Stainless Steel Welding by Weld Reality

Welding Stainless Steels and Stainless Data:

TIP TIG now available in North - South America and Australia.TIP TIG. Superior weld quality than TIG at Pulsed MIG & flux cored

feed rates.

http://www.weldreality.com/TIP-TIG-Welding.htm

The world's best process for welding any all position, thin or thick stainless / duplex or alloy applications is TIP TIG.

TIG Welding Stainless Steel

E-mail. Question: Ed as we have a variety of weld process selections for stainless . What MIG and flux cored wires / processes should we consider when welding stainless steel in the gage to 25 mm range?

Answer: The following primary weld considerations will influence the weld process required.

[] Distortion potential. [] Cleaning and oxidation concerns.[] Part thickness. [] Weld positions.

[] For welding stainless steel applications, it's been

http://www.weldreality.com/TIG-stainless-steel-welding.htm


traditional and logical to use use TIG or the MIG short circuit process with an 0.035 (1mm) wire, when welding < 2 mm stainless steels.

[] A REAL WORLD PULSED MIG BENEFIT: In contrast to "short circuit", to increase weld speeds on gage parts and provide superior weld surface, (more fluid) consider the pulsed MIG process. For pulsed on stainless consider the gas mix I developed argon 2 - 5% CO2 (see MIG gas section) and 0.045 wire. The pulsed choice is especially appropriate for stainless welds on applications in the range of 16 gage to 3/16 thick.

[] For stainless / duplex applications > 5 mm for flat and horizontal welds, consider an 0.045 MIG wire. Use spray with argon 2 - 5 % CO2 for optimum welds, and consider pulsed with the same gas mix if heat, distortion or spatter issues. For these weld also consider the 0.062 (1.6 mm) gas shielded flux cored wire with argon 20 to 25% CO2.

[] For MIG welding in the vertical position. If parts are < 4 mm, try welding vert down. Use argon 2 - 5% CO2 and spray with 0.035 wires and pulsed MIG with 0.045 wires.

[] For MIG welding in the vertical position on stainless steel parts over 3/16 thick, (> 5mm) welding vertical up or overhead applications, consider an 0.045 gas shielded flux cored wire with argon 20- 25% CO2. Do not weld vertical down with the gas shielded flux cored wires.

[] Now we have the MIG data out of the way, any weld shop that welds stainless and has not looked at TIP TIG is a weld shop thats way behing in weld technology.


Safety weld issues are a primary concern for anyone who welds stainless steels and nickel alloys...

OSHA held hearings on it's proposal to reduce the PEL for hexavelent chromium from 52 micrograms per cubic meter to 1 microgram per cubic meter as an 8 hour time weighted average. By court order OSHA is required to adopt a final rule by Jan 18 2006. Click for MIG Welding Stainless Steel safety issues

Don't forget with TIP TIG you get the lowest stainless or Inconel welds fumes and likely will not need exhaust equipment.

MIG WELDING STAINLESS STEEL GAS MIXES AND WELD REALITY....

In the last three decades, the biggest selling gas mix in North America for MIG welding stainless steel, thin gage applications, has been a tri-


http://www.weldreality.com/Safety%20stainless%20issues.htm


mix containing 90% helium - 7.5% argon and 2.5% CO2. In contrast to the three part helium tri-mix, a less costly, two part mix, argon - 2 % CO2, (a mix Ed developed in the nineteen eighties), has always provided more thin gage, stainless weld benefits.

There are over 60 MIG gas mixes available for all MIG applications. With these six mixes Ed has defined the world's best gas mixes.

Visit the MIG Welding Stainless Steel Gas Section

With TIP TIG ONLY ONE GAS IS REQUIRED FOR ANY WELD ON ANY ALLOYS


http://www.weldreality.com/MIG_welding_gases.htm

WHAT IS STAINLESS STEEL MADE OF?

STAINLESS STEEL COMES IN MANY FORMS.

Welding Stainless Steel Grades

Austenitic, Martensenitic and Ferritic STAINLESS STEELS.

Austenitic Stainless Steels are the ones we are most familiar with. These chrome nickel steels, in contrast to lower cost

stainless have more alloys and are "non magnetic" (Exception, types 310 - 330)

Austenitic Facts: Austenitic grades typically contain a minimum of 18% chrome - 8% nickel and are often called 18/8 steels.

Austenitic Stainless steel Grades 20-202-205-301-302-303-304-305-308-309-310-314-316-317-321-329-330-347-389-17 7PH- 17 4PH-PH15-7Mo-AM 350-AM 355 A 286.

Common Designations: 304 (S30400) - 304L (S30403) 316 (S31600) 316L (S31603) - 347 (S34700).

Stainless Steel Grades 301-302-304-305-308 usually welded with E308.

18/8 grades used for machine parts exterior buildings and industrial parts.

18/8 not to exceed 800F 426C service temperature.

Manganese grades of stainless "200" series similar to 18/8 grades. Manganese in this series is used for "extra strength" Welding the manganese grades usually requires the use of the E308L filler.|

Martensitic and Ferritic Grades are common stainless steel grades that we don't want to weld and if we do, we weld with great caution.

Martensitic Chrome steels. Weldability, limited. Preheating typical 250°C to 450°C. Postweld treatment: Slow cooling to 120°C (martensitic transformation) and annealing at 750°C or hardening (generally 1000°C / oil), tempering (generally 750°C). Watch for formation of chromium carbide between 500°C and 650°C...

Note: When welding these grades the weld procedure concerns and focus will be on HEAT treat requirements.

STAINLESS STEEL WIRE INTERNATIONAL SPECIFICATIONS.

US AWS A5.9 / UK BS2901 / Japan JIS Z3321/ ISO 3581/ Germany DIN 8555 - 8556

UNS International filler metal numbers start with WXXXXX

From Avesta: Stainless steel evaporators at Smurfit Kappa Kraftliner, Piteå.

TYPICAL STAINLESS STEEL FILLER METALS

Stainless Filler Metal Information:

StainlessFiller

International Specs

Chemistry

Manufacturesdesignations

Applications

Electrode

Germany SG X5 Cr

C 0.08Mn 1 -

Thyssen-Therm J

E308 is typically

E308

Ni 19.9ISO 23.12

UNS W30940

2.5Si 0.25-0.6Ni 9-11Cr 19.5-22

Kobe-MGSLincoln L18.8Pacweld -PW176SSSanvik 19.9

used when the corrosive conditions are not severe

ElectrodeE308L(low carbon)

Germany SG X2 Cr Ni 19.9

ISO 119.9L

UNS W30843

C 0.03Mn 1 - 2.5Si 0.25-0.6Ni 9-11Cr 19.5-22

ESAB -OK 16.10Thyssen -JESandvik 19.9L

Note (L).The lower carbon is used to avert the formation of carbide precipitation

Electrode308LSi

ESAB- OK 16.12Thyssen - JESiSandvik 19.9LSiFilarc - PZ6061/6561TREFIL 2PPSG

Note Si or Hi Si. The high silicon can increase arc stability and the weld wetting, which is important for some the low amp, sluggish, short circuit welds

Electrode309

Germany SG X12 Cr Ni 22.12

ISO 23.12

UNS W30940

C 0.012Mn 1 - 2.5Si 0.25-0.6Ni 12-14Cr 23-25

ESAB- OK 16.53Sandvik- 24.13Thyssen -Therm 25.14

Used for welding 309 and austenitic to ferritic (carbon) steels

Electrode309L

C 0.03Mn 1 - 2.5SI 0.25-0.6Ni 12-14Cr 23-25

Used for weld overlay applications or butter passes.

