ASME IX PRACTICE QUESTIONS
(Closed Book)
1. The purpose of the WPS and PQR is to determine that:A. The welder is qualifiedB. The base metals are strong enoughC. The weldment has the desired propertiesD. The skill of the welder
2. The WPS lists:A. Non-essential variablesB. Essential variablesC. Ranges of 1 & 2 aboveD. All of the above
3. The PQR must list:A. essential variablesB. qualification test & examination resultsC. supplementary essential variables (when notch
toughness is required)
4. What is the earliest Edition of Section IX recognized by the currentedition?
A. 1958B. 1992C. 1987D. 1962
5. New Welding Procedure Specifications must meet the _________Edition and Addenda of Section IX.
A. 1962B. currentC. 1986D. 1995
8/22/2019 ASME IX.questions Anwser
2/22
Professional Training and Consultation
8th Floor, Al-Subeaei Towers, King Abdulaziz cor. Prince Faisal Bin Fahd Streets, Al-Khobar, Saudi Arabia
TEL (966) 3 887 6633 FAX (966) 3 887 6565 [email protected] www.gotoitc.com
32
6. Each ____________________ shall conduct the tests required bySection IX to qualify the WPSs used during the construction,
alteration, or repair.
A. Welder or welding operatorB. Manufacturer or contractorC. InspectorD. All of the above
7. The records of procedure, welder and welding operator qualificationmust be available to the __________.
A. ManufacturerB. WelderC. Authorised InspectorD. Foreman
8. A welder qualifying with a groove weld in plate in the 4G position isqualified to weld groove welds in plate and pipe over 24O.D. in at
least the ________ positions.
A. VerticalB. Flat & horizontalC. Flat & overheadD. Horizontal
9. A welder qualifying with plate fillet welds in the 3F and $f positionsis qualified to weld groove welds in plate in the _____________positions.
A. Flat onlyB. Flat and horizontalC. Flat and verticalD. None of the above
10. A welder qualifying by making a groove weld on pipe with an O.D.of in the 5G position is qualified to weld groove welds in:A. O.D. Pipe in the overhead positionB. 6 O.D. Pipe in the vertical positionC. O.D. pipe in the horizontal positionD. None of the above
8/22/2019 ASME IX.questions Anwser
3/22
Professional Training and Consultation
8th Floor, Al-Subeaei Towers, King Abdulaziz cor. Prince Faisal Bin Fahd Streets, Al-Khobar, Saudi Arabia
TEL (966) 3 887 6633 FAX (966) 3 887 6565 [email protected] www.gotoitc.com
33
11. In general, qualification on groove welds also qualifies awelder to make:
A. Stud weldsB. Overhand weldsC. Fillet weldsD. All of the above
12. Charpy V-notch tests are performed to determine a weldmentsA. Tensile strengthB. DuctilityC. Notch toughnessD. All of above
13. A welder making a groove weld using the SAW process on P1materials may be qualified using radiography.
A. TrueB. False
14. When a tensile specimen breaks in the base metal outside of theweld or fusion line, the strength recorded may be at most ____below the specified tensile and be accepted.
A. 3.5%B. 0.5%C. 5%D. All of the above
15. Guided-bend specimens shall have no open defects in the weld orheat effected zone exceeding __________ measured in anydirection on the convex surface of the specimen after bending.
A. 1/16B. 3/32C. 1/8D. None of the above
16. When using radiographs to qualify welder, the acceptancestandards used are found in:
A. ASME Section V
8/22/2019 ASME IX.questions Anwser
4/22
Professional Training and Consultation
8th Floor, Al-Subeaei Towers, King Abdulaziz cor. Prince Faisal Bin Fahd Streets, Al-Khobar, Saudi Arabia
TEL (966) 3 887 6633 FAX (966) 3 887 6565 [email protected] www.gotoitc.com
34
B. ASME Section IXC. ASME Section VIID. The referencing code
17. A WPS must describe:A. Essential variablesB. Nonessential variablesC. Supplementary essential variable when
required for notch toughnessD. All of the above
18. A PQR must describe:A. Nonessential variablesB. Essential variablesC. Results of Welder Qualification testsD. Project description & NDE methods
