MEHMET SARIKAYA*1,2,CANDAN TAMERLER1,3,ALEX K. -Y. JEN1, KLAUS SCHULTEN4
AND FRANÇOIS BANEYX2,5
1Materials Science & Engineering,2Chemical Engineering and5Bioengineering,University of Washington,Seattle,Washington98195,USA3Molecular Biology and Genetics, Istanbul Technical University,Maslak, Istanbul,80626,Turkey4Theoretical Biophysics,Beckman Institute,University of Illinois,Urbana-Champaign, Illinois 61801,USA*e-mail: [email protected]
There is a rich and long history of gaining inspirationfrom nature for the design of practical materials andsystems1–4.Traditionally,biomimeticists, inspired bybiological structures and their functions, focused onemulating or duplicating biosystems using mostlysynthetic components and following traditionalapproaches5–7.With the recent developments ofmolecular8 and nanoscale9 engineering in physicalsciences,and advances in molecular biology10,biomimetics is now entering the molecular scale11,12.By combining nature’s molecular tools with syntheticnanoscale constructs,molecular biomimetics isemerging as a hybrid methodology13.
Materials have uniquely functional properties atnanometre-scale dimensions that, if harnessedeffectively,could lead to novel engineering systems withhighly useful characteristics14,15.Mechanical propertiesof nanostructured composites,electronic properties oflow-dimensional semiconductors,magnetic propertiesof single-domained particles,and solution properties ofcolloidal suspensions,are all attractive and interesting,
and correlate directly to the nanometre-scale structuresthat characterize these systems16,17.The realization of thefull potential of nanotechnological systems,however,has so far been limited due to the difficulties in theirsynthesis and subsequent assembly into usefulfunctional structures and devices.Despite all thepromise of science and technology at the nanoscale,the control of nanostructures and ordered assemblies of materials in two- and three-dimensions still remainslargely elusive14,18.
Biomaterials,on the other hand,are highlyorganized from the molecular to the nano- andmacroscales,often in a hierarchical manner,withintricate nano-architectures that ultimately make up amyriad of different functional soft19 and hard tissues20
(Fig. 1)21–23.Under genetic control,biological tissues aresynthesized in aqueous environments under mildphysiological conditions using biomacromolecules,primarily proteins but also carbohydrates and lipids.Proteins both collect and transport raw materials,andconsistently and uniformly self- and co-assemblesubunits into short- and long-range-ordered nuclei andsubstrates6,7,20.Whether in controlling tissue formation,biological functions or physical performance,proteinsare an indispensable part of biological structures andsystems.A simple conclusion is that next-generationbiomimetic systems should include protein(s) insynthesis,assembly or function11–13.
Engineering materials are synthesized using acombination of approaches, for example,melting andsolidification processes, followed by thermomechanicaltreatments,or solution/vacuum deposition and growthprocesses24. In many cases,however, the final product isdictated by the kinetics and thermodynamics of thesystem and often achieved through ‘heat-and-beat’approaches24,25 (Fig. 2).By contrast, in biological
Molecular biomimetics: nanotechnologythrough biologyProteins, through their unique and specific interactions with other macromolecules and inorganics, control
structures and functions of all biological hard and soft tissues in organisms. Molecular biomimetics is an
emerging field in which hybrid technologies are developed by using the tools of molecular biology and
nanotechnology. Taking lessons from biology, polypeptides can now be genetically engineered to specifically
bind to selected inorganic compounds for applications in nano- and biotechnology. This review discusses
combinatorial biological protocols, that is, bacterial cell surface and phage-display technologies, in the
selection of short sequences that have affinity to (noble) metals, semiconducting oxides and other
technological compounds. These genetically engineered proteins for inorganics (GEPIs) can be used in the
assembly of functional nanostructures. Based on the three fundamental principles of molecular recognition,
self-assembly and DNA manipulation, we highlight successful uses of GEPI in nanotechnology.
systems,evolutionary selection processes result inspecific molecular recognition26,27.
