to 3 coats.)

DRYING TIME To set: 45 minutes To re-coat: 12 hours To through: 12 hours At 24 deg C and 50% relative humidity

INSULATION Reflectance 82% Emittance 94% Endothermic Effect® Conductance 0.05 W/mK FLEXIBILITY Coating maintains it properties at –50 Deg F (-45.6 Deg C) – Eliminates thermal-shock damage – maintains its strength at 400 Deg F (204.44 Deg C).

ADHESION Excellent adhesion to steel and other substrates such as galvanized steel, aluminum, concrete, wood, urethane foam, asbestos and others.

ACCELERATED WEATHERING ASTM G53, Q-UV 3000 no evidence of chalking, de-laminating or loss of flexibility. RESISTANCE TO WATER PONDING Excellent resistance to ponding water. This is a result of a careful balancing of the following properties: Passage of bulk water at 50 hours … 40-55 mg/m2 Permeability (ASTM E 96-80) … 08.80% Perms Film Swelling (at Equilibrium) …10.17%

VARIABLE PERMEABILITY This feature, unique to Thermo-Shield®, allows the membrane to perform unlike any other coating. When conditions are dry, the polymers shrink and open pores to allow trapped water vapor to breathe out of the substrate, but when conditions are wet (raining, ponding of water, etc.), the polymers swell, close the pores, and the entire membrane becomes watertight.

SPREADING RATE PER C0AT (1 millimeter = 1000 microns) Suggested: 9 sm/gl – 371 microns WFT (15 mills) – 233 microns DFT (9 mills) Maximum: 12 sm/gl – 275 microns WFT (11 mills) – 175 microns DFT (7 mills) Minimum: 6 sm/gl – 567 microns WFT (22 mills) – 350 microns DFT (14 mills) This rate allows for 10% loss

MIXING Stir each container thoroughly using low speed mechanical agitation to avoid air entrapment.

NUMBER OF COATS Two to three-coat application (minimum dry film-build of 300 microns) will give the best long-term protection at minimum cost.


EQUIPMENT

Roller or airless spray application is recommended. Very small areas may be brushed. When Tank Shield is applied by brush, three (3) coasts are required for adequate protection. Airless spray: apply all coats in the same direction – do not cross spray. Cross spraying may reveal surface imperfections such as small undulation, etc.

Air less Spray: Tip Orifice .31 inches Atomizing Pressure 2200 - 2500 psi Fan Spread 0 degrees Pump 1gallon per minute at 2500 psi Filter Remove filters and screens

*** Prime pump with water before attempting to spray Thermo-Shield® Roof Coatings. (Acceptable equipment includes Binks Super Hornet, Graco 433 or larger, and many others)

METHODS To assure adequate and uniform coverage, the “spray and back roll” or the “cross spray” techniques are recommended. Thermo-Shield® Roof Coatings should be applied in full wet coats.

CLEAN UP Clean all tools and equipment with warm soapy water. Rinse with clean water; flush mineral spirits through spray equipment to prevent rusting and to lubricate packing and gaskets.



STORAGE Minimum 0 Deg. C Maximum 30 Deg. C (32 Deg F – 86 Deg F) DO NOT FREEZE


SETA FLASH POINT Non-Flammable (water based)

DOT CLASS Not regulated

PRODUCT CODES STD WHITE: 5962 – STD ACCENT BASE: 5965 – TROPICAL WHITE: 5966 – TROPICAL ACCENT BASE: 5967 – UL CLASS A: 5975

WARRANTY 5 to 10 year extendable LIMITED WARRANTY The sole remedy for goods not in conformance with any warranty is replacement of the product or return of purchase price. SPM Thermo-Shield® shall not be liable for any other damages, including but not limited to labor expenses.

Thermo-Shield® is a charter member of the U.S. Government Energy Star Roof Program.

Thermo-Shield® is a trademark of SPM Thermo-Shield since 1987 in the US and across many countries. Thermo-Shield is currently under trademark process in the UAE.

THERMO-SHIELD® CLEAR COATDESCRIPTIONThermo-Shield® Clear is a tough acrylic coating designed to give Thermo-Shield® Roof Coat, Thermo-Shield® Wall Coats, Stucco Shield and Tank Shield a shiny surface. This product will also protect white surfaces from the effects of smog and automobile gas pollution. It is non-toxic and friendly to the environment. It is completely washable and highly resistant to dirt pick-up. This water-based coating is made from an acrylic resin and leaves a beautiful clear and shiny finish.

