BRITISH STANDARD BS EN ISO 6508-1:2005 Metallic materials — Rockwell hardness test — Part 1: Test method (scales A, B, C, D, E, F, G, H, K, N, T) The European Standard EN ISO 6508-1:2005 has the status of a British Standard ICS 77.040.10 Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy Not for Resale No reproduction or networking permitted without license from IHS --`,,```,,,,````-`-`,,`,,`,`,,`---
36
Embed
Metallic materials — Rockwell hardness testaudascn.com/upload/file/ISO 6508-1-05-20151113114419.pdf · ISO 6508 consists of the following parts, under the general title Metallic
This document is posted to help you gain knowledge. Please leave a comment to let me know what you think about it! Share it to your friends and learn new things together.
Transcript
Copyright British StandardProvided by IHS under liceNo reproduction or network
--`,,```,,,,````-`-`,,`,,`,`,,`---
BRITISH STANDARD
BS EN ISO 6508-1:2005
Metallic materials — Rockwell hardness test —
Part 1: Test method (scales A, B, C, D, E, F, G, H, K, N, T)
The European Standard EN ISO 6508-1:2005 has the status of a British Standard
ICS 77.040.10
���������������� ������������������������������� �������������s Institution nse with BSI - Uncontrolled Copy
Not for Resaleing permitted without license from IHS
BS EN ISO 6508-1:2005
CopProNo
--`,,```,,,,````-`-`,,`,,`,`,,`---
This British Standard was published under the authority of the Standards Policy and Strategy Committee on 13 January 2006
yright British Standards Institution vided by IHS under license with BSI - Uncontrolled Copy reproduction or networking permitted without license from
National foreword
This British Standard is the official English language version of EN ISO 6508-1:2005. It is identical with ISO 6508-1:2005. It supersedes BS EN ISO 6508-1:1999 which is withdrawn.
The UK participation in its preparation was entrusted by Technical Committee ISE/NFE/4, Mechanical testing of metals, to Subcommittee ISE/NFE/4/5, Indentation hardness testing, which has the responsibility to:
A list of organizations represented on this subcommittee can be obtained on request to its secretary.
Cross-references
The British Standards which implement international or European publications referred to in this document may be found in the BSI Catalogue under the section entitled “International Standards Correspondence Index”, or by using the “Search” facility of the BSI Electronic Catalogue or of British Standards Online.
This publication does not purport to include all the necessary provisions of a contract. Users are responsible for its correct application.
Compliance with a British Standard does not of itself confer immunity from legal obligations.
— aid enquirers to understand the text;
— present to the responsible international/European committee any enquiries on the interpretation, or proposals for change, and keep UK interests informed;
— monitor related international and European developments and promulgate them in the UK.
Summary of pages
This document comprises a front cover, an inside front cover, the EN ISO title page, the EN ISO foreword page, the ISO title page, pages ii to v, a blank page, pages 1 to 24, an inside back cover and a back cover.
The BSI copyright notice displayed in this document indicates when the document was last issued.
Amendments issued since publication
Amd. No. Date Comments
Not for ResaleIHS
EUROPEAN STANDARD
NORME EUROPÉENNE
EUROPÄISCHE NORM
EN ISO 6508-1
December 2005
ICS 77.040.10 Supersedes EN ISO 6508-1:1999
English Version
Metallic materials - Rockwell hardness test - Part 1: Test method(scales A, B, C, D, E, F, G, H, K, N, T) (ISO 6508-1:2005)
Matériaux métalliques - Essai de dureté Rockwell - Partie 1:Méthode d'essai (échelles A, B, C, D, E, F, G, H, K, N, T)
(ISO 6508-1:2005)
Metallische Werkstoffe - Härteprüfung nach Rockwell - Teil1: Prüfverfahren (Skalen A, B, C, D, E, F, G, H, K, N, T)
(ISO 6508-1:2005)
This European Standard was approved by CEN on 14 December 2005.
CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this EuropeanStandard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such nationalstandards may be obtained on application to the Central Secretariat or to any CEN member.
This European Standard exists in three official versions (English, French, German). A version in any other language made by translationunder the responsibility of a CEN member into its own language and notified to the Central Secretariat has the same status as the officialversions.
CEN members are the national standards bodies of Austria, Belgium, Cyprus, Czech Republic, Denmark, Estonia, Finland, France,Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Slovakia,Slovenia, Spain, Sweden, Switzerland and United Kingdom.
EUROPEAN COMMITTEE FOR STANDARDIZATIONC OM ITÉ EUR OP ÉEN DE NOR M ALIS AT IONEUROPÄISCHES KOMITEE FÜR NORMUNG
Management Centre: rue de Stassart, 36 B-1050 Brussels
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
Foreword This document (EN ISO 6508-1:2005) has been prepared by Technical Committee ISO/TC 164 "Mechanical testing of metals" in collaboration with Technical Committee ECISS/TC 1 "Steel - Mechanical testing", the secretariat of which is held by AFNOR. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by June 2006, and conflicting national standards shall be withdrawn at the latest by June 2006. This document supersedes EN ISO 6508-1:1999. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.
Endorsement notice
The text of ISO 6508-1:2005 has been approved by CEN as EN ISO 6508-1:2005 without any modifications.
