· 2018-06-18 · MEP Shanghai Co., Ltd. T80, 15F, Shanghai World Financial Center, 100 Century Avenue Pudong New Area, Shanghai 200120, China TEL: +86-21-6841-1040 FAX: +86-21-6841-0577

Environment-friendly paper use http://www.m-ep.co.jp/

Polycarbonate Resin

Polycarbonate Resin

Polycarbonate Resin

High Performance Polyamide Resin

Polybutylene Terephthalate Resin

Polyacetal Resin

Modified PPE Resin

Modified PPE Resin

List No. H-11768-530C-0422018.03 500 DRIX

Head Office 9-2, Higashi-Shinbashi 1-chome, Minato ward, Tokyo 105-0021, Japan TEL: +81-3-6274-9000　FAX: +81-3-6274-9080

Technical Center

China(Hong Kong)

(Guangzhou)

(Shanghai)

(Beijing)

(Chengdu)

(Wuhan)

(Qingdao)

Taiwan

Singapore

Indonesia

India

Thailand

U.S.A.

Germany

Netherlands

6-2, Higashiyawata 5-chome, Hiratsuka, Kanagawa 254-0016, JapanTEL: +81-463-21-8610　FAX: +81-463-21-8631

MEP Hong Kong LimitedRm 1501-02, 15th Floor, World Trade Centre, 280 Gloucester RoadCauseway Bay, Hong KongTEL: +852-2536-4295　FAX: +852-2868-4718MEP Guangzhou LimitedRm 3311, 33rd Floor, Block B, China Shine PlazaNo.3-15, Linhe Xi Road, Guangzhou 510610, ChinaTEL: +86-20-8527-6246　FAX: +86-20-8527-2090MEP Guangzhou Customer Support CenterRm 3311, 33rd Floor, Block B, China Shine PlazaNo.3-15, Linhe Xi Road, Guangzhou 510610, ChinaTEL: +86-20-8527-6246　FAX: +86-20-8527-2090MEP Shanghai LimitedT80, 15F, Shanghai World Financial Center, 100 Century AvenuePudong New Area, Shanghai 200120, ChinaTEL: +86-21-6841-1025　FAX: +86-21-6841-0577MEP Shanghai Co., Ltd.T80, 15F, Shanghai World Financial Center, 100 Century AvenuePudong New Area, Shanghai 200120, ChinaTEL: +86-21-6841-1040　FAX: +86-21-6841-0577MEP Shanghai Customer Support CenterT80, 15F, Shanghai World Financial Center, 100 Century AvenuePudong New Area, Shanghai 200120, ChinaTEL: +86-21-6841-1025　FAX: +86-21-6841-0577MEP Technical Center China55 Muhua Road, SCIP, Shanghai 201507, ChinaTEL:+86-21-3127-3366　FAX:+86-21-3127-5775MEP Shanghai Co., Ltd. Beijing BranchRm 715, 7th Floor, Beijing Development Building, No.5, North Rd of East 3rd Ring Rd, Chaoyang District, Beijing 100004, ChinaTEL: +86-10-6590-9781　FAX: +86-10-6590-9786MEP Shanghai Co., Ltd. Chengdu BranchRm 03-A, 16th Floor, Tower 1, Plaza Central, 8 Shuncheng DajieChengdu 610016, ChinaTEL: +86-28-8672-5033　FAX: +86-28-8672-0876MEP Shanghai Co., Ltd. Wuhan BranchRm 1109, Tower 1, New World Trade Tower, No.568 JianShe AvenueJiangHan District, WuHan 430022, ChinaTEL: +86-27-5935-3604　FAX: +86-27-5935-3603MEP Shanghai Co., Ltd. Qingdao BranchRm 2810, Building 1, Yihe International, No.10 Xianggangzhong RoadQingdao 266071, ChinaTEL: +86-532-8502-6502　FAX: +86-532-8502-6531MEP Taiwan Limited5F-1, No.129, Sec. 2, Zhongshan N. Road, Zhongshan DistrictTaipei City 104, TaiwanTEL: +886-2-2521-2009　FAX: +886-2-2521-2039MEP Singapore Pte Ltd10 Shenton Way, #11 - 03/04 Mas Building, Singapore 079117TEL: +65-6223-3002　FAX: +65-6223-3920MEP Singapore Pte Ltd Jakarta Representative OfficeWisma Metropolitan 1, 7th Floor, JI. Jend. Sudirman Kav. 29-31Jakarta 12920, IndonesiaTEL: +62-21-522-9669　FAX: +62-21-522-9779MEP India Pvt. Ltd.Unit No.205, 2nd Floor, East Wing, Worldmark 1, Asset No.11, Aerocity New Delhi 110037, IndiaTEL: +91-11-4233-3000　FAX: +91-11-4233-3015MEP India Pvt. Ltd. ［Chennai Office］The Executive Centre, Unit No.35, Level 5, North Block, Tamarai Tech ParkS.P.Plot No.16-19 & 20A, Thiru Vi ka Industrial Estate, Inner Ring Road, GuindyChennai 600032, India　TEL: +91-44-4065-2803　FAX: +91-44-4065-2526

MEP Engineering-Plastics (Thailand) Co., Ltd.Emporium Tower, Floor 24/4-8, 622 Sukhumvit Road, Klongton KlongtoeyBangkok 10110, ThailandTEL: +66-2-261-9260　FAX: +66-2-261-9273MEP Technical Center Asia Ltd.700/458 Moo 7, Amata Nakorn Industrial Estate, Tambol DonhuarohAmpher Muangchonburi, Chonburi 20000, ThailandTEL: +66-38-717-062/063　FAX: +66-38-717-295MEP America, Inc. 790 Welch Road, Commerce Township, MI 48390, U.S.A.TEL: +1-248-669-6418　FAX: +1-248-669-6419MEP America, Inc. San Diego OfficeE-mail: [email protected]

MEP Europe GmbHWillstatterstr.30, 40549, Duesseldorf, GermanyTEL: +49-211-520542-0　FAX: +49-211-520542-72MEP Europe B.V.Technical Center at Chemelot Site, Gate 2, Building 82, Urmonderbaan 20A6167 RD Geleen, The NetherlandsTEL: +31-46-70-22046　FAX: +31-46-41-06999

NOTE

CONTENTSPolycarbonate Resin

1Polycarbonate Resin

15Polycarbonate Resin

17High Performance Polyamide Resin

19Polybutylene Terephthalate Resin

23Polyacetal Resin

29Modified PPE Resin

33Modified PPE Resin

37

●　The values described are typical values only.　●　The usage examples indicated here do not guarantee results applicable to relevant uses of the products.　●　It is the users' responsibility to investigate industrial property rights and the terms of use related to the uses and applications 　

indicated here.　●　For the handling (transport, storage, forming, disposal, etc.) of the products, it is advisable to refer to technical documents and

the Safety Data Sheet (SDS) of the proper materials and grades. Please contact us for consultations when the products are used for the purpose of food containers and packaging, medical parts, safety equipment, and toys for children.

　●　In Japan, the colored products of each grade may contain chemicals subject to reporting requirements under the applicable

law provided in Appendix 9 of Article 18-2 of the Enforcement Order, under Article 57-2 of the Industrial Safety and Health Act. For details, please contact us.

　●　For the export of our products and products incorporated with our products, please comply with the relevant laws and

regulations, such as the Foreign Exchange and Foreign Trade Law.　●　Please note that because of the chemical substance management systems in each country, the chemicals used in our products

are subject to control, and separate applications might be required or are banned from imports and exports. It is advisable to inquire about the status of regulations in the relevant countries if you are exporting or importing our products.

Electric and electronic fields, automobiles, OA, precision instruments, building materials....etc. Amid the dynamic, converging technological movements of high-tech industries, we respond to the diverse, advanced needs of the engineering plastics field. In order to meet these needs, Mitsubishi Engineering-Plastics Corporation was established with a global perspective of the engineering plastics market.

We offer a wide selection of general purpose engineering plastics and super engineering plastics which is unique in the world. We supply basic resins and polymer compounds. Given our background in material development and application development, we offer rapid and effective support for users through our extensive service system.

Our motto is, “ We respond to the needs of industry in a comprehensive way. ”

At the Mitsubishi Engineering-Plastics Technical Center, high-performance materials are developed and new applications are perfected. In addition, the Technical Center utilizes various kinds of simulation and design. Experimental production is used to provide the basis of our customer's manufacturing processes.

Mitsubishi Engineering-Plastics has a head office, two branches, a sales office, and a Technical Center in Japan. We also have many sales and technical service bases around the world. These offices are linked to information networks which provide users with quick response and efficient service to meet all of their needs.

RELIABILITY AND VERSATILITY. . . . THE ORGANIZATION

THE CHALLENGE OFFERED BY NEW POSSIBILITIES. . . THE TECHNICAL CENTER

RESPONDING TO YOUR NEEDS IN DIVERSE WAYS

SAE Approved for Lens of glasses

EFR2150 EFR2151H EFR3000 EFT3200 EFT3200H EMT3150 EMT3150H EMT3100 EFT2200 ML200 ML300 ML400 CLV1000 CLS1000 CLS400 CLS3400

Non Br & Non POpaque



Non Br & Non PClear

Non Br & Non PClear

High Flowability

Non Br & Non PClear

Non Br & Non PClear

High Flowability

Non Br & Non PClear

Non Br & Non PClear

Extrusion

MediumViscosity Low Viscosity High Flowability High Viscosity

Correcting glassHigh ViscosityLight stabilized

High ViscosityLight stabilized

Low ViscositySunglasses

1.19 1.19 1.19 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20

- - - - - - - - - - - - - - - -

0.24 0.24 0.24 0.24 0.24 0.24 0.24 0.24 0.24 0.24 0.24 0.24 0.24 0.24 0.24 0.24

9 15 22 7 12 4 7 3 5 9.5 16 31 7.9 5.3 8.0 15.0

8 14 21 8 11 4 7 3 5 8.8 15 30 7.4 5.0 7.5 14.0

300 300 300 300 300 300 300 300 300 300 300 300 300 300 300 300

1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20

0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7

0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7

2300 2300 2300 2400 2300 2300 2300 2300 2400 2500 2500 2500 2400 2400 2400 2400

61 62 61 62 62 64 63 64 63 63 62 64 60 60 60 62

4.7 6.5 4.7 6.5 6.5 6 6 5.8 6 6.8 6.6 4.9 5.5 5.4 5.5 6.7

67 115 67 100 100 65 90 56 100 116 121 80 105 108 105 119

- - - - - - - - - - - - - - - -

- - - - - - - - - - - - - - - -

- - - - - - - - - - - - - - - -

92 93 92 93 93 99 93 100 97 91 91 99 93 93 93 93

2500 2500 2500 2400 2300 2400 2400 2400 2350 2300 2300 2300 2300 2300 2300 2300

NB NB NB NB NB NB NB NB NB NB NB NB NB NB NB NB

75 65 50 16 14 67 65 58 70 76 64 9 84 88 84 67

125 126 125 124 122 122 122 125 125 125 124 123 131 131 131 124

137 140 137 136 135 135 135 136 136 138 139 135 145 145 145 139

6.6E-05 6.6E-05 6.6E-05 6.5E-05 6.5E-05 6.5E-05 6.5E-05 6.5E-05 6.5E-05 6.3E-05 6.3E-05 6.3E-05 6.5E-05 6.5E-05 6.5E-05 6.5E-05

6.7E-05 6.6E-05 6.7E-05 6.6E-05 6.6E-05 6.6E-05 6.6E-05 6.6E-05 6.6E-05 7.3E-05 7.3E-05 7.3E-05 6.6E-05 6.6E-05 6.6E-05 6.6E-05

V-0 (1.5mm) V-0 (1.5mm) V-0 (1.0mm) V-0 (2mm) V-0 (2.0mm) V-0 (1.5mm) V-0 (1.5mm) V-0 (1.0mm) V-0(2.0mm) V-1(1.5mm) - - - - - - -

3.1 3.1 3.1 - - - - - - 3.1 3.1 3.1 3.1 3.1 3.1 3.1

3.1 3.1 3.1 - - - - - - 3.1 3.1 3.1 3.1 3.1 3.1 3.1

0.0006 0.0006 0.0006 - - - - - - 0.0007 0.0007 0.0007 0.0006 0.0006 0.0006 0.0006

0.0090 0.0090 0.0090 - - - - - - 0.0090 0.0090 0.0090 0.0090 0.0090 0.0090 0.0090

3.E+14 3.E+14 3.E+14 3.E+14 3.E+14 3.E+14 3.E+14 3.E+14 3.E+14 3.E+14 3.E+14 3.E+14 3.E+14 3.E+14 3.E+14 3.E+14

6.E+15 6.E+15 6.E+15 6.E+15 6.E+15 6.E+15 6.E+15 6.E+15 6.E+15 4.E+15 4.E+15 4.E+15 6.E+15 6.E+15 6.E+15 6.E+15

31 31 31 - - - - - - 31 31 31 31 31 31 31

- - - - - - - - - - - - - - - -

18 18 18 - - - - - - 17 17 17 18 18 18 18

- - - 3 3 3 3 3 - - - - - - - -

EFR2150U(UV stabilized)

EFR2151HU(UV stabilized)

EFT3200U(UV Stabilized)

EFT3200HU(UV Stabilized)

EMT3150U(UV Stabilized)

EMT3150HU(UV Stabilized)

EMT3100U(UV Stabilized)

EFT2200U(UV Stabilized)

Cut UV ofunder 380nm

at 3mmt


at 3mmt


at 3mmt


at 3mmt

Iupilon is a polycarbonate resin with more than 30 successful years on the market. Used in a wide range of industries, including sports equipment, medical equipment, automobiles, optics, machinery, office automation equipment, and electronics, Iupilon has a reputation for reliability with users. In addition, Mitsubishi Engineering-Plastics backs up Iupilon with superior technical service and an abundance of application data.

Special features:1. Superior impact strength2. Superior transparency3. Usability in a wide range of temperatures: -40degC to

120degC4. Excellent precision molding properties and dimensional

stability

5. Superior self-extinguishing properties6. Excellent weather resistance7. Excellent electrical insulation capabilities

Polycarbonate Resin

Basic Flame Retardant

H-4000 H-3000 H-2000 S-3000 S-2000 S-1000 E-2000 FPR3000 FPR3500 FPR4500

Optical Disk High Flowability High Flowability Low Viscosity Medium Viscosity High Viscosity Extrusion

Phosphoric acidOpaque

High Flowability


High Flowability


High Flowability

1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.19 1.19

- - - - - - - - - -

0.24 0.24 0.24 0.24 0.24 0.24 0.24 0.24 0.24 0.24

63 30 22 15 10 7.5 5.3 19 18 27

60 28 20 14 9 7.1 5.0 18 17 26

300 300 300 300 300 300 300 300 300 300

1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20

0.4 - 0.6 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.4 - 0.6 0.3 - 0.5 0.3 - 0.5

0.4 - 0.6 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.4 - 0.6 0.3 - 0.5 0.3 - 0.5

　

2400 2400 2400 2400 2400 2400 2400 2500 2500 2600

63 62 62 62 61 60 60 61 63 63

6.5 6.6 6.6 6.7 5.6 5.5 5.4 6.1 4.4 4.2

76 118 118 119 113 105 108 85 81 72

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

94 93 93 93 93 93 93 94 98 97

2300 2300 2300 2300 2300 2300 2300 2400 2700 2700

NB NB NB NB NB NB NB NB NB NB

7 50 60 67 76 84 88 50 50 40

123 123 124 124 129 131 131 105 97 94

136 136 138 139 143 145 145 116 107 105

6.5E-05 6.5E-05 6.5E-05 6.5E-05 6.5E-05 6.5E-05 6.5E-05 6.6E-05 6.6E-05 6.6E-05

6.6E-05 6.6E-05 6.6E-05 6.6E-05 6.6E-05 6.6E-05 6.6E-05 6.7E-05 6.7E-05 6.7E-05

- - - - - - - V-0(1.5mm) V-2(0.38mm)

5VB(2.0mm) V-0(0.75mm) V-2(0.38mm)

V-0(0.8mm) V-2(0.4mm)

3.1 3.1 3.1 3.1 3.1 3.1 3.1 3.1 3.1 3.1

3.1 3.1 3.1 3.1 3.1 3.1 3.1 3.1 3.1 3.1

0.0006 0.0006 0.0006 0.0006 0.0006 0.0006 0.0006 0.0034 0.0034 0.0034

0.0090 0.0090 0.0090 0.0090 0.0090 0.0090 0.0090 0.0071 0.0071 0.0071

3E+14 3E+14 3E+14 3E+14 3E+14 3E+14 3E+14 2.E+14 2.E+14 2.E+14

6E+15 6E+15 6E+15 6E+15 6E+15 6E+15 6E+15 4.E+15 4.E+15 4.E+15

31 31 31 31 31 31 31 31 31 31

- - - - - - - 24 - -

18 18 18 18 18 18 18 18 18 18

2 2 2 2 2 2 2 2 2 -

H-3000V(R)(V-2)

H-3000R(Mold Release)

H-3000U(R)(UV Stabilized)

H-2000V(R)(V-2)

H-2000R(Mold Release)

H-2000U(R)(UV Stabilized)

S-3000V(R)(V-2)

S-3000R(Mold Release)

S-3000U(R)(UV Stabilized)

S-3001(R)(FDA compliant)

H-2000V(R)(V-2)




S-1000V(R)(V-2)




E-2000V(R)(V-2)

E-2000R(Mold Release)

E-2000U(R)(UV Stabilized)

E-2001(R)(FDA compliant)

Grade

Properties Test Method Terms Units

Physical properties

Density ISO 1183 - g/cm3

Water absorption -23degC, 50%RH

%23degC, Underwater

Rheological properties

Melt Mass-flow RateMelt Volume-flow Rate ISO 1133

- g/10min

- cm3/10min

Temperature degC

Load kgf

Moulding shrinkage (3.2mmt) -

MD%

TD

Mechanical properties

Tensile modulus

ISO527-1 ,527-2

-

MPaYield stress

Yield strain%

Nominal strain at break

Stress at 50% strain MPa

Stress at break

Strain at break %

Flexural strengthISO 178 - MPa

Flexural modulus

Charpy impact strength ISO179-1, 179-2

23 degC kJ/m2

Charpy notched impact strength 23 degC kJ/m2

Thermal properties

Temperature of deflectionunder load

ISO75-1 ,75-2

1.80MPadegC

0.45MPa

Coefficient of Linear thermal expansion

ISO11359-2

MD1/degC

TD

Flammability UL94 - -

Electrical properties

Relative permittivity IEC 60250100Hz -

1MHz -

Dissipation factor IEC 60250100Hz -

1MHz -

Volume resistivity IEC60093 - ohm-m

Surface resistivity IEC60093 - ohm

Electric strength IEC60243-1

1mmt

MV/m2mmt

3mmt

Comparative tracking index (CTI) UL746A - -

21

The listed properties are portrayed as general information only and are not product specifications. Mitsubishi Engineering-Plastics disclaims any liability in connection with the use of the information in this table.

