ARZONA™ 125C is a clear film based on Polyethylene Terephtalate (PET) without coating on both sides. ARZONA™ 125C is characterized by its excellent robustness, excellent mechanical properties and low shrinkage. It is designed as core material for the manufacturing of backsheets for solar modules. LOW SHRINKAGE ARZONA TM 125C ClEAR 125 CORE PET μ
This document is posted to help you gain knowledge. Please leave a comment to let me know what you think about it! Share it to your friends and learn new things together.
Transcript
ARZONA™ 125C is a clear film based on Polyethylene Terephtalate (PET) without coating on both sides.
ARZONA™ 125C is characterized by its excellent robustness, excellent mechanical properties and low shrinkage. It is designed as core material for the manufacturing of backsheets for solar modules.
Low shrinkage
ARZONATM 125CClEAR 125 CORE PET μ
1.Typical properties
2. application information
2. application information
ProPerTY UniT VaLUe TesT MeThoD
Dimensions
Thickness µm 125 ASTM 374-D
Tolerance % 4
Weight g/m² 175 Internal Agfa method
Technical properties
Haze % <4 Hazeguard: Internal Agfa method
Tensile strength MD, standard conditions N/mm² >160 ASTM - D882
initial strain rate = 1mm/(mm*min)
Tensile strength TD, standard conditions N/mm² >175 ASTM - D882
initial strain rate = 1mm/(mm*min)
Elongation to break MD, standard conditions % >100 ASTM - D882
initial strain rate = 1mm/(mm*min)
Elongation to break TD, standard conditions % >100 ASTM - D882
initial strain rate = 1mm/(mm*min)
Surface energy 10-3N/m >45 Internal Agfa method
Partial discharge VDC >600 TUV IEC 60664-1
Breakdown voltage kV/mm >80 ASTM - D149 (1” diameter electrode in air)
Notes: This information is the best currently available. The supplied data should, however, only be regarded as a general guideline to material properties and not as a guarantee. Subject to technical modifications.