Buderus Plastic Mould Steel 2767 ISO-B Buderus Edelstahl GmbH l Steel Bar Sales l Buderusstraße 25 l D-35576 Wetzlar Telephone +49 (0) 64 41-374 2468 l Fax +49 (0) 64 41-374 2784 l [email protected]l www.buderus-steel.com C Si Mn P S Cr Ni Mo Typical analysis 0.45 0.25 0.30 0.025 0.003 1.30 4.00 0.25 Chemical composition as per SEL 0.40– 0.50 0.10– 0.40 0.20– 0.50 ≤ 0.030 ≤ 0.030 1.20– 1.50 3.80– 4.30 0.15– 0.35 Figures in % by mass Register of European Steels (SEL) 45 NiCrMo 16 DIN EN ISO 4957 45 NiCrMo 16 AFNOR 45 NCD 16 AISI 6 F 7 Characteristics Low-distortion, air through-hardening nickel-alloy tool steel with very good toughness; polishable, grain-reliable. Applications Highly stressed compression and injection moulds such as tailgates, mudguards; mould inserts for high hardness and abrasive stress. Blanking dies for very thick materials (sheet steel up to 12 mm thick), billet shearing blades, industrial blades. Cutlery presses and stamping dies, forging dies, mandrel holders for extrusion mandrels. Delivered condition Annealed to max. 285 HB We recommend contour hardening for large moulds. Physical properties (reference values) Thermal expansion coefficient (10 –6 /K) 20–100 °C 11.0 20–250 °C 12.2 20–500 °C 13.7 Thermal conductivity (W/mK) 20 °C 31.0 250 °C 30.0 500 °C 32.0 Young’s modulus (GPa) 20 °C 215 250 °C 198 500 °C 179 l Buderus Plastic Mould Steel 2767 ISO-B
2
Embed
Buderus Plastic Mould Steel 2767 ISO-B...Cutlery presses and stamping dies, forging dies, mandrel holders for extrusion mandrels. Delivered condition Annealed to max. 285 HB We recommend
This document is posted to help you gain knowledge. Please leave a comment to let me know what you think about it! Share it to your friends and learn new things together.
Transcript
Bude
rus
Plas
tic
Mou
ld S
teel
276
7 IS
O-B
Buderus Edelstahl GmbH l Steel Bar Sales l Buderusstraße 25 l D-35576 WetzlarTelephone +49 (0) 64 41-374 2468 l Fax +49 (0) 64 41-374 2784 l [email protected] l www.buderus-steel.com
C Si Mn P S Cr Ni MoTypical analysis 0.45 0.25 0.30 0.025 0.003 1.30 4.00 0.25
Chemical composition as per SEL
0.40–0.50
0.10–0.40
0.20–0.50
≤0.030
≤ 0.030
1.20–1.50
3.80–4.30
0.15–0.35
Figures in % by mass
Register of European Steels (SEL)
45 NiCrMo 16
DIN EN ISO 4957 45 NiCrMo 16
AFNOR 45 NCD 16
AISI 6 F 7
CharacteristicsLow-distortion, air through-hardening nickel-alloy tool steel with very good toughness; polishable, grain-reliable.
ApplicationsHighly stressed compression and injection moulds such as tailgates, mudguards; mould inserts for high hardness and abrasive stress.Blanking dies for very thick materials (sheet steel up to 12 mm thick), billet shearing blades, industrial blades.Cutlery presses and stamping dies, forging dies, mandrel holders for extrusion mandrels.
Delivered conditionAnnealed to max. 285 HB We recommend contour hardening for large moulds.
Stress relieving Temperature: Approx. 600 °C in the annealed stateDuration: 1 hour per 50 mm wall thicknessCooling: Furnace
Soft annealing Temperature: 650 °CDuration: 1 hour per 25 mm wall thicknessCooling: Air
Hardening Temperature: 870 °CDuration: 1 minute per mm wall thickness
Quenching hardness Max. 56 HRC in oil, hot bath, air or vacuum
Tempering Temperature: See tempering curveDuration: 1 hour per 25 mm wall thicknessCooling: Air
Working hardness 50–54 HRC (temper at least twice 220 °C)
Note: If soft annealing is required: do not exceed annealing temperature, hold at temperature for the full annealing time!In the case of oil hardening, do not leave tools to cool down in the oil.
Tempering curve
TTT curve (continuous)
l 2767 ISO-B
40424446485052545658606264
0 100 200 300 400 500 600 700 800373392413436
(461)
HB
Har
dnes
s in
HRC
Tempering temperature in °C
Average values on samples dia. 25 x 50 mm longhardened at 870 °C in oilHB converted from HRC