Gamma-ray Resistance Light Diffusion

RS-3001R RS-1001R EB-3001R DS3205VUR DS3208VUR DS3212VUR EKD3408U DM2207VUR EKD2108U

Gamma-rayResistance

Gamma-rayResistance

Gamma-rayResistance

Light DiffusionLow class

Light DiffusionMedium class

Light DiffusionHigh class



Extrusion


Extrusion

1.21 1.21 1.20 1.20 1.20 1.20 1.20 1.20 1.20

- - - - - - - - -

0.24 0.24 0.24 0.24 0.24 0.24 0.24 0.24 0.24

15 8 15 20 20 20 24 8 5

15 7 14 20 20 20 23 8 5

300 300 300 300 300 300 300 300 300

1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20

0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7

0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7

2500 2200 2500 2500 2500 2500 2500 2500 2500

62 62 62 63 63 62 64 64 63

6.7 6.3 6.5 6.0 6.0 6.0 6.0 6 6

124 100 120 110 120 120 80 104 76

- - - - - - - - -

- - - - - - - - -

- - - - - - - - -

90 93 92 96 96 94 99 97 97

2100 2200 2300 2400 2400 2400 2400 2400 2400

NB NB NB NB NB NB NB NB NB

63 78 65 40 70 65 14 75 73

126 128 126 122 123 123 120 123 125

139 141 139 136 136 136 135 136 136

6.5E-05 6.5E-05 6.5E-05 6.5E-05 6.5E-05 6.5E-05 6.5E-05 6.5E-05 6.5E-05

6.6E-05 6.6E-05 6.6E-05 6.6E-05 6.6E-05 6.6E-05 6.6E-05 6.6E-05 6.6E-05

- - - V-2(0.4mm) V-2(0.4mm) V-2(0.4mm) V-0(1.0mm) V-2(0.75mm) V-0(1.0mm)

- - - - - - - - -

- - - - - - - - -

- - - - - - - - -

- - - - - - - - -

3E+14 3E+14 3E+14 3E+14 3E+14 3E+14 3E+14 3E+14 3E+14

6E+15 6E+15 6E+15 6E+15 6E+15 6E+15 6E+15 6E+15 6E+15

- - - - - - - - -

- - - - - - - - -

- - - - - - - - -

- - - 3 3 3 3 - 3

Light Reflection Light guide Grade Automotive Light guide Grade Glass Fiber Reinforced

EHR3100 EHR3150 EHR3400 EHR3200 EHG2010R HL-3000 HL-4000 HL-7001 HL-8000 HL-3003 HL-3503 GSH2010R2 GSH2020R2

Non-Br & Non-P Non-Br & Non-PHigh Flowability Non-Br & Non-P Non-Br & Non-P

Light Shielding

Non-Br & Non-PGF

10%High luminance High flow

High luminanceSuper high flowHigh luminance

Super high flowHigh luminance

High ImpactHeat aging resistance

High flowHeat aging resistance

GF10%

GF20%

1.30 1.30 1.30 1.41 1.37 1.20 1.20 1.20 1.20 1.20 1.20 1.27 1.35

- - - - - - - - - - - - -

0.20 0.20 0.20 0.20 0.18 0.24 0.24 0.24 0.24 0.24 0.24 0.14 0.11

24 46 19 26 13 34 63 113 139 34 56 10.0 8.5

22 43 18 24 13 32 60 108 136 32 53 9.0 8.0

300 300 300 300 300 300 300 300 300 300 300 300 300

1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20

0.4 - 0.6 0.4 - 0.6 0.4 - 0.6 0.4 - 0.6 0.3 - 0.5 0.5-0.7 0.4-0.6 0.4 - 0.6 0.4 - 0.6 0.5 - 0.7 0.4 - 0.6 0.3 - 0.5 0.1 - 0.3

0.4 - 0.6 0.4 - 0.6 0.4 - 0.6 0.4 - 0.6 0.3 - 0.5 0.5-0.7 0.4-0.6 0.4 - 0.6 0.4 - 0.6 0.5 - 0.7 0.4 - 0.6 0.4 - 0.6 0.3 - 0.5

2700 2700 2800 2700 4100 2400 2300 2300 2400 2400 2400 4400 6200

53 54 60 54 - 63 62 64 65 63 63 - -

5.0 5.1 5.6 4.9 - 6.6 5.7 5.5 5.7 5.8 5.6 - -

55 13 61 12 - 140 96 87 85 113 87 - -

- - - - - - - - - - - - -

- - - - 66 - - - - - - 82 104

- - - - 4.4 - - - - - - 3.8 3.2

89 89 93 90 110 97 100 100 100 98 99 130 160

2500 2600 2600 2700 3700 2400 2500 2500 2500 2300 2300 3900 5800

NB NB NB NB NB NB NB NB NB NB NB 60 55

37 9 49 13 4 40 40 12 9 57 49 10 13

120 117 125 122 129 125 123 118 118 123 122 140 143

135 134 136 135 137 140 136 132 132 137 135 145 146

6.2E-05 6.2E-05 6.2E-05 6.2E-05 - 6.5E-05 6.5E-05 6.5E-05 6.5E-05 6.5E-05 6.5E-05 4.0E-05 2.6E-05

6.3E-05 6.3E-05 6.3E-05 6.3E-05 - 6.6E-05 6.6E-05 6.6E-05 6.6E-05 6.6E-05 6.6E-05 6.7E-05 6.3E-05

V-0(1.5mm) V-0(1.5mm) V-0(1.0mm) V-0(1.0mm) V-0(1.5mm) V-2(0.38mm) V-2(0.38mm) V-2(0.38mm) V-2(0.38mm) - - HB(0.4mm) HB(0.4mm)

- - - - - 3.1 3.1 3.1 3.1 3.1 3.1 - -

- - - - - 3.1 3.1 3.1 3.1 3.1 3.1 - -

- - - - - 0.0006 0.0006 0.0006 0.0006 0.0006 0.0006 - -

- - - - - 0.009 0.009 0.009 0.009 0.0090 0.0090 - -

3E+14 3E+14 3E+14 3E+14 - 3.E+14 3.E+14 3.E+14 3.E+14 3E+14 3E+14 - -

6E+15 6E+15 6E+15 6E+15 - 6.E+15 6.E+15 6.E+15 6.E+15 6E+15 6E+15 - -

- - - - - 31 31 31 31 31 31 - -

- - - - - - - - - - - - -

- - - - - 18 18 18 18 18 18 - -

same as 2 - same as 1 same as 2 - 2 2 2 - same as 2 same as 2 same as 3 same as 3

HL-3000U(UV Stabilized)

HL-4002(YI Stabilized)

HL-8002(YI Stabilized)

Polycarbonate Resin

Grade


Physical properties



%23degC, Underwater



- g/10min

- cm3/10min

Temperature degC

Load kgf


MD%

TD


Tensile modulus

ISO527-1 ,527-2

-

MPaYield stress

Yield strain%



Stress at break

Strain at break %


Flexural modulus


23 degC kJ/m2


Thermal properties


ISO75-1 ,75-2

1.80MPadegC

0.45MPa


ISO11359-2

MD1/degC

TD




1MHz -


1MHz -




1mmt

MV/m2mmt

3mmt


43


Glass Fiber Reinforced Glass Fiber Reinforced (High Flowability) Glass Fiber Reinforced (High Flowability & High Stiffness)

GSH2030R2 GSH2040R2 GSH2010KR GSH2020KR GSH2030KR GSH2040KR GSH3110R GSH3120R GSH3130R GSH3140R

GF30%

GF40%

GF10%

GF20%

GF30%

GF40%

GF10%

GF20%

GF30%

GF40%

1.43 1.52 1.27 1.35 1.43 1.52 1.25 1.32 1.40 1.50

- - - - - - - - - -

0.09 0.08 0.14 0.11 0.09 0.08 0.14 0.11 0.09 0.08

5.7 3.7 12 9.7 7.0 5.1 - - - -

4.8 2.7 11 8.3 5.5 3.7 - - - -

300 300 300 300 300 300 300 300 300 300

1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20

0.05 - 0.25 0.05 - 0.25 0.3 - 0.5 0.1 - 0.3 0.05 - 0.25 0.05 - 0.25 0.3 - 0.5 0.1 - 0.3 0.05 - 0.25 0.05 - 0.25

0.25 - 0.45 0.2 - 0.4 0.4 - 0.6 0.3 - 0.5 0.25 - 0.45 0.2 - 0.4 0.4 - 0.6 0.3 - 0.5 0.25 - 0.45 0.2 - 0.4

8900 11700 4200 6100 8700 11000 4900 6800 10700 13300

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

120 135 75 95 116 130 94 121 144 155

2.5 2.1 3.4 2.5 2.0 1.8 3.4 2.5 2.0 1.8

180 210 120 153 175 205 150 178 210 230

8500 11200 3500 5600 8100 10000 4500 6600 9500 11900

50 55 68 50 45 50 52 57 45 44

15 16 6 9 13 15 8 11 13 13

144 144 134 140 141 142 139 141 141 141

148 149 139 144 145 145 143 145 145 145

1.8E-05 1.5E-05 4.0E-05 2.7E-05 1.8E-05 1.5E-05 3.9E-05 2.5E-05 1.7E-05 1.4E-05

6.3E-05 6.1E-05 6.7E-05 6.2E-05 6.3E-05 6.1E-05 6.3E-05 6.0E-05 5.8E-05 5.5E-05

HB(0.4mm) HB(0.4mm) HB(0.4mm) HB(0.4mm) HB(0.4mm) HB(0.4mm) HB(0.4mm) HB(0.4mm) HB(0.4mm) HB(0.4mm)

3.6 - - - - - - - - -

3.5 - - - - - - - - -

0.0011 - - - - - - - - -

0.0084 - - - - - - - - -

2E+14 - - - - - - - - -

2E+15 - - - - - - - - -

32 - - - - - - - - -

- - - - - - - - - -

20 - - - - - - - - -

same as 4 same as 4 same as 3 same as 3 same as 4 same as 4 - - - -

Glass Fiber Reinforced (Low Warpage) Glass Fiber Reinforced (Flame Retardant) Glass Fiber Reinforced (Low Warpage)

GSH2030R2K807

GSH2030R2991J GSH2030FT GS2010MN1 GS2020MN1 GS2030MN1 GSH2020DF GSH2030DF GSH2040DF GSH2050DF

GF30%

GF30%

GF30%

GF10%

GF20%

GF30%

GF20%

GF30%

GF40%

GF50%

1.43 1.43 1.43 1.29 1.37 1.45 1.35 1.43 1.52 1.63

- - - - - - - - - -

0.09 0.09 0.09 0.14 0.11 0.09 0.11 0.09 0.08 0.07

15 8.8 7.0 10.0 8.5 5.7 11 6.9 5.0 2.2

14 7.0 5.2 9.0 8.0 4.8 10 5.2 3.7 1.7

300 300 300 300 300 300 300 300 300 300

1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20

0.2 - 0.4 0.3 - 0.5 0.15 - 0.35 0.3 - 0.5 0.1 - 0.3 0.05 - 0.25 0.2 - 0.4 0.1 - 0.3 0.1 - 0.3 0.1 - 0.3

0.2 - 0.4 0.3 - 0.5 0.15 - 0.35 0.4 - 0.6 0.3 - 0.5 0.25 - 0.45 0.2 - 0.4 0.1 - 0.3 0.1 - 0.3 0.1 - 0.3

5100 4400 6200 4500 6500 9000 5700 7300 9300 11600

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

51 63 75 78 97 103 74 80 92 102

1.9 2.5 2.5 2.9 2.7 1.5 2.7 2.1 1.8 1.4

100 100 126 135 160 175 127 137 155 160

4600 3900 5800 4000 5900 8500 5300 6800 8400 10800

27 30 32 55 50 45 46 34 33 31

3 6 4 10 11 12 5 5 6 7

134 136 139 140 143 145 133 136 139 138

140 143 145 145 146 148 140 142 143 144

- - - 4.0E-05 2.7E-05 1.8E-05 3.4E-05 2.7E-05 2.0E-05 1.8E-05

- - - 6.7E-05 6.2E-05 6.3E-05 5.0E-05 4.5E-05 4.0E-05 3.9E-05

HB(0.4mm) HB(0.4mm) HB(0.4mm) V-0(0.75mm) V-0(0.75mm) V-0(0.75mm) HB(0.4mm) HB(0.4mm) HB(0.4mm) HB(0.4mm)

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

same as 4 same as 4 same as 4 4 4 4 3 4 4 4

Polycarbonate Resin

Grade


Physical properties



%23degC, Underwater



- g/10min

- cm3/10min

Temperature degC

Load kgf


MD%

TD


Tensile modulus

ISO527-1 ,527-2

-

MPaYield stress

Yield strain%



Stress at break

Strain at break %


Flexural modulus


23 degC kJ/m2


Thermal properties


ISO75-1 ,75-2

1.80MPadegC

0.45MPa


ISO11359-2

MD1/degC

TD




1MHz -


1MHz -




1mmt

MV/m2mmt

3mmt


65


Grade


Physical properties



%23degC, Underwater



- g/10min

- cm3/10min

Temperature degC

Load kgf


MD%

TD


Tensile modulus

ISO527-1 ,527-2

-

MPaYield stress

Yield strain%



Stress at break

Strain at break %


Flexural modulus


23 degC kJ/m2


Thermal properties


ISO75-1 ,75-2

1.80MPadegC

0.45MPa


ISO11359-2

MD1/degC

TD




1MHz -


1MHz -




1mmt

MV/m2mmt

3mmt


Polycarbonate Resin

Glass Fiber Reinforced (Flame Retardant, Low Warpage) Glass Fiber Reinforced (For Camera)

GPN2020DF GPN2030DF GPN2040DF GPF2040DF GPN2050DF GPX2050DF GSH2010LRY082

GSH2020LRY083

Phosphoric acidHigh Flowability

GF20%


GF30%


GF40%


GF40%


GF50%

Phosphoric acidHigh FlowabilityHigh Modulus

GF 50%

Good Surface Easy Coating

GF10%

Good Surface Easy Coating

GF20%

1.34 1.42 1.51 1.51 1.63 1.63 1.27 1.35

- - - - - - - -

0.11 0.09 0.08 0.08 0.07 0.07 0.14 0.11

13 9.4 9.6 10 4.3 7.9 17 9.2

11 7.4 7.1 7.9 2.9 5.3 15 7.9

300 300 300 300 300 300 300 300

1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20

0.1 - 0.3 0.05 - 0.25 0.05 - 0.2 0.05 - 0.2 0.05 - 0.2 0.05 - 0.2 0.3 - 0.5 0.1 - 0.3

0.1 - 0.3 0.05 - 0.25 0.05 - 0.2 0.05 - 0.2 0.05 - 0.2 0.05 - 0.2 0.3 - 0.5 0.3 - 0.5

6000 7500 9900 11000 13200 13800 3300 6000

- - - - - - - -

- - - - - - - -

- - - - - - - -

- - - - - - - -

71 72 82 90 91 122 60 85

2.6 1.9 1.5 2.0 1.1 1.5 4.6 2.3

128 140 150 150 165 208 105 135

5800 7700 10200 10000 12800 14200 2800 4900

29 23 21 23 29 36 70 40

4 4 4 5 5 7 6 7

116 118 117 110 115 110 126 133

123 124 123 115 120 115 132 137

3.4.E-05 2.7.E-05 2.2.E-05 2.2.E-05 1.9.E-05 2.0.E-05 5.0E-05 3.0E-05

4.0.E-05 3.3.E-05 2.9.E-05 2.9.E-05 2.6.E-05 2.6.E-05 5.9E-05 6.0E-05

V-0(1.6mm) V-0(1.6mm) V-0(1.6mm) V-0(1.5mm) V-0(1.6mm) V-1(2.0mm) HB(0.4mm) HB(0.4mm)

- - - - - - - -

- - - - - - - -

- - - - - - - -

- - - - - - - -

- - - - - - - -

- - - - - - - -

- - - - - - - -

- - - - - - - -

- - - - - - - -

- - - - - - same as 3 same as 3

5VA(3.0mm)

