Jfe Steel Octg

Legal NoticeThis catalog is edited for general information only. Although every possible effort is made to maintain the accuracy and reliability of the contents of this publication, JFE Steel Corporation in no ways assumes liability or for any loss, damage or injury resulting from the use of the information and data herein. It is requested to be undertaken solely at the customer's own risk and responsibility.

1.2.3.4.5.6.7.8.9.

10.11.

Preface FeaturesFacilities and LocationOCTG Line UpManufacturing ProcessAvailable Grades and SizesSpecification of JFE-Series-JFE Special OCTGPremium Threaded ConnectionsMarkingColor Identification of JFE OCTG (JFE-Series)Thread Protectors and PackagingInquiries and Orders

12456

10183133343536

Contents

Preface

Steel Corporation has been manufacturing Oil Country

Tubular Goods (OCTG) since 1971, during that time we have accumu-

lated extensive expertise and experience giving their customers great

confidence and satisfaction when purchasing JFE Steel OCTG.

In the past the well conditions in Oil and Gas drilling were relatively mild

and development was straight-forward. Today's Oil and Gas Industry has

become a much more complicated operation as Engineers continue to drill

deeper wells in harsher environments, encountering higher well bore

pressures and temperatures in addition to sweet and sour gas.

To meet these ever increasing industry demands, JFE has developed

its JFE series OCTG which has higher collapse resistance, yield strength,

toughness and corrosion resistance, than standard API OCTG material.

Especially, JFE's 13Cr OCTG has established an excellent reputation

world-widely in terms of quality and manufacturing capability.

In the early 1980s, JFE developed the FOXTM premium connection

which has now gained industry acceptance world wide. And the late 1990s,

JFE has also developed a new premium connection called JFEBEARTM

designed to meet todays toughest well condition. With these two

connections, JFE can offer customers a choice of products to suit their

various applications.

This OCTG brochure provides you with our ardent desire to assist you

in choosing the correct Oil Country Tubular Goods for your operation.

1

21. Features

Historical Advantage in Steel Making

Pipe Manufacturing

Quality System

Basic Oxygen Furnace

Mandrel Mill

High Frequency E. R. W. Machine

9-5/8" CNC Torque Process Control System

JFE Steel has been involved in the steel making business nearly one(1) hundred years and contributing to the industry with its technology. The Top and Bottom Gas Blowing system followed by Continuous Casting is a typical case, which was first introduced to the industry by JFE Steel.

JFE Steel revealed their technical advancement in the pipe manufacturing process. Recently, the process to roll 13Cr steel by the Mannessman piercing mill was realized first in JFE Steel.

All JFE OCTG's are inspected nondestructively for detection of internal and external imperfections by use of Eddy Current, Electromagnetic, Ultrasonic and/or Magnetic Particle method. These requirements play an important role in our rigid quality control and assurance system.

3Research and Development

Worldwide Service Network

Collapse Test

Electromagnetic Inspection

Magnetic Particle Inspection

JFE Steel boasts a wide range of testing facilities and equipment to evaluate new and existing products. The benefits generated as a result of this R & D work contribute to our customers and the industry as well as to our daily production activities.

JFE has established foreign offices and service centers throughout the world as listed on the back cover sheet.

4 JFE Steel ensures consistently high quality for all

its tubular products by way of production control at

every stage from blast furnace to pipe mill, using

inspection systems with advanced ultrasonic,

electromagnetic and other non-destructive inspection

equipment. Pipe production at JFE Steel is part of a

fully integrated steelmaking facility. This means JFE

tubular products are manufactured from beginning to

end under single-maker responsibility for quality and

performance.

OCTG is produced at Chita Works, which

specializes in pipe and tubes under the company's

well-known rigid quality control and assurance

systems.

Equipped with complete mass production systems for

all kinds of pipe and tubular products, Chita is one of

the foremost tubular products centers in the world.

The location of Chita has the advantage of easy

access to West Japan Works and East Japan Works

which supplies Chita Works with steel materials for

the production of their tubular products.

Chita Works

East Japan Works

West Japan Works

Tokyo Head Ofce

2. Facilities and Location

Nagoya

Tokaido Shinkansen

Ohbu

HandaCentral JapanInternationalAirport

Morozaki

Cape Irago

Toyohashi

Ise Bay

Mikawa BayKinu-ura Bay

Tomei Expressway

Chita Works

Tokaido Main Line

Chita Works located in the center of the Kinu-ura coastal industrial zone

Taketoyo

Type of String

Tubing 2-3/8" - 7"

16"

16" - 26"

4-1/2" - 7"

7" - 16"

Small-Diameter Seamless

Small-Diameter Seamless

Medium-Diameter Seamless

Medium-Diameter Seamless

ERW

20" and Over UOE

Casing

Conductor Casing

Size Mill Works

Chita Works

Chita Works

Chita Works

Thread and Coupling

End Upset Capability

Thread and Coupling

Plain End without

welded-on Connector

Plain EndChita Works

East Japan Works

West Japan Works

Note

1) Line up

2) Connections

3. OCTG Line up

5

a. API Connections Casing and tubing of API Specification and JFE-Series are furnished with threads and coupling conforming to API Spec. 5CT and 5B. API Round and Buttress thread with resilient sealing ring is also available. Plain End, API thread without coupling, and special end finish (special bevel, special clearance) are available according to customers' requirement.

b. Premium Connections b-1. FOXTM

FOXTM is a thread and coupling type premium connection jointly developed by JFE Steel Corporation and Hunting Energy Services U.K. LTD. Please see page 31 for further information. b-2. JFEBEARTM

JFEBEARTM is a thread and coupling type premium connection developed by JFE Steel Corporation. Please see page 32 for further information.

ERW7-5/8" - 26"

64. Manufacturing Process

Seamless Mill Electric Resistance Weld (ERW) MillSeamless pipes and tubes are produced either bythe mandrel mill or the plug rolling mill process. The former process is used for producing small-diameter pipes up to 7" and the latter for medium-diameter pipes over 7". On either type of mill, each heated billet is pierced through its center on a piercing mill. The pierced billet then moves on to a mandrel or plug rolling mill where it is rolled with a mandrel bar or pluginserted in it. After withdrawal of the mandrel or the plug, the rolled shell is reheated before being pro- cessed on stretch reducing mill or sizing mill where the desired OD and wall thickness are obtained. To ensure consistently high quality, the company con-ducts thorough testing and inspection, using advanced equipment including eddy current, ultrasonic, electromagnetic and magna flux devices.

East Japan Works

West Japan Works

Blast furnace

Converter

Smelting reduction furnaceContinuous casting

Continuous castingSlab

Bloom

High alloy slab

Billet mill

Hot strip mill

Stainless mill

Billet

Stainlesssteel coil

Hot coil

Hot coil

Plate

Electric Resistance Weld pipes are made from stripin coil form. 12-3/4" and above Mill in Chita Works and 8" and above Mill in East Japan Works produce ERW OCTG pipes.These mills are equipped with high frequency electric resistance welder to provide improved seam quality. And seam heat treatment system after welding helps to get better metallurgical structure.

