Top Banner
Pipe Reinforcement & Composite Repair for External Corrosion From +50°C (+122°F) to +110°C (+230°F) 3X ENGINEERING, 9 avenue Albert II Tel: +377.92.05.79.81 Fax: +377.92.05.72.71 98 000 MONACO www.3xengineering.com ref: RD4ECHT TDS – 11/2014 – EN CHECK OUT THE LATEST REVISON ON http://files.3xeng.com REINFORCEKiT4D DESCRIPTION REINFORCEKiT 4D is an advanced permanent composite repair system for pipelines and piping suffering from corrosion defects and mechanical damage. Reinforcekit 4D is engineered to restore pipe original integrity without shutdown. It is a non-metallic technical alternative to metal clamps, welded sleeves and pipe replacement. Thoroughly tested by third-party laboratories REINFORCEKiT is a 3X Engineering patented concept which provides the required strength according to ASME B31G, ISO 24817 and ASME PCC-2 codes and standards. The original 3X concept is a combination of Kevlar® tape and specific epoxy resin. The bi-directional woven high-strength aramid-fiber material provides reinforcement in the hoop and axial directions. The epoxy resin allows binding and transferring loading through the whole composite system. REINFORCEKiT 4D is a wet lay-up system. It is wrapped helicoidally around the pipe in order to bring the mechanical resistance to the damaged pipe section. The number of layers, determined by calculation, is linked not only to the pipe pressure, temperature, diameter and thickness but also to the pit depth and length, the steel grade and the pipe location. The repair design and material requirements is provided by 3X software REA after information compilation according to ASME B31G, ISO 24817 and ASME PCC-2 codes and standards. REINFORCEKiT4D-ECHT FEATURES REINFORCEKiT 4D-ECHT is recommended to repair and reinforce pipe operating at temperature between +50°C (+122°F) to +110°C (+230°F) subject to external corrosion, dents or mechanical damages. The system restores the pipe integrity and prevents from further deterioration. This composite sleeve is made of 400 g/m² Kevlar® tape and ceramic reinforced epoxy resin. This specific resin composition provides good anti- abrasion and chemical features. USES External corrosion Pitting Dents Weld defects Mechanical damages Suitable for +50°C (+122°F) to +110°C (+230°F) BENEFITS No heating or post-curing required Online repair (no shutdown) Conform to any shape including welds, elbows and tees In accordance with standards No overload on corroded pipelines Not hazardous for users RESIN SPECIFICATION Chemical Name R3X1080 Chemical Family Epoxy (bi-components) Color Black Mixing ratio by weight (Part A : Part B) = 4.66 : 1 Pack size 1.7 kg/set Solids 100% VOCs none Storage Between +10°C (+50°F) and +32°C (+90°F) if long term storage Shelf life 2 years in unopened containers FIBER SPECIFICATION Fiber nature Aramid Kevlar® 49 Fiber directions towards pipe axis Hoop/axial (0 / 90°) Fiber type Woven type Tensile strength 2 900 MPa (420.5 Kpsi) Tensile Modulus 110 GPa (15 950 Kpsi) Density 1 450 Kg/m3 (90.6 Ib/cu.ft.)
2
Welcome message from author
This document is posted to help you gain knowledge. Please leave a comment to let me know what you think about it! Share it to your friends and learn new things together.
Transcript
Page 1: Tds r4d Echt

Pipe Reinforcement & Composite Repair for External Corrosion From +50°C (+122°F) to +110°C (+230°F)

3X  ENGINEERING,  9  avenue  Albert  II  -­‐  Tel:  +377.92.05.79.81  -­‐  Fax:  +377.92.05.72.71  -­‐      98  000  MONACO      www.3xengineering.com  ref:  RD4-­‐ECHT  TDS  –  11/2014  –  EN      

CHECK  OUT  THE  LATEST  REVISON  ON  http://files.3xeng.com  

REINFORCEKiT4D DESCRIPTION

REINFORCEKiT 4D is an advanced permanent composite repair system for pipelines and piping suffering from corrosion defects and mechanical damage. Reinforcekit 4D is engineered to restore pipe original integrity without shutdown. It is a non-metallic technical alternative to metal clamps, welded sleeves and pipe replacement. Thoroughly tested by third-party laboratories REINFORCEKiT is a 3X Engineering patented concept which provides the required strength according to ASME B31G, ISO 24817 and ASME PCC-2 codes and standards.

The original 3X concept is a combination of Kevlar® tape and specific epoxy resin. The bi-directional woven high-strength aramid-fiber material provides reinforcement in the hoop and axial directions. The epoxy resin allows binding and transferring loading through the whole composite system.

REINFORCEKiT 4D is a wet lay-up system. It is wrapped helicoidally around the pipe in order to bring the mechanical resistance to the damaged pipe section. The number of layers, determined by calculation, is linked not only to the pipe pressure, temperature, diameter and thickness but also to the pit depth and length, the steel grade and the pipe location. The repair design and material requirements is provided by 3X software REA after information compilation according to ASME B31G, ISO 24817 and ASME PCC-2 codes and standards.

REINFORCEKiT4D-ECHT FEATURES

REINFORCEKiT 4D-ECHT is recommended to repair and reinforce pipe operating at temperature between +50°C (+122°F) to +110°C (+230°F)  subject to external corrosion, dents or mechanical damages. The system restores the pipe integrity and prevents from further deterioration. This composite sleeve is made of 400 g/m² Kevlar® tape and ceramic reinforced epoxy resin. This specific resin composition provides good anti-abrasion and chemical features.