5VA(3.0mm)

5VA(3.0mm)

Glass Fiber Reinforced (For Camera) Glass Fiber Reinforced (For Mobile Phone Housing)

Glass Fiber Reinforced (Flame Retardant) Glass Fiber Reinforced (Flame Retardant)

GSH2010DR9911A

GSH2020DR9913A GPX2010PH GSH2010PH EGN2010R2 EGN2020R2 EGN2030R2 EGN2010KR EGN2020KR EGN2030KR

Good Surface Easy CoatingGF

10%

Good Surface Easy CoatingGF

20%

Phosphoric acidHigh Impact

GF10%

High ImpactStrength

GF10%

Non Br & Non PGF

10%

Non Br & Non PGF

20%

Non Br & Non PGF

30%

Non Br & Non PHigh Flowability

GF10%


GF20%


GF30%

1.27 1.35 1.26 1.26 1.27 1.35 1.43 1.27 1.35 1.43

- - - - - - - - - -

0.14 0.11 0.14 0.14 0.14 0.11 0.09 0.14 0.11 0.09

16 7.6 17 15 - - - - - -

14 6.5 16 14 - - - - - -

300 300 300 300 - - - 300 300 300

1.20 1.20 1.20 1.20 - - - 1.20 1.20 1.20

0.3 - 0.5 0.1 - 0.3 0.3-0.5 0.3 - 0.5 0.3 - 0.5 0.1 - 0.3 0.1 - 0.3 0.25-0.45 0.15-0.35 0.1-0.3

0.3 - 0.5 0.3 - 0.5 0.3-0.5 0.3 - 0.5 0.4 - 0.8 0.3 - 0.5 0.3 - 0.5 0.3-0.5 0.25-0.45 0.2-0.4

3500 6200 3000 2900 4400 6200 8900 - - -

- - 55 52 - - - - - -

- - 4.8 5 - - - - - -

- - 10 10 - - - - - -

- - - - - - - - - -

63 86 - - 82 104 120 75 90 100

4.8 2.5 - - 5 4 3 4.1 2.9 2.3

107 141 93 90 129 153 177 121 139 153

2900 5500 2800 2700 3600 5700 8300 3500 5500 8000

73 43 NB NB 70 60 50 48 39 32

7 7 8 10 10 12 14 6 7 9

132 136 113 132 141 144 145 134 137 140

139 140 122 137 145 146 148 140 141 144

5.0E-05 3.0E-05 - 5.8.E-05 4.0E-05 2.6E-05 1.8E-05 - - -

5.9E-05 6.2E-05 - 5.8.E-05 6.7E-05 6.3E-05 6.3E-05 - - -

HB(0.4mm) HB(0.4mm) V-1(0.75mm) HB(0.4mm) V-0(1.5mm) V-2(0.75mm)

V-0(1.5mm) V-2(0.75mm)

V-0(1.5mm) V-2(0.75mm)

V-0(1.5mm) V-2(0.75mm)

V-0(1.5mm) V-2(0.75mm)

V-0(1.5mm) V-2(0.75mm)

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

same as 3 same as 3 - same as 3 same as 3 same as 3 same as 4 same as 3 same as 3 same as 4

87


Carbonfiber Reinforced Carbon+Glassfiber Reinforced Wear Resistance Improved

CFH2010 CFH2020 CFH2030 CGH1010R2 CGH1020KR CGH2010KR LSH2010 LSH2020 LSH2030 ELV2010 ELV2020 ELV2030

CF10%

CF20%

CF30%

CF+GF10%+10%

High FlowabilityCF+GF

10%+20%

High FlowabilityCF+GF

20%+10%

F5%

F10%

F15%

F5%

F10%

F15%

1.24 1.28 1.31 1.31 1.38 1.35 1.23 1.26 1.30 1.23 1.26 1.30

- - - - - - - - - - - -

0.11 0.09 0.07 0.11 0.09 0.09 0.13 0.12 0.10 0.13 0.12 0.10

7.0 4.8 3.9 6.9 6.2 4.3 10 10 9.1 10 10 9.1

6.6 4.2 3.6 6.1 4.6 3.5 9.7 9.3 8.1 9.7 9.3 8.1

300 300 300 300 300 300 300 300 300 300 300 300

1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20

0.1 - 0.3 0.05 - 0.2 0.01 - 0.15 0.1 - 0.3 0.05-0.2 0.02 - 0.15 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7

0.3 - 0.5 0.2 - 0.4 0.2 - 0.4 0.2 - 0.4 0.2-0.4 0.15 - 0.35 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7

8000 14000 17200 7200 13000 17300 2500 2500 2300 2500 2500 2300

- - - - - - 57 53 51 57 53 51

- - - - - - 6.7 6.6 6.2 6.7 6.6 6.2

- - - - - - 104 101 85 104 101 85

- - - - - - - - - - - -

111 141 155 91 127 163 - - - - - -

3.1 2.0 2.2 2.0 1.7 1.3 - - - - - -

165 200 210 180 195 210 90 85 81 90 85 81

7200 12500 16200 9000 12500 15000 2300 2300 2300 2300 2300 2300

49 45 40 50 45 40 NB NB NB NB NB NB

8 9 9 10 10 9 14 12 15 14 12 15

146 146 146 143 141 143 127 126 128 127 126 128

150 151 152 148 145 148 142 142 143 142 142 143

1.6E-05 9.0E-06 6.0E-06 2.4E-05 1.3.E-05 1.1.E-05 6.4E-05 6.6E-05 6.9E-05 6.4E-05 6.6E-05 6.9E-05

6.4E-05 5.9E-05 5.7E-05 5.9E-05 5.4.E-05 5.3.E-05 6.8E-05 7.0E-05 7.2E-05 6.8E-05 7.0E-05 7.2E-05

HB(0.4mm) HB(0.4mm) HB(0.4mm) HB(0.4mm) HB(0.4mm) HB(0.4mm) HB(0.4mm) HB(0.4mm) HB(0.4mm) V-2(0.8mm) V-2(0.8mm) V-2(0.8mm)

- - - - - - - - - - - -

- - - - - - - - - - - -

- - - - - - - - - - - -

- - - - - - - - - - - -

- - - - - - - - - - - -

- - - - - - - - - - - -

- - - - - - - - - - - -

- - - - - - - - - - - -

- - - - - - - - - - - -

- - - - - - 4 4 4 4 4 4

Glass Fiber Reinforced (Flame Retardant) Glass Fiber Reinforced (Flame Retardant, Low Warpage) Glass Fiber Reinforced (Flame Retardant)

EGN2010DR9911A

EGN2020DR9913A

EGW2010DR9005

EGW2020DR9005

EGN2030R2K807 EGN2020DF EGN2030DF EGN2040DF EGN2050DF EGN2020BR

Non Br & Non PGood SurfaceEasy Coating

GF　10%

Non Br & Non PGood SurfaceEasy Coating

GF　20%

Non Br & Non PGood Surface

GF10%

Non Br & Non PGood Surface

GF20%

Non Br & Non PLow Warpage

GF30%

Non Br & Non PGF

20%

Non Br & Non PGF

30%

Non Br & Non PGF

40%

Non Br & Non PGF

50%

Non Br & Non PLow Warpage

GF20%

1.27 1.35 1.27 1.35 1.43 1.35 1.43 1.52 1.63 1.35

- - - - - - - - - -

0.14 0.11 0.14 0.11 0.09 0.11 0.09 0.08 0.07 0.11

- - - - - - - - - -

- - - - - - - - - -

300 300 300 300 300 300 300 300 300 300

1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20

0.3-0.5 0.15-0.35 0.3-0.5 0.15-0.35 0.2-0.4 0.2-0.4 0.15-0.35 0.1-0.3 0.1-0.3 0.45-0.65

0.3-0.5 0.25-0.45 0.3-0.5 0.25-0.45 0.2-0.4 0.2-0.4 0.15-0.35 0.1-0.3 0.1-0.3 0.4-0.6

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

62 84 70 90 49 74 75 85 89 47

5.6 3.1 4.8 3.0 10 3.7 2.9 2.8 2.2 5.0

105 139 120 137 88 117 120 135 140 86

3100 5300 3600 5300 4600 5000 6500 8500 11000 3000

70 40 55 40 - 36 30 30 24 -

6 8 6 7 9 6 6 7 7 10

133 137 137 139 134 133 135 138 138 126

138 142 141 144 141 139 140 142 142 141

- - - - - - - - - -

- - - - - - - - - -

V-0(1.5mm) V-2(0.75mm)

V-0(1.5mm) V-2(0.75mm)

V-0(1.5mm) V-1(1.0mm)

V-0(1.5mm) V-1(1.0mm)

V-0(1.5mm) V-2(0.75mm)

V-0(1.5mm) V-2(0.75mm)

V-0(1.5mm) V-2(0.75mm) V-0(1.5mm) V-0(1.5mm) V-0(1.5mm)

V-2(0.75mm)

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

same as 3 same as 3 - - same as 4 same as 3 same as 4 same as 4 same as 4 same as 3

Polycarbonate Resin

Grade


Physical properties



%23degC, Underwater



- g/10min

- cm3/10min

Temperature degC

Load kgf


MD%

TD


Tensile modulus

ISO527-1 ,527-2

-

MPaYield stress

Yield strain%



Stress at break

Strain at break %


Flexural modulus


23 degC kJ/m2


Thermal properties


ISO75-1 ,75-2

1.80MPadegC

0.45MPa


ISO11359-2

MD1/degC

TD




1MHz -


1MHz -




1mmt

MV/m2mmt

3mmt


109


Carbon Fiber Reinforced (Flame Retardant) Wear Resistance Improved (Fiber Reinforced) Wear Resistance Improved (Fiber Reinforced)

ECF2010R ECF2015R ECF2020R ECF2030R LGH2230M LGH2330M LGH2410M LCH2315 LCH2410 LCH2415

CF10%

CF15%

CF20%

CF30%

F10%GF

30%

F15%GF

30%

F20%GF

10%

F15%CF

15%

F20%CF

10%

F20%CF

15%

1.24 1.26 1.28 1.32 1.52 1.55 1.41 1.37 1.37 1.38

- - - - - - - - - -

0.11 0.10 0.09 0.07 0.09 0.08 0.08 0.08 0.08 0.08

- - - - 5.1 1.5 5.0 1.7 4.6 1.1

- - - - 4.5 1.1 4.5 1.3 4.3 0.9

300 300 300 300 300 300 300 300 300 300

1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20

0.05-0.25 0.05-0.25 0.01-0.2 0.01-0.15 0.05 - 0.25 0.05 - 0.25 0.3 - 0.5 0.05 - 0.2 0.1 - 0.3 0.05 - 0.2

0.25-0.45 0.20-0.4 0.2-0.4 0.2-0.4 0.25 - 0.45 0.25 - 0.45 0.4 - 0.6 0.2 - 0.4 0.3 - 0.5 0.2 - 0.4

8000 11500 14000 17200 9000 9500 4100 10000 7500 10000

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

113 130 140 160 111 100 67 105 94 100

4.0 3.0 3.0 3.0 2.4 1.9 2.9 2.1 1.6 1.5

160 180 190 200 174 167 111 180 150 167

7200 9600 12500 16200 8200 8000 3700 9400 7000 9300

45 50 50 40 50 48 45 35 32 30

8 9 10 10 13 13 13 8 8 8

146 146 146 146 143 143 142 145 145 146

150 150 151 152 148 148 148 150 150 150

- - - - 2.0E-05 1.7E-05 3.7E-05 1.4E-05 1.8.E-05 1.6.E-05

- - - - 6.0E-05 6.7E-05 6.8E-05 6.5E-05 7.1.E-05 7.2.E-05

V-0(1.5mm) V-2(0.8mm)

V-0(1.5mm) V-2(0.8mm)

V-0(1.5mm) V-2(0.8mm)

V-0(1.5mm) V-2(0.8mm) HB(0.4mm) HB(0.4mm) HB(0.4mm) HB(0.4mm) HB(0.4mm) HB(0.4mm)

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

Polymer　Alloy　（PC/ABS)

MB2210R MB2212R MB2213R MB2215R MB2219R MB2220R MB2222R MB2223R MB1800

LowMold Deposit

High flow

LowMold DepositHeat Resistant

LowMold Deposit

High WeldStrength

High HeatResistance High Flowability High Impact

StrengthHigh Impact

StrengthPhosphoric acid

Standard

1.13 1.12 1.15 1.13 1.14 1.13 1.14 1.12 1.18

- - - - - - - - -

0.12 0.12 0.12 0.12 0.12 0.12 0.12 0.12 0.2

9 11 9 5 9 10 5 5 14

9 10 9 5 9 10 5 5 14

250 250 250 250 250 250 250 250 260

2.16 2.16 2.16 2.16 2.16 2.16 2.16 2.16 2.16

0.4 - 0.6 0.3 - 0.5 0.4 - 0.6 0.4 - 0.6 0.4 - 0.6 0.4 - 0.6 0.4 - 0.6 0.4 - 0.6 0.3 - 0.5

0.4 - 0.6 0.3 - 0.5 0.4 - 0.6 0.4 - 0.6 0.4 - 0.6 0.4 - 0.6 0.4 - 0.6 0.4 - 0.6 0.3 - 0.5

2800 2500 2500 2400 2400 2400 2300 2300 2800

55 55 59 52 57 54 52 51 60

4.3 4.4 4.9 5.1 4.8 4.5 4.8 4.7 4.0

35 46 76 51 50 50 50 50 92

- - - - - - - - -

- - - - - - - - -

- - - - - - - - -

90 88 94 85 91 87 83 80 95

2400 2400 2400 2300 2400 2400 2200 2200 2800

NB NB NB NB NB NB NB NB NB

34 70 50 70 60 70 60 60 40

100 96 110 100 110 103 107 102 81

115 114 130 123 130 123 128 124 89

7.0E-05 7.0E-05 7.0E-05 7.0E-05 7.0E-05 7.0E-05 7.0E-05 7.0E-05 -

7.0E-05 7.0E-05 7.0E-05 7.0E-05 7.0E-05 7.0E-05 7.0E-05 7.0E-05 -

HB(1.5mm) HB(1.5mm) HB(1.0mm) HB(1.5mm) - - - - V-0(1.2mm) 5VB(2.0mm)

- - - - - - - - -

- - - - - - - - -

- - - - - - - - -

- - - - - - - - -

- - - - - - - - -

- - - - - - - - -

- - - - - - - - -

- - - - - - - - -

- - - - - - - - -

- - - - - - - - -

Polycarbonate Resin

Grade


Physical properties



%23degC, Underwater



- g/10min

- cm3/10min

Temperature degC

Load kgf


MD%

TD


Tensile modulus

ISO527-1 ,527-2

-

MPaYield stress

Yield strain%



Stress at break

Strain at break %


Flexural modulus


23 degC kJ/m2


Thermal properties


ISO75-1 ,75-2

1.80MPadegC

0.45MPa


ISO11359-2

MD1/degC

TD




1MHz -


1MHz -




1mmt

MV/m2mmt

3mmt


1211


Polymer　Alloy　（PC/ABS) Polymer Alloy (PC/POLYESTER)

MB1700 MB8300 MB8500 MB8700 MB8900 TMB1412 TMB1615 MB2105 MB2112 MB2112N GMB1110

Phosphoric acid

High FlameRetardant


Hihg Heat Resistance

Phosphoric acidHigh

Flowability

Phosphoric acidHigh

Flowability


High Impact

Phosphoric acid

High Modulus

Phosphoric acid

High Modulus

ChemicalResistant

ChemicalResistant

Flame RetardantChemicalResistant

ChemicalResistant

GF10%

1.20 1.18 1.19 1.20 1.20 1.27 1.29 1.22 1.22 1.31 1.29

- - - - - - - - - - -

0.20 0.20 0.20 0.20 0.20 0.20 0.20 0.20 0.20 0.20 0.09

14 18 37 35 25 21 11 7.1 7.0 18 8.6

14 17 36 35 23 20 11 6.9 6.6 17 7.9

260 260 260 260 260 260 260 300 300 300 300

2.16 2.16 2.16 2.16 2.16 2.16 2.16 1.20 1.20 1.20 1.20

0.2-0.4 0.3-0.5 0.25-0.45 0.25-0.45 0.25-0.45 0.15-0.35 0.15-0.35 0.6 - 0.8 0.6 - 0.8 0.6 - 0.8 0.2 - 0.4

0.2-0.4 0.3-0.5 0.25-0.45 0.25-0.45 0.25-0.45 0.15-0.35 0.15-0.35 0.6 - 0.8 0.6 - 0.8 0.6 - 0.8 0.3 - 0.5

3200 2800 2900 3100 2800 4700 5300 2300 2100 2500 4400

61 59 64 63 55 58 67 57 59 55 -

3.9 4.0 4.0 3.5 3.5 2.6 3.8 5.2 5.5 5.9 -

55 69 38 16 44 10 8 90 93 93 -

- - - - - - - - - - -

- - - - - - - - - - 90

- - - - - - - - - - 4.0

100 98 98 99 88 100 108 90 86 86 134

3000 2700 2800 3100 2600 4200 4800 2300 2200 2300 3600

NB NB NB NB NB 85 130 NB NB NB 50

20 21 10 6 30 4 6 70 77 71 8

82 87 82 81 77 79 90 112 113 116 133

92 95 90 89 86 89 100 136 138 138 138

- - - - - - - 6.0E-05 6.0E-05 6.1E-05 4.5E-05

- - - - - - - 7.0E-05 7.0E-05 7.1E-05 7.0E-05

V-0(0.81mm) V-2(0.6mm) HB(0.4mm)