Electrode310H

C 0.10 -0.12Cr 26Ni 22

(H) Has minimum carbon content lower carbon can cause micro cracking causing tensile reductions

Electrode310

Germany SG X12CrNi 25.20

ISO 25.20

UNS W31040

C 0.08-0.15Mn 1 - 2.5Si 0.25-0.6Ni 20-22.5Cr 25-28

To weld 310 and 304 clad and stainless overlay

For low or high temp, corrosive or any critical applications always confirm electrode choice with wire manufacturer.Using ELC ensure weld gas has less than 3% CO2. A low co2 mix is

less oxidizing than a low oxygen mix.For low carbon base use low carbon filler identified by EXXXL

Electrode312

Germany SG 9250XRCUNS W31240ISO 29.9

C 0.15Mn 1 - 2.5Si 0.25-0.6Ni 8-10Cr 28-32

Higher Ferrite.More "crack resistance" than E309.

Electrode316

Germany SG9250ZRC UNS W31640ISO 19.12.2

C 0.08Mn 1 - 2.5Si 0.25-0.6Ni 11-14Cr 18-20Mo 2-3

ESAB- 16.35Thyssen - Therm G.Sandvik 19.12.2

for 316 steels and good for "high temp" corrosion resistance

Electrode316L

Germany SG X2 CrNiMo 19.12ISO 19.12.2LUNS W31643

C 0.03Mn 1 - 2.5Si 0.25-0.6Ni 11-14Cr 18-20Mo 2-3

Electrode317L

317 Germany SG CrNiMo 1813ISO 19.13.4UNS W31740

317L UNS 31743

C 0.03Mn 1 - 2.5Si 0.3-0.65Ni 13-15Cr 18.5-20.5Mo 3-4

Has moly to increase the tensile strength. Has excellent corrosion resistance and high temp properties Note contains considerable ferrite which can lower toughness

properties.

Electrode318

Germany SG X5 CrNiMoNb 1912

Electrode320

used for welding Carpenter 20 plus 20Cb-3 stainless

Electrode321

UNS W32140

C 0.07Mn 1.43Si 0.58Ni 10.52Cr 18.58

For weld data and information on Carbide Precipitation scroll down to weld data

Electrode347

Germany SG X5 CrNiHb 1999UNS W34740ISO 19.9No

C 0.069Mn 1.59Si 0.49Ni 9.96Cr 20.82

ESAB 16.11Thyssen Therm H.Sandvik - 19.9Nb

used for 321 - 347 better corrosion resistance than 308E347-321 wire is stabilized with small amounts of Ti or Cb to prevent carbide precipitation

Electrode 349

UNS 34940

Electrode410

Germany SG 5 350UNS

W41040ISO 13-EZ13-189

Electrode430

Germany SGS 250 ZrISO 17 - EZ17UNS W43040

13 May 2009. SELECT ARC ANNOUNCES NEW 430L-Cb METAL CORED WIRE:

US-based Select-Arc Inc. has introduced a metal cored, ferritic stainless steel electrode that is designed for welding on thin sheet metal materials. SelectAlloy 430L-Cb's higher chromium content combined with the columbium (niobium) stabilization provides similar heat and corrosion resistance to the base metals which are welded. This electrode handles poor fit up and gaps and is easier to weld than solid wire. SelectAlloy 430L-Cb delivers faster travel speeds, less burn through and less spatter to provide greater productivity. It also offers easy transition to spray transfer. SelectAlloy 430L-Cb is well suited to weld the heat resistant, corrosion resistant, ferritic stainless steels used in exhaust system components. Typical applications include manifolds, converters, mufflers and tubular components of automotive exhaust systems made of 430 grade materials. This electrode is available in .045in, .052in and 1/16in diameters.

Note from Ed. As many manufactures of exhaust components lack the engineering and manufacturing expertise to make their exhaust products within the specified design dimension tolerances, this 0.045 metal cored wire would provide weld benefits as it can utilize lower weld currents than MIG wires. This weld wire would do a good job bridging the weld gaps that are infamous in this industry. archive...

PICKLING AND SMUT ON STAINLESS:

From Avesta: Stainless smut is a common problem that results after pickling. Smut is an undesired discoloration that deposits on stainless steel surfaces after pickling, it appears as a dark sticky film. Its difficult to pinpoint why the smut has formed. There are a large number of possible causes and factors. The most frequent of these are:

• Contaminated surfaces (dirt and or glue residues from plastic film).• Uneven pickling.• Inadequate rinsing.• Poor water quality.• Substandard circulation/stirring in the pickling bath.• Old, contaminated pickling bath.• Poor steel quality.• Nitrate-free pickling solutions.

Research has shown that smut is more likely to occur when metal

dissolution by the pickling acid increases Fe2+ levels to the point where the redox potential of the pickling solution falls below a certain value (Fe + 2Fe3+=> 3Fe2+). Under these conditions, a passive chromium layer is not formed. This leaves the steel surface vulnerable. Loose oxide particles and other elements in the pickling acid may then easily attach themselves to the surface.

Low alloy-stainless steels are more sensitive to smut formation than are their high-alloy counterparts. This may be due to the high pickling rates that, particularly with high acid levels, are characteristic of low-alloy steel grades. Reducing smut with FinishOne™ Besides excellent NOx reduction and passivating power, FinishOne™ has also demonstrated that it is a real “smut killer”. Sprayed onto a still wet steel surface, it promotes Fe2+ to Fe3+ oxidation and thus prevents smut formation (Fe2+ + FinishOne => Fe3+ + H2O). Smut caused by silicone residues on the surface Smut and NOx reduction using FinishOne™. Smut caused by a film of oil on the surface When Fe3+ is the dominant ion, the resultant passivation protects steelsurfaces from both corrosion and adhesion. A final rinse with FinishOne™ ensures a passivated surface that is free from water stains. If they do not receive proper post-weld treatment, stainless steels soon lose their stainless property. Thus, correct pickling, passivation, et cetera are all vital. This is especially true in the pulp and paper industry, where highly aggressive media are used at high temperatures. Avesta Finishing Chemicals has the products, expertise and support to meet the stainless steel finishing requirements of the pulp and paper industry worldwide.

POOR WORK HABITS, POOR HANDLING AND POOR MAINTENANCE CAN MAKE STAINLESS FABRICATION SUSCEPTIBLE TO RUST.

If you work in a weld shop that welds stainless, you may have seen rust form on those stainless parts. To get corrosion to form on stainless does not take much. Lift the stainless parts with a fork lift, strap the parts with a steel band, clean the parts with a steel brush or steel wool or grind

steel parts near the stainless parts and a few days later that familiar rust will appear.

