SNI ISO 10545-4:2010 Standar Nasional Indonesia
Ubin keramik - Bagian 4: Penentuan kuat lentur dan beban
lentur
Ceramic tiles - Part 4: Determination of modulus of rupture
and
breaking strength
(ISO 10545-4:2004, IDT)
ICS 91.100.20
Badan Standardisasi Nasional
-
Ha k C
i p t a Ba d a n S
t a n d a r d i s a s i Na s i o n a l , C
o p y s t a n d a r i n i d i b u a t u n t u k p e n a y a n g
a n d i we b s i t e d a n t i d a k u n t u k d i k o m
e r s i a l k a n
BSN 2011 BSN 2011 Hak cipta dilindungi undang-undang. Dilarang
menyalin atau menggandakan sebagian atau seluruh isi dokumen ini
dengan cara dan dalam bentuk apapun dan dilarang mendistribusikan
dokumen ini baik secara elektronik maupun tercetak tanpa izin
tertulis dari BSN
Hak cipta dilindungi undang-undang. Dilarang menyalin atau
menggandakan sebagian atau seluruh isi dokumen ini dengan cara dan
dalam bentuk apapun dan dilarang mendistribusikan dokumen ini baik
secara elektronik maupun tercetak tanpa izin tertulis dari BSN BSN
BSN Gd. Manggala Wanabakti Gd. Manggala Wanabakti Blok IV, Lt.
3,4,7,10. Blok IV, Lt. 3,4,7,10. Telp. +6221-5747043 Telp.
+6221-5747043 Fax. +6221-5747045 Fax. +6221-5747045 Email:
[email protected] Email: [email protected] www.bsn.go.id
www.bsn.go.id Diterbitkan di Jakarta Diterbitkan di Jakarta
-
Ha k C
i p t a Ba d a n S
t a n d a r d i s a s i Na s i o n a l , C
o p y s t a n d a r i n i d i b u a t u n t u k p e n a y a n g
a n d i we b s i t e d a n t i d a k u n t u k d i k o m
e r s i a l k a n
SNI ISO 10545-4:2010
i BSN 2010
Daftar isi
Daftar isii
Prakataiii
1 Ruang lingkup..1
2 Acuan normatif....1
3 Istilah dan definisi1
4 Prinsip
................................................................................................................................
3
5
Peralatan............................................................................................................................
3
6 Benda uji
............................................................................................................................
5
7 Prosedur
............................................................................................................................
7
8
Perhitungan........................................................................................................................
7
9 Laporan hasil uji
.................................................................................................................
9
Bibliografi
...............................................................................................................................
13
-
Ha k C
i p t a Ba d a n S
t a n d a r d i s a s i Na s i o n a l , C
o p y s t a n d a r i n i d i b u a t u n t u k p e n a y a n g
a n d i we b s i t e d a n t i d a k u n t u k d i k o m
e r s i a l k a n
SNI ISO 10545-4:2010
Content
Contenti...ii
Foreword.iv
1
Scope.................................................................................................................................
2
2 Normative references
........................................................................................................
2
3 Terms and definitions
........................................................................................................
2
4 Principle
.............................................................................................................................
4
5 Apparatus
..........................................................................................................................
4
6 Test
specimens..................................................................................................................
6
7 Procedure
..........................................................................................................................
8
8 Calculation
.........................................................................................................................
8
9 Test report
.......................................................................................................................
10
Bibliography...........................................................................................................................