V-0(1.5mm) 5VB(2.0mm)

V-0(1.2mm) 5VB(2.0mm)

V-0(1.0mm) 5VB(1.2mm)

V-1(1.0mm) 5VB(1.5mm) V-0(1.0mm) V-0(1.0mm) - HB(1.6mm) V-0(1.6mm) -

- - - - - - - - - - -

- - - - - - - - - - -

- - - - - - - - - - -

- - - - - - - - - - -

- - - - - - - - - - -

- - - - - - - - - - -

- - - - - - - - - - -

- - - - - - - - - - -

- - - - - - - - - - -

- 0 - - - - - - - - -

Polymer Alloy (PC/POLYESTER) High Surface hardness

MB5002R MB4303 MB4306R MB4308 MB4405U MB6004UR KH4210UR KH3310UR KH3410UR KH3520UR

Anti-static ChemicalResistant

ChemicalResistantHigh WeldStrength

ChemicalResistant

ChemicalResistant

High Impact

High surfacehardness

Clear


Clear


Clear


Clear

Extra surfacehardness

Clear

1.20 1.23 1.23 1.21 1.20 1.19 1.18 1.17 1.16 1.17

- - - - - - - - - -

0.20 0.30 0.30 0.30 0.30 0.20 0.20 0.20 0.19 0.19

10 20 25 13 1.20 60 59 35 27 35

9.2 19 24 12 - 59 57 33 26 33

300 300 300 280 0.30 280 300 300 300 300

1.20 1.20 1.20 2.16 1.20 2.16 1.20 1.20 1.20 1.20

0.6 - 0.8 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 - 0.4 - 0.6 0.5-0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7

0.6 - 0.8 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.30 0.4 - 0.6 0.5-0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7

2100 2500 2400 2300 2000 2800 2500 2700 2700 2900

50 62 59 62 49 77 71 74 77 82

5.9 5.5 4.8 4.7 4.6 5.3 6.0 6.0 6.0 6.0

140 96 110 136 150 31 74 85 60 33

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

78 96 90 94 72 112 103 106 107 113

2000 2400 2300 2200 1900 2700 2500 2600 2700 2900

NB NB NB NB NB 105 NB NB 131 37

80 59 58 57 61 2 3 3 3 2

112 97 100 97 80 102 111 107 100 92

132 115 112 112 95 112 124 120 113 103

8.0E-05 6.8E-05 6.8E-05 6.8E-05 7.5E-05 6.5E-05 6.5E-05 6.5E-05 6.5E-05 6.5E-05

9.6E-05 6.8E-05 6.8E-05 6.8E-05 8.0E-05 6.7E-05 6.7E-05 6.7E-05 6.7E-05 6.7E-05

- - - - - - V-2(0.4mm) V-2(0.4mm) -

4.4 - - - - - - - - -

3.5 - - - - - - - - -

0.0081 - - - - - - - - -

0.0233 - - - - - - - - -

3.E+11 - - - - - - - - -

7.E+11 - - - - - - - - -

- - - - - - - - - -

24 - - - - - - - - -

18 - - - - - - - - -

- - - - - - - - - -

MB5002UR(UV Stabilized) Pemcil Hardness F Pemcil Hardness F Pemcil Hardness H Pemcil Hardness 2H Pemcil Hardness 3H

Polycarbonate Resin

Grade


Physical properties



%23degC, Underwater



- g/10min

- cm3/10min

Temperature degC

Load kgf


MD%

TD


Tensile modulus

ISO527-1 ,527-2

-

MPaYield stress

Yield strain%



Stress at break

Strain at break %


Flexural modulus


23 degC kJ/m2


Thermal properties


ISO75-1 ,75-2

1.80MPadegC

0.45MPa


ISO11359-2

MD1/degC

TD




1MHz -


1MHz -




1mmt

MV/m2mmt

3mmt


1413


Grade


Physical properties

Density ISO1183 - g/cm3

Water absorption -

23degC, 50%RH

%23degC,

Underwater


Melt Mass-flow RateMelt Volume-flow Rate

ISO 1133

- g/10min

- cm3/10min

Temperature degC

Load kgf


MD%

TD


Tensile modulus

ISO 527-1 ,527-2

-

MPaYield stress

Yield strain%



Stress at break

Strain at break %

Flexural strengthISO178 - MPa

Flexural modulus

Charpy impact strengthISO 179-1

,179-2

23 degC kJ/m2


Thermal properties


ISO75-1 ,75-2

1.80MPadegC

0.45MPa


ISO 11359-2

MD1/degC

TD




1MHz -


1MHz -




1mmt

MV/m2mmt

3mmt


Basic-1 Basic-2 Basic-3

M7020AD2 7020R 7022R 7025R 7027R 7030R M7025U-7 M7026U M7027U M7027BF

Optical Disk High Flowability Low Viscosity Medium

ViscosityHigh Viscosity

ExtrusionHigh Viscosity

ExtrusionProfile

ExtrusionProfile

ExtrusionProfile

Extrusion Blow Form

1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20

- - - - - - - - - -

0.24 0.24 0.24 0.24 0.24 0.24 0.24 0.24 0.24 0.24

63 19 14 8.4 6.0 4.2 6.5 5.0 3.2 2.4

60 18 13 8.0 5.7 3.9 6.0 4.9 2.9 2.3

300 300 300 300 300 300 300 300 300 300

1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20 1.20

0.4 - 0.6 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7

0.4 - 0.6 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7

2400 2400 2400 2400 2400 2400 2300 2300 2300 2300

62 62 60 61 60 60 62 62 62 62

6.5 6.6 6.9 5.6 5.5 5.4 6.0 6.0 6.0 6.0

80 120 140 115 104 107 100 100 100 100

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -

93 93 93 93 93 93 93 93 93 93

2300 2300 2300 2300 2300 2300 2300 2300 2300 2300

NB NB NB NB NB NB NB NB NB NB

7 67 67 76 84 88 70 70 70 70

121 123 124 129 131 131 123 127 128 129

136 138 139 143 145 145 136 142 142 143

6.5E-05 6.5E-05 6.5E-05 6.5E-05 6.5E-05 6.5E-05 6.5E-05 6.5E-05 6.5E-05 6.5E-05

6.6E-05 6.6E-05 6.6E-05 6.6E-05 6.6E-05 6.6E-05 6.6E-05 6.6E-05 6.6E-05 6.6E-05

- - - - - - - - - -

3.1 3.1 3.1 3.1 3.1 3.1 3.1 3.1 3.1 3.1

3.1 3.1 3.1 3.1 3.1 3.1 3.1 3.1 3.1 3.1

0.0006 0.0006 0.0006 0.0006 0.0006 0.0006 0.0006 0.0006 0.0006 0.0006

0.0090 0.0090 0.0090 0.0090 0.0090 0.0090 0.0090 0.0090 0.0090 0.0090

3.E+14 3.E+14 3.E+14 3.E+14 3.E+14 3.E+14 3.E+14 3.E+14 3.E+14 3.E+14

6.E+15 6.E+15 6.E+15 6.E+15 6.E+15 6.E+15 6.E+15 6.E+15 6.E+15 6.E+15

- - - - - - - - - -

24 24 24 24 24 24 24 24 24 24

17 17 17 17 17 17 17 17 17 17

same as 2 same as 2 same as 2 same as 2 same as 2 same as 2 same as 2 same as 2 same as 2 same as 2

7020IR(ice color)

7022IR(ice color)7022IRF

(FDA compliant)

7025IR(ice color)

Gamma-ray Resistance Anti-static

7022FD2 7022ETH

Gamma-ray Resistance Clear

1.21 1.20

- -

0.24 0.24

15 20

14 19

300 300

1.20 1.20

0.5 - 0.7 0.5 - 0.7

0.5 - 0.7 0.5 - 0.7

2500 2700

62 67

6.7 6.3

124 100

- -

- -

- -

90 100

2100 2500

NB NB

63 65

126 117

139 130

6.5E-05 6.5E-05

6.6E-05 6.6E-05

- -

- -

- -

- -

- -

3E+14 3.E+12

6E+15 3.E+13

- -

- -

- -

- -

The polycarbonate resin Novarex is a transparent resin with excellent dimensional stability, impact strength and electronic characteristics. Novarex is suited for components used by the electronic, optical, automobile, medical equipment and glazing industries . We offer Novarex in a variety of grades: branched grades for water bottle or multi-wall sheet, and a grade for optical discs.

Special features:1. Superior impact strength2. Usability in a wide range of temperatures: -40degC to

120degC3. Excellent electrical insulation capabilities4. Excellent precision molding properties and dimensional

stability

5. Low moisture absorption6. Excellent weather resistance7. Superior self-extinguishing properties8. Superior transparency

Polycarbonate Resin

1615


Polycarbonate Resin

Grade


Physical properties


Water absorption ISO 62 - %



ISO 1133

- g/10min

- cm3/10min

Temperature degC

Load kgf

Moulding shrinkage -MD

%TD


Tensile modulus

ISO 527-1, 527-2

-

MPaYield stress

Yield strain%



Stress at break

Strain at break %


Flexural modulus

Charpy impact strength ISO 179-1, 179-2 23 degC kJ/m2

Izod notched impact strength ISO 180/4A 23 degC kJ/m2

Thermal properties

Temperature of deflection under load

ISO75-1, 75-2

1.80MPadegC

0.45MPa


ISO11359-2

MD1/degC

TD



Relative permittivity IEC60250100Hz -

1MHz -

Dissipation factor IEC60250100Hz -

1MHz -



Electric strength IEC60243 -1 - kV/mm


RTI (e lec/ imp/s t r )

UL746BUL746C

Flame Retardant Glass Fiber Reinforced(Flame Retardant)

FC19R FC22R FC23R FC25R RX2125 XRM1006 G2F23R G4F23R G6F23R

Non Br & Non PVery Low Viscosity

Non Br & Non PLow Viscosity

Non Br & Non PMedium Viscosity

Non Br & Non PHigh Viscosity

Non Br & Non PLow ViscosityUV Stabilized

Non Br & Non PLow Temp.

Impact

Non Br & Non PGF

10%

Non Br & Non PGF

20%

Non Br & Non PGF

30%

1.20 1.20 1.20 1.20 1.20 1.20 1.27 1.35 1.43

0.35 0.35 0.35 0.35 0.35 0.35 0.31 0.29 0.26

17 10 7 5 14 6 6 6 4

16 10 7 5 13 6 6 6 4

300 300 300 300 300 300 300 300 300

1.2 1.20 1.20 1.20 1.20 1.20 1.2 1.2 1.2

0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.1 - 0.3 0.1 - 0.3 0.1 - 0.3

0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.45 - 0.65 0.4 - 0.6 0.3 - 0.5

2300 2300 2300 2300 2300 2200 3500 6000 9500

60 60 60 60 60 55 65 - -

6 6 6 6 6 6 5 - -

> 50 > 50 > 50 > 50 > 50 > 50 15 - -

- - - - - - - - -

- - - - - - - 95 110

- - - - - - - 4 2

90 90 90 90 90 80 110 145 150

2400 2400 2400 2400 2400 2300 3400 5500 7000

NB NB NB NB NB NB

70 80 80 80 70 70 25 10 10

130 130 130 130 130 130 145 145 145

- - - - - - - - -

6.5E-05 6.5E-05 6.5E-05 6.5E-05 6.5E-05 6.5E-05 4.5E-05 3.0E-05 2.5E-05

- - - - - - - - -

V-0(1.5mm) V-0(1.5mm) V-0(1.5mm)5VA(3mm)

V-0(1.5mm)5VA(3mm) V-0(0.75mm)

V-1(1.5mm)V-0(2.5mm)5VB(2mm)5VA(3mm)

V-0(1.5mm)5VB(2.2mm) 5VA(3mm)

V-0(1.2mm) V-0(1.5mm)

3 3 3 3 3 2.9 3.1 3.25 3.4

2.9 2.9 2.9 2.9 2.9 2.8 3.0 3.2 3.4

6.6 6.6 6.6 6.6 6.6 6.6 9 9 9

92 92 92 92 92 92 90 90 90

>1E13 >1E13 >1E13 >1E13 >1E13 >1E13 >1E13 >1E13 >1E13

>1E15 >1E15 >1E15 >1E15 >1E15 >1E15 >1E15 >1E15 >1E15

29 29 29 29 29 29 29 29 29

2 2 2 2 2 2 3 3 3

130/125/125(1.5mm)f1

FC 19 UR(UV Stabilized)

130/125/125(1.5mm)f1


130/125/125(1.5mm)f1


130/125/125(1.5mm)f1


125/120/125(0.75mm) 130/125/125(1.5mm)f1

130/125/125(1.5mm)f1

130/125/125(1.5mm)f1

Polyme Alloy (PC/ABS) PC/PET LDS (Laser Direct Structuring)

CM206 CM406 CM506 CF107 MC3433 CF407 EM605 LDS3710 LDS3720 LDS3724 LDS3730 LDS3760

Vicat110℃ Vicat120℃ Vicat130℃ PhosphateHigh Flow

PhosphateImproved Impact

PhosphateHigh Heat Resistant

Chemical Resistant Black only Black only

Improved Impact Improved Impact Non Br & Non PBlack only

PhosphateHigh FlowBlack only

1.12 1.13 1.14 1.17 1.17 1.19 1.21 1.19 1.19 1.23 1.26 1.27

0.7 0.6 0.5 0.6 0.6 0.6 0.35 0.6 0.6 - 0.35 0.35

42 25 18 53 42 24 7 15 14 14 8 29

40 24 17 50 40 23 7 14 13 13.5 8 28

260 260 260 260 260 260 280 260 260 260 260 260

5 5 5 5.0 5 5.0 1.2 5 5 5 5 5

0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.4 - 0.6 0.4 - 0.6 0.4 - 0.6 0.6 - 0.8 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.4 - 0.6

0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.4 - 0.6 0.4 - 0.6 0.4 - 0.6 0.6 - 0.8 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.4 - 0.6

2100 2200 2300 2850 2850 2700 2200 2200 2250 2250 2200 2500

45 50 55 60 60 60 55 50 51 49 52 60

4 4 5 4 4 4 6 4 4 4 5 5

> 50 > 50 > 50 > 50 > 50 > 50 > 50 > 50 > 50 > 50 > 50 > 50

- - - - - - - - - - - -

- - - - - - - - - - - -

- - - - - - - - - - - -

75 80 85 110 110 95 80 80 80 77 80 90

2200 2250 2300 2800 2800 2700 2200 2250 2250 2200 2300 2400

NB NB NB NB NB NB NB NB NB NB NB NB

65 65 70 35 45 50 70 60 50 55 60 55

95 105 110 90 90 100 120 102 102 100 122 103

- - - - - - - - - - - -

7.0E-05 7.0E-05 7.0E-05 - - - 8.0E-05 7.0E-05 7.0E-05 7.0E-05 - -

7.0E-05 7.0E-05 7.0E-05 - - - 8.0E-05 7.0E-05 7.0E-05 7.0E-05 - -

HB(1.5mm) HB(1.5mm) HB(1.5mm)V-0(1.5mm)5VB(2mm)5VA(3mm)

V-0(1.5mm) V-0(1.5mm)5VB(3mm) - HB(1.56mm) HB(0.7mm) -

HB(0.5mm)V-0(1.5mm)5VB(3mm)

V-1(0.6mm)

- - - - - - - - - - - -

2.9 2.9 2.9 3 3 3 - 2.8 2.8 3 3 3

- - - - - - - - - - - -

- - - - - - - 50 50 60 50 50

>1E13 >1E13 >1E13 >1E13 >1E13 >1E13 - >1E13 >1E13 >1E13 >1E13 >1E13

>1E15 >1E15 >1E15 >1E15 >1E15 >1E15 - >1E15 >1E15 >1E15 >1E15 >1E15

35 35 35 - - - - - - - - -

0 2 2 1 2 - - - - - - -

95/80/80(1.5mm) 95/80/80(1.5mm) 95/90/90(1.5mm)

Xantar is a family of high-end engineering plastics.Xantar was established over two decades ago - and has been successful since then in a significant number of high-end market segments.Thanks to their excellent mechanical, thermal and electrical properties, Xantar grades are very widely and successfully used in industry segments such as Electrical & Electronics (E&E), Information & Communication Technology (ICT), Automotive, and General Industries.