There is a good reason that weld and fab shop are asked when making stainless parts to to isolate stainless from carbon steel components. When you look at that shiny stainless part remember it's protected by a self healing, very thin oxide film and as long as that film is intact and there is oxygen present, the stainless remains rust resistant. Even when the stainless surface is damaged and not contaminated, the stainless film will recover. However when the stainless is attacked by carbon steel contamination, the film is unable to recover and under the film their is active metal waiting to corrode.

That welder grinding carbon steel parts creates micro steel particles that fly through the air and can attach themselves to a stainless part. Left in an open environment, the carbon steel grinding particles eventually dissolve and the iron oxides that result will contaminate the surface of the part. The iron oxide contamination prevents or reduces the oxygen from reacting with the stainless part in the contaminated area making not allowing the oxide film to occur. This results in an active stainless which is sensitive to the formation of rust.

Abrasive movement of any carbon steel against a stainless part, such as from steel rolls on conveyors, fork lifts or crane steel handling clamps will also contaminate the stainless. A common method of none abrasive carbon steel contact can come from manual or robot welding stainless in a carbon steel fixture. If the carbon steel fixture components are are in close proximity to the stainless welds, this can lead to carbon pickup in the stainless that will in a short period result in the formation of corrosion.

Apart from the common stainless contamination that results during material forming / handling, a very common cause of corrosion results from the use of grinding wheels contaminated with steel particles or steel wire brushes. When lifting parts with a fork lift, use none steel components that separate the steel

forks from the stainless. When you strap those stainless parts, place wood between the bands and the stainless. With stainless weld operations using carbon steel fixtures, ensure no carbon steel part is within 25 mm of the welds. If fixture parts are within close proximity of the welds replace the carbon steels components with stainless, copper or aluminum.

Rust around Stainless Welds

Question: Ed. Recently our company fabricated 316L gage pipe. The finished weld products have been out doors at the site for approximately 2 weeks and now about 15% of the welds are showing rust at the weld seams. Our procedure for weld cleanup was to use a stainless wire brush followed with a citric acid passivation. We really are at a loss as to why this happened.

Answer from Brad Hass. This very interesting for me, we had a similar problem on 304L structures for a blast freezer. It turned out to be from the use of a 302ss powered brushing operation. We had a company come in, to apply pickling gel to the damaged areas. It works! The reason I don't believe you had a carbon steel brush in use, is citric acid treatments will remove that, and will not remove contamination from 302

and 304 powered brushing. Nitric/Hydroflouric and brush electropolishing is the only thing we have found to remove this. I have confirmed all the above with salt spray testing 24 hr 5% solution. One other thing the larger the bristle diameter the worse the contamination. I recommend in the future 316L brushes for your clean up, this works. Brad..

Reply from Ed. In weld shops welding inconsistency is normal and therefore cleaning practices should also be looked at..

If the shop manager came in on the second shift, would he find Fred the welder cleaning the stainless welds with carbon steel brushes or wheels, or with contaminated stainless brushes or wheels.

When I look at the pipe seam and circumferential welds, it's notable that the corrosion is localized , (caused by one individual) and only a small percentage of the welds were contaminated. Therefore it's logical to assume that an inappropriate cleaning method was used during fabrication and welding. I believe that possibly in some areas the correct stainless brushes or wire wheels were utilized and at other times the welders picked up carbon steel brushes or used cleaning wheels or abrasives that were contaminated from their use on steel components

The stainless flange cleaned with B570 and coated with a nanolyer available from Innomet.

Any rust formation on stainless should be removed and the fab shop has many ways to approach this task..It's logical in the fab shop to pick up steel wool or a grinder and take that to the contaminated area, however the wheels or wool can cause surface damage which combined with the existing contamination can again lead to later corrosion spread over a wider area. Rust can be removed from the stainless surface without damaging the surface with the use of pickling liquids or inorganic chemicals. The negative aspect of pickling or inorganic chemical is the impact on the environment and the hazards to the people who apply the chemicals. With this in mind their are in 2008 some unique products available that eliminate iron oxides and provide deep cleaning of contaminated stainless parts . Of course the most cost effective practice for the e fab shop, is don't allow the stainless parts to be contaminated.Check out a company call Innomet and look at their unique chemical approach to stainless cleaning and rust removal. Innomet visit. http://inno-soft.nl/en/index.html.

Welding High Strength, High Carbon Steels with Austenitic Stainless or Nickel Filler Metals.

[] Austenitic stainless steels are prone to hot cracking and so attention is required to cleaning before welding and welding using low to medium weld parameters. Concern for formation of chromium carbide at grain interface especially if the carbon content is higher then 0.04%. No preheat is usually required.

Filler metal: % C = max. 0.04%

In welding carbon steels to stainless, the austenitic / nickel filler metals offer unique features that can reduce weld crack potential in both the welds and weld heat affected zone (HAZ). Carbon to stainless welds require that the stainless weld metal have sufficient ferrite to resist cracking. When welding carbon steel to stainless and a 309L wire is used, the resulting ferrite is approximately 14-16FN.

If the steel is a high carbon steel, a 309L, first weld pass on the carbon to stainless will likely end up with "insufficient ferrite". The carbon from the high carbon steel when mixed with the stainless weld will suppress the ferrite formation. Instead of the 309L for this application, a 312 electrode may be recommended.

The 312 filler metal, (70 to 90 FN in the weld metal) produces much higher ferrite levels than the 309L. This is the prime reason the 312 is recommended for applications sensitive to weld cracks. Filler metals such as 307 - 308 Mo and 310 can resist cracking with the aid of alloys and without the aid of ferrite.

HOW AUSTENITIC & NICKEL WELD ELECTRODES CAN HELP HIGH STRENGTH CARBON STEELS. High carbon, high strength steels welded to each are subject tohydrogen assisted cracking.

[1] High hardness.[2] A source of hydrogen.[3] High stresses. These are the three fundamental requirements for hydrogen assisted cracking.

With the high carbon steels, high hardness is typical in the HAZ unless very high, (often not practical) preheat and interpass temperatures are utilized for the welds.

The stresses that can influence HAZ cracking typically result from weld residual stresses caused by weld shrinkage, these stresses can be further exaggerated by weld joint restrictions as found in certain fixtures.

As we are all aware, hydrogen in the weld can be derived from many sources.

An alternative to a high carbon, high strength filler metals, in which the carbon dilution from the base metal will result in a hard weld, subjecting the weld to transverse cracking, is to use an austenitic or a specific nickel based filler metal (ENiCrFe-2).

The austenitic or nickel filler metals greatly reduces the weld transverse cracking potential. Also these filler metals greatly reduce, slow down or trap the weld hydrogen that can diffuse from the weld into the HAZ, this greatly reduces HAZ hydrogen cracking potential.