14
ii BSN 2010
-
Ha k C
i p t a Ba d a n S
t a n d a r d i s a s i Na s i o n a l , C
o p y s t a n d a r i n i d i b u a t u n t u k p e n a y a n g
a n d i we b s i t e d a n t i d a k u n t u k d i k o m
e r s i a l k a n
SNI ISO 10545-4:2010
Prakata
Standar Nasional Indonesia (SNI) Ubin keramik Bagian 4:
Penentuan kuat lentur dan beban lentur ini merupakan hasil adopsi
identik dengan metode terjemahan (bilingual) dari ISO 10545-4:2004
Ceramic tiles Part 4: Determination of modulus of rupture and
breaking strength. Untuk tujuan ini telah dilakukan perubahan
editorial berikut: a) tanda titik telah diganti dengan tanda koma
dan sebaliknya untuk penulisan bilangan, b) istilah International
Standard diganti dengan National Standard dan diterjemahkan
menjadi standar nasional. SNI ini disusun sesuai dengan
ketentuan yang diberikan dalam Pedoman Standardisasi Nasional (PSN)
03.1, Adopsi Standar Internasional dan Publikasi Internasional
lainnya Bagian 1: Adopsi Standar Internasional menjadi SNI (ISO/IEC
Guide 21-1-2005, Regional or national adoption of international
Standards and other International Deliverables Part 1: Adoption of
International Standard, MOD) dan PSN 08:2007 Penulisan SNI. Standar
ini disusun oleh Panitia Teknis 81-01, Industri Kaca dan Keramik
dan telah dibahas dalam rapat konsensus lingkup panitia teknis di
Bandung pada tanggal 17 September 2008. Hadir dalam rapat tersebut
wakil dari pemerintah, produsen, konsumen, pakar akademis dan
peneliti serta instansi teknis terkait lainnya. SNI ini juga telah
melalui konsensus nasional yaitu pemungutan suara (voting) pada
tanggal 22 Januari 2010 s.d 22 Februari 2010. SNI ISO 10545,
terdiri dari 17 bagian dengan menggunakan judul secara umum Ubin
keramik : Bagian 1: Sampling and basis for acceptance, (akan
disusun) Bagian 2: Penentuan dimensi dan kenampakan Bagian 3:
Penentuan penyerapan air, keporian semu, densitas relatif semu,
densitas Bagian 4: Penentuan kuat lentur dan beban lentur Bagian 5:
Determination of impact resistance by measurement of coefficient of
restitution (akan disusun) Bagian 6: Penentuan ketahanan abrasi
untuk ubin tak berglasir Bagian 7: Penentuan ketahanan abrasi untuk
permukan ubin berglasir Bagian 8: Determination of linear thermal
expansion (akan disusun) Bagian 9: Determination of resistance to
thermal shock (akan disusun) Bagian 10: Determination of moisture
expansion (akan disusun) Bagian 11: Penentuan ketahanan retak
glasir untuk ubin berglasir Bagian 12: Determination of frost
resistance (akan disusun) Bagian 13: Penentuan ketahanan terhadap
kimia Bagian 14: Penentuan ketahanan terhadap noda Bagian 15:
Determination of lead and cadmium given off by glazed tiles (akan
disusun) Bagian 16: Determination of small colour differences (akan
disusun) Bagian 17: Determination of coefficient of friction (akan
disusun)
iii BSN 2010
-
Ha k C
i p t a Ba d a n S
t a n d a r d i s a s i Na s i o n a l , C
o p y s t a n d a r i n i d i b u a t u n t u k p e n a y a n g
a n d i we b s i t e d a n t i d a k u n t u k d i k o m
e r s i a l k a n
SNI ISO 10545-4:2010
Foreword
The National Indonesia Standard (SNI) Ceramic Ubin keramik
Bagian 4: Penentuan kuat lentur dan beban lentur is identical
adoption by translation method (bilingual) of ISO 10545-4:2004
Ceramic tiles Part 4: Determination of modulus of rupture and
breaking strength. For this purposed, the following editorial
change have been made: a) dot mark has been changed by comma and
vice versa for the number writing, b) terminology of International
Standard has been changed by National Standard and translated to be
national standard. The SNI was drafted accordance with the rules
given in the National Standardization Guide (PSN 03.1:2007),
Adoption of International Standards and Other International
Deliverables Part 1: Adoption of International Standards into SNI
and PSN 08:2007, SNI Writing. The SNI was prepared by Technical
Committee 81-01, Glass and Ceramic Industry and has been discussed
in consensus meeting for Technical Committees in Bandung on 17
September 2008. The meeting was attended by the representatives
from government, producer, consumer, academic expert, researcher,
and other related institution. This SNI has passed national which
is the voting conducted on 22 January 2010 until 22 February 2010.
