MILD & MEDIUM CARBON STEEL ELECTRODES
1-1617-4849-7980-9596-110111-119120-125LOW ALLOY STEEL
ELECTRODESSTAINLESS STEEL ELECTRODESHARD FACING ELECTRODESNON
FERROUS ELECTRODESCAST IRON & CUTTING ELECTRODESFLUX CORED WIRE
& CO2 WELDING WIRESAbbreviations and SymbolsTypes of Current
CodesAbbreviationsNotes:Direct current electrode attached to
positive poleDirect current electrode attached to negative
poleDirect current electrode attached to either positive or
negative poleAlternating currentPreferably direct current attached
to positive pole, but also alternating current may be
usedPreferably direct current attached to negative pole, but also
alternating current may be usedPreferably direct current attached
to either positive or negative pole, but also alternating current
maybe usedtensile strengthyield strengthelongation after rupture
(1=5d)impact valueas- weldedstress relieved(brackets) - Minimum
open circuit voltage when welding using an alternating currentRm
[MPa]Rp 0.2 [MPa]A5 [%]Impact (ISO) [J]US=-~=+~=+
_=+ ~
_=-~=+All values listed in this guide are indicative only.All
information contained within this guide is based on careful
evaluation.Regardless, the manufacturer does not assume any
liability for their correctness.Further, the manufacturer reserves
the right to change the specifications listed in this guide at any
time andwithout prior notice.Electrode Brand Name - International
StandardsZ-610Z-611Z-6Z-9Z-11Z-14Z-15Z-15 (14)A5. 1: E 6010A5. 1: E
6011A5. 1: E 6013A5. 1: E 6013A5. 1: E 6013A5. 1: E 6013A5. 1: E
6013A5. 1: E 60131913: E 43 43 C41913: E 43 43 C41913: E 43 22
RR61913: E 42 22 R(C) 31913: E 43 22 RR61913: E 51 22 RR61913: E 43
22 RR61913: E 51 22 RR61913: E 51 22 R(C)31913: E 51 22 RR(C)
61913: E 51 22 RR11 1401913: E 51 22 RR11 1601913: E 51 22 RR11
1801913: E 51 32 RR11 1601913: E 51 22 RR11 1801913: E 51 44 B9
H101913: E 51 44 B10 H101913: E 51 44 B10 H101913: E 51 44 B10
H51913: E 51 44 B10 H58529: EY46 66 Mn BH51913: E 51 43 B(R)12 160
H51913: E 51 44 B(R)9 H10-8575: E Mo B 26-8575: E CrMo1 B 268575: E
CrMo1 B 268529: E SY 42 77 2Ni B H58529: E Y 46 76 1Ni B H51913: E
51 33 B10 H58529: E Y 50 76 Mn1Ni B H58529: E SY 50 66 Mn B H58529:
E Y 50 32 1NiCu B H58575: E CrMo2 B 268575: E CrMo2 B 268529: E SY
55 65 MnMo B H58529: E SY 50 0 1NiMo B H58529: E Y 55 87 2NiMo B
H58529: E Y 62 87 Mn2NiMo B H58529: E Y 69 76 Mn2NiCrMo B H58529: E
Y 79 76 Mn2Ni1.5CrMo B H58575: E CrMo5 B 268575: E CrMo9 B 26639: E
43 43 C 19639: E 43 43 C 16639: E 43 22 RR 22639: E 43 22 R 12639:
E 43 22 RR 22639: E 51 22 RR 32639: E 43 22 RR 32639: E 51 22 RR
32639: E 51 22 R 12639: E 51 22 RR 12639: E 51 22 RR 140 35639: E
51 22 RR 160 32639: E 51 22 RR 190 35639: E 51 22 RR 160 32639: E
51 22 RR 190 35639: E 51 44 B 16 HH639: E 51 44 B 26 HH639: E 51 44
B 26 HH639: E 51 44 B 26 H639: E 51 44 B 26 H639: E 51 55 B 120 16
H639: E 51 43 B 160 36 H639: E 51 44 B 110 54 HH2493: E Mo C2493: E
Mo B639: E 51 32 C 102493: E 1CrMo B2493: E 1CrMo L B2493: E 2Ni B
H2493: E 1Ni B H639: E 51 33 B 120 26 H639: E 51 54 B 120 26 H639:
E 51 55 B 120 16 H-2493: E 2CrMo B2493: E 2CrMo L B2493: E MnMo B
H-2493: E MnNi B H2493: E NiMo B H2493: E 2NiMo B H2493: E 2NiCrMo
B H2493: E 5CrMo B2493: E 9CrMo B499: E 42 2 C 41499: E 42 2 C
31499: E 42 0 RR 12499: E 42 0 R 12499: E 42 0 RR 12 499: E 42 0 RR
12499: E 38 0 RR 12499: E 42 0 RR
12123456789101112131415161718192021222324252627282930313233343536373839404142434445464748499:
E 42 0 RC 12499: E 46 0 RR 32499: E 42 0 RR 53499: E 46 0 RR 73499:
E 46 0 RR 73499: E 46 0 RR 73499: E 46 0 RR 732560-A: E-5000Z1499:
E 46 3 B 11 H10499: E 42 3 B 12 H10499: E 42 3 B 32 H10499: E 46 3
B 32 H5499: E 42 3 B 32 H15499: E 46 5 B 32 H5499: E 42 3 RB 53
H5499: E 42 3 B 35 H10499: E 42 0 Mo C 411599: E Mo B 32 mod499: E
46 2 1NiMo C 411599: E CrMo1 B 32mod1599: E CrMo1 L B 32 mod499: E
46 6 2Ni B 42 H5-499: E 50 2 B 32 H5503Mo: B 42 H5499: E 50 6 Mn1Ni
B 32 H5499: E 50 5 B 32 H5499: E 50 2 B 32 H51599: E CrMo2 B
32mod1599: E CrMo2 L B 32mod499: E 50 5 MnMo B 32 H5499: E 50 A 32
H5499: E 50 A 32 H5499: E 50 5 Z B 32 H5499: E 50 5 Z B 32 H5499: E
50 5 Z B 32 H5499: E 50 5 Z B 32 H51599: E CrMo5 B 32mod1599: E
CrMo9 B 32modA5. 1: E 6013A5. 1: E 7014A5. 1: E 7024A5. 1: E
7024A5. 1: E 7024A5. 1: E 7024-1A5. 1: E 70245.5 E-9010-GA5. 1: E
7016A5. 1: E 7016A5. 1: E 7018A5. 1: E 7018A5. 1: E 7018A5. 1: E
7018-1A5. 1: E 7028A5. 1: E 7048A5. 5: E 7010-A1A5. 5: E 7018-1A5.
5: E 8010-GA5. 5: E 8010-B2A5. 5: E 8010-B2LA5. 5: E 8010-C1A5. 5:
E 8010-C3A5. 5: E 8010-GA5.5 E-8018-GA5. 5: E 8018-GA5. 5: E
8018-GA5. 5: E 8018-WA5. 5: E 9018-B3A5. 5: E 9018-B3LA5. 5: E
9018-D1A5. 5: E 9018-GA5.5 E-9018-GA5. 5: E 9018-MA5. 5: E
10018-MA5. 5: E 11018-MA5. 5: E 12018-MA5. 4: E 502-15A5. 4: E
505-15A5.5
E-9015-B9Z-26Z-16Z-17Z-18Z-19Z-20Z-21Z-910Z-7DIALOGUEZ-2Z-4Z-4
ACZ-55Z-42Z-47Z-710Z-23Z- CELLUPIPEZ-31
SZ-31Z-32Z-34Z-3Z-3PZ-8Z-33Z-3 WZ-41 SZ-41Z-46Z-40
SZ-X70Z-48Z-50Z-52Z-53 MZ-502Z-505Z-91MILD & MEDIUM CARBON
STEEL ELECTRODESLOW ALLOY STEEL
ELECTRODESELECTRODEELECTRODEAWS/ASME SFAAWS/ASME
SFADINDINBSBSENENZ-307 BZ-307 RZ-307 HRZ-308 BZ-308 LZ-308 LVDZ-308
LHRZ-308 HZ-309 BZ-309 SZ-309 CbZ-309 MoZ-310Z-312Z-312 SZ-316
BZ-316 LZ-316 LVDZ-316 LHRZ-316 HSZ-317Z-318 BZ-318Z-320Z-347
BZ-347Z-ARM BSZ-Ni ViZ-2209 BZ-2209 RZ-2594 RA5. 4: E 307-15A5. 4:
E 307-16A5. 4: E 307-16A5. 4: E 308L-15A5. 4: E 308L-16A5. 4: E
308L-17A5. 4: E 308L-16A5. 4: E 308-16A5. 4: E 309L-15A5. 4: E
309L-16A5. 4: E 309Cb-16A5. 4: E 309MoL-16A5. 4: E 310-16A5. 4: E
312-16A5. 4: E 312-16A5. 4: E 316L-15A5. 4: E 316L-16A5. 4: E
316L-17A5. 4: E 316L-16A5. 4: E 316-16A5. 4: E 317L-16A5. 4: E
318-15A5. 4: E 318-16A5. 4: E 385-16modA5. 4: E 347-15A5. 4: E
347-16A5. 4: E 308Mo-15 mod A5. 4: E 308Mo-16 modA5. 4: E
2209-15A5. 4: E 2209-16A5. 4: E 2594-16----------A5. 13: EFe5-B mod
A5. 13: EFeMn-AA5. 13: EFeMn-A modA5. 13: ECoCr-AA5. 13:
ECoCr-B----8556: E 19 9 L B 20+8556: E 19 9 L R 238556: E 19 9 L R
138556: E 19 9 L R 36 1508556: E 19 9 R 238556: E 23 12 L B
20+8556: E 23 12 L R 238556: E 23 12 Nb R 238556: E 23 12 3 R
238556: E 25 20 R 268556: E 29 9 R 238556: E 29 9 R 238556: E 19
123 L B 20+8556: E 19 123 L R 238556: E 19 12 3 L R 138556: E 19 12
3 L R 26 1508556: E 19 12 3 MPR 23 170-8556: E 19 12 3 Nb B
20+8556: E 19 12 3 Nb R 238556: E 20 25 5 L Cu R 38556: E 19 9 Nb B
20+8556: E 19 9 Nb R 23--8556: E 22 9 3 L B 20+8556: E 22 9 3 L R
23---2926: E 19 9 L B2926: E 19 9 L R2926: E 19 9 L R2926: E 19 9 L
R2926: E 19 9 R2926: E 23 12 L B2926: E 23 12 L R2926: E 23 12 Nb
R2926: E 23 12 2 R2926: E 25 20 R2926: E 29 9 R2926: E 29 9 R2926:
E 19 12 3 L B2926: E 19 12 3 L R2926: E 19 12 3 L R2926: E 19 12 3
L R2926: E 19 12 3 RMP2926: E 19 13 4 L R2926: E 19 12 3 Nb B2926:
E 19 12 3 Nb R-2926: E 19 9 Nb B2926: E 19 9 Nb R2926: E 19 9 3
B2926: E 19 9 3 R-----1600: E 19 9 L B 221600: E 19 9 L R 121600: E
19 9 L R 111600: E 19 9 L R 53 mod1600: E 19 9 R 121600: E 23 12 L
B 421600: E 23 12 L R 121600: E 23 12 Nb R 121600: E 23 12 2 L R
121600: E 25 20 R 12 mod1600: E 29 9 R 121600: E 29 9 R 121600: E
19 12 3 L B 221600: E 19 12 3 L R 121600: E 19 12 3 L R 111600: E
19 12 3 L R 53 mod1600: E 19 12 2 R 721600: E 19 13 4 L R 12
mod1600: E 19 12 3 Nb B 221600: E 19 12 3 Nb R 121600: E 20 25 5 Cu
L R 121600: E 19 9 Nb B 221600: E 19 9 Nb R 12--1600: E 22 9 3 L B
221600: E 22 9 3 L R 121600: E 2594 NLR Z38555: E 1 UM 3008555: E 1