1817


Grade


Physical properties


Water absorption -

23degC, 50%RH

%23degC,

Underwater 24hrs


Melt Mass-flow Rate

ISO 1133

- g/10min

Melt Volume-flow Rate

- cm3/10min

Temperature degC

Load kgf

Mold shrinkage100口 2mmt -

TDMD

Mold Temperature

%%℃


Tensile modulusISO 527-1

, 527-2 23 degC MPa

Stress at break

Strain at break %

Flexural strengthISO 178 23 degC MPa

Flexural modulus

Charpy impact strength

ISO 179-1, 179-2

23 degC kJ/m2


Thermal properties

Melting temperature ISO 11357-3 - degC

Glass transition temperature ISO 11357-2 - degC


ISO 75-1 , 75-2

1.80MPadegC

0.45MPa

Vicat softening temperature ISO 306 - degC

Coefficient of Linear thermal expansion ISO 11359-2

MD1/degC

TD

FlammabilityUL94 - -

UL94 1.6mmt -



1MHz -


1MHz -

Volume resistivity IEC 60093 - ohm-m

Surface resistivity IEC 60093 - ohm

Electric strength IEC 60243- 1

1mmt

MV/m 2mmt

3mmt

Comparative tracking index

IEC 60112 - -

UL746A - -

General High Strength

1002H 1012H 1022H 1022HS 1032H 2041 1025

GlassfiberReinforced

G30%


G40%


G50%


G50%


G60%

GlassfiberMineral

ReinforcedG

40%


G50%

dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH)

1.46 1.56 1.65 1.66 1.79 1.70 1.67

1.5 1.2 1.1 0.9 0.9 1.3 1.0

0.20 0.18 0.14 0.10 0.11 0.28 0.14

40.9 22.0 8.3 6 9.4 15.4 7.7

31.0 15.1 3.4 3 5.3 10.5 4.7

275 275 275 275 275 275 275

2.16 2.16 2.16 2.16 2.16 2.16 2.16

0.72 0.31 130

0.67 0.31 130

0.60 0.30 130

0.63 0.31 130

0.57 0.29 130

0.64 0.27 130

0.61 0.30 130

12100 (11100) 16600 (13600) 20400 (19300) 21850 (21000) 24700 (22400) 18300 (14100) 19600 (18300)

181 (148) 218 (177) 260 (214) 236 (233) 249 (204) 187 (136) 275 (229)

1.7 (1.8) 1.8 (1.8) 2.0 (2.1) 1.5 (1.6) 1.4 (1.4) 1.4 (1.6) 1.9 (2.0)

286 (265) 349 (306) 390 (318) 384 (326) 429 (357) 299 (230) 436 (385)

11600 (10700) 14900 (13800) 18400 (15100) 19100 (19000) 23200 (21600) 16200 (12800) 18800 (17600)

35 (33) 52 (52) 72 (58) 61 (40) 54 (61) 47 (54) 77 (82)

6.3 (6.2) 8.5 (8.9) 11.3 (12.2) 11.8 (12.0) 14.0 (13.9) 6.6 (7.3) 14.2 (13.1)

- - - - - - -

- - - - - - -

224 (212) 226 (218) 230 (223) 245 230 (223) 214 (204) 231 (225)

237 (232) 237 (232) 238 (233) - 237 (232) 231 (225) 238 (233)

- - - - - - -

2E-5 2E-5 1E-5 1E-5 1E-5 2E-5 1E-5

5E-5 5E-5 4E-5 4E-5 4E-5 5E-5 4E-5

- - - equal to HB - - equal to HB

HB HB HB - HB HB -

(5) - 5 (5) - (6) 5 (8) -

(4) - 5 (5) 4.7 (5) 5 (5) -

(0.020) - 0.007 (0.020) - (0.020) 0.008 (0.096) -

(0.016) - 0.008 (0.017) 0.009 (0.013) 0.009 (0.038) -

1E+14 (2E+13) - 2E+14 (1E+13) 1E+14 2E+13 (8E+12) (2E+11) -

7E+14 (2E+14) - 1E+16 (8E+14) 5E+15 2E+14 (8E+14) (5E+12) -

31 (29) - 27 (25) 33 26 (26) 22 (21) -

27 (22) - - 24 20 (20) 18 (15) -

- - - - - - -

525 (550) - 575 (550) - 550 (600<) 500 (500) -

- - - - - - -

Thick Parts Weather Resistance UV Resistance Flame Retardant

1071 1027HU 1002HUS 1021UCS 1501AH 1511AH 1521AH 2505 2502AH 1507 1527

GlassfiberReinforcedThick Parts

G55%


G50%


G30%


G50%


G30%


G40%


G50%


G15%

GlassfiberMineral

ReinforcedG

20%


NonHalogenG

30%


Non HalogenG

50%

dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH)

1.70 1.63 1.49 1.61 1.56 1.65 1.73 1.81 1.66 1.51 1.71

1.5 0.8 1.1 1.3 1.2 1.1 1.1 0.7 0.9 - -

0.10 0.14 - 0.47 0.19 0.15 0.13 0.13 0.18 - -

- 1.6 7 13.1 19.8 - - 11.0 21.6 - -

- 1.1 5 11.1 13.8 - - 6.2 14.0 - -

- 275 275 275 275 - - 275 275 - -

- 2.16 2.16 2.16 2.16 - - 2.16 2.16 - -

0.55 0.29 130

0.60 0.30 130

0.72 0.30 130

0.72 0.32 130

0.57 0.28 130

0.55 0.26 130

0.53 0.26 130

0.45 0.27 130

0.52 0.30 130

0.70 0.27 130

0.61 0.27 130

24900 (23700) 18700 (17200) 15000 17800 (14400) 13300 (11700) 16500 (12700) 20600 13900 (13600) 18400 (14900) 12500 19000

264 (237) 227 (197) 192 252 (184) 162 (135) 197 (171) 215 124 (109) 150 (120) 169 220

1.6 (1.6) 1.6 (1.7) 1.4 2.5 (3.4) 1.6 (1.6) 1.8 (2.0) 2 1.2 (1.1) 1.2 (1.3) 1.8 1.6

423 (384) 329 (292) 308 392 (305) 251 (222) 302 (249) 339 200 (176) 249 (209) 288 360

20600 (20900) 18300 (15900) 13100 18300 (13800) 12100 (11800) 15000 (12700) 18900 13600 (12900) 16500 (14700) 12000 20000

83 (66) 45 (45) 48 87 (101) 37 (29) 45 (46) 49 25 (20) 27 (29) 52 61

17.0 (16.0) 9.0 (9.2) 7.0 14.1 (16.4) 5.3 (5.5) 7.7 (7.6) 9.3 3.2 (3.0) 4.1 (4.3) 7.8 12.0

- - - - - - - - - - -

- - - - - - - - - - -

230 221 (215) 237 217 (210) 220 (211) 224 (216) 228 215 (205) 217 (206) 222 231

- 233 (231) - 227 (221) 237 (232) 237 (233) 238 236 (231) 235 (229) - -

- - - - - - - - - - -

1E-5 - - - 2E-5 - - - 2E-5 - -

3E-5 - - - 5E-5 - - - 3E-5 - -

equal to HB equal to HB equal to HB equal to HB - - - - - - -

- - - - V-0 V-0 V-0 V-0 V-0 V-0 V-0

- - - - (5) - - - (5) - -

- - - - (4) 4.4 - - (5) - -

- - - - (0.016) - - - (0.050) - -

- - - - (0.014) 0.009 - - (0.017) - -

- - - - 1E+14 (1E+13) 7E+14 - - 2E+14 (1E+13) - -

- - - - 8E+14 (4E+14) 6E+15 - - 5E+15 (2E+14) - -

- - - - 29 (26) 33 - - 27 (26) - -

- - - - 22 (19) 24 20 - 21 (20) - -

- - - - - - 17 - - - -

- - - - 450 (400) 325 350 600< 200 (300) 325 325

- - - - - - - - - - -

Special features:1. Excellent mechanical strength and modulus over a wide

range of temperatures2. Superior to commodity polyamides in dimensional

stability and mechanical strength due to low water absorption

3. Low thermal expansion coefficient, equivalent to that of metal alloys

4. Highly resistant to oils and organic solvents5. Low mold shrinkage and low warpage6. Good surface finish even in highly filled grades

Reny is a proprietary molding compound based on mainly polyamide MXD6 that has been reinforced with glass fiber, carbon fiber or special minerals. Reny generally has superior mechanical strength and modulus compared with other engineering plastics. Thus, Reny is suitable as a metal substitute in many applications, including automobiles, electronics, electrical appliances, machinery, and construction.


2019


High Impact Painting Low Warpage High Rigidity Electroconductive

1313H 1322 1371 1722F 2620 2686 2051DS N-252 4001 4011


G40%


G50%


G55%


G50%

Glassfiber MineralReinforced

G20%

GlassbeadsReinforced

GB65%

GlassfiberMineral

ReinforcedG

20%

Glassfiber Mineral

ReinforcedG

25%


G30%


G40%

dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH)

1.47 1.60 1.66 1.65 1.66 1.80 1.62 1.72 1.50 1.66

1.2 - 0.9 0.7 1.3 0.7 - 1.1 1.00 0.9

0.21 - 0.11 0.13 0.14 0.11 - 0.24 0.09 0.09

2.3 - - 19.8 17.5 7.6 - 2.6 5.0 6.3

2.7 - - 12.5 12.3 6.9 - 1.9 3.4 4.5

275 - - 275 275 275 - 275 275 275

2.16 - - 2.16 2.16 2.16 - 2.16 2.16 2.16

0.65 0.27 130

0.58 0.25 130

0.55 0.23 130

0.61 0.28 130

0.59 0.32 130

0.70 0.69 130

0.78 0.35 130

0.36 0.22 130

0.64 0.29 130

0.60 0.29 130

12000 (11000) 18100 20800 20700 (19100) 17600 (11500) 9800 (7300) 15800 25700 (22200) 17900 (14700) 21600 (18600)

162 (136) 245 242 244 (208) 139 (86) 73 (52) 192 174 (138) 124 (126) 152 (143)

2.0 (2.4) 2.1 1.9 2.0 (1.7) 1.1 (1.3) 1.7 (1.8) 1.7 11 (1.4) 0.9 (1.1) 1.0 (1.1)

258 (219) 387 403 381 (319) 236 (151) 147 (103) 312 289 (219) 204 (188) 235 (228)

11600 (10900) 16500 19600 18900 (18800) 16000 (10900) 9600 (6600) 15100 21900 (17000) 16600 (14100) 19800 (19100)

66 (55) 94 93 58 (54) 27 (35) 32 (40) 64 31 (33) 19 (17) 16 (16)

12.2 (12.7) 17.0 15.7 11.4 (10.4) 4.1 (5.1) 2.2 (2.4) 8.0 5.9 (6.6) 5.2 (4.8) 7.3 (7.5)

- - - - - - - - - -

- - - - - - - - - -

217 (207) 225 227 226 (219) 214 (196) 147 (116) 242 227 (220) 224 (213) 226 (216)

235 (231) - 236 237 (235) 234 (231) 213 (207) - 236 (231) 236 (232) 235 (232)

- - - - - - - - - -

2E-5 - - - 1E-5 - 2E-5 2E-5 - 1E-5

6E-5 - - - 4E-5 - 5E-5 4E-5 - 4E-5

- equal to HB - - - - equal to HB - - -

HB equal to HB HB HB HB HB - HB HB HB

(5) - - - - - - 5 (5) - -

(4) - - - - - - 5 (5) - -

(0.020) - - - - - - 0.011 (0.011) - -

(0.015) - - - - - - 0.008 (0.018) - -

1E+14 (1E+13) - - - - - - 6E+13 (7E+12) - 3E+02 (6E+08)

1E+15 (3E+14) - - - - - - 4E+15 (2E+14) - 5E+05 (3E+06)

27 (28) - - - - - - 21 (20) - -

24 (22) - - - - - - - - -

- - - - - - - - - -

600< (600<) - - - - - - 325 (250) - -

- - - - - - - - - -

Electroconductive Low Friction & Wear Resistance Carbonfiber NX series PG series

4501 4511 W-38S2 G-07S G-09S G-16S F-34S C-36 C-56 NXG5050 NXG5050NF NXG5945S PG-1050A


G30%


G40%

Potassium-Titanate Whisker

ReinforcedW

30%


G20%


W50%

CarbonfiberReinforced

C20%

Potassium-Titanate Whisker

ReinforcedW

30%


C30%


C50%


G50%

GlassfiberNon Halogen

Flame RetardantG

50%


G45%


G50%

dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH) dry(50%RH)

1.66 1.77 1.64 1.52 1.71 1.43 1.58 1.35 1.44 1.62 1.67 1.52 1.57

0.80 0.7 1.0 1.1 0.9 1.1 - 1.4 - 0.9 0.9 0.7 0.8

0.06 0.06 0.12 0.13 0.10 0.12 0.20 0.25 - 0.17 0.16 - 0.06

10.1 1.8 48.5 15.7 4.6 8.8 - 12.0 10.0 4.5 - 12.7 5.5

7.5 1.0 31.2 10.9 2.7 6.1 - 10.3 7.0 3.7 - 8.5 2.8

275 275 275 275 275 275 - 275 280 275 - 280 275

2.16 2.16 2.16 2.16 2.16 2.16 - 2.16 5.00 2.16 - 5.0 2.16

0.53 0.22 130

0.51 0.22 130

0.65 0.35 130

0.73 0.36 130

0.62 0.33 130

0.51 0.18 130

0.77 0.38 130

0.43 0.14 130

0.32 0.10 130

0.58 0.24 130

0.55 0.25 130

0.53 0.24 130

0.66 0.28 130

20400 (16200) 20900 (20600) 16200 (15900) 9200 (9100) 19700 (19000) 20200 (19900) 12500 27200 (24200) 45000 (43800) 18800 (17400) 21900 16000 (15400) 19100 (18700)

107 (113) 130 (125) 121 (111) 155 (136) 250 (220) 230 (205) 120 249 (230) 304 (227) 205 (191) 198 208 (202) 215 (205)

0.7 (0.9) 0.6 (0.8) 0.9 (0.8) 2.5 (2.5) 1.9 (2.1) 1.6 (1.6) 1.0 1.2 (1.3) 0.6 (0.6) 1.5 (1.7) 1.2 2.0 (2.2) 1.7 (2.0)

190 (184) 215 (208) 226 (216) 230 (200) 382 338 (294) 205 411 (359) 517 (443) 338 (304) 348 349 (315) 363 (326)

19100 (15500) 22200 (22000) 15200 (15100) 9000 (8900) 18700 18800 (18200) 12500 23400 (21800) 43000 (41300) 16800 (16400) 18200 14300 (14000) 17400 (17100)

14 (15) 12 (12) 18 (22) 38 (37) 61 50 (39) 33 45 (48) 50 (33) 68 (58) 67 90 (77) 59 (55)

7.5 (6.6) 6.9 (8.9) 1.8 (2.1) 6.0 (5.9) 11.0 4.4 (4.5) 1.9 4.7 (4.9) 6 (6) 9.6 (9.6) 13 14.7 (13.8) 17.4 (18.4)

- - - - - - - - - - - 257 -

- - - - - - - - - - - 87 -

225 (216) 223 (218) 210 (206) 236 (227) 246 (240) 240 (234) 206 224 (218) 232 (222) 221 (216) 219 232 224 (220)

236 (232) 234 (232) 239 (239) 255 (251) 255 (253) - - 236 (232) 237 235 (231) - - 236 (233)

- - - - - - - - - - - - -

- 8E-6 2E-5 - - - - 5E-6 6E-6 1E-5 - 1E-5 1E-5

- 4E-5 4E-5 - - - - 5E-5 5E-5 4E-5 - 6E-5 5E-5

- - equal to HB - - - equal to HB - - - - - equal to HB

V-0 V-0 - HB HB HB - HB - HB V-0 HB -

- - - - - - - - - (5) - 4.2 (4.6) (5)

- - - - - - - - - (5) - 4.1 (4.2) (4)

- - - - - - - - - (0.018) - 0.006 (0.020) (0.026)

- - - - - - - - - (0.013) - 0.007 (0.012) (0.012)

- 3E+00 (7E+06) 2E+13 - 2E+13 - - 6E-03 (2E+05) 2E+4 1E+14 (4E+12) - - 2E+14 (8E+12)

- 5E+03 (4E+04) 2E+14 - 2E+14 - - 2E+01 (3E+03) 4E+3 1E+15 (2E+14) - - 6E+16 (1E+14)

- - 26 - 26 - - - - 26 (23) 25 - 29 (28)

- - - - - - - - - 21 (18) - - 23 (21)

- - - - - - - - - - - - -

- - - - - - - - - 200 (250) 250 - 600< (600<)