SNI ISO 10545, consists of 17 parts with general title Ceramic
tiles: Part 1: Sampling and basis for acceptance, (will be
arranged) Part 2: Determination of dimension and surface quality
Part 3: Determination of water absorption, apparent porosity,
apparent relative density and bulk density. Part 4: Determination
of modulus of rupture and breaking strength Part 5: Determination
of impact resistance by measurement of coefficient of restitution
(will be arranged) Part 6: Determination of resistance to deep
abrasion for unglazed tiles. Part 7: Determination of resistance to
surface abrasion for glazed Part 8: Determination of linear thermal
expansion (will be arranged) Part 9: Determination of resistance to
thermal shock (will be arranged) Part 10: Determination of moisture
expansion (will be arranged) Part 11: Determination of crazing
resistance for glazed tiles Part 12: Determination of frost
resistance (will be arranged) Part 13: Determination of chemical
resistance Part 14: Determination of resistance to stains Part 15:
Determination of lead and cadmium given off by glazed tiles (will
be arranged) Part 16: Determination of small color differences
(will be arranged) Part 17: Determination of coefficient of
friction (will be arranged)
iv BSN 2010
-
Ha k C
i p t a Ba d a n S
t a n d a r d i s a s i Na s i o n a l , C
o p y s t a n d a r i n i d i b u a t u n t u k p e n a y a n g
a n d i we b s i t e d a n t i d a k u n t u k d i k o m
e r s i a l k a n
SNI ISO 10545-4:2010
v BSN 2010
Ubin keramik Bagian 4: Penentuan kuat lentur dan beban
lentur
1 Ruang lingkup Standar Nasional Indonesia ini menetapkan metode
uji untuk menentukan kuat lentur dan beban lentur ubin keramik.
CATATAN ISO 13006 memberikan sifat-sifat yang diperlukan untuk ubin
dan informasi berguna lainnya pada produk tersebut. 2 Acuan
normatif Dokumen acuan berikut sangat diperlukan untuk penggunaan
dokumen ini. Untuk acuan bertanggal, hanya edisi tersebut yang
digunakan. Untuk acuan tidak bertanggal, acuan dengan edisi
terakhir yang digunakan (termasuk semua amandemennya). ISO 48,
Rubber, vulcanized or thermoplastic Determination of hardness
(hardness between 10 IRHRD and 100 IRHD) 3 Istilah dan definisi 3.1
beban patah (breaking load) Fbl gaya yang diperlukan yang
menyebabkan benda uji patah, seperti terbaca pada alat ukur tekanan
CATATAN 1 Lihat 7.5 dan Gambar 2. CATATAN 2 Beban patah dinyatakan
dalam newton (N). 3.2 kekuatan patah (breaking strength) Fbs gaya
yang diperoleh dengan mengalikan beban patah dengan perbandingan
(jarak antara penumpu) / (lebar benda uji) CATATAN 1 Lihat
Persamaan (1) di Butir 8. CATATAN 2 Kekuatan patah dinyatakan dalam
newton (N).
