The effect of the alkylammonium cation on the optical and physical properties of organic-inorganic perovskite nanoparticles Sigalit Aharon and Lioz Etgar* The Hebrew University of Jerusalem, The Institute of Chemistry, Casali Center for Applied Chemistry, Jerusalem, Israel E-mail: [email protected]Organic-inorganic perovskites (OIPs) function efficiently as active materials in optoelectronic applications. Confined OIP nanostructures are a promising substance for efficient optoelectronic devices. Here we present a facile, low temperature synthesis of OIP nanoparticles (NPs) of well- defined size and shape. To the best of our knowledge, this is the first time that OIP NPs are synthesized under ambient atmosphere having defined cubic shape. As opposed to their inorganic counterparts, the synthesis of OIP NPs is quite challenging, and major efforts should be invested in finding the right ligand for the stabilization of the surface. Three alkylammonium cations (C 8 H 17 NH 3 + / C 12 H 25 NH 3 + / C 18 H 37 NH 3 + ) that stabilize the NPs’ surface were studied. The size and the shape, as well as the optical properties of the NPs, were affected by the length of the alkylammonium cation. The OIP NPs showed a shift in the absorbance and the photoluminescence to higher energies than the OIP bulk. This shift is an evidence for their two-dimensional (2D) nature, which was controlled by the length of the alkylammonium cations. In order to elucidate the effect of the ligands on the optical properties of the NPs, layers of 2D perovskite of the formula (RNH 3 ) 2 (MA) n-1 Pb n X 3n+1 (R is an alkylic residue of the lengths C 8 , C 12 , or C 18 ) were synthesized. It can be concluded that the length of the alkylammonium cations affects the assembly of the OIP NPs and the 2D perovskite layers. In addition, it also influences on the optical and physical properties of the NPs, thus enabling the acquisition of many desired colors from the UV to the visible.
27
Embed
The effect of the alkylammonium cation on the optical and ......Preparation and in-system study of SnCl 2 precursor layers: First step towards the synthesis of Pb-free perovskites
This document is posted to help you gain knowledge. Please leave a comment to let me know what you think about it! Share it to your friends and learn new things together.
Transcript
The effect of the alkylammonium cation on the optical and physical
properties of organic-inorganic perovskite nanoparticles
Sigalit Aharon and Lioz Etgar*
The Hebrew University of Jerusalem, The Institute of Chemistry, Casali Center for Applied
As an emerging photovoltaic technology, hybrid perovskite solar cells have attracted enormous
research attention because of their ease of fabrication and high power conversion efficiencies. A
typical formula for the hybrid perovskite is ABX3, where A stands for cation such as MA, FA, Rb,
and Cs, B is a metal, and X represents a halogen anion). However, MAPbI3 and FAPbI3 have
different properties such as thermal stability, moisture-related degradation, and hysteretic I−V
behavior. The incorporation of MA, Cs, and Rb stabilizes the perovskite structure, resulting in
better PV performance. These facts indicate that using mixed cation perovskites combined with
high-throughput experimentation can lead us to improved perovskites. As such, development of
new mixed-cation perovskites, with lower bandgaps as absorbers and better stability for solar cells
is important.
In this work, combinatorial material science was used, to form FAxMA1-xPbI3, as an opening shot
for further development and research capabilities. The FAxMA1-xPbI3 was synthesized in a
combinatorial library by dip-coating of a MAPbI3 film in a solution of FAI dissolved in 2-propanol
(Cation Exchange). Optical characterizations reveal that the obtained bandgaps for the change
from MAPbI3 to FAxMA1-xPbI3 is 0.19 eV, allowing fine tuning of the bandgap. The cation
exchange process was characterized by x-ray diffraction (XRD) and PL measurements The
capability of tunable bandgaps by different ratio of the mixed-cation in a perovskite indicate its
potential to be used as a new technique to get better absorber materials in photovoltaic devices.