The diffusion of hydrogen though austenitic and nickel filler metal welds and steel can be approximately 80 - 110 times slower than through carbon steels and welds. The use of the austenitic and nickel filler metals can greatly reduce cracking however these filler metals can still absorb hydrogen so these electrodes should be treated with the same respect and rules that apply to any low hydrogen filler metals.

Note: MIG welding. Use Ed's unique Stainless, Duplex MIG Gas Mix to reduce any types of weld cracking. With any stainless flux cored wires

use the argon CO2 mixes recommended for carbon steel flux cored wires.

When to use a 308L, 309L or 316L filler metal.

[] 308L and 308LSi is predominately used on austenitic stainless steels, such as types 301, 302, 304, 305 and cast alloys CF-8 and CF-3.

[] For high temperature applications such as in the power industry, higher carbon 308H electrodes will provide superior creep resistance than does 308L .

[] Use 309L and 309LSi when joining 309 or mild steels / low alloy steels to stainless steels. Use 309 when joining dissimilar stainless steels such as 409 to itself or to 304L stainless. CG-12 is the cast equivalent of 309.

[] Some 308L applications may be substituted with 309L filler metal, but 316L or 316 applications generally require molybdenum. Note, 309L contains no molybdenum.

[] 316L and 316LSi should be used with 316L and 316 base metals. CF-8M and CF-3M are the cast equivalents of 316 and 316L, respectively.

[] Type 347 stainless steel filler metal is used for 347 and 321 base materials because it matches these stabilized grades. CF-8C is the cast equivalent of 347. Type 347 filler metal is also suitable most 308L filler metal applications.

Excellent stainless gas shielded flux cored wires are available from Alloy Rods and Kobleco.

Around the Globe Sanvik and Avesta setthe standard for MIG Stainless wires.

ELIMINATE STAINLESS WELD POROSITY:

Weld porosity, a cavity discontinuity that forms from a gas reaction. The porosity can be trapped in the weld or at the weld surface. The porosity is typically round in shape but can also be elongated. In contrast to argon oxygen mixes, Ed's MIG Stainless. Duplex gas mix was developed for less oxide reaction, less porosity potential.

The world's best process for producing optimum stainless

or duplex welds will always be is TIP TIG.

ROBOTS AND MIG POROSITY. When you find the robot weld porosity is always at the same location and the weld porosity is not at the weld starts or ends, examine the robot movement and see if the robot arm is causing a restriction of the gas flow line. Also it's common with robot cells to see a severe gas flow restiction due to the narrow orrifice found in gas line connections. In a robot cell its critical to measure gas flow as it exits the gun. If the porosity is at the weld start or stop increase the gas pre flow and post flow times.


Weld porosity, a cavity or discontinuity that forms in the weld from a gas reaction in molten metal. The weld porosity can be trapped in the weld or evident at the weld surface. Weld porosity is typically round in shape, but can also be elongated.

Weld porosity is caused by the absorption of oxygen, nitrogen and hydrogen into the molten weld pool. The gases are then released on solidification and may become trapped in the weld metal.

Nitrogen and oxygen absorption in the weld pool usually originates from inadequate or contaminated gas shielding, leaks in the MIG gas line, excess gas flow rates, draughts and plate contamination.

Hydrogen can originate from a number of sources including moisture from the electrodes,moisture on the parts, contaminates on the workpiece surface. (Use dry pre-heat > 100F , oxy fuel > 250 F)

CLUSTER WELD POROSITY. A localized group of pores with random distribution. Causes. Arc blow, insufficient, inconsistent or excessive weld gas flow,

material or weld wire contamination, (low) weld parameters or poor technique.

PIPING, WORM HOLE, WAGGON TRACKS POROSITY. Sometimes called "waggon tracks". Typically found in the center of the weld, parallel to weld axis. Classic porosity when moisture is evident in gas shielded flux cored wires, (the cheaper the product the more prone to waggon tracks).

Increasing the flux cored wire stick out and increasing the wire feed rate helps by adding energy to the wire.

Baking flux cored wires and storing the wires in a dry environment also reduces potential. Slow weld speeds, make welds larger, avoid weaves. All recommendations are intended to increase the weld arc energy and decrease the weld cooling rate.

Worm holes are elongated gas pores producing a herring bone appearance on a radiograph. Worm hole porosity is common in gas shielded flux cored welds when the electrodes have too much moisture in the wire flux.

WELD ROOT POROSITY. Weld root porosity frequently occurs when MIG welding using "argon oxygen" (oxidizing) mixes on parts >6 mm. With these gas mixes the resulting root is typically narrow, finger shaped. The root finger area solidifies rapidly trapping porosity. To reduce the stainless root weld porosity, change to an argon 2 - 4 CO2 gas mix. Increase the weld parameters, slow the weld speed and avoid weld weaves.

ALIGNED WELD POROSITY. Linear porosity, an array of small round pores typically found in a line. Often caused from the base metal lubricants or metal surface contaminate. Add weld energy (increase wire feed), increase push angle allowing the arc to break up surface oxides ahead of weld.

SCATTERED WELD POROSITY. Weld porosity scattered randomly throughout the weld or welds. If the MIG weld surface is gray and looks oxidized, the porosity is typically a result of insufficient gas flow. If

the weld surface looks clean with scattered porosity the porosity is usually caused by the base metal part or electrode contamination, or perhaps the weld data used causes the weld to freeze too rapidly.

LARGE PORE WELD POROSITY. If weld surface is clean and does not look oxidized, the large pore MIG / FCAW porosity could be a result of excessive gas flow. Gas turbulence is caused with gas flow greater than 40 cuft/hr. Optimum MIG and flux cored gas flow for carbon steels is 25 to 35 cuft/hr, the gas flow should be measured as it exits the gun nozzle. If the weld surface is dirty (oxidized) the cause of larger pore porosity is ofen a result of insufficient gas flow, less than 20 cuft /hr.

Jan 2004. Sandvik Announces New Ultrahigh- Strength Stainless Steel "NANOFLEX":

Sandvik Materials Technology recently developed a new stainless steel called Sandvik Nanoflex that features ultra high strength and good formability, corrosion resistance, and surface finish. According to the

company, the steel is well suited for mechanical applications requiring lightweight, rigid designs such as medical equipment and for replacement of hard-chromed, low-alloy steels in the automotive industry.

Examples of the strength properties of Sandvik Nanoflex are 1700 MPa tensile strength, 1500 MPa yield strength, 8% elongation, 45-58 HRC hardness, and a Charpy V impact strength of a minimum of 27 J at -20°C. Exact strength values depend on the product form and the manufacturing route.

Despite its high hardness, the company claims it is easy to perform cold forming operations such as bending, cutting, turning, and grinding. After reaching the desired shape, a simple low-temperature heat treatment gives the material its high strength without distorting the workpiece.

This material also displays good welding properties. It is available in tube, strip, wire, and bar forms.

Stainless Steel Filler Metal Selection Stainless Type

FILLER METAL SELECTION AWS A5-9. Use first choice. Confirm choice with wire manufacturer

AUSTENITIC CHROME NICKEL NONE MAGNETIC

Stainless 201 to austenitic 200-300 series use

201 used for low temp cryo applications to -320F

308 for 330 use 312


308 for 330 use 312

Stainless 201-202-301 303 to mild steel use

312

Stainless 210 - 202 -301 to mild steel.Stainless type 201 requires special consideration required to avoid hot cracking as ferrite extremely low

312 can reduce cracking as it provides much higher ferrite than 309.


