EBSD EBSD Steel Datasheet Datasheet part # 51-H5-057 Related to sample part # 51-H5-056 Introduction Oxford Instruments supplies an electro-polished austenitic stainless steel sample with every new EBSD system to assist you with getting started with EBSD data acquisition and post-processing. This report provides guidelines for acquiring and analysing EBSD data using this sample. For more detailed instructions please refer to the manuals provided with the system. Sample Details and Preparation This sample, extracted from a sheet of austenitic stainless steel, was mechanically planed and electro-polished in the central region as shown by the optical image in Fig. 1a. The electro-polishing was conducted using electrolyte A3 at 14°C and 30 V. Fig.1b is a schematic diagram of the sample, where the cut corners give reference to the rolling (RD) and transverse (TD) directions. As shown by Fig. 1c, in this analysis, the sample was mounted in the SEM, so that the RD was aligned to the SEM stage tilt axis and the cut corners were on the right hand side of the sample as seen by the EBSD detector. We recommend that you mount the sample in the same way so that your orientation data can be compared directly to that presented later in this report. Fig. 1a. Optical image of the sample – the sample length is approximately 5 mm. Fig. 2. An FSD image of the sample acquired at 70º tilt. If your Nordlys detector is fitted with forward scatter diodes (FSD), this type of image can be collected using the lower two diodes and is useful for showing orientation contrast, giving you an idea of the step size you need to use to resolve the grains satisfactorily. If your Nordlys detector also has the upper diodes fitted, these can be used for showing atomic number contrast and identifying where the different phases lay in the sample. Fig.1b. Schematic diagram of the sample dis- playing the rolling and transverse directions with respect to cut corners. Fig.1c. Schematic diagram of the sample position relative to the EBSD detector. TD RD Tilt axis 250 mm
4
Embed
Steel sample datasheet - Microscopy Consumablesmicroscopyconsumables.com/.../EBSD_Steel_Datasheet_51-H5-057.pdf · Oxford Instruments supplies an electro-polished austenitic ... The
This document is posted to help you gain knowledge. Please leave a comment to let me know what you think about it! Share it to your friends and learn new things together.
Transcript
EBSDEBSD Steel DatasheetDatasheet part # 51-H5-057
Related to sample part # 51-H5-056
IntroductionOxford Instruments supplies an electro-polished austenitic stainless steel sample with every new EBSD system to assist you with getting started with EBSD data acquisition and post-processing. This report provides guidelines for acquiring and analysing EBSD data using this sample. For more detailed instructions please refer to the manuals provided with the system.
Sample Details and Preparation This sample, extracted from a sheet of austenitic stainless steel, was mechanically planed and electro-polished in the central region
as shown by the optical image in Fig. 1a. The electro-polishing was conducted using electrolyte A3 at 14°C and 30 V. Fig.1b is
a schematic diagram of the sample, where the cut corners give reference to the rolling (RD) and transverse (TD) directions. As
shown by Fig. 1c, in this analysis, the sample was mounted in the SEM, so that the RD was aligned to the SEM stage tilt axis and
the cut corners were on the right hand side of the sample as seen by the EBSD detector. We recommend that you mount the
sample in the same way so that your orientation data can be compared directly to that presented later in this report.
Fig. 1a. Optical image of the sample – the sample length is approximately 5 mm.
Fig. 2. An FSD image of the sample acquired at 70º tilt.
If your Nordlys detector is fitted with forward
scatter diodes (FSD), this type of image can be
collected using the lower two diodes and is useful
for showing orientation contrast, giving you an idea
of the step size you need to use to resolve the grains
satisfactorily. If your Nordlys detector also has the
upper diodes fitted, these can be used for showing
atomic number contrast and identifying where the
different phases lay in the sample.
Fig.1b. Schematic diagram of the sample dis-playing the rolling and transverse directions with respect to cut corners.
Fig.1c. Schematic diagram of the sample position relative to the EBSD detector.
TD
RD
Tilt axis
250 mm
EBSD Analysis
The data presented in this datasheet was collected using the Oxford Instruments AZtecHKL EBSD system with a NordlysMax2
EBSD detector.
Prior to EBSD mapping, the major constituent phases in the sample should be identified using the EBSD and / or EDS system. This
sample only contains austenitic steel which can be indexed using the iron FCC phase from the HKL Phases database. An example
of a typical EBSD pattern is shown in Fig. 3a. Fig. 3b, shows how this EBSP can be correctly indexed using the Iron FCC phase.
The conditions used to acquire the EBSD data presented here are given in Table 1. However, it is not necessary to use identical
settings, although you should ensure that the area mapped includes sufficient grains in order to get reasonable statistics.
Raster 1069 x 801 pixels
Step size 1.0 μm
Solver Refined Accuracy
Number of Bands 12
Hough Resolution 70
EBSD Camera Binning Mode 6 x 6
EBSD Camera Gain 3
Hit rate 98.4% Table 1: EBSD acquisition settings.
Grain Detection can be used to reconstruct individual grains in an EBSD map. Once this has been done various parameters
including the grain diameter, area and aspect ratio can be determined.
In this study, a grain was defined as a region of ten or more pixels being completely surrounded by boundaries that have
a misorientation angle larger than a critical value of 10° (shown by the black lines in Fig. 4). Furthermore, the special twin
boundaries (60º misorientation around the 111 axis) shown by the red lines in Fig. 4, were excluded as they may be considered
part of the parent grains.
Once the grain parameters had been defined and the grains detected, a summary of the statistics for the grains is given in the
Grain Statistics window, which displays statistical information about the grain reconstruction parameters. As can be seen from
Table 2, in this example, ~1900 grains were analysed with an average grain size of ~20 μm. Note that the grain size may vary
from the value given here due to statistical variation of the number of grains.
Average, Expectation 20.0
Standard Deviation 11.5
Minimum Value 3.6
Maximum Value 83.5
Number of Grain (not including border grains) 1888Table 2: The grain size statistics.
ConclusionIn this report, a brief EBSD analysis has been presented for the Austenitic Steel sample provided with your EBSD system. It details the methodology of acquiring the EBSD map data and describes how the microstructure was interpreted in terms of texture and average grain size.
Meanwhile, the contoured IPF for the RD shown in Fig. 6, is
a typical example of a rolling texture as would be expected
given that the sample is cut from a rolled sheet and the
alignments are as indicated in Fig. 1b.
Fig. 6: Inverse pole figure showing a high intensity