TYPICAL USES

As a shinny coat on Thermo-Shield® Roof Coat, Exterior Wall Coats, Stucco Shield or Tank Shield, or as extra protection against smog stains on white Thermo-Shield® Roof Systems. This coating will give a lasting shine without getting dull, cracking or peeling. Use over white Roof Coat in carbon-polluted environments. Smog and pollution fallout in the air can turn the surface of white Roof Coats into a gray color, Thermo-Shield® Clear will prevent this from happening.

SURFACE PREPARATIONAll surfaces must be clean and free from dust, dirt, oil and grease.

APPLICATIONOne coat application of 50 to 75 microns WFT (2 to 3 Mills) with a coverage of 37 to 55 Sq M gallon.

TESTS & CERTIFICATIONSTHERMO-SHIELD HAS BEEN WIDELY TESTED IN ACCREDITED LABORATORIES AND IN ACTUAL FIELD-TESTS.

THERMO-SHIELD ROOF COATING RESULTS ON AMERICA’S ASTM TESTS

TENSILE STRENGTH Tensile stress at 25% elongationTensile strength at break

ASTM D-412525 psi615 psi elongation 70%

DETERIORATION BY HEATING IN AIR (Tensile strength after heating 21 days at 150° C)

ASTM D-865

Tensile stress at 25% elongationTensile strength at break

515 psi640 psi elongation 85%

IMPORTANT: These two tests show THERMO-SHIELD ROOF COATING ACTUALLY GETS STRONGER AND MORE DURABLE WITH AGING

WATER VAPOR PERMEABILITY AND PERMEABILTIY

ASTM D-1653ASTM E-96

Both tests show ROOF COATING with 8.8 perm in. rating. This is excellent Permeability: it has 160 times more than one of our main competitors claiming the same properties.

WATER ABSORPTION ASTM D-570After water saturation for 5 weeks “NO CHANGES IN APPEARANCE ON ROOF COATING AFFER RECONDITONING”. IMPORTANT! The above 3 tests show ROOF COATING will stand up to ponding water, yet has the ability to BREATHE OUT trapped water vapor when weather conditions are dry - WATERPROOFING WITHOUT BLISTERING

BRITTLENESS ASTM D-746

ROOF COATING passed the 90° bend test at -37° C. FLEXIBLE AT VERY COLD TEMPERATURES

SURFACE OZONE CRACKING ASTM D-1149

70-DAY EXPOSURE TO OZONE, Time to failure, “NONE OBSERVED IN DURATION OF TEST”

CHEMICAL RESISTANCE ASTMD-1380

16-hour spot test to 26 harsh or staining chemicals. ROOF COATING blistered only with some

concentrated acids, stained only with gasoline, aircraft hydraulic fluid, and lipstick. ROOF COATING undamaged by animal urine, battery acid, bleach, de-icing chemical, 40% salt solution and others.

STEADY STATE HEAT FLUX MEASUREMENTS AND THERMAL TRANSMISSION PROPERTIES

ASTM C-177 / ASTM C-l045

ROOF COATING (at 5-MIL thickness) K Value 0.0454 (R 22) NOTE: Some specialists say the ASTM formula for R Values in this test “R = 1/K” is oversimplified, and does not take enough information into consideration.

JAPANESE INDUSTRIAL STANDARDS TESTS “JIS”

(Materials must pass strict limits on these tests before they can be sold on the Japanese market) THERMO-SHIELD ROOFING, INTERIOR AND EXTERIOR COATINGS have all passed the required tests:

LOW TEMPERATURE STABILITY JIS A 6906 (1984) 5.5

RESISTANCE TO CRACKING DURING CURING AND DRYING STAGE

JIS A 6906 (1984) 5.7

ADHESION STRENGTH TEST JIS A 6909 (1984) 5.8

Normal Condition Test, THERMO-SHIELD has 3 times the minimum requirement for Adhesion. After Saturation Test, THERMO-SHIELD had 8 times the minimum requirement for Adhesion.

REPEATED TEMPERATURE CHANGE ***No peeling, cracking, blistering, discoloration or dullness***

JIS A 6909 (1984) 5.9

TEST FOR WATERPROOF***Maximum to pass test is 1.0 CM rating, THERMO-SHIELD WAS 0.1 CM TEN TIMES better than required***

JIS A6909 (1984) 5.10

WASHABILITY JIS A6909 (1984) 5.11

IMPACT; SHOCK TEST ***Did not crack, peel, nor change shape or form under impact***

JIS A6909 (1984) 5.12

AKALINITY TEST ***Did not crack, blister, peel, gum, change color or dull***

JIS A6909 (1984) 5.13.2

RESISTANCE TO WEATHER & CLIMATE***Did not crack, peel or discolor to minimum scale color of #3*** THERMO-SHIELD maintained a 4-5 scale, EXCELLENT, best of any paint tested by the Japanese National Testing Lab.