1 dari 14
-
Ha k C
i p t a Ba d a n S
t a n d a r d i s a s i Na s i o n a l , C
o p y s t a n d a r i n i d i b u a t u n t u k p e n a y a n g
a n d i we b s i t e d a n t i d a k u n t u k d i k o m
e r s i a l k a n
SNI ISO 10545-4:2010
Ceramic tiles Part 4: Determination of modulus of rupture and
breaking strength
1 Scope This part of SNI ISO 10545 specifies a test method for
determining the modulus of rupture and breaking strength of all
ceramic tiles. NOTE ISO 13006 provides property requirements for
tiles and other useful information on these products. 2 Normative
references The following referenced documents are indispensable for
the application of this document. For dated references, only the
edition cited applies. For undated references, the latest edition
of the referenced document (including any amendments) applies. ISO
48, Rubber, vulcanized or thermoplastic Determination of hardness
(hardness between 10 IRHRD and 100 IRHD) 3 Terms and definitions
For the purposes of this document, the following terms and
definitions apply. 3.1 breaking load Fbl Force necessary to cause
the test specimen to break, as read from the pressure gauge NOTE 1
See 7.5 and Figure 2. NOTE 2 The breaking load is expressed in
newtons. 3.2 breaking strength Fbs Force obtained by multiplying
the breaking load by the ratio (span between support rods)/(width
of the test specimen) NOTE 1 See Equation (1) in Clause 8. NOTE 2
The breaking strength is expressed in newtons.
2 dari 14 BSN 2010
-
Ha k C
i p t a Ba d a n S
t a n d a r d i s a s i Na s i o n a l , C
o p y s t a n d a r i n i d i b u a t u n t u k p e n a y a n g
a n d i we b s i t e d a n t i d a k u n t u k d i k o m
e r s i a l k a n
SNI ISO 10545-4:2010
3.3 modulus lentur (modulus of rupture) Fbl nilai yang diperoleh
dengan membagi hasil perhitungan kekuatan patah oleh luas pada
tebal minimal sepanjang sisi yang patah CATATAN 1 Lihat Persamaan
(2) di Butir 8. CATATAN 2 Modulus lentur dinyatakan dalam newton
per milimeter persegi (N/mm2). 4 Prinsip Penentuan beban patah,
kekuatan patah dan modulus lentur ubin dinyatakan oleh gaya yang
bekerja pada laju tertentu di tengah-tengah ubin. Pastikan bahwa
titik tumpu harus kontak dengan permukaan ubin dengan baik. 5
Peralatan 5.1 Oven pengering, mampu dioperasikan pada 110 C 5 C.
Microwave, infra merah atau sistem pengering lainnya dapat
digunakan apabila hasil yang didapatkan sama. 5.2 Alat pengukur
tekanan, akurasinya hingga 2 %. 5.3 Dua batang silinder penumpu,
terbuat dari logam, bagian-bagian yang kontak dengan benda uji
terbungkus karet yang mempunyai kekerasan 50 IRHD 5 IRHD,,
pengukuran dilakukan sesuai dengan ISO 48. Satu batang harus berada
pada porosnya (lihat Gambar 1) dan batang lainnya harus dapat
sedikit berputar pada porosnya (Lihat Tabel 1 untuk penyesuaian
dimensi). 5.4 Batang silinder tengah, diameter sama dengan
batang-batang penumpu lain (5.3) dan terbungkus karet yang sama,
untuk transmisi beban Fbl. Batang ini juga harus berada pada
porosnya (lihat Gambar 1). (Lihat Tabel 1 untuk penyesuaian
dimensi).
Gambar 1 - Pergerakan batang penumpu yang diijinkan
3 dari 14 BSN 2010
-
Ha k C
i p t a Ba d a n S
t a n d a r d i s a s i Na s i o n a l , C
o p y s t a n d a r i n i d i b u a t u n t u k p e n a y a n g
a n d i we b s i t e d a n t i d a k u n t u k d i k o m
e r s i a l k a n
SNI ISO 10545-4:2010
3.3 modulus of rupture Fbl quantity obtained by dividing the
calculated breaking strength by the square by the square of the
minimum thickness along the broken edge NOTE 1 See Equation (2) in
Clause 8. NOTE 2 The modulus of rupture is expressed in newtons per
square millimetre. 4 Principle Determination of the breaking load,
breaking strength and modulus of rupture of a tile by applying a
force at a specified rate to the centre of the tile, the point of
application being in contact with the proper surface of the tile. 5
Apparatus 5.1 Drying oven, capable of being operated at (110 5) C.
