7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs) http://slidepdf.com/reader/full/qachl1858n-qatar-petqachl1858n-qatar-petroleum-new-specsroleum-new-specs 1/55 Specification sheet Customer: Qatar Petroleum P.O. Box 47 Doha State of Qatar Project: Area: Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2 Area size: Coating Schedule 1Un (Revision 1) : General exposure to atmosphere : Uninsulated newly constructed items : temperature range = 0oC to 120oC sqm 100 Hempel Paints (Qatar) W.L.L Surface preparation: Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure 3000psi) fresh water hosed in order to remove salts and other contaminants. When the surface is dry: Abrasive blasting to minimum Sa 3.0 according to ISO 8501-1:2007. Surface profile corresponding to Rugotest No. 3, BN 10, Keane-Tator Comparator, 3.0 G/S, or ISO Comparator Rough Medium (G), QP requirement 50 to 75µm. Dust off residues. Product name (including quality number) Treated area % Colour Shade no. Film thickness (micron) Wet Dry (sqm/ltr) Brush Roller Spray Nozzle orifice Recommended Nozzle pressure Application methods Theoretical spreading rate HEMPADUR ZINC 15350 100 Metal grey 19840 100 50 .017"-.021" 150 bar 9.4 (X) X f/c HEMPADUR MIO 47950 100 Grey 12130 125 100 .019"-.021" 225 bar 7.6 X X f/c HEMPADUR MIO 47950 100 Grey 13480 125 100 .019"-.021" 225 bar 7.6 X X f/c HEMPATHANE ENAMEL 55100 100 To Be Advised T.B.A 100 50 .017"-.019" 100 bar 10.4 X X f/c t/u: touch up f/c: full coat s/c: stripe coat Total d.f.t. 300 X: Recommended (X): Possible Recoating intervals. Ample ventilation Hrs=Hour(s) Mth=Month(s) N/R=Not Recommended Quality no D.F.T. (micron) Recoated with quality no 40°C 30°C 20°C 10°C 0°C -10°C Min. Max. Min. Max. Min. Max. Min. Max. Min. Max. Min. Max. 100 Min None 3 Hrs None 5 Hrs None 13 Hrs None N/R N/R N/R N/R 47950 15350 50 2 Hrs Ext 3 Hrs Ext 5 Hrs Ext 9 Hrs Ext 21 Hrs Ext N/R N/R 47950 47950 100 3 Hrs Ext 5 Hrs Ext 6 Hrs Ext 13 Hrs Ext 29 Hrs Ext N/R N/R 55100 47950 100 Hempel's PreSale System 2.6.17 (Build 790) Printed at: Environment : 1 Page: 01.10.2013 13:42 User name: Department name: Created/Last modified: 17.09.2013 14:23 Quality Code: Cheryl Leitch Admin Severe QACHL1858N Remarks and Product information see next page. HEMPEL
55
Embed
Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
This document is posted to help you gain knowledge. Please leave a comment to let me know what you think about it! Share it to your friends and learn new things together.
Transcript
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 1Un (Revision 1) : General exposure to atmosphere : Uninsulated newly constructed items : temperature range = 0oC to 120oC
sqm 100
Hempel Paints (Qatar) W.L.L
Surface preparation:
Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure3000psi) fresh water hosed in order to remove salts and other contaminants. When thesurface is dry: Abrasive blasting to minimum Sa 3.0 according to ISO 8501-1:2007.Surface profile corresponding to Rugotest No. 3, BN 10, Keane-Tator Comparator, 3.0G/S, or ISO Comparator Rough Medium (G), QP requirement 50 to 75µm.Dust off residues.
Product name (including quality number)
Treated area% Colour
Shade no.
Film thickness
(micron)
Wet Dry (sqm/ltr) Brush
Roller
Spray
Nozzleorifice
Recommended
Nozzlepressure
Application methodsTheoretical spreadingrate
HEMPADUR ZINC 15350 100 Metal grey 19840 100 50 .017"-.021" 150 bar 9.4 (X) Xf/c
HEMPADUR MIO 47950 100 Grey 12130 125 100 .019"-.021" 225 bar 7.6 X Xf/cHEMPADUR MIO 47950 100 Grey 13480 125 100 .019"-.021" 225 bar 7.6 X Xf/c
HEMPATHANE ENAMEL 55100 100 To Be Advised T.B.A 100 50 .017"-.019" 100 bar 10.4 X Xf/c
t/u: touch up f /c: full coat s/c: stripe coat Total d.f.t. 300 X: Recommended (X): Possible
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 1Un (Revision 1) : General exposure to atmosphere : Uninsulated newly constructed items : temperature range = 0oC to 120oC
sqm 100
Hempel Paints (Qatar) W.L.L
Product information:
Shade no.
Volumesolids %
Curingagent
Mixing ratiovolume
Pot life Dry to touch Application restrictions
Thinner
Flashpoint Min. Temp. Max. RH%
20°C 20°C °C °C
HEMPADUR ZINC 15350 19840 47 95350 4 : 1 8 h 45 min 25 08450 10
HEMPADUR MIO 47950 12130 76 98140 5 : 1 1 h 2 h 24 08450 0
HEMPADUR MIO 47950 13480 76 98140 5 : 1 1 h 2 h 24 08450 0
HEMPATHANE ENAMEL 55100 T.B.A 52 95370 7 : 1 2 h 4 h 35 08080 -10
Remarks:
When the interval is denoted "Extended", the coated structure can possibly be overcoated even after longer periods. This will depend on the actual exposure conditions, such aslimited exposure to sun, and on the condition and cleanliness of the paint surface. The evaluation of the specific situation must be based on local experience, contact HEMPEL for advice.Stripe coat by brush all edges, welds, inaccessible areas etc. prior to application of primer and in between each subsequent coat.
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
2Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Severe
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 1Un (Revision 1) : General exposure to atmosphere : Uninsulated newly constructed items : temperature range = 0oC to 120oC "EXTERNAL OF TANKROOF"
sqm 100
Hempel Paints (Qatar) W.L.L
Surface preparation:
Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure3000psi) fresh water hosed in order to remove salts and other contaminants. When thesurface is dry: Abrasive blasting to minimum Sa 3.0 according to ISO 8501-1:2007.Surface profile corresponding to Rugotest No. 3, BN 10, Keane-Tator Comparator, 3.0G/S, or ISO Comparator Rough Medium (G), QP requirement 50 to 75µm.Dust off residues.
Product name (including quality number)
Treated area% Colour
Shade no.
Film thickness
(micron)
Wet Dry (sqm/ltr) Brush
Roller
Spray
Nozzleorifice
Recommended
Nozzlepressure
Application methodsTheoretical spreadingrate
HEMPADUR ZINC 15350 100 Metal grey 19840 100 50 .017"-.021" 150 bar 9.4 (X) Xf/cHEMPADUR MIO 47950 100 Grey 13480 125 100 .019"-.021" 225 bar 7.6 X Xf/c
HEMPADUR MIO 47950 100 Grey 12130 125 100 .019"-.021" 225 bar 7.6 X Xf/c
HEMPADUR MIO 47950 100 Grey 13480 125 100 .019"-.021" 225 bar 7.6 X Xf/c
HEMPATHANE ENAMEL 55100 100 To Be Advised T.B.A 100 50 .017"-.019" 100 bar 10.4 X Xf/c
t/u: touch up f /c: full coat s/c: stripe coat Total d.f.t. 400 X: Recommended (X): Possible
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
3Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Severe
QACHL1858N
Remarks and Product information see next page.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 1Un (Revision 1) : General exposure to atmosphere : Uninsulated newly constructed items : temperature range = 0oC to 120oC "EXTERNAL OF TANKROOF"
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 1Un (Revision 1) : General exposure to atmosphere : Uninsulated newly constructed items : temperature range = 0oC to 120oC "EXTERNAL OF TANKROOF"
sqm 100
Hempel Paints (Qatar) W.L.L
Product information:
Shade no.