USES

• External corrosion • Pitting • Dents • Weld defects • Mechanical damages • Suitable for +50°C (+122°F) to +110°C (+230°F)

BENEFITS

• No heating or post-curing required • Online repair (no shutdown) • Conform to any shape including welds, elbows and tees • In accordance with standards • No overload on corroded pipelines • Not hazardous for users

RESIN SPECIFICATION Chemical Name R3X1080 Chemical Family Epoxy (bi-components) Color Black Mixing ratio by weight (Part A : Part B) = 4.66 : 1 Pack size 1.7 kg/set Solids 100% VOCs none Storage Between +10°C (+50°F) and

+32°C (+90°F) if long term storage Shelf life 2 years in unopened containers

FIBER SPECIFICATION Fiber nature Aramid Kevlar® 49 Fiber directions towards pipe axis Hoop/axial (0 / 90°) Fiber type Woven type Tensile strength 2 900 MPa (420.5 Kpsi) Tensile Modulus 110 GPa (15 950 Kpsi) Density 1 450 Kg/m3 (90.6 Ib/cu.ft.)

Page 2: Tds r4d Echt

Pipe Reinforcement & Composite Repair for External Corrosion From +50°C (+122°F) to +110°C (+230°F)

3X  ENGINEERING,  9  avenue  Albert  II  -­‐  Tel:  +377.92.05.79.81  -­‐  Fax:  +377.92.05.72.71  -­‐      98  000  MONACO      www.3xengineering.com  ref:  RD4-­‐ECHT  TDS  –  11/2014  –  EN      

CHECK  OUT  THE  LATEST  REVISON  ON  http://files.3xeng.com  

COMPOSITE SPECIFICATION

TEC

HN

ICA

L S

PE

CIF

ICA

TIO

N

Percentage of Fiber in Volume Between 30% to 35% Nominal ply Thickness 0.8 mm* (0.032inch)

*: depends on ambient temperature and viscosity Total layers normal range (Typical) 6 to 30 layers Density 1.25 Kg/m3 (78.0 Ib/cu.ft.) Application temperature From +70°C (+158°F) to +110°C (+230°F) Service temperature From +50°C (+122°F) to +110°C (+230°F) Glass transition temperature (ASTM D7426) +130°C (+266°F) Curing time after job completion:

- given values could be shorten by using ATEX approved heating belts

- values just given as information

+70°C (+158°F) +110°C (+230°F) Light load 4 days 5 hrs

Full load 7 days 10 hrs

ME

CH

AN

ICA

L P

RO

PE

RTI

ES*

Tensile Strength in Hoop direction long-term (ASTM D1598) 188 MPa (27 260 psi)

Tensile Strength in Axial direction long-term (ASTM D1598) 50 MPa (7250 psi)

Tensile Modulus in Hoop direction (ISO 527 or ASTM D3039) 31 GPa (4 500 Kpsi)

Tensile Modulus in Axial direction (ISO 527or ASTM D3039) 8 GPa (1 160 Kpsi)

Poissons ratio (ISO 527 or ASTM D3039) 0.16 Shear Modulus (ASTM D5379) 3 GPa (435 Kpsi) Impact resistance (ASTM G14) 11.2 J/m2 Shore D hardness (ISO 868 or ASTM D2583) >73 shore D Lap Shear Strength (BS EN 1465 or ASTM D3165) 16 MPa (2 320 psi) Cathodic disbondment (NF A49 711) Passed Fatigue test (defect dependent) >35 000 cycles (70-100% MAOP) with wall-through defect

CH

EM

ICA

L P

RO

PE

RTI

ES

Resistance to pH From 3 to 12

Chemical resistance Excellent

*  values  are  given  for  indication  and  may  vary  depending  on  the  environment

APPLICATION NOTES

KIT COMPOSITION The REINFORCEKiT 4D-ECHT is made of 50 m long Kevlar® tape and 5 kg of R3X1080 epoxy resin.

SURFACE PREPARATION Proper surface preparation is critical to the long term performance of the composite. All rust, mill scale, corrosion products and foreign matter must be removed from the surface by a combination of solvent washing and MBX or abrasive blasting. After surface preparation, roughness should achieve a minimum of 70µm and match with SA 2 ½ or ST3 standards. Then the surface must be cleaned and rinsed using an adequate solvent which evaporates leaving no film residue.

APPLICATION Check atmospheric conditions before job start (TDew point +3°C< TSupport; 85%RH). If the pipe presents some pitted areas, specific filler must be used to fill pits and reshape the pipe. Apply a uniform layer of R31080 resin on the whole surface. The Kevlar tape is then impregnated and wrapped helicoidally over the pipe. Application instructions are provided to technicians during a 3X training course. Apply a protective coating as per company standards and local pipe environment (UV, swamp, etc).

SAFETY Each applicator should read and understand the Material Safety Datasheet before use 3X products.

WARRANTY DISCLAIMER Every reasonable effort is made to insure the technical information and recommendations of this data sheet are true and accurate to the best of our knowledge at the date of issuance. However, improvements being continuously implemented to 3X products, this information is subject to change without notice. Please contact your 3X distributor for the most current products specifications. This 3X Engineering technical datasheet warrants the quality of this product when used according to directions. User shall determine suitability of the product for use and assumes all risk.