Hand Lay-up of Woven Mat or Chopped Strand Mat in Open Mold
Post on 14-Mar-2022
1 Views
Preview:
Transcript
1
Fabrication Processes for Polymer Matrix Composites
*Programmable Powdered Preform Process (P4)
****Thermoplastic Molding
****Resin Infusion (RI)
**Automated Fiber Placement (AFP)
*Reinforced Reaction Injection Molding (RRIM)
****Liquid Composite Molding (LCM)
**Pultrusion
*Filament Winding
****Compression Molding
**Autoclave
*
**
Open moldHand Lay-upSpray-up
HybridWovenChoppedContinuousProcess
Type of fiber Reinforcement
Hand Lay-up of Woven Mat or Chopped Strand Mat in Open Mold
For development work, prototypes, large components, small quantities
Resin
MatGel Coat
Wax coating on mold ( or mold release)
Mold
Roller
2
Chopper-Spray Gun
Prepreg tape - fibers pre-impregnated with matrix resin and partially cured in tape form
3
Hot-Melt Prepegging Process
Courtesy of SACMA
Autoclave Molding ( Thermosetting Polymers)
4
Autoclave-Style Press Cure
Filament Winding
5
Natural Gas Vehicle (NGV) Composite Fuel Tank
• Filament wound composite wrap• Operating pressure 3,000 psi
Source: Brunswick Composites
6
Courtesy of McClean Anderson, Inc.
Courtesy of McClean Anderson Inc.
7
Roll wrapping of composite tubes
From A. L. Browne and N. L Johnson, Proc. ASCAnnual Technical Conference, Philadelphia, PA, 2005
SMC Machine
From Reinhart, et al., 1987
8
Compression Molding with Matched Metal Dies
For production of large quantities
Heated Die
Prepreg Tape or Sheet Molding
Compound (SMC)
Molding with SMC• 3-5 day maturation period to reach desired
molding viscosity• Limited shelf life-about two weeks• Charged placed in steel mold• Mold heated to • Mold closed under 800-1200 psi pressure• Cure time 30-150 seconds• Mold opened and part ejected• Part placed on cooling rack
F°−° 325250
9
Compression Molding
Heated Die
Premix or Bulk Molding
Compound (BMC)
Pultrusion Process
• Thermoset matrix resin (e.g., polyester, vinyl ester, etc.)
• continuous fibers coated by pulling through premixed thermoset resin bath
• resin-coated emerges from other end of die• limitation: part geometry cannot change
along length (e.g., I-beams, channel sections, etc.)
10
Pultrusion Process
Resin Bath
Heated Die
Fiber rovingPuller
Pultruded fiberglass composite structural elements.(Courtesy of Strongwell Corporation)
11
Large (3 m x 3 m) interlocked composite grid structure fabricated from pultruded carbon/epoxy ribs and rib caps (Tsai, 2001)
Pultrusion Process
• Automotive Applications– Drive shafts (General Motors)– Fuel tank stiffeners (Chrysler)– Side panels for buses (Greyhound)– Bumper beams (Chrysler - discontinued)– Leaf springs (Ford, General Motors -
discontinued)
Source: D.J. Evans, “Pultruded Products: An Automotive History”, Proc. 6th Annual ASM/ESD Advanced Composites Conference, Detroit, Michigan, Oct. 8-11, 1990, PP. 327-331.
12
Thermoplastic stamping (Thermoplastic Molding)
• Thermoplastic resin matrix (e.g., polypropylene, nylon, PPS, PEEK)
• Fiber reinforced thermoplastic blank is heated in an infrared oven
• After heating to above the melting point, blank is quickly placed in matched metal die
• Die closed and part formed under high pressure (1,500-3,000 psi)
• Typical cycle times 30-90 seconds, depending upon part thickness
• High forming pressures limit use of foam cores due to crushing
Conveyor Belt Mold
Press
Infrared Oven
Blank
Thermoplastic stamping (Thermoplastic Molding)
13
Thermoplastic Stamping
Heated blank loaded into mold
Mold closing, compressing material to
fill cavity
Co-mingled fiber/thermoplastic matrix yarn
Thermoplastic fibers which form matrix after melting
Reinforcing fibers
14
Thermoplastically stamped E-glass/polypropylene Twintex® composite
isogrid panel and steel mold
Manufacturing of Specimens
• Laboratory sized composite isogrid and orthogrid panels (305 mm x 264 mm) made from co-mingled E-glass/polypropylene (Twintex® by Vetrotex)
• Used a grooved mold thermoplastic stamping process (Goldsworthy and Hiel, 1999)
• Co-mingled unidirectional roving used for ribs• Co-mingled woven fabric used for skins
15
Reinforced Reaction Injection Molding (RRIM)
Constituents:• Chopped glass fibers• Thermosetting resin, typically polyurethane• Fillers, internal mold release agents, etc.