Volumesolids %
Curingagent
Mixing ratiovolume
Pot life Dry to touch Application restrictions
Thinner
Flashpoint Min. Temp. Max. RH%
20°C 20°C °C °C
HEMPADUR ZINC 15350 19840 47 95350 4 : 1 8 h 45 min 25 08450 10
HEMPADUR MIO 47950 13480 76 98140 5 : 1 1 h 2 h 24 08450 0
HEMPADUR MIO 47950 12130 76 98140 5 : 1 1 h 2 h 24 08450 0
HEMPADUR MIO 47950 13480 76 98140 5 : 1 1 h 2 h 24 08450 0
HEMPATHANE ENAMEL 55100 T.B.A 52 95370 7 : 1 2 h 4 h 35 08080 -10
Remarks:
When the interval is denoted "Extended", the coated structure can possibly be overcoated even after longer periods. This will depend on the actual exposure conditions, such aslimited exposure to sun, and on the condition and cleanliness of the paint surface. The evaluation of the specific situation must be based on local experience, contact HEMPEL for advice.Stripe coat by brush all edges, welds, inaccessible areas etc. prior to application of primer and in between each subsequent coat.
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
5Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Severe
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 1In (Revision 1) : General Exposure to atmosphere : Insulated newly constructed items : temperature range = minus 46oC to 120oC
sqm 100
Hempel Paints (Qatar) W.L.L
Surface preparation:
Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure3000psi) fresh water hosed in order to remove salts and other contaminants. When thesurface is dry: Abrasive blasting to minimum Sa 3.0 according to ISO 8501-1:2007.Surface profile corresponding to Rugotest No. 3, BN 10, Keane-Tator Comparator, 3.0G/S, or ISO Comparator Rough Medium (G), QP requirement 50 to 75µm.Dust off residues.
Product name (including quality number)
Treated area% Colour
Shade no.
Film thickness
(micron)
Wet Dry (sqm/ltr) Brush
Roller
Spray
Nozzleorifice
Recommended
Nozzlepressure
Application methodsTheoretical spreadingrate
HEMPADUR ZINC 15350 100 Metal grey 19840 100 50 .017"-.021" 150 bar 9.4 (X) Xf/c
HEMPADUR MIO 47950 100 Grey 12130 125 100 .019"-.021" 225 bar 7.6 X Xf/cHEMPADUR MIO 47950 100 Grey 13480 125 100 .019"-.021" 225 bar 7.6 X Xf/c
t/u: touch up f /c: full coat s/c: stripe coat Total d.f.t. 250 X: Recommended (X): Possible
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 1In (Revision 1) : General Exposure to atmosphere : Insulated newly constructed items : temperature range = minus 46oC to 120oC
sqm 100
Hempel Paints (Qatar) W.L.L
Product information:
Shade no.
Volumesolids %
Curingagent
Mixing ratiovolume
Pot life Dry to touch Application restrictions
Thinner
Flashpoint Min. Temp. Max. RH%
20°C 20°C °C °C
HEMPADUR ZINC 15350 19840 47 95350 4 : 1 8 h 45 min 25 08450 10
HEMPADUR MIO 47950 12130 76 98140 5 : 1 1 h 2 h 24 08450 0
HEMPADUR MIO 47950 13480 76 98140 5 : 1 1 h 2 h 24 08450 0
Remarks:
When the interval is denoted "Extended", the coated structure can possibly be overcoated even after longer periods. This will depend on the actual exposure conditions, such aslimited exposure to sun, and on the condition and cleanliness of the paint surface. The evaluation of the specific situation must be based on local experience, contact HEMPEL for advice.Stripe coat by brush all edges, welds, inaccessible areas etc. prior to application of primer and in between each subsequent coat.
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
7Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Severe
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 1F (Revision 1) : General Exposure to atmosphere : Fireproofed newly constructed items : temperature range minus 46oC to 120oC
sqm 100
Hempel Paints (Qatar) W.L.L
Surface preparation:
Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure3000psi) fresh water cleaned in order to remove salts and other contaminants. When thesurface is dry: Abrasive blasting to minimum Sa 3.0 according to ISO 8501-1:2007, usingsuitably sized abrasive to produce a surface profile equivalent to 35 to 50microns.
Product name (including quality number)
Treated area% Colour
Shade no.
Film thickness
(micron)
Wet Dry (sqm/ltr) Brush
Roller
Spray
Nozzleorifice
Recommended
Nozzlepressure
Application methodsTheoretical spreadingrate
HEMPADUR FAST DRY 17410 100 Red 50630 75 50 .019"-.021" 225 bar 14.8 (X) (X) Xf/c
HEMPADUR MIO 47950 100 Grey 13480 125 100 .019"-.021" 225 bar 7.6 X Xf/c
t/u: touch up f /c: full coat s/c: stripe coat Total d.f.t. 150 X: Recommended (X): Possible
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 1F (Revision 1) : General Exposure to atmosphere : Fireproofed newly constructed items : temperature range minus 46oC to 120oC
sqm 100
Hempel Paints (Qatar) W.L.L
Product information:
Shade no.
Volumesolids %
Curingagent
Mixing ratiovolume
Pot life Dry to touch Application restrictions
Thinner
Flashpoint Min. Temp. Max. RH%
20°C 20°C °C °C
HEMPADUR FAST DRY 17410 50630 74 98410 4 : 1 h 30 m 1 h 30 min 27 08450 -10
HEMPADUR MIO 47950 13480 76 98140 5 : 1 1 h 2 h 24 08450 0
Remarks:
When the interval is denoted "Extended", the coated structure can possibly be overcoated even after longer periods. This will depend on the actual exposure conditions, such aslimited exposure to sun, and on the condition and cleanliness of the paint surface. The evaluation of the specific situation must be based on local experience, contact HEMPEL for advice.Stripe coat by brush all edges, welds, inaccessible areas etc. prior to application of primer and in between each subsequent coat.
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
9Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Severe
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 2Un (Revision 1) : General Exposure to atmosphere : Uninsulated existing items maintenance : temperature range 0oC to 120oC
sqm 100
Hempel Paints (Qatar) W.L.L
Surface preparation:
Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (highpressure3000psi) fresh water cleaned in order to remove salts and other contaminants.When the surface is dry utilise the appropriate surface preparation method as indicated :
1)No visible coating breakdown Ri 0 (ASTM No 10) level (where overcoating for aestheticor other reasons). = Abrade pretreated surfaces with emery paper for good topcoatadhesion.