In molecular biomimetics11–13, a marriage of thephysical and biological fields, hybrid materials couldpotentially be assembled from the molecular levelusing the recognition properties of proteins (Fig. 2)under the premise that inorganic surface-specificpolypeptides could be used as binding agents tocontrol the organization and specific functions ofmaterials. Molecular biomimetics simultaneouslyoffers three solutions to the development of hetero-functional nanostructures. The first is that proteintemplates are designed at the molecular level throughgenetics. This ensures complete control over themolecular structure of the protein template (that is,DNA-based technology). The second is that surface-specific proteins can be used as linkers to bindsynthetic entities, including nanoparticles, functionalpolymers, or other nanostructures onto moleculartemplates (molecular and nanoscale recognition).The third solution harnesses the ability of biologicalmolecules to self- and co-assemble into orderednanostructures. This ensures a robust assemblyprocess for achieving complex nano-, and possiblyhierarchical structures, similar to those found innature (self-assembly).
The current knowledge of protein-foldingpredictions and surface-binding chemistries does notprovide sufficiently detailed information to performrational design of proteins28.To circumvent thisproblem,massive libraries of randomly generatedpeptides can be screened for binding activity toinorganic surfaces using phage and cell-surface displaytechniques29. It may ultimately be possible to construct a‘molecular erector’set, in which different types ofproteins,each designed to bind to a specific inorganicsurface,could assemble into intricate,hybrid structures
composed of inorganics and proteins.This would be asignificant leap towards realizing molecularly designed,genetically engineered technological materials11.
SELECTION OF INORGANIC-BINDING PROTEINS THROUGH DISPLAY TECHNOLOGIES
There are several possible ways of obtainingpolypeptide sequences with specific affinity toinorganics.A number of proteins may fortuitouslybind to inorganics, although they are rarely tested forthis purpose. Inorganic-binding peptides may bedesigned using a theoretical molecular approachsimilar to that used for pharmaceutical drugs30. This iscurrently impractical because it is time consumingand expensive.Another possibility would be to extractbiomineralizing proteins from hard tissues followedby their isolation, purification and cloning31–35.Several such proteins have been used as nucleators,growth modifiers, or enzymes in the synthesis ofcertain inorganics33–40. One of the major limitations ofthis approach is that a given hard tissue usuallycontains many proteins, not just one, all differentlyactive in biomineralization and each distributedspatially and temporally in complex ways33–35.Furthermore, tissue-extracted proteins may only beused for the regeneration of the inorganics that theyare originally associated with, and would be of limitedpractical use. The preferred route, therefore, is to usecombinatorial biology techniques29,41. Here, a largerandom library of peptides with the same number ofamino acids, but of different sequences, is used tomine specific sequences that strongly bind to a choseninorganic surface29,42–45.
Since their inception,well-established in vivocombinatorial biology protocols (for example,phagedisplay (PD)46,47 and cell-surface display (CSD)48) havebeen used to identify biological ligands and to map theepitope (molecular recognition site) of antibodies.Libraries have also been screened for various biologicalactivities, such as catalytic properties or altered affinityand specificity to target molecules in many applicationsincluding the design of new drugs,enzymes,antibodies,DNA-binding proteins and diagnostic agents49–52.The power of display technologies relies on the fact that an a priori knowledge of the desired amino acidsequence is not necessary,as it can simply be selectedand enriched if a large enough population of randomsequences is available. In vitro methods53, such asribosomal and messenger RNA display technologies,have been developed for increased library size (1015)compared to those of in vivo systems (107–10).
Combinatorial biology protocols can be followed inmolecular biomimetics to select polypeptide sequencesthat preferentially bind to the surfaces of inorganiccompounds chosen for their unique physical propertiesin nano- and biotechnology29,43–45.Libraries aregenerated by inserting randomized oligonucleotideswithin certain genes encoded on phage genomes44,45 oron bacterial plasmids29,42,43 (step 1 in Fig. 3).This leads to the incorporation of a random polypeptide sequencewithin a protein residing on the surface of the organism(for example, the coat protein of a phage or an outer membrane or flagellar protein of a cell; step 2).The eventual result is that each phage or cell produces
1 µm 50 µm
3 µm 10 µm
a b
dc
Figure 1 Examples ofbiologically synthesizedcomplex materials. a, Scanningelectron microscope (SEM)image of a growth edge ofabalone (Haliotis rufescens)displaying aragonite platelets(blue) separated by organic film(orange) that eventuallybecomes nacre (mother-of-pearl).This is a layered, tough,and high-strengthbiocomposite (inset:transmission electronmicroscope (TEM) image21.b, Magnetite nanoparticlesformed by magnetotacticbacterium (Aquaspirillummagnetotacticum, inset:TEMimage) are single-crystalline,single-domained andcrystallographically aligned6.c, Mouse enamel (SEM image)is hard, wear-resistant materialwith highly ordered micro/nanoarchitecture consisting ofhydroxyapatite crystallites thatassemble into woven rodstructure (inset: schematiccross-section of a human tooth) 22. d, Sponge spicule(with a cross-shaped apexshown in inset) of Rosella haslayered silica with excellentoptical and mechanicalproperties, a biological opticalfibre (SEM image)23.