Reinforced Reaction Injection Molding
Resin +
Fibers
Hardener
Mix Head
Heated Mold
16
Molding Process:
• Two liquid reactant streams, one containing chopped fibers, are mixed by impingement under pressure in a mixing head just before injection into a closed mold where polymerization occurs (e.g., polyisocyanate and polyol, the precursors for polyurethane)
• Low viscosity liquids, so pressure in mold is low, typically 50 psi
• Cycle time typically no more than several minutes• After demolding, polyurethane typically post
cured for 1 hr. @
≈
°120
Resin Transfer Molding
Mold
Dry Fiber Mat
(preform)
17
Resin Transfer Molding
Resin
Injection of resin into fiber mat in mold
under pressure
Courtesy of Ford Motor Company, Research Staff
18
Examples of Automotive RTM Application
Experimental Ford Ranger two Piece RTM Truck Cab
Experimental Ford Ranger Two Piece RTM Truck Cab
• RTM continuous random strand mat glass fibers/vinyl ester resin matrix over urethane rigid foam core
• RTM cab has 2 pieces compared with 100 piece steel cab
• Beam structure integral with body skin panels (semi-monocoque)
• Weight 157lb compared with 189lb for steel cab
• Passed 35 mph front barrier crash test
19
Experimental Ford Ranger Two Piece RTM Truck Cab
• Bending and torsional stiffness 1.75 to 2.5 times greater than those of steel cab
• Passed 16,000 mi rough road durability test• NVH characteristic as good or better than
steel cab• Passed roof crush resistance and seat belt
anchorage tests
Source: R.E.Bonnett, R.A.Carpenter and S.W.Gallagher, SAE Paper No. 900306, 1990.
Seeman Composites Resin Infusion Molding Process (SCRIMP)(Source: TPI Composites Inc.)
20
• References on Fabrication of Composites:
– Composite Materials Handbook, Schwartz
– Handbook of Composites, Lubin– Composites Engineering Handbook,
Mallick
Critical Issues in Design, Manufacturing and Performance – Current ACC
Technology Programs
• Material Test Standards– Development and publication of “Test
Procedures for Automotive Structural Composite Materials” to provide reliable design data
– Development of durability test methods (fatigue, bolt load retention, impact damage tolerance, environment effects)
21
Critical Issues in Design, Manufacturing and Performance – Current ACC
Technology Programs• Joining Technology
– Development and verification of a general methodology to optimize performance, reliability and durability of adhesively bonded joints in composite structure
• Crash Energy Management– Development and demonstration of technology
required to apply production feasible structural composites in crash energy management applications
Critical Issues in Design, Manufacturing and Performance – Current ACC
Technology Programs
• Composite Processing– Development and demonstration of cost-
effective, high-volume manufacturing technology to produce reliable structural composite parts (focus on Liquid Composite Molding)
22
ACC Focal Project – Automobile front end structure
• RTM braided/continuous strand mat/chopped fibers/vinyl ester resin with polyurethane foam cores
• Shock tower durability tests showed performance superior to steel
ACC Focal Project
23
ACC Focal Project
Future Opportunities in Automotive Composites
• New and improved methods for high speed, low cost processing needed to compete with steel
• Design for assembly and disassembly: part integration, reduction of part count, reduction of number of joints and fasteners
24
Future Opportunities in Automotive Composites
• Composite automotive primary structures not widely used yet, but have great potential if issues such as high speed, low cost manufacturing, crash energy management and damage tolerance are resolved
Future Opportunities in Automotive Composites
• Advanced thermoplastic matrix materials (e.g., PEEK, PPS, PEI, PS) offer many advantages such as fast cycle times, excellent temperature and moisture resistance, recyclability, unlimited shelf life, and excellent toughness, but they are relatively new and expensive, and more research is needed.