Correlative Scanning Electron and Probe Microscopy Characterization of Inorganic Halide-perovskite-type Materials
Sebastián Caicedo-Dávila1, Carolin Rehermann1, Eva Unger1, Christian Müller2, Michael Sendner3, Robert Lovrincic2, Daniel Abou-Ras1
1 Helmholtz Zentrum Berlin for Materials and Energy, Berlin, Germany 2 Institute for High-Frequency Technology, InnovationLab, TU Braunschweig, Heidelberg, Germany 3 Kirchhoff Institute of Physics, Heidelberg University, Heidelberg, Germany
Understanding what limits the performance in wide-gap, halide-perovskite-based solar cells is a critical issue for the design of high-efficiency devices. Therefore, correlating microscopic electrical and optoelectronic properties with macroscopic material and device characteristics is a fundamental task in research and development. One of the wide-gap, halide-perovskite-based materials of interest is CsPbBr3 (band-gap energy of 2.3 eV). We report preliminary results obtained by using scanning electron microscopy (SEM) imaging, energy-dispersive X-ray spectrometry, and cathodoluminescence at room temperature, which allowed for correlating local composition and optoelectronic properties of CsPbBr3 thin films synthesized by spin-coating and evaporation. Additionally, local transport measurements by scanning probe microscopy were performed on the same areas as the SEM analyses. We will discuss the challenges concerning specimen preparation and the issue of damaging by the electron beam.
Dis-covering Self-Healing in Halide Perovskites
D. R. Ceratti1, Y. Rakita1, L. Cremonesi2, R.Tenne1, V. Kalchenko1, G. Hodes1, Dan
Oron1, M. A. C. Potenza2, D. Cahen1 1Weizmann Institute of Science, 234 Herzl Street, 7610001, Rehovot, Israel.
2Department of Physics and CIMAINA, University of Milan, via Celoria, 16 20133, Milan, Italy.
Quantifying hysteresis: developing tools to characterize the transient response of metal halide perovskite devices on different time scales.
A. Czudek, L. Kegelmann, M. Jost, K. Hirselandt, P. Tockhorn, E. Unger
Hysteresis is among the most debated phenomena in metal halide perovskite solar cell research1. Apart from being an obstacle and source of inaccuracy in reported device efficiency metrics, the underlying causes for hysteresis can be related to reversible and irreversible changes in devices. If evaluated as a quantitative metric, hysteresis can be an indicator of transient processes in devices that might affect long term stability. We employed two different approaches to quantify hysteresis phenomena in different device types prepared in our laboratory. The first is a detailed analysis of the hysteresis index as function of delay time, inspired by the work of Cahen et al.2. The second is the analysis of current transients upon voltage steps to extract time constants of the transient response3.
Hysteresis indices can be a valid method of characterization of perovskite solar cells, as long as they are not used at one single scan condition, but analyzed as a function of delay time. These plots often exhibit "peaks" that indicate the temporal regimes of maximum discrepancy (hysteresis), which provides direct insight into time constants of capacitive effects causing current-voltage hysteresis. We here present a quantitative comparison between different architecture types and discuss how the nature of the interface between selective contact and and perovskite critically influence the magnitude and temporal response domain of metal halide perovskite solar cells. In comparison, we analyzed and transient photocurrent response time constants. We discuss data for different device types using these two different analysis approaches to compare the practical value of these characterization methods forthe quantification of hysteresis phenomena in metal halide perovskite devices. Both can be used as quantitative tools to determine the magnitude and timescale of processes responsible for hysteresis and provide reliable comparison between different cell architectures.
1. Unger, E. L. et al. Hysteresis and transient behavior in current–voltage measurements of hybrid-perovskite absorber solar cells. Energy Environ. Sci. 7, 3690–3698 (2014).
2. Levine, I. et al. Interface-dependent ion migration/accumulation controls hysteresis in MAPbI3 solar cells. J. Phys. Chem. C 120, 16399–16411 (2016).
3. Christoforo, M., Hoke, E., McGehee, M. & Unger, E. L. Transient Response of Organo-Metal-Halide Solar Cells Analyzed by Time-Resolved Current-Voltage Measurements. Photonics 2, 1101–1115 (2015).
