RepRint of papeR published in inteRnational Cement Review septembeR 2007
Cement additivesCReative gRinding solutions
In the mid-1930s, cement plants started to use cement additives to increase the production volume of cement. It
became evident, that the use of cement additives enabled producers to achieve cement fineness and qualities which would hardly be possible without them.
The basic raw materials used then were amines, amino-acetates, glycols and gluconates. In the last decades, the main focus was to find new and more efficient amines concerning grindability and hydration-enhancement.
New technologySika has now developed a new raw material with excellent properties in terms of improved grindability. The
latest generation of SikaGrind® cement additives is based on polycarboxylate (PCE) polymers. These products allow for a consistent production at the highest production rates. The special ViscoCrete polymers have been developed in Sika’s central R&D laboratory in Zürich,
Switzerland and are produced worldwide by all Sika’s polymer-production plants.
The PCE polymers, which look similar at the molecular level to amines and glycols, and contain similar ionic groups are quickly distributed to their field of action due to the excellent mixing behaviour of the mill.
ICreative grinding solutions
ADDITIVES/IMPROVERS
by Philippe Jost and Jorg M Schrabback, Sika Services AG, Switzerland/Germany
The use of chemical processing agents in the manufacture of cement is well known and state-of-the-art today. The latest developments in the chemical industry have opened new possibilities to further improve the cost structure. Sika has introduced a new approach to the grinding aid business. The brand SikaGrind stands for new creative solutions for grinding aids and performance enhancers.
Figure 1: total feed of cement mill consisting of fresh material, the return from the separator and SikaGrind
80
85
90
50.2
47.3
44.7
45
50
55
60
65
70
75
80
85
90
95
Blank 0.018% SikaGrind 0.035% SikaGrind35
40
45
50
55
60
Production [tph] Energy [kWh/t
Figure 2: adjustable mill output related to the dosage of SikaGrind®-800
The brand SikaGrind® stands for cement grinding aids which are developed to improve the production rates of ball mills and increase the separator efficiency.
As a joint effect, the grinding installation produces more tonnes per hour and leads to cost savings due to a lower relative power consumption per ton of cement. Sika offers various types of products, from basic grinding aids which achieve a constant production on higher output-level to special grinding aids with additional quality enhancing properties like impoved strength, accurate air entrainment and adjustment of cement powder flowability.
SikaGrind® Technology
ICR SEPTEMBER 2007
The easy dispersable PCE polymers support cracking behaviour of the cement particles by direct contact of the millions of smallest molecules which can be found in each drop of SikaGrind. This critical property of grinding aids is achieved in the case of these new polymers mainly through two mechanisms: (1) they avoid re-agglomeration of particles, and (2) they improve the performance of the separator significantly, decreasing the return feed, allowing for an increase of the fresh feed and thereby increasing the overall production rate.
SynergiesDuring the laboratory grinding trials in Sika’s research and development centre for cement additives in Leimen, Germany, it became evident, that the best grinding behaviour could be achieved with products based on formulations of special PCE polymers and existing, proven raw materials. This synergy effect was confirmed in multiple international plant trials with different cement types and
grinding conditions (see Figure 1).
Production increase Products developed out of these new PCE polymers include the new SikaGrind®-800 Series. These new products respond very well to ball mill systems. Cement output could be easily increased. The
higher the dosage, the more production gain could be achieved (Figure 2). This makes it possible to quickly find an economical solution for each individual situation and react flexible on the demand for cement volume in the market. Process optimisationFigures 4 and 5 show the results of one of the many executed plant trials, in this case a CEM II/B-S 32.5 R (Blaine 4100cm²/g). Sika’s new grinding aid technology achieved at a significant lower dosage an additional six per cent production throughput compared to a traditional Glycol based product while maintaining the performance of the finished cement.
Since the usually achieved final strengths for this particular cement where always at the upper limit according to EN 197-1, an additional test series was performed targeting a 200cm²/g lower Blaine value of the finished cement, which ultimately resulted in another production increase. In total, product performance of these new PCE polymer based products allowed for a production increase of 18 per cent.
Strength increaseAnother of the plant trials was set the target to increase the slag content at a constant production rate, in this case of a CEM II/B-S 32.5 R (Blaine 3100cm²/g). Sika’s new grinding aid technology allowed for the production of a cement with finer granulometry, all at the same low dosage rate of the grinding aid and the same production parameters,
compared to the amine based product currently in use.
This lead to an increased early strength as well as an increased final strength (see Table 1) which then can be used to reduce the clinker content and hence reduce the CO2 emissions of this cement plant. Powder flowabilityIn addition to the standard grinding and performance enhancing properties, SikaGrind®-800 series offers also the possibility to adjust the cement powder flowability to the desired performance: flowable enough to ensure a quick loading and unloading of silos and transportation vessels and resistant enough to stay on conveyor belts at critical slopes. This effect can be measured for example with the test method according to Imse or indirectly with the bulk density of the cement powder.
