KUALITAS REPAIR WELDING METODE MIG DENGAN PERLAKUAN PREHEATING PADA CAST WHEEL ALUMINIUM SEBAGAI SUPLEMEN MATERI MATA KULIAH TEKNIK PENGELASAN SKRIPSI Oleh : UUT PRIHONGGO K2510063 FAKULTAS KEGURUAN DAN ILMU PENDIDIKAN UNIVERSITAS SEBELAS MARET SURAKARTA Maret 2015
17
Embed
PREHEATING PADA CAST WHEEL ALUMINIUM SEBAGAI …eprints.uns.ac.id/18924/1/Halaman_Awal_Skripsi.pdfSampel dalam penelitian ini adalah velg cast wheel Aluminium. ... data menggunakan
This document is posted to help you gain knowledge. Please leave a comment to let me know what you think about it! Share it to your friends and learn new things together.
Transcript
KUALITAS REPAIR WELDING METODE MIG DENGAN PERLAKUAN
PREHEATING PADA CAST WHEEL ALUMINIUM SEBAGAI
SUPLEMEN MATERI MATA KULIAH TEKNIK PENGELASAN
SKRIPSI
Oleh :
UUT PRIHONGGO
K2510063
FAKULTAS KEGURUAN DAN ILMU PENDIDIKAN
UNIVERSITAS SEBELAS MARET
SURAKARTA
Maret 2015
i
PERNYATAAN KEASLIAN TULISAN
Saya yang bertanda tangan di bawah ini :
Nama : Uut Prihonggo
NIM : K2510063
Jurusan/Program Studi : PTK/Pendidikan Teknik Mesin
menyatakan bahwa skripsi saya berjudul “KUALITAS REPAIR WELDING
METODE MIG DENGAN PERLAKUAN PREHEATING PADA CAST
WHEEL ALUMINIUM SEBAGAI SUPLEMEN MATERI MATA KULIAH
TEKNIK PENGELASAN” ini benar-benar merupakan hasil karya saya sendiri.
Selain itu, sumber informasi yang dikutip dari penulis lain telah disebutkan dalam
teks dan dicantumkan dalam daftar pustaka.
Apabila pada kemudian hari terbukti atau dapat dibuktikan skripsi ini jiplakan,
saya bersedia menerima sanksi atas perbuatan saya.
Surakarta, Maret 2015
Yang membuat pernyataan,
Uut Prihonggo
ii
KUALITAS REPAIR WELDING METODE MIG DENGAN PERLAKUAN
PREHEATING PADA CAST WHEEL ALUMINIUM SEBAGAI
SUPLEMEN MATERI MATA KULIAH TEKNIK PENGELASAN
Oleh :
UUT PRIHONGGO
K2510063
Skripsi
Diajukan untuk memenuhi salah satu persyaratan
mendapatkan gelar Sarjana Pendidikan Program Pendidikan Teknik Mesin,
Jurusan Pendidikan Teknik Kejuruan
FAKULTAS KEGURUAN DAN ILMU PENDIDIKAN
UNIVERSITAS SEBELAS MARET
SURAKARTA
Maret 2015
iii
iv
v
ABSTRAK
Uut Prihonggo. KUALITAS REPAIR WELDING METODE MIG DENGAN
PERLAKUAN PREHEATING PADA CAST WHEEL ALUMINIUM
SEBAGAI SUPLEMEN MATERI MATA KULIAH TEKNIK
PENGELASAN. Skripsi, Fakultas Keguruan dan Ilmu Pendidikan Universitas
Sebelas Maret Surakarta. Maret 2015.