308 for 330 use 312


308 for 330 use 312

Stainless 302 - 302b 304 to mild steel use

310

Stainless 302 - 302B -304 to mild steel use

310


308 for 330 use 312

Stainless 303 to 310-314-330- use 312

Stainless 303 to mild steel use 312


308 for 330 use 312

Stainless 305 308 to mild steel use 312


308 for 330 use 312

Stainless 305 - 308 to mild steel use 312


308 for 330 use 312

Stainless 309 to 309 - 310 - 314 -316 - 317 use

309

Stainless 309 to 330 use 312

Stainless 309 to 347 use 308 - 347

Stainless 310 to 310-3140 310






Stainles 310 to mild steel use 310




Stainless 314 to 321 308



Stainless 314 to mild steel use 310

Stainless 316 to 316 - 317 use 316


Stainless 316 to 330 312 - 309

Stainless 316L to mild steel use 309

Stainless 316LN a nitrogen addition to a low carbon stainless Incesase both corrosion resistance and strength as compared to 316L

316L or 317L317L typical for corrosion316L for toughness(cryogenic type applications




Stainless 317 to 347 use 308L

Stainless 317 - 321 - 348 403 - 405 410 414 416 to mild steel use

309

Stainless 321 to 321 - 347 347



Stainless330 to 347 use 312 - 309

Stainless 348 347

Stainless 384 309

Stainless AM 350 AM 350

Stainless 410 Condition AASTM 27612% Chrome, chrominum / martensitic steel

to itself or carbon309L

Stainless 501 502 430 431 442 448 to mild steel use

310

17-7PH use W17-7PH

PH15-7Mo use WPH 15-7Mo

17-4PH use 17-4PH

A286 A286

Sanicro 2827 Cr - 31 Ni -Mo 3.5 -Cu 1Tensile 73 ksi Yield 31 ksi

Sanvik 27.31.4.LCu ER028L

Duplex Ferritic AusteniticSAF 2304UNS 32304DIN X2CrNiN 24-423 Cr - 4 Ni - N 0.1Tensile 87 ksi - Yield 58 ksi

308 MoL

Duplex Ferritic AusteniticSAF 2205UNS S3180322 Cr - 5.5 Ni -Mo 3 - N Tensile 990 ksi - Yield 65 ksiWeld Note: For MIG use argon with 2% CO2. When welding 2205 or 2304 to dissimilar butter first with ER309MoL then weld with 308MoLNo concern for interpass temp, high amps can be use

2209

Duplex 3RE6018.5 Cr - 4.9 Ni - 2.7 Mo

weld same as 2205

254 SMO alloyElectrode Avesta p12Sanvik Sanicro 60 ENiCrMo3

Stainless to carbon 309 or 312 which has higher ferrite reduces cracking

MARTENSITIC STEELS 403 - 410 - 414 416- 420- 422 -431- 440Preheat and interpass temp 500F 260C Post heat 1350F 732C>Control cool 50F / hr to 1100F>Control cool to 1100F 600C then air cool.Treat the 500 series the same as the Martensitic series

Stainless 403 to 400 series use 410 ASTM 276






Stainless 405 to 400 series use 410

Stainless 410 to carbon steel 309L

Stainless 410 - 414 WELD same as 405

Stainless 416 - 440 butter with 312 or 309 first

Stainless 416 to 505 -502-501 -446 - 440 -430 -420 use

309

Stainless 416 to 431-420-416 use 410


Stainless 420 to 501-502 use 502


Stainless 420 to 440 -420 use 420




Stainless 430 to 446 - 440 - 431 - 430 430

use

Stainless 430F to 400 series use 309



Stainless 431 to 446-440 use 309

Stainless 440 weld same as 431





Stainless 501 to 505 - 502 - 501 use 502


Ferritic steels 405 - 409 - 429 - 430 -434 - 436 - 442 -444 - 446

444 to 444 or to other metal use 316L or 309MoL

Ferritic magnetic avoid prolong heat in the range of 750F -1700F (400-925C

Feritic preheat at 350F 176C To improve ductility

Ferritic steels most frequent electrodes

309 - 310 - 312

Ferritic steel if post heat required use Austenitic filler

Intergranular corrosion, also called intercrystalline corrosion, occurs on or adjacent to the grain boundaries of a metal. It is caused by microsegregation of impurities and alloying elements on the grain boundaries.The driving force of intergranular corrosion is the difference between the electrode potentials of the grain boundary and the grain itself, which form a galvanic cell in presence of an electrolyte.

Intergranular corrosion of stainless steels:

The microstructure of metals consist of a granular composition. The grains formed are small crystals. The crystal surfaces join the surfaces of other grains to form grain boundaries. Grain boundaries separate the grains. With stainless, intergranular corrosion, (intercrystalline corrosion), occurs on or adjacent to the grain boundaries of a metal.

Some causes of intergranular corrosion are welding, stress annealing, improper heat treating or overheating in service. Inspectors have difficulty in detecting the early stages of intergranular corrosion. This form of corrosion results in a loss of strength in metal parts where the grains have fallen out.

Intergranular corrosion is caused by microsegregation of impurities and alloying elements on the grain boundaries. The driving force of intergranular corrosion is the difference between the electrode potentials of the grain boundary and the grain itself, which form a galvanic cell in presence of an electrolyte.

If the phases segregated at the grain boundaries have lower value of electrode potential they will oxidize (anodic reaction) and the grain metal having higher value of electrode potential will provide cathodic reaction (reduction). Dissolution of anodic grain boundaries starts from the surface and advances along the grains interfaces. The process results in deterioration of the bonding between the grains and drop of mechanical properties. If the precipitates at the grain boundaries have higher electrode potential the grains will dissolve (anodic reaction). In this case the grain boundaries will not be attacked.

A summary of Stainless Steel Welds and Sensitization.

Metallurgist could write a book on this subject. I will try to keep it short and I hope its easy to understand.

[] With a stainless welds on specific alloys, sensitization occurs in the weld's heat affected zone (HAZ) when this zone is between approx. 900 and 1600F.

[] Sensitization occurs when the carbon content is sufficient to produce precipitation of chromium rich carbides along the HAZ grain boundaries.

[] The formation the chromium carbides results in a chrome depleted area around the grain boundaries. This location will be in the weld's HAZ at the furthest point from the weld.

[] If the weld's HAZ depleted chromium carbide area is subject to a corrosive medium the grains can rapidly corrode and cause separation from the weld.

[] A 304L metal will contain a maximum of 0.03% carbon. In contrast a 304 base metal can contain twice the carbon level of the 304L.

[] Welding and subjecting a 304 base to 900F to 1600F will cause sensitization in HAZ.

Solution to Stainless Steel Sensitization.

[1] Use a low carbon ( L grade) stainless. The typical 0.03 max carbon content is not sufficient for carbide precipitation.