UM 4008555: E 6 UM 55 R8555: E 6 UM 558555: E 6 UM 608555: E 6 UM
608555: E 10 UM 60 Z8555: E 10 UM 60 GR8555: E 10 UM 65 GR8555: E
10 UM 65 GR8555: E 4 UM 60 S8555: E 7 UM 250 KP8555: E 7 UM 250
KP-8555: E 20 UM 45 CTZ8555: E 20 UM 50
CTZ--------------------------------4950515253545556575859606162636465666768697071727374757677787980818283848586878889909192939495Z-104Z-105Z-110Z-111Z-113Z-114Z-120Z-120
BZ-123Z-125Z-130Z-151Z-151 NCZ-152Z-STEL 6Z-STEL 12STAINLESS STEEL
ELECTRODESELECTRODE AWS/ASME SFAHARD FACING ELECTRODESELECTRODE
AWS/ASME SFADIN BS EN Pg.DIN BS EN Pg.Z-Ni 1Z-Ni BZ-Ni A2Z-Ni
182Z-Ni 182R1Z-Ni 112Z-Ni 112RZ-NiCroMo3Z-NiCroMo4Z-Ni CZ-Ni
190Z-Ni 187Z-BRONZE AZ-BRONZEZ-BRONZE MZ-SuperNiZ-Ni 99Z-Ni 99
NCZ-Ni 55Z-GSMZ-GMZ-71Z-72Z-OXYCUTZ-71T1Z-71T5Z-R2Z-R3Z-R6Z-RMoA5.
11: ENi-1A5. 11: ENiMo-1A5. 11: ENiCrFe-2A5. 11: ENiCrFe-3A5. 11:
ENiCrFe-3A5. 11: ENiCrMo-3A5. 11: ENiCrMo-3A5. 11: ENiCrMo-3A5. 11:
ENiCrMo-4A5. 11: ENiCrMo-5A5. 11: ENiCu-7A5. 6: ECuNiA5. 6:
ECuSn-AA5. 6: ECuSn-CA5. 6: ECuSn-CA5. 15: ENi-CIA5. 15: ENi-CIA5.
15: ENi-CIA5. 15: ENiFe-CI-A5. 15: ENiCu-B---A5. 20: E71T-1A5. 20:
E71T-5A5. 18: ER-70S-2A5. 18: ER-70S-3A5. 18: ER-70S-6A5. 28:
ER-80S-D28573: E Ni-BG-218573: E Ni-BG-238573: E Ni-BG-238573: E
NiFe-1-BG-238573: E FeC-G-BG-268573: E NiCu-BG-23----8559: SG
18559: SG 28559: SG Mo--2901: A 182901: A 30/A 31440: G2 Ti-440: G3
Si 1 mod440: G4 Mo1736: EL-NiTi 31736: EL-NiMo 291736: EL-NiCr 15
FeNb1736: EL-NiCr 15 FeMn1736: EL-NiCr 15 FeMn1736: EL-NiCr 20 Mo 9
Nb1736: EL-NiCr 20 Mo 9 Nb1736: EL-NiCr 20 Mo 9 Nb1736: EL-NiMo15
Cr 15 W1736: EL-NiMo15 Cr 15 W mod1736: EL-NiCu 30 Mn1733: EL-CuNi
30-1733: EL-CuSn 71733: EL-CuSn
7---------------------------------------------96979899100101102103104105106107108109110111112113114115116117118119120121122123124125NON
FERROUS ELECTRODESELECTRODE AWS/ASME SFA DIN BS EN Pg.CAST IRON
& CUTTING ELECTRODESELECTRODE AWS/ASME SFA DIN BS EN Pg.FLUX
CORED WIREELECTRODE AWS/ASME SFA DIN BS EN Pg.SEMI AUTOMATIC SOLD
WIREELECTRODE AWS/ASME SFA DIN BS EN Pg.---------1Mild & Medium
Carbon Steel ElectrodesZ-610Cellulose electrode for pipe and
general weldingDeep penetration and good X-ray qualitySuitable for
welding pipes, pressure vessels, storagetanks, shipsDescription and
Applications:Welding positionASME:1G2F2G3G3G4G5GI
SO6947PAPBPCPFPGPEPF/PGCMnSi0.100.500.20Unalloyed construction
steelsBoiler and pressure vessel steelsPipe steelsDIN 17 100DIN 17
155DIN 17 172DIN 17 175DIN 1629API 5LXDIN 17 102St 33 to St 52.3HI,
HIIStE 210.7 to StE 415.7St 35.8 to ST 45.8St 35 to St 52.4X42 to
X63StE 255 to StE 355A,B,DFine grained steelsShipbuilding
steelsRe-drying not
necessary.3/321/85/323/161/42.53.254.05.06.0141414141435035035035035060-9080-125120-180160-230220-2801.82.94.36.69.55.05.05.05.05.015.015.015.015.015.0Rp
0.2 [MPa]Rm [MPa]A5 [%]Impact [ISO-V]Heat Treatment4305502580 J@-
20o-CU45 J@- 30o-CCurrentTypical all weld metal composition
[wt%]Typical all weld metal mechanical propertiesMaterials to be
weldedWelding parameters and packaging dataAWS/ASME SFA A5.1 : E
6010DIN1913 :E 43 43 C4BS639:E 43 43 C 19EN499:E 42 2 X
41Specifications:= +Diain mmLengthin mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Mild & Medium Carbon Steel
ElectrodesZ-611Description and Application:Welding positionTypical
all weld metal composition [wt%]Typical all weld metal mechanical
propertiesMaterials to be weldedCurrentCellulose electrode for pipe
and general weldingDeep penetration and good X-ray qualitySuitable
for welding pipes, pressure vessels, storagetanks, ships on both AC
and DCASME:ISO
69471GPAC0.12Mn0.50Si0.202GPB2GPC3GPF3GPG4GPE5GPF/PGAWS/ASME SFA
A5.1 : E 6011DIN1913 :E 43 43 C4BS639:E 43 43 C 16EN499:E 42 2 C
31Rp 0.2[MPa]430Unalloyed construction steelsBoiler and pressure
vessel steelsPipe steelsFine grained steelsShipbuilding steelsRm
[MPa]550Heat TreatmentU2A5 [%]25Impact [ISO-V]80 J @-20oC45 J
@-30oCSpecifcations:=+~ (Uo : 70 v)DIN 17 100DIN 17 155DIN 17
172DIN 17 175DIN 1629API 5LXDIN 17 102St 33 to St 52.3HI, HIIStE
210.7 to StE 415.7St 35.8 to ST 45.8St 35 to St 52.4X42 to X63StE
255 to StE 355A,B,DRe-drying not
necessary.3/321/85/323/161/42.53.254.05.06.0141414141435035035035035060-9080-125120-180160-230220-2801.82.94.36.69.55.05.05.05.05.015.015.015.015.015.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]3Mild & Medium Carbon Steel
ElectrodesZ-6Rutile coated electrode for welding on
uncleanedsurfaces like paint, oil or galvanized steelUsable for
pipes, storage tanks and machine partsDescription and
Applications:Welding positionASME:I
SO69471GPA2FPB2GPC3GPF4GPEC0.07Mn0.50Si0.25DIN 17 100DIN 17 172DIN
1629API 5LXDIN 1681St 33 to St 37.2 to St 44.3StE 210.7 to StE
360.7St 35 to St 52.4X42, X46GS 38A,B,C,DCast steelsShipbuilding
steelsRe-drying not
necessary.3/321/85/323/162.53.254.05.01414141435035035035070-95100-150140-200180-2701.93.04.57.05.55.55.55.516.516.516.516.5Typical
all weld metal composition [wt%]Rp 0.2 [MPa]450Rm [MPa]550A5
[%]23Impact [ISO-V]70 J @ 0oCHeat TreatmentUTypical all weld metal
mechanical propertiesUnalloyed construction steelsPipe
steelsMaterials to be weldedWelding parameters and packaging
dataAWS/ASME SFA A5.1 : E 6013DIN1913 :E 43 22 RR6BS639:E 43 22 RR
22EN499:E 42 0 RR 12Specifications:Diain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :50 V)4Mild
& Medium Carbon Steel ElectrodesZ-9Rutile coated universal
electrode for welding generalstructural steelsSuitable for badly
prepared plates of differentthicknesses and bad surface
conditionsEasy slag release and arc striking Description and
Applications:Welding positionASME:I
SO69471GPA2FPB2GPC3GPF4GPEC0.08Mn0.50Si0.30DIN 17 100DIN 17 172DIN
1629API 5LXDIN 1681St 33 to St 37.2 to St 44.3StE 210.7 to StE
360.7St 35 to St 52.4X42, X46GS 38A,B,C,DCast steelsShipbuilding
steelsRe-drying not
necessary.5/643/321/85/323/162.02.53.254.05.01214141414/18300350350350350/45055-8570-100100-150140-200180-2301.11.93.04.57.0/9.04.05.55.55.55.5/7.012.016.516.516.516.5/21Typical
all weld metal composition [wt%]Rp 0.2 [MPa]400Rm [MPa]520A5
[%]24Impact [ISO-V]70 J @ 0oCHeat TreatmentUTypical all weld metal
mechanical propertiesUnalloyed construction steelsPipe
steelsMaterials to be weldedWelding parameters and packaging
dataAWS/ASME SFA A5.1 : E 6013DIN1913 :E 43 22 R(C)3BS639:E 43 22
R12EN499:E 42 0 R 12Specifications:Diain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :50 V)5Mild
& Medium Carbon Steel ElectrodesZ-11Thickly coated all purpose
rutile electrodeSuitable for badly prepared surfaces such asrust
and paint and different plate thicknessVery easy slag release and
arc strikingDescription and Applications:Welding positionASME:I
SO69471GPA2FPB2GPC3GPF4GPEC0.08Mn0.50Si0.25DIN 17 100DIN 17 172DIN
17 175DIN 1629DIN 1681St 33, St 37.2 to St 52.3StE 210.7 to StE
360.7St 35.8, St 45.8St 35 to St 52.4GS 38Cast steelsRe-drying not
necessary.5/643/321/85/323/162.02.53.254.05.0121414/1814/1814/18300350350/450350/450350/45050-7060-100100-150140-200180-2601.12.03.3/4.24.9/6.27.7/9.94.05.05.0/6.05.0/6.05.0/6.012.015.015.0/18.015.0/18.015.0/18.0Typical
all weld metal composition [wt%]Rp 0.2 [MPa]440Rm [MPa]520A5
[%]26Impact [ISO-V]70 J @ 0oCHeat TreatmentUTypical all weld metal
mechanical propertiesUnalloyed construction steelsPipe
steelsMaterials to be weldedWelding parameters and packaging
dataAWS/ASME SFA A5.1 : E 6013DIN1913 :E 43 22 RR6BS639:E 43 22 RR