Microwave, infrared or other drying systems may be used provided
that it has been determined that equal results are obtained. 5.2
Recording pressure gauge, accurate to 2,0 %. 5.3 Two cylindrical
support rods, made of metal, the parts in contact with the test
specimens being covered with rubber having a hardness of (50 5)
IRHD, measured in accordance with ISO 48. One rod shall be slightly
pivotable (see Figure 1) and the other shall be slightly rotatable
about its own axis. (See Table 1 for relevant dimensions). 5.4
Central cylindrical rod, of the same diameter as the support rods
(5.3) and covered with the same rubber, for transmission of the
load Fbl. This rod shall also be slightly pivotable (see Figure 1).
(See Table 1 for relevant dimensions).
Figure 1 - Allowable movement of rods
4 dari 14 BSN 2010
-
Ha k C
i p t a Ba d a n S
t a n d a r d i s a s i Na s i o n a l , C
o p y s t a n d a r i n i d i b u a t u n t u k p e n a y a n g
a n d i we b s i t e d a n t i d a k u n t u k d i k o m
e r s i a l k a n
SNI ISO 10545-4:2010
Tabel 1 - Diameter batang penumpu, d, ketebalan karet, t, dan
bagian ubin yang menutup sisi batang penumpu l1
(lihat Gambar 2)
Dimensi dalam milimeter Dimensi ubin
L
Diameter batang penumpu
d
Ketebalan karet t
Bagian ubin yang menutup sisi batang
penumpu l1
18 L < 48 48 L < 95
L 95
5 10 20
1 0,2 2,5 0,5
5 1
2 5
10
Keterangan gambar: Fbl beban patah (breaking load) l1 bagian
ubin yang menutup sisi batang penumpu l2 jarak antara dua batang
penumpu L dimensi ubin t ketebalan karet d diameter batang
penumpu
Gambar 2 - Penggunaan beban pada benda uji 6 Benda uji 6.1 Pilih
benda uji secara acak dari lot yang akan diuji. Apabila
memungkinkan, yang harus diuji adalah ubin utuh. Untuk ubin
berukuran sisi-sisinya di atas 300 mm dapat dilakukan pemotongan
dan untuk beberapa yang bentuknya tidak empat persegi panjang,
sehingga dapat dipasang pada alat uji. Benda uji empat persegi
panjang yang besar, dipotong pada bagian tengah, yang merupakan
bagian pusat atau titik tengah ubin. Dalam hal masih meragukan,
hasil yang diperoleh dari ubin yang utuh lebih dipilih dari hasil
ubin yang dipotong. 6.2 Jumlah minimal benda uji untuk setiap
contoh sesuai Tabel 2.
5 dari 14 BSN 2010
-
Ha k C
i p t a Ba d a n S
t a n d a r d i s a s i Na s i o n a l , C
o p y s t a n d a r i n i d i b u a t u n t u k p e n a y a n g
a n d i we b s i t e d a n t i d a k u n t u k d i k o m
e r s i a l k a n
SNI ISO 10545-4:2010
Table 1 - Diameter of rods, d, thickness of rubber, t, and
overlap of tile beyond the edge supports l1
(see Figure 2)
Dimensions in millimetres Dimension of
tile L
Diameter of rod
d
Thickness of rubber
t
Overlap of tile beyond the edge supports
l1 18 L < 48 48 L < 95
L 95
5 10 20
1 0,2 2,5 0,5
5 1
2 5
10
Figure 2 Application of load to test specimen
6 Test specimens
6.1 Select the specimens at random from the lot to be tested.
Whenever possible, whole tiles shall be tested. However, it may be
necessary to cut exceptionally large tiles (that is, those greater
than 300 mm in length) and some non-rectangular shapes in order to
fit them in the apparatus. Rectangular test specimens of the
largest possible size shall then be cut, having their centres
coinciding with the centres of the tiles. In case of doubt, results
obtained using whole tiles shall always be preferred to results
obtained with cut tiles.