25
Future Opportunities in Automotive Composites
• Under-the-hood applications: great potential for not only polymer matrix composites, but metal matrix and ceramic matrix composites as well
• Design for NVH with composites: damping designed in, not added as an afterthought
MicromechanicsMacromechanics
FibersLamina
Matrix
Laminate
Structure
26
Randomly Oriented Short Fiber Reinforcement
FibersMaterial is Isotropic like steel or aluminum
Strength:= Yield Strength = Ultimate Strength
YσUσProperties are independent of orientation.
Elastic Properties:E = Young’s Modulus G = Shear Modulus v = Poisson’s Ratio
Randomly Oriented Short Fiber Reinforcement
∴
27
Unidirectional Continuous Fiber Reinforcement
1
2
Fibers
Material is Orthotropic, not Isotropic
Strength:SL = Longitudinal Strength ST = Transverse Strength SLT = Shear Strength
Properties depend on orientation.
Elastic Properties:E1 = Longitudinal Young’s Modulus E2 = Transverse Young’s Modulus G12 = In-plane shear Modulus v12 = Major Poisson’s Ratio
∴
Unidirectional Continuous Fiber Reinforcement
28
Micromechanics of Composites
• Prediction of composite properties based on corresponding properties of constituent materials
• Example: prediction of the longitudinal young’s modulus of a unidirectional continuous fiber composite by “Rule of mixtures”
mmff VEVEE +=1
Where, Ef = Young’s modulus of fiber Em = Young’s modulus of matrix Vf = Fiber volume fraction Vm = Matrix volume fraction
Rule of Mixtures
29
Laminate Analysis:
Plies or laminae
Analysis of composite structures such as laminates using effective properties, but not concerned with constituents like fiber and matrix.
Macromechanics of Composites
Review of basic Mechanics of Material Equations
• Equations of static equilibrium based on Newton’s Second Law
• Force-deformation, or stress-strain relationships for the materials
• Geometric compatibility equations or assumed relationships regarding the geometry of deformation
30
Composite bar system – series arrangement
For static equilibrium of Bar A which has internal force PA,
Similarly, for Bar B which has internal force PB,
so that
∑ =−= 0Bx PPF
∑ =−= 0PAPxF
PBPAP ==
31
The axial elongations of the bars are given by the force-deformation equations
The total axial elongation is
Note: system is statically determinate
AEAAALAP
A=δBEBABLBP
B=δ
BAtotal δδδ +=
Composite bar system – parallel arrangement
32
Static equilibrium equation
The axial elongations of the bars are given by the force-deformation equations
But the geometric compatibility equation is now
Note: system is now statically indeterminate
BPAPPorPBPAPxF +=∑ =−+= 0
AEAAALAP
A=δBEBABLBP
B=δ
BA δδ =
Statically indeterminate composite system
33
Static equilibrium equation
Geometric compatibility equation
Force-deformation equations
Note: system is statically indeterminate
∑ =+−= 0asFbwFPcoM
asbw δδ =
wEwAwLwP
w=δsEsAsLsP
s=δ
34
Composite ring assembly subjected to temperature drop TΔ
Coefficients of thermal expansion
From thin-wall pressure vessel theory
From mechanics of materials, the radial displacements of the rings, and , are related to the corresponding tangential strains, and by
sa αα >
atapr
a=σstspr
s −=σ
arara
Δ=εsrsrs
Δ=ε
arΔ srΔaε sε
Since the rings are bonded together, the radial displacementsmust be equal, so that
srar Δ=Δ
35
Tangential stress-strain relationships
Combining the above equations, the problem is reduced to one equation in one unknown, the interface pressure p
After solving for p, the stresses and strains in the rings can be found
TaaEaa Δ+= ασε TssE
ss Δ+= ασε
⎟⎟⎟⎟
⎠
⎞
⎜⎜⎜⎜
⎝
⎛
Δ+−=Δ+ TssEstspr
arsrTaaEat
apr αα