1 2.008-spring-2004 S.Kim 1 2.008 Design & Manufacturing II Spring 2004 Welding & Joining 2.008-spring-2004 S.Kim 2 Today Ask “Dave and Pat” Joining & Welding PP 771-861, Kalpakjian Quiz 1 on March 17 th , 12:30 PM Closed book, calculator Lecture notes, HWs Q&A session? March 15 th , Monday, 5-6PM ? HW# 4, due next Monday 2.008-spring-2004 S.Kim 3 Joining Cost: Cheap, but expensive labor Quality: Wide range Flexibility: Manual vs automated Rate: Slow in general Very Large Crude Carrier (VLCC) 2.008-spring-2004 S.Kim 4 Joining processes non Laser welding engine emission controller ECUs fasteners door Body muffler windshield plastic fans door hinges 2.008-spring-2004 S.Kim Figures, B. Benhabib 5 Mechanical Fastening Any shape and material almost Disassemblable (except Rivets, etc.) Least expensive for low volume (standardized) Problems: strength, seal, insertion, loosening Threaded Bolted Rivets Snap fit 2.008-spring-2004 S.Kim 6 Rivets Cheap, light weight, don’t get loose Permanent, less strong than bolts Rule of thumb Minimum spacing = 3 x d Maximum spacing = 16 x thickness of the outer plate Rivets
7
Embed
Joining Joining processes - MIT OpenCourseWare · PDF fileMechanical Joining Hemming, seaming ... deep penetration (keyhole technology)
This document is posted to help you gain knowledge. Please leave a comment to let me know what you think about it! Share it to your friends and learn new things together.
Transcript
1
2.008-spring-2004 S.Kim 1
2.008 Design & Manufacturing II
Spring 2004
Welding & Joining
2.008-spring-2004 S.Kim 2
Today
Ask “Dave and Pat”Joining & Welding
PP 771-861, Kalpakjian
Quiz 1 on March 17th, 12:30 PMClosed book, calculatorLecture notes, HWsQ&A session? March 15th, Monday, 5-6PM ?HW# 4, due next Monday
2.008-spring-2004 S.Kim 3
Joining
Cost:Cheap, but expensive labor
Quality:Wide range
Flexibility:Manual vs automated
Rate:Slow in general
Very Large Crude Carrier (VLCC)2.008-spring-2004 S.Kim 4
Joining processes
non
Laser welding
engine
emission controllerECUs
fastenersdoor
Bodymuffler
windshieldplastic fans
door hinges
2.008-spring-2004 S.Kim Figures, B. Benhabib 5
Mechanical Fastening
Any shape and material almostDisassemblable (except Rivets, etc.)Least expensive for low volume (standardized)Problems: strength, seal, insertion, loosening
Threaded Bolted Rivets Snap fit
2.008-spring-2004 S.Kim 6
Rivets
Cheap, light weight, don’t get loosePermanent, less strong than boltsRule of thumb
Minimum spacing = 3 x dMaximum spacing = 16 x thickness of the outer plate
Adhesive BondingQuick and non-invasiveMost materials with high surface to volume ratioInsulation (thermal, electrical), conducting adhesives availableGood dampingClean surface preparationLong curing, hold time, low service TReliability, quality?Disassembly?
2.008-spring-2004 S.Kim 10
Stefan Equation
u
y
r
a
h/2h/2
F
⎥⎥⎦
⎤
⎢⎢⎣
⎡−= 22
4 114
3
if hhaFt µπ
Squeeze a drop of liquid
hf goes down, andViscosity goes up (curing)
Ft goes up (to separate)
When pullin apart?
⎥⎦
⎤⎢⎣
⎡−= 2
i2
f
4
h1
h1
43µµπFt
( )223
3 ardtdh
hp −=
µ
2.008-spring-2004 S.Kim 11
DFA for bonding
Do DoDo not Do not
Weak to tensile loading, strong to shear and compressiveOrganic
Epoxy, acrylic, etc..Inorganic
solder, cement, etc..
2.008-spring-2004 S.Kim B. Benhabib 12
Solid-Liquid: Brazing and SolderingIn brazing, the filler material (silver, brass, bronze) has a melting point above 425 ºC; and, in soldering, the filler material (lead, tin) has a melting point well below 425 ºC.
Capillary forces for the wetting and flow of the liquid metal into the gaps.
Proper fluxes for lowering surface tension, remove oxides, and prevent oxidation.
If the weld pool size is d in diameter, then you must feed at a rate that exceeds d/tmax. HI increases, welding speed must go upα Ja increases, interaction time must go up
Weld pool size d
Vmin = d / tmax
2.008-spring-2004 S.Kim J. Chun 21
Weld Pool – Heat Source Interaction Time
10-3
10-2
10-1
100
101
102
103
104
105
106
107
108
103 104 105 106 107 108
103
102
101
100
10-1
10-2
10-3
10-4
10-5
10-6
10-7
10-8
Heat Intensity (Watts/cm2)
Inte
ract
ion
Rat
e (S
econ
ds-1
)
Inte
ract
ion
Tim
e (S
econ
ds)
Copper,Aluminum
Steels,Nickels
Uranium,Ceramics H
ighe
r α, J
a
2.008-spring-2004 S.Kim 22
HAZ(Heat Affected Zone)Bad microstructure, course grains, weak to corrosionPlastic vs. Metal
Base metalHAZWeld metal
Temp Molten metalMelting point
Microstructure change temperature
Base metal temperature
2.008-spring-2004 S.Kim 23
Heat Affected Zone
Region near the weld pool is affected by heat. Microstructure changes.s ~ (α t)0.5
The size of the heat affected zone is controlled by the thermal diffusivity, α: Al, CuHI, time (speed)Metal vs. Plastic
More oxygen will cause oxidization (Oxidizing flame): bad for steels, OK for copperMore fuel will cause carburization (carburizing flame): Low heat for brazing, soldering, flame hardening
Inner cone: 3300oC
2100oC 1300oC
CNT
2.008-spring-2004 S.Kim 26
Arc fusion weldingTemperature up to 30000oCHeat travels with the electrons!Straight polarity: workpiece +, electrode –
Shallow penetration, sheet metal, wide gaps
reverse polarityDeeper penetration
-
+e-
Arrangement forconsumable electrodes
Heat generated at anode is about 15% of the heat generated at cathode.