2)Partial or variable coating breakdown with primer intact or localised under rusting to nomore than Ri 3 (ASTM No 6) level = Locally blast clean degraded areas to Sa 2.5standard as per ISO 8501-1 plus supplement or where blast cleaning is impractical,power tool clean to St 3 standard. At the QP engineer's discretion, fully blast clean the
surfaces to Sa 2.5 standard.
3)More extensive coating breakdown to Ri 4 (ASTM No 4) level or worse = Fully blastclean surfaces to Sa 2.5 standard per ISO 8501-1 plus supplement. Power tool cleaningto St 3 standard is only acceptable for small areas and areas that are impractical for blastcleaning by agreement. use suitable blast cleaning abrasive to give a surface profile of 50- 75microns.
Product name (including quality number)
Treated area% Colour
Shade no.
Film thickness
(micron)
Wet Dry (sqm/ltr) Brush
Roller
Spray
Nozzleorifice
Recommended
Nozzlepressure
Application methodsTheoretical spreadingrate
HEMPADUR MASTIC 45881 100 Red 50630 150 125 .017"-.023" 250 bar 6.4 (X) Xf/c
HEMPADUR MIO 47950 100 Grey 13480 175 125 .019"-.021" 225 bar 6.1 X Xf/c
HEMPATHANE ENAMEL 55100 100 To Be Advised T.B.A 100 50 .017"-.019" 100 bar 10.4 X Xf/c
t/u: touch up f /c: full coat s/c: stripe coat Total d.f.t. 300 X: Recommended (X): Possible
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
10Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Severe
QACHL1858N
Remarks and Product information see next page.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 2Un (Revision 1) : General Exposure to atmosphere : Uninsulated existing items maintenance : temperature range 0oC to 120oC
sqm 100
Hempel Paints (Qatar) W.L.L
Product information:
Shade no.
Volumesolids %
Curingagent
Mixing ratiovolume
Pot life Dry to touch Application restrictions
Thinner
Flashpoint Min. Temp. Max. RH%
20°C 20°C °C °C
HEMPADUR MASTIC 45881 50630 80 95881 3 : 1 3 h 3 h 39 08450 15
HEMPADUR MIO 47950 13480 76 98140 5 : 1 1 h 2 h 24 08450 0
HEMPATHANE ENAMEL 55100 T.B.A 52 95370 7 : 1 2 h 4 h 35 08080 -10
Remarks:
When the interval is denoted "Extended", the coated structure can possibly be overcoated even after longer periods. This will depend on the actual exposure conditions, such aslimited exposure to sun, and on the condition and cleanliness of the paint surface. The evaluation of the specific situation must be based on local experience, contact HEMPEL for advice.Stripe coat by brush all edges, welds, inaccessible areas etc. prior to application of primer and in between each subsequent coat.
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
12Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Severe
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 2Un (Revision 1) : General Exposure to atmosphere : Uninsulated existing items maintenance : temperature range 0oC to 120oC "EXTERNAL OF TANKROOF"
sqm 100
Hempel Paints (Qatar) W.L.L
Surface preparation:
Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (highpressure3000psi) fresh water cleaned in order to remove salts and other contaminants.When the surface is dry utilise the appropriate surface preparation method as indicated :
1)No visible coating breakdown Ri 0 (ASTM No 10) level (where overcoating for aestheticor other reasons). = Abrade pretreated surfaces with emery paper for good topcoatadhesion.
2)Partial or variable coating breakdown with primer intact or localised under rusting to nomore than Ri 3 (ASTM No 6) level = Locally blast clean degraded areas to Sa 2.5standard as per ISO 8501-1 plus supplement or where blast cleaning is impractical,
power tool clean to St 3 standard. At the QP engineer's discretion, fully blast clean thesurfaces to Sa 2.5 standard.
3)More extensive coating breakdown to Ri 4 (ASTM No 4) level or worse = Fully blastclean surfaces to Sa 2.5 standard per ISO 8501-1 plus supplement. Power tool cleaningto St 3 standard is only acceptable for small areas and areas that are impractical for blastcleaning by agreement. use suitable blast cleaning abrasive to give a surface profile of 50- 75microns.
Product name (including quality number)
Treated area% Colour
Shade no.
Film thickness
(micron)
Wet Dry (sqm/ltr) Brush
Roller
Spray
Nozzleorifice
Recommended
Nozzlepressure
Application methodsTheoretical spreadingrate
HEMPADUR MASTIC 45881 100 Red 50630 150 125 .017"-.023" 250 bar 6.4 (X) Xf/c
HEMPADUR MIO 47950 100 Grey 12130 175 125 .019"-.021" 225 bar 6.1 X Xf/c
HEMPADUR MIO 47950 100 Grey 13480 125 100 .019"-.021" 225 bar 7.6 X Xf/cHEMPATHANE ENAMEL 55100 100 To Be Advised T.B.A 100 50 .017"-.019" 100 bar 10.4 X Xf/c
t/u: touch up f /c: full coat s/c: stripe coat Total d.f.t. 400 X: Recommended (X): Possible
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
13Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Severe
QACHL1858N
Remarks and Product information see next page.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 2Un (Revision 1) : General Exposure to atmosphere : Uninsulated existing items maintenance : temperature range 0oC to 120oC "EXTERNAL OF TANKROOF"
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 2Un (Revision 1) : General Exposure to atmosphere : Uninsulated existing items maintenance : temperature range 0oC to 120oC "EXTERNAL OF TANKROOF"
sqm 100
Hempel Paints (Qatar) W.L.L
Product information:
Shade no.
Volumesolids %
Curingagent
Mixing ratiovolume
Pot life Dry to touch Application restrictions
Thinner
Flashpoint Min. Temp. Max. RH%
20°C 20°C °C °C
HEMPADUR MASTIC 45881 50630 80 95881 3 : 1 3 h 3 h 39 08450 15
HEMPADUR MIO 47950 12130 76 98140 5 : 1 1 h 2 h 24 08450 0HEMPADUR MIO 47950 13480 76 98140 5 : 1 1 h 2 h 24 08450 0
HEMPATHANE ENAMEL 55100 T.B.A 52 95370 7 : 1 2 h 4 h 35 08080 -10
Remarks:
When the interval is denoted "Extended", the coated structure can possibly be overcoated even after longer periods. This will depend on the actual exposure conditions, such aslimited exposure to sun, and on the condition and cleanliness of the paint surface. The evaluation of the specific situation must be based on local experience, contact HEMPEL for advice.Stripe coat by brush all edges, welds, inaccessible areas etc. prior to application of primer and in between each subsequent coat.
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
15Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Severe
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 2In (Revision 1) : General Exposure to atmosphere : Insulated existing items maintenance : temperature range minus 46oC to 120oC
sqm 100
Hempel Paints (Qatar) W.L.L
Surface preparation:
Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (highpressure3000psi) fresh water cleaned in order to remove salts and other contaminants.When the surface is dry utilise the appropriate surface preparation method as indicated :
1)No visible coating breakdown Ri 0 (ASTM No 10) level = No overcoating required.
2)Partial or variable coating breakdown with primer intact or localised under rusting to nomore than Ri 3 (ASTM No 6) level = Locally blast clean degraded areas to Sa 2.5standard as per ISO 8501-1 plus supplement or where blast cleaning is impractical,power tool clean to St 3 standard. At the QP engineer's discretion, fully blast clean thesurfaces to Sa 2.5 standard.