19. The _______ must certify the PQR as accurate.A. InspectorB. Manufacturer or contractorC. WelderD. All of the above
20. For the SMAW process ___________________ is an essentialvariables for the WPS.
A. Groove designB. Post Weld Heat TreatmentC. Root spacingD. Method of cleaning
21. For the SAW process ________________________ is an essentialvariable for the WPS.
A. Supplemental powdered filler metal (if used)B. Filler metal diameterC. Preheat maintenanceD. Addition or deletion of peening
8/22/2019 ASME IX.questions Anwser
5/22
Professional Training and Consultation
8th Floor, Al-Subeaei Towers, King Abdulaziz cor. Prince Faisal Bin Fahd Streets, Al-Khobar, Saudi Arabia
TEL (966) 3 887 6633 FAX (966) 3 887 6565 [email protected] www.gotoitc.com
35
22. The basic purpose of testing a welder is to establish the welders____________________________.
A. Knowledge of welding requirementsB. Ability to deposit sound weld metalC. Mechanical ability to operate equipmentD. General attitude toward welding inspectors
23. The record of a welders performance test is called a _______.A. PQRB. WQRC. WPSD. WPQ
24. If a welder qualified with the SMAW process on Jan. 1,1994 and lastwelded with SMAW on March 15, 1994, would he still be qualifiedon October 7, 1994?
A. YesB. No.
25. A welder qualifying with a groove weld welded from both sides isqualified to weld ________________.
A. Without backingB. With all base metalsC. With backing onlyD. With P1 backing only
26. Immediate retests of welders qualifications coupons:A. Must use the same methodB. May use any methodC. Are not allowedD. Require Inspector approval
27. Welder performance qualification records must describe all the___________ variables specified.
A. Essential & nonessentialB. Nonessential
8/22/2019 ASME IX.questions Anwser
6/22
Professional Training and Consultation
8th Floor, Al-Subeaei Towers, King Abdulaziz cor. Prince Faisal Bin Fahd Streets, Al-Khobar, Saudi Arabia
TEL (966) 3 887 6633 FAX (966) 3 887 6565 [email protected] www.gotoitc.com
36
C. EssentialD. Brazing
28. A welder depositing 1/2" of weld metal with the SMAW process isqualified to deposit up to ____________ of weld metal.
A. 8B. Max to be weldedC. 1D.
29. P numbers are used to designate groups of:A. ElectrodesB. FluxC. Base metalsD. Joints
30. A welder qualifying by welding P-No. 21 to P-No.21 isqualified to weld:
A. P-1- P-11 to P-1 P 11B. P-8 P8C. P-21 P-25 TO P-21-P-25D. P21 to P21 only
31. Welding electrodes are grouped in Section IX by:A. AWS classB. ASME specificationC. SFAD. F number
32. Ferrous weld metal chemical composition may be designatedusing:
A. P numberB. Welder I.D.C. A numberD. Page number
8/22/2019 ASME IX.questions Anwser
7/22
Professional Training and Consultation
8th Floor, Al-Subeaei Towers, King Abdulaziz cor. Prince Faisal Bin Fahd Streets, Al-Khobar, Saudi Arabia
TEL (966) 3 887 6633 FAX (966) 3 887 6565 [email protected] www.gotoitc.com
37
33. For welder qualifications with the SMAW process______________________ is an essential variable.
A. Base metal thicknessB. PeeningC. P-numberD. Electrode diameter
34. Each welder must be assigned a(n):A. P numberB. Unique identifierC. Hood & glovesD. Inspector
35. May a welder, qualified in the 2G position on inch thick plate,weld a 1 inch outside diameter pipe, inch thick in the horizontalposition without re-qualification?
A. YesB. NoC. Not enough information providedD. Yes, provided pipe is carbon steel, P#1
36. What is the difference between gas metal arc-welding and gastungsten arc-welding processes?
A. GMAW uses a continuously fed fillet metal andGTAW a tungsten electrode
B. The SFA specification of the filler metalC. The F-number of the filler metalD. GTAW is run with gas; gas is optional with
GMAW
37. A welder has been tested in the 6-G position, using as E-7018 F-4electrode, on 6 Sch 160 (0.718 nom) SA 106B pipe. Is this welderqualified to weld a 2 300# ANSI schedule 80 bore flange to a 2Schedule 80 SA 106 B nozzle neck?