JIS A 6909 (1984) 5.14

FIRE RESISTANCE TEST - CLASS 1 ***Did not fuse, crevice, change form or bow when cooled. Flame Retention: No flame to remain over 30 seconds after heating is stopped. THERMO-SHIELD Retention was 0.00***

JIS A 1321

UNDERWRITERS LABORATORIES ASTM E-108 “FIRE TESTS OF ROOF COVERINGSResults: Flying Brands Produced: NoneDeck Exposure: NoneLateral Flame Spread: None

Under UL File reference “R12343, THERMO-SHLELD ROOF COATING is available with a CLASS A fire resistant rating. NOTE: This is a special “Class-A formula”, not our standard Formula.

HAUSER LABORATORIES TESTS - Comparison of heat transfer through THERMO-SHIELD vs. other common coatings:

1. THERMO-SHIELD INTERIOR PAINT heat transfer 0.871 BTU/hr Sq.-Ft., white paint heat transfer 1.163 BTU/hr Sq.-Ft (Normal white paint allowed 25% more heat to pass through).

2. THERMO-SHIELD ROOF COATING Solar heat transfer 6.1 BTU/hr Sq.-Ft., Black Asphalt solar heat transfer 38.1 BTU/hr Sq.-Ft. (Asphalt allowed 84% more heat to pass through).

3. THERMO-SHIELD ROOF COATING .005”-thick (5-mil = .127MM) painted on galvanized steel - solar heat transfer 17.2 BTU/hr Sq.-Ft. Untreated Galvanized Steel -heat transfer 48.0 BTU/hr Sq.-Ft (64% more heat pass through)

HEMISPHERICAL LIGHT REFLECTANCE DSET Test 89r12 1001

Test on THERMO-SHIELD WHITE ROOF COATING, it reflected 82% of the solar light (88% of S-VISUAL LIGHT and 84% of NIR “Near Infra Red”, the portions of light that account for heat - Reflectance of other typical roof systems: Dark pea gravel 12% - Light pea gravel 34% - gravel coated asphalt 23% - black roof 5% - dark gray 15% - white paint 55% - aluminum 40% - aluminum fiber coating 36% - white asphalt shingles 30% - SPM-60 (EPDM) 11%. (THERMO-SHIELD Reflects 49% more than 2nd best, white paint. SOLAR HEAT THAT

DOES NOT GET INTO THE BUILDING, DOES NOT BECOME A PROBLEM.

WATER EXTRACTABLES - SIMULATION OF ENVIRONMENTAL LEACHING

ROOF COATING leachables are composed of common (non-toxic) elements, predominately Calcium salts.

FIELD TESTS OF THERMO-SHIELD INSULATING VALUE

JAPANESE TESTS ON 8-TON CAPACITY FIBERGLAS FEED STORAGE TANKSThe interior of the THERMO-SHIELD coated tank stayed about 40° F cooler during the daytime.

ST. LOUIS COMPARISON TESTS ON THREE HOUSES, ONE WAS PAINTED WITH THERMO-SHIELD EXTERIOR PAINT.After one year, the THERMO-SHIELD house showed 41.6% less electrical consumption.

FLORIDA HOME WITH THERMO-SHIELD ROOFINGBefore coating, daily temperatures in the attic averaged 125° F, with outside temperatures of 87° F. After coating the roof, the attic temperature dropped to 95° F. After one year, the customer compared his electric bills and found a 29.4% reduction.

LONG TERM HEAT FLUX TESTS OF ROOFING SYSTEMS AT OAKRIDGE NATIONAL LABORATORIES, TENNESSEESummer-long tests closely monitored on actual roofs showed Thermo-Shield Roof Coatings reduced heat flux through the APP Bitumen Roofing System by 75 to 85% during daylight hours each week.

TESTS AT A CERTIFIED JAPANESE LABORATORY ON METAL STORAGE BUILDINGS: Thermo-Shield Exterior Coating outperformed 2” of fiberglass in the walls and 3” in the roof in keeping the interior cooler. The Thermo-Shield building also cooled quicker after the sun went down, reinforcing our belief that bulk insulation stores up heat during the day and keeps the building hotter well into the night.