Preparation and in-system study of SnCl2 precursor
layers: First step towards the synthesis of Pb-free
perovskites at EMIL
Roberto Félix,1 Núria Llobera-Vila,1 Claudia Hartmann,1 Carola Klimm,1 Dan
R. Wargulski,1 Manuel Hartig,1,2 Regan G. Wilks,1,3 and Marcus Bär1,3
1Renewable Energy, Helmholtz-Zentrum Berlin für Materialien und Energie GmbH, Hahn-
Meitner-Platz 1, D-14109 Berlin, Germany 2 Technologie für Dünnschicht-Bauelemente, Technische Universität Berlin - Fak. IV, HFT 5-
2, Einsteinufer 25, D-10587 Berlin, Germany 3Energy Materials In-Situ Laboratory Berlin (EMIL), Helmholtz-Zentrum Berlin für
Materialien und Energie GmbH, Albert-Einstein-Straße 15, D-12489 Berlin, Germany
Hybrid organic-inorganic metal halide perovskite-based solar cells – particularly those using
APbX3 (A = CH3NH3+, HC(NH2)2
+, Cs+ and X = I-, Cl-, Br-) as the absorber layer – have
demonstrated rapid improvement in power conversion efficiencies in recent years, reaching
values in excess of 21% for lab-scale devices. A major concern related to this type of absorber
is the toxicity of the Pb. Ongoing efforts to replace Pb by Sn have so far yielded relatively low-
performing solar cells, likely limited by defect formation in the absorber material due to the
tendency of Sn to oxidize from Sn+2 to Sn+4. Preparing Sn-based perovskite films under vacuum
conditions may be the key to inhibiting Sn oxidation and improving cell performance.
We present the first experimental results towards synthesizing Pb-free perovskite thin-films at
the Energy Materials In-Situ Laboratory Berlin (EMIL). A detailed x-ray photoelectron and
Auger electron spectroscopy study of SnCl2 precursor layers of different thicknesses vacuum-
deposited on Mo/glass substrates reveals significant changes in the chemical environment of
Sn and Cl along the layer profile. These findings show the effect that substrate conditions can
exert on the deposited material.
Structural and Compositional Analyses of Perovskite-like Cesium Lead Halides Hannah Funk, Carolin Rehermann, Eva Unger, Robert Lovrincic, Christian Müller, Michael Sendner, Frederike Lehmann, René Gunder, Alexandra Franz, Daniel Abou-Ras Inorganic CsPbX3 (X=I, Cl, Br) thin films are investigated as supposedly more stable alternative to methyl-ammonium-containing, perovskite-like CH3NH3PbI3 layers for thin-film solar cells. For the present contribution, wide-gap CsPbBr3 thin films were synthesized by spin-coating and evaporation. In addition, also corresponding powder samples were produced as reference. Structural properties were obtained by X-ray diffraction as well as by high-resolution imaging and electron diffraction in transmission electron microscopy, while elemental distributions were analyzed by means of energy-dispersive X-ray spectrometry. Evaluation of these results has so far not resulted in unambiguous phase identification of the Cs-Pb-Br thin films, in contrast to the powder sample. The present contribution will report also about experiences with beam damage in the electron beam and how to avoid it.
High Resolution Study of TiO2 Contact Layer Thickness on the
Performance of Over 800 Perovskite Solar Cells
Laxman Gouda,† Kevin J. Rietwyk,+ Jiangang Hu, Adi Kama, Adam Ginsburg, Maayan Priel, David A.
Keller, Shay Tirosh, Simcha Meir, Ronen Gottesman and Arie Zaban*
Department of Chemistry, Institute for Nanotechnology & Advanced Materials, Bar-Ilan University,
Ramat Gan 5290002, Israel.
Abstract:
In this research, we systematically explore the influence of the TiO2 thickness with nanometric
variations over a range of 20–600 nm on the photovoltaic parameters (open-circuit voltage, short circuit
current, fill-factor and power conversion efficiency) of CH3NH3PbI3 based solar cells. We fabricate
several sample libraries of 13 × 13 solar cells on large substrates with spatial variations in the thickness
of TiO2 layers while maintaining similar properties for the other layers. We show that the optimal
thickness is ~ 50 nm for maximum performance; thinner layers typically resulted in short circuited cells
while increasing the thickness led to a monotonic decrease in performance. Furthermore, by assuming
a fixed bulk resistivity of TiO2 we were able to correlate the TiO2 thickness to the series and shunt
resistances of the devices and model the variation in the photovoltaic parameters with thickness using
the diode equation to gain quantitative insights.