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
Reference numberISO 6508-1:2005(E)
INTERNATIONAL STANDARD
ISO6508-1
Second edition2005-12-15
Metallic materials — Rockwell hardness test — Part 1: Test method (scales A, B, C, D, E, F, G, H, K, N, T)
Matériaux métalliques — Essai de dureté Rockwell —
Partie 1: Méthode d'essai (échelles A, B, C, D, E, F, G, H, K, N, T)
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
ii
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
iii
Contents Page
Foreword............................................................................................................................................................ iv Introduction ........................................................................................................................................................ v 1 Scope ..................................................................................................................................................... 1 2 Normative references ........................................................................................................................... 1 3 Principle................................................................................................................................................. 1 4 Symbols, abbreviated terms and designations ................................................................................. 1 5 Testing machine.................................................................................................................................... 4 6 Test piece .............................................................................................................................................. 4 7 Procedure .............................................................................................................................................. 5 8 Uncertainty of the results .................................................................................................................... 6 9 Test report ............................................................................................................................................. 6 Annex A (normative) Conventional HR30Tm and HR15Tm test for thin products...................................... 8 Annex B (normative) Minimum thickness of the test piece in relation to the Rockwell hardness............ 9 Annex C (normative) Corrections to be added to Rockwell hardness values obtained on convex
cylindrical surfaces ............................................................................................................................ 12 Annex D (normative) Corrections to be added to Rockwell hardness C scale values obtained on
spherical test surfaces of various diameters .................................................................................. 15 Annex E (informative) Procedure for periodic checking of the testing machine by the user .................. 16 Annex F (informative) Notes on diamond indenters..................................................................................... 17 Annex G (informative) Uncertainty of the measured hardness values....................................................... 18 Bibliography ..................................................................................................................................................... 24
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
iv
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2.
The main task of technical committees is to prepare International Standards. Draft International Standards adopted by the technical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights.
ISO 6508-1 was prepared by Technical Committee ISO/TC 164, Mechanical testing of metals, Subcommittee SC 3, Hardness testing.
This second edition cancels and replaces the first edition (ISO 6508-1:1999), which has been technically revised.
ISO 6508 consists of the following parts, under the general title Metallic materials — Rockwell hardness test:
— Part 1: Test method (scales A, B, C, D, E, F, G, H, K, N, T)
— Part 2: Verification and calibration of testing machines (scales A, B, C, D, E, F, G, H, K, N, T)
— Part 3: Calibration of reference blocks (scales A, B, C, D, E, F, G, H, K, N, T)
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
v
Introduction
The periodic checking of the testing machine described in informative Annex E is good metrological practice. It is intended to make the annex normative in the next revision of this part of ISO 6508.
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
blankCopyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
1
Metallic materials — Rockwell hardness test —
Part 1: Test method (scales A, B, C, D, E, F, G, H, K, N, T)
1 Scope
This part of ISO 6508 specifies the method for Rockwell and Rockwell superficial hardness tests (scales and field of application according to Table 1) for metallic materials.
Attention is drawn to the fact that, in this part of ISO 6508, the use of hardmetal for ball indenters is considered to be the standard type of Rockwell indenter ball. Steel indenter balls may be continued to be used if specified in a product specification, or by special agreement.
NOTE 1 Attention is drawn to the fact that results obtained with hardmetal balls can be significantly different than when using a steel ball. For specific materials and/or products, other specific International Standards apply (for instance ISO 3738-1 and ISO 4498-1).
NOTE 2 For certain materials, the fields of application may be narrower than those indicated.
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 6508-2:2005, Metallic materials — Rockwell hardness test — Part 2: Verification and calibration of testing machines (scales A, B, C, D, E, F, G, H, K, N, T)
3 Principle
Forcing an indenter of specified size, shape and material into the surface of a test piece in two steps under specified conditions (see Clause 7). Measuring the permanent depth h of indentation under preliminary test force after removal of additional test force.
From the values of h and that of the two constants N and S (see Table 2), the Rockwell hardness is calculated according to the formula:
Rockwell hardness hNS
= − (1)
4 Symbols, abbreviated terms and designations
4.1 See Tables 1 and 2 and Figure 1.
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
2
Table 1 — Rockwell scales
Rockwell hardness
scale
Hardness symbol
Type of indenter Preliminary test force
F0
Additional test force
F1
Total test force
F
Field of application (Rockwell hardness test)
Aa HRA Diamond cone 98,07 N 490,3 N 588,4 N 20 HRA to 88 HRA
Bb HRB Ball 1,587 5 mm 98,07 N 882,6 N 980,7 N 20 HRB to 100 HRB
Cc HRC Diamond cone 98,07 N 1,373 kN 1,471 kN 20 HRC to 70 HRC
D HRD Diamond cone 98,07 N 882,6 N 980,7 N 40 HRD to 77 HRD
E HRE Ball 3,175 mm 98,07 N 882,6 N 980,7 N 70 HRE to 100 HRE
F HRF Ball 1,587 5 mm 98,07 N 490,3 N 588,4 N 60 HRF to 100 HRF
G HRG Ball 1,587 5 mm 98,07 N 1,373 kN 1,471 kN 30 HRG to 94 HRG
H HRH Ball 3,175 mm 98,07 N 490,3 N 588,4 N 80 HRH to 100 HRH
K HRK Ball 3,175 mm 98,07 N 1,373 kN 1,471 kN 40 HRK to 100 HRK
15N HR15N Diamond cone 29,42 N 117,7 N 147,1 N 70 HR15N to 94 HR15N
30N HR30N Diamond cone 29,42 N 264,8 N 294,2 N 42 HR30N to 86 HR30N
45N HR45N Diamond cone 29,42 N 411,9 N 441,3 N 20 HR45N to 77 HR45N
15T HR15T Ball 1,587 5 mm 29,42 N 117,7 N 147,1 N 67 HR15T to 93 HR15T
30T HR30T Ball 1,587 5 mm 29,42 N 264,8 N 294,2 N 29 HR30T to 82 HR30T
45T HR45T Ball 1,587 5 mm 29,42 N 411,9 N 441,3 N 10 HR45T to 72 HR45T
a The field of application can be extended to 94 HRA for testing carbides.
b The field of application can be extended to 10 HRBW if specified in the product specification or by special agreement.
c The field of application can be extended to 10 HRC if the indenter possesses the appropriate dimensions.