3)More extensive coating breakdown to Ri 4 (ASTM No 4) level or worse = Fully blastclean surfaces to Sa 2.5 standard per ISO 8501-1 plus supplement. Power tool cleaningto St 3 standard is only acceptable for small areas and areas that are impractical for blastcleaning by agreement. use suitable blast cleaning abrasive to give a surface profile of 50- 75microns.
Product name (including quality number)
Treated area% Colour
Shade no.
Film thickness
(micron)
Wet Dry (sqm/ltr) Brush
Roller
Spray
Nozzleorifice
Recommended
Nozzlepressure
Application methodsTheoretical spreadingrate
HEMPADUR MASTIC 45881 100 Red 50630 150 125 .017"-.023" 250 bar 6.4 (X) Xf/c
HEMPADUR MIO 47950 100 Grey 13480 175 125 .019"-.021" 225 bar 6.1 X Xf/c
t/u: touch up f /c: full coat s/c: stripe coat Total d.f.t. 250 X: Recommended (X): Possible
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
16Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Severe
QACHL1858N
Remarks and Product information see next page.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 2In (Revision 1) : General Exposure to atmosphere : Insulated existing items maintenance : temperature range minus 46oC to 120oC
sqm 100
Hempel Paints (Qatar) W.L.L
Product information:
Shade no.
Volumesolids %
Curingagent
Mixing ratiovolume
Pot life Dry to touch Application restrictions
Thinner
Flashpoint Min. Temp. Max. RH%
20°C 20°C °C °C
HEMPADUR MASTIC 45881 50630 80 95881 3 : 1 3 h 3 h 39 08450 15
HEMPADUR MIO 47950 13480 76 98140 5 : 1 1 h 2 h 24 08450 0
Remarks:
When the interval is denoted "Extended", the coated structure can possibly be overcoated even after longer periods. This will depend on the actual exposure conditions, such aslimited exposure to sun, and on the condition and cleanliness of the paint surface. The evaluation of the specific situation must be based on local experience, contact HEMPEL for advice.Stripe coat by brush all edges, welds, inaccessible areas etc. prior to application of primer and in between each subsequent coat.
AREAS THAT PROTRUDE THROUGH THE INSULATION ALSO REQUIRE 50micron THICK COAT OF ALIPHATIC POLYURETHANE HIGH GLOSS TOPCOAT "HEMPATHANEENAMEL 55100"
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
18Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Severe
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 2F (Revision 1) : General Exposure to atmosphere : Fireproofed existing items maintenance : temperature range 0oC to 120oC
sqm 100
Hempel Paints (Qatar) W.L.L
Surface preparation:
Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (highpressure3000psi) fresh water cleaned in order to remove salts and other contaminants.When the surface is dry utilise the appropriate surface preparation method as indicated :
1)No visible coating breakdown Ri 0 (ASTM No 10) level = No overcoating required.
2)Partial or variable coating breakdown with primer intact or localised under rusting to nomore than Ri 3 (ASTM No 6) level = Locally blast clean degraded areas to Sa 2.5standard as per ISO 8501-1 plus supplement or where blast cleaning is impractical,power tool clean to St 3 standard. At the QP engineer's discretion, fully blast clean thesurfaces to Sa 2.5 standard.
3)More extensive coating breakdown to Ri 4 (ASTM No 4) level or worse = Fully blastclean surfaces to Sa 2.5 standard per ISO 8501-1 plus supplement. Power tool cleaningto St 3 standard is only acceptable for small areas and areas that are impractical for blastcleaning by agreement. use suitable blast cleaning abrasive to give a surface profile of 35- 50microns.
Product name (including quality number)
Treated area% Colour
Shade no.
Film thickness
(micron)
Wet Dry (sqm/ltr) Brush
Roller
Spray
Nozzleorifice
Recommended
Nozzlepressure
Application methodsTheoretical spreadingrate
HEMPADUR MASTIC 45881 100 Red 50630 150 125 .017"-.023" 250 bar 6.4 (X) Xf/c
t/u: touch up f /c: full coat s/c: stripe coat Total d.f.t. 125 X: Recommended (X): Possible
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
19Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Severe
QACHL1858N
Remarks and Product information see next page.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 2F (Revision 1) : General Exposure to atmosphere : Fireproofed existing items maintenance : temperature range 0oC to 120oC
sqm 100
Hempel Paints (Qatar) W.L.L
Product information:
Shade no.
Volumesolids %
Curingagent
Mixing ratiovolume
Pot life Dry to touch Application restrictions
Thinner
Flashpoint Min. Temp. Max. RH%
20°C 20°C °C °C
HEMPADUR MASTIC 45881 50630 80 95881 3 : 1 3 h 3 h 39 08450 15
Remarks:
When the interval is denoted "Extended", the coated structure can possibly be overcoated even after longer periods. This will depend on the actual exposure conditions, such aslimited exposure to sun, and on the condition and cleanliness of the paint surface. The evaluation of the specific situation must be based on local experience, contact HEMPEL for advice.Stripe coat by brush all edges, welds, inaccessible areas etc. prior to application of primer and in between each subsequent coat.
AREAS THAT PROTRUDE THROUGH THE INSULATION ALSO REQUIRE TO BE COATED WITH AN ADDITIONAL 125µm OF MIO PIGMENTED EPOXY MIDCOAT PAINT PLUS A 50µm THICK COAT OF ALIPHATIC POLYURETHANE HIGH GLOSS TOPCOAT PAINT = HEMPADUR 47950-13480 AT 125µm + HEMPATHANE ENAMEL 55100-T.B.A. AT50µm.
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
20Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Severe
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 3 (Revision 1) : Uninsulated steel items with a design temperature of 120oC to 400oC
sqm 100
Hempel Paints (Qatar) W.L.L
Surface preparation:
Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (highpressure3000psi) fresh water cleaned in order to remove salts and other contaminants.When the surface is dry: Abrasive blasting to minimum Sa 3.0 according to ISO8501-1:2007, using a suitably sized abrasive blast media to produce a surface profile of between 35 and 50microns.
Maintenance :
1)If the primer is intact, lightly blast clean or mechanically abrade to remove damagedtopcoat paint and thoroughly fresh water wash using a stiff bristle brush to remove solublezinc salts.
2)If the primer has suffered breakdown or a marked reduction in film thickness, blastclean affected areas to Sa 3.0 standard as per ISO 8501-1 plus supplement using asuitable sized abrasive to give a surface profile of 35 to 50µm.
Product name (including quality number)
Treated area% Colour
Shade no.
Film thickness
(micron)
Wet Dry (sqm/ltr) Brush
Roller
Spray
Nozzleorifice
Recommended
Nozzlepressure
Application methodsTheoretical spreadingrate
HEMPEL'S GALVOSIL 15700 100 Metal grey 19840 75 50 .019"-.023" 100 bar 12.8 (X) Xf/c
HEMPEL'S SILICONE ACRYLIC 56940 100 Light alu 19000 75 25 .017" 125 bar 12.0 (X) Xf/c
HEMPEL'S SILICONE ACRYLIC 56940 100 Light alu 19000 75 25 .017" 125 bar 12.0 (X) Xf/c
t/u: touch up f /c: full coat s/c: stripe coat Total d.f.t. 100 X: Recommended (X): Possible
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
21Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Severe
QACHL1858N
Remarks and Product information see next page.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 3 (Revision 1) : Uninsulated steel items with a design temperature of 120oC to 400oC
sqm 100
Hempel Paints (Qatar) W.L.L
Product information:
Shade no.