Tujuan penelitian ini adalah : (1) Menyelidiki pengaruh repair welding
pada cast wheel aluminium dengan metode pengelasan MIG dengan perlakuan
preheating terhadap tingkat kekerasannya; (2) Menyelidiki pengaruh repair
welding pada cast wheel aluminium dengan metode pengelasan MIG dengan
perlakuan preheating terhadap tingkat kekuatan impaknya; (3) Menyelidiki
pengaruh repair welding pada cast wheel aluminium dengan metode pengelasan
MIG dengan perlakuan preheating terhadap struktur foto mikro; (4) Menyusun
hasil penelitian ini menjadi kajian bahan ajar mata kuliah teknik pengelasan di
Prodi Pendidikan Teknik Mesin Jurusan Pendidikan Teknik dan Kejuruan
Fakultas Keguruan dan Ilmu Pendidikan UNS Surakarta.
Pengujian dilaksanakan di LKP Inlastek Surakarta, Politeknik
Manufaktur Ceper, Klaten dan Laboratorium Teknik S-1 UGM Yogyakarta.
Penelitian ini menggunakan metode MIG dengan perlakuan preheating.
Temperatur preheating yang digunakan adalah 121oC. Populasi dalam penelitian
ini adalah semua velg Aluminium. Sampel dalam penelitian ini adalah velg cast
wheel Aluminium. Penelitian ini merupakan penelitian eksperimen dan anilisis
data menggunakan teknik analisis deskriptif yaitu mengamati secara langsung
hasil eksperimen kemudian menganalisis dan menyimpulkan hasil penelitian.
Pengujian yang dilakukan meliputi: pengujian komposisi bahan, pengujian
ketangguhan, pengujian kekerasan, dan struktur foto mikro.
Berdasarkan hasil penelitian dapat disimpulkan bahwa (1) Komposisi
bahan penyusun utama velg adalah Al-7,22%Si. (2) Hasil pengujian ketangguhan
pengelasan (0,049 J/mm2) lebih rendah dibandingkan sebelum pengelasan (0,077
J/mm2). Hal ini menunjukkan bahwa hasil las lebih getas dibandingkan raw
material. (3) Hasil pengujian kekerasan menunjukan daerah raw material sebesar
466,26 BHN, daerah HAZ sebesar 550,31 BHN, dan daerah las sebesar 455,03
BHN. (4) Hasil foto struktur mikro menunjukkan penyebaran logam Al dan Si
lebih merata pada daerah Las dan raw material. Akan tetapi butiran logam pada
las lebih kecil dibandingkan raw material.
Kata kunci: Pengelasan, MIG, preheating, komposisi bahan, ketangguhan,
kekerasan, struktur foto mikro
vi
ABSTRACT
Uut Prihonggo. QUALITY REPAIR WELDING MIG METHOD WITH
PREHEATING TREATMENT AT CAST WHEEL ALUMINIUM AS A
SUPLEMENT COURSE MATERIAL WELDING TECHNIQUES. Thesis/Essay. Faculty of Teaching and Science Education, Sebelas Maret
University of Surakarta. March 2015.
The purpose of this research are: (1) to investigate the effect of repair
welding on cast wheel Aluminium with MIG welding method by preheating
treatment on hardness. (2) to investigate the effect of repair welding on cast wheel
Aluminium with MIG welding method by preheating treatment on the level of
toughness. (3) to investigate the effect of repair welding on cast wheel Aluminium
with MIG welding method by preheating treatment on microstructure photo. (4) to
compile the results of this research into the study of teaching material welding
engineering courses in mechanical engineering education program majoring in
technical and vocational education in faculty of teaching and science education,
UNS Surakarta.
The testing was conducted in LKP Inlastek Surakarta, Politeknik
Manufaktur Ceper, Klaten and in the laboratory techniques S-1 UGM
Yogyakarta. This research that the used MIG welding method with preheating
treatment. The temperature as used in preheating is 121oC. The population in this
research is all of wheels using aluminium alloy. The sample in this study is the
cast wheel aluminium alloy. The research is an experimental research and data
analysis using descriptive analysis techniques to directly observe experimental
results and then analyze and summarize the results of research. The test
performed include: testing of material composition, toughness testing, hardness
testing, and microstructure.