NOTE Indenter balls with diameter 6,350 mm and 12,70 mm may also be used, if specified in the product specification or by special agreement.
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
3
Table 2 — Symbols and abbreviated terms
Symbol/ Abbreviated
term Designation Unit
F0 Preliminary test force N
F1 Additional test force N
F Total test force N
S Scale unit, specific to the scale mm
N Number, specific to the scale
h Permanent depth of indentation under preliminary test force after removal of additional test force (permanent indentation depth)
mm
HRA
HRC
HRD
Rockwell hardness 1000,002
h= −
HRB
HRE
HRF
HRG
HRH
HRK
Rockwell hardness 130 0,002
h= −
HRN
HRT Rockwell hardness 100
0,001h
= −
4.2 The following is an example of the designation of Rockwell hardness.
EXAMPLE
NOTE The numbers representing the test forces were originally based on units of kgf. For example, the test force of 30 kgf has been converted to 294,2 N.
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
4
Key
1 Indentation depth by preliminary force F0 2 Indentation depth by additional test force F1 3 Elastic recovery just after removal of additional test force F1 4 Permanent indentation depth h
5 Surface of specimen 6 Reference plane for measurement 7 Position of indenter
Figure 1 — Rockwell principle diagram
5 Testing machine
5.1 Testing machine, capable of applying predetermined forces as shown in Table 1 and in accordance with ISO 6508-2.
5.2 Conical diamond indenter, in accordance with ISO 6508-2, with an angle of 120° and radius of curvature at the tip of 0,2 mm.
5.3 Hardmetal ball indenter, in accordance with ISO 6508-2, with a diameter of 1,587 5 mm or 3,175 mm.
5.4 Measuring system, in accordance with ISO 6508-2.
NOTE A suggested procedure for periodic checks is given in Annex E. See also notes on diamond indenters in Annex F.
6 Test piece
6.1 The test shall be carried out on a surface which is smooth and even, free from oxide scale, foreign matter and, in particular, completely free from lubricants, unless specified otherwise in product or materials standards. An exception is made for reactive metals, such as titanium, which might adhere to the indenter. In such situations, a suitable lubricant such as kerosene may be used. The use of a lubricant shall be reported on the test report.
6.2 Preparation shall be carried out in such a way that any alteration of the surface hardness due to excessive heating or cold-working for example, is minimized. This shall be taken into account, particularly in the case of low-depth indentations.
6.3 After the test, no deformation shall be visible on the surface of the test piece opposite the indentation, except for HR30Tm (in this case, the test shall be performed in accordance with Annex A).
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
5
The thickness of the test piece, or of the layer under test (minimum values given in Annex B), shall be at least ten times the permanent indentation depth for cone indenters and fifteen times the permanent indentation depth for ball indenters, unless it can be demonstrated that the use of a thinner test piece does not affect the measured hardness value.
6.4 For tests on convex cylindrical surfaces and spherical surfaces, the corrections given in Annex C (Tables C.1, C.2, C.3 or C.4) and in Annex D (Table D.1) shall be applied.
In the absence of corrections for tests on concave surfaces, tests on such surfaces should be the subject of a special agreement.
7 Procedure
7.1 The test is normally carried out at ambient temperature within the limits of 10 °C to 35 °C. However, because temperature variation may affect the results, users of the Rockwell test may choose to control the temperature within a tighter range.
NOTE The temperature of the test material and the temperature of the hardness testing machine may effect the test results; consequently users should ensure that the test temperature does not adversally affect the hardness measurement.
7.2 The test piece shall be placed on a rigid support and supported in such a manner that the surface to be indented is in a plane normal to the axis of the indenter and the line of the indenting force, as well as to avoid a displacement of the test piece. If a locking device is used, it should be used in accordance with Clause 3 of ISO 6508-2:2005.
Before beginning a series of tests or when more than 24 h have elapsed since the last test, and after each change, or removal and replacement, of the indenter or test piece support, it shall be ascertained that the indenter and the test piece support are correctly mounted in the machine. The first two readings after such a change has been made shall be disregarded.
Products of cylindrical shape shall be suitably supported, for example, on centering V-blocks of steel with a Rockwell hardness of at least 60 HRC. Special attention shall be given to the correct seating, bearing and alignment of the indenters, the test piece, the centering V-blocks and the specimen holder of the testing machine, since any perpendicular misalignment may result in incorrect results.
7.3 Bring the indenter into contact with the test surface and apply the preliminary test force F0 without shock, vibration or oscillation. The duration of the preliminary test force F0 shall not exceed 3 s.
NOTE For testing machines with electronic control, the application time of the preliminary test force (Ta) and the duration time of the preliminary test force (Tpm) are combined by the following formula:
Tp = Ta/2 + Tpm u 3 s (2)
where
Tp is the total time of preliminary test force;
Ta is the application time of preliminary test force;
Tpm is the duration time of preliminary test force.
7.4 Set the measuring system to its datum position and, without shock, vibration or oscillation, increase the force from F0 to F in not less than 1 s and not more than 8 s.
NOTE In normal practice, the duration from F0 to F is between 2 s and 3 s on a test piece of about 60 HRC. For the Rockwell scales N and T, it is recommended that the duration is between 1 s and 1,5 s on a test piece of about 78 HR30N.
7.5 The total test force F shall be maintained for a duration of 4 s ± 2 s. Remove the additional test force F1 and, while the preliminary test force F0 is maintained, after a short time stabilisation, the final reading shall be made.