3436
40
3840
40774117
10
15
20
25
30
35
40
0.05% Glycol 0.03% SikaGrind 0.03% SikaGrindoptimised
3200
3600
4000
4400Production (tons/h)Blaine (cm²/g)
Production+ 18%target Blaine
4000 +/- 100cm²/g
Production+ 6%
Production Blaine
ADDITIVES/IMPROVERS
Figure 3: increased mill efficiency with SikaGrind®-800 technology
0
10
20
30
40
50
60
24h 9.1 7.6 7.82d 22.2 21 207d 37.3 35.7 34.628d 54.8 54.7 52.3
0.05% Glycol 0.03% SikaGrind 0,03% SikaGrindoptimized
Compressive strength in N/mm²
Max. 28d strength -1
min. 2d strength CEM 32.5 R acc. EN 197-1
CEM 32.5 R acc. EN 197
Figure 4: optimised strength results with SikaGrind®-800 technology
05
101520
2530
3540
1 10 100
amine based grinding aid
SikaGrind®-800 Technology
Particle diameter in µm
Density q3lg in 1/mm
Mill temp.: about 100 °CSympatec Helos dry dispersion
Figure 5: finer granulometry with SikaGrind®-800 technology
SEPTEMBER 2007 ICR
Tailor made solutions and on-site supportSince every type of cement has its own characteristic and the challenges of cement manufacturing vary according to the local conditions, every single cement plant needs to be handled individually.
Therefore, Sika offers different basic technologies and tailor made solutions, always with the target to assist producers in creating new markets and improve their profitability.
In one of the applications, the target set by the cement manufacturer was to supply a special amine free grinding aid, which would at least meet the same productivity and achieve the same cement performance as the up to this date used amine based grinding aid. Grinding trials as well as all standard cement powder and mortar analyses in Sika’s central cement laboratory (Figure 6) demonstrated the capablity of SikaGrind and enabled Sika’s team to prove the company’s quality in plant trials. Finally, the production rates with this tailor made product could additionally be increased by five per cent compared to the conventional grinding aid.
In addition to these new generation of grinding aids and existing technologies for cement additives, Sika offers also the necessary support in the preparation, execution and analysis of the plant trials (see Figure 7). Usually, during a first screening plant production, different types and dosages of SikaGrind are tested to see the reaction of the mill on this new technology.
The positive performance of the ball mill in combination with Sika’s product at the chosen dosage is then analysed in a longer
plant trial with constant production conditions.
Figure 8 displays the fresh feed and the return from the separator from a CEM I
52.5R production (Blaine 5000cm²/g) after the balanced system had been reached and before next variations where tested.
It demonstrated how Sika’s products lead to very constant production parameters at an increased level compared to the traditional and commonly used grinding aid (amine based). SummaryBesides offering a range of traditional cement additives, Sika has developed and introduced a new generation of
grinding aids based on polycarboxylate polymer technology.
These new products offer all the positive effects, why grinding aids have been used over the last decades, mainly which improve the production rates of ball mills and increase the separator efficiency, resulting in improved through-put over existing products.
The increased productivity of this new grinding aid technology enables producers to react flexible to the demands for cement volume in the market.
In addition, these products improve the granulometry as well as powder flowability of the finished cement.
These advantages can be used to obtain cost savings due to lower relative power consumption per tonne of cement or to gain quality enhancement. As a joint effect of the multiple reduction of CO2 emission, from energy saving and clinker replacement, costs are saved and the environment is better protected. _______I
ADDITIVES/IMPROVERS
ICR SEPTEMBER 2007
Figure 7: Sika supports plant trials with a consulting service and active participation, like the taking of samples
Figure 6: in addition to the ball mill, Sika’s central cement laboratory is equipped with all the necessary tools to provide support
Table 1: optimised fineness and strength results with SikaGrind®-800 series
Product amine based SikaGrind®-800 competitor technologyDosage ml/min 220 220Product (tph) 70 71Dosage % 0.20 0.20Blain cm2/g 3090 3125Sieve residue 32mm in % 31.5 24.9Inclination ‘n’ in RRSB net 0.80 0.83‘x’ in RRSB net 21.5 19.8Compressive strength N/mm2 – –
1 day 7.2 9.12 days 17.6 19.47 days 32.9 36.228 days 50.9 54.9
0102030405060708090
0:00 1:00 2:00 2:59 3:59 4:59 5:59
with amine based grinding aidwith SikaGrind
Material flow in tph
Fresh feed of mill 39
81
45
75Production
+ 15%
Time in hours:minutes
Return to mill
Figure 8: constant and increased cement productionwith SikaGrind technology