6.2 The minimum number of test specimens for each sample is
given in Table 2.
6 dari 14 BSN 2010
-
Ha k C
i p t a Ba d a n S
t a n d a r d i s a s i Na s i o n a l , C
o p y s t a n d a r i n i d i b u a t u n t u k p e n a y a n g
a n d i we b s i t e d a n t i d a k u n t u k d i k o m
e r s i a l k a n
SNI ISO 10545-4:2010
Tabel 2 - Jumlah minimal benda uji
Dimensi ubin L
mm
Jumlah minimal benda uji
18 L < 48 L 48
10 7
7 Prosedur 7.1 Bersihkan semua kotoran partikel yang melekat
pada seluruh permukaan ubin depan, belakang, atas dan bawah benda
uji dengan kuas kaku. Keringkan setiap benda uji di dalam oven
(5.1) pada 110 C 5 C hingga didapatkan berat yang tetap, jika
perbedaan antara dua penimbangan berturut-turut pada interval 24
jam kurang dari 0,1 %. Benda uji dapat didinginkan dalam oven
tertutup atau dalam desikator berisi silika gel atau desikan
lainnya yang sesuai, tapi tidak mengandung asam, sampai tercapai
suhu kamar. Benda uji harus diuji tidak lebih dari 3 jam setelah
suhu kamar tercapai. 7.2 Tempatkan benda uji pada batang penumpu
(5.3) dengan permukaan yang berglasir ditempatkan di bagian atas
dengan memperhitungkan panjang, l1, benda uji (lihat Tabel 1 dan
Gambar 2) melebihi masing-masing batang penumpu.
7.3 Dalam hal ubin yang dapat dibalik, seperti ubin mosaik tak
berglasir, tidak masalah sisi ubin mana yang berada paling atas.
Untuk ubin yang diekstrusi, tempatkan benda uji secara melintang
tegak lurus terhadap batang penumpu. Untuk ubin empat persegi
panjang lainnya, tempatkan benda uji sehingga sisi terpanjang, L,
berada tepat pada sudut-sudut batang-batang penumpu. 7.4 Untuk
ubin-ubin dengan permukaan bertekstur, tempatkan karet pada lapisan
kedua dengan ketebalan sesuai Tabel 1, pada batang penumpu tengah
(5.4) yang menyentuh permukaan bertekstur. 7.5 Posisi batang
penumpu tengah sama jaraknya terhadap dua batang penumpu yang lain.
Pasang beban sehingga laju kenaikan tekanan yang didapat 1
N/(mm2.s) 0,2 N/(mm2.s); laju awal per detik dapat dihitung dari
Persamaan (2) di Butir 8. Catat beban patah Fbl. 8 Perhitungan
Untuk menghitung beban lentur dan modulus lentur hanya digunakan
hasil benda uji yang patah di bagian tengah dengan posisi patahan
di area diameter batang penekan. Minimal lima hasil yang dapat
diterima diperlukan untuk menghitung nilai rata-rata (mean). Jika
hasil yang dapat diterima kurang dari lima, contoh uji kedua harus
diuji yang terdiri dari dua kali jumlah ubin semula. Minimal 10
hasil yang dapat diterima digunakan untuk menghitung nilai
rata-rata (average).