A. YesB. NoC. Not enough information provided
8/22/2019 ASME IX.questions Anwser
8/22
Professional Training and Consultation
8th Floor, Al-Subeaei Towers, King Abdulaziz cor. Prince Faisal Bin Fahd Streets, Al-Khobar, Saudi Arabia
TEL (966) 3 887 6633 FAX (966) 3 887 6565 [email protected] www.gotoitc.com
38
D. Yes, provided a backing strip is provided in the2 weld.
38. May a welder who qualified using a double-groove weld, make asingle V-groove weld without backing?
A. YesB. NoC. Not enough information providedD. Yes, because backing is not an essential
variable for a welder
39. May a GTAW welder be qualified by radiography, in lieu ofbend tests? The test coupon will be P-22 material and the
production welds will be P-22 also.A. YesB. NoC. Not enough information providedD. Yes, provided the P-22 is welded with F-22
fillers
40. Who is responsible for qualification of welding procedures, weldersand welding operators?
A. The InspectorB. The A.I.C. The Shop ForemanD. The Manufacturer of Contractor
41. A welding electrode has the marking E-6010. The 1 markingindicates:
A. Flat position onlyB. Horizontal position onlyC. All positionsD. Only good for heat treated welds
42. May a FCAW welder qualified using UT, be used to weld inproduction?
A. Yes, welder can be usedB. No welder cannot be usedC. Yes, if welder is using GMAW (Short Arc)
8/22/2019 ASME IX.questions Anwser
9/22
Professional Training and Consultation
8th Floor, Al-Subeaei Towers, King Abdulaziz cor. Prince Faisal Bin Fahd Streets, Al-Khobar, Saudi Arabia
TEL (966) 3 887 6633 FAX (966) 3 887 6565 [email protected] www.gotoitc.com
39
D. Yes, if welder is qualified with backing43. A welder may deviate from the parameters specified in a WPS if
they are a nonessential variable.
True Or False (circle one)
44. What is the number of transverse guided bend tests required forPerformance Qualification in a 6G position?
A. 2B. 4C. 6D. 3
45. What positions are necessary to qualify a welder for all position pipewelding?
A. 3G and 4GB. 2G and 5GC. 3G and 1GD. 4G and 5G
46. What ASME Code Section has welding electrode storagerequirements?
A. ASME IXB. ASME VIIIC. ASME B31.1D. ASME II Part C
47. A repair organization has a WPS which states it is qualified for P-8to P-8 material welded with E308, E308L, E309, E316, electrodes(SMAW process). The PQR, supporting this WPS, states the weldtest coupons were SA-240 Type 304L material, welded with E308
electrodes. Is the WPS properly qualified for the base materiallisted?
A. YesB. NoC. Not enough information givenD. Yes, if properly heat treated
8/22/2019 ASME IX.questions Anwser
10/22
Professional Training and Consultation
8th Floor, Al-Subeaei Towers, King Abdulaziz cor. Prince Faisal Bin Fahd Streets, Al-Khobar, Saudi Arabia
TEL (966) 3 887 6633 FAX (966) 3 887 6565 [email protected] www.gotoitc.com
40
48. May a GMAW, short circuit transfer, welding procedure be qualifiedusing real-time ultrasonics?
A. YesB. NoC. Not enough information givenD. Yes, provided bend tests are done
49. Three arc-welding processes are:A. BMAW, SMAW, EFGAWB. FCAW, SAW, ESWC. SMAW, GTAW, PAWD. PTAW, SLAW, PEAW
50. A welder was qualified with a P-1 test coupon using SMAW E 7018electrodes. May the welder weld P-4 material using E8028electrodes with backing in production? (Assume the P-4 procedureusing E8028 electrodes has been qualified)
A. YesB. NoC. Not enough information providedD. None of the above
51. Is a welding procedure qualified under the 1965 ASME Code SectionIX still applicable?
A. YesB. No, must be re-qualifiedC. Is only applicable for 1965 pressure vesselsD. Cannot be used for new construction repairs
only
52. What are the various positions in which a welder may qualify forplate groove welds?
A. 1GB. 3GC. 4GD. All of the above
8/22/2019 ASME IX.questions Anwser
11/22
Professional Training and Consultation
8th Floor, Al-Subeaei Towers, King Abdulaziz cor. Prince Faisal Bin Fahd Streets, Al-Khobar, Saudi Arabia
TEL (966) 3 887 6633 FAX (966) 3 887 6565 [email protected] www.gotoitc.com
41
53. You are reviewing a WPQ (QW-484) for a welder testing in the 6-Gposition, on SA-53 grade B pipe (TS-60,000 psi). The test resultsindicate the following:
No.1 Tensile developed 51,000 psi, broke in the weldNo.2 Tensile developed 56,900 psi, broke in base metalNo.1 Transverse root bend satisfactoryNo.2 Transverse face bend satisfactory
Will this test qualify the welder?
