HAL Id: hal-00874064 https://hal.archives-ouvertes.fr/hal-00874064 Submitted on 17 Oct 2013 HAL is a multi-disciplinary open access archive for the deposit and dissemination of sci- entific research documents, whether they are pub- lished or not. The documents may come from teaching and research institutions in France or abroad, or from public or private research centers. L’archive ouverte pluridisciplinaire HAL, est destinée au dépôt et à la diffusion de documents scientifiques de niveau recherche, publiés ou non, émanant des établissements d’enseignement et de recherche français ou étrangers, des laboratoires publics ou privés. Experimental study of locally loaded timber in compression perpendicular to the grain Laurent Bleron, Louis Denaud, Robert Collet, Rémy Marchal To cite this version: Laurent Bleron, Louis Denaud, Robert Collet, Rémy Marchal. Experimental study of locally loaded timber in compression perpendicular to the grain. European Journal of Environmental and Civil Engineering, Taylor & Francis, 2011, 15 (3), pp.357-366. hal-00874064
12
Embed
Experimental study of locally loaded timber in compression ...
This document is posted to help you gain knowledge. Please leave a comment to let me know what you think about it! Share it to your friends and learn new things together.
Transcript
HAL Id: hal-00874064https://hal.archives-ouvertes.fr/hal-00874064
Submitted on 17 Oct 2013
HAL is a multi-disciplinary open accessarchive for the deposit and dissemination of sci-entific research documents, whether they are pub-lished or not. The documents may come fromteaching and research institutions in France orabroad, or from public or private research centers.
L’archive ouverte pluridisciplinaire HAL, estdestinée au dépôt et à la diffusion de documentsscientifiques de niveau recherche, publiés ou non,émanant des établissements d’enseignement et derecherche français ou étrangers, des laboratoirespublics ou privés.
Experimental study of locally loaded timber incompression perpendicular to the grain
Laurent Bleron, Louis Denaud, Robert Collet, Rémy Marchal
To cite this version:Laurent Bleron, Louis Denaud, Robert Collet, Rémy Marchal. Experimental study of locally loadedtimber in compression perpendicular to the grain. European Journal of Environmental and CivilEngineering, Taylor & Francis, 2011, 15 (3), pp.357-366. �hal-00874064�
Science Arts & Métiers (SAM)is an open access repository that collects the work of Arts et Métiers ParisTech
researchers and makes it freely available over the web where possible.
This is an author-deposited version published in: http://sam.ensam.euHandle ID: .http://hdl.handle.net/10985/7398
To cite this version :
Laurent BLERON, Louis DENAUD, Robert COLLET, Remy MARCHAL - Experimental study oflocally loaded timber in compression perpendicular to the grain - European Journal ofEnvironmental and Civil Engineering - Vol. 15, n°3, p.357-366 - 2011
Any correspondence concerning this service should be sent to the repository
Experimental study of locally loaded timber in compression perpendicular to the grain
Laurent Bleron* - Louis Denaud* - Robert Collet
* -
Rémy
Marchal*
* Laboratoire Bourguignon des Matériaux et Procédé (LaBoMap), EA3633 Arts et Métiers ParisTech Cluny Rue Porte de Paris F-71250 Cluny [email protected]
ABSTRACT. Since the test method for compression strength perpendicular to the grain was changed from a partial area to a full area loading test, strength values for softwood in EN 338 were significantly reduced. Consequently, a change in Eurocode 5 was necessary to ensure an equivalent resistance level in compression perpendicular to the grain. Experimental results are presented with wood in compression perpendicular to the grain. A numerical model is also presented. This model was used to establish a rule of calculation proposed at the P21A-Committee of the technical and construction equipment standardization office (BNTEC).
RÉSUMÉ. Depuis que la méthode de caractérisation de la résistance en compression transversale du bois a été modifiée, les valeurs de résistances des bois résineux ont été considérablement réduite dans la norme EN338. Par conséquent, une modification de l�Eurocode 5 était nécessaire pour assurer un niveau équivalent de résistance. Les résultats expérimentaux d�essais en compression perpendiculaire aux fibres sont présentés. Un modèle numérique est également présenté. Ce modèle a permis d�établir une règle de calcul qui a été proposé au niveau de la commission P21A du Bureau de Normalisation des Techniques et des Équipements de la Construction (BNTEC).
Wood materials in timber applications are subjected to various loading
conditions ranging from static to impact forces. Wood under static and quasi-static
loading is used in many structural members such as building members, bridges, etc.
The European standard EN 338 (EN338, 2003) provides a strength class system for
structural timber and strength profiles (characteristic strength values for bending,
tension, compression and shear stresses) for each strength class. Contact joints in
timber structures are often loaded in compression perpendicular to the grain.
Contrary to most types of timber connections (Ehlbeck and al., 1989), (Smith and al., 1988), (Bleron, 2000), the load-deformation behaviour of contact joints is
generally very ductile (figure 1). For compression perpendicular to the grain the two
options of tests are discussed.
The first one is a test where a block of wood is loaded in uniform compression
over the full surface. The second one is a situation where the test specimen is loaded
over part of the length corresponding to a rail on a sleeper. The latter method that is
used in US and Australia gives higher strength values than the block test because the
fibres adjacent to the loaded area contributes in taking the load (figure 1). The first
method was chosen in Europe and it was assumed that the rail test results could be
derived from the block results. Since the test method for compression strength
perpendicular to the grain was changed from a partial area to a full area loading test,
strength values for softwood in EN 338 were significantly reduced. Consequently, a
change in design rules was necessary to ensure an equivalent resistance level in
compression perpendicular to the grain.
