Ognjevzdržni betoni • Dense castables • Feuerbeton C O N D U R Izolacijski ognjevzdržni betoni • Insulating castables • Feuerlichtbetone C O N D U R - I Z O C O N D U R - M C C C O M A L Nizko in srednje cementni betoni • Low and medium cement castable • Niedrig und mittelzement Betone Ognjevzdržne nabojne mase • Refractory mixes • Feuerfeste Massen Ognjevzdržni kiti • Refractory mastics • Feuerkitte C O N D U K T I T Ognjevzdržne malte • Refractory mortars • Feuermörtel C O N D U M A L mm °C kg/dm 3 NAZIV PRODUCT NAME PRODUKTBEZEICHUNG OSNOVNA SUROVINA BASIC RAW MATERIAL ROHSTOFFBASIS GRANULACIJA GRAIN SIZE KÖRNUNG TEMPERATURA UPORABE TEMPERATUR LIMIT MAXIMALTEMPERATUR POTREBNA KOLIČINA MATERIAL REQUIRED MATERIALBEDARF KEMIJSKA ANALIZA CHEMICAL ANALYSIS CHEMISCHE ANALYSE TLAČNA TRDNOST COLD CRUSHING STRENGTH KALTDRUCKFESTIGKEIT Al 2 O 3 SiO 2 Fe 2 O 3 CaO 110°C 1100°C % MPa CONDUR 95 CONDUR 92 CONDUR 90 CONDUR 85 CONDUR 80 CONDUR 75 CONDUR 70 CONDUR 60 CONDUR 50 CONDUR 40 KORUND FUSED ALUMINA KORUND 0 - 6 0 - 6 0 - 6 0 - 6 0 - 6 0 - 6 0 - 6 0 - 6 0 - 6 0 - 6 KORUND FUSED ALUMINA KORUND KORUND, BOKSIT FUSED ALUMINA, BAUXIT KORUND, BAUXIT BOKSIT BAUXIT BAUXIT BOKSIT BAUXIT BAUXIT BOKSIT, ŠAMOT BAUXIT, FIRE CLAY BOXIT, SCHAMMOTE BOKSIT, ŠAMOT BAUXIT, FIRE CLAY BOXIT, SCHAMMOTE ŠAMOT FIRE CLAY SCHAMMOTE ŠAMOT FIRE CLAY SCHAMMOTE ŠAMOT FIRE CLAY SCHAMMOTE 1750 1700 1650 1600 1550 1450 1350 1300 1200 1150 2,90 2,85 2,85 2,80 2,75 2,65 2,50 2,35 2,25 2,20 74 68 64 57 56 58 45 45 45 30 110 65 58 49 48 30 30 28 26 25 0,1 0,5 0,8 1,5 1,5 1,0 1,3 2,0 3,0 4,0 Ognjevzdržni beton za torketiranje • Gunning castable • Spritzbeton C O N D U R - T mm °C kg/dm 3 NAZIV PRODUCT PRODUKTBEZEICHUNG OSNOVNA SUROVINA BASIC RAW MATERIAL ROHSTOFFBASIS GRANULACIJA GRAIN SIZE KÖRNUNG TEMP. UPORABE TEMPERATUR LIMIT MAXIMALTEMPERATUR POTREBNA KOLIČINA MATERIAL REQUIRED MATERIALBEDARF KEMIJSKA ANALIZA CHEMICAL ANALYSIS CHEMISCHE ANALYSE Al 2 O 3 SiO 2 Fe 2 O 3 CaO % CONDUMAL 80 CONDUMAL 70 CONDUMAL 42 KORUND FUSED ALUMINA KORUND 0 - 0,5 0 - 0,3 0 - 0,3 BOKSIT BAUXIT BAUXIT 1600 1500 1200 2,3 2,2 1,8 mm °C kg/dm 3 NAZIV PRODUCT PRODUKTBEZEICHUNG OSNOVNA SUROVINA BASIC RAW MATERIAL ROHSTOFFBASIS GRANULACIJA GRAIN SIZE KÖRNUNG TEMP. UPORABE TEMPERATUR LIMIT MAXIMALTEMPERATUR POTREBNA KOLIČINA MATERIAL REQUIRED MATERIALBEDARF KEMIJSKA ANALIZA CHEMICAL ANALYSIS CHEMISCHE ANALYSE TLAČNA TRDNOST COLD CRUSHING STRENGTH KALTDRUCKFESTIGKEIT Al 2 O 3 SiO 2 Fe 2 O 3 CaO 110°C 1100°C % MPa CONDUR 90 T CONDUR 85 T CONDUR 75 T CONDUR 50 T CONDUR 40 T IZO KORUND FUSED ALUMINA KORUND 0 - 5 0 - 5 0 - 5 0 - 5 0 - 8 KORUND, BOKSIT FUSED ALUMINA, BAUXIT KORUND, BAUXIT BOKSIT, ŠAMOT BAUXIT, FIRE CLAY BAUXIT, SCHAMOTTE ŠAMOT FIRECLAY SCHAMOTTE ŠAMOT FIRECLAY SCHAMOTTE VERMIKULIT 1600 1550 1400 1200 1100 2,70 2,75 2,55 2,20 1,20 