A. YesB. NoC. Not enough information givenD. Tension test is acceptable but No.1 isunacceptable
54. What are the primary classifications of guided-bend tests permittedby the Code?
A. Side and TransverseB. Face and RootC. Transverse and LongitudinalD. Side and Face
55. A welder qualified by welding in the 5G position is qualified for whatposition on plate?
A. F,H,OHB. F,V,OHC. V,OH,SPD. H,V,OH
56. Which of the following is a covered electrode?A. E6010B. E7018C. E9028D. All of the above
8/22/2019 ASME IX.questions Anwser
12/22
Professional Training and Consultation
8th Floor, Al-Subeaei Towers, King Abdulaziz cor. Prince Faisal Bin Fahd Streets, Al-Khobar, Saudi Arabia
TEL (966) 3 887 6633 FAX (966) 3 887 6565 [email protected] www.gotoitc.com
42
57. Applicable essential variables must be documented on which of thefollowing?
A. The WPSB. The PQRC. The WPQD. All of the above
58. In performance qualification of pipe welds to ASME Section IX,which positions require more than two guided bend specimens forqualification?
A. 5G and 6GB. 2G and 4FC. 4G and 5GD. None of the above
59. Name two defects that would cause visual rejection of a welderstest pipe or plate?
A. Porosity, underfillB. Lack of penetration/fusionC. Slag, overlapD. Any of the above
60. A variable that, when changed will cause a change in themechanical properties of the weldment is called a:
A. Essential variableB. Non-essential variableC. Supplementary essential variableD. All of the above
61. The test that determines the ultimate strength of groove-weldjoints is a:
A. Notch Toughness TestB. Tension TestC. Fillet Weld TestD. Guided-Bend Test
8/22/2019 ASME IX.questions Anwser
13/22
Professional Training and Consultation
8th Floor, Al-Subeaei Towers, King Abdulaziz cor. Prince Faisal Bin Fahd Streets, Al-Khobar, Saudi Arabia
TEL (966) 3 887 6633 FAX (966) 3 887 6565 [email protected] www.gotoitc.com
43
62. The procedure qualification test is used to determine:A. The skill of the welderB. That the proposed production weldment is
capable of having the required propertiesC. The corrosion-resistance of the proposed
weldmentD. None of the above
63. A change in a supplementary essential variable requires re-qualification, when notch-toughness is a consideration.
True or False (circle one)
64. When using Macro-examination of fillet weld tests, the weld and theHAZ must not reveal cracks when magnified at:A. 5XB. 2XC. 10XD. No magnification is required visual
examination is required, only
65. A non-essential variable may be changes without re-qualification because:
A. Nobody cares about non-essential variablesB. The welder is allowed to change variables at
his discretionC. Non-essential variables do not affect the
mechanical or notch-toughness propertiesD. Non-essential variables cannot be changes
without re-qualification
66. A WPS must only address essential and, if applicable,supplementary essential variables.
True Or False (circle one)
67. The data recorded on a PQR (non-editorial) may bechanged provided :
A. The AI approves
8/22/2019 ASME IX.questions Anwser
14/22
Professional Training and Consultation
8th Floor, Al-Subeaei Towers, King Abdulaziz cor. Prince Faisal Bin Fahd Streets, Al-Khobar, Saudi Arabia
TEL (966) 3 887 6633 FAX (966) 3 887 6565 [email protected] www.gotoitc.com
44
B. The test data on a PQR is a record of whatoccurred and should never be changed. Onlyeditorial information can be changed on a PQR.
C. The API 510 inspector approvesD. The date of the WPS is changed
68. Tension tests may be used in lieu of bend tests to qualify welders orwelding operators.
True or False (circle one)
69. A groove weld bend test reveals a linear indication on the face ofthe bend surface that measures exactly 1/8 long. No other
indications are seen. Does this coupon pass or fail?
A. PassB. Fail
70. Unless notch-toughness is a consideration, a qualification in anyposition qualifies a welding procedure for all positions.