S. Gupta, 10-2017
The Critical Roles of SnF2 in the Optoelectronic Properties of Lead-
Free Tin Halide Perovskites
Satyajit Gupta, Tatyana Bendikov‡, Gary Hodes
* and David Cahen
*
Department of Materials & Interfaces Weizmann Institute of Science, Rehovot, 76100,
Israel. ‡Chemical
Research Support Unit, Weizmann Institute of Science, Rehovot, 76100, Israel.
Lead-based halide perovskites (APbX3) have shown a dramatic improvement in
efficiencies in the past few years. Due to toxicity issues of lead, tin-based halide
perovskites are being studied. It is observed that tin fluoride (SnF2) addition can generally
improve the device properties of tin-based halide perovskites. This effect is thought to be
due to suppression of Sn(II) Sn(IV) oxidation, Sn(II)Sn (0) reductions, and /or a
decrease in Sn vacancy concentration. All these effects will change the doping, but in
opposite directions. Here we report on the role of SnF2 concentration on various
properties of cesium tin bromide (CsSnBr3)-based halide perovskite, such as energetics
(work function - WF and ionization energy, IE, X-ray beam damage and device properties.
We find that the SnF2 concentration strongly influences the device properties (open
circuit voltage-VOC, short circuit current-ISC, fill factor-FF and photoconversion
efficiency-η) but not the work function (WF) or ionization energy By monitoring the XPS
signals over time as a function of SnF2 concentration, we find that pristine CsSnBr3
(without SnF2 added) is highly susceptible to X-ray beam damage if deposited on titania
(TiO2), gold (Au) or poly(3,4-ethylenedioxythiophene) polystyrene sulfonate
(PEDOT:PSS) substrates, but is stable if deposited on ZnO substrates. About 5 mol% of
SnF2 was sufficient to protect the perovskite from beam damage on all the substrates,
possibly because of a SnF2-induced change in the Sn2+
/Sn0 electrochemical potential that
makes that process energetically less probable. For solar cells adding ~20 mol% of SnF2
was found to be optimum for device performance. Time-resolved surface photovoltage
(SPV) results are consistent with SnF2 addition reducing trap state concentration. Apart
from that, we found that SnF2 (1) improves conduction band-alignment of the perovskite
with TiO2, at their interface in a solar-cell (2) making the perovskite somewhat less ‘n-
type’, compared to highly n-doped pristine CsSnBr3.
Abstract 24/10/17
Utilizing combinatorial material science and high-throughput
analysis as a new method to promote and improve the field of
Department of Chemistry, Center for Nanotechnology & Advanced Materials, Bar-Ilan
University
In order to accelerate the process of developing and improving perovskite materials and
device structures, a combinatorial synthesis approach with high-throughput analysis
techniques is applied. In the combinatorial method we define a library as a single
substrate with 169 individual experiments, which are individual solar cells, making it
possible to study more materials and gain more knowledge about them. In our lab we
adapted all measurements to suit and automatically scan the libraries.
This work focuses on the interface between the electron selective contact, TiO2, and the
perovskite absorbing material, MAPbI3. Throughout this interface, many charge transfer
processes occur. Forward movement, injection of electrons in to conduction band of TiO2,
contribute to solar cell photocurrent, as well as some recombination processes that reduce
solar cell photocurrent. In order to affect this interface, increase injection of electrons,
and reduce recombination rate, different thin insulating oxide layers were applied in
between the TiO2 and the perovskite. By preventing the electrons from going back to the
perovskite layer, the recombination rates at this interface were reduced, with the intension
of improving solar cell performance. Characterization was performed by high-throughput
analysis and combinatorial material science methods.
Abstract
Submitted by: Hadar Kaslasi (MSc.)
Supervisor: Prof David Cahen
Synthesis and Characterization of Mixed Cesium-Methylammonium Lead
Bromide Single Crystals
Hadar Kaslasi, Y. Rakita, G. Hodes, D. Cahen.