7 dari 14 BSN 2010
-
Ha k C
i p t a Ba d a n S
t a n d a r d i s a s i Na s i o n a l , C
o p y s t a n d a r i n i d i b u a t u n t u k p e n a y a n g
a n d i we b s i t e d a n t i d a k u n t u k d i k o m
e r s i a l k a n
SNI ISO 10545-4:2010
Table 2 - Minimum number of test specimens
Dimension of tile L
mm
Minimum number of test specimens
18 L < 48 L 48
10 7
7 Procedure 7.1 Remove any loosely adhering particles from the
back of each test specimen with a stiff brush. Dry each test
specimen in the oven (5.1) maintained at (110 5) C until constant
mass is reached, i.e. when the difference between two successive
weighings at intervals of 24 h is less than 0,1 %. The test
specimens may be cooled in the closed oven or in a desiccator oven
silica gel or another suitable desiccant, but not over an acid,
until they reach room temperature. Test specimens shall be tested
no later than 3 h after they have reached room temperature. 7.2
Place a test specimen on the support rods (5.3) with the glazed or
proper surface uppermost so that the test specimen projects by a
length l1 (see Table 1 and Figure 2) beyond each support rod. 7.3
In the case of reversible tiles, such as unglazed ceramic mosaic
tiles, it does not matter which side of the tile is uppermost. For
extruded tiles, place the test specimen so that the projecting ribs
are at right angles to the support rods. For all other rectangular
tiles, place the test specimens so that the longer side, L, is at
right angles to the support rods. 7.4 For tiles with a relief
surface, place a second layer of rubber, of the appropriate
thickness given in Table 1, on the central rod (5.4) in contact
with the relief surface. 7.5 Position the central rod equidistant
between the support rods. Apply the load evenly in such a way as to
obtain a rate of increase in stress of (1 0,2) N/mm2 per second;
the actual rate per second can be calculated by Equation (2) given
in Clause 8. Record the breaking load Fbl. 8 Calculation Use only
the results for test specimens that break within a central portion
of length equivalent to the diameter of the central rod to
calculate the mean breaking strength and the mean modulus of
rupture. A minimum of five acceptable results is necessary to
calculate the mean value. If there are fewer than five acceptable
results, a second sample shall be tested consisting of twice the
number of tiles. A minimum of 10 acceptable results is then
required to calculate the average value.
8 dari 14 BSN 2010
-
Ha k C
i p t a Ba d a n S
t a n d a r d i s a s i Na s i o n a l , C
o p y s t a n d a r i n i d i b u a t u n t u k p e n a y a n g
a n d i we b s i t e d a n t i d a k u n t u k d i k o m
e r s i a l k a n
SNI ISO 10545-4:2010
9 dari 14 BSN 2010
Kekuatan lentur (breaking strength) Fbs, dinyatakan dalam newton
(N), dihitung dengan Persamaan (1)
blFF blbs 2= (1)
Keterangan: Fbl adalah beban patah, dinyatakan dalam newton (N);
l2 adalah jarak antara dua batang penumpu, dinyatakan dalam
milimeter (mm) (lihat Gambar 2); b adalah lebar benda uji,
dinyatakan dalam milimeter (mm); Modulus lentur Fbl, dinyatakan
dalam newton per milimeter persegi (N/mm2), dihitung dari Persamaan
(2)
22
23bhlFF blbl =
223hFbs= (2)
Keterangan: Fbl adalah beban patah, dinyatakan dalam newton (N);
l2 adalah jarak antara dua batang penumpu, dinyatakan dalam
milimeter (mm) (lihat Gambar 2); b adalah lebar benda uji,
dinyatakan dalam milimeter (mm); h adalah ketebalan minimal benda
uji, dinyatakan dalam milimeter (mm), diukur setelah diuji
sepanjang sisi yang patah. Perhitungan modulus lentur didasarkan
pada bagian potongan melintang yang empat persegi panjang. Dalam
hal ini, ketebalan sepanjang sisi yang patah bervariasi. Tekstur
yang dangkal, lebih pasti untuk pendekatan. Catat semua hasil
pengukuran individu. Hitung rata-rata (mean) kekuatan lentur dan