22EN499:E 42 0 RR 12Specifications:Diain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :50 V)6Mild
& Medium Carbon Steel ElectrodesZ-14Thickly coated electrode
for general purposesExceptionally smooth welding seams, low
spatterloss and self detaching slagDescription and
Applications:Welding positionASME:I
SO69471GPA2FPB2GPC3GPF4GPEC0.09Mn0.55Si0.30DIN 17 100DIN 1681DIN 17
172DIN 17 175DIN 1629St 33, St 37.2 to St 52.3GS 38, GS 45StE 210.7
to StE 360.7St 35.8 to St 45.8St 35 to St 52.4A,B,C,D,EShipbuilding
steelsRe-drying not
necessary.3/321/85/323/162.53.254.05.014181818350350/450350/45045070-110100-160160-200200-2702.14.87.210.35.05.0/6.05.0/6.06.015.015.0/18.015.0/18.018.0Typical
all weld metal composition [wt%]Rp 0.2 [MPa]420Rm [MPa]520A5
[%]24Impact [ISO-V]70 J @ 0oCHeat TreatmentUTypical all weld metal
mechanical propertiesUnalloyed construction steelsCast steelsPipe
steelsMaterials to be weldedWelding parameters and packaging
dataAWS/ASME SFA A5.1 : E 6013DIN1913 :E 51 22 RR6BS639:E 51 22 RR
32EN499:E 42 0 RR 12Specifications:Diain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :50 V)7Mild
& Medium Carbon Steel ElectrodesZ-15Heavy coated rutile
electrode for general purposesVery even weld in flat and fillet
positionsDescription and Applications:Welding positionASME:I
SO69471GPA2FPB2GPCC0.09Mn0.60Si0.50DIN 17 100DIN 1681DIN 17 172DIN
17 175DIN 1629St 33, St 37.2 to St 52.3GS 38, GS 45StE 210.7 to StE
360.7St 35.8 to St 45.8St 35 to St 52.4A,B,C,D,EShipbuilding
steelsRe-drying not
necessary.3/321/85/323/162.53.254.05.01418181835045045045070-110100-160160-200200-2702.14.87.210.35.06.06.06.015.018.018.018.0Typical
all weld metal composition [wt%]Rp 0.2 [MPa]400Rm [MPa]480A5
[%]24Impact [ISO-V]60 J @ 20oCHeat TreatmentUTypical all weld metal
mechanical propertiesUnalloyed construction steelsCast steelsPipe
steelsMaterials to be weldedWelding parameters and packaging
dataAWS/ASME SFA A5.1 : E 6013DIN1913 :E 43 22 RR6BS639:E 43 22 RR
32EN499:E 38 0 RR 12Specifications:Diain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :50 V)8Mild
& Medium Carbon Steel ElectrodesZ-15 (14)Rutile coated
electrode for general purposesExceptionally smooth welding
seamsSuitable for welding thin metal platesDescription and
Applications:Welding positionASME:I
SO69471GPA2FPB2GPC3GPF4GPEC0.07Mn0.55Si0.50DIN 17 100DIN 1681DIN 17
172DIN 17 175DIN 1629St 33, St 37.2 to St 52.3GS 38, GS 45StE 210.7
to StE 360.7St 35.8 to St 45.8St 35 to St 52.4A,B,C,D,E
Shipbuilding steelsRe-drying not
necessary.3/321/85/323/162.53.254.05.014181818350350/450350/45045070-110100-160160-200200-2702.14.87.210.305.05.0/6.05.0/6.06.015.015.0/18.015.0/18.018.0Typical
all weld metal composition [wt%]Rp 0.2 [MPa]420Rm [MPa]520A5
[%]24Impact [ISO-V]50 J @ 0oCHeat TreatmentUTypical all weld metal
mechanical propertiesUnalloyed construction steelsCast steelsPipe
steelsMaterials to be weldedWelding parameters and packaging
dataAWS/ASME SFA A5.1 : E 6013DIN1913 :E 51 22 RR6BS639:E 51 22 RR
32EN499:E 42 0 RR 12Specifications:Diain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :50 V)9Mild
& Medium Carbon Steel ElectrodesZ-26Welding positionASME:I
SO69471GPA2FPB2GPC3GPF4GPEC0.07Mn0.55Si0.25DIN 17 100DIN 17 155DIN
17 172DIN 17 175DIN 1629DIN 1681St 33, St 37.2 to St 52.3HI, HII,
17Mn4, 19Mn5StE 210.7 to StE 360.7St 35.8,St 45.8St 35 to St 52.4GS
38,GS 45Cast steelsRe-drying not
necessary.5/643/321/85/323/161/42.02.53.254.05.06.012141414/181414300350350350/450350/45045055-7070-100100-150140-200160-230240-3401.11.93.04.5/5.89.013.04.0/2.05.55.55.5/7.05.5/7.07.012.016.516.516.5/21.016.5/21.021.0Typical
all weld metal composition [wt%]Rp 0.2 [MPa]470Rm [MPa]550A5
[%]25Impact [ISO-V]60 J @ 0oCHeat TreatmentUTypical all weld metal
mechanical propertiesUnalloyed construction steelsBoiler and
pressure vessel steelsPipe steelsMaterials to be weldedWelding
parameters and packaging dataAWS/ASME SFA A5.1 : E 6013DIN1913 :E
51 22 R(c)3BS639:E 51 22 R12EN499:E 42 0 RC 12Specifications:Diain
mmLengthin mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :50 V)Rutile
Coated all position electrode with a widerange of applications in
shipbuilding and structuralworkSuitable for badly prepared plates
of differentthicknessesDescription and Applications:10Mild &
Medium Carbon Steel ElectrodesZ-16Welding positionASME:I
SO69471GPA2FPB2GPC3GPF4GPEC0.08Mn0.60Si0.25DIN 17 100DIN 17 155DIN
17 172DIN 17 175DIN 1629DIN 1681St 33, St 37.2 to St 52.3HI, HII,
17Mn4, 19Mn5StE 210.7 to StE 360.7St 35.8,St 45.8St 35 to St 52.4GS
38,GS 45Cast steelsRe-drying not
necessary.5/643/321/85/323/162.02.53.254.05.0121414141430035035035035050-7060-100110-150130-170190-2301.12.03.64.97.54.05.05.05.05.012.015.015.015.015.0Typical
all weld metal composition [wt%]Rp 0.2 [MPa]460Rm [MPa]540A5
[%]25Impact [ISO-V]70 J @ 0oCHeat TreatmentUTypical all weld metal
mechanical propertiesUnalloyed construction steelsBoiler and
pressure vessel steelsPipe steelsMaterials to be weldedWelding
parameters and packaging dataAWS/ASME SFA A5.1 : E 7014DIN1913 :E
51 22 RR(C)6BS639:E 51 22 RR12EN499:E 46 0 RR
32Specifications:Diain mmLengthin mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Thick rutile electrode for fast
deposition rateFocused, stable and penetrating arcSelf detaching
slagSuitable for badly prepared plates of
differentthicknessesDescription and Applications:Current= + ~ (Uo
:50 V)11Mild & Medium Carbon Steel ElectrodesZ-17Welding
positionASME:I SO69471GPA2FPB2GPCC0.08Mn0.50Si0.30Re-drying: not
necessary.3/321/85/323/162.53.254.05.01418181835045045045060-110120-150150-190200-2502.45.57.811.55.06.06.06.015.018.018.018.0Typical
all weld metal composition [wt%]Welding parameters and packaging
dataAWS/ASME SFA A5.1 : E 7024DIN1913 :E 51 22 RR11 140BS639:E 51
22 RR140 35EN499:E 42 0 RR 53Specifications:Diain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :50 V)Rutile
coated electrode for welding engineeringstructures140% metal
recoverySmooth weld appearance and self detaching slagDescription
and Applications:Rp 0.2 [MPa]430Rm [MPa]510A5 [%]25Impact [ISO-V]60
J @ 0oCHeat TreatmentUTypical all weld metal mechanical
propertiesDIN 17 100DIN 17 155DIN 17 172DIN 1629DIN 1681St 33, St
37.2 to St 52.3HI, HII, 17Mn4StE 210.7 to StE 360.7St 35 to St
52.4GS 38A,B,C,DCast steelsShipbuilding steelsUnalloyed
construction steelsBoilerPlatePipe steelsMaterials to be
welded12Mild & Medium Carbon Steel ElectrodesZ-18Welding
positionASME:I SO69471GPA2FPBC0.07Mn0.70Si0.25DIN 17 100DIN 17
155DIN 1681St 33, St 37.2 to St 52.3HI, HII, 17Mn4GS
38A,B,C,DRe-drying: not
necessary3/321/85/323/161/42.53.254.05.06.0141818181835045045045045085-125130-175150-240210-290290-4203.06.510.015.019.54.56.06.06.06.013.518.018.018.018.0Typical
all weld metal composition [wt%]Rp 0.2 [MPa]480Rm [MPa]550A5
[%]26Impact [ISO-V]60 J @ 0oCHeat TreatmentUTypical all weld metal
mechanical propertiesUnalloyed construction steelsBoiler and
pressure vessel steelsCast steelShipbuilding steelMaterials to be
weldedWelding parameters and packaging dataAWS/ASME SFA A5.1 : E
7024DIN1913 :E 51 22 RR11 160BS639:E 51 22 RR160 32EN499:E 46 0 RR
73Specifications:Diain mmLengthin mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :50 V)Rutile
electrode for fillet welds and horizontalV-welds165% metal recovery
with high speed weldingSmooth weld appearance and self detaching
