Aluminium EN AW 6082Alloy  6082  is  a  heat  treatable  medium­high­strength  construction  alloy  with  medium­high  fatigue  strength.  It  offers  acombination of very good corrosion resistance and very good weldability due to its lowered strength values in the weldingzone. Good machinability and good cold formability after stabilising heat  treatment are  important benefits. This product  isnot suitable for complex sections.

Applications:• rail coaches, truck frames, ship building, bridges, military bridges, bicycles and boilers

• platforms, flanges, hydraulic systems, mining equipment, motor boats, pylons and towers

• Heavy duty structures:

• Machinery applications:

The information on our web site is accurate to the best of our knowledge and understanding. Although every effort has been made to ensureaccuracy, the company cannot accept any responsibility for any direct or indirect damages resulting from possible errors or incorrect

application of the information of this publication. We reserve the right to make changes.

Copyright © 2014 Rautaruukki Corporation. All rights reserved.

Document printed on 10.04.2014 www.ruukki.com

Dimensions

• EN AW 6082 T6 (AlSi1MgMn)

• From our Norway stock

• Material according to EN 573­3

• Tolerances according to EN 485­3, 485­4

• Temper T6

• Packing: sheets á 500 kg/bundle and 1000 kg/bundle

• Material certificate EN 10204 / 3.1

Dimensions mm     Theor. weightThickness Width Length kg/unit

8 1270 2520 71.69

10 1270 2520 89.61

12 1270 2520 107.53

15 1270 2520 134.42

20 1270 2520 179.22

25 1270 2520 224.03

30 1270 2520 268.83

40 1270 2520 358.44

Properties

Chemical Properties

  Element Si Fe Cu Mn Mg Cr Ni Zn Ti Ga V Remarks Others/E

Others/T

Al

EN573­3

Weight%

0.7­1.3 0.50 0.10 0.40­1.0 0.6­1.2 0.25 ­ 0.20 0.10 ­ ­ ­ 0.05 0.15 Remainder

Mechanical properties

  Property/Temper O T4 T42 T6 T61

EN 485­2 Rp0.2 max 85 110 95 260 205

t=2mm Rm max 150 205 205 310 280

  A50 mm 16 14 14 7 11

  HBW 40 58 57 94 82

  Bending R 180° 1.0 t 3.0 t ­ ­ ­

  Bending R 90°  1.0 t 2.0 t 2.0 t 3.5 t 2.5 t

Physical properties

Density: 2.71 g/cm3 Thermal Expansion: 23.1 µm/(mK)

Melting Point: 650°C Resistivity: 39 nΩm

Modulus of Elasticity: 70000 MPA Thermal Conductivity: 172 W/(mK)

Modulus of Rigidity: 26400 MPA Electrical Conductivity: 44 %IACS

Aluminium EN AW 6082

2

Poisson's ratio: 0.33    

Specific heat capacity: 894 J/(kgK)    