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
6
As an exception for test materials exhibiting excessive plastic flow (indentation creep) during the application of the total test force, special considerations may be necessary since the indenter will continue to penetrate. When materials require the use of a total force duration that exceeds the 6 s allowed by the tolerances, this requirement should he specified in the product specification. In these cases, the actual extended total force duration used shall be reported following the test results (for example, 65 HRFW, 10 s).
7.6 The Rockwell hardness number is derived from the permanent indentation depth h using the formulas given in Table 2 and is usually read directly from the measuring system. The derivation of the Rockwell hardness number is illustrated in Figure 1.
7.7 Throughout the test, the apparatus shall be protected from shock or vibration.
7.8 The distance between the centres of two adjacent indentations shall be at least four times the diameter of the indentation (but not less than 2 mm).
The distance from the centre of any indentation to an edge of the test piece shall be at least two and a half times the diameter of the indentation (but not less than 1 mm).
8 Uncertainty of the results
A complete evaluation of the uncertainty should be done according to the Guide to the expression of uncertainty in measurement (GUM) [3].
Independent of the type of sources, for hardness there are two possibilities for the determination of the uncertainty.
⎯ One possibility is based on the evaluation of all relevant sources appearing during a direct calibration. As a reference, an EA guideline [4] is available.
⎯ The other possibility is based on indirect calibration using a hardness reference block [abbreviated as CRM (certified reference material)] (see [2–5] in the Bibliography). A guideline for the determination is given in Annex G.
It may not always be possible to quantify all the identified contributions to the uncertainty. In this case, an estimate of type A standard uncertainty may be obtained from the statistical analysis of repeated indentations into the test piece. Care should be taken, if standard uncertainties of type A and B are summarised, that the contributions are not counted twice (see Clause 4 of GUM:1993).
9 Test report
The test report shall include the following information:
a) a reference to this part of ISO 6508, i.e. ISO 6508-1;
b) all details necessary for the complete identification of the test piece;
c) the test temperature, if it is not within the limits of 10 °C to 35 °C;
d) the result obtained (see the second-last paragraph of this clause);
e) all operations not specified in this part of ISO 6508, or regarded as optional;
f) details of any occurrence which may have affected the result (see Note);
g) the actual extended total-force duration time used, if greater than the 6 s allowed by the tolerances.
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
7
There is no general process for accurately converting Rockwell hardness into other scales, or hardness into tensile strength. Such conversions, therefore, should be avoided, unless a reliable basis for conversion can be obtained by comparison tests.
NOTE There is evidence that some materials may be sensitive to the rate of straining which causes small changes in the value of the yield stress. The corresponding effect on the termination of the formation of an indentation can make an alteration in the hardness value.
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
8
Annex A (normative)
Conventional HR30Tm and HR15Tm test for thin products
A.1 General
This test is carried out under conditions similar to those in the HR30T or HR15T test defined in this part of ISO 6508 but, by agreement, the appearance of indentations on the back of the test pieces (not permitted in the HRT test) is allowed.
This test is applicable with adequate precision to products of thickness less than 0,6 mm up to the minimum thickness indicated in the product standards and of a maximum HR30T Rockwell hardness of 80 (respectively 90 HR15T). The product standard specifies when the conventional HR30Tm or HR15Tm hardness test shall be applied.
The following requirements shall be met, in addition to those specified in this part of ISO 6508.
A.2 Test piece support
The test piece support shall comprise a polished and smooth diamond plate approximately 4,5 mm in diameter. This support surface shall be centred on the axis of the indenter and shall be perpendicular to it. Care shall be taken to ensure that it is seated correctly on the machine table.
A.3 Test piece preparation
If it is necessary to remove material from the test piece, this should be done on both sides of the test piece. Care shall be taken to ensure that this process does not change the condition of the base metal, for example by heating or work hardening. The base metal shall not be made thinner than the minimum allowable thickness.
A.4 Position of the test piece
The distance between the centres of two adjacent indentations or between the centre of one of the indentations and the edge of the test piece shall be at least 5 mm, unless otherwise specified.
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
9
Annex B (normative)
Minimum thickness of the test piece in relation to the Rockwell hardness
The minimum thickness of the test piece, or of the layer under test, is given in Figures B.1, B.2 and B.3.
Key
X Rockwell hardness Y minimum thickness of the test piece, mm
Figure B.1 — Test with diamond cone indenter (scales A, C and D)
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
10
Key
X Rockwell hardness Y minimum thickness of the test piece, mm
Figure B.2 — Test with ball indenters (scales B, E, F, G, H and K)
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
11
Key
X Rockwell hardness Y minimum thickness of the test piece, mm
Figure B.3 — Rockwell superficial test (scales N and T)
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
12
Annex C (normative)
Corrections to be added to Rockwell hardness values
obtained on convex cylindrical surfaces
For tests on convex cylindrical surfaces, the corrections given in Tables C.1, C.2, C.3 or C.4 shall be applied.
Table C.1 — Test with diamond cone indenter (scales A, C and D)
Radius of curvature
mm Rockwell hardness reading
3 5 6,5 8 9,5 11 12,5 16 19
20
25
30
35
40
45
50
55
60
65
70
75
80
85
90
3,0
2,5
2,0
1,5
1,5
1,0
1,0
0,5
0,5
0,5
3,0
2,5
2,0
2,0
1,5
1,0
1,0
1,0
0,5
0,5
0,5
0
3,0
2,5
2,0
2,0
1,5
1,5
1,0
1,0
1,0
0,5
0,5
0,5
0,5
0
2,5
2,5
2,0
1,5
1,5
1,0
1,0
1,0
0,5
0,5
0,5
0,5
0,5
0
0
2,0
2,0
1,5
1,5
1,0
1,0
1,0
0,5
0,5
0,5
0,5
0,5
0,5
0
0
1,5
1,5
1,5
1,0
1,0
1,0
0,5
0,5
0,5
0,5
0,5
0,5
0
0
0
1,5
1,0
1,0
1,0
1,0
0,5
0,5
0,5
0,5
0,5
0,5
0
0
0
0
1,0
1,0
1,0
0,5
0,5
0,5
0,5
0,5
0
0
0
0
0
0
0
1,0
1,0
0,5
0,5
0,5
0,5
0,5
0
0
0
0
0
0
0
0
NOTE Corrections greater than 3 HRA, HRC and HRD are not considered acceptable and are therefore not included in this table.