[2] Consider a stabilized stainless steel such as 347 or 321. These steels are stabilized against chrome depletion with alloy elements that have a greter affinity to form carbides.

[3] Type 347 which is similar to 304 has niobium (columbium) for carbide formation. Let the niobium do its job and the chrome has no carbides to attach to, thus we prevent carbide precipitation.

[4] Type 321 is also similar to 304. Type 321 contains titanium and the titanium does the same job as the niobium. Keep in mind both the 321 and 347 are typically much more costly than the 304L.

[5] What about those common multi-pass "316 or 308 welds"? Of course the multi-pass welds are subject to the 900F to 1600F, however the weld metal in contrast to the stainless base metal will contain a small amount of ferrite in the austenitic structure. Chrome diffuses in ferrite approx. 100 times faster than it will in the austenite. The ferrite has more chrome than the austenitic matrix. The ferrite area will be rich in chrome so this area can supply an area subject to sensitization.

Avesta: A typical Pulp and Paper Mill Layout

Typical Pulp and Paper Mill Weld Consumables from Avesta

AVESTA 308L/MVRAvesta 308L is excellent for the welding of evaporators,storage tanks, etc. made from 304L (EN 1.4307, Outokumpu4307), a general purpose steel.

AVESTA 316L/SKRFor welding 316L (EN 1.4404/1.4436, Outokumpu 4404/4436), a well-proven austenitic grade that is used extensively in the pulp and paper industry.

AVESTA P12Avesta P12 was specially designed for welding fully austenitic 6 Mo steels, e.g. Outokumpu 254 SMO (EN 1.4547). Owing to their good resistance to corrosion (stress, pitting and crevice), these steels are used in, amongst other things, filter washers and wash presses in modern ECF bleaching plants.

AVESTA P54Avesta P54 is an iron-based filler metal that was speciallydeveloped for welding fully austenitic 6 and 7 Mo steels (e.g. Outokumpu 254 SMO) in applications where conventional nickel-based alloys are vulnerable to transpassive corrosion. D stage filters in the ClO2 bleaching of pulp are just one example.

AVESTA P5A molybdenum-alloyed filer of the 309MoL type, commonly used in the pulp and paper industry for dissimilar welding.

Stainless and Nitrogen Purge Gas Question.

Ed as you are aware Nitrogen is a lot cheaper than argon when utilized as a purge gas for

stainless. My question, When MIG welding stainless tanks edge or corner welds, tube or pipe open root welds, can nitrogen react with the stainless and have a negative impact?

Answer: Nitrogen has a diatomic, "two atoms" per molecule. Nitrogen in the diatomic form is usually insoluble in molten stainless. However if the nitrogen gets into the weld arc, the plasma arc energy can seperate the diatomic molecules and create monatomic molecules.

The monatomic molecules are soluble in the weld. The nitrogen, monatomic (seperated molecules) become an alloying element and can reduce the ferrite in a stainless weld. A reduction in ferrite in some alloys can cause the weld to be more austenitic and sensitive to hot cracking. If nitrogen enters a weld or the welding arc, it can have a negative and sometimes a positive influence. Thats the reason one of my gas mixes for duplex has the addition of nitrogen, and the other gas mix does not.

There are stainless alloys which do not need ferrite like 320 / 310. With these alloys nitrogen has no negative impact on these alloys. Also if the stainless alloys have high ferrite levels they typically can afford to loose a little of the ferrite to the nitrogen.

With closed root, austenitic stainless welds, as found in tanks, corner, edge welds, or thin gage, partial penetration tube welds, nitrogen is the logical, economical, purge gas choice for all austenitic, duplex, martensitic and precipitation hardening stainless steel applications. The only concern would be a few specific, ferritic alloys in which nitrogen could cause severe weld mechanical issues.

With an open root "MIG stainless weld" the nitrogen purge gas has little opportunity to get into the weld arc as the gas flow rate / pressure of the welding gas should be higher than that of the purging gas . However nitrogen could still be picked up by the weld. .

With duplex stainless there should be no concerns for open root nitrogen issues. The majority of the common, open root

stainless alloys will not be adversely affected by nitrogen purge gas. However in the world of product liability, here is the welding bottom line. If your weld job is large enough to produce a substantial cost reduction from using nitrogen gas, then it's logical to "pre qualify the nitrogen purge welds" and have the weld chemistry, ferrite and mechanicals tested.

Failed Stainless Pipe Weld Tests.

Question: Ed we weld austenitic stainless and carbon steel pipes. For cost reduction, in our stainless weld tests we only utilize "carbon steel pipes" and 309L SMAW or flux cored, electrodes. We frequently have root cracking issues, or during the bend test the weld sample breaks. What is strange is that we visually examine all the roots and we wont let them be mechanically tested unless the welds look OK. Why the inconsistency? why do

some tests welds pass and other good looking welds fail?

Ed's Answer: The bottom line the 309L electrode is designed to weld "carbon steel to stainless" this electrode was not designed to weld carbon steel to carbon steel thats why we have carbon steel electrodes.

Use the 309L electrode on two carbon steel pipes and weld dilution

becomes a concern in the weld root area. If the weld parameters and edge prep is such that the resulting weld dilution is minimal, the resulting 309L weld should be austenite with a little ferrite. It's the austenite / ferrite combination that provides weld ductility.

If while welding the carbon steel pipe root, the welder uses higher current, slower weld speeds or a wider weld weave, the 309L weld can end up with more weld dilution with the carbon steels, reducing the weld ferrite level and making the weld more austenitic. A reduction or loss of ferrite can make the weld subject to "hot centerline cracking" (hot cracking, the weld cracks during the weld or soon after).

A hot weld crack surface in a bend test can be identified by a blue or gray color. Even if the root pass does not crack the high austenite composition can turn to martensite when cooling. The brittle martensite can readily fracture during the bend test. (a silver color or bright fracture surface).

The bottom line if you look at the costs involved in the stainless to carbon steel pipe weld test, it makes little sense to use two carbon steel pipes. Ensure for your weld test that one of the test pipes is at least stainless.

FAILED 308L FLUX CORED WELDS SUBJECT TO HIGH TEMP:

Gas shielded stainless flux cored wires have an Achilles Heel: As pointed out by Kotecki in the QA section, March Weld Journal, it would appear that there is a problem with the use of specific stainless flux cored wires on pressure vessel applications subject to high temperatures or post heat treatment. In the stainless application reviewed, the weld shop applied a stress relief of 1475F for 12 hours to a 304L pressure vessel welded with gas shielded 308L flux cored wires. After the heat treatment many cracks were found in the 308L flux cored welds. These welds had no

cracks before the post heat treat.

It would appear the flux cored wire manufactures add specific alloys and compounds for easy slag removal. One compound contains bismuth.

Note from Ed: The bottom line for the 308L gas shielded flux cored weld cracking issues or part / weld premature creep failures at elevated temperatures is the stainless gas shielded flux cored wires utilized contain a compound containing "bismuth" This compound assists in easy slag removal. It's been reported that with levels of bismuth at 200 ppm. (200 ppm is a typical bismuth level) weld cracks have occurred at a reheat temp of 1050F.