Figure 1. Compressive strength perpendicular to the grain
2
4
5 1510
%
6
(MPa)
Compression perpendicular to the grain 3
EN 408 (EN408, 2004) provides an explicit definition of the compressive
strength. It is the stress obtained at the intersection with a 0,01h0 off-set line parallel
to the linear part of the stress-strain curve, where h is the height of the specimen
(figure 2). Eurocode 5 (Eurocode 5, 2004) enables an increase of design strength
values depending on the deformation, the specimen type and loading conditions.
Figure 2. Definition of the maximum compressive load perpendicular to the grain in accordance with EN 408
The compressive strength of a fully supported beam is:
75.11 90,90,90, ≤≤×= cccs kandfkf [1]
Where:
- fs is the compressive strength in the contact (area perpendicular to the grain),
- fc,90 is the reference compressive strength according to EN408,
- kc,90 is a factor taking into account the load configuration, the contact length
and the member depth,
- h0 is the gauge length, in millimetres.
A comprehensive survey of research work is given by Gehri (Gehri, 1997),
Blass (Blass and al., 2004) and Augustin (Augustin and al, 2006). Eurocode 5 is
based on a model set out in (Blass and al., 2004). The starting point for this model is
the tests reported in Madsen (Madsen, 2000) where an effective length of contact
was found. This length is equal to the length of actual contact increased by 30 mm.
The length of 30 mm is also punitive for timber construction, specifically for glulam
structures.
F c,90,max
0.1 ×F
Load
Displacement
0.01 × h 0
hh0
c,90,max
c,90,max
0.4 ×F
Some empirical models proposed by Riberholt (Riberholt, 2000). Van der Put
(Van der Put, 2006) presented an analytical model based on plasticity theory. Wood
materials are commonly assumed to be orthotropic for analytical study. The linear
material behavior of wood is generally observed in longitudinal and transverse
tension, while the stress-strain relationships in compression and shear exhibit
significant nonlinearity and ductility (figure 3). When loaded in compression, the
response for the three main directions (L: longitudinal, R: radial, T: tangential) can
be characterized by an initial elastic region, followed by a plateau region and finally
a region of rapidly increasing stress. To simulate wood nonlinearity in shear and
compression, Patton-Mallory (Patton-Mallory, 1997) used bilinear functions for
wood nonlinear modelling.
Figure 3. Typical stress-strain curves for wood loaded in compression and tension (Kollmann, 1984)
Here we propose to test different loading cases and simulations in order to check
the compression strength perpendicular to the grain of locally loaded timber. The
objective is to propose an original formula for estimating the effective contact area
in the case of compression perpendicular to the grain depending on the type of
loading
2. Material and methods
2.1. Experimental procedure
Mechanical testing was carried out using an INSTRON universal testing
machine, with a 100 kN load cell. The standard test method of EN 408 was applied
for all tests, resulting in a well defined value for the reference compressive strength
Stress
Strain
Tension (L)
Compression (L)
Compression (T)
LR
T
Compression perpendicular to the grain 5
and other data. The loading rate was 5 mm/min. The compressive strength fc,90
perpendicular to the grain is defined as the conventional value determined by a
residual deformation of 0.01h0, where h is the height of the sample. The stiffness of
wood, in the direction perpendicular to the grain, is determined by its modulus of
elasticity Ec,90. This secant modulus is conventionally defined as the slope of the
linear part in the stress�strain relationship, between 10% and 40% of the
conventional failure stress.
Glued laminated timber blocks of Norway Spruce (Picea abies Karst) were tested
to show the compressive strength perpendicular to the grain for different loading
condition. Test material was conditioned between 10% and 12% MC. The reference
compressive test pieces are summarized in the table 1 and figure 4. The different
rules of calculation take into consideration only the effect of the beam heights. The
strength in compression perpendicular to the grain being independent of the width,
we then chose as a single 78 mm width.
Figure 4. Different loading cases in compression perpendicular to the grain (Lap=100mm)
Loading cases No of
tests
b h L
Case 1 Uniform compression � EN 408 22 78 300 100
Case 2.1 Continuous beam in local compression 10 78 300 800
Case 2.2 Continuous beam in local compression 10 78 150 800
Case 2.3 Continuous beam in local compression 10 78 300 160
Case 3 ASTM D 143 10 78 300 800
Case 4 Beam end in local compression 10 78 300 800
Table 1. Dimension of the sample
3. Results
Failure occurs at the plastic threshold by compression and lateral deformation.
After local compression failure a load increase is possible. The test results are
presented in table 4 (mean & standard deviation). The compression stress
perpendicular to the grain is calculated using an effective contact length parallel to
the grain. Comparison shows that the member height has no influence on the load-
carrying-capacity (comparing case 2.1 and 2.2) for low beams heights. If the timber
member protrudes over the end of the contact area, the actual contact length has to
be extended on both sides by a length. Indeed, the strength in compression
perpendicular to the grain doubles between the case 1 and the case 2.1. Some
simulations have been made in order to determine this effective length.
The presented material model has been implemented in the 3D nonlinear
explicit finite element simulation code ANSYS. FE analyses were carried out using
8-nodes solid elements (SOLID45). Parameters EL, ER and ET are the moduli of
elasticity in the three orthotropic directions and GLR, GLT and GRT are the shear
moduli in the respective orthotropic planes. Mechanical behaviour was taken as
orthotropic and elastoplastic. Data of spruce used for the model were taken from
literature ((Guitard, 1987), (Pluvinage, 1992)) (table 2 and table 3). The mechanical
properties values were chosen based on our test samples densities and elastic
modulus to better estimate the behaviour of wood.
Young�s Modulus (MPa) EL = 10700 ER = 710 ET = 430