modulus lentur benda uji sebagai hasil rata-rata (mean) yang dapat
diterima. 9 Laporan hasil uji Laporan hasil uji harus memberikan
informasi berikut: a) acuan untuk bagian SNI ISO 10545 (SNI ISO
10545-4:2004) b) uraian ubin, termasuk permukaan bertekstur, jika
ada;
-
Ha k C
i p t a Ba d a n S
t a n d a r d i s a s i Na s i o n a l , C
o p y s t a n d a r i n i d i b u a t u n t u k p e n a y a n g
a n d i we b s i t e d a n t i d a k u n t u k d i k o m
e r s i a l k a n
SNI ISO 10545-4:2010
10 dari 14 BSN 2010
The breaking strength Fbs, expressed in newtons, is calculated
by means of Equation (1)
blFF blbs 2= (1)
where
Fbl is the breaking load, expressed in newtons; l2 is the span,
expressed in millimetres, between the support rods (see Figure 2);
b is the width, expressed in millimetres, of the test specimen;
The modulus of rupture Fbl, expressed in newtons per square
miilimetre, is calculated by means of Equation (2)
22
23bhlFF blbl =
223hFbs= (2)
where
Fbl is the breaking load, expressed in newtons; l2 is the span,
expressed in millimetres, between the support rods (see Figure 2);
b is the width, expressed in millimetres, of the test specimen; h
is the minimum thickness of the test specimen, expressed in
millimetres, measured after
the test along the broken edge. The calculation of the modulus
of rupture is based on a rectangular cross-section. In the case of
tiles with variable thickness along the broken edge, approximate
results only are produced. The shallower the relief, the more exact
are the approximations. Record all individual results. Calculate
the mean breaking strength and the mean modulus of rupture of the
sample as the mean of the acceptable results. 9 Test report
The test report shall include the following information: a)
reference to this part of SNI ISO 10545 (SNI ISO 10545-4:2004); b)
description of the tiles, including relief surface, if any;
-
Ha k C
i p t a Ba d a n S
t a n d a r d i s a s i Na s i o n a l , C
o p y s t a n d a r i n i d i b u a t u n t u k p e n a y a n g
a n d i we b s i t e d a n t i d a k u n t u k d i k o m
e r s i a l k a n
SNI ISO 10545-4:2010
c) jumlah benda uji; d) nilai d, t, l, dan l2 (lihat Gambar 2);
e) beban patah Fbl setiap benda uji; f) nilai rata-rata (mean)
beban patah; g) kekuatan lentur Fbs setiap benda uji; h) nilai
rata-rata (mean) kekuatan lentur; i) modulus lentur Fbl setiap
benda uji; j) nilai rata-rata (mean) modulus lentur.
11 dari 14 BSN 2010
-
Ha k C
i p t a Ba d a n S
t a n d a r d i s a s i Na s i o n a l , C
o p y s t a n d a r i n i d i b u a t u n t u k p e n a y a n g
a n d i we b s i t e d a n t i d a k u n t u k d i k o m
e r s i a l k a n
SNI ISO 10545-4:2010
c) number of test specimens in the sample; d) the values of d,
t, l1 and l2 (see Figure 2); e) the breaking load Fbl of each test
specimen; f) the mean breaking load; g) the breaking strength Fbs
of each test specimen; h) the mean value of the breaking stength;
i) the modulus of rupture Fbl of each test specimen; j) the mean
value of the modulus of rupture.
12 dari 14 BSN 2010
-
Ha k C
i p t a Ba d a n S
t a n d a r d i s a s i Na s i o n a l , C
o p y s t a n d a r i n i d i b u a t u n t u k p e n a y a n g
a n d i we b s i t e d a n t i d a k u n t u k d i k o m
e r s i a l k a n
SNI ISO 10545-4:2010
Bibliografi ISO 13006, Ceramic tiles Definitions,
classification, characteristics and marking
13 dari 14 BSN 2010
-
Ha k C
i p t a Ba d a n S
t a n d a r d i s a s i Na s i o n a l , C
o p y s t a n d a r i n i d i b u a t u n t u k p e n a y a n g
a n d i we b s i t e d a n t i d a k u n t u k d i k o m
e r s i a l k a n
SNI ISO 10545-4:2010
14 dari 14 BSN 2010
Bibliography ISO 13006, Ceramic tiles Definitions,
classification, characteristics and marking
Ubin keramik - Bagian 4:Ceramic tiles - Part 4: Determination of