What should you do if your stainless pressure vessel is to be used in a high temp application or the vessel requires post heat treat.

[] POST HEAT TREAT: To avoid major issues on an application subject to high temp post heat treat, its logical that a weld qualification procedure should encompass the required post heat treatment. This way you can check the welds in the real world welded condition.

[] CONTROL THE BISMUTH LEVELS: For high temp applications gas shielded stainless flux cored wires are available with bismuth levels < 20 ppm. These products are supposed not to exhibit reheat cracks or premature creep failure. Talk to your weld wire supplier about your concerns for the high temp.

[] REPUTABLE WIRE MANUFACTURERS: Don't purchase weld consumables that fell of the back of a truck on their way from China. Deal with reputable flux cored wire companies like Sanvik, Avesta and ESAB.

[] PROCESS ALTERNATIVES. Consider SAW or MIG.

Its important to note, that the majority of stainless are put into service at tempertures below < 500F and these applications have not been subject to the issues discussed. However there are also 300 series that undergo annealing and stress relief or are subject to high temp > 900F applications in the power industry.

Microfissures and 310 stainless.

Question. Ed when welding 310 stainless we a longitudinal bend test evaluation of weld samples we often end up with small linear shaped porosity which so far has gone unexplained. We weld a lot of stainless in this shop and so we are aware of cleanliness requirements and the use of good weld consumables , however the 310 pores are something we can't seem to shake. Most of the pores are less than 2 mm in length, and so they are acceptable however our designer has expressed concern that we may not be using the best weld consumables. Any ideas Regards Paul.

Answer: First 310 stainless and a few other grades are completely austenitic containing no ferrite. It's common with 310 - 330 multi-pass welds to find microfissures (not porosity) forming at the interface between the welds. It's also common to find these microfissures with longitudinal face or root bend tests. The microfissures don't occur with austenitic grades like 308L that contain ferrite. Reports from the WRC state that the small microfissures typically will not influence fatique, creep and corrosion properties, and as the 310 is very tough the microfissures typically don't propogate, however they can initiate pitting corrosion or reduce the critical pitting temperture. You can reduce the amount of microfissures by using filler metals with extra low sulfur and phosphororus, use stringer passes, maximum size similar to 6 mm fillet and ensure you use a max interpass temp of 250F.

Stainless Weld Data.

When MIG Welding stainless Steel you can use the optimum MIG wire feed data recommended at this site for carbon steels. The only change that will be required is weld voltage. As stainless will use a low reactive gas mix, less weld volts will typically be required. In contrast to MIG on carbon steels, when MIG stainless welds are made, typically 2 - 3 lower volts are required. Keep stainless clean, only use stainless wire brushes.

Stainless steel has a very thin and stable oxide film rich in chrome. This film reforms rapidly by reaction with the atmosphere if upset or damaged. If stainless steel is not adequately protected from the atmosphere during welding or is subject to very heavy grinding operations, a very thick oxide layer will form. The thick oxide layer will be

noted by it's blue tint. This oxide will have a chrome-depleted layer under it and this layer can impair corrosion resistance.

With stainless weld applications, both the oxide film and depleted layer must be removed, either mechanically (grinding with a fine grit is recommended, wire brushing and shot blasting will have less effect), or chemically (acid pickle with a mixture of nitric and hydrofluoric acid). Once cleaned, the surface can be chemically passivated to enhance corrosion resistance, (passivation reduces the anodic reaction involved in the corrosion process).

Carbon steel tools such as drilss, wire brushes or steel grinding wheels can contaminate the stainless surface. Also sparks from grinding carbon steel can embed fragments into the surface of the stainless steel. The carbon contamination or grinding fragments can rust if moistened.

STAINLESS STEEL & CARBON PICKUP.

With fixtures avoid carbon steels in close proximity to stainless welds, as carbon pick up possible, the weld area will rust. There are many ways to introduce carbon to stainless welds.

For stainless vert up welds on parts 3 to 6 mm, consider pulsed,

For stainless all position welds on parts > 6 mm, first logical choice will be always be stainless gas shielded flux cored wires.

Minimize the drive roll tension applied to stainless flux cored wires. For stainless flux cored weld data, use the carbon steel flux cored wire data found in my flux cored book. For stainless flux cored use an argon mix with 15 - 25 CO2.

STAINLESS & CARBIDE PRECIPITATION (chrome depletion):

Use weld data to avoid Carbide Precipitation. (CP)

If any part of stainless-steel is heated in the range 900-1400°F (482-760°C) for any reasonable time there is a risk that the chrome will form chrome carbides Cr23C6 with any carbon present in the steel along the austenite grains. Thi results in depletion of chromium from the austenitic grains resulting in decreasing the corrosion protective passive film. This effect is called sensitization. It is also called weld decay since it usually happens during welding process when the zone around the weld is heated. For stainless corrosive environments control of CP is critical.

CP typically occurs within 3 mm of either side of a weld HAZ

A chrome depleted area may not resist the corrosive environment. To combat CP use (L) low carbon base and filler metals. Ensure the C02 gas composition has less than 5 % CO2.

STAINLESS AND STABILIZED ELECTRODES:

You can combat CP with stabilized fillers which provide alloys that grab the carbon before it can affect the chrome. Alloys like E347 which work at reducing chrome depletion.

Stabilized fillers are typically used in high strength high temp service. However if base metal is not an L

grade CP will occur.

Rapid cooling of stainless through the 800 - 1600F range reduces Carbide Precipitation.

TIG welding and the influence of "sulfur" in austenitic stainless applications.

When the parts to be welded

have normal sulfur content (greater than 0.005%) an interesting event can occur. With increasing weld temperature the surface tension of the weld pool also increases. The result is the hottest part of the fluid weld surface is attracted to the middle of the weld pool causing deep narrow weld penetration.

With lower sulfur in the weld, the weld surface tension is less. The resulting weld is wider with less fusion. When two parts welded together have different levels of sulfur tension the weld may pull towards the lower tension, lower sulfur part, resulting in inconsistent weld fusion or penetration favoring one side of the weld joint. This occurrence is especially notable when automated TIG welding Dissimilar parts such as cast parts to sheet or pipe.

The following weld solutions may assist the sulfur issues.[1] Pulse the application.[2] Use a weave.[3] Weld twice.[4] Use heat sink back up bars in close proximity to weld.

Stainless Weld Cracks:

308 WELDS CRACK DURING POST HEAT TREAT.

Question: We just finished welding a 304L pressure vessel. The procedure called for 308 welds which were made with the gas shielded

flux cored process. A stress relief of 1475F for 10 hours was required. We know the welds were sound before the heat treatment, however immediately after the post heat treat we found cracks in the flux cored welds.