Based on the results of this study concluded that (1) the composition of
cast wheels are Al-7,22%Si. (2) the weld toughness test results (0,049 J/mm2)
lower than before welding (0,077 J/mm2). This suggests that the welds more
brittle than the raw material. (3) the hardness test results show the raw material
area are 466,26 BHN, the HAZ area are 550,31 BHN, and the welding area are
455,03 BHN. (4) the images show the distribution of the metal microstructure of
Al and Si is more evenly distributed in the weld area and raw material but the
weld metal grains smaller than raw material.
Keywords: welding, MIG, preheating, material composition, toughness, hardness,
microstructure
vii
MOTTO
“Inna ma‟al „usri yusraa”
“Sesungguhnya beserta kesulitan itu ada kemudahan”
(QS. Al Insyirah : 6)
“Hal jazaa-ul ihsaani illa ihsaan..”
“Tidak ada balasan kebaikan kecuali kebaikan pula..”
(QS. Ar-Rahman: 60)
“Kamu harus lebih bisa menghargai diri sendiri sebelum kamu menjualnya.”
(Uut Prihonggo)
“Untuk menggapai sesuatu yang kamu inginkan, kamu harus bersabar."
(Orochimaru –komik Naruto-)
“Sukses bukanlah akhir dari segalanya, kegagalan bukanlah sesuatu yang fatal,
namun keberanian untuk meneruskan kehidupanlah yang diperhatikan”
(Sir Winston Churchill)
viii
PERSEMBAHAN
Teriring syukurku pada-Mu, kupersembahkan karya ini untuk :
“Bapak, Ibu dan Kakak”
Terimakasih atas doa, bimbingan dan kasih sayang yang tiada henti telah
diberikan kepadaku, untuk saat ini dan selamanya kalian adalah segalanya
bagiku
“Ayub Budhi Anggono, Fachrudin Iskha”
Terimakasih untuk rekan 1 tim penelitian skripsi yang telah membantu dengan
penuh keikhlasan, memberikan semangat dan motivasi sehingga skripsi ini bisa
terselesaikan, semoga kita diberi jalan kesuksesan.
ACT Group
Terimakasih untuk kawan – kawan ACT yang tak pernah berhenti mendukung
untuk segera menyelesaikan ini.
“Teman-teman Pendidikan Teknik Mesin „10”
“Almamaterku”
ix
KATA PENGANTAR
Segala puji dan syukur penulis panjatkan kehadirat Allah SWT atas
limpahan rohmat, taufik, hidayah, dan karunia-Nya, sehingga penulis dapat
menyelesaikan skripsi ini. Skripsi ini berjudul ”KUALITAS REPAIR
WELDING METODE MIG DENGAN PERLAKUAN PREHEATING PADA
CAST WHEEL ALUMINIUM SEBAGAI SUPLEMEN MATERI MATA
KULIAH TEKNIK PENGELASAN”.
Skripsi ini disusun untuk memenuhi sebagian dari persyaratan dalam
mendapatkan gelar Sarjana Pendidikan pada Program Pendidikan Teknik Mesin
Jurusan Pendidikan Teknik dan Kejuruan, Fakultas Keguruan dan Ilmu
Pendidikan, Universitas Sebelas Maret, Surakarta. Skripsi ini dapat diselesaikan
tidak lepas dari berbagai pihak, oleh karena itu penulis mengucapkan terimakasih
kepada yang terhormat:
1. Dekan Fakultas Keguruan dan Ilmu Pendidikan Universitas Sebelas Maret
yang telah memberikan ijin menyusun skripsi.
2. Ketua Jurusan Pendidikan Teknik dan Kejuruan FKIP UNS yang telah
memberikan persetujuan atas permohonan penyusunan skripsi.
3. Ketua Program Studi Pendidikan Teknik Mesin JPTK FKIP UNS yang telah
memberikan persetujuan atas permohonan penyusunan skripsi.