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
13
Table C.2 — Tests with 1,587 5 mm ball indenter (scales B, F and G)
Radius of curvature
mm Rockwell hardness reading
3 5 6,5 8 9,5 11 12,5
20
30
40
50
60
70
80
90
100
5,0
4,0
3,5
5,0
4,0
3,5
3,0
2,5
5,0
4,5
4,0
3,5
3,0
2,5
2,0
1,5
4,5
4,5
4,0
3,5
3,0
2,5
2,0
1,5
1,5
4,0
3,5
3,0
3,0
2,5
2,0
1,5
1,5
1,0
3,5
3,0
2,5
2,5
2,0
2,0
1,5
1,5
1,0
3,0
2,5
2,5
2,0
2,0
1,5
1,5
1,0
0,5
NOTE Corrections greater than 5 HRB, HRF and HRG are not considered acceptable and are therefore not included in this table.
Table C.3 — Rockwell superficial test (scale N) a, b
Radius of curvature c
mm Rockwell superficial
hardness reading 1,6 3,2 5 6,5 9,5 12,5
20
25
30
35
40
45
50
55
60
65
70
75
80
85
90
(6,0) d
(5,5) d
(5,5) d
(5,0) d
(4,5) d
(4,0) d
(3,5) d
(3,5) d
3,0
2,5
2,0
1,5
1,0
0,5
0
3,0
3,0
3,0
2,5
2,5
2,0
2,0
2,0
1,5
1,5
1,0
1,0
0,5
0,5
0
2,0
2,0
2,0
2,0
1,5
1,5
1,5
1,5
1,0
1,0
1,0
0,5
0,5
0,5
0
1,5
1,5
1,5
1,5
1,5
1,0
1,0
1,0
1,0
0,5
0,5
0,5
0,5
0,5
0
1,5
1,5
1,0
1,0
1,0
1,0
1,0
0,5
0,5
0,5
0,5
0,5
0
0
0
1,5
1,0
1,0
1,0
1,0
1,0
1,0
0,5
0,5
0,5
0,5
0
0
0
0
a These corrections are approximate only and represent the averages, to the nearest 0,5 Rockwell superficial hardness units, of numerous actual observations of the test surfaces having the curvatures given in this table.
b When testing convex cylindrical surfaces, the accuracy of the test will be seriously affected by misalignement of the elevating screw, V-anvil and indenter and by imperfections in the surface finish and straightness of the cylinder.
c For radii other than those given in this table, corrections may be derived by linear interpolation.
d The corrections given in parentheses shall not be used, except by agreement.
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
14
Table C.4 — Rockwell superficial test (scale T) a, b
a These corrections are approximate only and represent the averages, to the nearest 0,5 Rockwell superficial hardness units, of numerous actual observations of the test surfaces having the curvatures given in this table.
b When testing convex cylindrical surfaces, the accuracy of the test will be seriously affected by misalignement of the elevating screw, V-anvil and indenter and by imperfections in the surface finish and straightness of the cylinder.
c For radii other than those given in this table, corrections may be derived by linear interpolation.
d The corrections given in parentheses shall not be used, except by agreement.
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
15
Annex D (normative)
Corrections to be added to Rockwell hardness C scale values obtained
on spherical test surfaces of various diameters
For tests on convex spherical surfaces, the corrections given in Table D.1 shall be applied.
Table D.1
Diameter of sphere
d
mm
Rockwell hardness reading
4 6,5 8 9,5 11 12,5 15 20 25
55 HRC 6,4 3,9 3,2 2,7 2,3 2,0 1,7 1,3 1,0
60 HRC 5,8 3,6 2,9 2,4 2,1 1,8 1,5 1,2 0,9
65 HRC 5,2 3,2 2,6 2,2 1,9 1,7 1,4 1,0 0,8
The values of the correction to be added to Rockwell hardness C scale, ∆H, given in Table D.1, are calculated using the following formula:
21
16059
H
Hd
⎛ ⎞−⎜ ⎟⎝ ⎠∆ = × (D.1)
where
H is the Rockwell hardness reading;
d is the diameter of the sphere, expressed in millimetres.
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
16
Annex E (informative)
Procedure for periodic checking of the testing machine by the user
A check of the machine should be carried out on each day that the machine is used, at approximately each hardness level and for each range or scale that is to be used.
Prior to making the check, the measuring system should be indirectly verified (for each range/scale and hardness level) using a reference indentation on a hardness reference block, calibrated in accordance with ISO 6508-3. The measured dimension should agree with the certified value to within the maximum permissible error given in Table 5 of ISO 6508-2:2005. If the measuring system fails this test, appropriate action should be taken.
The check involves at least one indentation being made on a hardness reference block, calibrated in accordance with ISO 6508-3. If the difference between the mean measured hardness and the block’s certified value is within the permissible error limits given in Table 5 of ISO 6508-2:2005, the machine may be regarded as satisfactory. If not, an indirect verification should be performed.
A record of these results should be maintained over a period of time, and used to measure reproducibility and monitor drift of the machine.
