CC-COM-05-2019-003862 SI R1 · 2019-07-02 · S3 Dielectric measurements The dielectric measurements were carried on a TH2828A impedance analyzer for 1 from 500 Hz to 1 MHz, with
This document is posted to help you gain knowledge. Please leave a comment to let me know what you think about it! Share it to your friends and learn new things together.
Transcript
S1
Supporting Information A New Ferroelastic Hybrid Material with a Large Spontaneous Strain: (Me3NOH)2[ZnCl4] Wei Yuan,a Ying Zeng,a Ya-Yin Tan,b Jian-Hua Zhou,b Wei-Jian Xu,a,c,* Wei-Xiong Zhanga,* and Xiao-Ming Chena a MOE Key Laboratory of Bioinorganic and Synthetic Chemistry, School of Chemistry, Sun Yat-Sen
University, Guangzhou, 510275, P. R. China. b Key Laboratory of Sensing Technology and Biomedical Instruments of Guangdong Province, School
of Biomedical Engineering, Sun Yat-Sen University, Guangzhou 510275, China. c Department of Chemistry & CICECO-Aveiro Institute of Materials, University of Aveiro, 3810-193
Figure S4. Temperature dependence of ε” of 1 measured on the powder sample at 0.5-80
kHz.
S11
300 350 400 450 500 550 600 65030
40
50
60
70
80
90
100
Wei
ght /
%
T / K
463 K
Figure S5. TG profiles of 1.
S12
Figure S6. Decomposed fingerprint plots for 1 resolved into H···Cl, H···O and H···H contacts. Upper for Me3NOH+ with O1 atom and the bottom for Me3NOH+ with O2 atom.
S13
Reference S1. O. V. Dolomanov, L. J. Bourhis, R. J. Gildea, J. A. K. Howard and H. Puschmann, J. Appl. Crystallogr.,
2009, 42, 339-341.
S2. K. Aizu, J. Phys. Soc. Jpn., 1969, 27, 387-396.
S3. K. Aizu, J. Phys. Soc. Jpn., 1970, 28, 706-716.
S4. J. Sapriel, Phys. Rev. B, 1975, 12, 5128.
S5. C.-Y. Mao, W.-Q. Liao, Z.-X. Wang, Z. Zafar, P.-F. Li, X.-H. Lv and D.-W. Fu, Inorg. Chem., 2016, 55,
7661-7666.
S6. S. Han, X. Liu, J. Zhang, C. Ji, Z. Wu, K. Tao, Y. Wang, Z. Sun and J. Luo, J. Mater. Chem. C, 2018, 6,
10327-10331.
S7. Z.-X. Wang, W.-Q. Liao, H.-Y. Ye and Y. Zhang, Dalton Trans., 2015, 44, 20406-20412.
S8. X.-N. Li, P.-F. Li, Z.-X. Wang, P.-P. Shi, Y.-Y. Tang and H.-Y. Ye, Polyhedron, 2017, 129, 92-96.
S9. Q. Li, P.-P. Shi, Q. Ye, H.-T. Wang, D.-H. Wu, H.-Y. Ye, D.-W. Fu and Y. Zhang, Inorg. Chem., 2015,
54, 10642-10647.
S10. X.-N. Hua, C.-R. Huang, J.-X. Gao, Y. Lu, X.-G. Chen and W.-Q. Liao, Dalton Trans., 2018, 47,
6218-6224.
S11. J.-X. Gao, X.-N. Hua, P.-F. Li, X.-G. Chen and W.-Q. Liao, J. Phys. Chem. C, 2018, 122,
23111-23116.
S12. X.-F. Sun, P.-F. Li, W.-Q. Liao, Z. Wang, J. Gao, H.-Y. Ye and Y. Zhang, Inorg. Chem., 2017, 56,
12193-12198.
S13. W.-Q. Liao, J.-X. Gao, X.-N. Hua, X.-G. Chen and Y. Lu, J. Mater. Chem. C, 2017, 5, 11873-11878.
S14. K. Tao, Z. Wu, S. Han, J. Zhang, C. Ji, Y. Wang, W. Zhang, J. Luo and Z. Sun, J. Mater. Chem. C,
2018, 6, 4150-4155.
S15. A. Zeb, Z. Sun, T. Khan, M. A. Asghar, Z. Wu, L. Li, C. Ji and J. Luo, Inorg. Chem. Front., 2017, 4,
1485-1492.
S16. Y.-W. Zhang, P.-P. Shi, W.-Y. Zhang, Q. Ye and D.-W. Fu, Inorg. Chem., 2018, 57, 10153-10159.
S17. A. Zeb, Z. Sun, A. Khan, S. Zhang, T. Khan, M. A. Asghar and J. Luo, Inorg. Chem. Front., 2018, 5,
897-902.
S18. M. Amami, S. van Smaalen, L. Palatinus, A. Ben Salah, X. Helluy and A. Sebald, Z. Kristallogr. Cryst.
Mater., 2002, 217, 532.
S19. P.-F. Li, W.-Q. Liao, Q.-Q. Zhou, H.-Y. Ye and Y. Zhang, Inorg. Chem. Commun., 2015, 61, 77-81.
S20. W.-Q. Liao, H.-Y. Ye, Y. Zhang and R.-G. Xiong, Dalton Trans., 2015, 44, 10614-10620.
S21. G.-Q. Mei and W.-Q. Liao, J. Mater. Chem. C, 2015, 3, 8535-8541.