This stainless expert (Kotececki March 2008 Weld Journal) provides a good summary of this unique cracking problem. It seems that with gas shielded flux cored wires you will find a small amount of bismuth-bearing compounds. These compounds assist in weld slag removal. Bismuth and similar elements at specific levels can causes cracks if the parts are put into service and the temps are above 900F and possibly

lower temperatures at long time periods. The bottom line, if your stainless vessel is going to have post heat treatment or be placed in service with high temperatures ensure your flux cored wire contains < 20ppm bismuth. Ask the electrode manufacturer does their wires contain any elements that can cause reheat cracks or premature creep failure.

MIG OR TIG WELDING THAT STAINLESS ROOT... To ensure good corrosion resistance of the stainless weld root, the root must be protected from the atmosphere by an inert gas shield during welding and subsequent cooling. The gas shield should be contained around the root of the weld by a suitable dam, which must permit a continuous gas flow through the area.

Welding should not commence until sufficient time has elapsed to allow the volume of purging gas flowing through the dam to equal at least the 6 times the volume contained in the dam.

Once purging is complete, the purge flow rate should be reduced so that it only exerts a small positive pressure, sufficient to exclude air. If good corrosion resistance of the root is required, the oxygen level in the dam

should not exceed 0.1% (1000 ppm); for extreme corrosion resistance this should be reduced to 0.015% (150 ppm). Backing gasses used for purging are typically argon or helium; nitrogen is often used as an economic alternative where corrosion resistance is not critical, nitrogen + 10% helium is a good mix.

A wide variety of proprietary pastes and backing materials are available than can be use to protect the stainless root instead of a gas shield. In some applications where corrosion and oxide coking of the weld root is not important, such as large stainless steel ducting, no gas backing is used. To eliminate filling stainless tanks with a purge gas go to TIP TIG at this site.

General Stainless (P-8) 300 Series Pipe Weld Procedure Data.Max interpass Temp 350F

ProcessFiller Diameter

Metal Polarity AmpsWire Feed

Volts

GTAW3/32 Tungst

1/16 - 1.6mm

300 seriesStainless

DC Straight

95-145 N/A 14

SMAWEXXX-15-16

1/83.2mm

300 seriesStainless

DCReverse

95-145 N/A 20-24

SMAWEXXX-15-16

5/324mm

300 seriesStainless

DCReverse

125-175 N/A 21-25

FCAWEXXX-T1 argon with 25 CO2

045300 seriesStainless

DCReverse

130-180(140)

230/280 22-25

Who said you can't take it with you?

Typical forms of corrosion

Corrosion Potential. From Sanvik..

This data is from Sanvik: Materials used in oil and gas extraction are affected to several different types of corrosion, often caused by seawater and spray. The types of corrosion, which can occur on stainless steels in marine environment, are pitting and crevice corrosion, and for standard austenitic grades also stress corrosion cracking (SCC), if the material temperature is above 60°C (140°F). These are all localised attacks – general corrosion need not be considered for stainless steels in seawater. High temperatures, high chloride contents and low pH values increase the risk of localised attacks in any chloride-

http://www.weldreality.com/STEELS%20NICKEL%20ALLOYS.htm


containing environment. Of these, temperature is usually the most influential factor.

However, there is a fourth important consideration: the electro-chemical corrosion potential of the environment. In seawater, this potential is affected by biological activities on the steel surface. Since seawater is, in a sense, a living corrosive environment, it is sometimes difficult to define exactly what the service conditions will be. At normal seawater temperatures, a biofilm will form on the steel surface and result in a corrosion potential of +300 to +500 mV/SCE.

At temperatures above ~40°C (100°F) the biological activity will cease and the corrosion potential will drop. The use of continuous chlorination, to stop marine growth, may increase the corrosion potential to values as high as +600 to +800 mV/SCE. This, however, can be avoided through the use of intermittent rather than continuous chlorination.

Benefits over Cu and CuNi-based alloysStainless steels are very resistant to erosion corrosion compared with Cu and CuNi-based alloys, which are very sensitive to this form of attack. Water in harbours, around offshore platforms, and near chemical plant sites is often contaminated e.g. with ammonia (NH 3 ) and sulphides (S 2- ). These compounds, even in very small quantities, cause localised attacks on copper-base alloys, while stainless steels are not affected at the impurity levels involved.

Sour corrosion: Wet and sour service: The corrosivity of an oil

and gas well is increased by the presence of chlorides in water solutions, carbon dioxide, and hydrogen sulphide.

The environment is considered sweet as long as no hydrogen sulphide is present. Carbon dioxide alone can however cause high corrosion rates on carbon steel, since it is acidifying the solution. This is further accelerated if chlorides are present.

Sour environments are defined when the partial pressure of hydrogen sulphide is above 0.05 psi. At higher partial pressures, the corrosion rate on carbon steel is substantially increased by means of making the water phase more acidic and by forming iron sulphide scale. Sulphide Stress Cracking (SSC) is common in high strength steels containing martensite. It can also occur in ferritic steels.

Stainless steels are different. Sandvik Sanicro 28, Sanicro 29, SAF 2205 and SAF 2507 grades are completely resistant to corrosion in wells rich in carbon dioxide with a high amount of chlorides in the water phase. If hydrogen sulphide is present, there is still no general corrosion, but the risk of localised corrosion increases, especially with regard to SSC.

The NACE TM-0177 test. Experiments have been carried out at room temperature in accordance with the NACE TM-0177 test (5% sodium chloride, 0.5% acetic acid, saturated with hydrogen sulphide).

The threshold stress for cold-worked Sandvik SAF 2205/22Cr is about 90% of the yield strength, which is very good when compared to results for high strength, ferritic stainless steels.

Sandvik Sanicro 28, in the cold-worked condition, results in no failures up to very high stress levels. The high alloy duplex stainless steel Sandvik SAF 2507 is also resistant to cracking in the solution-annealed condition.

In general terms, this test shows that Sandvik Sanicro 28 has a higher resistance to sulphide stress cracking compared to SAF 2205/22Cr, which is much more resistant than 13Cr. Sandvik Sanicro 29 has an ever higher resistance to localised corrosion and sulphide stress cracking than Sandvik Sanicro 28.

It should be remembered that the chemistry of the “NACE solution” is not representative of the conditions in most sour oil and gas wells. This is especially true for acidity, where the pH value is lower in the NACE test. Results from the NACE TM-0177 test, therefore, should not be used for determining the suitability of different grades, but more as a ranking test. Other tests, more representative of actual service conditions, must be used to determine the suitability of different grades. Practical experience of specific grades is, of course, extremely useful.

Visit Sanvik's web site for more excellent data on stainless and duplex products, however if you want the best stainless steel MIG welding process control data visit here,

The world's best process for welding any all position, thin or thick stainless / duplex

application is TIP TIG.

Welding Stainless Steels Safety Issues

Stainless Steel Welding Consumables

MIG Welding Stainless Steel Under 4mm

MIG Welding Stainless Steel Over 4mm Welding Nickel Alloys


http://www.weldreality.com/short_circuit_under100.htm

http://www.weldreality.com/spray_transfer_above100.htm



http://www.weldreality.com/steels_weld_consumables.htm





http://www.weldreality.com/eds_training_materials.htm

http://www.weldreality.com/eds_training_materials.htm