Hot process Cold processChita Works

Small diameterseamless pipe

Seamless squarecolumn

Medium diameterseamless pipe

Special Tube

Small diameterERW pipe

Medium diameterERW pipe

Square column

HISTORYTM pipe

Galvanizedpipe mill

SpecialTube mill

Galvanized pipe

4mill

(East Japan Works)

(East Japan Works)

(West Japan Works)

[Seamless pipes]

[Welded pipes]

Small diameterseamless pipe mill

Small diameterERW pipe mill

Medium diameterERW pipe mill

UOE pipe mill

Butt welded pipe mill

Spiral tube mill

Medium diameterseamless pipe mill

36mill

7

8Round Billet

Straightening

Straightening

Upsetting

Piercing

Elongator Plug Mill

Reeling

Sizing

Rotary Heating Furnace

Reheating Furnace

NDE(UST,MPI,EMI)

Visual & DimensionalInspection

Inspection, Stenciling,Coating

Drift Testing

Hydrostatic TestingCoupling Making upThreading

Drill Pipe

Plain End Unprocessed Pipes

Casing Tubing

Sizing

Stretch Reducing

Quenching

CasingFabrication

TubingFabrication

Heat Treatment

7" Mill (Mandrel Mill)

163/4" Mill (Plug Mill)

C

D

E

F

G

H

C

D

E

F

G

H

A

B

A

B

SEAMLESS MILL

Drill Pipe

Casing

Tubing

Mandrel Mill

8Round Billet

Straightening

Straightening

Upsetting

Piercing

Elongator Plug Mill

Reeling

Sizing

Rotary Heating Furnace

Reheating Furnace

NDE(UST,MPI,EMI)


Inspection, Stenciling,Coating

Drift Testing

Hydrostatic TestingCoupling Making upThreading

Drill Pipe

Plain End Unprocessed Pipes

Casing Tubing

Sizing

Stretch Reducing

Quenching

CasingFabrication

TubingFabrication

Heat Treatment

7" Mill (Mandrel Mill)

163/4" Mill (Plug Mill)

C

D

E

F

G

H

C

D

E

F

G

H

A

B

A

B

SEAMLESS MILL

Drill Pipe

Casing

Tubing

Mandrel Mill

9

Electric Resistance Weld (ERW) Mill

24-in. ERW Mill

26-in. ERW Mill

Hydrostatic Testing

No.1 SeamUltrasonic Inspection

(Mill Control)Post Annealing

CoolingSizing Cutting

1 2

Marking(& Coating) Shipping3

3

21

2 3


Weighting&

Measuring

Facing & Chamfering

3

No.2 SeamUltrasonic Inspection

Full Body UltrasonicInspection(Option)

Hydrostatic Testing

Seam Ultrasonic Inspection(Mill Control)

Post AnnealingCooling

Sizing Cutting

Marking(& Coating) Shipping


Weighting&

Measuring

Facing & ChamferingSeam Ultrasonic Inspection

Full Body UltrasonicInspection(Option)

2

Hot Rolled Coil

Edge MillingRoll FormingPre Forming

Welding(Inside & Outside Flash Triming)

1

Hot Rolled Coil

Edge Milling Cage Forming

Welding(Inside & Outside Flash Triming)

1

HighCollapseStrength

JFE-80T

JFE-95T

JFE-110T

Yield Strength

Minimum

psi (MPa)

90,000 ( 621)

85,000 ( 586)

40,000 ( 276)

80,000 ( 552)

55,000 ( 379)

140,000 ( 965)

95,000 ( 655)

125,000 ( 862)

110,000 ( 758)

65,000 ( 448)

Deep Well

Service

Group

2

Group

3

Group

1

Group

4

Group

2

API 5CT

Group

1

ERWSeamless

P110C110

H40

J55

K55

N80/Type1

C90/Type1

T95/Type1R95 R95

Q125/Type1

M65

JFE-125V

JFE-140V

H40

J55

K55

N80/Type1

N80/TypeQ

L80/Type1

L80/13Cr

L80/Type1

10

5. Available Grades and Sizes1) Available Grades

11

General GeneralSpecialHigh

Collapse

High

Temperature

High Strength

High Temperature

Arctic

Service

General

Service

HighCollapseStrength

JFE Special OCTG : JFE-Series

Seamless

Sour Service Wet CO2 Service

ERW

JFE-110S JFE-110SS

JFE-40E

JFE-55E

JFE-80S JFE-80TS JFE-80L JFE-13CR-80 JFE-80E JFE-80ET

JFE-90S

JFE-85S

JFE-90SS

JFE-85SS JFE-13CR-85

JFE-110L

JFE-HP1-13CR-95

JFE-HP2-13CR-95

JFE-HP1-13CR-110

JFE-HP2-13CR-110

JFE-125L JFE-UHPTM-15CR-125

JFE-95TS JFE-95L JFE-13CR-95JFE-95SSJFE-95S

5. Available Grades and Sizes

12

2) Physical Properties of API and JFE-Series

Series Application

Group 1

Group 2

High CollapseStrength

Sour Service

SpecialSour Service

Sour Service &High Collapse

Group 4Group 3

Grade Type

Yield Strength Tensile Strength

Minimum

psi (MPa)

API

H40J55K55N80

R95M65L80

C90T95C110P110Q125JFE-80TJFE-95TJFE-110TJFE-80SJFE-85SJFE-90SJFE-95SJFE-110SJFE-85SSJFE-90SSJFE-95SSJFE-110SSJFE-80TSJFE-95TSJFE-80LJFE-95LJFE-110LJFE-125LJFE-125VJFE-140VJFE-13CR-80JFE-13CR-85JFE-13CR-95JFE-HP1-13CR-95JFE-HP1-13CR-110JFE-HP2-13CR-95JFE-HP2-13CR-110

JFE-UHPTM-15CR-125

JFE-40EJFE-55EJFE-80EJFE-80ET

40,000 ( 276)

55,000 ( 379)

55,000 ( 379)

80,000 ( 552)

80,000 ( 552)

95,000 ( 655)

65,000 ( 448)

80,000 ( 552)

80,000 ( 552)

90,000 ( 621)

95,000 ( 655)

110,000 ( 758)

110,000 ( 758)

125,000 ( 862)

80,000 ( 552)

95,000 ( 655)

110,000 ( 758)

80,000 ( 552)

85,000 ( 586)

90,000 ( 621)

95,000 ( 655)

110,000 ( 758)

85,000 ( 586)

90,000 ( 621)

95,000 ( 655)

110,000 ( 758)

80,000 ( 552)

95,000 ( 655)

80,000 ( 552)

95,000 ( 655)

110,000 ( 758)

125,000 ( 862)

125,000 ( 862)

140,000 ( 965)

80,000 ( 552)

85,000 ( 586)

95,000 ( 655)

95,000 ( 655)

110,000 ( 758)

95,000 ( 655)

110,000 ( 758)

125,000 ( 862)

40,000 ( 276)

55,000 ( 379)

80,000 ( 552)

80,000 ( 552)

1

Q

113Cr

11

1

JFE-Series

Wet CO2 Service

General Service

High Collapse Strength

High StrengthHigh TemperatureWet CO2 Service

Note:Elongation Requirement is according to API 5CT Specication.

Maximum

psi (MPa)Minimum

psi (MPa)

80,000 ( 552)

80,000 ( 552)

80,000 ( 552)

110,000 ( 758)

110,000 ( 758)

110,000 ( 758)

85,000 ( 586)

95,000 ( 655)

95,000 ( 655)

105,000 ( 724)

110,000 ( 758)

120,000 ( 828)

140,000 ( 965)

150,000 (1,034)

110,000 ( 758)

125,000 ( 862)

140,000 ( 965)

95,000 ( 655)

100,000 ( 689)

105,000 ( 724)

110,000 ( 758)

125,000 ( 862)

100,000 ( 689)

105,000 ( 724)

110,000 ( 758)

125,000 ( 862)

95,000 ( 655)

110,000 ( 758)

95,000 ( 655)

125,000 ( 862)

140,000 ( 965)

150,000 (1,034)

150,000 (1,034)

170,000 (1,172)

95,000 ( 655)

100,000 ( 689)

110,000 ( 758)

110,000 ( 758)

130,000 ( 896)

110,000 ( 758)

130,000 ( 896)

150,000 ( 1034) 80,000 ( 552)

80,000 ( 552)

110,000 ( 758)

110,000 ( 758)

60,000 ( 414)

75,000 ( 517)

95,000 ( 655)

100,000 ( 689)

100,000 ( 689)

105,000 ( 724)

85,000 ( 586)

95,000 ( 655)

95,000 ( 655)

100,000 ( 689)

105,000 ( 724)

115,000 ( 793)

125,000 ( 862)

135,000 ( 931)

100,000 ( 689)

110,000 ( 758)

125,000 ( 862)

95,000 ( 655)

95,000 ( 655)

100,000 ( 689)

105,000 ( 724)

120,000 ( 828)

95,000 ( 655)

100,000 ( 689)

105,000 ( 724)