and displays a different,but random peptide (step 3).At this stage,a heterogeneous mixture of recombinantcells or phages are contacted with the inorganic substrate(step 4).Several washing cycles of the phages or the cellseliminate non-binders by disrupting weak interactionswith the substrate (step 5).Bound phages or cells are nexteluted from the surfaces (step 6).In PD,the eluted phagesare amplified by reinfecting the host (step 7).Similarly inCSD,cells are allowed to grow (steps 7,8).This stepcompletes a round of biopanning.Generally, three to fivecycles of biopanning are repeated to enrich for tightbinders.Finally, individual clones are sequenced (step 9)to obtain the amino acid sequence of the polypeptidesbinding to the target substrate material.
Outer membrane proteins, lipoproteins, fimbriaand flagellar proteins have all been used forheterologous surface display on bacteria. In PD,most ofthe research has been performed using filamentousphages such as M13 or the closely related fd and f1.Random peptide libraries have been displayed onbacteriophages T7,T4 and λ,but these systems are notyet used on a routine basis.PD and CSD need to beinvestigated and optimized in the selection ofinorganic-surface-binding polypeptides46–52. In general,cell surfaces are more complex than the coat ofbacteriophages,but a single host is required.By contrast,PD requires bacteriophage and its host bacterium,andreinfection is necessary for the amplification of selectedvariants.Eluting bound phages from an inorganicsurface might be problematic leading to a loss of goodbinders.This may be overcome by reamplifyingunreleased phages from the substrate despite the lowyields.Material instability in the screening buffers andnon-specific binding of phages or bacteria to inorganicsurfaces could also be a problem.These issues can beremedied by a careful choice of buffer combinations.It should be noted that even if a material appears to beunaffected in a particular screening buffer, its surfacemight be chemically modified,resulting in the recoveryof peptides that bind to a surface or morphology
different from the one that was originally intended.Growth competition or poor expression of a peptidedue to rare codons,misfolding,degradation orinefficient export,may also bias the screen.Thus,paralleluse of multiple screening techniques may allow greaterflexibility in working with unstable materials andmaximizing the number of useful screens. In the questfor inorganic-binding polypeptides,new methodologiesare likely to be needed.For example, the use of in vitrosystems and a combination of rational and randomapproaches could prove useful for the identification ofvery rare sequences,and to increase the diversity andaffinity of sequences isolated in previous selections41,53.
CHEMICAL SPECIFICITY OF INORGANIC-BINDING POLYPEPTIDES
A genetically engineered polypeptide for inorganics(GEPI) defines a sequence of amino acids thatspecifically and selectively binds to an inorganic surface.The surface could be well defined,such as a single crystalor a nanostructure. It might also be rough,or totallynon-descriptive, such as a powder.Many early studiesused powder samples42–45,54,55, including the seminalwork of Brown29.Our recent research has focused onusing materials that can be synthesized in aqueousenvironments under physiological conditions(biocompatible) and that exhibit fairly stable surfacestructures and compositions.These include noblemetals (Pt and Pd) as well as oxide semiconductors(Cu2O and ZnO) that were biopanned using either PDor flagellar display (both studies unpublished).Some ofthe identified binders as well as sequences selected byother researchers are listed in Table 1.
In our PD panning,a disulphide-constrained M13 peptide library,seven amino acids long,was used.The purpose was to determine whether there were anysimilarities in metal-binding domains between theshort Pt- and Pd-binding sequences and the 14-aa Au-binding sequences29,43 selected by CSD and/or the 12-aa
Figure 2 Molecularbiomimetics.This is the marriageof materials science engineeringand molecular biology fordevelopment of functional hybridsystems,composed of inorganicsand inorganic-binding proteins.The new approach takesadvantage of DNA-based design,recognition,and self-assemblycharacteristics of biomolecules27.Traditional materials scienceengineering produces materials(for example,medium-carbonsteels depicted in the bright- anddark-field TEM images)25, thathave been successfully used overthe last century.Molecularbiology focuses onstructure–function relations inbiomacromolecules, for example,proteins. In molecularbiomimetics, inorganic-bindingproteins could potentially be usedas (i) linkers for nanoparticleimmobilization; (ii) functionalmolecules assembled on specificsubstrates; and (iii)heterobifunctional linkersinvolving two (or more) bindingproteins linking severalnanoinorganic units.(I1: inorganic-1, I2: Inorganic-2,P1 and P2: inorganic specificproteins,LP: linker protein,FP:fusion protein).