Volumesolids %
Curingagent
Mixing ratiovolume
Pot life Dry to touch Application restrictions
Thinner
Flashpoint Min. Temp. Max. RH%
20°C 20°C °C °C
HEMPEL'S GALVOSIL 15700 19840 64 97170 7.4 : 2.6 4 h 30 min 14 08700 0
HEMPEL'S SILICONE ACRYLIC 56940 19000 30 1 h 25 08080
HEMPEL'S SILICONE ACRYLIC 56940 19000 30 1 h 25 08080
Remarks:
1) See product data sheet and / or APPLICATION INSTRUCTIONS regarding drying time and recoating intervals.RESPECTFULLY SUGGEST MODIFIED SILICONE ALUMINIUM PRODUCTS CAN NOW BE REPLACED BY PURE SILICONE MOISTURE CURING RESIN BASED PRODUCTSSUCH AS :HEMPEL SILICONE ALUMINIUM 56914-19000
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
23Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Severe
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 3HT (Addition) :Uninsulated steel items operating at temperatures above 400oC " metal sprayed items"
sqm 100
Hempel Paints (Qatar) W.L.L
Surface preparation:
Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure)fresh water cleaned in order to remove salts and other contaminants.When the surface is dry: Abrasive blasting to minimum Sa 3.0 according to ISO 8501-1,with a suitable sized abrasive to give a surface profile of 75 to 100 microns.Followed by metal (aluminium) spraying to dry film thickness of at least 200microns.
Maintenance :
1)If metal coating is intact : sweep blast clean and fresh water wash to remove aluminiumsalts.
2)If metal coating has suffered breakdown, blast clean affected areas to Sa 3.0 standard
to ISO 8501-1 plus supplement using a suitable abrasive to give a surface profile of 50 to75microns.
Product name (including quality number)
Treated area% Colour
Shade no.
Film thickness
(micron)
Wet Dry (sqm/ltr) Brush
Roller
Spray
Nozzleorifice
Recommended
Nozzlepressure
Application methodsTheoretical spreadingrate
HEMPEL'S SILICONE ALUMINIUM 56914 100 Light alu 19000 50 25 0.017" 125 bar 17.2 (X) Xf/c
HEMPEL'S SILICONE ALUMINIUM 56914 100 Light alu 19000 50 25 0.017" 125 bar 17.2 (X) Xf/c
t/u: touch up f/c: full coat s/c: stripe coat Total d.f.t. 50 X: Recommended (X): Possible
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
24Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Severe
QACHL1858N
Remarks and Product information see next page.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 3HT (Addition) :Uninsulated steel items operating at temperatures above 400oC " metal sprayed items"
sqm 100
Hempel Paints (Qatar) W.L.L
Product information:
Shade no.
Volumesolids %
Curingagent
Mixing ratiovolume
Pot life Dry to touch Application restrictions
Thinner
Flashpoint Min. Temp. Max. RH%
20°C 20°C °C °C
HEMPEL'S SILICONE ALUMINIUM 56914 19000 43 1 h 30 08080
HEMPEL'S SILICONE ALUMINIUM 56914 19000 43 1 h 30 08080
Remarks:
A flash-coat before applying the full coat is strongly recommended when recoating Metal Sprayed Coatings.
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
26Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Severe
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 4 (Revision 1) : Insulated ferrous items with a design temperature of 120oC to 250oC
sqm 100
Hempel Paints (Qatar) W.L.L
Surface preparation:
Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure)fresh water cleaned in order to remove salts and other contaminants. When the surface isdry:1)No visible coating breakdown Ri 0 (ASTM No 10) level = No overcoating required.
2)Partial or variable coating breakdown with primer intact or localised under rusting to nomore than Ri 3 (ASTM No 6) level = Locally blast clean degraded areas to Sa 2.5standard as per ISO 8501-1 plus supplement or where blast cleaning is impractical,power tool clean to St 3 standard. At the QP engineer's discretion, fully blast clean thesurfaces to Sa 2.5 standard.
3)More extensive coating breakdown to Ri 4 (ASTM No 4) level or worse = Fully blast
clean surfaces to Sa 2.5 standard per ISO 8501-1 plus supplement. Power tool cleaningto St 3 standard is only acceptable for small areas and areas that are impractical for blastcleaning by agreement. use suitable blast cleaning abrasive to give a surface profile of 35to 50microns.
Product name (including quality number)
Treated area% Colour
Shade no.
Film thickness
(micron)
Wet Dry (sqm/ltr) Brush
Roller
Spray
Nozzleorifice
Recommended
Nozzlepressure
Application methodsTheoretical spreadingrate
HEMPEL'S SILVIUM 51570 100 Light alu 19000 125 50 .017'' 100 bar 7.6 (X) Xf/c
HEMPEL'S SILVIUM 51570 100 Light alu 19000 125 50 .017'' 100 bar 7.6 (X) Xf/c
t/u: touch up f /c: full coat s/c: stripe coat Total d.f.t. 100 X: Recommended (X): Possible
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
27Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Medium
QACHL1858N
Remarks and Product information see next page.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 4 (Revision 1) : Insulated ferrous items with a design temperature of 120oC to 250oC
sqm 100
Hempel Paints (Qatar) W.L.L
Product information:
Shade no.
Volumesolids %
Curingagent
Mixing ratiovolume
Pot life Dry to touch Application restrictions
Thinner
Flashpoint Min. Temp. Max. RH%
20°C 20°C °C °C
HEMPEL'S SILVIUM 51570 19000 38 5 h 38
HEMPEL'S SILVIUM 51570 19000 38 5 h 38
Remarks:
STRONGLY RECOMMEND DUE TO VERY SLOW CURING OF OLEORESINOUS HIGH TEMPERATURE PRODUCTS THEIR APPLICATION IS BEST SUITED TO MAINTENANCEPROJECTS ONLY.
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
29Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Medium
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Shedule 5 (Revision 1) : Items exposed to seawater and seaspray in the splash zone (excluding riser lines which is covered by QP:SPC:L:003)
sqm 100
Hempel Paints (Qatar) W.L.L
Surface preparation:
Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure)fresh water hosed in order to remove salts and other contaminants. When the surface isdry: Abrasive blasting to minimum Sa 3.0 according to ISO 8501-1:2007. Surface profilecorresponding to Rugotest No. 3, BN 10, Keane-Tator Comparator, 3.0 G/S, or ISOComparator Rough Medium (G), profile amplitude of 75 to 100microns.Dust off residues.
Repair of damaged coatings : vacuum or spot blast to ISO 8501-1 plus supplement usinga suitably sized abrasive to give a surface profile of 75 to 100µm. Power tool cleaning isnot acceptable for even local repair of this coating system when fully cured. Sweep blastcleaning may be used by agreement.
Maintenance : Unless no visible coating breakdown is evident. Blast clean the surfaces toSa 2.5 standard as per ISO 84501-1 plus supplement using a suitably sized abrasive togive a surface profile amplitude of 75 to 100µm. Power tool cleaning is not acceptable for this schedule.