120,000 ( 828)

100,000 ( 689)

105,000 ( 724)

95,000 ( 655)

110,000 ( 758)

125,000 ( 862)

135,000 ( 931)

135,000 ( 931)

150,000 (1,034)

95,000 ( 655)

100,000 ( 689)

105,000 ( 724)

105,000 ( 724)

120,000 ( 828)

105,000 ( 724)

120,000 ( 828)

135,000 ( 931) 60,000 ( 414)

75,000 ( 517)

100,000 ( 689)

100,000 ( 689)

Arctic Service

High TemperatureWet CO2 Service

Deep Well Service

13

Charpy V-notch Test

ft-lbs (J)

Manufacturing

Process

Seamless ERW

Hardness(HRC)

Collapse

Value F ( C)MinimumAverage

Minimumsingle

Other Specied

ItemsMaximum Variation

222323

25.425.430

2223242531232425312225

23242728323032

37

3.0-6.0 3.0-6.0 3.0-6.0

3.0-5.0

3.0-5.0 3.0-5.0 3.0-5.0 3.0-5.0

3.0-5.0 3.0-5.0 3.0-5.0

GuaranteedGuaranteedGuaranteed

Guaranteed

-50 (-46)-50 (-46)-50 (-46)-50 (-46)-4 (-20)-4 (-20)

25 (34)

25 (34)

25 (34)

25 (34)

20 (27)

20 (27)

19 (26)

19 (26)

19 (26)

19 (26)

15 (20)

15 (20)

Grain Size & SSC TestGrain Size & SSC TestGrain Size & SSC Test

Grain Size & SSC TestGrain Size & SSC TestGrain Size & SSC TestGrain Size & SSC Test

Depends on specied wall thickness.

14

lb/ft

Outside DiameterPlainEnd

Threads &Coupling

Nominal weight

NUE

lb/ft lb/ft

WallThickness

InsideDiameter

(mm)(mm) inchinch inch

Drift

EUE

inch

2-3/8

2-7/8

3-1/2

4

4-1/2

4.004.605.806.607.356.407.808.609.35

10.5011.507.709.20

10.2012.7014.3015.5017.009.50

10.7013.2016.1018.9022.2012.6015.2017.0018.9021.5023.7026.10

(60.32)

(73.02)

(88.90)

(101.60)

(114.30)

4.705.95

7.456.507.908.709.45

9.30

12.95

11.00

12.75

3.944.445.766.567.326.177.678.459.21

10.4011.457.588.819.92

12.5314.1115.3916.839.12

10.4712.9515.9018.7122.1112.2515.0016.7718.7121.3823.5926.06

0.1670.1900.2540.2950.3360.2170.2760.3080.3400.3920.4400.2160.2540.2890.3750.4300.4760.5300.2260.2620.3300.4150.5000.6100.2710.3370.3800.4300.5000.5600.630

2.0411.9951.8671.7851.7032.4412.3232.2592.1952.0911.9953.0682.9922.9222.7502.6402.5482.4403.5483.4763.3403.1703.0002.7803.9583.8263.7403.6403.5003.3803.240

1.9471.9011.7731.6911.6092.3472.2292.1652.1011.9971.9012.9432.8672.7972.6252.5152.4232.3153.4233.3513.2153.0452.8752.6553.8333.7013.6153.5153.3753.2553.115

( 4.24)( 4.83)( 6.45)( 7.49)( 8.53)( 5.51)( 7.01)( 7.82)( 8.64)( 9.96)(11.18)( 5.49)( 6.45)( 7.34)( 9.52)(10.92)(12.09)(13.46)( 5.74)( 6.65)( 8.38)(10.54)(12.70)(15.49)( 6.88)( 8.56)( 9.65)(10.92)(12.70)(14.22)(16.00)

5. Available Grades and Sizes3) API and JFE-Series Tubing List

9.5010.5011.6013.5015.1011.5013.0015.0018.0021.4023.2024.1014.0015.5017.0020.0023.0026.8029.7032.6035.3038.0040.5043.1020.0024.0028.0032.0017.0020.0023.0026.0029.0032.00

(114.30)

(127.00)

(139.70)

(168.28)

(177.80)

4-1/2

5

5-1/2

6-5/8

7

9.4110.2411.3613.0515.0011.2412.8414.8817.9521.3223.1124.0513.7115.3616.8919.8322.5626.7229.6732.5735.3538.0840.6943.2619.5123.6027.6731.2316.7219.5622.6525.6928.7531.70

0.2050.2240.2500.2900.3370.2200.2530.2960.3620.4370.4780.5000.2440.2750.3040.3610.4150.5000.5620.6250.6870.7500.8120.8750.2880.3520.4170.4750.2310.2720.3170.3620.4080.453

4.0904.0524.0003.9203.8264.5604.4944.4084.2764.1264.0444.0005.0124.9504.8924.7784.6704.5004.3764.2504.1264.0003.8763.7506.0495.9215.7915.6756.5386.4566.3666.2766.1846.094

3.9653.9273.8753.7953.7014.4354.3694.2834.1514.0013.9193.8754.8874.8254.7674.6534.5454.3754.2514.1254.0013.8753.7513.6255.9245.7965.6665.5506.4136.3316.2416.1516.0595.969

6.250

6.000

( 5.21)( 5.69)( 6.35)( 7.37)( 8.56)( 5.59)( 6.43)( 7.52)( 9.19)(11.10)(12.14)(12.70)( 6.20)( 6.98)( 7.72)( 9.17)(10.54)(12.70)(14.27)(15.88)(17.45)(19.05)(20.62)(22.22)( 7.32)( 8.94)(10.59)(12.06)( 5.87)( 6.91)( 8.05)( 9.19)(10.36)(11.51)

5. Available Grades and Sizes4) API and JFE-Series Casing List

lb/ft lb/ft

Outside Diameter

Nominal weight

(mm)inch

PlainEnd

WallThickness

InsideDiameter

(mm)inch inch inch inch

Drift SpecialDriftThreads &

Coupling

15

16

35.0038.0042.7046.4050.1053.6057.1024.0026.4029.7033.7039.0042.8045.3047.1051.2055.3046.1024.0028.0032.0036.0040.0044.0049.0032.3036.0040.0043.5047.0053.5058.40

34.6137.2942.5946.3650.1153.7157.2923.4925.5929.0633.0738.0842.4344.7146.7750.9555.1245.5123.6027.0431.1335.1739.3343.4348.0431.0634.8938.9742.7346.1852.9057.44

(177.80)

(193.68)

(196.85)

(219.08)

(244.48)

7

7-5/8

7-3/4

8-5/8

9-5/8

0.4980.5400.6250.6870.7500.8120.8750.3000.3280.3750.4300.5000.5620.5950.6250.6870.7500.5950.2640.3040.3520.4000.4500.5000.5570.3120.3520.3950.4350.4720.5450.595

6.0045.9205.7505.6265.5005.3765.2507.0256.9696.8756.7656.6256.5016.4356.3756.2516.1256.5608.0978.0177.9217.8257.7257.6257.5119.0018.9218.8358.7558.6818.5358.435

5.8795.7955.6255.5015.3755.2515.1256.9006.8446.7506.6406.5006.3766.3106.2506.1266.0006.4357.9727.8927.7967.7007.6007.5007.3868.8458.7658.6798.5998.5258.3798.279

6.500

7.875

7.625

8.750

8.5008.375

(12.65)(13.72)(15.88)(17.45)(19.05)(20.62)(22.22)( 7.62)( 8.33)( 9.52)(10.92)(12.70)(14.27)(15.11)(15.88)(17.45)(19.05)(15.11)( 6.71)( 7.72)( 8.94)(10.16)(11.43)(12.70)(14.15)( 7.92)( 8.94)(10.03)(11.05)(11.99)(13.84)(15.11)


lb/ft lb/ft

Outside Diameter

Nominal weight

(mm)inch

PlainEnd

WallThickness

InsideDiameter


Drift SpecialDriftThreads &

Coupling

lb/ft lb/ft

Nominal weight

PlainEnd

WallThickness

InsideDiameter


Drift SpecialDrift

59.4064.9070.3075.6032.7540.5045.5051.0055.5060.7065.7073.2079.2085.3042.0047.0054.0060.0065.0071.0048.0054.5061.0068.0072.0065.0075.0084.00