Ag-binding sequences54 selected by PD.Others focusedon PD-based sequences with interesting size-selectivebinding capabilities to semiconductors (GaAs and ZnSrefs 44 and 55 respectively),metal-oxide-binding-motifs (SiO2,ZnO,and zeolites, refs 45,56 and 57respectively),and binders to ionic crystals (CaCO3,Cr203,and Fe203/Fe304, refs 58,59 and 60 respectively).
The specificity of a protein for a surface mayoriginate from both chemical61 (for example,hydrogenbonding,polarity and charge effects) and structural62
(size and morphology) recognition mechanisms.Someconclusions may be drawn from the available set ofinorganic-binding sequences.For example,gold-binding sequences isolated by CSD could be movedfrom an extracellular loop of maltoporin to the N-terminus of alkaline phosphotase with retention ofgold-binding activity, suggesting portability andindependence of the surrounding protein framework29.Although many proteins bind to Au at low saltconcentrations, the gold-binding sequences wereselected for binding at high salt concentrations.As aresult, they exhibit substantially improved bindingcompared with native Escherchia coli alkalinephosphotase even in the presence of a detergent.Ourinitial assembly studies63 focused on the 14-amino-acid-long Au-binding peptide,GBP1 (MHGKTQATSGTIQS).To increase binding activity, tandem repeats of thesequence were generated by genetic engineering,and itwas found that at least three repeats were required forhigh-affinity binding29,43.Similar tetrapeptide repeats(SEKL and GASL) were observed in the sequencesidentified that control the morphology of gold crystals43
(Table 1,also see Fig. 5).The Ag-,Pt-,and Pd-binderswere all selected using M13 PD libraries.For Ag
binders54, a 12-aa library was used whereas we used aconstrained heptamer library to identify the smallestsequences capable of binding Pt and Pd. Inspection ofthe sequences of the noble-metal binders (Table 1)suggests that serine and threonine are important forbinding. These amino acids have similar structuresand contain aliphatic hydroxyl groups in their sidechains. Participation in hydrogen bonding by nitrogenatoms was also a common feature of noble-metalbinders. Interestingly, most of the sequences isolatedto date have not contained cysteine, and only a few ofthem contained histidines, two residues known to bindto transition metal ions64.Aromaticity was rarelyobserved, and only when it was coupled with ahydroxyl or amine functional group. Overall, noble-metal-binding sequences appear to predominantlyconsist of hydrophobic and hydroxyl-containing polaramino acids.
A similar analysis can be performed on the non-metal binding sequences listed in Table 1.For bothmetal oxides and zeolites,basic amino acids (arginineand lysine) and hydroxyl-containing residues werecommon,especially in ZnO (ref.56),zeolite59 and, to alesser extent, in SiO2 (ref.45).Of the ionic crystals,Cr2O3 (ref.59) and Fe2O3 (ref.60) binders have similar characteristics, such as being basic and charged.Unlike biological CaCO3-binding proteins whereasparagines and glutamine dominante36–39,62,PD-selected CaCO3-binders contained mostly uncharged orbasic amino acids58,with small differences possiblyoriginating from different mineral forms,aragonite andcalcite.Finally, sequences binding to semiconductorsGaAs (ref.44) and ZnS (ref.55) contain polar aminoacids composed of mostly uncharged ones.Overall,both
DNA fragments withrandom sequencesPhage display Cell-surface display
Binding
Binding
Wash (7–12)
Wash (7–12)
Elution
Substrate material
Substrate material
HWTR DPGI KTHHLIGK DPGI GGT
HCRTYW DPGI HHH
DNA fragment coding for binding peptide
Exact DNA fragment
Growth
Replication
Elution
DNA plasmid
Figure 3 Phage display andcell-surface display.Principles ofthe protocols used for selectingpolypeptide sequences that have binding affinity to giveninorganic substrates.
metal oxide and ionic crystal binders exhibit strongbasic characteristics and high positive charges,whereasnon-oxide semiconductor binders are close to theneutral range,and metal binders are slightly basic (Table 1).