True Or False (circle one)
71. The purpose of a WPS and PQR is to determine if a welder has theskill necessary to make sound production welds.
True Or False (circle one)
72. Welders can be qualified by radiograph when using P 6X materials?True Or False (circle one)
73. It is permissible to sub-contract welding of coupons as well as otherwork to prepare coupons.
True Or False (circle one)
74. Variable QW 402.4 for SMAW procedure qualification is a_____________ variable.
A. EssentialB. Non-essentialC. Supplemental essential
8/22/2019 ASME IX.questions Anwser
15/22
Professional Training and Consultation
8th Floor, Al-Subeaei Towers, King Abdulaziz cor. Prince Faisal Bin Fahd Streets, Al-Khobar, Saudi Arabia
TEL (966) 3 887 6633 FAX (966) 3 887 6565 [email protected] www.gotoitc.com
45
D. None of the above75. Variable QW 404.24 for SAW procedure qualification is an
______________variable.
A. EssentialB. Non-EssentialC. Supplemental essentialD. None of the above
76. Each manufacturer must certify the PQR (by signature) indicatingthat the information given is true and correct.
True Or False (circle one)
77. Welder variable QW-405.1 (for welder qualifying with the SMAWprocess) is a __________ variable.
A. EssentialB. Non-essentialC. Supplemental essentialD. None of the above
78. The purpose of a WPS and PQR is to determine if a proposedweldment to be used in construction is capable of providing the
required properties for the intended application.
True Or False (circle one)
79. A qualification in a 4G position qualifies a welder for all groove weldpositions.
True Or False (circle one)
80. A WPS must address all applicable non-essential variables.True Or False (circle one)
81. Groove weld coupons shall be tested by macro-examination whenqualifying a welding procedure.
True Or False (circle one)
8/22/2019 ASME IX.questions Anwser
16/22
Professional Training and Consultation
8th Floor, Al-Subeaei Towers, King Abdulaziz cor. Prince Faisal Bin Fahd Streets, Al-Khobar, Saudi Arabia
TEL (966) 3 887 6633 FAX (966) 3 887 6565 [email protected] www.gotoitc.com
46
82. A welding procedure must be qualified with impact tests only whenrequired by the applicable construction code, such as ASME VIIIDiv.1.
True Or False (circle one)
83. A welder qualified to weld in the 2G position on pipe would have tobe qualified in which of the additional positions to qualify for allposition groove welding on pipe?
A. 1GB. 2GC. 5GD. 6GE. All of the above
84. The maximum preheat temperature decrease allowed without re-qualification of a GMAW groove weld procedure is:
A. 500FB. 1000FC. 1250FD. 1500FE. None of the above
85. A welder is qualified to weld all thick nesses of material when:A. The test is any thickness above 3/8 inchB. The test thickness was inchC. The test thickness was inch or overD. The test pipe wall thickness was 5/8 inch and
nominal pipe size was over inches
86. What is the maximum defect permitted on the convex surface of awelder qualification bend test after bending except for corner cracksand corrosion resistant weld overlay?
A. inchB. 1/8 inchC. 1/16 inchD. 3/16 inchE. No defects are allowed
8/22/2019 ASME IX.questions Anwser
17/22
Professional Training and Consultation
8th Floor, Al-Subeaei Towers, King Abdulaziz cor. Prince Faisal Bin Fahd Streets, Al-Khobar, Saudi Arabia
TEL (966) 3 887 6633 FAX (966) 3 887 6565 [email protected] www.gotoitc.com
47
87. What period of inactivity from a given welding process requires thewelder to re-qualify in that process?
A. 3 monthsB. 6 monthsC. 9 monthsD. 12 monthsE. As stated by the AI
88. Notch-toughness requirements are mandatory:A. For heat treated metalsB. For quenched and tempered metalsC. For hardened and tempered metalsD. For annealed and tempered metalsE. When specified as required by the referencing
Code Section
89. A welder qualified for SMAW using an E7018 electrode is alsoqualified to weld with:
A. E7015B. E6011C. E6010D. E7024E. All of the above
90. Macro examination of an etched fillet weld section for performancequalification is acceptable if the examination shows:
A. Complete fusion and freedom from cracks,excepting linear indication not exceeding 1/32inch at the root.
B. Concavity or convexity no greater than 1/16inch
C. Not more than 1/8 difference in leg lengthsD. All of the aboveE. Both B and C above
8/22/2019 ASME IX.questions Anwser
18/22
Professional Training and Consultation
8th Floor, Al-Subeaei Towers, King Abdulaziz cor. Prince Faisal Bin Fahd Streets, Al-Khobar, Saudi Arabia
TEL (966) 3 887 6633 FAX (966) 3 887 6565 [email protected] www.gotoitc.com
48
91. Each manufacturer or contractor is responsible for the welding orbrazing done by his organization. Whenever these words are usedin Section IX, they shall include:
A. Designer or architectB. Designer or installerC. Architect or installerD. Installer or assemblerE. Assembler or designer
92. For P-11 materials, weld grooves for thick nesses________________ shall be prepared by thermal processes, whensuch processes are to be employed during fabrication.