109.0087.5094.00

106.50133.00

58.7064.3269.7675.2131.2338.9144.2649.5554.2659.4564.5972.4078.5984.8040.6445.6052.6258.8764.0369.4846.0252.7959.5066.1770.6762.6472.8682.05

107.6084.5991.59

104.23131.45

0.6090.6720.7340.7970.2790.3500.4000.4500.4950.5450.5950.6720.7340.7970.3330.3750.4350.4890.5340.5820.3300.3800.4300.4800.5140.3750.4380.4950.6560.4350.4380.5000.635

8.4078.2818.1578.031

10.19210.050

9.9509.8509.7609.6609.5609.4069.2829.156

11.08411.00010.88010.77210.68210.58612.71512.61512.51512.41512.34715.25015.12415.01014.68817.75519.12419.00018.730

8.2518.1258.0017.875

10.0369.8949.7949.6949.6049.5049.4049.2509.1269.000

10.92810.84410.72410.61610.52610.43012.55912.45912.35912.25912.19115.06214.93614.82214.50017.56718.93618.81218.542

9.875

9.625

11.000

10.62510.625

12.250

(15.47)(17.07)(18.64)(20.24)( 7.09)( 8.89)(10.16)(11.43)(12.57)(13.84)(15.11)(17.07)(18.64)(20.24)( 8.46)( 9.52)(11.05)(12.42)(13.56)(14.78)( 8.38)( 9.65)(10.92)(12.19)(13.06)( 9.53)(11.13)(12.57)(16.66)(11.05)(11.13)(12.70)(16.13)

(244.48)

(273.05)

(298.45)

(339.72)

(406.40)

(473.08)

(508.00)

9-5/8

10-3/4

11-3/4

13-3/8

16

18-5/8

20


Threads &Coupling

17

Outside Diameter

(mm)inch

18

6. Specification of JFE-Series

JFE-95T-110T

1) High Collapse Casing

JFE Special OCTG

(c) Physical Properties

b. Actual Collapse Data of JFE-95T

a. Specifications

(a) Process of Manufacture and Heat Treatment Seamless, quenched and tempered

(b) Chemical Requirements

With a recent increase in deep well drilling, there is a growing need for high collapse casing in a minimum yield strength of 95 ksi (655 MPa) grade. Collapse resistance is affected by yield strength, deviation of wall thick-ness, roundness, residual stress and D/t (D for outside diameter and t for wall thickness).Reducing the deviation of wall thickness at hot rolling, control-ling yield strength by closely reg- ulating heat treatment conditions,and minimizing the deterioration of roundness and straightness during cooling are performed. This process is governed by our special techniques and knowhow. By using the same material as that for JFE-95T, JFE Steel manufactures JFE-110T which has higher collapse resistance properties than JFE-95T.

Grade

JFE-95TJFE-110T

Tensile Requirement

Grade

95~125(655~862)

110~140(758~965)

CollapseResistance

See PerformanceProperties Table

As PerAPI 5CT

YieldStrengthksi (MPa)

TensileStrength

min. ksi (MPa)Elongation

(wt %)

0.35 0.35 1.60 0.030 0.030

Si, max. Mn, max. P, max. S, max.C, max.

Collapse test results of JFE-95TD/t

20 2515

5

10

15

500

1000

JFE-95T

Min. value specied in API 5CT C-95

(kgf

/cm

2 )

Col

laps

e st

reng

th p

(ksi

)

JFE-95T

JFE-110T

110 (758)

125 (862)

19

JFE-125V-140V

2) Deep Well Service

Drilling of deep wells in excess of 15,000 feet and high-pressure gas wells is on the increase. P-110's burst pressure, collapse resistance and tension are not always sufficient for these applications. Therefore, JFE-125V casing and tubing and JFE-140V casing have been developed. Cr-Mo-Cb steel with excellent hardenability and high temperature resistance are used to make OCTG which have superb strength, toughness, and restricted varia-tion of HRC.

a. Specifications



(d) Hardness Test on Casing and Coupling Stock Variation of HRC among three locations (O.D., Mid wall, I.D.) of one quadrant of a ring shall be as below.


Tensile Requirements 2mm V Charpy Impact Requirements (casing only)

JFE-125V

JFE-140V

135 ( 931)

150 (1034)

10 10

10 7.5

20 (27)

16 (22)

15 (20)

12 (16)

As Per

API 5CT-4 F (-20 C)

Grade

Grade C Simax.

Mnmax.

Pmax.

Smax.

Cumax.

Nimax.

Cbmax.

Cr Mo

125~150(862~1034)

TestTemperature


JFE-125VJFE-140V

0.15~0.35 0.35 1.00 0.030 0.015 0.30 0.10 0.80~1.60 0.15~1.10 0.050

TensileStrength

min. ksi (MPa)

Minimum Average Absorbed Energy

ft-lb (J)

Minimum Individual Absorbed Energy

ft-lb (J)SpecimenElongation

140~170(965~1171)

(wt %)

0.500 or less

0.501 to 0.749

0.750 and above

Wall thickness (inch)

3.0

4.0

5.0

JFE-125V, JFE-140V

Maximum Variation

20

JFE-80S-85S, 85SS-90S, 90SS-95S, 95SS-110S, 110SS

3) Sour and Special Sour Service


Sour servicesJFE-80S, -85S, -90S, -95S and -110S for continuous operating temperature above 149 F (65 C)

Special sour servicesOCTG for sour wells must above all have improved resistance to sulfide stress cracking (SSC) in fluids containing H2S. Intensive research has led to a modified Cr-Mo-Cb steel for OCTG for sour wells. This steel features both excellent hardenability and good temper resistance. Consequently, fine and homogeneous tempered martensite with lower HRC25 for 95 ksi grade is obtained after tempering at higher tempering temperature. As a result, OCTG of these grades possess excellent resistance to SSC for its strength grades.These OCTG are subjected to more stringent quality control. SSC-resistant steel of these grades thoroughly tested by major oil compa-nies enjoys high ratings and is now widely used for sour gas and oil wells all over the world.


(wt %)

Grade

1.35

max. 0.50 max. 1.10max. 1.600.20

0.10

1.00

0.15~0.350.35 0.010 0.30 0.050 0.00400.020

max. 1.60

0.80~1.60

0.05~1.10

0.15~1.10

Cbmax.

Simax.

Mnmax.

Pmax.

Smax.

Cumax.

Nimax.

Bmax.

CrC Mo

Tensile Requirement Hardness Requirements

JFE-80SJFE-85SJFE-90SJFE-95SJFE-110SJFE-85SSJFE-90SSJFE-95SSJFE-110SS

80~ 95 (552~655)85~100 (586~689)90~105 (621~724)95~110 (655~758)

110~125 (758~862)85~100 (586~689)90~105 (621~724)95~110 (655~758)

110~125 (758~862)

95 (655)95 (655)

100 (689)105 (724)120 (827)95 (655)

100 (689)105 (724)120 (827)

222324253123242531

Yield Strengthksi (MPa)

Hardness (HRC) Maximum

As PerAPI 5CT

Elongation As-Quenched

Mimimumequivalent to90% martensiticStructure

Minimum Tensile Strengthksi (MPa)

Item

Grade

JFE-110S, -110SS

JFE-85SS, -90SSJFE-95SS,

JFE-80S, -85SJFE-90S, -95S

a. Specification



21

Note: (Time to failure Hr)NF = No failure during 30 days (720 hours)

= No test c = Maximum applied stress resulted in no failure y = Specied Minimum Yield Strength

HRC test results show relatively low and stable values indispensable for increasing sulfide stress cracking (SSC) resistance for its yield strength. SSC test results show excellent SSC-resistant properties.

(a) Hardness Test Result of Products

b. Examples of Physical Tests on JFE-90SS Casing

(b) SSC Test Results (NACE Standard TM0177)

Rockwell C Hardness Values

Quadrant No.