PHYSICAL SPECIFICITY OF PEPTIDE BINDING
Ideally, selection of sequences should be performedusing an inorganic material of specific morphology,size, crystallography or surface stereochemistry29–45.
In practice, however, powders of various sizes and morphologies have been used for selection.The sequence space should be largest for powders,as peptides can attach to surfaces with variousmorphological features. On the other hand, becausepowders are non-descriptive, the selectedpolypeptides may exhibit little or no homology and‘solve’ the binding problem through differentstrategies. Binders selected for a given size,morphology, crystallography or stereochemistry mayshare a higher degree of homology. For example, a
Table I Examples of polypeptide sequences exhibiting affinity for various inorganics.
Materials Sequences Size pIa MWb Chargec DisplayRef
a Isoelectric points and bMolecular masses of peptides are calculated using Compute pI/Mw tool (http://us.expasy.org/tools/pi_tool.html).c Calculated by subtracting the number of basic residues (R and K) from the number acidic residues (D and E).d Unpublished results by the authors.e Most frequently observed sequences.
GEPI binding to a material of a certain size may alsobind to a smaller particle of the same material, but lessstrongly. Similarly, a GEPI binding strongly to aspecific crystallographic surface may bind with analtered affinity to another surface of the samematerial. Finally, a GEPI strongly binding to amaterial of composition A may bind less strongly to a material B with a different composition buthaving similar structure (for example, perovskites).Therefore, if one seeks highly specific binders, thephysical and chemical characteristics of the materialmust be known.An alternative approach is that, oncea relatively large number of binders have beenidentified by panning on powders, a subset specific formorphology, size or surface could be identified onwell-defined materials.
We performed structure-modelling studies topredict the shape of the 3-repeat Au-binding peptideGBP1 in solution65. This work was carried out in thehope that a match between amino acids of GBP1 andthe spacing of the inorganic atomic lattice would shedlight on the mechanism of binding. Figure 4 showsthe polypeptide placed on Au atomic lattices.Simulation results indicate that the repeats form anantiparallel β-sheet, and that their close contactsbetween peptide and Au(111) surfaces mainly involvethe polar side chains of serine and threonine, whichplaces a periodic structure of OH– groups into aregular lattice. In the same study, we also showed thatGBP1 does not bind to Au(112) as tightly, because ofthe migration of water molecule through the atomicgrooves of the crystallographic surface, whichdecouples the polypeptide from the surface65.
INORGANIC-BINDING POLYPEPTIDES AND NANOASSEMBLY
Nanometre-sized particles and nanostructuredinorganics could be fundamental building blocks forfuture technological materials and devices8,14,18.Numerous challenges must be addressed before they are successfully implemented into working systems.
These include synthesizing nanostructures (forexample,particles, rods and tubes) with uniform sizeand shape,controlling their mineralogy, surfacestructures and chemistry,and predicting their spatialdistribution.The molecular biomimetics approachholds great promise in overcoming some of thesedifficulties.Because inorganic surface-bindingpolypeptides are selected to specifically bind to amaterial based on its physical or chemicalcharacteristics, they may find applications incontrolling materials morphology and uniformity,andcould be used to generate heterostructures combiningdifferent inorganics and molecules that wouldnormally phase-separate.
The availability of amino acid sequences binding toinorganics offers a fresh perspective towards futurestudies in self-assembling nanostructured componentswith distinct functionalities.One could select a GEPIfrom the available sequences (Table 1) and insert itwithin the framework of another protein exhibitingproperties (for example,DNA-binding) and use theresulting designer protein or the DNA as a molecularsubstrate.Alternatively,a GEPI could be chemicallylinked to a synthetic polymer with functional properties(for example,conductive or light-sensitive) to createmultifunctional hybrid polymeric units.Whether fusedto biological or synthetic macromolecules, the role ofthe GEPI would be to endow them with anotherfunctionality: specific inorganic-binding.Examplesattained using these three fundamental aspects of GEPI(genetic selection,molecular recognition and self-assembly) in the applications of material synthesis,formation and assembly are discussed below.