mm °C kg/dm 3 Al 2 O 3 SiO 2 Fe 2 O 3 CaO 110°C 1100°C % MPa CONDUR 95 IZO KORUND FUSED ALUMINA KORUND 0 - 6 1700 1,60 CONDUR 40 IZO 0 - 8 VERMIKULIT 1100 1,25 CONDUR 30 IZO 0 - 8 PERLIT VERMIKULIT 1050 1,10 CONDUR IZO 0,8 0 - 8 PERLIT VERMIKULIT 950 0,8 NAZIV PRODUCT PRODUKTBEZEICHUNG OSNOVNA SUROVINA BASIC RAW MATERIAL ROHSTOFFBASIS GRANULACIJA GRAIN SIZE KÖRNUNG TEMP. UPORABE TEMPERATUR LIMIT MAXIMALTEMPERATUR POTREBNA KOLIČINA MATERIAL REQUIRED MATERIALBEDARF KEMIJSKA ANALIZA CHEMICAL ANALYSIS CHEMISCHE ANALYSE TLAČNA TRDNOST COLD CRUSHING STRENGTH KALTDRUCKFESTIGKEIT mm °C kg/dm 3 NAZIV PRODUCT PRODUKTBEZEICHUNG OSNOVNA SUROVINA BASIC RAW MATERIAL ROHSTOFFBASIS GRANULACIJA GRAIN SIZE KÖRNUNG TEMP. UPORABE TEMPERATUR LIMIT MAXIMALTEMPERATUR POTREBNA KOLIČINA MATERIAL REQUIRED MATERIALBEDARF KEMIJSKA ANALIZA CHEMICAL ANALYSIS CHEMISCHE ANALYSE TLAČNA TRDNOST COLD CRUSHING STRENGTH KALTDRUCKFESTIGKEIT Al 2 O 3 SiO 2 Fe 2 O 3 CaO 110°C 1100°C % MPa CONDUR 80 LCC CONDUR 95 MCC CONDUR 80 MCC CONDUR 50 MCC BOKSIT BAUXIT BAUXIT 0 - 6 0 - 6 0 - 6 0 - 6 KORUND FUSED ALUMINA KORUND KORUND, BOKSIT FUSED ALUMINA, BAUXIT KORUND, BAUXIT ŠAMOT FIRECLAY SCHAMOTTE 1500 1750 1550 1200 2,65 2,85 2,59 2,22 mm °C kg/dm 3 NAZIV PRODUCT PRODUKTBEZEICHUNG OSNOVNA SUROVINA BASIC RAW MATERIAL ROHSTOFFBASIS GRANULACIJA GRAIN SIZE KÖRNUNG TEMP. UPORABE TEMPERATUR LIMIT MAXIMALTEMPERATUR POTREBNA KOLIČINA MATERIAL REQUIRED MATERIALBEDARF KEMIJSKA ANALIZA CHEMICAL ANALYSIS CHEMISCHE ANALYSE TLAČNA TRDNOST COLD CRUSHING STRENGTH KALTDRUCKFESTIGKEIT Al 2 O 3 SiO 2 Fe 2 O 3 CaO 110°C 1100°C % MPa COMAL 95 IN COMAL 90 COMAL 80 COMAL 70 COMAL 50 KORUND FUSED ALUMINA KORUND 0 - 6 0 - 6 0 - 6 0 - 6 0 - 6 KORUND FUSED ALUMINA KORUND KORUND, BOKSIT FUSED ALUMINA, BAUXIT KORUND, BAUXIT BOKSIT BAUXIT BAUXIT ŠAMOT FIRECLAY SCHAMOTTE 1700 1600 1500 1350 1200 3,1 2,95 2,85 2,65 2,30 95 92 90 86 82 75 70 60 50 40 0,4 1,0 2,7 3,5 5,8 14,0 18,7 26,0 35,0 40,0 4,5 6,5 6,5 9,0 10,2 10,0 10,0 12,0 12,0 16,0 95 40 35 30 0,4 39 45 48 0,1 4,0 4,0 5,0 4,5 17 16 17 12 7 7 2 4 3 3 1 90 85 75 50 40 4,0 4,5 8,0 32 39 1,0 1,5 2,0 3,0 4,0 5,0 9,0 15,0 15,0 17,0 75 60 58 52 8 35 28 25 26 3 80 95 80 55 15,5 2,9 14,5 39 1,0 0,1 1,0 1,5 3 2 4,5 4,5 33 41 35 35 45 86 77 68 80 70 42 14 23 53 1 2 3 5 5 2 95 90 80 70 50 4,5 9,0 18 27 45 0,1 0,7 0,5 1,2 2 0,3 0,3 0,5 1,8 2,5 35 30 30 25 15 55 50 40 35 25 mm °C kg/dm 3 NAZIV PRODUCT PRODUKTBEZEICHUNG OSNOVNA SUROVINA BASIC RAW MATERIAL ROHSTOFFBASIS GRANULACIJA GRAIN SIZE KÖRNUNG TEMP. UPORABE TEMPERATUR LIMIT MAXIMALTEMPERATUR POTREBNA KOLIČINA MATERIAL REQUIRED MATERIALBEDARF KEMIJSKA ANALIZA CHEMICAL ANALYSIS CHEMISCHE ANALYSE Al 2 O 3 SiO 2 Fe 2 O 3 CaO % CONDUKTIT 90 CONDUKTIT 60 KORUND FUSED ALUMINA KORUND 0 - 0,3 0 - 0,5 BOKSIT BAUXIT BAUXIT 1750 1300 2,65 2,3 90 60 9,6 35 0,3 1 0,1 3