1 2 3 4

Pipe DimensionsO.D. W.T. Maximum

Variation

O.D.I.D.

O.D.Mid Wall

I.D.O.D.

Mid WallI.D.

19.819.719.419.419.118.6

20.019.418.818.919.418.0

20.420.019.619.319.218.5

20.520.119.818.619.118.7

20.920.8

20.120.1

20.620.6

20.920.8 0.15

1/2'' 0.415''

5 1/2'' 0.725''

7'' 1.200''

1.2

1.4

Location

0.415''

0.725''

1.200''

Mid Wall

Mid Wall

Mid Wall

Inside

NF

NF

31.0

3.2

NF

NF

NF

NF

NF

NF

NF

NF

546.8

301.4

284.0

499.0

0.95

0.95

0.95

0.95

85.5

85.5

85.5

85.5

Threshold StressApplied Stress, ksi (MPa)Wall

Thickness Location c/ y c ksi80.1(552)

71.1(490)

85.5(590)

90.0(621)

99.0(683)

Variation (Wall Thickness, inch)

Less than 0.750 0.750 to 0.999 1.000 and over

Hardness Requirements

3.03.03.03.0

4.04.04.04.0

5.05.05.05.0

80808080

Prior AusteniticGrain Size

Threshold StressRequirementsfor SSC Test

according to NACE TM0177Minimum % of SMYS

ASTM 5 andner

22

JFE-80L-95L-110L-125L


Representing the casing and tubing to be used in frigid zones, this series is designed with increased resistance for low-temperature impact in order to withstand shock during delivery, handling, storage, make up, and running in frigid zones. Quenching and tempering is performed to ensure both high yield strength and good low-temperature toughness. Note that the Charpy impact test data of JFE-125L with heavy wall of 0.725 in. below show good results at 50 F. Tensile test results and variation of HRC also show good properties.

a. Specification


(b) Physical Properties

(c) Hardness Tests (HRC) on JFE-125L Casing and Coupling Stock Variation of HRC among three locations (O.D., Mid wall, I.D.) of one quadrant of a ring from JFE-125L shall be as below.

Wall Thickness (inch)

0.500 or less

0.501 to 0.749

0.750 and above

Maximum Variation

3.0

4.0

5.0

2mm V Charpy Impact Requirement (casing only)

JFE-80L

JFE-95L

JFE-110L

JFE-125L

95 (655)

110 (758)

125 (862)

135 (931)

10 10

10 7.5

10 5

25 (34)

20 (27)

14 (19)

19 (26)

15 (20)

10 (14)

As Per

API 5CT -50 F (-46 C)

Grade

80~95(552~655)


Minimum Average Absorbed Energy

ft-lb (J)

Minimum Individual Absorbed Energy

ft-lb (J)SpecimenElongation

95~125(655~862)

110~140(758~965)

125~150(862~1034)

4) Low-Temperature Service

Tensile Requirements

TestTemperature

TensileStrength

min. ksi (MPa)

23

(a) HRC Variation Measurements were made on four quadrants of one test ring.

b. Example of Physical Properties of JFE-125L Casing O.D. 5-1/2'' 0.725'' (139.7 18.42mm)

(b) 2 mm Charpy Test Result Specimen : full size (10 10)

Variation 0.3 1.1 1.0 0.7

OutsideMid WallInside

31.331.231.6

30.531.331.6

30.731.231.7

30.831.531.5

1 2 3 4Quadrant

Location

-250 -200 -150 -100

Test Temperature ( C) ( F)

-50 0 +50 ( F)-300

-140 -100-180 -50 -20 +20 ( C)

20

15

10

5

0

100

50

0

150

100

50

2520

Longitudinal

Transverse

Frac

ture

Ap

pea

ran

ce (

%, S

hea

r)A

bso

rbed

En

erg

y (

kg-m

)

(ft-

lb)

24

JFE-13CR-80

JFE

JFE

-13CR-85-13CR-95-HP1-13CR-95-HP1-13CR-110-HP2-13CR-95-HP2-13CR-110

5) Corrosive Wet CO2 Service


(c) Specified Physical Properties (at Ambient Temperature)

JFE-13CR-80

JFE-13CR-85

JFE-13CR-95

JFE-HP1-13CR-95JFE-HP2-13CR-95

JFE-HP1-13CR-110JFE-HP2-13CR-110

Grade

JFE-13CR

JFE-HP1-13CR

JFE-HP2-13CR

23

24

27

28

30

32

32

API Formula

API Formula

API Formula

API Formula

API Formula

80,000 (552)

85,000 (586)

95,000 (655)

95,000 (655)

110,000 (758)

95,000 (655)

100,000 (689)

110,000 (758)

110,000 (758)

130,000 (896)

95,000 (655)

100,000 (689)

105,000 (724)

105,000 (724)

120,000 (827)

C

0.15~0.22

max. 0.04

max. 0.04

Cr

12.0~14.0

12.0~14.0

12.0~14.0

Ni

max. 0.50

3.50~4.50

4.50~5.50

Mn

0.25~1.00

max. 0.60

max. 0.60

Si, max.

1.00

0.50

0.50

P, max.

0.020

0.020

0.020

S, max.

0.010

0.010

0.005

Mo

0.80~1.50

1.80~2.50

Cu, max.

0.25

GradeElongation

%psi(MPa)

psi(MPa)

psi(MPa)

Tensile Strengthmin.

Hardnessmax.HRC

Yield Strength min. max.

In oil and gas fields being looked to for future development, gas which includes CO2 is an increasingly common occurrence. Corrosion has become the major problem for production strings used in environments including CO2, and there is a great demand for a tubing that has strong resistance to CO2 cor-rosion. JFE Steel's JFE-13CR is a mertensitic stainless steel which combines high performance in such kind of corrosive condition with low cost. For fields with more severe conditions such as high temperature and containing not only CO2 but small amounts of H2S, JFE Steel developed JFE-HP-13CR (HP1 and HP2) material which has higher strength and outstanding anti-corrosion property. It also shows excellent low-temperature toughness.

a. Specifications

(a) Process of Manufacture Process : Seamless Heat Treatment : Quenched and Tempered/Ausformed Tempered

(b) Chemical Composition(wt %)

Notes: -The corrosion testing data in this brochure were obtained from laboratory testing results. Care should always be taken whenselecting materials, as operating conditions may change during the period of usage.-Regarding completion/packer uidCare should be taken in the selection of well uids such as completion/packer uids used in connection with this material in order tominimize the risk of stress corrosion cracking. JFE recommends that you consult with a person knowledgeable about uidcompatibility with this material in making a selection.-Cr tubulars have shown a tendency toward localized pitting corrosion when stored in moist environments.Special precautions during coating, shipping and storage are required.-Anti-galling connectionCr tubulars have been categorized as prone to thread galling, JFE Steel recommends to use FOXTM & JFEBEARTM premium connection which overcomes this concem by its special design criteria. (Please see page 31, 32)

25

0 50 100 150 200 250

10

9

8

7

6

5

4

3

2

1

0

38.6 3.5%NaCl sol.Pco2 = 30 atm(initial)Velocity = 0m/s

13Cr stainless

Carbon steel

Low alloy steel

Duplex stainless

Temperature ( C)

Cor

rosi

on r

ate

(mm

/y)

3.5%NaClCarbon steelLow alloy steel13Cr stainless steelDuplex stainless steel

0.01 0.1 1 10

8

7

6

5

4

3

2

1

0

100

0

200

30010 100 1000

23.5 38.5

Carbon steelLow alloy steel13Cr stainless steelDuplex stainless steel

3.5%NaCl

(psi)

Partial pressure of CO2(MPa)Temperature : 80 C (176 F)

Cor

rosi

on r

ate

(mm

/y)

(mil/

y)

0.01 0.1 1 10

8

7

6

5

4

3

2

1

0

100

0

200

30010 100 1000

Carbon steelLow alloy steel13Cr stainless steelDuplex stainless steel

3.5%NaCl

(psi)