CONTROL OF CRYSTAL GROWTH
In biomineralization,a significant aspect of biologicalcontrol over materials formation is throughprotein/inorganic interaction,such as in thebiosynthesis of bone32,dental structures33,molluscshells40,and particles formed by single-celledorganisms34,66–68.With the emergence ofcombinatorially selected inorganic-binding peptides,anatural step was to examine how they would affectinorganic formation.In the first such study43,wecharacterized the effects of GBP1 on the morphology ofgold particles.Using the well-known Faradaytechnique69,monodispersed nanogold particles 12 nmin diameter can be formed by reducing AuCl3 withsodium citrate under ambient conditions.Reducing thegold concentration and temperature allows particleformation at a slower rate,giving the protein time tointeract with surfaces during growth,and providesconditions to examine the effect of gold-binding duringcolloidal gold formation.We conducted a search formutants that modulated the morphology of goldcrystallites by taking advantage of the change of colourin the gold colloid (from pale yellow to red),which isrelated to altered rates of crystallization.Out of fiftymutants, two accelerated crystal growth and changedthe particle morphology from cubo-octahedral (theusual shape of the gold particles under equilibriumgrowth conditions) to flat, triangular or pseudo-hexagonal particles (Fig. 5a)43.The polypeptides, inspite of being slightly basic,may have caused the
Figure 4 A gold-bindingprotein (3-repeat GBP1) onAu(111) and Au(112) surfaces.Viewed from above (a and c)and edge-on (b and d),respectively.The colouringcorresponds to residue type:polar residues are highlightedin green, charged in blue, andhydrophobic in white.
formation of gold crystals similar to those formedunder boiling and acidic conditions (Figs 5b and crespectively) possibly by acting as an acid andmodulating crystal growth rather than serving as atemplate.A similar study54 was also carried out usingmetallic Ag-binding polypeptides that were selectedusing PD.In this case,although the exact mechanism isnot yet known, it was observed that metal ions werereduced to Ag precipitates in mostly flat morphology,anindication that 12-aa-long peptide may have directedthe preferred mineral shape,similar to flat Ag-particlesformed in bacteria67.
PEPTIDE-MEDIATED NANOPARTICLE ASSEMBLY
Organization and immobilization of inorganicnanoparticles in two- or three-dimensionalgeometries are fundamental in the use of nanoscaleeffects14,70. For example, quantum dots can beproduced using vacuum techniques14,71, such asmolecular beam epitaxy, shown in Fig. 5d for theGaInAs/GaAs system. However, this can only beaccomplished under stringent conditions of hightemperature, very low pressures and a toxicenvironment71.A desirable alternative would be notonly to synthesize inorganic nanodots under mildconditions, but also to immobilize/self-assemblethem. Inorganic particles have been functionalizedwith synthetic molecules, including thiols and citrates,and with biological molecules, such as lipids, aminoacids, polypeptides and ligand-functionalized DNA8.Using the recognition properties of the couplingagents, novel materials have been generated8 andcontrolled growth has been achieved72,73. Thesemolecules, however, do not exhibit specificity for agiven material. For example, thiols couple gold as wellas silver nanoparticles in similar ways74,75.Likewise,citrate ions cap noble metals indiscriminately8.
A desirable next step would be to use GEPIs thatspecifically recognize inorganics63,76 for nanoparticleassembly.An advantage of this approach is that GEPIcan be genetically or synthetically fused to otherfunctional biomolecular units or ligands to produceheterobifunctional (or multifunctional) molecularentities.Figure 5e,f shows the assembly of nanogoldparticles on GBP1-coated flat polystyrene surfaces63,which resembles the distribution of quantum dotsobtained by high-vacuum deposition techniques(Fig. 5d).The homogenous decoration of the surfacewith nanogold suggests that proteins may be useful inthe production of tailored nanostructures underambient conditions and aqueous solutions.Furthermore, the recognition activity of the proteincould provide an ability to control the particledistribution,and particle preparation conditions couldallow size control.This approach makes it possible topattern inorganic-binding polypeptides into desirablearrays to produce inorganic particles throughtemplating54 using, for example,dip-pen lithography77.
FUTURE PROSPECTS
Controlled binding and assembly of proteins ontoinorganics is at the core of biological materials scienceand engineering with wide-ranging applications78–81.
Protein adsorption and macromolecular interactions atsolid surfaces play key roles in the performance ofimplants78 and hard-tissue engineering33,40,82.DNA andproteins adsorbed specifically onto probe substrateshave been used to build microarrays suitable for moderngenomics83,pharmogenetics84 and proteomics85.