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
17
Annex F (informative)
Notes on diamond indenters
Experience has shown that a number of initially satisfactory indenters can become defective after use for a comparatively short time. This is due to small cracks, pits or other flaws in the surface. If such faults are detected in time, many indenters may be reclaimed by regrinding. If not, any small defects on the surface rapidly worsen and make the indenter useless.
Therefore,
⎯ the condition of indenters should be checked initially and at frequent intervals using appropriate optical devices (microscope, magnifying glass, etc.);
⎯ the verification of the indenter is no longer valid when the indenter shows defects;
⎯ reground or otherwise repaired indenters should be reverified in accordance with 4.3.1 of ISO 6508-2:2005.
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
18
Annex G (informative)
Uncertainty of the measured hardness values
G.1 General requirements
The approach for determining uncertainty presented in this annex considers only those uncertainties associated with the overall measurement performance of the hardness testing machine with respect to the hardness reference blocks (abbreviated as CRM below). These performance uncertainties reflect the combined effect to all the separate uncertainties (indirect verification). Because of this approach, it is important that the individual machine components are operating within the tolerances. It is strongly recommended that this procedure should be applied for a maximum of one year after the successful passing of a direct verification.
Figure G.1 shows the four-level structure of the metrological chain necessary to define and disseminate hardness scales. The chain starts at the international level using international definitions of the various hardness scales to carry out international intercomparisons. A number of primary hardness standard machines at the national level "produce" primary hardness reference blocks for the calibration laboratory level. Naturally, direct calibration and the verification of these machines should be at the highest possible accuracy.
Figure G.1 — Structure of the metrological chain for the definition and dissemination of hardness scales
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
19
G.2 General procedure
The procedure calculates a combined uncertainty uI by the Root-Squared-Sum-Method (RSS) out of the different sources given in Table G.1, containing all symbols used and their designation. The expanded uncertainty, U, is derived from uI by multiplying with the coverage factor, k = 2.
G.3 Bias of the machine
The bias b of a hardness testing machine (also named error) which is derived from the difference between
⎯ the mean value of the five indentations during calibration of the hardness testing machine, and
⎯ the calibration value of the hardness reference block,
can be implemented in different ways into the determination of uncertainty.
G.4 Procedures for calculating uncertainty: hardness measurement values
NOTE In this Annex, the index CRM “Certified Reference Material” means, according to the definitions of the hardness testing standards, “Hardness Reference Block”.
G.4.1 Procedure without bias (method 1)
Method 1 (abbreviated as M1) is a simplified method, which can be used without considering the systematic error of the hardness testing machine.
In M1, the error limit, that means the range in which the machine is allowed to differ from the reference standard, is used to define the source uE of the uncertainty. There is no correction of the hardness values with respect to the error.
The procedure for the determination of U is explained in Table G.1 (see [3, 4] in the Bibliography).
2 2 2 2 2E CRM H msxU k u u u u u= ⋅ + + + + (G.1)
Where the result of the measurement is given by
X x U= ± (G.2)
G.4.2 Procedure with bias (method 2)
As an alternative to (M1), method 2 (abbreviated as M2) may be used, which is correlated with the conduct of a control chart. M2 may lead to smaller values of uncertainty.
The error b (step 10) can be expected to be a systematic effect. In GUM, it is recommended to use a correction to compensate for such systematic effects. This is the base of M2. The error limit uE is no longer in the calculation of the uncertainty but all determined hardness values have to be corrected by b or Ucorr has to be increased by b. The procedure for the determination of Ucorr is explained in Table G.1, (see [6, 7] in the Bibliography).
2 2 2 2 2corr CRM H msx bU k u u u u u= ⋅ + + + + (G.3)
Where the result of the measurement is given by
corr corr( )X x b U= + ± (G.4)
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
20
or by
ucorr corr( )X x U b= ± + (G.5)
depending on whether the bias (error) b is thought to be part of the mean value or of the uncertainty.
G.5 Expression of the result of measurement
For the expression of the result of measurement, the method used should be indicated. In general, as a result of the measurement, method 1 [Equation (G.2)] should be used (see also Table G.1, step 12).
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
Tabl
e G
.1 —
Det
erm
inat
ion
of th
e ex
pand
ed u
ncer
tain
ty a
ccor
ding
to m
etho
ds M
1 an
d M
2
Step
M
etho
d So
urce
s of
unc
erta
inty
S
ymbo
ls
Form
ula
Lite
ratu
re/C
ertif
icat
e Ex
ampl
e [..
] = H
RC
1 M1
Sta
ndar
d un
certa
inty
acc
ordi
ng to
th
e (1
σ) m
axim
um p
erm
issi
ble
erro
r u E
E
,2r
E2,
8u
u=
Per
mis
sibl
e er
ror u
E,2
r ac
cord
ing
to IS
O 6
508-
2:20
05,
Tabl
e 5
See
Not
e 1.
E
1,5
0,54
2,8
u=
=
2 M1
M2
Sta
ndar
d un
certa
inty
and
mea
n va
lue
of h
ardn
ess
of th
e C
RM
(fo
r det
aile
d ca
lcul
atio
n se
e IS
O 6
508-
3:20
05, T
able
B.4
)
u CR
M,
CR
MX
C
RM
CR
M2
Uu
=
UC
RM
, C
RM
X
acco
rdin
g to
cal
ibra
tion
certi
ficat
e of
CR
M
See
Not
e 2.
C
RM
CR
M0,
30,
15,
60,8
22
uX
==
=
3 M1
M2
Mea
n va
lue
and
stan
dard
dev
iatio
n of
the
mea
sure
men
t on
CR
M
,H
s H
1n
iI
HH
n=
=∑
2H
1
1(
)1
n
ii
sH
Hn
=
=−
−∑
Hi
acco
rdin
g to
ISO
650
8-2:
2005
, 5.
