PENGARUH KONSENTRASI DAN TEMPERATUR LARUTAN TERHADAP
KARAKTERISTIK RAPAT ARUS DIFUSI-BEDA TEGANGAN DARI
MEMBRAN KITOSAN DENGAN VARIASI MATRIK / PELARUT
SKRIPSI
BIDANG MINAT BIOFISIKA
Angelia Bella Kusumaningtyas
JURUSAN FISIKA
FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
UNIVERSITAS UDAYANA
2015
PENGARUH KONSENTRASI DAN TEMPERATUR LARUTAN TERHADAP KARAKTERISTIK RAPAT ARUS DIFUSI-BEDA TEGANGAN DARI
MEMBRAN KITOSAN DENGAN VARIASI MATRIK / PELARUT
SKRIPSI
BIDANG MINAT BIOFISIKA
Angelia Bella Kusumaningtyas
JURUSAN FISIKA
FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
UNIVERSITAS UDAYANA
2015
i
ii
iii
iv
v
PENGARUH KONSENTRASI DAN TEMPERATUR LARUTAN TERHADAP KARAKTERISTIK RAPAT ARUS DIFUSI-BEDA TEGANGAN DARI
MEMBRAN KITOSAN DENGAN VARIASI MATRIK / PELARUT
[SKRIPSI]
Karya tulis ini tidak dipublikasikan tetapi tersedia di perpustakaan
Dilingkungan Universitas Udayana;
diperkenankan dipakai sebagai referensi kepustakaan
tetapi pengutipan harus menyebutkan sumbernya
sesuai dengan kebiasaan ilmiah.
Karya tulis ini merupakan hak milik intelektual
Universitas Udayana
vi
vii
ABSTRAK Telah dilakukan penelitian tentang karakteristik rapat arus difusi-beda tegangan (J-V) dari membran kitosan. Penelitian bertujuan untuk mengetahui pengaruh konsentrasi (C), temperatur (T) larutan, dan variasi komposisi matrix/pelarut pada pembuatan membran terhadap kurva karakteristik J-V dari membran tersebut. Membran dibuat dari kitosan, sebagai bahan dasar (matrix) dan asam asetat 1% sebagai pelarut, dengan komposisi matrix/pelarut yaitu 1%, 2%, 3%, dan 4%. Pada eksperimen transport ion digunakan larutan elektrolit NaCl dengan variasi konsentrasi 0,1 mM, 1 mM, 10 mM, 100 mM, dan 1000 mM, dan temperatur antara 300,9-340,9 K. Hasil penelitian menunjukkan bahwa nilai rapat arus difusi ion (J) bertambah seiring dengan bertambah besarnya perbandingan konsentrasi larutan di ruang 1 (C1) dan ruang 2 (C2). Kurva J-V memperlihatkan hubungan kenaikan tidak linear dan kurva bergeser kearah potensial yang lebih besar seiring dengan kenaikan temperatur. Variasi komposisi matrix/pelarut juga berpengaruh terhadap kurva karakteristik J-V, dimana semakin banyak jumlah matrix pada pembuatan membran menyebabkan rapat arus difusi dan beda tegangan dari membran meningkat. Hasil-hasil ini menunjukkan bahwa gradient konsentrasi, temperatur, dan komposisi matrix/pelarut sangat berpengaruh terhadap karakteristik J-V dari membran kitosan. Kata Kunci: Kitosan, membran, larutan elektrolit, rapat arus difusi-tegangan
ABSRACT The study about the characteristics of the diffusion current density-potential different (J-V) ofchitosan membrane has been done. It aims to determine the effect of concentration (C), temperature (T) of solution, and the ratio of matrix/solvent to the J-V characteristic curve of the membrane. The membrane made of chitosan, as the base material (matrix) and 1% acetic acid as the solvent, with the various composition ofmatrix/solvent of 1%, 2%, 3%, and 4%. In the ion transport experiments, NaCl electrolyte solution with various concentration of 0.1mM, 1mM, 10mM, 100mM, and 1000mM and with variation of temperature of 300.9 to 340.9 K. The results showed that the value of the diffusion current density of ion increases with increasing the ratio of the concentration of solution in room 1 (C1) and room 2 (C2). The J-V curve shows non-linear relationship and it’s shifted toward larger potential different with increased in temperature. These results indicate that the gradient of concentration of solution, temperature, and the ratio of matrix/solvent greatly affect the J-V characteristics of chitosan membrane. Keywords: chitosan, membranes, electrolyte solution, the diffusion current density-
voltage
viii
DAFTAR ISI
Halaman
HALAMAN JUDUL .......................................................................................... i
FAKTA INTEGRITAS ..................................................................................... ii
LEMBAR PERSYARATAN GELAR ............................................................. iii
LEMBAR PENGESAHAN TUGAS AKHIR .................................................. iv
LEMBAR PERSETUJUAN .............................................................................. v
PEDOMAN PENGGUNAAN ........................................................................... vi
KATA PENGANTAR ........................................................................................ vii
ABSTRAK .......................................................................................................... viii
DAFTAR ISI ..................................................................................................... ix
DAFTAR TABEL .............................................................................................. xi
DAFTAR GAMBAR .......................................................................................... xii
BAB I PENDAHULUAN .................................................................................. 1
1.1 Latar Belakang ......................................................................................... 1
1.2 Rumusan Masalah .................................................................................... 3
1.3 Batasan Masalah ... ................................................................................. 3
1.4 Tujuan Penelitian ... ................................................................................. 3