Partial pressure of CO2(MPa)Temperature : 25 C (77 F)

Cor

rosi

on r

ate

(mm

/y)

(mil/

y)

b. Test Data

(a-1) Effect of Temperature on Corrosion Rate

(a-2) Effect of CO2 Partial Pressure on Corrosion Rate

26

1000

20

8

6

4

2

0

Co

rro

sio

n r

ate

(mm

/y)

Cr content (mass%)

No Crack

No Crack Conventional 13Cr

13CRHP1-13CR

SolidOpen

CrackNo Crack

::

Crack

Crack

Temperature ( C)

H2S

Pre

ssu

re (

MPa

)

10050 150

0.001

0.003

0.01

HP1-13CRConventional 13Cr

Sol.: (5%NaCl) Gas: P(H2S+CO2)=3.0MPa 7days

No CrackCrack

No Crack

CrackConventional 13Cr

HP1-13CR

OpenSolid

No CrackCrack

::

Ap

plie

d s

tres

s (%

SM

YS

)

(pH)

100

90

80

70

602.3 2.8 3.3 3.8 4.3

HP1-13CRConventional 13Cr

Sol.: (5%NaCl+0.5%CH3COOH)+CH3COONaGas: 10%H2S+90%CO2 7days

0.300.18 0.22

0.25

0.17

0.13

0.13

0.08

0.120.10

0.15

0.15

0.016

0.060

0.057 0.04220% NaCl sol.

API-13CR

API-13CRHP13CR

pH : 4.50.200.97

0.018

0.910.011

0.071

0.39

Temperature ( C)10075 125 150 175 200 225

CO

2 Pre

ssu

re (

MPa

)

0.01

0.1

1.0

10

HP13CR0.26

Flow rate : 1m/sTemp. : 50 CCO2 : 0.1MPa

0.1%NaCl sol.Sea water

OpenClosed

Corrosion Rate Corrosion Rate

0.127mm/Yr0.127mm/Yr

::

(a-4) CO2 Corrosion Test Results of HP1-13CR and conventional 13Cr

(b-1) C-Ring SSC Test Results of HP1-13CR and conventional 13Cr steels

(b-2) U-Bend SSC Test Results of HP1-13CR and conventional 13Cr steels

(a-3) Effect of Cr Content on CO2 Corrosion Rate

27

(b-3) Effect of Mo content on the resistance to SSC

(C) Physical and Thermal Properties (Information Purpose Only)

Open : No Failure Closed : Failure

2.52 3 3.5 4 54.50.0001

0.001

0.01

0.1

HP2-13CR

HP1-13CR

PH

2S (

MPa

)

pH

4Ni-1Mo (HP1-13CR)5Ni-2Mo (HP2-13CR)

0.025C - 13Cr

Young Modulus Poisson's Ratio

JFE-13CR-80 0.3031,290 ksi (215,700 MPa) 0.0000099/ C for 21.1 C up to 100 C0.0000115/ C for 21.1 C up to 538 C

Thermal Expansion

Minimum Value TemperatureGrade

JFE-13CR-80

JFE-13CR-95

JFE-HP1-13CR-95

JFE-HP1-13CR-110

JFE-HP2-13CR-95

JFE-HP2-13CR-110

YieldStrength

psi(MPa)

50 C(122 F)80,000(550)

98,000(680)

92,000(630)

106,000(730)

98,000(680)

117,000(810)

115,000(790)

126,000(870)

100,000(690)

125,000(860)

78,000(540)

95,000(660)

89,000(610)

101,000(700)

97,000(670)

112,000(770)

110,000(760)

119,000(820)

98,000(680)

120,000(830)

75,000(520)

91,000(630)

88,000(610)

98,000(680)

96,000(660)

108,000(740)

106,000(730)

115,000(790)

96,000(670)

115,000(790)

72,000(500)

90,000(620)

85,000(590)

95,000(660)

94,000(650)

106,000(730)

104,000(720)

114,000(780)

95,000(660)

113,000(780)

109,000(750)

106,000(730)

103,000(710)

101,000(700)

129,000(890)

123,000(850)

117,000(810)

114,000(790)

100 C(212 F)

150 C(302 F)

200 C(392 F)

psi(MPa)

TensileStrength

YieldStrength

psi(MPa)

psi(MPa)

TensileStrength

YieldStrength

psi(MPa)

psi(MPa)

TensileStrength

YieldStrength

psi(MPa)

psi(MPa)

TensileStrength

YieldStrength

psi(MPa)

psi(MPa)

TensileStrength

YieldStrength

psi(MPa)

psi(MPa)

TensileStrength

28

JFE- HP-15CR-1255) High Strength High Temperature Wet CO2 Service

JFE-UHPTM-15CR-125

Grade

JFE-UHPTM-15CR-125

37API Formula125 (862) 150 (1034) 135 (931)

C

max. 0.04

Cr

14.0~16.0

Ni

6.00~7.00

Mn

max. 0.60

Si, max.

0.50

P, max.

0.020

S, max.

0.005

Mo

1.8~2.5

Cu, max.

1.5

GradeElongation

%

Tensile Strengthmin.

Hardnessmax.HRC

Yield Strength min. max.

(wt %)


Notes:

(c) Specified Physical Properties (at Ambient Temperature)

ksi(MPa)

ksi(MPa)

ksi(MPa)

High demand for natural gas, deep water drilling and an increasing number of high pressure, high temperature (HPHT) wells has generated the need for a high strength OCTG material which can provide superior corrosion resistance at high temperatures. JFE-UHPTM-15CR-125 is that material. A tempered Martensitic microstructure provides high strength at ambient and elevated temperatures with excellent corrosion resistance properties in both productive and none productive environments.

a. Specifications

(a) Process of Manufacture Process : Seamless Heat Treatment : Quenched and Tempered/Ausformed Tempered

(b) Chemical Composition

-The corrosion testing data in this brochure were obtained from laboratory testing results. Care should always be taken whenselecting materials, as operating conditions may change during the period of usage.-Regarding completion/packer uidCare should be taken in the selection of well uids such as completion/packer uids used in connection with this material in order tominimize the risk of stress corrosion cracking. JFE recommends that you consult with a person knowledgeable about uidcompatibility with this material in making a selection.-Cr tubulars have shown a tendency toward localized pitting corrosion when stored in moist environments.Special precautions during coating, shipping and storage are required.-Anti-galling connectionCr tubulars have been categorized as prone to thread galling, JFE Steel recommends to use FOXTM & JFEBEARTM premium connection which overcomes this concem by its special design criteria. (Please see page 31, 32)

TM

29

b. Test Data

(1) CO2 Corrosion Test Results of UHPTM-15CR-125

(2) SSC Test Results of UHPTM-15CR-125

0.31

0.18

0.11

0.09

0.07

20% NaCl sol.

OpenClosed

Corrosion Rate Corrosion Rate

0.127mm/Yr0.127mm/Yr

::

Temperature ( C)10050 150 200 250

212122 302 392 482

CO

2 Pre

ssu

re (

MPa

)

CO

2 Pre

ssu

re (

psi

)

0.1

0.01

1

10

14.5

145

1450

UHP -15CR

Temperature ( F)

20% NaCl sol.(Cl - 121,200ppm)

0.5%CH3COOH+CH3COONa

100%SMYS(125ksi)720h

Open : No Failure Closed : Failure

21 3 4 5 60.0001

0.001

0.01

0.1

0.0145

0.145

1.45

14.5

PH

2S (

MP

a)

PH

2S (

psi

)

pH

NACE-TM0177-Method ANACE-TM0177-Method C

0.165% NaCl sol.(Cl - 1,000ppm)

0.5%CH3COOH+CH3COONa

100%SMYS(125ksi)720hOpen : No Failure

Closed : Failure

21 3 4 5 60.0001

0.001

0.01

0.1

0.0145

0.145

1.45

14.5

PH

2S (

MP

a)

PH

2S (

psi

)

pH

NACE-TM0177-Method A

TM

30

15050 100 200 250 300

1000

900

800

700

600

140

125

110

95

Yie

ld S

tren

gth

(M

Pa)

Yie

ld S

tren

gth

(ks

i)

Temperature( C)

(3) Tensile test results of UHPTM-15CR-125 at elevated temperature

(4) Corrosion test results in acidizing condition

JFE-UHPTM-15CR-125 provides better tensile properties at elevated temperature than Duplex stainless steel, which requires cold drawn.