Weizmann institute of Science, Department of Materials and Interfaces, Rehovot, Israel, 7610001;
Halide perovskites (APbX3) are an intriguing group of optoelectronic materials, due, in part, to
their remarkably high open circuit voltages. These voltages make them relevant for use in
photovoltaic solar cells as, for instance, a high photo energy-absorbing component in a tandem
solar cell configuration. In this context, two types of high bandgap X=Br perovskites are of
special interest: The Cubic hybrid organic−inorganic Methylammonium lead bromide
perovskite (MAPbBr3) and its orthorhombic, all inorganic analog, CsPbBr3. MAPbBr3 Shows
somewhat better open circuit voltages than CsPbBr3 which is, in turn, more stable. To
understand the role of the A group (i.e. organic vs. in-organic) and its influence on these
desirable properties, fundamental studies of mixed single crystals with both the organic MA
and inorganic Cs cations are needed. We present first results of the growth of such crystals
with varying Cs/methylammonium (Cs/MA) ratios, and their characterization using structural
and compositional techniques.
Mixtures of PEDOT and dopant-free Spiro-OMeTAD
as hole selective contact in regular perovskite solar cells
Lukas Kegelmann1, Christian M. Wolff2, Philipp Tockhorn1, Lars Korte1, Dieter Neher2,
Bernd Rech1, Steve Albrecht3 1 Helmholtz-Zentrum Berlin, Institute Silicon Photovoltaics, Berlin, 12489, Germany.
2 University of Potsdam, Institute of Physics and Astronomy, Potsdam, 14476, Germany. 3 Helmholtz-Zentrum Berlin, Young Investigator Group Perovskite Tandem Solar Cells,
The highest efficiencies of regular perovskite solar cells reported to date are obtained
with doped hole selective contacts (HSC).[1,2] Although these dopants are necessary to
provide sufficient conductivity in the HSC, they were shown to impose the dominating
source for non-radiative recombination in high efficiency solar cells.[3] It is therefore of
key importance to suppress recombination losses at the perovskite/HSC interface in
order to increase the open circuit voltage (VOC) and consequently the efficiency of the
solar cells.
In this study, a poly(3,4-ethylenedioxythiophene) (PEDOT) layer doped with sulfonated
copolymers is coated from a water-free dispersion and used as the HSC in regular
perovskite solar cells. By adding undoped 2,2′,7,7′-tetrakis(N,N-di-p-
methoxyphenylamine)-9,9′-spirobifluorene (Spiro-OMeTAD) into the PEDOT
dispersion, the VOC of the resulting devices increases to above 1.15 V. This even exceeds
the VOC for reference solar cells prepared here with doped Spiro OMeTAD as HSC.
Furthermore, the stabilized efficiency is boosted beyond 15 % which more than doubles
the highest value of around 7.5 % reported so far for regular perovskite solar cells
comprising PEDOT as the hole contact.[4,5]
Transient photoluminescence and electroluminescence measurements imply enhanced
hole extraction at the perovskite interface for solar cells with Spiro-OMeTAD enriched
PEDOT layers. Photoelectron spectroscopy reveals a strong shift in ionisation energies at
the surfaces of the mixed PEDOT layers and conductivity measurements shows a linear
dependence of lateral conductivity of the resulting mixed films with the amount of added
Spiro-OMeTAD. Both results indicate a homogeneus distribution of Spiro-OMeTAD
throughout the PEDOT layer and the shift in ionization energies correlates with the
increase in VOC observed for the resulting solar cells.
In conclusion, a mixture of PEDOT and Spiro-OMeTAD as HSC is introduced in this
study. The high VOC values achieved for solar cells with this mixed HSC indicate
suppressed recombination losses at the perovskite/HSC interface by the dopant-free
Spiro-OMeTAD while the significantly more conductive PEDOT facilitates charge
transport to the metal electrode. This mixed material approach and its capability to omit
dopant-induced recombination losses might therefore provide potential to further
enhance the overall efficiencies in regular perovskite solar cells.
References
[1] M. Saliba, T. Matsui, K. Domanski et al., Science (2016), vol. 354, pp. 206–209.
[2] W.S. Yang, B.-W. Park, S.I. Seok et al., Science (2017), vol. 356, pp. 1376–1379.