A. Less than 5/8 inchB. 5/8 inchC. 1 inchD. 11/4 inchesE. None of the above
93. A SWPs may be used in lieu of a manufacturer qualified WPS when:A. Approved by the Inspectors SupervisorB. Allowed by ASME VC. One test coupon is tension tested per Article VD. Compliance to Article V and Appendix E of
ASME IX is shown
94. A change in a non-essential variable requires recertification of thePQR
True Or False (circle one)
95. Reduced-section tensile test specimens conforming to QW-462.1(b) may be used on all thicknesses of pipe having an outside
diameter greater than:
A. 2 inchesB. 21/2 inchesC. 3 inchesD. 31/2 inchesE. 4 inches
8/22/2019 ASME IX.questions Anwser
19/22
Professional Training and Consultation
8th Floor, Al-Subeaei Towers, King Abdulaziz cor. Prince Faisal Bin Fahd Streets, Al-Khobar, Saudi Arabia
TEL (966) 3 887 6633 FAX (966) 3 887 6565 [email protected] www.gotoitc.com
49
96. Groove weld test may be used for qualification of welders. Which ofthe following shall be used for evaluation?
A. Only bend testsB. Only radiographyC. Both radiography and bend testsD. Either bend tests or radiographyE. None of the above
97. Under which of the following conditions can a welder be qualifiedduring production work?
A. A 6 length of the first production groove weldmay be qualified by radiography
B. A bend test coupon may be cut from the first12 length of weldC. A macro examination may be taken from the
first 3 of weld lengthD. None of the above
98. Two plate tensile test specimens have been tested and found to beacceptable. The characteristics of each specimen are as follows:
Specimen 1: Width of 0.752; thickness of 0.875; ultimate tensile
value of 78.524 psi
Specimen 2: Width of 0.702; thickness of 0.852; ultimate tensile
value of 77,654 psi
What is the ultimate load for each specimen that was reported onthe laboratory report?
A. 51,668 & 46,445B. 67,453 & 56,443C. 78,524 & 77,654D. None of the above
99. Which of the following welding processes are currently notpermitted to be used with SWPs as referenced in Appendix E ofASME IX?
A. GMAWB. SAW
8/22/2019 ASME IX.questions Anwser
20/22
Professional Training and Consultation
8th Floor, Al-Subeaei Towers, King Abdulaziz cor. Prince Faisal Bin Fahd Streets, Al-Khobar, Saudi Arabia
TEL (966) 3 887 6633 FAX (966) 3 887 6565 [email protected] www.gotoitc.com
50
C. PAWD. All of the above
8/22/2019 ASME IX.questions Anwser
21/22
Professional Training and Consultation
8th Floor, Al-Subeaei Towers, King Abdulaziz cor. Prince Faisal Bin Fahd Streets, Al-Khobar, Saudi Arabia
TEL (966) 3 887 6633 FAX (966) 3 887 6565 [email protected] www.gotoitc.com
51
ANSWER KEY
1. C 52. C
2. D 53. D3. D 54. A4. D 55. C5. B 56. B6. B 57. D7. C 58. D8. C 59. A9. D 60. B10. B 61. A11. C 62. B12. C 63. True13. A 64. D14. C 65. C15. C 66. False16. B 67. B17. D 68. False18. B 69. Pass19. B 70. True20. B 71. False21. A 72. False22. B 73. False23. D 74. B24. B 75. A25. C 76. True26. A 77. A27. C 78. True28. C 79. False29. C 80. True30. C 81. False31. D 82. True32. C 83. C33. C 84. B34. B 85. C35. B 86. B36. A 87. B37. B 88. E38. B 89. E39. A 90. D40. D 91. D
8/22/2019 ASME IX.questions Anwser
22/22
Professional Training and Consultation
8th Floor Al-Subeaei Towers King Abdulaziz cor Prince Faisal Bin Fahd Streets Al-Khobar Saudi Arabia 52
41. C 92. A42. B 93. D43. B 94. False44. A 95. C45. B 96. D46. D 97. A47. B 98. A48. B 99. D49. C50. A51. A