JFE-UHPTM-15CR-125 provides better corrosion resistance than Duplex stainlesssteel during acidizing operations.

Duplex(22Cr)

S-Duplex (25Cr)

UHPTM-15CR

4.88

125.53

UHPTM-15CR-125 22Cr

140

120

100

80

60

40

20

0

Co

rro

sio

n R

ate(

mm

/yr)

1.5%HF + 13.5%HCl + Inhibitor 80C(176F) 24Hrs

Simulatd Live Acid Condition

0.51

4.01

UHPTM-15CR-125 22Cr

4.5

4

3.5

3

2.5

2

1.5

1

0.5

0

Co

rro

sio

n R

ate(

mm

/yr)

5%CH3COOH + 7%HCOOH + 1%HF+ Inhibitor ,80C(176F) 168Hrs

Simulatd Spent Acid Condition

7. Premium Threaded Connections

3

10

THREAD FORM

Modied Buttress Thread

2 3/8", 2-7/8" :8TPI,

3 1/2", 4" :6TPI,

4 1/2" to 13 3/8" :5TPI

SEAL GEOMETRY

Contoured

Metal to Metal Seal

FOXTM is an advanced premium threaded connection jointly developed by JFE Steel Corporation, and Hunting Oilfield Services, in early 1980s.The connection was created using an advanced thread geometry and unique seal design to reduce thread galling and enhance sealing performance. FOXTM is a field proven connection with over 50 million ft sold world wide.

Thread

SealOtherSize

Buttress Modified TypePitch Change on Coupling threadContoured Metal to Metal SealInternal Flash2-3/8" 13-3/8"

1) FOXTM

31

-5

25

THREAD FORM

Special Hook Thread

2 3/8", 2-7/8" :8TPI,

3 1/2", 4" :6TPI,

4 1/2" to 9 5/8" :5TPI

SEAL GEOMETRY

Contoured

Metal to Metal Seal

In today's oil & gas industry, companies are drilling deeper highdeviation wells into high pressure reservoirs using the latest generation of drilling rigs and tools. As a result, the loads placed on OCTG connections in certain well conditons exceed those of an API class1 qualified connection. JFEBEARTM has been designed and tested to withstand today's toughest well conditions.

Thread

SealOtherSize

Negative Load Flank AngleDifferent Load Flank Angles and Corner Radius on Pipe and Coupling ThreadsContoured Metal to Metal SealInternal Flash2-3/8" 9-5/8"

* Detailed information on connections can be found in the FOXTM, and JFEBEARTM brouchures.

2) JFEBEARTM

32

8. Marking

Marking Example

Tubing and casing are paint-stenciled as shown below. The color identification table for JFE-series tubing and casing are shown next page.

33

API5CT L80-13CR FOXTM or JFEBEARTM

License No.

Hydrostatic Test

Size & Nominal Weight

API Monogram

Special End Finish Mark

Process

Drift

Grade

Type of Thread

JFE STEEL 21 9-5/8 53.50 JFE-110T S P9200 BC D 1-12345 76543-01 NO.1 40.1FT

JFE-Series (JFE-110T) BUTC

Process

DriftGrade

Type of Thread

API5CT L80 BUTC

License No.

Year & Quarter

Manufacturer's Name

Size & Nominal Weight

API Monogram

API Spec 5CT

Length

Drift

MFG Number

Shipping Mark

Grade

Process

Type of Thread Pipe NumberHeat Number

(JFEBEAR)JFE STEEL 21 2-7/8 6.40 JFE-13CR-80 S P9700 FOX D 1-12345 76543-01 NO.1 32.0FT

JFE-Series (JFE-13CR-80) FOXTM or JFEBEARTM

Process Drift

Grade

Type of Thread

JFE STEEL 5CT 5CT-0015 21 9-5/8 53.50 L S P7100 BC D 1-12345 76543-01 NO.1 40.1FT

(JFEBEAR)JFE STEEL 5CT 5CT-0015 21 SF 2-7/8 6.40 L13 S P9700 FOX D 1-12345 76543-01 NO.1 32.0FT

Hydrostatic Test

Hydrostatic Test

Hydrostatic TestColor coating for Grade Identification

Grade

JFE 5CT 21 L BC

JFE-110T

(JFEBEAR)FOX

JFE-13CR-802 7/8 6.4

(JFEBEAR)FOX

JFE-13CR-802 7/8 6.4

(JFEBEAR)FOX

JFE 5CT 21 SF L132 7/8 6.4

(JFEBEAR)FOX

JFE 5CT 21 SF L132 7/8 6.4

Type Grade Coupling Pipe Body Type Grade Coupling Pipe Body

9. Color Identification of JFE OCTG(JFE-Series)

HighCollapseCasing(Seamless)

SourService

HighCollapseCasing(ERW)

GeneralService(ERW)

JFE-40E

JFE-55E

JFE-80E

JFE-80ET

JFE-80T

JFE-95T

JFE-110T

JFE-80S

JFE-85S

JFE-90S

JFE-95S

JFE-110S

JFE-85SS

JFE-90SS

JFE-95SS

JFE-110SS

JFE-80TS

JFE-95TS

JFE-80L

JFE-95L

JFE-110L

JFE-125L

JFE-125V

JFE-140V

JFE-13CR-80

JFE-13CR-85

JFE-13CR-95

JFE-HP1- 13CR-95

JFE-HP1- 13CR-110

JFE-HP2- 13CR-95

JFE-HP2- 13CR-110

JFE-UHP- 15CR-125

SpecialSourService

SourService&HighCollapse

ArcticService

DeepWellService

Wet CO2Service

High TemperatureWet CO2Service

High StrengthHigh TemperatureWet CO2Service

The special clearance coupling is painted with a black band adjacent to a color identication band on the coupling.

34

TM

10. Thread Protectors and Packaging

1) Thread Protectors

2) Packaging Bare in bundle or bare in loose is the standard packaging method for carbon OCTG. Other than the standard packaging, customer can choose special packaging such as rack pack (in wooden or plastic), spacer rings or JFE-PACK all of which avoid metal to metal contact during transport and storage.

2. JFE-PACK is composite-type packing unit fit for repetitive re-bundling.

3. JFE-PACK can pack different number of pipes by changing the number of parts.

4. JFE-PACK has drainage function,anti-slip function at the contact portion with pipes.

Various types of protector including composite type are available according to customer's requests.

2000

1500

1000

500

0

4408

3306

2204

1102

011 12 13 14 15 16

DEVIATION (mm)

LOAD-DEVIATIONLB

JFE-PACK1810KG(3989LB)

OTHER PRODUCT1620KG(3570LB)

KG

35

X

SPACER

1. JFE-PACK can be used for all pipe sizes ranging from 2-3/8" to 10-3/4" by changing the spacers.

11. Inquiries and Orders

The following information if available should be specified in your order or inquiry.

1. Specification, Grade and Type

2. Quantity (feet, meters, or number of joints, delivery allowance)

3. Seamless, Electric Welded (ERW) or UOE

4. Casing or Tubing /Threaded or Plain End /Thread Type (API, FOXTM or other premium connection) /With or Without Couplings /Special Clearance Couplings /Special Bevel Couplings

5. Size (Outside Diameter)

6. Nominal Weight with Specified Unit or Wall Thickness

7. Range Length

8. Marking and Packaging (if specification is outside that presented in this brochure)

9. Delivery Date and Shipping Instructions

10. Third Party Inspection

11. Any Other Special Requirements such as; /Hydrostatic Test Pressure /Non Destructive Inspection /Thread Protectors /Thread Compound /Coupling Make Up Other Than Power Tight /Special Drift /Internal Descaling (In case of 13Cr material)

36

1403P(1303) UMPrinted in Japan

NoticeWhile every effort has been made to ensure the accuracy of the information contained within this publication, the use of the information is at the readers risk and no warranty is implied or expressed by JFE Steel Corporation with respect to the use of information contained herein.The information in this publication is subject to change or modification without notice. Please contact the JFE Steel office for the latest information.