[3] J.-P. Correa-Baena, W. Tress, A. Hagfeldt et al., Energy Environ. Sci. (2017),
vol. 10, pp. 1207–1212.
[4] J. Liu, S. Pathak, H.J. Snaith et al., J. Phys. Chem. Lett. (2015), 6 (9), 1666–1673.
[5] Y. Hou, H. Zhang, C. Brabec et al., Adv. Energy Mater. (2015), 5 (15), 1500543.
Control over self-doping in high-band gap perovskite films
Michael Kulbak1, Igal Levine
1, Einav Barak-Kulbak
1, Gary Hodes
1, Doron Azulay
2, Oded Milo
2,
Isaac Balberg2*
and David Cahen1
1Dept. of Materials & Interfaces, Weizmann Inst. of Science, Rehovot 76100, Israel
2The Racah Institute, The Hebrew University, Jerusalem 91904, Israel
The effects of different cations and anions on carrier diffusion lengths and formation of a
junction in high bandgap halide perovskite (HaP) film-based solar cells is studied in
detail. HaP cells are of interest as high bandgap ones in solar spectrum splitting for
boosting solar to electrical energy conversion efficiency/area by adding them to c-Si
photovoltaic cells and driving photo-electrochemical reactions for chemical energy
storage. Resolving how the addition of cations and anions change the (unintentional)
doping of the HaP is of great importance for understanding the film and device physics as
well as for performance improvement. We study Pb-based, APbX3, HaP films, where A
can be a mixture of formamidinium, methylammonium and cesium and X a mixture of
bromine and chlorine, using a combination of Dark-conductivity, Photoconductivity and
Steady-State Photocarrier-Grating (SSPG) techniques [1]. This way we measure the
effect of the different cations and anions compositions on the majority and minority
carrier diffusion lengths. We also use Electron Beam Induced Current (EBIC), [2] to
identify the formation of the junction and built-in voltage and to track the position and
size of the space charge region width following the changes in the HaP composition. In
some HaP structures, EBIC is needed to measure diffusion length when it is
unmeasurable in SSPG. We find mixed-cation HaP form a p-i-n junction with relatively
long and ambipolar carrier diffusion lengths, in contrast to the single cation based
bromide HaPs, who form a p-n junction and shorter diffusion lengths.
References
[1] I. Levine, et al., J. Phys. Chem. Lett. 2016, 7, 5219.
[2] N. Kedem, M. Kulbak, et al., Phys. Chem. Chem. Phys. 2017, 19, 5753.
Polyoxometalate as novel materials for Perovskite Solar Cells
Yasemin Topal1,2
, Esma Yenel2, Mahmut Kuş
2
1Pamukkale Üniversitesi Çal Meslek Yüksek Okulu, Çal, Denizli, Turkey
2Selcuk University Advanced Technology Research and Application Center, Konya, Turkey,
Perovskite solar cells (PSCs) have been gaining great attention due to their low cost and high
efficiency. However, reporoducibility and stability problems are main disadvantages must be
solved for large area production and commezilation.
Here we report interface engineering for improving the satbility and reporducibility of PSCs.
Polyoxometalates (POMs) whihc are interesting clusters and exhibit excellent optical and
electrochemical behaviours used as surface modification agent at c-TiO2 and perovskite
interface. Modification of c-TiO2 surface with POM derivatives leads decrease in pin holes on
c-TiO2 surface and thus efficiency increases. The average increase in efficiency is around
20% in comparison with reference PSC. Beside using POMs as surface modification material,
they also used as electron transport layer in inverted type of PSCs. The results show that
POMs are extremely interesting material as electron transport layer as well as a material for
interface engineering.
Measurement of Mobility-Lifetime products in MAPbI3 films
Igal Levine1, Doron Azulay2 , Satyajit Gupta1, Gary Hodes1, David Cahen1, Oded Millo2 and Isaac
Balberg2
1Dept. of Materials & Interfaces, Weizmann Inst. of Science, Rehovot 76100, Israel
2The Racah Institute, The Hebrew University, Jerusalem 91904, Israel
Photovoltaic solar cells operate under steady-state conditions that are established during charge
carrier excitation and recombination. However, hitherto no model of the steady-state
recombination scenario in the Halide Perovskites has been proposed. Here we present such a
model that is based on a single type of recombination center, which is deduced from our
measurements of the illumination intensity-dependence of the photoconductivity and the
ambipolar diffusion length in those materials. We find that the dominant recombination
mechanism is trap-mediated via a recombination level lying close to mid-gap. We also find that
under steady-state illumination conditions MAPbI3 is ambipolar, with hole and electron diffusion
lengths of ~800 and 350 nm, respectively.
