ESAB E7016 TWINCOAT ELECTRODE OK 53.16 SPEZIAL THE ORIGINAL ESAB TWINCOAT FORMULATION FROM EUROPE VACPAC - Vacuum Sealed To Reduce Moisture Absorbtion & Electrode Damage Smaller Pack Sizes Reduce Waste & Cost Smooth Running & Low Spatter For All 7016 Electrode Users CIGWELD.COM.AU ESABASIA.COM 1300 654 674 | F: 03 9474 7391 | [email protected]OK 53.16 is a double-coated electrode combining the running characteristics of a rutile electrode with the mechanical properties of a basic electrode. ESAB’s OK 53.16 welds on both AC and DC and the spatter loss is minimal. ESAB OK 53.16 Electrode
2
Embed
ESAB E7016 TWINCOAT ELECTRODE THE ORIGINAL ESAB … OK5316 Flyer.pdf · ESAB E7016 TWINCOAT ELECTRODE OK 53.16 SPEZIAL THE ORIGINAL ESAB TWINCOAT FORMULATION FROM EUROPE VACPAC -
This document is posted to help you gain knowledge. Please leave a comment to let me know what you think about it! Share it to your friends and learn new things together.
Transcript
ESAB E7016 TWINCOAT ELECTRODE
OK 53.16 SPEZIAL
THE ORIGINAL ESAB TWINCOAT FORMULATION FROM EUROPE
OK 53.16 is a double-coated electrode combining the running characteristics of a rutile electrode with the mechanical
properties of a basic electrode. ESAB’s OK 53.16 welds on both AC and DC and the spatter
loss is minimal.
ESAB OK 53.16 Electrode
OK 53.16 SPEZIAL
All Weld Metal (%) Min MaxC 0.10Si 0.30 0.70Mn 0.70 1.20P 0.030S 0.030Cr 0.19Ni 0.29Mo 0.19V 0.049Nb 0.049Cu 0.29
OK 53.16 is a double coated electrode combining the running characteristics of a rutile with the mechanical properties of a basic electrode. The double coating enables it to be used with small arc welding machines with low OCV. OK 53.16 welds on both AC and DC.
ISO AWS
As welded As welded
Properties Min Max Min
Rp0.2 (MPa) 400
ReH (MPa) 380
Rm (MPa) 510 560 490
A4 (%) 22
A5 (%) 22
Charpy V at -20°C (J) 47
Charpy V at -30°C (J) 27
CHEMICAL COMPOSITION ECONOMICS & CURRENT DATA
MECHANICAL PROPERTIES OF WELD METAL
CLASSIFICATIONS ElectrodeAS/NZS 1553.1: (old) E4816-2 H10AS/NZS 4855: (new) B E4916 A U H10SFA/AWS A5.1 E7016 EN ISO 2560-A E 38 2B 32 H10
Minimum AC or DC OCV: 50 VElectrode Polarity: AC, DC+, DC-
Part Dimension Current (A) Packet Carton W h N B H T U WeldingNumber (mm)- Ø x Length Min Max Positions
53162534G0 2.5 x 350 50 90 2KG 12kg - 6 x 2kg 2,1 102 0,58 83,3 0.73 59 26,8 1,2,3,4,6,7
53163234G0 3.2 x 350 90 150 1.6KG 9.6kg - 6 x 1.6kg 3,4 101 0,54 53,6 1,2 56 31,2 1,2,3,4,6,7
53164044G0 4.0 x 450 120 190 2.2KG 13.2kg - 6 x 2.2kg 6.9 105 0.59 24 1.65 90 28 1,2,3,4,6,7
W = Weight (kg / 100 electrodes)h = Efficiency (g weld metal x 100 / g core wire)N = Effective value (kg weld metal / kg electrodes)B = Changes (number of electrodes / kg weld metal)
H = Deposit rate at 90% of max current (kg weld metal / hour arc time)T = Fusion time at 90% of max current (s / electrode)U = Arc voltage (V)