Product name (including quality number)
Treated area% Colour
Shade no.
Film thickness
(micron)
Wet Dry (sqm/ltr) Brush
Roller
Spray
Nozzleorifice
Recommended
Nozzlepressure
Application methodsTheoretical spreadingrate
HEMPADUR MULTI-STRENGTH GF 35870 100 Red 50630 575 500 .023"-.027" 250 bar 1.7 Xf/c
HEMPADUR MULTI-STRENGTH GF 35870 100 Black 19990 575 500 .023"-.027" 250 bar 1.7 Xf/c
t/u: touch up f/c: full coat s/c: stripe coat Total d.f.t. 1000 X: Recommended (X): Possible
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
30Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Severe
QACHL1858N
Remarks and Product information see next page.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Min. Max. Min. Max. Min. Max. Min. Max. Min. Max. Min. Max.
2 Hrs 9 Day 4 Hrs 15 Day 8 Hrs 30 Day 20 Hrs 75 Day N/R N/R N/R N/R3587035870 500
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
31Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Severe
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Shedule 5 (Revision 1) : Items exposed to seawater and seaspray in the splash zone (excluding riser lines which is covered by QP:SPC:L:003)
sqm 100
Hempel Paints (Qatar) W.L.L
Product information:
Shade no.
Volumesolids %
Curingagent
Mixing ratiovolume
Pot life Dry to touch Application restrictions
Thinner
Flashpoint Min. Temp. Max. RH%
20°C 20°C °C °C
HEMPADUR MULTI-STRENGTH GF35870
50630 87 98870 3 : 1 1 h 2 h 30 min 35 08450 5
HEMPADUR MULTI-STRENGTH GF35870
19990 87 98870 3 : 1 1 h 2 h 30 min 35 08450 5
Remarks:
Stripe coating with brush before or after spray application of each coat is to be carried out on areas difficult to cover properly by spray as eg edges, corners, flanges, cutouts,handwelds and other rough surfaces.
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
32Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Severe
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 6 (Revision 1) : Internal surfaces of steel, hydrocarbon, and water storage tanks.
sqm 100
Hempel Paints (Qatar) W.L.L
Surface preparation:
Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure)fresh water hosed in order to remove salts and other contaminants. When the surface isdry:1)NEW CONSTRUCTION : Abrasive blasting to minimum Sa 3.0 according to ISO8501-1:2007. Surface profile corresponding to Rugotest No. 3, BN 10, Keane-Tator Comparator, 3.0 G/S, or ISO Comparator Rough Medium (G) using suitably sizedabrasive to give a surface profile of 75 to 100 microns.Dust off residues.2)Repair of Damaged Coating : Vacuum or spot blast clean to ISO 8501-1 plussupplement using a suitable sized abrasive to give a surface profile amplitude of 75 to100 microns. Power tool cleaning to St 3 standard is only acceptable by agreement for areas that are inaccessible or impractical for blast cleaning .
3)Maintenance : Unless no visible coating breakdown is evident, blast clean the surfacesto Sa 2.5 standard as per ISO 8501-1 plus supplement using a suitable sized abrasive togive a surface profile amplitude of 75 to 100µm. Power tool cleaning to St 3 is onlyacceptable for small and inaccessible areas.
Product name (including quality number)
Treated area% Colour
Shade no.
Film thickness
(micron)
Wet Dry (sqm/ltr) Brush
Roller
Spray
Nozzleorifice
Recommended
Nozzlepressure
Application methodsTheoretical spreadingrate
HEMPADUR 35600 100 Light red 50900 300 300 .017"-.021" 250 bar 3.3 (X) Xf/c
Min. Max. Min. Max. Min. Max. Min. Max. Min. Max. Min. Max.
22 Hrs 36 Hrs 36 Hrs 60 Hrs 72 Hrs 5 Day 7½ Day 12½ Day N/R N/R N/R N/R3560035600 300
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
34Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Immersion
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 6 (Revision 1) : Internal surfaces of steel, hydrocarbon, and water storage tanks.
sqm 100
Hempel Paints (Qatar) W.L.L
Product information:
Shade no.
Volumesolids %
Curingagent
Mixing ratiovolume
Pot life Dry to touch Application restrictions
Thinner
Flashpoint Min. Temp. Max. RH%
20°C 20°C °C °C
HEMPADUR 35600 50900 100 98600 14.8 : 5.2 h 30 m 24 h 93 08450 15
HEMPADUR 35600 20320 100 98600 14.8 : 5.2 h 30 m 24 h 93 08450 15
Remarks:
Stripe coating with brush before or after spray application of each coat is to be carried out on areas difficult to cover properly by spray as eg edges, corners, flanges, cutouts,handwelds and other rough surfaces.DEPENDANT UPON THE TANK STORAGE SERVICE VARIOUS OTHER EPOXY PRODUCTS MAY PROVE ACCEPTABLE PLEASE CONSULT HEMPEL OFFICE FOR DETAILEDRECOMMENDATION.
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
35Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Immersion
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
S ifi ti h t
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 6 (Revision 1) : Internal surfaces of steel hydrocarbon and water storage tanks "OPTION FOR HYDROCARBON STORAGE ONLY"
sqm 100
Hempel Paints (Qatar) W.L.L
Surface preparation:
Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure)fresh water hosed in order to remove salts and other contaminants. When the surface isdry:1)NEW CONSTRUCTION : Abrasive blasting to minimum Sa 3.0 according to ISO8501-1:2007. Surface profile corresponding to Rugotest No. 3, BN 10, Keane-Tator Comparator, 3.0 G/S, or ISO Comparator Rough Medium (G) using suitably sizedabrasive to give a surface profile of 75 to 100 microns.Dust off residues.2)Repair of Damaged Coating : Vacuum or spot blast clean to ISO 8501-1 plussupplement using a suitable sized abrasive to give a surface profile amplitude of 75 to100 microns. Power tool cleaning to St 3 standard is only acceptable by agreement for areas that are inaccessible or impractical for blast cleaning .
3)Maintenance : Unless no visible coating breakdown is evident, blast clean the surfacesto Sa 2.5 standard as per ISO 8501-1 plus supplement using a suitable sized abrasive togive a surface profile amplitude of 75 to 100µm. Power tool cleaning to St 3 is onlyacceptable for small and inaccessible areas.
Product name (including quality number)
Treated area% Colour
Shade no.
Film thickness
(micron)
Wet Dry (sqm/ltr) Brush
Roller
Spray
Nozzleorifice
Recommended
Nozzlepressure
Application methodsTheoretical spreadingrate
HEMPADUR 35760 100 Light red 50900 300 300 .021" 250 bar 3.3 (X) (X) Xf/c
Min. Max. Min. Max. Min. Max. Min. Max. Min. Max. Min. Max.
5 Hrs 9 Day 8 Hrs 15 Day 16 Hrs 30 Day 40 Hrs 75 Day N/R N/R N/R N/R3576035760 300
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
37Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Immersion
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
S ifi ti h t
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Stripe coating with brush before or after spray application of each coat is to be carried out on areas difficult to cover properly by spray as eg edges, corners, flanges, cutouts,handwelds and other rough surfaces.