Is it possible to identify solar illumination-induced phase segregation in perovskite thin-film solar cells
absorber by hard x-ray photoelectron spectroscopy?
D. Liu1, C. Hartmann1, E. Handick1, R. Félix1, R.G. Wilks1,2, E.L. Unger3,4, M. Bär1,2,5
1 Renewable Energy, Helmholtz-Zentrum Berlin für Materialien und Energie GmbH (HZB), Hahn-Meitner Platz 1,
14109 Berlin, Germany
2 Energy Materials In-Situ Laboratory Berlin, Helmholtz-Zentrum Berlin für Materialien und Energie GmbH,
Albert-Einstein-Straße 15, 12489 Berlin, Germany
3 Institut für Silizium-Photovoltaic, Helmholtz-Zentrum Berlin für Materialien und Energie GmbH, Kekuléstrasse 5,
12489 Berlin, Germany
4 Chemical Physica and Nano Lund, Lund University, Box 124, SE-22100 Lund, Sweden
5 Institut für Physik und Chemie, Brandenbrgische Technische Universität Cottbus-Senftenberg, Platz der Deutschen
Einheit 1, 03046 Cottbus, Germany
It has been observed that in methylammonium lead and cesium lead bromide-iodide perovskite solar cells the VOC of
the device increases with the band gap of the absorber, which increases with bromine concentration, up to a certain
saturation point. The VOC then cannot be increased further until a pure bromide perovskite absorber is used, at which
point the VOC attains the expected value. It is believed that in certain cases this behavior is related to illumination-
induced phase segregation - the so-called “Hoke Effect.” Aiming at studying this effect, we have measured
CH3NH3Pb(Br0.75I0.25)3, CsPb(Br0.75I0.25)3, and CsPb(Br0.5I0.5)3 films on FTO using hard x-ray photoelectron
spectroscopy (HAXPES) before, during, and after illumination. Focusing on the spectral changes in the core level
and valence band HAXPES spectra, we hope to gain insight into related changes in chemical and electronic
structure. In our contribution, we compare the composition dependence of our results to published observations of
the effects and likelihood of illumination-induced phase segregation.
Photoluminescence Excitation Microsocpy of Halide Perovskite Material
Aboma Merdasaa, Alexander Kiligaridisb, Jonas Stöberb, Caroline Rehermanna, Katrin Hirselandta, Boris
Louisb, Marina Gerhardc, Eva L. Ungera,b, Ivan Scheblykina
aHelmholtz-Zentrum Berlin für Materialen und Energie GmbH, Kekulestraße 5, 12489 Berlin, Germany dDepartment of Chemical Physics, Lund University, P.O. Box 118, 22100 Lund, Sweden
In this work, the second step of this sequential deposition is monitored by in-situ UV-vis
measurements. The second step is the conversion from a lead iodide (PbI2) film into a mixed
halide perovskite film MAPb(IxBr1-x)3 by immersion of MABr. Using MABr we can distinguish
different reaction products and hence reaction pathways and track the different conversion
kinetics between a direct conversion and a dissolution-reformation process. The influence of
following parameters is investigated: film thickness and morphology, reaction time and
concentration of the MABr dipping solution. Additional UV-vis, SEM and XRD measurements
after annealing are carried out to complete the study.
In-situ UV-vis measurements show a change of the evolution of the absorption onset of the
direct conversion product, MAPbBrI2, that disappears over time in favor ofa pure dissolution-
reformation product of MAPbBr3. Due to the two competing reaction pathways, the PbI2 films
are converted into a perovskite phase with varying halide composition in MAPb(IxBr1-x)3
depending on dipping time and film thickness. XRD shows residual PbI2 not converted in the
dipping step. Dependencies on reaction parameters are giving insights into the reaction
pathway. Our experiments allow us to distinguish the two different reaction pathways and under
which conditions one or the other product is favored. Understanding transformation is necessary
to control degree of material conversion and morphology.
