K-CLAD 800 RANGE K-CLAD 801 - MILD STEEL BACKING PLATE FOR TEMPERATURES UP TO 450 DEGREES TYPICAL HARDNESS 60 HRC K-CLAD 801 (MILD STEEL) S801 (STAINLESS STEEL) As above but with 304L Stainless Steel Backing Plate TYPICAL ANALYSIS OF HARDFACING LAYER C : 5.0 Mn : 0.7 Cr : 30.0 TYPICAL HARDNESS 60 HRC STRUCTURE Primary carbides M7 C3 eutectic carbides Austenite MACHINABILITY Only by grinding PROPERTIES & APPLICATIONS Highly resistant to extreme abrasion and gouging at temperatures up tp 450˚C. Typical applications: dredge pump parts, hoppers, wearplates, crusher rolls, screw conveyors, shovel bucket teeth, palm oil expeller screws, catalytic pipes, etc. CARBON CHROME WITH MOLYBDENUM / WORKING TEMPERATURE UP TO 450˚C TECHNICAL DATA FILE NO. 0002 K-CLAD 803 (MILD STEEL) S803 (STAINLESS STEEL) As above but with 304L Stainless Steel Backing Plate TYPICAL ANALYSIS OF HARDFACING LAYER C : 5.0 Mn : 0.75 N : 5.0 Cr : 30.0 TYPICAL HARDNESS 59 HRC STRUCTURE Primary carbides M7 C3 eutectic carbides Austenite MACHINABILITY Only by grinding PROPERTIES & APPLICATIONS Resists corrosive wear and abrasive wear. Typical applications: chutes, feeders, scrolls CARBON CHROME NICKEL FOR CORROSIVE ENVIRONMENT / WORKING TEMPERATURE UP TO 450˚C K-CLAD 802 (MILD STEEL) S802 (STAINLESS STEEL) As above but with 304L Stainless Steel Backing Plate TYPICAL ANALYSIS OF HARDFACING LAYER C : 5.0 Mn : 0.7 Si : 0.5 Mo : 7.0 Nb : 7.0 W : 2.0 Cr : 22.0 TYPICAL HARDNESS 20c:62 HRC 550c:54 HRC 650c:50 HRC STRUCTURE Austenitic matrix with various complex carbides such as chromium rich hexagonal primary carbides, complex eutectic and globular niobium rich carbides MACHINABILITY Only by grinding PROPERTIES & APPLICATIONS Resists severe high stress abrasion resistant at temperatures up to 750˚C. Typical applications: blast furnace bells and hoppers, sinter plant, cement kilns, screens, exhaust fan blades, pearlite crushers, etc. COMPLEX CARBIDE DEPOSIT OF CHROMIUM, MOLYBDENUM, NIOBIUM, VANADIUM & TUNGSTEN / WORKING TEMPERATURES UP TO 750˚C K-CLAD 802 - STAINLESS STEEL BACKING PLATE FOR TEMPERATURES UP TO 750 DEGREES TYPICAL HARDNESS 50-62 HRC K-CLAD 803 - STAINLESS STEEL BACKING PLATE FOR CORROSIVE ENVIRONMENTS METALLIC TECHNICAL DATA Kingfisher TEE MILD S K-CLAD 800 K-CLAD 800 Wear Life Comparison The information contained on this product information sheet is to be used as guidance only. The advice and technical data given is done so in good faith and does not constitute any warranty or guarantee on product performance or suitability. We hereby reserve the right to change the technical information herewith without notification or prior agreement. T +44 (0)1384 410 777 F +44 (0)1384 410 877 E enquiries@kingfisher-industrial.com www.kingfisher-industrial.com Kingfisher Industrial Cradley Business Park Overend Road Cradley Heath West Midlands United Kingdom B64 7DW Protecting Industry Worldwide Kingfisher