slagDescription and Applications:13Mild & Medium Carbon Steel
ElectrodesZ-19Welding positionASME:I
SO69471GPA2FPBC0.07Mn0.70Si0.25Re-drying not
necessary.1/85/323/161/43.254.05.06.018181818450450450450130-170150-230200-350280-4806.911.215.722.16.06.06.06.018.018.018.018.0Typical
all weld metal composition [wt%]Rp 0.2 [MPa]460Rm [MPa]550A5
[%]27Impact [ISO-V]60 J @ 0oCHeat TreatmentUTypical all weld metal
mechanical propertiesWelding parameters and packaging dataDiain
mmLengthin mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :50 V)AWS/ASME
SFA A5.1 : E 7024DIN1913 :E 51 22 RR11180BS639:E 51 22 RR
19035EN499:E 46 0 RR 73Specifications:Rutile electrode for fillet
welds and horizontalV-welds185% metal recovery with high speed
weldingSmooth weld appearance and self detaching slagDescription
and Applications:DIN 17 100DIN 17 155DIN 1681St 33, St 37.2 to St
52.3HI, HII, 17Mn4, 19Mn5GS 38A,B,C,DCast steelsUnalloyed
construction steelsBoiler and pressure vessel steelsCast
steelsShipbuilding steelsMaterials to be welded14Mild & Medium
Carbon Steel ElectrodesZ-20Welding positionASME:I
SO69471GPA2FPBRe-drying not
necessary.1/85/323/161/43.254.05.06.018181818450450450450130-170150-230200-350280-4807.210.616.023.86.06.06.06.018.018.018.018.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :50 V)AWS/ASME
SFA A5.1 : E 7024-1DIN1913 :E 51 32 RR11160BS639:E 51 32 RR
16032EN499:E 46 0 RR 73High speed, high deposit (160% metal
recovery),rutile electrodeIdeal for very fast fillet welding and
for fillinghorizontal groovesFully controlled molten pool, spatter
free and selfdetaching slagSuitable for welding on moderate and
thick platesfor buildings, bridges, shipbuilding, etcDescription
and Applications:Specifications:C0.09Mn0.85Si0.45Typical all weld
metal composition [wt%]Rp 0.2 [MPa]460Rm [MPa]550A5 [%]25Impact
[ISO-V]65 J @ 0oC50 J @ -20oCHeat TreatmentUTypical all weld metal
mechanical propertiesDIN 17 100DIN 17 155DIN 1681St 33, St 37.2 to
St 52.3HI, HII, 17Mn4, 19Mn5GS 38A,B,C,DUnalloyed construction
steelsBoiler and pressure vessel steelsCast steelsShipbuilding
steelsMaterials to be welded15Mild & Medium Carbon Steel
ElectrodesZ-21Welding positionASME:I SO69471GPA2FPBRe-drying not
necessary.1/85/323/161/43.254.05.06.018181818450450450450130-170150-230200-350280-4007.210.616.024.36.06.06.06.018.018.018.018.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :50 V)AWS/ASME
SFA A5.1 : E 7024DIN1913 :E 51 22 RR11180BS639:E 51 22 RR
19035EN499:E 46 0 RR 73Rutile electrode for fillet and horizontal
V-welds190% metal recovery with high speed weldingSmooth weld
appearance and self detaching slagDescription and
Applications:Specifications:C0.07Mn0.70Si0.25Typical all weld metal
composition [wt%]Rp 0.2 [MPa]460Rm [MPa]550A5 [%]27Impact [ISO-V]70
J @ 0oCHeat TreatmentUTypical all weld metal mechanical
propertiesDIN 17 100DIN 17 155DIN 1681St 33, St 37.2 to St 52.3HI,
HII, 17Mn4, 19Mn4GS 38A,B,C,DUnalloyed construction steelsBoiler
and pressure vessel steelsCast steelsShipbuilding steelsMaterials
to be welded16Mild & Medium Carbon Steel
ElectrodesZ-910C0.11Mn1.1Si0.55Ni0.62Mo0.23Typical all weld metal
composition [wt%]Rp 0.2 [MPa]690Rm [MPa]616A5 [%]21Impact [ISO-V]79
J @ 0oCTypical all weld metal mechanical propertiesAPI SPEC5L: X65,
X70Materials to be weldedAWS/ASME SFA 5.5 : E 9010-GEN ISO 2560-A
E50021Specifications:Cellulose electrode designed for welding in
all positionincluding vertical down for high diameter
pipelines.Especially recommended for hot passes, filler and
coverlayers.Description and Applications:Re-drying not
necessary.3/321/85/322.53.254.014141435035035080-125110-180140-230555151515Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightpacket[kg]Weightcarton[kg]Welding
position17Low Alloy Steel ElectrodesZ-7Welding positionAWS/ASME SFA
A5.1 : E 7016DIN1913 :E 51 44 B9 H10BS639:E 51 44 B16 HEN499:E 46 3
B 11 H10Specifications:Basic coated electrode for high quality
joiningof general construction steelsVery good X-ray
propertiesSuitable for rool pass welding in narrow jointsGood
impact toughness at low temperaturesDescription and
Applications:ASME:I
SO69471GPA2FPB2GPC3GPF3GPG4GPEC0.07Mn1.00Si0.60Re-drying:
2h/300oC3/321/85/323/162.53.254.05.01414141835035035045070-80100-120140-160190-2101.93.14.79.25.05.05.06.015.015.015.018.0Typical
all weld metal composition [wt%]Rp 0.2 [MPa]490Rm [MPa]570A5
[%]26Impact [ISO-V]120 J @ 0oC100 J @ -20oC80 J @ -30oCHeat
TreatmentUTypical all weld metal mechanical propertiesDIN 17 100DIN
17 155DIN 17 172API 5LXDIN 1626-1630DIN 1681St 33, St 37.2 to St
52.3HI, HII, 17Mn4, 19Mn5StE 210.7, StE 240.7, StE 290.7, StE
320.7, StE 360.7X42, X46, X52, X60St 37.0/4, St 44.0/4, St 52.0/4GS
38, GS 45, GS 52A,B,C,D,EAH, DH, EHCast steelsShipbuilding
steelsGeneral structure steelsBoiler and pressure vessel steelsPipe
steelsMaterials to be weldedWelding parameters and packaging
dataDiain mmLengthin mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :70 V)18Low
Alloy Steel ElectrodesDIALOGUEWelding positionASME:I
SO69471GPA2FPB2GPC3GPF4GPEC0.06Mn1.10Si0.65Re-drying:
300oC/2h3/321/85/323/162.53.254.05.01414/181818350350/450350/45045060-9095-150140-190190-2502.03.4/4.36.7104.54.55/6613.513.515/1818Typical
all weld metal composition [wt%]Rp 0.2 [MPa]420Rm [MPa]530A5
[%]30Impact [ISO-V]110 J @ -20oC100 J @ -30oCHeat TreatmentUTypical
all weld metal mechanical propertiesWelding parameters and
packaging dataDiain mmLengthin mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :70 V)AWS/ASME
SFA A5.1 : E 7016DIN1913 :E 51 44 B10 H10BS639:E 51 44 B26
HHEN499:E 42 3 B 12 H10Specifications:Double coated basic
electrodeSuitable for repair and maintenance workExcellent for root
pass and all positional weldingHigh impact toughness at low
temperaturesDescription and Applications:DIN 17 100DIN 17 155DIN 17
172API 5LXDIN 1626-1630DIN 1681DIN 17 175DIN 17 102St 33, St 37.2
to St 52.3HI, HII, 17Mn4, 19Mn5StE 210.7, StE 240.7, StE 290.7, StE
320.7, StE 360.7X42, X46, X52, X60St 37.0/4, St 44.0/4, St 52.0/4GS
38, GS 45, GS 52St 35.8, St 45.8StE 255 to StE 420A,B,C,D,EAH, DH,
EHCast steelsElevated temperature steelsFine grained
steelShipbuilding steelsGeneral structure steelsBoiler and pressure
vessel steelsPipe steelsMaterials to be welded19Low Alloy Steel
ElectrodesZ-2Welding positionASME:I
SO69471GPA2FPB2GPC3GPF4GPEC0.06Mn1.00Si0.35Re-drying:
300oC/2h3/321/85/323/161/42.53.254.05.06.01414/1814/181818350350/450350/45045045060-9090-140140-190190-240250-3202.33.6/4.65.3/6.810.1014.204.54.5/6.04.5/6.06.06.013.513.5/18.013.5/18.018.018.0Typical
all weld metal composition [wt%]Welding parameters and packaging
dataDiain mmLengthin mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :70 V)AWS/ASME
SFA A5.1 : E 7018DIN1913 :E 51 44 B10 H10BS639:E 51 44 B26
HHEN499:E 42 3 B 32 H10Basic coated all position welding
electrodeGood toughness at low temperaturesSuitable for welding
general structural steelsDescription and
Applications:Specifications:Rp 0.2 [MPa]430Rm [MPa]510A5
[%]28Impact [ISO-V]130 J @ -20oC90 J @ -30oCHeat TreatmentUTypical
all weld metal mechanical propertiesDIN 17 100DIN 17 155DIN 17
172DIN 1626-1630DIN 1681DIN 17 175DIN 17 102St 33, St 37.2 to St
52.3HI, HII, 17Mn4, 19Mn5StE 210.7, StE 240.7, StE 290.7, StE
320.7, StE 360.7St 37.0/4, St 44.0/4, St 52.0/4GS 38, GS 45, GS
52St 35.8, St 45.8StE 255 to StE 420A,B,C,D,ECast steelsElevated