4.1
For t
he c
alcu
latio
n of
sH
the
larg
er v
alue
of s
H1
and
s H2
will
be
take
n.
Sin
gle
mea
sure
men
ts:
(1) 6
0,9
− 61
,0 −
61,
1 −
61,1
− 6
0,7
1H
160
,96:
0,17
Hs
==
(2
) 60,
7 −
60,8
− 6
1,1
− 61
,0 −
60,
8 2
H2
60,8
8:0,
16H
s=
=
4 M1
M2
Sta
ndar
d un
certa
inty
of h
ardn
ess
test
ing
mac
hine
whe
n m
easu
ring
CR
M
Hu
HH
ts
un⋅
=
t = 1
,14
for n
= 5
1,
140,
170,
095
Hu⋅
==
5 M1
M2
Mea
n va
lue
and
stan
dard
dev
iatio
n of
the
test
ing
of a
test
pie
ce
,x s
x
1n
iI
xx
n=
=∑
2
1
1(
)1
n
xi
is
xx
n=
=−
−∑
n =
5 5
mea
sure
men
ts o
n th
e te
st
piec
e S
ee N
ote
3. If
n =
1, s
x = 0
. Th
e ce
rtific
ate
shou
ld s
tate
th
at th
e un
certa
inty
app
lies
only
to th
e sp
ecifi
c re
adin
g,
not t
o th
e te
st p
iece
as
a w
hole
Sin
gle
valu
es
62,1
− 6
1,5
− 61
,2 −
63,
1 −
60,3
61
,64
1,04
xx s= =
21
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
Tabl
e G
.1 (c
ontin
ued)
Step
M
etho
d So
urce
s of
unc
erta
inty
S
ymbo
ls
Form
ula
Lite
ratu
re/C
ertif
icat
e Ex
ampl
e [..
] = H
RC
6 M1
M2
Sta
ndar
d un
certa
inty
whe
n m
easu
ring
a te
st p
iece
x
u
xx
ts
un⋅
=
t = 1
,14
for n
= 5
1,
141,
040,
535
xu
×=
=
7 M2
Sta
ndar
d un
certa
inty
acc
ordi
ng to
th
e re
solu
tion
of th
e le
ngth
m
easu
ring
syst
em
u ms
ms
ms
23
uδ
=
δ ms
= 0,
1 H
RC
m
s0,
10,
032
3u
==
×
8 M2
Dev
iatio
n of
har
dnes
s te
stin
g m
achi
ne fr
om c
alib
ratio
n va
lue
b
CR
Mb
HX
=−
S
teps
2 a
nd 3
S
ee N
ote
4.
b 1 =
60,9
6 −
60,8
2 =
0,14
b 2
= 60
,88
− 60
,82
= 0,
06
9 M2
Sta
ndar
d de
viat
ion
of th
e de
viat
ion
b
s b
m
m1
1n
ii
bb
n=
=∑
m1
2b
im
1
1(
)1
n is
bb
n=
=−
−∑
Ste
p 8
for n
m =
2
num
ber o
f mea
sure
men
t se
ries
0,10
b=
0,05
65
bs=
10 M
2
Sta
ndar
d un
certa
inty
of t
he
dete
rmin
atio
n of
b. C
an b
e de
term
ined
onl
y af
ter t
he s
econ
d se
ries
of m
easu
rem
ents
u b mb
bt
su
n⋅=
S
tep
9 t =
1,8
4 fo
r nm
= 2
S
ee N
ote
5.
1,84
0,05
65
0,07
2bu
×=
=
11 M
1
Det
erm
inat
ion
of th
e ex
pand
ed
unce
rtain
ty
U
22
22
2E
CR
Mm
sx
HU
ku
uu
uu
=⋅
++
++
Ste
p 1
to 7
k
= 2
22
22
2
0,54
0,15
20,
080,
530,
031,
55H
RC
U U
+=
×+
++
=
12
M1
Res
ult o
f the
mea
sure
men
t X
X
xU
=±
S
teps
5 a
nd 1
1 (6
1,6
1,6)
HR
CX
=±
(M1)
22
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
Tabl
e G
.1 (c
ontin
ued)
Step
M
etho
d So
urce
s of
unc
erta
inty
S
ymbo
ls
Form
ula
Lite
ratu
re/C
ertif
icat
e Ex
ampl
e [..
] = H
RC
13 M
2
Det
erm
inat
ion
of th
e co
rrec
ted
expa
nded
unc
erta
inty
U
corr
22
22
2co
rrC
RM
ms
xb
HU
ku
uu
uu
=⋅
++
++
Ste
p 2
to 7
and
10
k =
2
22
corr
22
2
corr
0,15
0,08
20,
530,
030,
071,
13H
RC
U U
+=
×+
++
=
14 M
2
Res
ult o
f the
mea
sure
men
t with
co
rrec
ted
mea
n va
lue
corr
X
corr
corr
()
Xx
bU
=+
±
Ste
ps 5
, 8 a
nd 1
3 co
rr(6
1,7
1,1)
HR
CX
=±
(M2)
15 M
2
Res
ult o
f the
mea
sure
men
t with
co
rrec
ted
unce
rtain
ty
corr
uX
co
rrco
rr(
)u
Xx
Ub
=±
+
Ste
ps 5
, 8 a
nd 1
3 co
rr(6
1,6
1,2)
HR
Cu
X=
± (M
2)
NO
TE 1
Th
e fa
ctor
2,8
is d
eriv
ed fr
om th
e de
term
inat
ion
of th
e st
anda
rd u
ncer
tain
ty fo
r a re
ctan
gula
r dis
tribu
tion.