The preliminary results of self-assembly andmolecular-recognition properties of combinatoriallyselected polypeptides provide insights into potentialfuture applications of GEPI.Thiol and silane linkages,two major molecular linkers for noble metal and oxidesurfaces, respectively,have so far dominated the field ofself-assembled molecules on solid substrates74,75.Self-assembled GEPI monolayers could open up newavenues for designing and engineering novel surfacesfor a wide variety of nano- and biotechnologyapplications (Fig. 6).For example,a GEPI recognizingand assembling on the surface of a therapeutic devicecould be fused to a human protein to enhancebiocompatibility78,or used for drug delivery throughcolloidal inorganic particles86.A GEPI may also beconjugated to a peptide–amphiphilic system leading to a molecular biomineralization substrate87–89.Taking advantage of recognition and self-assemblyproperties,DNA90 or proteins91,92 could be fused toGEPIs to create functional molecular substrates.Coupled with a molecular motor93,94,a GEPI mayprovide a critical step towards creating dynamicnanostructures.Ultimately,using nanopatternedmultimetallic or multisemiconducting particles,andlocalized surface plasmon effects (for example,surface-enhanced Raman95 or surface plasmon resonance96
spectroscopies), several different GEPI molecules couldserve as specific linkers in creating nanoscale platformsfor rapid development of nanoarrays for proteomics97.
Although significant advances have been made indeveloping protocols for the selection of surface-binding polypeptides through display technologies,many questions remain before their robust geneticdesign and practical applications as building blocks arerealized.These include, for example, the physical andchemical basis for GEPI recognition of inorganic
Figure 5 Effect of GEPI onnanocrystal morphology.a–c, One of the two mutants(RP1) from a library of gold-binding GEPIs were tested inthe formation of flat goldparticles, shown in a, similar tothose formed under acidic (b) orboiling (c) conditions. Particlesformed in the presence ofvector-encoded alkalinephosphatase and neutralconditions do not result inmorphological change of gold particles (not shown)43.d,e,The atomic forcemicroscope images showquantum (GaInAs) dotsassembled on GaAs substrate;d, through high-vacuum(molecular beam epitaxy)strain-induced self-assembly(courtesy of T. Pearsall,University of Washington), ande, through 7-repeat GBP1.f, Schematic illustration of e.PS: polystyrene substrate,GA: glutaraldehyde, GBP: 7-repeat GBP1, and gold:12-nm-diameter colloidal gold particles.
surfaces and quantification of their cross-specificity fordiverse materials.Based on the insights achievedthrough these studies in the coming decade,andfollowing the lead of molecular biology,a roadmapcould be developed in which GEPI could be used as aversatile molecular linker and open new avenues in theself-assembly of molecular systems in nano- andnanobiotechnology.
doi:10.1038/nmat964
References1. Thompson, D. W. On the Growth and Form (Cambridge Univ. Press,
Cambridge, UK, 1942).
2. Stevens, P. S. Patterns in Nature (Atlantic Monthly, Boston, 1974).
3. Wainwright, S. A., Biggs, W. D., Currey, J. D. & Gosline, J. M. (eds) Mechanical
Design in Organisms (Princeton Univ. Press, Princeton, 1976).
4. Vogel, S. Cats’ Paws and Catapults (W. W. Norton & Company, New York, 1998).
5. Mann, S. & Calvert, P. Synthesis and biological composites formed by in-situ
precipitation. J. Mater. Sci. 23, 3801–3815 (1988).
6. Sarikaya, M. & Aksay, I. A. (eds.) Biomimetics: Design & Processing of Materials
(American Institute of Physics, New York, 1995).
7. Mann, S. (ed.) Biomimetic Materials Chemistry (VCH, New York, 1996).
8. Niemeyer, C. M. Nanoparticles, proteins, and nucleic acids: Biotechnology
Designer protein unit GEPI-A GEPI-B Inorganic-A Inorganic-B
Figure 6The potential of usingGEPI as ‘molecular erector’ sets.Two different GEPI proteins(GEPI-A and GEPI-B) areassembled on orderedmolecular or nanoscalesubstrates.One could use eithera designer protein, followed bygenetic fusion of the respectiveGEPIs,or directly assembleGEPIs on the patternedsubstrate.The inorganicparticles A and B areimmobilized selectively on GEPI-A and GEPI-B, respectively.Synthetic molecules (that is,conducting17 or photonic18) areassembled using functionalizedside-groups on thenanoparticles.Size, shape,separation,and distribution ofnanostructural units, as well asself-assembly,are parametersunique to this approach.