temperature steelsFine grained steelShipbuilding steelsGeneral
structure steelsBoiler and pressure vessel steelsPipe
steelsMaterials to be welded20Low Alloy Steel ElectrodesZ-4Welding
positionASME:I SO69471GPA2FPB2GPC3GPF4GPERe-drying:
300oC/2h3/321/85/323/161/42.53.254.05.06.01414/1814/181818350350/450350/45045045075-100110-140140-190190-240230-3302.63.8/4.95.6/7.210.514.34.54.5/6.05.0/6.06.06.013.513.5/18.015.0/18.018.018.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :70 V)AWS/ASME
SFA A5.1 : E 7018DIN1913 :E 51 44 B10 H5BS639:E 51 44 B26 HEN499:E
46 3 B 32 H5Basic coated low hydrogen electrode with
highductilitySuitable for welding general construction steelsVery
good bead appearranceGood impact toughness at -30oCDescription and
Applications: Specifications:C0.08Mn1.00Si0.60Typical all weld
metal composition [wt%]Rp 0.2 [MPa]480Rm [MPa]570A5 [%]26Impact
[ISO-V]130 J @ -20oC100 J @ -30oCHeat TreatmentUTypical all weld
metal mechanical propertiesDIN 17 100DIN 17 155DIN 17 172DIN
1626-1630DIN 1681DIN 17 175DIN 17 102St 33, St 37.2 to St 52.3HI,
HII, 17Mn4, 19Mn5StE 210.7, StE 240.7, StE 290.7, StE 320.7, StE
360.7St 37.0/4, St 44.0/4, St 52.0/4GS 38, GS 45, GS 52St 35.8, St
45.8StE 255 to StE 420A,B,C,D,ECast steelsElevated temperature
steelsFine grained steelShipbuilding steelsGeneral structure
steelsBoiler and pressure vessel steelsPipe steelsMaterials to be
welded21Low Alloy Steel ElectrodesZ-4 ACRe-drying:
300oC/2h3/321/85/323/162.53.254.05.01414/1814/1814/18350350/450350/450350/45075-100110-140130-170180-2402.53.7/4.95.5/7.18.1/10.44.54.5/6.05.0/6.05.0/6.013.513.5/18.015.0/18.015.0/18.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]C0.09Mn1.00Si0.65DIN 17 100DIN
17 155DIN 17 172DIN 1626-1630DIN 1681DIN 17 175DIN 17 102St 33, St
37.2 to St 52.3HI, HII, 17Mn4, 19Mn5StE 210.7, StE 240.7, StE
290.7, StE 320.7, StE 360.7St 37.0/4, St 44.0/4, St 52.0/4GS 38, GS
45, GS 52St 35.8, St 45.8StE 255 to StE 420A,B,C,D,ECast
steelsElevated temperature steelsFine grained steelShipbuilding
steelsGeneral structure steelsBoiler and pressure vessel steelsPipe
steelsMaterials to be weldedAWS/ASME SFA A5.1 : E 7018DIN1913 :E 51
44 B10 H5BS639:E 51 44 B26 HEN499:E 42 3 B 32 H5Basic coated low
hydrogen electrode with highductilitySuitable for welding general
construction steelsVery good bead appearranceGood impact toughness
at -30oCPreferably welded on ACDescription and Applications:
Specifications:Welding positionASME:I
SO69471GPA2FPB2GPC3GPF4GPECurrent= + ~ (Uo :70 V)Typical all weld
metal composition [wt%]Rp 0.2 [MPa]450Rm [MPa]550A5 [%]28Impact
[ISO-V]130 J @ -20oC100 J @ -30oCHeat TreatmentUTypical all weld
metal mechanical properties22Low Alloy Steel ElectrodesZ-55Welding
positionASME:I SO69471GPA2FPB2GPC3GPF4GPECurrent= + ~ (Uo :70
V)C0.06Mn1.45Si0.45API SPEC5L: X65, X70, X70Materials to be
weldedAWS/ASME SFA A5.1 : E 7018-1DIN8529 :EY 46 66 MN BH5EN499:E
46 5B 32 H5Low hydrogen basic electrode designed for weldingin all
positions.Excellent strength and high toughness down to -46oC.
suitable for welding medium and highstrength steels.It can be used
in as welded conditions or after heattreatment.Description and
Applications: Specifications:Typical all weld metal composition
[wt%]Rp 0.2 [MPa]520580Rm [MPa]600500A5 [%]2527Impact [ISO-V]140 J
@ -29oC140 J @ -30oC155 J @ -30oC115J @ -46oCHeat
TreatmentPWHT620oC@8hrTypical all weld metal mechanical
properties3/321/85/323/162.53.254.05.014141817.735035045045060-90110-140140-190190-260556615151818Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightpacket[kg]Weightcarton[kg]23Low Alloy Steel
ElectrodesZ-42Re-drying:
300oC/2h1/85/323/161/43.254.05.06.018181818450450450450120-190190-230230-300300-3506.710.216.023.05.55.55.55.516.516.516.516.5Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Welding positionASME:I
SO69471GPA2FPBCurrent= + ~ (Uo :70 V)Rp 0.2 [MPa]540Rm [MPa]550A5
[%]24Impact [ISO-V]120 J @ -20oC100 J @ -30oCHeat TreatmentUTypical
all weld metal mechanical propertiesAWS/ASME SFA A5.1 : E
7028DIN1913 :E 51 43 B(R)12160 H5BS639:E 51 43 B 160 36 HEN499:E 42
3 RB 53 H5High efficiency basic electrode (160% metalrecovery)Fast
deposition rates and high productivityIdeal for steel construction,
bridges, ship building,containers and storage tank weldingHigh
porosity resistanceDescription and Applications:
Specifications:C0.05Mn1.10Si0.30Typical all weld metal composition
[wt%]DIN 17 100DIN 17 155DIN 17 172DIN 1681DIN 17 102DIN 17 175St
33 to St 52.3HI, HII, 17Mn4, 19Mn5StE 210.7, StE 240.7, StE 290.7,
StE 320.7, StE 360.7GS 38, GS 45, GS 52StE 255 to StE 420St 35.8,
St 45.8A,B,C,D,E,AH,DH,EHUnalloyed construction steelsBoiler and
pressure vessel steelsPipe steelsCast steelsElevated temperature
steelsFine grained steelsShipbuilding steelsMaterials to be
welded24Low Alloy Steel ElectrodesZ-47Welding positionRe-drying:
300oC/2h3/321/85/323/162.53.254.05.014141418350350/45035045070-9090-140135-180175-2551.72.94.48.95.05.0/6.05.0/6.06.015.015.0/18.015.0/18.018.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :70 V)Rp 0.2
[MPa]430Rm [MPa]530A5 [%]26Impact [ISO-V]100 J @ -29oCHeat
TreatmentUC0.08Mn1.00Si0.60Typical all weld metal composition
[wt%]AWS/ASME SFA A5.1 : E 7048DIN1913 :E 51 44 B(R)9H10BS639:E 51
44 B 110 54 HHEN499:E 42 3 B 35 H10Vertical down welding basic
electrodeRecommended for welding in shipbuildingconstructionVery
little slag and spatter lossHigh welding speedDescription and
Applications:Specifications:ASME:I SO69471GPA2FPB3GPG5GPGTypical
all weld metal mechanical propertiesDIN 17 100DIN 17 155DIN 17
172DIN 1626-1630DIN 1681DIN 17 175DIN 17 102St 33 to St 52.3HI,
HII, 17Mn4, 19Mn5StE 210.7, StE 240.7, StE 290.7, StE 320.7, StE
360.7St37.0/4, St44.0/4, St52.0/4GS 38, GS 45, GS 52St 35.8, St
45.8StE 255 to StE 420A,B,C,D,E,AH,DH,EHGeneral structural
steelsBoiler and pressure vessel steelsPipe steelsCast
steelsElevated temperature steelsFine grained steelsShipbuilding
steelsMaterials to be welded25Low Alloy Steel
ElectrodesZ-710Welding positionRe-drying: not
necessary3/321/85/323/162.53.254.05.01414141435035035035060-9090-120120-160160-2001.62.84.36.65.05.05.05.015.015.015.015.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= +Rp 0.2 [MPa]500Rm
[MPa]580A5 [%]23Av [ISO-V]70 J @ 0oCHeat
TreatmentSC0.10Mn0.50Si0.20Mo0.50Typical all weld metal composition
[wt%]AWS A5.5:E 7010-A1BS2493 :E MoCEN499: E 42 0 Mo C 41 Cellulose
coated electrodeVertical down welding of high strength pipesHigh
mechanical propertiesDescription and Applications:
Specifications:Typical all weld metal mechanical propertiesDIN 17
100DIN 17 155DIN 17 172DIN 17 175DIN 1629API 5LXDIN 17 102St 37 to
St 52.3HIIStE 210.7 to StE 415.7St 35.8, St 45.8St 35 to St 52.4X42
to X63StE 255 to StE 355Unalloyed construction steelsBoiler and
pressure vessel steelsPipe steelsFine grained steelsMaterials to be
weldedASME:I SO69471GPA2FPB2GPC3GPF3GPG4GPE5GPF/PG26Low Alloy Steel
ElectrodesZ-23Welding positionRe-drying:
300oC/2h3/321/85/323/162.53.254.05.0141414/1814350350350/45045060-9090-130130-190180-2202.33.55.0/6.06.04.55.05.0/6.06.013.515.015.0/18.018.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :70 V)ASME:I
SO69471GPA2FPB2GPC3GPF4GPERp 0.2 [MPa]410Rm [MPa]540A5 [%]28Impact
[ISO-V]140 J @ 20oCHeat TreatmentSC0.05Mn0.70Si0.40Mo0.50Typical
all weld metal composition [wt%]AWS/ASME SFA A5.5 : E