NO
TE 2
If
nece
ssar
y, th
e ha
rdne
ss c
hang
e of
the
CR
M h
as to
be
cons
ider
ed.
NO
TE 3
If
betw
een
the
mea
sure
men
t of C
RM
and
test
pie
ce th
e op
tics
of th
e de
vice
are
cha
nged
, the
cor
resp
ondi
ng in
fluen
ce s
houl
d be
con
side
red.
NO
TE 4
If
0,8
u E,2r
< b
< 1
,0 u
E,2,
the
rela
tions
hip
of h
ardn
ess
valu
es b
etw
een
CR
M a
nd s
ampl
e sh
ould
be
cons
ider
ed.
NO
TE 5
B
ecau
se, f
or n
m =
2, i
n th
e un
certa
inty
ub t
he in
fluen
ce o
f the
long
-term
cha
nge
of b
is n
ot c
onta
ined
, for
crit
ical
app
licat
ions
it m
ay b
e ne
cess
ary
to ra
ise
the
num
ber o
f m
easu
rem
ents
nm
.
23
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
24
Bibliography
[1] ISO 3738-1, Hardmetals — Rockwell hardness test (scale A) — Part 1: Test method
[2] ISO 4498-1, Sintered metal materials, excluding hardmetals — Determination of apparent hardness — Part 1: Materials of essentially uniform section hardness
[3] BIPM, IEC, IFCC, ISO, IUPAC, IUPAP, OIML, Guide to the Expression of Uncertainty in Measurement,1) 1993
[4] EA 10-16, Guidelines on the Estimation of Uncertainty in Hardness Measurements, 2001
[5] GABAUER W., Manual of Codes of Practice for the Determination of Uncertainties in Mechanical Tests on Metallic Materials, The Estimation of Uncertainties in Hardness Measurements, Project, No. SMT4-CT97-2165, UNCERT COP 14: 2000
[6] GABAUER W., BINDER O., Abschätzung der Messunsicherheit in der Härteprüfung unter Verwendung der indirekten Kalibriermethode, DVM Werkstoffprüfung, Tagungsband 2000, S. pp. 255-261
[7] POLZIN T., SCHWENK D., Estimation of uncertainty of hardness testing; PC file for the determination, Materialprüfung, 3, 2002 (44), pp. 64-71
[8] ISO 6508-3:2005, Metallic materials — Rockwell hardness test — Part 3: Calibration of reference blocks (scales A, B, C, D, E, F, G, H, K, N, T)
1) Corrected and reprinted: 1995.
EN ISO 6508-1:2005
Copyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
blankCopyright British Standards Institution Provided by IHS under license with BSI - Uncontrolled Copy
Not for ResaleNo reproduction or networking permitted without license from IHS
--`,,```,,,,````-`-`,,`,,`,`,,`---
CopProNo
BS EN ISO 6508-1:2005
vr
--`,,```,,,,````-`-`,,`,,`,`,,`---
BSI
389 Chiswick High Road
London
W4 4AL
yright British Standards Institution ided by IHS under license with BSI - Uncontrolled Copy eproduction or networking permitted without license from IHS
BSI — British Standards InstitutionBSI is the independent national body responsible for preparing British Standards. It presents the UK view on standards in Europe and at the international level. It is incorporated by Royal Charter.
Revisions
British Standards are updated by amendment or revision. Users of British Standards should make sure that they possess the latest amendments or editions.
It is the constant aim of BSI to improve the quality of our products and services. We would be grateful if anyone finding an inaccuracy or ambiguity while using this British Standard would inform the Secretary of the technical committee responsible, the identity of which can be found on the inside front cover. Tel: +44 (0)20 8996 9000. Fax: +44 (0)20 8996 7400.
BSI offers members an individual updating service called PLUS which ensures that subscribers automatically receive the latest editions of standards.
Buying standards
Orders for all BSI, international and foreign standards publications should be addressed to Customer Services. Tel: +44 (0)20 8996 9001. Fax: +44 (0)20 8996 7001. Email: [email protected]. Standards are also available from the BSI website at http://www.bsi-global.com.
In response to orders for international standards, it is BSI policy to supply the BSI implementation of those that have been published as British Standards, unless otherwise requested.
Information on standards
BSI provides a wide range of information on national, European and international standards through its Library and its Technical Help to Exporters Service. Various BSI electronic information services are also available which give details on all its products and services. Contact the Information Centre. Tel: +44 (0)20 8996 7111. Fax: +44 (0)20 8996 7048. Email: [email protected].
Subscribing members of BSI are kept up to date with standards developments and receive substantial discounts on the purchase price of standards. For details of these and other benefits contact Membership Administration. Tel: +44 (0)20 8996 7002. Fax: +44 (0)20 8996 7001. Email: [email protected].
Information regarding online access to British Standards via British Standards Online can be found at http://www.bsi-global.com/bsonline.
Further information about BSI is available on the BSI website at http://www.bsi-global.com.
Copyright
Copyright subsists in all BSI publications. BSI also holds the copyright, in the UK, of the publications of the international standardization bodies. Except as permitted under the Copyright, Designs and Patents Act 1988 no extract may be reproduced, stored in a retrieval system or transmitted in any form or by any means – electronic, photocopying, recording or otherwise – without prior written permission from BSI.
This does not preclude the free use, in the course of implementing the standard, of necessary details such as symbols, and size, type or grade designations. If these details are to be used for any other purpose than implementation then the prior written permission of BSI must be obtained.
Details and advice can be obtained from the Copyright & Licensing Manager. Tel: +44 (0)20 8996 7070. Fax: +44 (0)20 8996 7553. Email: [email protected].