- - - - - - - - - - - - -


Grade


Physical properties


Water absorption -

23degC, 50%RH

%23degC,

Underwater 24hrs


Melt Mass-flow Rate

ISO 1133

- g/10min

Melt Volume-flow Rate

- cm3/10min

Temperature degC

Load kgf

Mold shrinkage100口 2mmt -

TDMD

Mold Temperature

%%℃


Tensile modulusISO 527-1

, 527-2 23 degC MPa

Stress at break

Strain at break %

Flexural strengthISO 178 23 degC MPa

Flexural modulus


ISO 179-1, 179-2

23 degC kJ/m2


Thermal properties


Glass transition temperature ISO 11357-2 - degC


ISO 75-1 , 75-2

1.80MPadegC

0.45MPa

Vicat softening temperature ISO 306 - degC


MD1/degC

TD

FlammabilityUL94 - -

UL94 1.6mmt -



1MHz -


1MHz -




1mmt

MV/m 2mmt

3mmt

Comparative tracking index

IEC 60112 - -

UL746A - -

2221


Grade


Physical properties


Water absorption - 23degC, Underwater %

Demensional properties

Moulding shrinkage (100×100×2mmt) -

MD%

TD


Tensile modulus

ISO 527-1 , 527-2 -

MPaYield stress

Yield strain%


Stress at 50% strainMPa

Stress at break

Strain at break %


Flexural modulus


ISO 179-1, 179-2

23 degC kJ/m2


Thermal properties



ISO 75-1 , 75-2

1.80MPadegC

0.45MPa


ISO 11359-2

MD : -30~120degC

1/degC

MD : -30~35degC

MD : 35~120degC

TD : -30~120degC

TD : -30~35degC

TD : 35~120degC



Relative permittivity IEC 60250 1MHz -

Dissipation factor IEC 60250 1MHz -




1mmt

MV/m 2mmt

3mmt

Comparative tracking index UL746A - -

Unreinforced UL-HB type

5010R3-2 5010R5 5010R5-L2 5010CR2 5010TRXA 5010TRX5 5010R8M 5020 5026

High Toughness Standard Easy Flow High Cycle Moldable

Impact Modified

Highly ImpactModified

ImprovedFlexibility Extrusion Extrusion

High Viscosity

1.31 1.31 1.31 1.31 1.27 1.26 1.30 1.31 1.31

0.10 0.10 0.10 0.10 0.10 0.10 0.09 0.10 0.10

1.9 1.9 1.9 2.2 1.9 2.0 2.0 1.9 1.9

1.8 1.8 1.8 2.1 1.8 1.8 1.9 1.8 1.8

2550 2550 2550 2770 2500 2340 1550 2550 2550

55 55 56 60 51 47 45 51 51

4 4 4 4 4 3 11 4 4

>200 170 135 70 >200 140 >200 >200 >200

- - - - - - - - -

- - - - - - - - -

- - - - - - - - -

80 80 80 86 77 70 56 76 75

2300 2300 2350 2540 2250 2200 1650 2300 2300

NB NB >200 >200 NB NB >200 NB NB

6 6 4 4 7 10 6 5 5

224 224 224 224 224 224 222 224 224

67 67 67 77 65 65 70 65 65

165 165 165 170 160 155 155 155 154

12.E-05 12.E-05 12.E-05 12.E-05 12.E-05 12.E-05 14.E-05 12.E-05 12.E-05

8.E-05 8.E-05 8.E-05 8.E-05 8.E-05 9.E-05 11.E-05 8.E-05 8.E-05

14.E-05 14.E-05 14.E-05 14.E-05 14.E-05 14.E-05 17.E-05 14.E-05 14.E-05

12.E-05 12.E-05 12.E-05 12.E-05 12.E-05 12.E-05 14.E-05 12.E-05 12.E-05

9.E-05 9.E-05 9.E-05 9.E-05 9.E-05 9.E-05 11.E-05 9.E-05 9.E-05

15.E-05 15.E-05 15.E-05 15.E-05 15.E-05 15.E-05 16.E-05 15.E-05 15.E-05

HB (0.83mmt) HB (0.83mmt) HB (0.83mmt) HB (0.83mmt) HB (0.75mmt) HB (0.75mmt) HB (0.83mmt) HB (0.8mmt) HB (0.8mmt)

3.3 3.3 3.3 3.3 3.3 3.4 3.4 3.2 3.2

0.022 0.022 0.022 0.022 0.025 0.027 0.025 0.020 0.020

4E+14 4E+14 4E+14 4E+14 1E+14 1E+14 1E+14 1E+14 1E+14

3E+15 3E+15 3E+15 3E+15 5E+15 5E+15 4E+15 1E+14 1E+14

22 22 22 22 22 23 23 22 22

17 17 17 17 17 17 17 17 17

- - - - - - - - -

PLC 0 PLC 0 PLC 0 PLC 0 - - PLC 0 - -

Unreinforced UL-HB type Unreinforced Flame Retardant GF Reinforced UL-HB type GF Reinforced toughness UL-HB type

5505S 5510S 5010N6-3X SEF-500T 5010G15 5010G30 5010G45 5010G30X4 5010GT15 5010GT30 5010GT15X 5010G30TZ

ExtrusionImproved Flexibility

ExtrusionHighly Improved

FlexibilityV-0

Non-BromineHigh Tracking

Resistance

StandardGF15

StandardGF30

StandardGF45

ImprovedHydrolytic Resistance

GF30

ImprovedToughness

GF15

ImprovedToughness

GF30

Improved ThermalShock Durability

GF15

Improved ThermalShock Durability

GF30

1.28 1.24 1.43 1.31 1.41 1.53 1.67 1.53 1.40 1.51 1.39 1.50

0.10 0.40 0.08 0.08 0.08 0.07 0.06 0.07 0.09 0.08 0.09 0.08

2.2 2.2 1.9 2.2 0.5 0.4 0.4 0.4 0.6 0.4 0.6 0.4

2.0 2.0 1.8 1.8 1.3 1.2 0.9 1.2 1.2 1.1 1.1 1.0

1000 420 2800 2700 5800 9500 15000 9700 5200 9000 4100 8700

28 21 57 35 - - - - - - - -

19 21 4 - - - - - - - - -

>200 >200 20 40 - - - - - - - -

- - - - - - - - - - - -

- - - - 110 140 165 150 85 110 85 115

- - - - 3 3 2 3 3 4 5 4

31 22 90 62 165 215 260 220 135 180 130 180

740 360 2500 2200 5500 9000 14500 9100 5000 8600 4000 8000

NB NB 120 62 24 59 60 59 40 63 69 64

13 30 3 6 7 10 14 11 6 10 12 12

222 219 224 224 224 224 224 224 224 224 224 224

67 74 77 86 198 207 209 208 188 191 175 178

145 139 165 180 215 >220 >220 >220 212 217 206 208

14.E-05 15.E-05 12.E-05 14.E-05 3.E-05 2.E-05 1.E-05 2.E-05 3.E-05 2.E-05 3.E-05 2.E-05

11.E-05 14.E-05 8.E-05 11.E-05 3.E-05 2.E-05 1.E-05 2.E-05 3.E-05 2.E-05 3.E-05 2.E-05

17.E-05 17.E-05 14.E-05 17.E-05 3.E-05 2.E-05 1.E-05 2.E-05 3.E-05 2.E-05 3.E-05 2.E-05

14.E-05 15.E-05 12.E-05 14.E-05 12.E-05 11.E-05 10.E-05 11.E-05 13.E-05 12.E-05 14.E-05 13.E-05

11.E-05 14.E-05 9.E-05 11.E-05 9.E-05 8.E-05 7.E-05 8.E-05 10.E-05 9.E-05 11.E-05 10.E-05

16.E-05 17.E-05 15.E-05 16.E-05 14.E-05 14.E-05 13.E-05 14.E-05 15.E-05 15.E-05 16.E-05 16.E-05

HB (0.8mmt) - V-0 (0.71mmt) V-0 (0.75mmt) HB (0.84mmt) HB (0.8mmt) HB (0.75mmt) HB (0.8mmt) HB (1.5mmt) HB (1.5mmt) HB (1.5mmt) HB (0.8mmt)

3.2 3.2 3.2 3.5 3.2 3.4 3.4 3.4 3.2 3.4 3.2 3.4

0.020 0.020 0.020 0.019 0.020 0.016 0.016 0.016 0.020 0.016 0.020 0.016

1E+14 1E+14 1E+14 1E+14 5E+14 2E+14 2E+14 6E+14 4E+13 4E+14 4E+13 3E+13

1E+15 1E+15 1E+15 1E+15 4E+16 5E+16 5E+16 4E+15 3E+15 3E+15 3E+15 1E+15

22 22 21 - 24 27 28 27 24 30 24 30

17 17 18 22 21 24 25 25 21 24 21 24

- - - - - - - - - - - -

- - PLC 1 PLC 0 - PLC 1 PLC 1 PLC 1 - - - PLC 1

Novaduran offers excellent mechanical properties, rigidity, heat aging resistance and chemical resistance. Novaduran also provides superb moldability, abrasion resistance, colorability and electric properties. Recently, demand for PBT has been growing sharply, particularly in the electronics and automobile industries. Mitsubishi Engineering-Plastics produces PBT in an integrated manufacturing process using the raw materials dimethyl terephthalate and 1, 4-butylene glycol.

Special features:1. Excellent mechanical properties2. Excellent heat resistance3. Excellent moldability and flowability4. Low moisture absorption rate for high dimensional

stability5. Excellent surface gloss and color

6. Excellent oil and chemical resistance7. Excellent electrical properties8. Excellent friction and abrasion resistance9. Flame retardant grades also available


2423


GF Reinforced Alloy

5308F20 5710G30S2 5710F40 5810G15 5810G30 5820G30H 5810G40 5820G40H

Excellent SurfaceGlossMD20

Low WarpageImproved Surface

AppearanceGF30

Superior Low WarpageImproved Surface

AppearanceGF+GS

40

Low WarpageLow Density

GF15


GF30

Low WarpageHigh Strength

GF30


GF40

Low WarpageHigh Strength

GF40

1.49 1.51 1.57 1.29 1.44 1.50 1.53 1.58

0.10 0.07 0.07 0.08 0.08 0.07 0.08 0.07

1.4 0.4 0.3 0.5 0.3 0.4 0.3 0.3

1.6 0.8 0.6 0.7 0.5 1.0 0.6 0.9

5200 10500 11300 5500 9400 10500 13000 12500

- - - - - - - -

- - - - - - - -

- - - - - - - -

- - - - - - - -

58 130 110 90 120 145 130 160

2 2 2 3 2 2 1 2

100 190 167 135 185 210 195 240

5000 9000 10400 5300 9000 9500 12000 11500

25 52 50 50 59 50 60 50

2 9 9 9 10 7 11 9

- 224 224 224 224 224 224 224

115 194 203 - 185 205 190 208

195 220 >220 210 217 >220 218 >220

6.E-05 1.E-05 1.E-05 3.E-05 2.E-05 2.E-05 1.E-05 1.E-05

5.E-05 1.E-05 1.E-05 3.E-05 2.E-05 2.E-05 1.E-05 1.E-05

8.E-05 1.E-05 1.E-05 3.E-05 2.E-05 2.E-05 1.E-05 1.E-05

8.E-05 10.E-05 9.E-05 11.E-05 10.E-05 11.E-05 9.E-05 10.E-05

6.E-05 7.E-05 7.E-05 9.E-05 8.E-05 8.E-05 7.E-05 7.E-05

9.E-05 12.E-05 11.E-05 12.E-05 12.E-05 14.E-05 11.E-05 13.E-05

- - - - HB (0.75mmt) - - -

3.3 3.4 3.4 3.2 3.2 3.3 3.2 3.3

0.014 0.020 0.020 0.017 0.017 0.017 0.017 0.017

3E+14 9E+14 5E+14 2E+15 2E+15 6E+14 1E+14 6E+14

3E+15 5E+15 2E+16 1E+16 7E+15 6E+15 1E+16 9E+15

- 28 28 - 40 33 40 32

- 24 24 20 30 30 30 26

- - - - - - - -

- - - - - - - -

GF Reinforced Flame Retardant

5010GN1-15AM 5010GN1-30AM2 5010GN1-15-8S 5010GN2-30X2 5010GN6-15M8AM 5010GN6-15M8X 5010GN6-15T 5010GN6-20M8X 5010GN6-30 5010GN6-30M8X 5010GN6-30T

StandardGF15

StandardGF30

ImprovedFlexibility

GF15

StandardGF30

Low OutgasTracking Resistance

GF15

Low Outgas0.3mmt V-0

Tracking ResistanceGF15

ImprovedFlexibility




StandardLow Outgas




ImprovedToughness


1.54 1.66 1.52 1.66 1.55 1.57 1.53 1.62 1.66 1.71 1.64

0.07 0.07 0.07 0.07 0.07 0.07 0.07 0.07 0.07 0.07 0.07

0.4 0.5 0.6 0.4 0.7 0.8 0.7 0.7 0.5 0.5 0.5

1.2 1.2 1.4 1.1 1.6 1.7 1.5 1.5 1.3 1.2 1.2

6700 11000 6300 11000 6700 6800 6900 8400 11000 11000 11200

- - - - - - - - - - -

- - - - - - - - - - -

- - - - - - - - - - -

- - - - - - - - - - -

110 140 100 135 110 105 100 116 142 142 125

3 2 3 2 3 3 3 3 3 3 3

170 220 150 210 170 165 150 186 215 215 195

6200 10500 5400 10500 6100 6600 5900 7900 10500 10500 9900

25 46 29 45 30 30 53 54 55 55 55

6 10 7 9 7 7 8 8 10 10 10

224 224 224 224 224 224 224 224 224 224 224

197 206 195 208 198 198 195 195 206 208 204

217 >220 215 >220 218 216 216 216 >220 >220 >220

3.E-05 1.E-05 4.E-05 2.E-05 3.E-05 3.E-05 3.E-05 3.E-05 2.E-05 2.E-05 2.E-05

3.E-05 1.E-05 4.E-05 2.E-05 3.E-05 3.E-05 3.E-05 3.E-05 2.E-05 2.E-05 2.E-05

3.E-05 1.E-05 4.E-05 2.E-05 3.E-05 3.E-05 3.E-05 3.E-05 2.E-05 2.E-05 2.E-05

12.E-05 11.E-05 13.E-05 11.E-05 12.E-05 12.E-05 12.E-05 12.E-05 11.E-05 11.E-05 11.E-05

8.E-05 7.E-05 9.E-05 7.E-05 8.E-05 8.E-05 8.E-05 8.E-05 8.E-05 7.E-05 8.E-05

15.E-05 13.E-05 16.E-05 14.E-05 15.E-05 15.E-05 15.E-05 15.E-05 14.E-05 14.E-05 14.E-05

V-0 (0.71mmt) V-0 (0.71mmt) V-0 (0.71mmt) V-0 (0.81mmt) V-0 (0.75mmt) V-0 (0.30mmt) V-0 (0.71mmt) V-0 (0.30mmt) V-2 (0.38mmt) V-0 (0.76mmt)

V-0 (0.25mmt/BK) V-0 (0.30mmt/ALL) V-0 (0.71mmt)

3.7 3.9 3.7 3.9 3.7 3.7 3.7 3.7 3.9 3.9 3.9

0.017 0.014 0.017 0.014 0.017 0.017 0.017 0.017 0.014 0.014 0.014

2E+15 3E+14 4E+14 5E+14 3E+14 3E+14 3E+13 1E+15 3E+14 3E+14 4E+13

9E+15 6E+15 6E+15 6E+15 4E+16 4E+16 2E+16 2E+16 6E+15 6E+15 2E+15

23 24 23 24 23 23 23 - 24 24 24

- - - - - - - - - - -

- - - - - - - - - - -

PLC 3 PLC 3 PLC 3 PLC 3 PLC 2 PLC 2 PLC 2 PLC 2 PLC 2 PLC 2 PLC 2

5VA 1.5mmt


Grade


Physical properties





MD%

TD


Tensile modulus

ISO 527-1 , 527-2 -

MPaYield stress

Yield strain%



Stress at break

Strain at break %


Flexural modulus


ISO 179-1, 179-2

23 degC kJ/m2


Thermal properties



ISO 75-1 , 75-2

1.80MPadegC

0.45MPa


ISO 11359-2

MD : -30~120degC

1/degC

MD : -30~35degC

MD : 35~120degC

TD : -30~120degC

TD : -30~35degC

TD : 35~120degC








1mmt

MV/m 2mmt

3mmt


2625


GF Reinforced Flame Retardant GF Reinforced Alloy Flame Retardant

SEF-515T SEF-515X SEF-530 SEF-530X 5010CTN33 5010GPN33 5830GN6-40 5810GN6-30 5817GN2-30

Non-Bromine HighTracking Resistance

GF15


Low OutgasGF15


GF30


Low OutgasGF30

ImprovedTracking

ResistanceGF+MD

33

Highly ImprovedTracking

ResistanceGF+MD

33

Improved Glow WireResistance and

Tracking ResistanceGF+MD

40

Low WarpageGF30

Low WarpageGF30

1.44 1.44 1.58 1.55 1.71 1.64 1.70 1.58 1.53

0.07 0.07 0.07 0.07 0.07 0.07 0.07 0.07 0.07

0.5 0.5 0.4 0.4 0.6 0.6 0.4 0.3 0.3

1.2 1.2 1.1 1.1 1.0 1.0 1.0 0.6 0.6

5300 6400 11000 11000 9100 7200 11500 10300 11000

- - - - - - - - -

- - - - - - - - -

- - - - - - - - -

- - - - - - - - -

75 80 90 110 90 75 100 114 136

3 3 1 2 2 2 1 2 2

110 123 150 165 145 110 150 172 196

5300 6300 10800 10800 8700 7000 10700 9700 9800

37 40 32 43 35 39 32 35 44

9 6 8 7 5 6 7 10 10

224 224 224 224 224 224 224 224 224

208 208 215 210 205 174 206 183 182

>220 >220 >220 >220 >220 210 212 213 210

3.E-05 3.E-05 2.E-05 2.E-05 3.E-05 2.E-05 1.E-05 1.E-05 1.E-05

3.E-05 3.E-05 2.E-05 2.E-05 2.E-05 2.E-05 1.E-05 1.E-05 1.E-05

3.E-05 3.E-05 2.E-05 2.E-05 3.E-05 3.E-05 1.E-05 1.E-05 1.E-05

12.E-05 11.E-05 9.E-05 9.E-05 10.E-05 10.E-05 9.E-05 10.E-05 10.E-05

9.E-05 8.E-05 7.E-05 7.E-05 7.E-05 6.E-05 7.E-05 7.E-05 7.E-05

15.E-05 13.E-05 11.E-05 11.E-05 12.E-05 13.E-05 11.E-05 12.E-05 12.E-05

V-0 (0.75mmt) V-0 (0.75mmt) V-0 (0.75mmt) V-0 (0.75mmt) V-0 (0.75mmt) V-0 (0.38mmt) V-0 (0.3mmt) V-0 (0.35mmt/BK) V-0 (0.75mmt/ALL) V-0 (1.5mmt)