7018-A1DIN8575 :E Mo B 26BS2493 :E Mo BEN1599 :E Mo B 32 modBasic
coated electrodeFor welding creep resistant Mo containing low-alloy
steelsWithstands service temperatures up to 525oCDescription and
Applications:Specifications:Typical all weld metal mechanical
propertiesDIN 17 155DIN 17 245DIN 17 175DIN 17 10214Mn4, 19Mn5,
15Mo3St 45.8, 15Mo3GS C25, GS 22 Mo415Mo3, 16Mo5StE 285 to StE
420Boiler and pressure vessel steelsPipe steel for elevated
temperaturesCast steelsElevated temperature steelsFine grained
steelsMaterials to be welded27Low Alloy Steel
ElectrodesZ-CELLUPIPEWelding positionRe-drying: not
necessary3/321/85/323/162.53.254.05.01414181835035045045060-9080-125120-180160-2301.82.95.68.65.05.05.05.015.015.015.015.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= +Rp 0.2 [MPa]550Rm
[MPa]600A5 [%]23Impact [ISO-V]60 J @ 0oC50 J @ -20oCHeat
TreatmentUC0.10Mn0.80Si0.25Ni0.45Mo0.45Typical all weld metal
composition [wt%]Typical all weld metal mechanical propertiesDIN 17
172API 5LXDIN 17 102StE 290.7 to StE 415.7, StE 290.7 TM to StE
445.7 TMX42 to X70StE 255 to StE 355Pipe steelsFine grained
steelsMaterials to be weldedASME:I
SO69471GPA2FPB2GPC3GPF3GPG4GPE5GPF/PGAWS/ASME SFA A5.5 : E
8010-GBS639:E 51 32 C 10EN499: E 46 2 1NiMo C 41Cellulosic
electrode for vertical down pipe weldingEasy peentration due to
forceful arcSuitable for hot passes in the root, filler andcapping
passesLow suscptability to wagon tracks, windowsand pinholesGood
X-ray qualityDescription and Applications:Specifications:28Low
Alloy Steel ElectrodesZ-31 SWelding positionRe-drying: 300o
C/2h3/321/85/323/162.53.254.05.0141414/1818350350350/45045060-10090-130130-180180-2502.23.45.0/6.410.04.55.05.0/6.06.013.515.015.0/18.018.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :70 V)ASME:I
SO69471GPA2FPB2GPC3GPF4GPEAWS/ASME SFA A5.5 : E 8018-B2DIN8575 :E
CrMo1 B 26BS2493 : E 1 CrMoBEN1599 : E CrMo 1 B 32 modBasic coated
electrode for welding creep resistingsteels containing 1% Cr and
0.5% MoService temperatures of maximum 550oCDescription and
Applications: Specifications:Rp 0.2 [MPa]540Rm [MPa]690A5
[%]20Import [ISO-V]120 J @ 20oCHeat
TreatmentSC0.08Mn0.80Si0.35Cr1.10Mo0.50Typical all weld metal
composition [wt%]Typical all weld metal mechanical propertiesDIN 17
155DIN 17 200DIN 17 210DIN 17 24513CrMo44, 16CrMo44, 15CrMo5,
24CrMo5,22CrMo4425CrMo415Cr3, 16MnCr5, 20MnCr5GS 17CrMo55, GS
22CrMo54, GS 17CrMo55Elevated temperature steelsQuenched and
tempered steelsCase hardening steelsCast steelsMaterials to be
welded29Low Alloy Steel ElectrodesZ-31Welding positionRe-drying:
300o
C/2h3/321/85/323/162.53.254.05.0141414/1818350350350/45045060-10090-130130-180180-2502.23.45.0/6.410.04.55.05.0/6.06.013.515.015.0/18.018.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :70 V)ASME:I
SO69471GPA2FPB2GPC3GPF4GPEAWS/ASME SFA A5.5 : E 8018-B2 LDIN8575 :E
CrMo1 B 26BS2493 : E 1 CrMoL BEN1599 : E CrMo 1 L B 32 modBasic
coated electrode for welding creep resistingsteels containing 1% Cr
and 0.5% MoService temperatures of maximum 550oCSpecifications:
Description and Applications:Rp 0.2 [MPa]540Rm [MPa]690A5
[%]20Import [ISO-V]120 J @ 20oCHeat
TreatmentSC0.05Mn0.90Si0.50Cr1.15Mo0.55Typical all weld metal
composition [wt%]Typical all weld metal mechanical propertiesDIN 17
155DIN 17 200DIN 17 210DIN 17 24513CrMo44, 16CrMo44, 15CrMo5,
24CrMo5, 22CrMo4425CrMo415Cr3, 16MnCr5, 20MnCr5GS 17CrMo55, GS
22CrMo54, GS 17CrMo55Elevated temperature steelsQuenched and
tempered steelsCase hardening steelsCast steelsMaterials to be
welded30Low Alloy Steel ElectrodesZ-32Welding positionRe-drying:
300o
C/2h3/321/85/323/161/42.53.254.05.06.01414/1814/181818350350/450350/45045045080-100100-140130-185190-250240-3202.23.6/4.5.4/6.910.815.04.55.0/6.05.0/6.06.06.013.515.0/18.015.0/18.018.018.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :70 V)ASME:I
SO69471GPA2FPB2GPC3GPF4GPERp 0.2 [MPa]520Rm [MPa]590A5 [%]27Import
[ISO-V]110 J @ -59oCHeat TreatmentSAWS/ASME SFA A5.5 : E
8018-C1DIN8529 :E SY 42 77 2Ni B H5BS2493 : E 2NiBHEN499: 46 6 2Ni
B 42 H5Basic coated electrode for welding low alloystructures
subjected to service down to -60oCGood corrosion resistance to
chloric and sulphuricacidSpecifications:Description and
Applications:C0.05Mn0.90Si0.40Ni2.15Typical all weld metal
composition [wt%]Typical all weld metal mechanical propertiesDIN 17
102DIN 17 280StE315 to StE46011MnNi53, 13MnNi63, 14NiMn6,
10Ni14Fine grained steelsLow temperature steelsMaterials to be
welded31Low Alloy Steel ElectrodesZ-34Welding positionRe-drying:
300o
C/2h3/321/85/323/162.53.254.05.01414/1814/1818350350/450350/45045075-110100-140130-200200-2752.33.8/4.95.5/7.011.04.55.0/6.05.0/6.06.013.515.0/18.015.0/18.018.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :70 V)ASME:I
SO69471GPA2FPB2GPC3GPF4GPERp 0.2 [MPa]490Rm [MPa]580A5 [%]28Import
[ISO-V]70 J@ -40oC40 J@ -60oCHeat TreatmentUAWS/ASME SFA A5.5 : E
8018-C3DIN8529 :EY 46 76 1Ni B H5BS2493 : E 1NiBHLow hydrogen basic
coated electrodeSuitable for welding of low alloyed, fined
grained,high tensile strength steelsSpecifications: Description and
Applications:C0.05Mn0.90Si0.35Ni0.90Mo0.25Typical all weld metal
composition [wt%]Typical all weld metal mechanical propertiesDIN 17
102DIN 17 280StE255 to StE50011MnNi53, 13MnNi63, 14NiMn6,
10Ni14Fine grained steelsLow temperature steelsMaterials to be
welded32Low Alloy Steel ElectrodesZ-3Welding positionRe-drying:
300o
C/2h3/321/85/323/161/42.53.254.05.06.01414/1814/1814/1818350350/450350/45045045075-110110-140140-180190-260240-3302.53.6/4.65.1/6.68.0/10.315.04.55.0/6.05.0/6.06.06.013.515.0/18.015.0/18.018.018.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :70 V)ASME:I
SO69471GPA2FPB2GPC3GPF4GPERp 0.2 [MPa]500Rm [MPa]580A5 [%]26Impact
[ISO-V]150 J@ -20oCHeat TreatmentUAWS/ASME SFA A5.5 : E
8018-GDIN1913 :E51 33 B10 H5BS639:E 51 33 B 120 26 HEN 499:E 50 2 B
32 H5Basic coated low hydrogen electrodeSuitable for maintenance
repairing of agriculturalequipmentElectrode produces crack free and
tough weldedjointsSpecifications: Description and
Applications:C0.06Mn1.30Si0.25Mo0.20Typical all weld metal
composition [wt%]Typical all weld metal mechanical propertiesDIN 17
100DIN 1681DIN 17 175DIN 17 102St 52.3GS 52St45.8StE 315 to StE
500General structural steelsCast steelsElevated temperature
steelsFine grained steelsMaterials to be welded33Low Alloy Steel
ElectrodesZ-3PWelding positionRe-drying: 300o
C/2h3/321/85/322.53.254.01414/1818350350/45045060-9090-140110-1904.55.0/6.06.013.513.5/18.018.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :70
V)ASME:I SO69471GPA2FPB2GPC3GPF4GPERp 0.2 [MPa]620Rm [MPa]540A5
[%]26Impact [ISO-V]85 J@ -30oCAWS/ASME SFA A5.5 : E 8018-GEN ISO
2500-A2005 E503MoB42H5Low hydrogen welding electrode with basic
coating.Designed for all position welding except vertical
down.Especially recommended for filler and cover layers
ofpipeline.Specifications: Description and
Applications:C0.050Mn1.03Si0.38Mo0.36Typical all weld metal
composition [wt%]Typical all weld metal mechanical propertiesAPI
SPEC 5L: X46, X52, X56, X60Materials to be welded34Low Alloy Steel
ElectrodesZ-8Welding positionRe-drying: 300o
C/2h3/321/85/323/161/42.53.254.05.06.01414/1814/181818350350/450350/45045045060-9090-135140-180180-240260-3102.13.5/4.56.8/8.710.615.14.55.0/6.05.0/6.06.06.013.515.0/18.015.0/18.018.018.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :70 V)ASME:I