1. Unger, E. L.; Kegelmann, L.; Suchan, K.; Sorell, D.; Korte, L.; Albrecht, S., Roadmap and roadblocks for the band gap tunability of metal halide perovskites. Journal of Materials Chemistry A 2017, 5 (23), 11401-11409. 2. Burschka, J.; Pellet, N.; Moon, S.-J.; Humphry-Baker, R.; Gao, P.; Nazeeruddin, M. K.; Gratzel, M., Sequential deposition as a route to high-performance perovskite-sensitized solar cells. Nature 2013, 499 (7458), 316-319.
3. Ummadisingu, A.; Steier, L.; Seo, J.-Y.; Matsui, T.; Abate, A.; Tress, W.; Grätzel, M., The effect of illumination on the formation of metal halide perovskite films. Nature 2017, advance online publication. 4. Ko, H.; Sin, D. H.; Kim, M.; Cho, K., Predicting the Morphology of Perovskite Thin Films Produced by Sequential Deposition Method: A Crystal Growth Dynamics Study. Chemistry of Materials 2017, 29 (3), 1165-1174.
Structural investigation of organic-inorganic perovskite
based solar cells with carbon cathodes
Avi Schneider, Lioz Etgar
The Institute of Chemistry at the Hebrew University of Jerusalem
Organic-Inorganic Perovskite photovoltaics have gained much scientific attention over the
past decade as a potential competitor or complimentary strategy for the currently prevalent
and commercialized solar cell technologies. In recent years a number of groups have focused
their research on replacing the expensive metal counter electrodes of the cells with carbon
based electrodes, with the general goal of lowering production costs. In 2013 Han et. al.
reported a novel cell structure based on the use of a screen printed conductive porous
carbon film as the counter electrode of the cell, through which the photoactive Perovskite
solution is filtrated, reaching and penetrating the functional layers beneath it. Benefits of
this structure include a large area of interface between light absorber and counter
electrode, increased stability of the cell due to the hydrophobicity of the carbon, and a
better compatibility for large scale production, owing to the simple and cheap methods and
materials. Other cell structures and methods, implementing Carbon films as their counter
electrodes, have been reported by various groups over the past few years, making carbon
based PSC's a quite popular approach to overcoming some of the present limitations of this
type of cell. Though the various Carbon based PSC's show much promise, they are still
lacking in performance when compared with some of the leading Perovskite cell structures.
Our main goal in this research is to explore ways to improve the photovoltaic performance
of carbon based PSC's, while maintaining the low cost and simple fabrication methods of
these cells. Our strategies involve thorough investigation of the nano-scale structure of
these cells while intelligently tailoring new methods and materials aimed at maximizing the
performance of this specific cell type. A significant improvement could label these cells as
the most suitable Perovskite based cells for commercial mass production.
Au - Decorated ZnO Nanorod Arrays for Mixed-cation Lead Mixed-halide Perovskite
Photovoltaics
Tulusa,b, Magdalena Marszaleka, Andreas Peukerta, Martin Slamana, Yulia Galaganc, Simon
Christian Böhmea and Elizabeth von Hauff a
a. Physics of Energy, Faculty of Sciences, Vrije Universiteit Amsterdam, The Netherlands.
b. Center of the Polymer Technology, Agency for the Assessment and Application of Technology
(BPPT), Indonesia.
c. Solliance / TNO Eindhoven, Eindhoven, The Netherlands
Abstract
We fabricated ZnO nanorods decorated with Au nanoparticles for electron transport layers in
perovskite solar cells. We compared the performance of double : Cs/ FA and triple : Cs/FA/MA cation
with mixed double halide : I/ Br perovskite layers in this configuration . The current-voltage
characteristics and impedance spectra indicate that Au improves charge extraction in the devices,
confirmed by changes in the photoluminescence spectra. The use of Au particles in the solar cells
resulted in an increase in power conversion efficiency from 11.52 % to 12.62 % (double cation) and