Lesson 4 - Phase Identificationprofex.doebelin.org/wp-content/uploads/2015/01/Lesson-4-Phase... · - Phase identification is independent of Rietveld refinement (must be done before)

Lesson 4

Phase Identification

Nicola DöbelinRMS Foundation, Bettlach, Switzerland

January 14 – 16, 2015, Bern, Switzerland

Repetition: X-Rays and Diffraction

2

n · λ = 2 · d · sin(θ)

d

λ

θθ

Wavelength (nm)

Inte

nsity

0.00 0.05 0.10 0.15 0.20 0.25 0.30

Cu

Kα1

Kα2

Kβ

Kα1

Kα2

Kβ

Mo

Repetition: Bragg-Brentano Diffractometer Setup

3

Repetition: Sample Preparation

4

- Graininess

- Micro-absorption

- Texture

- Sample height displacement

- Surface roughness

- Sample transparency

Diffraction Pattern

5

10 20 30 40 50 60

0

200

400

600

800

1000

Inte

nsity [counts

]

Diffraction Angle [°2θ]

Features:

Peak Positions (°2theta)

Peak Intensities (counts)

Peak Width (°2theta)

Phase Identification

6

10 20 30 40 50 60

0

200

400

600

800

1000

Inte

nsity [

cou

nts

]

Diffraction Angle [°2θ]

«Pattern Features» originate from crystallographic properties

Feature Origin

Peak positions - Symmetry of the unit

cell (space group)

- Dimensions of the

unit cell

Relative peak intensities - Coordinates of atoms

in unit cell

- Species of atoms

Absolute peak intensities - Abundance of phase

Peak width - Crystallite size

- Stress/Strain in crystal

lattice

Usually sufficient for identification

Phase Identification

7

10 20 30 40 50 60

0

200

400

600

800

1000

Inte

nsity [counts

]

Diffraction Angle [°2θ]

1. Extract peak positions

Phase Identification

8

10 20 30 40 50 60

0

200

400

600

800

1000

Inte

nsity [counts

]

Diffraction Angle [°2θ]

Sample

Corundum

Fluorite

1. Extract peak positions

2. Compare withdata base

9

Databases

10

Database Publisher # of Entries Data sets

PDF-2 ICDD(http://www.icdd.com)

274’443 All

PDF-4+ ICDD(http://www.icdd.com)

354’264 Inorganics

PDF-4/Minerals ICDD(http://www.icdd.com)

41’423 Minerals(Subset of PDF-4+)

PDF-4/Organics ICDD(http://www.icdd.com)

494’966 Organics

Crystallography

open database

CODhttp://www.crystallography.net

305’168* All(excl. biopolymers)

Databases containing powder diffraction data (line positions)

Commercial

Open Access

*2013: 215’708

Programmes for Search / Match

11

Programme Publisher Supported Databases*

HighScore PANalytical PDF-2/4

COD

EVA Search/Match Bruker PDF-2/4

COD

PDXL2 Rigaku PDF-2

COD

RayfleX GE PDF-2/4

Sleve ICDD PDF-2/4

Match! Crystal Impact PDF-2/4

COD

CSM Oxford Cryosystems PDF-2/4

Jade MDI PDF-2/4

+ many more

(see http://www.ccp14.ac.uk/solution/search-match.htm)

*incomprehensive

Search / Match: Peak Search

12

Automatic Peak Search:

- Subtract background

- Strip Kα2

- Smooth raw data

- Search and fit peaks

Search / Match: Peak Search

13

Not all peaks found automatically

� Add manually

Search / Match: Peak Search

14

Too many peaks found

� Delete manually

Search / Match: Phase Matching

15

Peak search ok

Run phase matching

Search / Match: False Positives

16

Search / Match: Restrictions

17

By chemical Composition

Use additional information from…

… synthesis

… chemical analysis

... geological situation

Search / Match: Restrictions

18

By Subfile

Only supported by PDF-2 andPDF-4+ database

No subfiles in COD database

Search / Match: Restrictions

19

All: Calcium Phosphate

Known from synthesis: Sample = synthetic calcium phosphate

Optionally: hydrate or

hydrogen phosphate

Chemical restrictions:

Summary: Phase Identification I

20

- Phases are identified from XRD patterns by comparing peakpositions with database entries

- Search/Match software & database are required

- Various commercial / open programmes and databases

- Qualitative (sometimes semi-quantitative) results are obtained

- Phase identification is independent of Rietveld refinement(must be done before)

Question I: Polytypes

21

a

b

Definition:

A lattice plane is a plane

which intersects atoms of

a unit cell across the whole

3‐dimensional lattice.

d(100)

d(010)

d(110)

d(-210)

- Each lattice plane

generates a diffraction

peak.

- The 2θ angle of thepeak depends on the plane’s d-spacing.

- Diffraction peaks canbe labelled with the plane’s Miller index.

Question I: Polytypes

22

Is powder XRD the ideal tool to distinguishand identify the following phases?

Phase Composition Space Group

Calcite CaCO3 R-3c

Magnesite MgCO3 R-3c

Siderite FeCO3 R-3c

Structurally very similar (polytypes)

They generate similar diffraction patterns

XRD provides no direct information on Ca/Mg/Fe content

Only changes in unit cell dimensions.

Question II: Polymorphs

23

Is powder XRD the ideal tool to distinguishand identify the following phases?

Phase Composition Space Group

Calcite CaCO3 R-3c

Vaterite CaCO3 P63/mmc

Aragonite CaCO3 Pnam

Structurally different (polymorphs)

Chemical analyses not able to distinguish (chem. identical)

XRD can easily distinguish

Summary: Phase identification II

24

- XRD is mostly sensitive to structural differences

- Only little information on chemical differences

- Chemical analyses (XRF, ICP, EDX,…) providecomplementary information

- Sometimes additional chemical information can be veryhelpful for phase identification (� restrictions)

- For a comprehensive material characterization, combineXRD with chemical analysis