Bioplastics Compounding

Page 2: Bioplastics Compounding

Bioplastics

Plastics which are biodegradableand/or

partly or wholly derived from renewable resources

Page 3: Bioplastics Compounding

Bioplastics

Many different types– starch, processed starch and starch blends– fermentation products from plant sugars and starches– polymers produced directly by microbes– blends with renewable resource derived polymers– PE and PP from renewable resources (sugarcane ethanol)

• have identical properties to standard PE and PP

Page 4: Bioplastics Compounding

Bioplastics

Page 5: Bioplastics Compounding

Bioplastics• Diverse range of polymer types• Wide range of characteristics for some bioplastics depending

on details of chemistry. e.g.– Isomers (eg l-PLA vs d-PLA)– Co-monomers– Chain branching vs linear

• Starch is processed to produce ‘thermoplastic starch’ (TPS)– ‘cooking’ with water– plasticization – reaction extrusion

• Many proprietary blends and patents• Generalizations, even for one polymer type, are not possible

Page 6: Bioplastics Compounding

Blending BioplasticsSustainability

– Renewable content– Biodegradability– Greenhouse gas– Energy & water

Performance– Mechanical– Water resistance– Gas barrier– Colour & appearance

Processability– Temp stability– Melt strength– Rheology

Cost

Page 7: Bioplastics Compounding

Blending Bioplastics

Some examples of commercial bioplastic blends

Page 8: Bioplastics Compounding

Blending Bioplastics

Example: CeralloyTM Eco HD– 50% non-renewable HDPE– 50% CerestarchTM thermoplastic starch

kg C

O2

eq/k

g

Source: www.cerestech.com

Page 9: Bioplastics Compounding

Plasticizers

Page 10: Bioplastics Compounding

Plasticizers

• Addition of plasticizers is often used to lower Tg and melt viscosity

• Improve processability and properties (impact, low temperature flex)

• Plasticizers should be: – low molecular weight and high b.p.– low viscosity which is not temperature sensitive– compatable with base polymer– biodegradable– made from renewable resources

Page 11: Bioplastics Compounding

Plasticizers• Problems can occur with blooming and leaching of

very low m.w. or incompatible plasticizers• Water is used as a plasticizer for starch

– Limits processing temperature– Evaporation over time leads to embrittlement

Page 12: Bioplastics Compounding

Plasticizers

Some plasticizers used in bioplastics

Page 13: Bioplastics Compounding

Processing

Page 14: Bioplastics Compounding

Processing• Biodegradable polymers must have relatively low main

chain bond strengths to allow breakdown by microbes– e.g. starch amylopectin

• This leads to low thermal degradation temperatures

Page 15: Bioplastics Compounding

Processing

• Generally hygroscopic and moisture content needs to be controlled

• Degradation can produce corrosive acids• Minimize process temperatures and residence times• Degradation can occur in extruder ‘dead zones’• Purge with PE before shut down

Page 16: Bioplastics Compounding

Processing

Processing‘window’

Page 17: Bioplastics Compounding

Processing

• Good mixing required– Twin screw co-rotating extruder

• Feeding may be difficult– Hydrophyllic starch surfaces tend to cause powders to clump– Control moisture content

• Mixing hydrophyllic starch and other bioploymers with hydrophobic polymers (e.g. PP, PE) requires compatibilizers

Page 18: Bioplastics Compounding

Processingbiopolymerbiopolymer

thermoplastic starch

thermoplastic starch

plasticizers(renewable based)plasticizers

(renewable based)

polymer(non-renewable based)

polymer(non-renewable based)

plasticizers(non-renewable based)

plasticizers(non-renewable based)

additivesadditives

fillers(organic & inorganic)

fillers(organic & inorganic)

extruderextruder

mixermixer

pelletizer

compound• Sustainability• Performance• Processability• Cost

liquid injection

devolatilization

Page 19: Bioplastics Compounding

Chain Extenders

• PLA and other condensation polymers suffer from chain scission due to heat & shear

• Chain extenders can re-join chains– Improves melt strength– Improves rheology– Aids recycling

• Consider for blown film, thermoforming and foam processes

Page 20: Bioplastics Compounding

Chain Extenders

• Clariant CESA-extend– Biodegradable– Derived form renewable resources

• Arkema Biostrength 700– Not biodegradable

Source: Bioplastics 03/08 p35

Page 21: Bioplastics Compounding

Mechanical Properties

Page 22: Bioplastics Compounding

Property Profiles

Page 23: Bioplastics Compounding

Impact Modifiers

• Du Pont Biomax Strong 120– FDA compliant toughening agent for PLA packaging

• Rohm & Haas Paraloid BPM-500– Improves impact & tear strength of PLA film– Maintains clarity– Acrylic based

• Sukano® PLA im S550– Improves resiliance and toughness in transparent PLA

Page 24: Bioplastics Compounding

Colour

Page 25: Bioplastics Compounding

Colour

• Many bioplastics, especially starch based, are opaque with a yellow/brown colour

• This may be exacerbated with processing• High intensity colours will not be possible• PLA can have excellent clarity• Pigment systems need to maintain biocompostability

and be non-toxic

Page 26: Bioplastics Compounding

Colour

Clariant Renol-naturTM pigment systems• Biodegradable• Natural sources:

– Orange from tumeric root– Yellow from tropical flowers

• Lower light resistance than conventional pigments

Page 27: Bioplastics Compounding

Colour

PolyOne OnColor BioTM Colorants• Suitable for many bioplastics• Certified for compostability

Page 28: Bioplastics Compounding

Colour

Teknor Colour Company• Colour concentrates for PLA bottles, film, sheet,

profiles and injection moulding• Various carrier types:

– Biodegradable PLA– Biodegradable (non-renewable) polyester– Non degradable PET for durable applications

Page 29: Bioplastics Compounding

Other Additives

Page 30: Bioplastics Compounding

Other Additives

PolyOne OnCap additives for use in bioplastics• Antistat• Antiblock • UV stabilizers• Anti-fog

Nucleation should also be considered as slow set-up times are a problem with some bioplastics

e.g. PLA, PHA’s

Page 31: Bioplastics Compounding

Biocomposites

Page 32: Bioplastics Compounding

BiocompositesUse of renewable and/or biodegradable fillers or fibres

to make composites with bioplastics• Inorganic fillers e.g. talc, calcium carbonate (chalk)

– Small increase in properties– Increase in s.g.– Acceptable degradation products for compostability tests– Reduce renewable content (which is based on carbon)

• Organic fillers e.g. wood flour, ground peanut husks– Increase renewable content

Page 33: Bioplastics Compounding

Natural Fibres

• Addition of natural fibres provides reinforcement and useful increases in strength & stiffness

• Increased renewable content• Natural fibres include:

– Flax – Sugarcane bagasse– Hemp – Wood– Kenaf – Jute

• All cellulose based, but with varying amounts of lignin and other materials, including silica

Page 34: Bioplastics Compounding

Additives

REINFORCING NATRAL FIBRES

NON WOOD NATURAL/BIOFIBERS WOOD FIBRES

BASTGRASS FIBRESSEED/FRUITLEAF

STRAW FIBRES

Soft and Hard Woods

Cotton, CoirKenaf, Flax,Jute, Hemp

Corn/WheatRice Straws

Sisal, Pineapple Leaf Fibre

Bamboo Fibre, Elephant Grass

Page 35: Bioplastics Compounding

Natural Fibres

Specific Young’s Modulus

Source: A.K.Mohanthy et al,’Natural Fibres, Biopolymers and Biocomposites’,CRC, 2005, and others

Page 36: Bioplastics Compounding

Biocomposites• Addition of natural fibre to increase stiffness and

strength • Natural fibre properties are lower than for E-glass• Density is also lower• Higher fibre content is required for similar properties• Can provide light weight and high renewable content• Aim to retain as much fibre length as possible

– Downstream feeding– Low shear

Page 37: Bioplastics Compounding

Effects of additives on mechanical properties

Matrix polymer

Modulus (MPa)

Reinforcement Volume fraction (%)

Modulus of composite (MPa)

TPS a) 47.2 Ethanolamine activated montmorilonite

5 145.5

TPS 87 Medium size fibers b) 5 190

TPS 87 Medium size fibers 12 522 c)

TPS 80 Cellulose microfibrils 10 3000

PLA 2700 Recycled newspaper 10 5300

PLA 3500 flax 30 8000

TPS 81.5 montmorilonite 20 850

TPS 45 Waxy maize starch crystals/ 5 d) 298

a) Thermoplastic starchb) 2-3mm in lengthc) as a comparison the author also reported that HDPE module only increased two times with 12% fibres, d) 20 % glycerol as a plasticiser

Page 38: Bioplastics Compounding

Biocomposites

• Natural fibres need to be processed to obtain a fibrelength range, generally 1 – 5 mm with low particulate level

• Surface treatment to improve bonding to matrix– Surface fibrillation, corona, plasma– Alkaline swelling– Acetylation, silane, isocyanate reactions

• The environmental effects of chemical methods needs to be considered!

Page 39: Bioplastics Compounding

Biocomposites

• Compatibilizers can be used to improve bonding of hydrophobic fibres to hydrophyllic matrixes (e.g. PP)

• Clariant Licocene PP MA 6452 TP– Maleated PP wax

Page 40: Bioplastics Compounding

Biocomposites

Some examples of commercial biocomposites

Page 41: Bioplastics Compounding

Biocomposites

PLA/kenaf fibre biocomposites developed by NEC and Unitika Ltdfor mobile phone housings

Source: K.Inoue, NEC, Bioplastics 2007 Conference paper

Page 42: Bioplastics Compounding

Certification

Page 43: Bioplastics Compounding

End-of-Life Environments

Page 44: Bioplastics Compounding

Certifying Bioplastics - US

• Testing to ASTM D6400 or D6868– Active municipal or commercial composting– Inherent biodegradability similar to natural biopolymers

over 180 days (or longer with additional tests)– Disintegrates into small pieces (<2mm)– No ecotoxicity

• Reviewed and certified by Biodegradable Products Institute (BPI)

Page 45: Bioplastics Compounding

Certifying Bioplastics - Europe

• Testing to EN 13432– Controlled composting with elevated temperature and

aeration – Inherent biodegradability similar to natural biopolymers

over 180 days (or longer with additional tests)– Disintegrates into small pieces (<2mm)– No ecotoxicity

• Reviewed and certified by – DIN Certco, or – AVI Certest