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
38Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Immersion
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
S ifi ti h t
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 7 (Revision 1) : Underside surface of Steel Storage Tank Floor Plates
sqm 100
Hempel Paints (Qatar) W.L.L
Surface preparation:
Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure)fresh water hosed in order to remove salts and other contaminants. When the surface isdry: Abrasive blasting to minimum Sa 3.0 according to ISO 8501-1:2007. Surface profilecorresponding to Rugotest No. 3, BN 10, Keane-Tator Comparator, 3.0 G/S, or ISOComparator Rough Medium (G), using suitably sized abrasive to give a surface profileamplitude of 75 to 100microns.Dust off residues.
Product name (including quality number)
Treated area% Colour
Shade no.
Film thickness
(micron)
Wet Dry (sqm/ltr) Brush
Roller
Spray
Nozzleorifice
Recommended
Nozzlepressure
Application methodsTheoretical spreadingrate
HEMPADUR QUATTRO 17634 100 Red 50630 275 200 .021"-.025" 250 bar 3.6 Xf/c
HEMPADUR QUATTRO 17634 100 Black 19990 275 200 .021"-.025" 250 bar 3.6 Xf/ct/u: touch up f /c: full coat s/c: stripe coat Total d.f.t. 400 X: Recommended (X): Possible
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 7 (Revision 1) : Underside surface of Steel Storage Tank Floor Plates
sqm 100
Hempel Paints (Qatar) W.L.L
Product information:
Shade no.
Volumesolids %
Curingagent
Mixing ratiovolume
Pot life Dry to touch Application restrictions
Thinner
Flashpoint Min. Temp. Max. RH%
20°C 20°C °C °C
HEMPADUR QUATTRO 17634 50630 72 97334 4 : 1 2 h 4 h 27 08450
HEMPADUR QUATTRO 17634 19990 71 97334 4 : 1 2 h 4 h 27 08450
Remarks:
Stripe coating with brush before or after spray application of each coat is to be carried out on areas difficult to cover properly by spray as eg edges, corners, flanges, cutouts,handwelds and other rough surfaces.
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
40Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin buried
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
S ifi ti h t
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 8A (Addition) : Internal surfaces of Vessels in Corrosive service at low pressure/temperature up to 70oC
sqm 100
Hempel Paints (Qatar) W.L.L
Surface preparation:
Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure)fresh water hosed in order to remove salts and other contaminants. When the surface isdry:1)NEW CONSTRUCTION :Abrasive blasting to minimum Sa 3.0 according to ISO8501-1:2007. Surface profile corresponding to Rugotest No. 3, BN 10, Keane-Tator Comparator, 3.0 G/S, or ISO Comparator Rough Medium (G), using a suitably sizedabrasive to produce a surface profile of 75 to 100µm.Dust off residues.2)Repair of damaged coating : Vacuum or spot blast to ISO 8501-1 plus supplement withsuitably sized abrasive to give a surface amplitude of 75 to 100µm. Power tool cleaning isnot acceptable for even local repair of this coating. Abrade partially damaged coatingswith emery paper and solvent wipe them.
3)Maintenance : Unless no visible coating breakdown is evident, blast clean the surfacesto Sa 3 standard as per ISO 8501-1 plus supplement using a suitably sized abrasive togive a surface amplitude of 75 to 100 microns. Power tool cleaning is not acceptable for this schedule.
Product name (including quality number)
Treated area% Colour
Shade no.
Film thickness
(micron)
Wet Dry (sqm/ltr) Brush
Roller
Spray
Nozzleorifice
Recommended
Nozzlepressure
Application methodsTheoretical spreadingrate
HEMPADUR 35900 100 Light red 50900 300 300 .018'' - .021'' 250 bar 3.3 Xf/c
Min. Max. Min. Max. Min. Max. Min. Max. Min. Max. Min. Max.
N/R N/R ½ Day 30 Day 1 Day 60 Day 2½ Day 90 Day N/R N/R N/R N/R3590035900 300
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
42Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Immersion
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
Specification sheet
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Stripe coating with brush before or after spray application of each coat is to be carried out on areas difficult to cover properly by spray as eg edges, corners, flanges, cutouts,handwelds and other rough surfaces.
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
43Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Immersion
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
Specification sheet
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 8B (Addition) : Internal surfaces of Vessels in Corrosive service at high pressure/temperature in excess of 70oC
sqm 100
Hempel Paints (Qatar) W.L.L
Surface preparation:
Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure)fresh water hosed in order to remove salts and other contaminants. When the surface isdry:1)NEW CONSTRUCTION :Abrasive blasting to minimum Sa 3.0 according to ISO8501-1:2007. Surface profile corresponding to Rugotest No. 3, BN 10, Keane-Tator Comparator, 3.0 G/S, or ISO Comparator Rough Medium (G), using a suitably sizedabrasive to produce a surface profile of 75 to 100µm.Dust off residues.2)Repair of damaged coating : Vacuum or spot blast to ISO 8501-1 plus supplement withsuitably sized abrasive to give a surface amplitude of 75 to 100µm. Power tool cleaning isnot acceptable for even local repair of this coating. Abrade partially damaged coatingswith emery paper and solvent wipe them.
3)Maintenance : Unless no visible coating breakdown is evident, blast clean the surfacesto Sa 3 standard as per ISO 8501-1 plus supplement using a suitably sized abrasive togive a surface amplitude of 75 to 100 microns. Power tool cleaning is not acceptable for this schedule.
Product name (including quality number)
Treated area% Colour
Shade no.
Film thickness
(micron)
Wet Dry (sqm/ltr) Brush
Roller
Spray
Nozzleorifice
Recommended
Nozzlepressure
Application methodsTheoretical spreadingrate
HEMPADUR 35900 100 Light red 50900 300 300 .018'' - .021'' 250 bar 3.3 Xf/c
Min. Max. Min. Max. Min. Max. Min. Max. Min. Max. Min. Max.
N/R N/R ½ Day 30 Day 1 Day 60 Day 2½ Day 90 Day N/R N/R N/R N/R3590035900 300
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
45Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Immersion
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
Specification sheet
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Stripe coating with brush before or after spray application of each coat is to be carried out on areas difficult to cover properly by spray as eg edges, corners, flanges, cutouts,handwelds and other rough surfaces.
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
46Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Immersion
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
Specification sheet
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Remove oil and grease and any other contamination using a water soluble degreasingagent, followed by thorough fres water washing.
NEW CONSTRUCTION : Remove soluble zinc corrosion products by scrubbing with astiff bristle brush during fresh water washing. At QP engineer's discretion, lightly roughenthe surface by sweep blast cleaning using a fine abrasive or, if pretreatment primer is tobe applied, abrade with emery paper.
REPAIR OF DAMAGED COATING : If zinc is intact, remove soluble zinc corrosionproducts by scrubbing with stiff bristle brush during fresh water washing. If rusting of thesteel is evident, remove the rust by lightly abrading affected areas with emery cloth beforescrubbing with a stiff bristle brush during fresh water washing.
MAINTENANCE : As for repair of damaged coating but lightly sweep blast clean rustedareas to Sa 2.5 standard
Product name (including quality number)
Treated area% Colour
Shade no.