3.8 3.6 4.1 3.9 3.9 3.9 3.9 3.9 3.9

0.020 0.015 0.013 0.013 0.016 0.016 0.015 0.015 0.015

4E+13 4E+13 3E+14 3E+14 2E+14 1E+15 4E+14 4E+14 3E+14

2E+16 2E+16 2E+16 2E+16 1E+16 4E+15 4E+15 4E+15 2E+16

- - - - 25 25 24 - -

26 27 27 30 - - - 20 24

- - - - - - - - 17

PLC 0 PLC 0 PLC 0 PLC 0 PLC 1 PLC 0 PLC 2 PLC 2 PLC 3


Grade


Physical properties





MD%

TD


Tensile modulus

ISO 527-1 , 527-2 -

MPaYield stress

Yield strain%



Stress at break

Strain at break %


Flexural modulus


ISO 179-1, 179-2

23 degC kJ/m2


Thermal properties



ISO 75-1 , 75-2

1.80MPadegC

0.45MPa


ISO 11359-2

MD : -30~120degC

1/degC

MD : -30~35degC

MD : 35~120degC

TD : -30~120degC

TD : -30~35degC

TD : 35~120degC








1mmt

MV/m 2mmt

3mmt


2827


Standard

F10-01F10-02 F20-03 F25-03 F30-03 F40-03 F20-54 F20-61 FV30 F10-EW F20-EW

HighViscosity

-01:For Extruding Molding-02:For General Molding

MediumViscosity

For General Molding

MediumViscosity

For General Molding

LowViscosity

For General Molding

LowViscosity

For General Molding

WeatherResistanceImprovedGeneral

AntistaticAntistaticand LowViscosity

High ViscosityFor water fitting

application

Medium Viscosity

For water fitting application

1.41 1.41 1.41 1.41 1.41 1.41 1.41 1.41 1.41 1.41

0.22 0.22 0.22 0.22 0.22 0.22 0.22 0.22 0.22 0.22

2.5 9.0 16 27 52 9.0 9.0 31 - -

2.2 7.7 14 23 45 7.7 7.7 27 3.4 7.7

190 190 190 190 190 190 190 190 190 190

2.16 2.16 2.16 2.16 2.16 2.16 2.16 2.16 2.16 2.16

2.2 2.0 2.0 2.0 2.0 2.0 2.0 2.0 - 2.0

- - - - - - - - - -

2800 2900 2900 2900 2900 2800 2800 2800 2750 2900

63 64 64 64 64 62 63 63 62 64

10 8.5 8.0 7.5 7.0 8.5 8.5 8.5 10 8.5

33 30 27 25 20 30 30 30 35 30

- - - - - - - - - -

- - - - - - - - - -

89 90 90 91 91 88 88 88 88 90

2500 2600 2600 2700 2700 2500 2500 2500 2450 2600

280 250 200 150 100 240 230 150 - 250

8.0 7.0 6.5 6.0 5.0 6.5 6.0 6.0 8.0 7.0

166 166 166 166 166 166 166 166 165 166

100 100 100 100 100 100 100 100 100 100

156 156 156 156 156 156 156 156 - -

1.1E-04 1.1E-04 1.1E-04 1.1E-04 1.1E-04 1.1E-04 1.1E-04 1.1E-04 1.1E-04 1.1E-04

1.1E-04 1.1E-04 1.1E-04 1.1E-04 1.1E-04 1.1E-04 1.1E-04 1.1E-04 1.1E-04 1.1E-04

HB HB HB HB HB HB HB HB HB HB

3.9 3.9 3.9 3.9 3.9 - - - - -

3.9 3.9 3.9 3.9 3.9 - - - - -

0.002 0.002 0.002 0.002 0.002 - - - - -

0.007 0.007 0.007 0.007 0.007 - - - - -

1E+12 1E+12 1E+12 1E+12 1E+12 1E+12 1E+11 1E+11 - -

1E+16 1E+16 1E+16 1E+16 1E+16 1E+16 1E+13 1E+13 - -

32 32 32 32 32 - - - - -

19 19 19 19 19 - - - - -

600 600 600 600 600 - - - - -

Standard High Rigdity Reinforced/Filled Low friction and Wear-Resistant

FRC-20 F20-73R1 A10-03 A25-03 FG2025 MF3020 FB2025 FC2020D FC2020H FT2010 FT2020 LO-21A FX-11 FX-11J WA-11H

Chlorine resistant

LowEmission of

Formaldehyde

HighViscosityGeneral

MediumViscosityGeneral

GlassfiberReinforcedGlassfiber

25%

MilledfiberReinforcedMilledfiber

20%

GlassbeadFilled25%

Electro-ConductiveCarbonfiber

20%

HighRigidity

Carbonfiber20%

WhiskerFilled

Whisker10%

WhiskerFilled

Whisker20%

Lubricant Lubricant Lubricant Lubricant

1.39 1.41 1.41 1.41 1.59 1.55 1.59 1.46 1.46 1.49 1.59 1.39 1.39 1.39 1.39

0.29 0.22 0.22 0.22 0.20 0.20 0.20 0.36 0.28 0.23 0.23 0.22 0.22 0.22 0.22

- 9.1 2.5 14 9.0 20 5.0 3.5 6.0 7.5 5.5 10 10 53 29

8.3 7.9 2.2 12 6.3 15 3.8 3.2 5.4 5.9 4.0 8.6 8.6 46 25

190 190 190 190 190 190 190 190 190 190 190 190 190 190 190

2.16 2.16 2.16 2.16 2.16 2.16 2.16 2.16 2.16 2.16 2.16 2.16 2.16 2.16 2.16

2.0 2.0 2.2 2.1 0.6 1.7 1.6 0.4 0.4 1.7 0.9 2.0 2.1 2.1 2.1

- 2.0 - - - - - - - - - - - - -

- 2900 2900 3050 10000 4500 4000 17000 17000 5200 7800 2700 2700 2700 2900

57 65 67 69 - - - - - - - 56 55 55 58

- 8.5 9.0 11.0 - - - - - - - 9.0 9.0 7.5 8.0

42 30 35 35 - - - - - - - 40 35 25 21

- - - - 140 60 60 130 170 73 87 - - - -

- - - - 3.0 4.0 6.0 1.5 2.0 5.5 4.5 - - - -

77 91 94 98 210 100 100 200 270 120 160 80 81 81 89

2300 2610 2750 2950 9100 3900 3700 16000 16000 4800 7600 2500 2500 2500 2800

- 250 280 250 60 40 60 30 50 90 50 150 200 100 150

8.0 7.0 8.0 8.0 9.0 4.0 4.0 4.5 7.0 5.0 4.0 7.0 7.0 5.0 5.0

165 166 168 170 166 166 166 166 166 166 166 166 166 166 170

94 100 104 105 162 118 115 162 162 140 154 100 95 95 100

- 156 158 160 164 160 158 164 164 160 163 156 156 156 -

- 1.1E-04 1.1E-04 1.1E-04 3.0E-05 - - - 1.5E-05 - - 1.1E-04 1.1E-04 1.1E-04 1.1E-04

- 1.1E-04 1.1E-04 1.1E-04 1.1E-04 - - - 1.1E-04 - - 1.1E-04 1.1E-04 1.1E-04 1.1E-04

- HB HB HB HB HB HB HB HB HB HB HB HB HB HB

- 3.9 - - 4.1 - - - - - - - - - -

- 3.9 - - 4.1 - - - - - - - - - -

- 0.002 - - 0.003 - - - - - - - - - -

- 0.007 - - 0.008 - - - - - - - - - -

- 1E+12 1E+12 1E+12 1E+12 - - 2E+00 2E+03 - - 1E+12 1E+12 1E+12 1E+12

- 1E+16 1E+16 1E+16 1E+16 - - 2E+02 5E+05 - - 1E+16 1E+16 1E+16 1E+16

- 32 - - 25 - - - - - - 30 36 36 -

- 19 - - 16 - - - - - - 18 19 19 -

- 600 - - 600 - - - - - - 600 600 600 -

Polyacetal Resin

Iupital is a copolymer-type acetal resin produced with our proprietary manufacturing process. Used in a wide range of industries, Iupital is ideal for precision machinery, automobile, OA and electronics applications.

Special features:1. Well-balanced mechanical properties and high fatigue

resistance2. Excellent anticreep properties3. Excellent low friction and anti-wear properties4. Wide range of operating temperatures5. High oil and organic chemical resistance

6. Excellent thermal stability in molding

Grade


Physical properties


Water absorption - 23degC, 60%RH %



ISO 1133

-g/10min

cm3/10min

Temperature degC

Load kg

Moulding shrinkage (3mmt) -

MD%

TD


Tensile modulus

ISO527-1 , 527-2

-

MPaYield stress

Yield strain%


Stress at break MPa

Strain at break %


Flexural modulus

Charpy impact strengthISO

179-1, 179-2

23 degC kJ/m2

Charpy notched impact strength

23 degC kJ/m2

Thermal properties



ISO 75-1 , 75-2

1.80MPadegC

0.45MPa


MD1/degC

TD

Flammability UL94 0.8mmt -



1MHz -


1MHz -



Electric strength IEC 60243-11mmt

MV/m3mmt

Comparative tracking index IEC 60112 - -

3029


Low friction and Wear-Resistant Impact resistance & Toughness Electric Conductive

FL2010 FL2020 FS2022 FW-21 FW-24 FU2025 FU2050 ET-25

fluororesin10%

fluororesin20%

Silicone OilContained

Oil Contained

OilContained

ImpactResistance

ImpactResistance

Low Modulus

ElectricConductive

Carbon Filled

1.46 1.51 1.41 1.41 1.41 1.35 1.29 1.41

0.19 0.18 0.22 0.22 0.22 - - 0.22

7.5 6 10 9.5 9.5 6.0 4.5 -

6.1 4.7 8.6 8.2 8.2 5.2 3.9 -

190 190 190 190 190 190 190 -

2.16 2.16 2.16 2.16 2.16 2.16 2.16 -

2.0 2.1 2.0 2.0 2.0 1.7 1.2 1.6

- - - - - - - -

2650 2400 2700 2800 2600 1600 800 2400

52 44 56 56 51 39 24 51

8.0 8.0 10.0 10.0 11.0 12 20 5.0

18 15 51 30 35 >100 >200 10

- - - - - - - -

- - - - - - - -

77 67 83 81 75 48 24 80

2400 2200 2500 2500 2400 1400 750 2400

60 50 150 100 100 NB NB 100

5.0 5.0 7.5 6.5 7.0 19 65 5.0

166 166 166 166 166 166 166 160

97 96 100 104 102 76 64 94

154 151 150 154 154 - - -

1.1E-04 - 1.1E-04 1.1E-04 1.1E-04 1.2E-04 - 1.1E-04

1.1E-04 - 1.1E-04 1.1E-04 1.1E-04 1.2E-04 - 1.1E-04

HB HB HB HB HB HB HB HB

- - - - - - - -

- - - - - - - -

- - - - - - - -

- - - - - - - -

1E+12 1E+12 1E+12 - - - - 3E-01

1E+16 1E+16 1E+16 - - - - 8E+01

25 - - - - - - -

16 - - - - - - -

600 - - - - - - -

Talc Filled Low Emission of Formaldehyde

TC3015 TC3030 F20-73R1 F20-73R2 F30-73R1 F20-55R2 FX-11R1 FX-11JR1 FU2010R2 FU2020R2

Talc15%

Talc30%

MediumViscosity

MediumViscosity

LowViscosity

WeatherResistanceImproved

Low friction and Wear-Resistant

Lubricant

Low friction and Wear-Resistant

Lubricant

ImpactResistance

ImpactResistance

1.52 1.63 1.41 1.41 1.41 1.41 1.39 1.39 1.38 1.37

0.21 0.20 0.22 0.20 0.22 - - - - -

11 9.5 9.1 - 27 - - - - 6.8

8.3 6.9 7.9 7.9 23 7.7 9.0 45 6.0 5.8

190 190 190 190 190 190 190 190 190 190

2.16 2.16 2.16 2.16 2.16 2.16 2.16 2.16 2.16 2.16

1.9 1.5 2.0 2.0 2.0 2.0 2.0 2.0 - -

- - 2.0 - - - - - - -

4900 6900 2900 2900 2900 - 2700 2700 - -

- - 65 63 64 62 55 55 51 45

- - 8.5 9.0 7.5 8.5 9.0 7.5 10 11

- - 30 30 26 30 35 26 50 65

54 62 - - - - - - - -

4.0 3.0 - - - - - - - -

103 111 91 89 91 90 82 81 70 61

4600 7000 2610 2600 2700 2700 2500 2500 2000 1700

50 30 250 - 150 - - - NB NB

4.0 4.0 7.0 7.0 6.0 6.5 7.0 5.0 9.0 12

166 166 166 166 166 166 166 166 166 166

135 144 100 100 100 100 95 95 87 82

- - 156 156 156 - 156 156 - -

7.0E-05 - 1.1E-04 1.1E-04 - - - - - -

7.0E-05 - 1.1E-04 1.1E-04 - - - - - -

HB HB HB HB HB HB HB HB HB HB

- - 3.9 3.9 - - - - - -

- - 3.9 3.9 - - - - - -

- - 0.002 0.002 - - - - - -

- - 0.007 0.007 - - - - - -

- - 1E+12 1E+12 - - - - - -

- - 1E+16 1E+16 - - - - - -

31 - 32 32 - - - - - -

- - 19 19 - - - - - -

600 - 600 600 - - - - - -

Polyacetal Resin

Grade


Physical properties


Water absorption - 23degC, 60%RH %



ISO 1133

-g/10min

cm3/10min

Temperature degC

Load kg

Moulding shrinkage (3mmt) -

MD%

TD


Tensile modulus

ISO527-1 , 527-2

-

MPaYield stress

Yield strain%


Stress at break MPa

Strain at break %


Flexural modulus

Charpy impact strengthISO

179-1, 179-2

23 degC kJ/m2

Charpy notched impact strength

23 degC kJ/m2

Thermal properties



ISO 75-1 , 75-2

1.80MPadegC

0.45MPa


MD1/degC

TD

Flammability UL94 0.8mmt -



1MHz -


1MHz -




MV/m3mmt

Comparative tracking index IEC 60112 - -

3231


Grade


Physical properties



%23degC, 60%RH23degC, Underwater



-g/10mincm3/10min

Temperature degCLoad kg

Moulding shrinkage - - %Moulding shrinkage (3.2mmt) -

MD%

TDMoulding shrinkage (1mmt) -

MD%


MD%


MD%

TD


Tensile modulus

ISO527-1

, 527-223degC

MPaYield stressYield strain

%Nominal strain at breakStress at 50% strain

MPaStress at breakStrain at break %Flexural strength

ISO 178 23degC MPaFlexural modulus


23degC kJ/m2

Charpy notched impact strength 23degC kJ/m2

Thermal properties

Melting temperature ISO 11357-3 - degCGlass transition temperature ISO 11357-2 - degCTemperature of deflection under load

ISO 75-1 , 75-2

1.80MPadegC

0.45MPaVicat softening temperature ISO 306 - degCCoefficient of Linear thermal expansion ISO 11359-2

MD1/degC

TD

Flammability UL94

- -0.75mmt -1.5mmt -2.0mmt -3.0mmt -

GWFI(Glow-wire flammability test method for materials) IEC 60695-2-12 3.0mmt -

GWIT(Glow-wire ignitability test method for materials) IEC 60695-2-13 3.0mmt -


Relative permittivity IEC 60250100Hz -1MHz -

Dissipation factor IEC 60250100Hz -1MHz -

Volume resistivity IEC 60093 - ohm-mSurface resistivity IEC 60093 - ohm


MV/m2mmt3mmt

Comparative tracking indexIEC 60112 - -UL746A - -

UL V-0 Grade UL V-1 Grade

LN23 LN30 LN40 LN60 JBS70 LN80 LN91 LV40 LV60 AV90

- - - - - - - - - -

1.10 1.10 1.10 1.10 1.10 1.10 1.10 1.10 1.09 1.08 - - - - - - - - - -- - - - - - - - - -

0.07 0.07 0.07 0.07 0.07 0.07 0.07 0.07 0.07 0.07

- - - - - - - - - -32 16 14 9.5 7.5 6.5 4.0 16 8.5 2.8

300 300 300 300 300 300 300 300 300 300 2.16 2.16 2.16 2.16 2.16 2.16 2.16 2.16 2.16 2.16

- - - - - - - - - -0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.70.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7

- - - - - - - - - -- - - - - - - - - -- - - - - - - - - -- - - - - - - - - -- - - - - - - - - -- - - - - - - - - -

- - - - 2400 2400 - - - 2600 47 55 65 73 70 79 70 60 60 70 - - - - 5.0 - - - - 5.6

25 25 25 25 20 20 55 20 25 30 - - - - - - - - - -- - - - - - - - - -- - - - - - - - - -

80 90 95 105 105 115 105 97 100 103 2400 2400 2500 2380 2400 2400 2700 2550 2650 2600

- - - - - - - - - -

11 13 12 7 26 6 7 12 12 9

- - - - - - - - - -- - - - - - - - - -

80 90 100 115 130 127 145 100 115 145 95 105 115 130 145 140 160 115 130 160 - - - - - - - - - -

5.5E-05 5.5E-05 5.5E-05 5.5E-05 5.5E-05 5.5E-05 5.5E-05 6.3E-05 6.3E-05 6.0E-055.8E-05 5.8E-05 5.8E-05 5.8E-05 5.8E-05 5.8E-05 5.8E-05 6.6E-05 6.6E-05 6.3E-05

- - - - - - - - - -- V-0 V-0 V-0 V-0 V-0 V-0 V-1 V-1 V-1

V-0 - - - - - - - - -- - - - 5VA - - - - -- 5VA 5VA 5VA - - - - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - - -- - - - - - - - - -- - - - - - - - - -- - - - - - - - - -