Eelectron at cathode is given by three components:I(φ + Va + Vthomson)
Kinetic energyDrop across cool gas boundary
Work function(heat of condensation)
2.008-spring-2004 S.Kim 27
Consumable electrode processes
Shielded metal arc weldingCheapest and most basic process < $1,50050A-300A, <10KWWorkpiece thickness 3-20mm
Coating deoxidizes weld and provides shielding gasShielding gasSlag
Weld Base metal
Fille
r/elec
trode
Multiple passSlag removal
2.008-spring-2004 S.Kim 28
Fusion Arc Welding
Preventing oxidation is the most important problem. Coated electrodes to provide shielding gas
Coatings: fluorides, silicate binders(clay), cellulose, carbonatesElectrodes: different materials such as mild steel.
Submerged arc welding: covered by granular flux Flat surfaces, high throughput, good quality
Inert gas from external sourceGas metal arc welding (MIG)Flux-cored arc welding, etc. (very versatile with proper fluxes)
2.008-spring-2004 S.Kim 29
Gas Metal Arc WeldingGas metal arc welding is a special variation on arc welding in which the electrode filler metal is fed directly through the torch tip. As arcing occurs the electrode instantly melts, forming molten droplets that fall into the weld pool. Shielding gas is supplied through the torch tip to prevent chemical interactions with the surrounding atmosphere
Metal transfer- Spray transfer- Globular transfer- Short circuiting
Gas tungsten arc welding, formerly known as TIG weldingTungsten electrode + filler wire. Good for thin materials, better control, Al, Mg,Ti, etcHigh quality and finishTungsten electrode contamination200A DC-500A AC, 8kW-50kW
Travel
Shielding gas
Filler wire
Tungsten electrode
Arc Solidified weld metal
Molten metal
6
2.008-spring-2004 S.Kim 31
Other non-consumable electrode processes
Plasma arc welding: very higher energy concentration (33000oC), high feed rate 120-1000 mm/min, arc stablility, less thermal distortion, deep penetration (keyhole technology)
Laser beam welding, electron beam welding, etc
Electrodeplasma gas
Shielding gas
Work
Shielding gas nozzle
Orifice
Arc plasma
Plasma Arc Welding
2.008-spring-2004 S.Kim 32
Resistance WeldingSpot, seam, projection weldingHigh current through the weld, 3000A-100,000A (0.5 – 10 V)
Extremely high heat flux (105 W/cm2)Heat generated: H=i2Rt K (K=efficiency)Ex: 5000 A, 5 mm dia elctrodes, two 1mm thick steel plates
Effective resistance 200 Ω, Then H= 500 JNugget volume, 30 mm3, mass 0.24 g, 1400 J/g needed to melt336 J for melting < 500 J
Weld nugget
2.008-spring-2004 S.Kim 33
Resistance welding
Spot welding SequencePressure onCurrent onCurrent offPressure off
Projection welding
Weld nugget
indentation separation
2.008-spring-2004 S.Kim 34
Solid-state: interatomic bonding
UltrasonicOscillating tangential shear + static normal forces10KHz to 75 KHzShear plastic deformation breaking up top layer (contaminated) inter-atomic bond
FrictionRotational part (at least one), flash
DiffusionGoldsmiths bonded gold over copperDiffusion T > 0.5 TmInterface is the same as the bulk.Fuselage frames
2.008-spring-2004 S.Kim 35
Weld quality and defectsPorosity
Trapped gases, contaminantsPreheat or increase rate of heat inputReduce speed allowing gas to escape, cleaning
Slag inclusions
Oxides, fluxes, electrode coating trapped in weld zone
Clean weld bead during multi-weld processes
Provide enough shielding gas
2.008-spring-2004 S.Kim 36
Incomplete fusion/penetration
Preheat and clean joint
Clean weld area, enough shielding gas
Change joint design or type of electrode
Weld quality and defects
7
2.008-spring-2004 S.Kim Kalpakjian 37
Cracks, residual stresses
Temperature gradients, embrittlement of grain boundaries
Inability of weld metal to contract during cooling
Weld quality and defects
2.008-spring-2004 S.Kim 38
DFA - Welding
Loading conditions
2.008-spring-2004 S.Kim 39
DFM welding
2.008-spring-2004 S.Kim 40
Welding accessibility, DFM
Electrode must be held close to 45° when making these fillers
Easy to draw, but the 2nd weld will be hard to make
Very difficult
Easy
Easy to specify “weld all around” but …..
Try to avoid placing pipe joints near wall so that one or two sides are
inaccesible. These welds must be made with bent electrodes and mirror
Too close to side to allow proper electrode positioning. May be OK for average work but bad for leakproof welding