SO69471GPA2FPB2GPC3GPF4GPERp 0.2 [MPa]500Rm [MPa]590A5 [%]30Impact
[ISO-V]100 J@ -20oC90 J@ -40oC60 J@ -60oCHeat TreatmentUAWS/ASME
SFA A5.5 : E 8018-GDIN8529 :EY 50 76 Mn 1Ni B H5BS639:E 51 54 B 120
26 HEN 499:E 50 6 Mn 1Ni B 32 H5Basic coated electrode with maximum
1% NiExcellent impact toughness at very
lowtemperaturesSpecifications: Description and
Applications:C0.06Mn1.60Si0.30Mo0.60Typical all weld metal
composition [wt%]Typical all weld metal mechanical propertiesDIN 17
100DIN 1681DIN 17 175DIN 17 102DIN 17 280St 52.3GS 52St45.8StE 315
to StE 50011MnNi53, 13MnNi63, 14MnNi6General structural steelsCast
steelsElevated temperature steelsFine grained steelsLow temperature
steelsMaterials to be welded35Low Alloy Steel ElectrodesZ-33Welding
positionRe-drying: 300o
C/2h5/643/321/85/323/161/42.02.53.254.05.06.0121414/1814/181818300350350/450350/45045045050-7575-9590-140135-185175-255250-3301.22.33.7/4.85.8/7.511.416.54.04.54.5/6.05.0/6.06.06.01213.513.5/18.015.0/18.018.018.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :70 V)ASME:I
SO69471GPA2FPB2GPC3GPF4GPERp 0.2 [MPa]530Rm [MPa]600A5 [%]25Impact
[ISO-V]135 J@ -29oC105 J@ -46oCHeat TreatmentSAWS/ASME SFA A5.5 : E
8018-GDIN8529 :ESY 50 66 Mn B H5BS639:E 51 55 B 120 16 HEN 499:E 50
5 B 32 H5Basic coated low hydrogen electrodeDesigned for all
position weldingSuited for welding high strength fine
grainedstructural steelsHigh impact toughness at
-46oCSpecifications: Description and
Applications:C0.08Mn1.50Si0.35Typical all weld metal composition
[wt%]Typical all weld metal mechanical propertiesDIN 17 100DIN
1681DIN 17 175DIN 17 102DIN 17 280St 52.3GS 52St45.8StE 315 to StE
50011MnNi53, 13MnNi63, 14MnNi6General structural steelsCast
steelsElevated temperature steelsFine grained steelsLow temperature
steelsMaterials to be welded36Low Alloy Steel ElectrodesZ-3
WWelding positionRe-drying: 300o
C/2h3/321/85/323/162.53.254.05.01414/1814/1814/18350350/450350/45045075-110110-140150-200190-2602.53.7/4.85.5/7.18.2/10.54.54.5/6.05.0/6.06.013.513.5/18.015.0/18.018.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :70 V)ASME:I
SO69471GPA2FPB2GPC3GPF4GPERp 0.2 [MPa]500Rm [MPa]600A5 [%]25Impact
[ISO-V]70 J@ -20oCHeat TreatmentUAWS/ASME SFA A5.5 : E
8018-WDIN8529 :EY 50 32 1NiCu B H5EN 499:E 50 2 B 32 H5Basic coated
electrode for welding thick structuralweathering steels of similar
compositionresistant to atmospheric corrosionHigh mechanical
propertiesSpecifications: Description and
Applications:C0.05Mn1.20Si0.35Cr0.50Ni0.60Cu0.50Typical all weld
metal composition [wt%]Typical all weld metal mechanical
propertiesDIN 17 100DIN 17 175API 5LXDIN 17 102St 37.2 to St
52.3HI, HII, 17Mn4, 19Mn5X42, X52, X60StE 255 to StE 420A,B,C,D,E,
AH, DH, EHWTSt 37, WTSt 52.3Unalloyed construction steelsBoiler and
pressure vessel steelsPipe steels Fine grained steelsShipbuilding
steelsWeather resistant structural steelsMaterials to be
welded37Low Alloy Steel ElectrodesZ-41 SWelding positionRe-drying:
300o
C/2h3/321/85/323/162.53.254.05.0141414/1818350350350/45045070-11090-130130-180180-2502.23.55.1/6.610.04.55.05.0/6.06.013.515.015.0/18.018.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :70 V)ASME:I
SO69471GPA2FPB2GPC3GPF4GPERp 0.2 [MPa]580Rm [MPa]720A5 [%]18Impact
[ISO-V]110 J@ 20oCHeat TreatmentSAWS/ASME SFA A5.5 : E
9018-B3DIN8575:ECrMo2 B 26BS2493 : E 2CrMo BEN1599 : E CrMo2 B 32
modBasic coated electrode for welding creep resistingsteels
containing 2% Cr and 1% MoService temperatures of maximum
600oCSpecifications: Description and
Applications:C0.09Mn0.75Si0.40Cr2.25Mo1.05Typical all weld metal
composition [wt%]Typical all weld metal mechanical propertiesDIN 17
175DIN 17 24510CrMo9 10, 12CrMo9 10, 10CrSiMo V7, 24CrMo10GS
12CrMo9 10, GS 18CrMo9 10GS 19CrMo9 10Creep and hydrogenresisting
steelsCast steelsMaterials to be welded38Low Alloy Steel
ElectrodesZ-41Welding positionRe-drying: 300o
C/2h3/321/85/323/162.53.254.05.0141414/1818350350350/45045070-11090-130130-180180-2502.23.55.1/6.610.04.55.05.0/6.06.013.515.015.0/18.018.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :70 V)ASME:I
SO69471GPA2FPB2GPC3GPF4GPERp 0.2 [MPa]580Rm [MPa]720A5 [%]18Impact
[ISO-V]110 J@ 20oCHeat TreatmentSAWS/ASME SFA A5.5 : E 9018-B3
LDIN8575:ECrMo2 B 26BS2493 : E 2CrMo L BEN1599 : E CrMo2 L B 32
modBasic coated electrode for welding creep resistingsteels
containing 2% Cr and 1% MoService temperatures of maximum
600oCSpecifications: Description and
Applications:C0.05Mn0.80Si0.40Cr2.00Mo1.00Typical all weld metal
composition [wt%]Typical all weld metal mechanical propertiesDIN 17
175DIN 17 24510CrMo9 10, 12CrMo9 10, 10CrSiMo V7, 24CrMo10GS
12CrMo9 10, GS 18CrMo9 10GS 19CrMo9 10Creep and hydrogenresisting
steelsCast steelsMaterials to be welded39Low Alloy Steel
ElectrodesZ-46Welding positionRe-drying: 300o
C/2h3/321/85/323/162.53.254.05.014141418350350/450350/45045075-100110-140150-190190-2602.13.66.011.25.05.0/6.05.0/6.06.015.015.0/18.015.0/18.018.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :70 V)ASME:I
SO69471GPA2FPB2GPC3GPF4GPERp 0.2 [MPa]600Rm [MPa]650A5 [%]23Impact
[ISO-V]130 J@ -29oC80 J@ -51oCHeat TreatmentSAWS/ASME SFA A5.5 : E
9018-D1DIN8529:E SY 55 65 MnMo B H5BS2493 : E MnMo B HEN499: E 50 5
MnMo B 32 H5Basic coated electrode suited for welding hightensile
structural steels, working at very lowtemperaturesExtremely low
diffusible hydrogen contentSpecifications: Description and
Applications:C0.07Mn1.45Si0.40Mo0.35Typical all weld metal
composition [wt%]Typical all weld metal mechanical propertiesDIN 17
100DIN 17 155St 33, St 37.2 to St 52.3DOMEX 400TE, 450, 480HI, HII,
17Mn4, 19Mn5USS-TGeneral structural steelsBoiler and pressure
vessel steelsFine grained steelsMaterials to be welded40Low Alloy
Steel ElectrodesZ-40 SWelding positionRe-drying: 300o
C/2h3/321/85/323/162.53.254.05.01414141835035035045075-100110-140150-190190-2602.13.65.210.34.55.05.06.013.515.015.018.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= +ASME:I
SO69471GPA2FPB2GPC3GPF4GPERp 0.2 [MPa]500Rm [MPa]600A5 [%]25Impact
[ISO-V]-Heat TreatmentSAWS/ASME SFA A5.5 : E 9018-GDIN8529:E SY 50
0 1NiMo B H5EN499: E 50 A 32 H5Basic coated electrode for welding
steels suchas 4130 and 8630 subjected to heat treatingWelded joints
are crack free and toughSpecifications: Description and
Applications:C0.05Mn1.25Si0.40Cr0.60Mo0.35Ni1.20Typical all weld
metal composition [wt%]Typical all weld metal mechanical
propertiesAPI 5LXDIN 17 102DIN 17 102X70, X 75, X80StE420, StE460,
StE50022NiMoCr37, 17MnMoV64, 15NiCuMoNb5,20MnMoNi45, 20MnMoNi55Pipe
steelsFine grained steelsHigh temperature fine grained
steelsMaterials to be welded41Low Alloy Steel
ElectrodesZ-X70Welding positionRe-drying: 300o
C/2h3/321/85/322.53.254.0141414/18350350350/45060-9090-140110-1902.252.52.513.51515Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightpacket[kg]Weightcarton[kg]Current= + ~ (Uo :70
V)ASME:I SO69471GPA2FPB2GPC3GPF4GPERp 0.2 [MPa]690Rm [MPa]605A5
[%]25Impact [ISO-V]60 J@ -60oCAWS/ASME SFA A5.5 : E 9018-GEN 757
E552MnMoBLow hydrogen basic electrode designed for weldingin al
positions except vertical down.Especially recommended for filler
and cover layers of high diameter pipelines.Specifications:
Description and Applications:C0.05Mn1.5Si0.32Mo0.50Typical all weld
metal composition [wt%]Typical all weld metal mechanical
propertiesAPI SPEC5L: X65, X70,X70Materials to be welded42Low Alloy