Copyright JFE Steel Corporation. All Rights Reserved.Any reproduction, modification, translation, distribution, transmission, uploading of the contents of the document, in whole or in part, is strictly prohibited.

JFE Steel Asia Pte. Ltd.16 Raffles Quay, No. 15-03, Hong Leong Building, 048581, Singapore Phone : (65)6220-1174 Fax : (65)6224-8357

SINGAPORE OFFICE

JFE Steel America, Inc.600 Third Avenue, 12th Floor, New York, NY 10016, U.S.A.Phone : (1)212-310-9320 Fax : (1)212-308-9292

JFE Steel Australia Resources Pty Ltd. Level 19, CPA Centre, 307 Queen St, Brisbane, QLD 4001, AustraliaPhone : (61)7-3229-3855 Fax : (61)7-3229-4377

JFE Steel India Private Limited1101, 11th Floor, Unitechs Signature Tower, Tower-A, South City-I, NH-8, Gurgaon, Haryana, 122002, IndiaPhone : (91)124-426-4981 Fax : (91)124-426-4982

JFE Steel (Thailand) Ltd. 22nd Floor, Abdulrahim Place 990, Rama IV Road, Bangkok 10500, ThailandPhone : (66)2-636-1886 Fax : (66)2-636-1891

JFE Steel Corporation, Jakarta Office 16th Floor Summitmas II, JL Jendral Sudirman Kav. 61-62, Jakarta 12190, IndonesiaPhone : (62)21-522-6405 Fax : (62)21-522-6408

JFE Steel Corporation, Manila Office 23rd Floor 6788 Ayala Avenue, Oledan Square, Makati City, Metro Manila, PhilippinesPhone : (63)2-886-7432 Fax : (63)2-886-7315

JFE Steel Korea Corporation6th Floor. Geumgang-Tower. 889-13, Daechi-dong, Gangnam-gu, Seoul, 135-570, KoreaPhone : (82)2-3468-4130 Fax : (82)2-3468-4137

JFE Steel Corporation Beijing1009 Beijing Fortune Building No.5, Dongsanhuan North Road, Chaoyang District, Beijing, 100004, P.R.ChinaPhone : (86)10-6590-9051 Fax : (86)10-6590-9056

JFE Consulting (Shanghai) Co., Ltd.Room 801, Building A, Far East International Plaza, 319 Xianxia Road, Shanghai 200051, P.R.ChinaPhone : (86)21-6235-1345 Fax : (86)21-6235-1346

TOKYO HEAD OFFICE

NEW YORK OFFICE

BRISBANE OFFICE

JFE Steel do Brasil LTDA / JFE Steel Corporation, Rio de Janeiro OfficePraia de Botafogo, 228 Setor B, Salas 508 & 509, Botafogo, CEP 22250-040, Rio de Janeiro-RJ, BrazilPhone : (55)21-2553-1132 Fax : (55)21-2553-3430

RIO DE JANEIRO OFFICE

NEW DELHI OFFICE

JFE Steel India Private Limited Mumbai Office308, A Wing, 215 Atrium, Andheri - Kurla Road, Andheri (East), Mumbai - 400093, Maharashtra, IndiaPhone : (91)22-3076-2760 Fax : (91)22-3076-2764

MUMBAI OFFICE

JFE Steel Europe Limited 15th Floor, The Broadgate Tower, 20 Primrose Street, London EC2A 2EW, U.K. Phone : (44)20-7426-0166 Fax : (44)20-7247-0168

LONDON OFFICE

JFE Steel Corporation, Dubai OfficeP.O.Box 261791 LOB19-1208, Jebel Ali Free Zone Dubai, U.A.E.Phone : (971)4-884-1833 Fax : (971)4-884-1472

DUBAI OFFICE

BANGKOK OFFICE

JFE Steel Vietnam Co., Ltd.Unit 1401, 14th Floor, Kumho Asiana Plaza , 39 Le Duan Street, Dist 1, HCMC, VietnamPhone : (84)8-3825-8576 Fax : (84)8-3825-8562

VIETNAM OFFICE

JAKARTA OFFICE

MANILA OFFICE

SEOUL OFFICE

BEIJING OFFICE

SHANGHAI OFFICE

GUANGZHOU OFFICE JFE Consulting (Guangzhou) Co., Ltd./ JFE Steel Corporation, Guangzhou OfficeRoom 3901, Citic Plaza, 233 Tian He North Road, Guangzhou 510613, P.R.ChinaPhone : (86)20-3891-2467 Fax : (86)20-3891-2469

Hibiya Kokusai Building, 2-3 Uchisaiwaicho 2-chome, Chiyodaku, Tokyo 100-0011, Japan Phone : (81)3-3597-3111 Fax : (81)3-3597-4860

JFE Steel America, Inc., Houston Office 10777 Westheimer, Suite 230, Houston, TX 77042, U.S.A. Phone : (1)713-532-0052 Fax : (1)713-532-0062

HOUSTON OFFICE

http://www.jfe-steel.co.jp/en/

Cat.No.E1E-012-11

/ColorImageDict > /JPEG2000ColorACSImageDict > /JPEG2000ColorImageDict > /AntiAliasGrayImages false /CropGrayImages false /GrayImageMinResolution 150 /GrayImageMinResolutionPolicy /OK /DownsampleGrayImages true /GrayImageDownsampleType /Bicubic /GrayImageResolution 150 /GrayImageDepth -1 /GrayImageMinDownsampleDepth 2 /GrayImageDownsampleThreshold 1.50000 /EncodeGrayImages true /GrayImageFilter /DCTEncode /AutoFilterGrayImages true /GrayImageAutoFilterStrategy /JPEG /GrayACSImageDict > /GrayImageDict > /JPEG2000GrayACSImageDict > /JPEG2000GrayImageDict > /AntiAliasMonoImages false /CropMonoImages false /MonoImageMinResolution 300 /MonoImageMinResolutionPolicy /OK /DownsampleMonoImages true /MonoImageDownsampleType /Bicubic /MonoImageResolution 300 /MonoImageDepth -1 /MonoImageDownsampleThreshold 1.50000 /EncodeMonoImages true /MonoImageFilter /CCITTFaxEncode /MonoImageDict > /AllowPSXObjects true /CheckCompliance [ /None ] /PDFX1aCheck false /PDFX3Check false /PDFXCompliantPDFOnly false /PDFXNoTrimBoxError true /PDFXTrimBoxToMediaBoxOffset [ 0.00000 0.00000 0.00000 0.00000 ] /PDFXSetBleedBoxToMediaBox true /PDFXBleedBoxToTrimBoxOffset [ 0.00000 0.00000 0.00000 0.00000 ] /PDFXOutputIntentProfile () /PDFXOutputConditionIdentifier () /PDFXOutputCondition () /PDFXRegistryName () /PDFXTrapped /False

/CreateJDFFile false /Description > /Namespace [ (Adobe) (Common) (1.0) ] /OtherNamespaces [ > /FormElements false /GenerateStructure false /IncludeBookmarks false /IncludeHyperlinks false /IncludeInteractive false /IncludeLayers false /IncludeProfiles true /MarksOffset 0 /MarksWeight 0.283460 /MultimediaHandling /UseObjectSettings /Namespace [ (Adobe) (CreativeSuite) (2.0) ] /PDFXOutputIntentProfileSelector /NA /PageMarksFile /JapaneseWithCircle /PreserveEditing false /UntaggedCMYKHandling /UseDocumentProfile /UntaggedRGBHandling /UseDocumentProfile /UseDocumentBleed false >> > ]>> setdistillerparams> setpagedevice

Jfe Steel Octg

Documents

jfe steel octg

jfe steel corporation

jfe series octg

sizesspecification of

jfe octgs

cr steel

cr octg

octg brochure