THERMO-SHIELD PROJECT REFERENCES IN THE MIDDLE EAST

ABU DHABI HH SHEIK ZAYED BIN SULTAN II GRAND MOSQUE

CONCRETE WALLS OF MEP AND WATER FACILITIES - 1999

AMIRI FLIGHT METAL GUTTERS 2003

PUBLIC WORKS DEPARTMENT PRIMARY SCHOOLS, CONCRETE ROOFS - 2003

SHEIKH MOHD. BIN ZAYED PRIVATE WAREHOUSES IN MUSSAFA, METAL ROOFS - 2003

ZAYED SPORTS CITY , NEW INTERNATIONAL TENNIS STADIUM

CONCRETE FLAT ROOFS & OTHER AREAS NEAR STAIRS AND SPECTATORS' SEATS - 2003

GEN. DIRECTORATE OF POLICE MISCELLANEOUS PROJECTS, CONCRETE ROOFS – 2000 TO 2003

SAMALIAH ISLAND ABU DHABI HERITAGE FOUNDATION - ALL WOOD SURFACES (CEILINGS, DOORS, WINDOWS, RAILINGS, BRIDGES, OTHERS) - 2001

AL WATHBA MOSQUE ABU DHABI TOWN PLANNING, CONCRETE ROOF - 1998

HH SHEIK KHALIFA BIN ZAYED’S NEW VILLA AT BATEEN PALACE

CONCRETE MULTIPLE-LEVEL ROOFS - 1998

HH SHEIK KHALIFA BIN ZAYED’S WATER FOUNTAIN AT BATEEN PALACE

WATERPROOFING OF WATER FOUNTAIN - 1998

HH SHEIK SULTAN BIN ZAYED’S LIWA CONSULTANTS, METAL GUTTERS - 2000ABU DHABI GULF HOTEL FIBERGLASS AND WOOD ROOFS - 1998HH SHEIKH KHALIFA BIN ZAYED OLD VILLA IN ABU AL ABIAD

CONCRETE ROOF – 1998

KAMZI VILLA TECHNICAL ARCHITECTS, CONCRETE ROOF – 1998

MOSQUE BETWEEN 2 BRIDGES ABU DHABI TOWN PLANNING, CONCRETE ROOF - 1998

MOSQUE DOME FOR A. AL KHOORI METAL DOME - 1998SHAHAMA MEDICAL CENTER ADMIN BUILDING ABU DHABI PUBLIC WORKS DEPT., CONCRETE

DOME - 1998SKYLIGHT AREA OVER VIP HALL FOR ABU DHABI PUBLIC WORKS MAINT DEPT

CONCRETE AND METAL AREAS - 1998

ZAYED SPORTS CITY BOWLING CENTER ABU DHABI TOWN PLANNING, FIBERGLASS DOMED ROOF – 1998

HYSNA INTERNATIONAL, MINA ZAYED METAL ROOFS AND EXTERIOR WALLS - 1996HIGHER COLLEGES OF TECHNOLOGY FOUNTAIN FLUTES - 1998KADDAS OIL FIELD SERVICES METAL ROOFS – 1997

Ozone Energie Solutions FZE • PO Box 4489, Ras Al Khaimah, UAE • E: [email protected] • T: +971-50-5811920www.thermoshield.me

DUBAIMERCATO MALL EXTERIOR WALLS – 4500 SQUARE METERS,

2011.PALM JUMEIRAH NAKHEEL, CONCRETE DOMES OF VILLAS

UNDER CHINA STATE CONSTRUCTION – 2006AL NASR RESIDENCE CONCRETE CEILINGS AND WALLS OF

UNDERGROUND DRIVE-IN LOADING PARKING AREA – 2006

DIFC PRECINCT BUILDINGS 1, 2, 3, 4, 5 AND 6 DUBAI HOLDING, CONCRETE WALLS OF CARGO AREAS AND TOP LEVELS ON ROOFS – 2005-06

IKEA AT DUBAI FESTIVAL CITY AIR-CONDITIONING DUCTS – 2006 HYPER PANDA AT DUBAI FESTIVAL CITY AIR-CONDITIONING DUCTS – 2006 AL BUSTAN ROTANA HOTEL GAS TANKS – 2006 LE MERIDIEN MINA SEYAHI BEACHRESORT ROOF COAT FOR NEW BARASTI RESTAURANT