Film thickness
(micron)
Wet Dry (sqm/ltr) Brush
Roller
Spray
Nozzleorifice
Recommended
Nozzlepressure
Application methodsTheoretical spreadingrate
HEMPADUR MASTIC 45881 100 Red 50630 150 125 .017"-.023" 250 bar 6.4 (X) Xf/c
HEMPATHANE ENAMEL 55100 100 To Be Advised T.B.A 100 50 .017"-.019" 100 bar 10.4 X Xf/c
t/u: touch up f /c: full coat s/c: stripe coat Total d.f.t. 175 X: Recommended (X): Possible
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
47Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Severe
QACHL1858N
Remarks and Product information see next page.
HEMPEL
Specification sheet
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
Specification sheet
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
HEMPADUR MASTIC 45881 50630 80 95881 3 : 1 3 h 3 h 39 08450 15
HEMPATHANE ENAMEL 55100 T.B.A 52 95370 7 : 1 2 h 4 h 35 08080 -10
Remarks:
When the interval is denoted "Extended", the coated structure can possibly be overcoated even after longer periods. This will depend on the actual exposure conditions, such aslimited exposure to sun, and on the condition and cleanliness of the paint surface. The evaluation of the specific situation must be based on local experience, contact HEMPEL for advice.
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
49Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Severe
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
Specification sheet
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure)fresh water hosed in order to remove salts and other contaminants. When the surface isdry: Abrasive blasting to minimum Sa 3.0 according to ISO 8501-1, Using suitableabrasive media to give a surface profile amplitude of 75 to 100µm.Dust off residues.REPAIR OF DAMAGED COATING : Vacuum or spot blast clean to ISO 8501-1 plussupplement using a suitably sized abrasive to give a surface profile amplitude of 75 to100µm. Power tool cleaning to St-3 standard is only acceptable by agreement for areasthat are inaccessible or impractical for blast cleaning.MAINTENANCE : Blast clean areas of coating breakdown or, at QP Engineer' sdiscretion, fully blast clean surfaces to Sa 2.5 standard as per ISO 8501-1 plussupplement using a suitable sized abrasive to give a surface profile of 75 to 100µm.Power tool cleaning is only acceptable for small areas.
HEMPADUR SPRAY-GUARD 35490 11480 100 95690 5.6 : 1 1 h 8 h 60 10
HEMPADUR MULTI-STRENGTH 35530 T.B.A 100 95530 3 : 1 1 h 24 h 100 10 85
Remarks:
Helideck Markings to CAP437 shall be made with brush applied aliphatic polyurethane topcoat paint, applied over the epoxy seal coat.
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
51Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Severe
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
Specification sheet
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Oil and grease etc. to be removed by emulsion cleaning. Entire area to be (high pressure)fresh water hosed in order to remove salts and other contaminants. When the surface isdry: Abrasive blasting to minimum Sa 3.0according to ISO 8501-1. Surface profilecorresponding to Rugotest No. 3, BN 10, Keane-Tator Comparator, 3.0 G/S, or ISOComparator Rough Medium (G), surface profile 75 to 100µmDust off residues.
Product name (including quality number)
Treated area% Colour
Shade no.
Film thickness
(micron)
Wet Dry (sqm/ltr) Brush
Roller
Spray
Nozzleorifice
Recommended
Nozzlepressure
Application methodsTheoretical spreadingrate
HEMPADUR 85531 100 Red 50890 325 275 .021"-.023" 250 bar 3.1 (X) Xf/c
HEMPADUR 85531 100 Red 50630 350 275 .021"-.023" 250 bar 2.9 (X) Xf/c
t/u: touch up f /c: full coat s/c: stripe coat Total d.f.t. 550 X: Recommended (X): Possible
HEMPADUR 85531 50890 84 97531 4 : 1 1 h 6 h 14 08450 5
HEMPADUR 85531 50630 81 97531 4 : 1 1 h 6 h 14 08450 5
Remarks:
Stripe coating with brush before or after spray application of each coat is to be carried out on areas difficult to cover properly by spray as eg edges, corners, flanges, cutouts,handwelds and other rough surfaces.
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
53Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Buried
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.
HEMPEL
Specification sheet
7/18/2019 Qachl1858n - Qatar PetQACHL1858N - QATAR PETROLEUM (NEW SPECSroleum (New Specs)
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 12 (Revision 1) : Stainless Steel and Non Ferrous Metal Surfaces
sqm 100
Hempel Paints (Qatar) W.L.L
Surface preparation:
Remove oil and grease, etc. with suitable detergent. Remove salt and other contaminantsby (high pressure) fresh water hosing. When the surface is dry:
Abrasive sweep blasting with mineral (non metallic) abrasive to an evenly flattenedsurface with a dense profile of between 35 and 50µm.Dust off residues.
Product name (including quality number)
Treated area% Colour
Shade no.
Film thickness
(micron)
Wet Dry (sqm/ltr) Brush
Roller
Spray
Nozzleorifice
Recommended
Nozzlepressure
Application methodsTheoretical spreadingrate
HEMPADUR 15553 100 Off white 11630 100 50 .017"-.019" 175 bar 11.0 (X) Xf/c
HEMPADUR MIO 47950 100 Grey 13480 175 125 .019"-.021" 225 bar 6.1 X Xf/c
HEMPATHANE ENAMEL 55100 100 To Be Advised T.B.A 100 50 .017"-.019" 100 bar 10.4 X Xf/c
t/u: touch up f /c: full coat s/c: stripe coat Total d.f.t. 225 X: Recommended (X): Possible
Qatar Petroleum "Q.P." Document number : QP - SPC - L - 002 Revision 2
Area size:
Coating Schedule 12 (Revision 1) : Stainless Steel and Non Ferrous Metal Surfaces
sqm 100
Hempel Paints (Qatar) W.L.L
Product information:
Shade no.
Volumesolids %
Curingagent
Mixing ratiovolume
Pot life Dry to touch Application restrictions
Thinner
Flashpoint Min. Temp. Max. RH%
20°C 20°C °C °C
HEMPADUR 15553 11630 55 98021 3 : 1 2 h 3 h 30 08450 5
HEMPADUR MIO 47950 13480 76 98140 5 : 1 1 h 2 h 24 08450 0
HEMPATHANE ENAMEL 55100 T.B.A 52 95370 7 : 1 2 h 4 h 35 08080 -10
Remarks:
When the interval is denoted "Extended", the coated structure can possibly be overcoated even after longer periods. This will depend on the actual exposure conditions, such aslimited exposure to sun, and on the condition and cleanliness of the paint surface. The evaluation of the specific situation must be based on local experience, contact HEMPEL for advice.
Hempel's PreSale System 2.6.17 (Build 790)
Printed at: Environment :
55Page:
01.10.2013 13:42
User name:
Department name:
Created/Last modified: 17.09.2013 14:23
Quality Code:Cheryl Leitch
Admin Severe
QACHL1858N
The data, specifications, directions and recommendations (hereinafter "Information") given in this painting specification are based upon test results obtained under controlled or specifically defined conditions and said Information is correct to thebest of our knowledge. The User must satisfy itself that it is appropriate to use the Product in accordance with the Information in the actual conditions under which the Product is intended to be used, and the Manufacturer and Seller do notguarantee the accuracy, completeness or appropriateness of the Information when the Product is used in those conditions. The provisions regarding Hempel’s liability in its applicable conditions for sale, delivery and service shall apply to any andall claims arising out of or in connection with the use of the products recommended above, overleaf or otherwise.