Steel ElectrodesZ-48Welding positionRe-drying: 300o
C/2h3/321/85/323/161/42.53.254.05.06.01414141818350350350/45045045070-10090-140140-190180-250240-3202.13.65.210.414.94.55.05.0/6.06.06.013.515.015.0/18.018.018.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= ~ (Uo : 70 V) +ASME:I
SO69471GPA2FPB2GPC3GPF4GPERp 0.2 [MPa]580Rm [MPa]640A5 [%]24Impact
[ISO-V]135 J @ -29oC105 J @ -51oC50 J @ -73oCHeat
TreatmentUAWS/ASME SFA A5.5 : E 9018-MDIN8529 : E Y 55 87 2NiMo B
H5BS2493 : E MnNi B HEN499: E 50 5 Z B 32 H5Basic coated electrode
for welding of lowtemperature, high strength, fine grained
structuralsteelsGood impact toughness at low
temperaturesSpecifications:Description and
Applications:C0.05Mn0.90Si0.25Ni1.75Mo0.30Typical all weld metal
composition [wt%]Typical all weld metal mechanical propertiesDIN 17
100DIN 17 155DIN 17 172 DIN 1681DIN 17 175DIN 17 102DIN 17 102St
50.2, St 60.215Mo3StE 210.7, StE 240.7, StE 290.7, StE 320.7, StE
360.7GS 6010Mo3, 16Mo5TStE420 to TStE50022NiMoCr37, 17MnMoV64, 15
NiCuMoNb5,20MnMoNi45, 20MnMoNi55General structural steelsBoiler and
pressure vessel steelsPipe steelsCast steelsElevated temperature
steelsFine grained steelsHigh temperature fine grained
steelsMaterials to be welded43Low Alloy Steel ElectrodesZ-50Welding
positionRe-drying: 300o
C/2h3/321/85/323/161/42.53.254.05.06.01414141818350350/450350/45045045070-9590-140135-185175-255250-3302.33.75.611.216.24.55.0/6.05.0/6.06.06.013.515.0/18.015.0/18.018.018.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= ~ (Uo : 70 V) +ASME:I
SO69471GPA2FPB2GPC3GPF4GPERp 0.2 [MPa]630Rm [MPa]790A5 [%]22Impact
[ISO-V]95 J @ -29oC65 J @ -51oC45 J @ -73oCHeat TreatmentUAWS/ASME
SFA A5.5 : E 10018-MDIN8529 : E Y 62 87 2Mn2NiMo B H5BS2493 : E
NiMo B HEN499: E 50 5 Z B 32 H5Basic coated electrode for welding
of lowtemperature, high strength, fine grained structuralsteels
such as navel crafts and submarines.Particularly low diffusible
hydrogen content.Specifications: Description and
Applications:C0.05Mn1.65Si0.40Ni2.00Cr0.20Mo0.40Typical all weld
metal composition [wt%]Typical all weld metal mechanical
propertiesDIN 17 100DIN 17 155DIN 17 172 DIN 1681DIN 17 175DIN 17
102DIN 17 102St 50.2, St 60.215Mo3StE 210.7, StE 240.7, StE 290.7,
StE 320.7, StE 360.7GS 6010Mo3, 16Mo5TStE420 to TStE50022NiMoCr37,
17MnMoV64, 15 NiCuMoNb5,20MnMoNi45, 20MnMoNi55General structural
steelsBoiler and pressure vessel steelsPipe steelsCast
steelsElevated temperature steelsFine grained steelsHigh
temperature fine grained steelsMaterials to be welded44Low Alloy
Steel ElectrodesZ-52Welding positionRe-drying: 300o
C/2h3/321/85/323/161/42.53.254.05.06.01414141818350350/450350/45045045070-9590-140135-185175-255250-3302.33.75.611.216.24.55.0/6.05.0/6.06.06.013.515.0/18.015.0/18.018.018.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= ~ (Uo : 70 V) +ASME:I
SO69471GPA2FPB2GPC3GPF4GPERp 0.2 [MPa]700Rm [MPa]780A5 [%]22Impact
[ISO-V]90 J @ -29oC65 J @ -51oCHeat TreatmentUAWS/ASME SFA A5.5 : E
11018-MDIN8529 : E Y 69 76Mn2NiCrMo B H5BS2493 : E 2NiMo B HEN499:
E 50 5 Z B 32 H5Basic coated electrode for welding high
strengthsteels for military applicationsExcellent X-ray
qualitySpecifications: Description and
Applications:C0.05Mn1.60Si0.30Cr0.25Ni2.25Mo0.40Typical all weld
metal composition [wt%]Typical all weld metal mechanical
propertiesDIN 17 100DIN 17 155DIN 17 172 DIN 1681DIN 17 175DIN 17
102DIN 17 102St 50.2, St 60.215Mo3StE 210.7, StE 240.7, StE 290.7,
StE 320.7, StE 360.7GS 6010Mo3, 16Mo5TStE420 to TStE50022NiMoCr37,
17MnMoV64, 15 NiCuMoNb5,20MnMoNi45, 20MnMoNi55General structural
steelsBoiler and pressure vessel steelsPipe steelsCast
steelsElevated temperature steelsFine grained steelsHigh
temperature fine grained steelsMaterials to be welded45Low Alloy
Steel ElectrodesZ-53 MWelding positionRe-drying: 300o
C/2h3/321/85/323/161/42.53.254.05.06.01414/1814/181818350350/450350/45045045065-9590-135140-185180-240240-3202.13.65.2/6.810.414.94.55.05.0/6.06.06.013.515.015.0/18.018.018.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= ~ (Uo : 70 V) +ASME:I
SO69471GPA2FPB2GPC3GPF4GPERp 0.2 [MPa]800Rm [MPa]940A5 [%]20Impact
[ISO-V]60 J @ -29oC50 J @ -51oCHeat TreatmentUAWS/ASME SFA A5.5 : E
12018-MDIN8529 : E Y 79 76Mn2Ni1.5CrMo B H5BS2493 : E 2NiCrMo B
HEN499: E 50 5 Z B 32 H5Basic coated electrode for welding very
highstrength steels for military applicationsSpecifications:
Description and
Applications:C0.06Mn1.90Si0.30Cr2.20Ni1.20Mo0.50Typical all weld
metal composition [wt%]Typical all weld metal mechanical
propertiesDIN 17 100DIN 17 155DIN 17 172 DIN 1681DIN 17 175DIN 17
102DIN 17 102St 50.2, St 60.215Mo3StE 210.7, StE 240.7, StE 290.7,
StE 320.7, StE 360.7GS 6010Mo3, 16Mo5TStE420 to TStE50022NiMoCr37,
17MnMoV64, 15 NiCuMoNb5,20MnMoNi45, 20MnMoNi55General structural
steelsBoiler and pressure vessel steelsPipe steelsCast
steelsElevated temperature steelsFine grained steelsHigh
temperature fine grained steelsMaterials to be welded46Low Alloy
Steel ElectrodesZ-502Welding positionRe-drying: 300o
C/2h3/321/85/323/162.53.254.05.01214141430035035035065-9590-130125-180180-2402.03.65.48.54.05.05.05.012.015.015.015.0Welding
parameters and packaging dataDiain mmLengthin
mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]Current= ~ (Uo : 70 V) +ASME:I
SO69471GPA2FPB2GPC3GPF4GPERp 0.2 [MPa]490Rm [MPa]620A5 [%]20Impact
[ISO-V]80 J @ -20oCHeat TreatmentSAWS/ASME SFA A5.4 : E
502-15DIN8575 : E CrMo5 B 26BS2493 : E 5CrMo BEN 1599 : E CrMo5 B
32 modBasic coated 5% Cr - 0.5% Mo electrodeService temperature of
maximum 600oCWelding of Cr-Mo alloys of similar compositionSuitable
for critical thick jointsSpecifications: Description and
Applications:C0.06Mn0.60Si0.35Cr5.20Mo0.60Typical all weld metal
composition [wt%]Typical all weld metal mechanical propertiesDIN 17
155DIN 17 24512CrMo19 5 GS 12CrMo19 5 Boiler and pressure vessel
steelsCast steelsMaterials to be welded47Low Alloy Steel
ElectrodesZ-505Basic coated 9% Cr- 1% Mo electrodeService
temperatures of maximum 6500CDescription and
Applications:CurrentSpecifications:=+~(Uo : 70V)AWS/ASME SFA A5.4 :
E 505-15DIN8575: E CrMo9 B 26BS2493 : E 9CrMO BEN1599 : E CrMo9 B
32 modWelding positionASME:1G2F2G3G4GI SO6947PAPBPCPFPEDIN 17
176DIN 17 245Boiler and pressure vessel steelsCast steelsTypical
all weld metal composition [wt%]Typical all weld metal mechanical
propertiesMaterials to be weldedWelding parameters and packaging
dataX12 CrMO91GX 12CrMo 10 1CMnSiCrMo0.080.750.659.501.00Rp 0.2
[MPa]Rm [MPa]A5 [%]Impact [ISO-V]Heat Treatment5507002280 J@
20oCSRe-drying:
3000C/2h3/321/85/323/162.53.254.05.01214141430035035035065-105110-140150-190180-2301.93.65.48.44.05.05.05.012.015.015.015.0Diain
mmLengthin mmCurrent[amps]Weightkg/100
pcsWeightpacket[kg]Weightcarton[kg]48Low Alloy Steel
ElectrodesZ-91Low hydrogen electrode suitable for welding9%Cr-1%Mo
steels, also known as GRADE 91designed to provide excellent
endurance in creep,fatigue, oxidation and corrosion resistance on
hightemperatures.ASTMA213 T91A335 P91A369 FP91EN1.4903 (X10CrMoVNb
91)A387 G91A217 C12AA182/A336 F91A234 P91Description and
Applications:Rp 0.2 [MPa]Rm[MPa]A5 [%]Impact
[ISO-V]57070018121J@20oCCurrentTypical all weld metal composition
[wt%]Typical all weld metal mechanical propertiesMaterials to be
weldedWelding parameters and packaging dataAWS/ASME SFA 5.5:
E9015-B9Specifications:CMn*SiCrNi*Mov0.110.25 90.310.2*Mn+Ni