– 2007 RYDGES PLAZA CONCRETE ROOF MAINTENANCE WORK –

2007 AL MULLA SHOPPING MALL - 2007 CONCRETE ROOF MAINTENANCE WORK –

2007 DUBAI NEW FRUIT & VEGETABLE MARKET DUBAI MUNICIPALITY , METAL ROOFS – 2004UAE MINISTRY OF EDUCATION & YOUTH EREC BUILDING NO 1, CONCRETE ROOFS –

2002-'03AL FUTTAIM ENGINEERING, DUBAI METAL ROOFS – 2002SHERATON DEIRA ROOF TOP & WOODEN SURFACES FOR POOL

AREA – 2001 DUBAL ASBESTOS ROOF – 2001 DUCAMZ 56 DUBAI CUSTOMS BUILDINGS – CONCRETE

ROOFS – 2001ENGINEER'S OFFICE, DUBAI ROOF FOR RECREATIONAL BLDG, VILLA FOR

SHEIKH MOHD. BIN RASHID AL MAKTOUM, JUMERIA – 2001

ETISALAT CONCRETE AREA IN MAIN BUILDING, THE CREEK AREA – 2001

H H SHEIK SAEED. BIN MOH BIN HASHER AL MAKTOUM

AL FALAJ VILLAS, CONCRETE ROOFS AND WALLS – 1996 AND 2001

HAL CHEMICALS, JEBEL ALI HYDROCHLORIC ACID HOLDING TANKS – 1998 ARABIAN MIX HOUSING FOR ICE MACHINE – 1998 KADDAS OIL FIELD SERVICES JABEL ALI, METAL ROOF – 2001 TOYS R US/ AL FUTTAIM METAL ROOF – 1997GREEN COAST ENTERPRISES METAL ROOF – 1998


OTHER GULF COUNTRIESSABIC (SAFCO), SAUDI ARABIA METAL ROOFS – 2003,2004, 2005ARAMCO, SAUDI ARABIA MISC. BUILDINGS, CONCRETE AND METAL

ROOFS – 2002, 2003, 2004, 2005, 2006A.K. JAHROMI EST., BAHRAIN CONCRETE WALLS – 2001 MINISTRY OF HOUSING, BAHRAIN CONCRETE WALLS – 2000 PRIVATE VILLA, BAHRAIN CONCRETE FLAT ROOF – 2000 ROICC BAHRAIN, BAHRAIN US NAVY CABINS – 2001 WAREHOUSES FOR DEFENSE, BAHRAIN METAL ROOFS – 1999 VILLAS FOR THE HOUSING AUTHORITY, BAHRAIN CONCRETE FLAT ROOFS – 1999QATAR GENERAL PETROLEUM CO. STORAGE TANK W/ FLOATING ROOF – 1998

SOME OF OUR INTERNATIONAL CLIENTSAMOCO OIL CO. MARTIN MARRIETA

BENTLEY POWER COMPANIES

BMW ROLLS ROYCE

BRITISH GOVERNMENT SHELL OIL CO.

BROADMOOR INT. HOTEL TELEPHONE COMPANIES

CANADIAN GOVERNMENT U.S. GOVERNMENT

CHEVRON OIL CO. TEAM CONSULTANT

COLORADO INTERSTATE GAS CO. TEST

COORS BREWERY TRACTABEL

EXXON OIL CO. TURNER INTERNATIONAL

HH SHK. KHALIFA HOSPITAL(QUETTA-PAKISTAN) WINNER

HOLIDAY INNS CRANG & BOAKE


CONSULTANTS FAMILIAR WITH THERMO-SHIELDACG KHATIB & ALAMI

AL BURJ LIWA CONSULTANTS

AL HASHEMI MACE

AL TURATH DMJM

AREX PAN EMIRATES

CONSECO INTL. PARC INTL

HALCROW INTL. PARSONS

HOPKINS RMJM

J.A.JONES SHANKLAND COX

SOME LOCAL USERSABU DHABI PUBLIC WORKS EMIRATES REAL ESTATE CORPORATION

ABU DHABI TOWN PLANNING SHARJAH UNIVERSITY

BP AMOCO, SHARJAH SHEIKH KHALIFA BIN ZAYED PVT. OFFICE

DUBAI ALUMINIUM SHEIKH MOHD. BIN RASHID'S EO

DUBAI HOLDINGS SHEIKH MOHD. BIN ZAYED PVT. OFFICE


thermoshield

Documents

flush mineral

foreign material

avoid showing

replace evaporation

seta flash

ras al khaimah

thermally

correspondingly