3E+14 3E+14 3E+14 3E+14 3E+14 3E+14 3E+14 3E+14 3E+14 3E+142E+15 2E+15 2E+15 2E+15 2E+15 2E+15 2E+15 2E+15 2E+15 2E+15

- - - - - - - - - -- - - - - - - - - -- - - - - - - - - -- - - - 250< - - - - -- - - - - - - - - -

IPT:120minat 2.0kV

UL HB Grade Filler Reinforced Fiber Reinforced V-0 Fiber Reinforced V-1

AH40 AH60 AH70 AH80 AH91 TX403 TX903B TH620 GN10 GN20 GN30 GV10 GV20 GV30

- - - - - LowWarpage

AnticreepHigh　impact

LowWarpage

GF10%

GF20%

GF30%

GF10%

GF20%

GF30%

1.06 1.06 1.07 1.07 1.07 1.09 1.09 1.20 1.17 1.24 1.33 1.15 1.22 1.31 - - - - - - - - - - - - - -- - - - - - - - - - - - - -

0.07 0.07 0.07 0.07 0.07 0.06 0.06 0.06 0.06 0.06 0.06 0.06 0.06 0.06

- - - - - - - - - - - - - -13 8.1 5.9 4.0 3.0 16 2.5 12.0 7.0 5.0 2.9 5.5 3.6 3.0 300 300 300 300 300 280 300 300 300 300 300 300 300 300 2.16 2.16 2.16 2.16 2.16 5 2.16 2.16 2.16 2.16 2.16 2.16 2.16 2.16

- - - - - - - - - - - - - -0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 - 0.3 - 0.4 0.2 - 0.4 0.1 - 0.3 0.1 - 0.2 0.2 - 0.4 0.1 - 0.3 0.1 - 0.20.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 0.5 - 0.7 - 0.3 - 0.4 0.3 - 0.5 0.2 - 0.4 0.2 - 0.4 0.3 - 0.5 0.2 - 0.4 0.2 - 0.4

- - - - - - - - - - - - - -- - - - - - - - - - - - - -- - - - - - - - - - - - - -- - - - - - - - - - - - - -- - - - - - - - - - - - - -- - - - - - - - - - - - - -

2500 2500 2500 2600 2700 2600 2400 5200 4200 6700 9000 4200 6500 8400 40 50 58 63 70 51 60 - - - - - - -3.2 5.0 5.4 5.5 5.5 2.6 - - - - - - - -34 30 24 25 25 24 40 12 - - - - - -- - - - - - - - - - - - - -- - - - - - - 50 83 99 110 83 103 110 - - - - - - - - 2.5 2.5 1.5 2.5 2.5 1.5

76 95 102 110 118 80 90 100 140 160 180 135 161 170 2500 2500 2500 2600 2700 2500 2350 5100 4000 6200 8500 4100 6300 8300

153 119 NB 150 140 NB NB - - - - - - -

14 16 20 18 15 20 32 4 7 7 7 8 7 9

- - - - - - - - - - - - - -- - - - - - - - - - - - - -

95 115 125 135 145 95 145 115 125 130 132 130 132 135 110 130 140 150 160 100 - - 130 135 137 135 137 140

- - - - - - - - - - - - - -6.7E-05 6.6E-05 6.6E-05 6.6E-05 6.6E-05 6.0E-05 - - 4.5E-05 3.0E-05 2.5E-05 4.5E-05 3.0E-05 2.5E-057.1E-05 6.9E-05 6.9E-05 6.9E-05 6.9E-05 6.0E-05 - - 7.5E-05 6.8E-05 6.0E-05 7.5E-05 6.8E-05 6.0E-05

- - - - - - - - - - - - - -HB HB HB HB HB HB - HB V-0 V-1 V-1 V-1 V-1 V-1- - - - - - - - - V-0 V-0 - - -- - - - - - - - 5VA 5VA 5VA - - -- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - 3.4 - - 3.2 -- - - - - - - - - 3.3 - - 3.2 -- - - - - - - - - 0.0045 - - 0.0021 -- - - - - - - - - 0.0055 - - 0.0027 -

3E+14 3E+14 3E+14 3E+14 3E+14 3E+14 - - 3E+14 3E+14 3E+14 3E+14 3E+14 3E+142E+15 2E+15 2E+15 2E+15 2E+15 2E+15 - - 2E+15 2E+15 2E+15 2E+15 6E+15 6E+15

38 - 44 - - - - - - 25 - - 26 -- - - - - - - - - - - - - -

20 - >65 - - - - - - 17 - - 17 -- 275 - - - - - - 200 225 200 200 200 200 - - - - - - - - - - - - - -

Modified PPE Resin

Iupiace is a polymer alloy made by modifying PPE with high impact polystyrene (HIPS), nylon-6 or nylon-66. Iupiace provides well-balanced mechanical, electrical and thermal properties. In addition, Iupiace boasts relatively lower density than other engineering plastics. These enable Iupiace to respond to the needs of customers for compactness, superior performance and flame retardance.

Special features:1. Usability in a wide range of temperatures (-40℃ to 160℃)2. Higher rigidity, impact strength and fatigue resistance3. Excellent insulation properties, low dielectric constant

and low dielectric dissipation factor4. Excellent dimensional stability with low water absorption5. Flame retardance and excellent self-extinguishing

properties

6. Low density7. Low shrinkage rate, ensuring quality precision parts8. Good mold release, easy flow properties and a wide

range of stock temperatures

3433


Fiber Reinforced HB High Flowability High Flowability

GH10 GH20 GH30 AP4 AH8P GX1050 GX1210 AP6GM2 AP6GM4 AP4GM6

GF10%

GF20%

GF30% Unreinforced Unreinforced

ReinforcedGF+Filler

20%

ReinforcedGF+Filler

35%

ReinforcedGF+Filler

10%

ReinforcedGF+Filler

20%

ReinforcedGF+Filler

30%

1.14 1.22 1.31 1.11 1.10 1.25 1.38 1.16 1.23 1.32 - - - - - - - - - -- - - - - - - - - -

0.06 0.06 0.06 0.07 0.06 0.06 0.06 0.06 0.06 0.06

- - - - - - - - - -5.0 4.4 2.7 85 18 24 9 28 31 25 300 300 300 280 280 300 300 280 280 280 2.16 2.16 2.16 5 5 2.16 2.16 5 5 5

- - - - - - - - - -0.2 - 0.4 0.1 - 0.3 0.1 - 0.2 0.5 - 0.7 0.5 - 0.7 0.2 - 0.4 0.1 - 0.3 0.3 - 0.5 0.2 - 0.4 0.1 - 0.30.3 - 0.5 0.2 - 0.4 0.2 - 0.4 0.5 - 0.7 0.5 - 0.7 0.3 - 0.5 0.2 - 0.4 0.3 - 0.5 0.3 - 0.5 0.2 - 0.4

- - - - - - - - - -- - - - - - - - - -- - - - - - - - - -- - - - - - - - - -- - - - - - - - - -- - - - - - - - - -

4500 6600 8900 2000 2600 6100 10500 4000 5700 7800 - - - 49 56 - - - - -- - - 3.2 3.2 - - - - -- - - 45 20 - - - - -- - - - - - - - - -

75 89 103 - - 75 115 65 80 91 2.6 1.5 1.3 - - 2.7 2.0 2.9 2.7 3.1 130 154 170 82 93 122 175 116 132 145 4000 6400 8400 2000 2400 6000 10500 3800 5500 7300

- - - - - - - - - -

6 7 8 9 7 5 5 6 6 6

- - - - - - - - - -- - - - - - - - - -

130 135 137 80 85 105 115 95 115 115 135 140 142 90 95 - - - - -

- - - - - - - - - -4.5E-05 3.0E-05 2.5E-05 - 6.0E-05 3.7E-05 - 4.7E-05 3.7E-05 2.6E-057.5E-05 6.8E-05 6.0E-05 - 6.0E-05 6.8E-05 - 5.8E-05 6.8E-05 6.1E-05

- - - - - - - - - -HB HB HB - - - - - - -- - - V-0 V-0 V-1 V-1 V-1 V-1 V-1- - - - - - - - - -- - - - - 5VB 5VB - - -

- - - - - - - - - -

- - - - - - - - - -

- - - - - - - - 3.2 3.5 - - - - - - - - 3.1 3.3 - - - - - - - - 0.0057 0.0092 - - - - - - - - 0.0067 0.0077

3E+14 3E+14 3E+14 3E+14 3E+14 5E+13 - 5E+13 5E+13 2E+136E+15 6E+15 6E+15 2E+15 2E+15 1E+15 - 1E+15 1E+15 3E+15

34 32 30 - - - - - 35 34 - - - - - - - - - -

20 17 17 - - - - - 18 17 175 175 150 - - 175 - 200 200 150

- - - - - - - - - -

High Flowability Friction/Wear Resistance Improved Antivibration High dielectric Anti-static PPE/PA6 Alloy PPE/PA66 Alloy

ANP6GM4 LMX420N AHF6010B GHF3010 VSG635V HD7007 EHM1010A EHM10009905M2 EHM103R NX7000 NXG7201

8240 NX9000

ReinforcedGF+Filler

20%

ReinforcedFiller20%

UnreinforcedPTFE10%

Fiber Reinforced

PTFE10%

ReinforcedGF+Filler

35%- CB CB CB Unreinforced

dry(50%RH)

Fiber ReinforcedGF

20%dry(50%RH)

Unreinforceddry(50%RH)

1.27 1.34 1.12 1.37 1.44 1.32 1.16 1.14 1.16 1.10 1.26 1.11 - - - - - - - - - - - -- - - - - - - - - - - -

0.06 0.06 0.06 0.10 0.06 0.10 0.06 0.06 0.06 - - -

- - - - - - - - - - - -29 40 4.5 1.9 9.0 6.5 - 12.0 - 5.5 6.0 2.0

280 280 300 300 280 300 - 320 - 275 290 275 5 5 2.16 2.16 5.00 2.16 - 5 - 2.16 2.16 2.16 - - - - - - - - - - - -

0.2 - 0.4 0.2 - 0.4 0.5 - 0.7 0.1 - 0.2 0.1 - 0.3 - 0.55 - 0.75 0.70 - 0.90 0.85 - 1.05 1.2 - 1.4 0.3 - 0.5 1.1 - 1.30.3 - 0.5 0.2 - 0.4 0.5 - 0.7 0.2 - 0.4 0.2 - 0.4 - 0.55 - 0.75 0.70 - 0.90 0.85 - 1.05 1.1 - 1.3 0.4 - 0.6 1.1 - 1.3

- - - - - - - - - - - -- - - - - - - - - - - -- - - - - - - - - - - -- - - - - - - - - - - -- - - - - - - - - - - -- - - - - - - - - - - -

6100 6000 2400 9000 8600 4900 4200 2400 2600 2500 (1600) 6000 (4100) 2500 (-)- - 51 - - - - - - 65 (46) - (73) 65 (-)- - 5.0 - - - - - - 4.1 (9.9) - (5.1) 4.5 (-)- - 15 - - - - - - 20 (143) - (11) 50 (-)- - - - - - - - - - - -

94 60 - 90 74 60 64 60 62 - 97 (-) -2.7 3.0 - 1.8 1.2 2.0 2.2 9.0 8.0 - 2.2 (-) -140 105 84 140 140 95 110 102 105 102 (59) 171 (73) 100 (-)

5800 6000 2500 9000 8500 4800 3860 2500 2700 2500 (1500) 5700 (4100) 2500 (-)

- - - - - 12 20 60 40 - - -

5 2 8 6 5 - 3 - - 30 (77) 6 (9) 25 (-)

- - - - - - - - - - - -- - - - - - - - - - - -

121 105 110 130 115 125 155 159 150 - 190 -- - - - 120 - 165 - 160 180 - 188 - - - - - - - - - - - -

3.7E-05 4.0E-05 6.0E-05 2.5E-05 2.5E-05 - 5.3E-05 - - 9.0E-05 3.0E-05 7.0E-056.8E-05 5.5E-05 6.0E-05 6.0E-05 6.1E-05 - 5.5E-05 - - - - -

- - - - - - - - - - - -- - - - - - - - - - - -

V-0 V-0 HB HB V-1 - - - - - - -- - - - - - - - - - - -- - - - - - - - - - - -

- - - - - - - - - - - -

- - - - - - - - - - - -

3.2 - - - - - - - - - - -3.1 - - - - 8.0 - - - - - -

0.0057 - - - - - - - - - - -0.0067 - - - - 0.0060 - - - - - -5E+13 3E+14 3E+14 2E+14 4E+13 - - - - - - -1E+15 2E+15 6E+15 2E+15 8E+14 - 6E+05 5E+03 2E+03 - - -

35 - - - - - - - - - - -- - - - - - - - - - - -

18 - - - - - - - - - - -200 - - - - - - - - - - -

- - - - - - - - - - - -

Modified PPE Resin

Grade


Physical properties



%23degC, 60%RH23degC, Underwater



-g/10mincm3/10min



MD%


MD%


MD%


MD%

TD


Tensile modulus

ISO527-1

, 527-223degC




ISO 178 23degC MPaFlexural modulus


23degC kJ/m2

Charpy notched impact strength 23degC kJ/m2

Thermal properties


ISO 75-1 , 75-2

1.80MPadegC


MD1/degC

TD

Flammability UL94

- -0.75mmt -1.5mmt -2.0mmt -3.0mmt -








MV/m2mmt3mmt


3635


Grade


Physical properties


Water absorption -23degC,50%RH

%23degC,60%RH23degC,Underwater



-g/10mincm3/10min



MD%


MD%


MD%


MD%

TD


Tensile modulus

ISO527-1 , 527-2

23 degC




ISO 178 23 degC MPaFlexural modulusCharpy impact strength ISO

179-1, 179-2

23 degC kJ/m2


Thermal properties


ISO 75-1 , 75-2

1.80MPadegC


MD1/degC

TD

Flammability UL94

- -0.75mmt -1.5mmt -2.0mmt -3.0mmt -







Electric strength IEC 60243 11mmt

MV/m 2mmt3mmt


PPE/PA6 Alloy Filler Reinforced PPE/PA6 PPE/PA66 Alloy PPE/PP Alloy

BX505 BX528A-3 BX503A-1 BX504D C61HL C82HL PX603Y

Standardsdry(50%RH)

High Rigiditydry(50%RH)

High RigidityFiller

dry(50%RH)

High RigidityFiller

dry(50%RH)dry(50%RH)

HighFlowability

dry(50%RH)

HighFlowability

1.09 1.15 1.19 1.22 1.10 1.13 0.98 - - - - - - -- - - - - - -- - - - - - -

- - - - - - -14 15 40 21 31 100 55 280 280 280 280 280 280 280

5 5 5 5 5 5 5 - - - - - - -

1.2 - 1.4 1.2 - 1.4 1.0 - 1.2 0.7 - 0.9 1.1 - 1.3 1.1 - 1.3 1.0 - 1.21.1 - 1.3 1.0 - 1.2 0.9 - 1.1 0.6 - 0.8 1.1 - 1.3 1.1 - 1.3 1.1 - 1.3

- - - - - - -- - - - - - -- - - - - - -- - - - - - -- - - - - - -- - - - - - -

2200 (1200) 2500 (1400) 3100 (1700) 4200 (2200) 2500 (1600) 2600 (1500) 1900 54 (38) 62 (37) 65 (46) - (42) 66 (51) 60 (45) 42

4.2 (18.8) 5.0 (14.9) 4.5 (9.0) - (8.4) 5.3 (11.4) 4.8 (19.2) -41 (115) 57 (140) 29 (60) - (74) 42 (73) 47 (88) -

- - - - - - -- - - 62 (-) - - -- - - 6.1 (-) - - -

80 (47) 91 (60) 100 (68) 100 (57) 90 (71) 90 (60) 59 2000 (1200) 2300 (1400) 2900 (1800) 3650 (2100) 2300 (1700) 2400 (1500) 1900

- - - - NB (NB) NB (NB) NB

22 (88) 26 (66) 9 (14) 6 (12) 20 (45) 20 (62) 5

- - - - - - -- - - - - - -- - - - - - -

150 170 175 175 175 165 120 - - - - - - -

9.0E-05 9.0E-05 - - 9.0E-05 - -- - - - - - -- - - - - - -- - - - - - -- - - - - - -- - - - - - -- - - - - - -

- - - - - - -

- - - - - - -

- - - - 3.3 3.4 -- - - - 3.2 3.2 -- - - - 0.0040 0.0050 -- - - - 0.0094 0.0121 -- - - - 1E+14 2E+13 -- - - - 5E+14 7E+14 -- - - - 30 33 -- - - - - - -- - - - 17 18 -- - - - - - -- - - - - - -

Lemalloy is a polymer alloy made by modifying PPE with high-impact polystyrene (HIPS), polyamide-6, or polyamide-66. Lemalloy provides well-balanced mechanical, electrical, and thermal properties. In addition, Lemalloy boasts the lowest specific gravity among engineering plastics. Equipped with the above features, Lemalloy meets market requirements for compactness, high performance, and flame retardance.

Special features:1. Stable rigidity, impact strength and fatigue resistance

through a wide range of temperatures2. Excellent insulation properties, low dielectric constant

and low dielectric dissipation factor3. Excellent dimensional stability with low water absorption4. Excellent heat stability5. Flame retardant, and excellent self-extinguishing

properties

6. Low specific gravity7. Excellent moldability and low shrinkage rate for quality

precision parts8. Excellent processability; good mold release, easy flow

properties and a wide range of stock temperatures

Modified PPE Resin

3837